{'fraction_non_alphanumeric': 0.028833551769331587, 'fraction_numerical': 0.028833551769331587, 'mean_word_length': 5.643478260869565, 'pattern_counts': {'":': 0, '<': 0, '<?xml version=': 0, '>': 0, 'https://': 0, 'lorem ipsum': 0, 'www.': 0, 'xml': 0}, 'pii_count': 0, 'substrings_counts': 0, 'word_list_counts': {'cursed_substrings.json': 0, 'profanity_word_list.json': 0, 'sexual_word_list.json': 0, 'zh_pornsignals.json': 0}}
Intrinsic vacancy-induced nanoscale wire structure in heteroepitaxial Ga2Se3/Si(001).

A highly anisotropic growth morphology is found for heteroepitaxial gallium sesquiselenide (Ga2Se3) on the lattice matched substrate, arsenic-terminated Si(001). Scanning tunneling microscopy of Ga2Se3 films reveals nanoscale, wirelike structures covering the surface in parallel lines, less than 1 nm wide and up to 30 nm long. Core-level photoemission spectroscopy and diffraction reveals the local structure of buried Ga and Se atoms to reflect the bulk, defected zinc-blende structure of beta-Ga2Se3, which contains ordered 110 arrays of Ga vacancies. These ordered vacancy lines are proposed to be responsible for the observed growth anisotropy in heteroepitaxial Ga2Se3.