{'fraction_non_alphanumeric': 0.03383008811051887, 'fraction_numerical': 0.014141194387033613, 'mean_word_length': 4.80214578731461, 'pattern_counts': {'":': 0, '<': 0, '<?xml version=': 0, '>': 1, 'https://': 0, 'lorem ipsum': 0, 'www.': 0, 'xml': 0}, 'pii_count': 0, 'substrings_counts': 0, 'word_list_counts': {'cursed_substrings.json': 0, 'profanity_word_list.json': 0, 'sexual_word_list.json': 0, 'zh_pornsignals.json': 0}}
Stable films of zinc-hexacyanoferrate: electrochemistry and ion insertion capabilities

A stable film of zinc hexacyanoferrate is deposited on a GC (glassy carbon) substrate following a specific electrochemical protocol. The electrode maintains its characteristic even after dry and wet processes. SEM characterization confirms the cubic morphology of the materials and the IR suggests the presence of the FeII-C-N-ZnII structural unit. The electrochemical characterization indicates a very good stability of the film, thus opening application in ion exchange system. The focus is on monovalent, divalent, and trivalent ions. These results, the zinc low toxicity, and cost make zinc hexacyanoferrate films a promising candidate for many electrochemical applications.


Introduction
In situ generation of thin film materials on a conductive substrate is a useful technique for the preparation of electrodes and electrochemical devices for many technological applications. For instance these methods allow steady film fabrication for ion sensors or ion sieve testing [1][2][3]. The advantage of the electrodeposition consists of the in situ functionalization of the electrode surface. This allows to tailor the thin film by controlling some experimental variables such as the applied potential, the precursor concentration, and the supporting electrolytes [4,5]. The electrode modification could be achieved also by adsorption or via mechanical attachment. Metal hexacyanoferrates (MHCFs) or Prussian Blue analogues (PBAs) are inorganic compounds which were successfully electrodeposited [6][7][8]. MHCF thin films fabricated by electrodeposition were used for several applications such as electrocatalysis, energy storage, and above all for ion-sensing detection and exchange capability [9][10][11][12]. Their open structures, also called zeolitic-like, allow to intercalate and store alkali cations upon electrical charging, ensuring the electroneutrality of the compounds. So, they are the perfect candidates for the ion separation controlled by electrochemically switched ion exchange systems, which was reported for the first time by Lilga et al. [13]. The method explained the selective and reversible removal of cesium using an electrode modified by Prussian blue analogue. Briefly, the potential was modulated and switched in polarity, forcing the oxidation/reduction of the thin film, which in turn caused the release or uptake of the alkali metal cation, as described by Eq. (1).
Cations are host in a given lattice site in MHCFs during the reduction reaction, while released during the oxidation step. The relative reduction and oxidation potential are closely related to both the hydration energy and the adsorption energy into the MHCF [23]. The transition metal of the MHCF material also influences their ability as ionic sieve [24,25].
Additional key aspect refers to the abundance of the metal and safety concerns. Among MHCFs, zinc, manganese, and iron analogues are characterized by low toxicity and low cost, therefore making them promising systems for development in several industrial applications [26,27]. In particular, zinc hexacyanoferrate (ZnHCF) is one of the MHCFs used in aqueous ion battery improvement, thanks to its very high operating potential [28]. As shown in Table 1, the precursor salt ZnCl 2 has a LD50 of 350 mg/kg, and relatively cheap while compared to other transition metal chloride salts [22]. LD50, lethal dose or median lethal dose, is defined as the amount of a toxic agent lethal to the 50% of the experimental animals exposed to it. However, although procedures for the deposition of zinc hexacyanoferrate film are available, there is a lack of deposition protocol on the common electrode support (glassy carbon electrode) [29]. For instance, Fenga and Stradiotto suggest a controlled electrodeposit procedure of ZnHCF on piezoelectric quartz crystal [30] and the ZnHCF preparation on graphiteepoxy composite [31]. Eftekhari [32] reported the dependence of the formal potential values in different supporting electrolytes and the electrocatalytic activity of ZnHCF obtained by a direct modification of the Zn electrode. Several procedures of chemical modification of an electrode are reported as well. Joseph et al. [33] studied the behavior of ZnHCF on waximpregnated graphite electrode, evaluating the influence of the Zn 2+ and ferricyanide salt ratio on electrosynthesis step as well as the electrochemical behavior in different supporting electrolytes. Kemmegne-Mbouguen et al. [34] investigate the clay-zinc hexacyanoferrate carbon paste electrode as sensor for uric acid, dopamine, and tryptophan.
This work reports a facile approach to a stable modification of GCE by ZnHCF, obtaining a well-defined redox couple with a formal potential of about +1.0/0.8 V assigned to the redox couples [K 2 ZnFe II (CN) 6 ]/[KZnFe III (CN) 6 ]. Furthermore, ZnHCF was investigated in different support electrolytes, in order to highlight its capability as ionic sieve.

Apparatus
Electrochemical measurements were performed with a Model 730e (CH Instruments) electrochemical workstation using a standard three-electrode electrochemical glass cell (10 ml). The substrate of the working electrode was glassy carbon, GC (diameter 3 mm) or graphite foil, GF (0.10 mm thick, 99.9%, Goodfellow), and a Pt counter electrode was used. All potentials were reported vs Ag/AgCl reference electrode in saturated KCl. The electrochemical behavior in presence of different monovalent, divalent, and trivalent metal cations was investigated by recording CVs in various supporting electrolytes following the protocol: firstly, a CV was recorded in a KCl 0.1 M, then a CV was recorded in other cation 0.1 M solution, and finally, a last CV scan was repeated in 0.1 M KCl [16].

Physical characterization
To perform SEM and ATR-FTIR analysis, ZnHCF was deposited on graphite foil following the protocol described in the "Experimental" section used for GCE modification. Briefly, the oxidized electrode (ZnHCF-O) was obtained potentiodynamically by applying a linear sweep from OCP to +1.2 V in KCl 0.1 M, while the reduced electrode (ZnHCF-R) from OCP to +0.4 V, in the same electrolyte.

ATR-FTIR
IR spectra were recorded from 4000 to 400 cm −1 on a Perki-nElmer Frontier FT-IR instrument, equipped with single reflection ATR unit (universal diamond ATR top-plate) as a sample support.

SEM
SEM experiments were performed on a field emission scanning electron microscope (FESEM) ZEISS SIGMA 300.

ZnHCF electrochemical characterization
Zinc hexacyanoferrate films were obtained on a GCE following the double-step electrosynthesis protocol detailed in the "Experimental section." The soaking of Zn-modified GCE in a K 3 Fe(CN) 6 solution causes the redox reaction in about 10 min. It takes place on the surface of the electrode, with the conversion of zinc to potassium zinc hexacyanoferrate, as follows: The ZnHCF films on GCE were characterized in a 0.1 M KCl solution by cyclic voltammetry. Voltammograms show the K 2 Zn 3 [Fe II (CN) 6 ] 2 /KZn 3 [Fe III (CN) 6 ] 2 reversible redox couple with a formal potential of about +0.9 V vs Ag/AgCl and a steady current density for the first 30 segments (Fig. 1B). The CV shape is characterized also by the weak anodic and cathodic peaks at approximately 0.65 V. As reported, this particular morphology is due to the cubic structure [23] that is confirmed also by the SEM analysis ("Physico-chemical characterization of ZnHCF films" section). Furthermore, the stability of the film by repeated CV scans at 0.1 V s −1 was checked. The intensity of the cathodic  and anodic peak current is stable until the 15th cycle, then it decreases gradually until 50th cycle, and the last cycles are characterized by a fast decrease of the current with the number of the cycles (Fig. 1C). The procedure, described in the "Experimental section," was tested several times obtaining charge values with a RSD % of 21. The data is affected by the electrochemical control lacking during the deposition.
The stickiness was ensured by the electrode drying at room temperature, whereas the electrode rinsing was a precondition to obtain a well-defined peak. Three ZnHCF film comparable CV responses were shown in Fig. 1D, with similar peak current values. The current involved in the process is closely related to the amount of the electroactive material originated from the reaction taking place on the electrode surface during the soaking step. The calculated surface coverage value was 1.46 × 10 −08 mol/cm 2 , considering the average charge value of the first five CVs.
ZnHCF films were characterized using different concentrations of a KCl solution, and the results are reported in Fig. 2. This test reveals the role of the potassium cation in the redox reaction, based on Nerstian equation for a solid film: According to Eq. (4), Fig. 2 shows linear dependence of the two variables (E cathodic vs log of KCl solution (3) K 2 Zn 2 Fe III (CN) 6 concentration) with a slope of about 68 mV, close to theoretical value of 59 mV. This, in turn, confirms a Nerstian behavior and a one-electron transfer reaction. In addition, the effect of other supporting electrolytes was investigated; the results are shown in the "ZnHCF as ionic sieves" section. Figure 3B shows the characterization of the ZnHCF electrode in terms of anodic current dependence to the scan rate. Specifically, the CVs of ZnHCF-GCE at several scan rates are displayed in Fig. 3A. The curves highlighted that the decreasing of the scan rate causes a decreasing of the anodic and cathodic peaks, as expected, and a shifting of E 0 . A checking of the power-law relationship with the scan rate, i.e., i = av b where i is the current of anodic and cathodic peaks, v is the scan rate, and a and b are the experimental parameters, is shown in the panel B of Fig. 3. The panel displays two different slopes for the log(v) − log(i) plot, where b value is about 0.5 at higher scan rate underling a diffusioncontrolled process, whereas b is quoted around 1 at low scan rate, indicating a surface-controlled process. Therefore, the K + insertion/de-insertion processes are surface-controlled at lower scan rates and diffusion-controlled at higher ones. In light of this evidence, we consider that 100 mVs −1 is a suitable scan rate to investigate ZnHCF capability as ionic sieve, which ensure the occurrence of a diffusion-controlled process. Similar results were reported by Eftekhari and Joseph et al. [32,33], who studied the effect of the support electrolytes at high scan rate and at low scan rate, respectively. Eftekhari reported the effect of the support electrolytes on the voltammogram shape and formal potential shifting of the

Physico-chemical characterization of ZnHCF films
The ZnHCF was electrodeposited on grafoil following the same experimental protocol, in order to be investigated by SEM and ATR -FTIR spectroscopy. For this purpose, two different electrodes were analyzed: ZnHCF-O, referring to the oxidized electrode and ZnHCF-R to the reduced one.
SEM characterization reveals a surface morphology composed of poly-dispersed particles that are aggregated to form a porous network. The ZnHCF samples consist of size-heterogeneous particles, of about 100-300 nm (Fig. 4C), although some particles are bigger (Fig. 4B). The morphology is characterized by cubic particles which are pointed out distinctly, at a nanometric level as well. The cubes visible in the figure can be related to the cubic structure of zinc hexacyanoferrate. The morphologies displayed in Fig. 4A, B, for the ZnHCF-R and ZnHCF-O, respectively, confirms a similar behavior of the modified electrode. Therefore, the potentiodynamic modification does not affect the overall shape and morphology of the films.
FTIR characterization provides useful information on the oxidation state of the studied compounds. The ATR-FTIR spectra of the oxidized and reduced electrodes are represented in Fig. 5. All samples show a broad band of the v CN adsorption at about 2000-2200 cm −1 , as expected for bimetallic cyanide Fe-C-N-Zn, which can be used as a fingerprint of the oxidation state. A close inspection of the figure reveals that the spectrum recorded for ZnHCF-O shows a band at 2096 cm −1 , which is close to the band at 2091 cm −1 founded for Fe II -C-N-Zn II system [36]. In addition, the insert in the figure displays a couple of broad peaks at 489 cm −1 and 603 cm −1 which are related to Zn-N and Fe-C stretching, respectively. Lastly, peaks at 1622 cm −1 and 3620 cm −1 are due to the presence of OH from water molecules.

ZnHCF as ionic sieves
A precise protocol was followed to investigate the ZnHCF-GCE electrochemical behavior in several monovalent, divalent, and trivalent cations in order to evaluate the affinity of the tested cations compared to K + : the first CV was recorded in 0.1 M KCl, the second CV was recorded in 0.1 M of cation tested, and finally the last CV was repeated in 0.1 M KCl [16].
The CVs of ZnHCF-GCE were studied in different support electrolyte cations in addition to K + . The results are shown in Fig. 6A (all cations), B (monovalent cations), C (divalent cations), and D (trivalent cations).
The various cation species cause a potential shifting and a peak shape variation (Fig. 6A). This behavior has been reported for other MHCFs [37][38][39] and rationalized in terms of cation overall dimension. An insertion/de-insertion mobility order of monovalent cations was reported for ZnHCF film, and potassium shows the best cation mobility [33]. Figure 6B, C, and D show the ZnHCF film capability to intercalate/de-intercalate, respectively, monovalent, divalent, and trivalent cations compared to K + . The perfect reversibility of the process is confirmed for all the cations, by the CV recorded in K + before and after the CV. There is almost complete match of the pristine and of the recovered CVs in potassium salt, also in terms of peak current. This unambiguously suggest that ZnHCF film here reported has the capacity to exchange monovalent, divalent, and trivalent cations with high efficiency.
Kinetics of the exchange was also investigated, and our experimental data suggests that the uptake of divalent or trivalent ions is slower than the uptake of the potassium. For example, Fig. 7 shows the CVs of ZnHCF recorded in KCl 0.1 M, in CaCl 2 0.1 M, and then back to KCl. Unlike the CV related to the re-uptake of K + ion, the CV recorded during the insertion of Ca 2+ shows a potential shift from the first segment to the steady last ones. A similar behavior does not occur for the potassium insertion; in fact, the voltammogram (Fig. 7) is characterized by the overlapping segments. Therefore, these processes are controlled by kinetics and the uptake of divalent and trivalent cations takes place slowly, whereas smaller radii cations were exchanged easily. Although the channel diameter for metal hexacyanoferrates is similar and close to 320 pm, the cationic radii influence the potential shift and also the attitude of each ion to be inserted and de-inserted [40]. Figure 8 shows the relationship between radii size (hydrated radius) of alkali cations and the ZnHCF intercalation potential. It decreases with the hydrated radii size (in details in Table 2), following the order K ≫ Na > Li, as also accepted for other MHCFs [41]. ZnHCF easily hosts alkali earth cations as well. The diffusion coefficients (D app ) were calculated by the Ip vs v ½ slope. As shown in Table 3, potassium D app is by far the highest as described by the potential vs hydrated radius. As a matter of fact, Li + shows a faster diffusion then Na + into ZnHCF, even though their D app values are comparable. The CVs (Fig. 6C) show a good reversible process in spite of the increasing of ionic radii size of the cations accommodated into the structure. As matter of fact, the lattice might go to microstructural distortions. Ions with smaller ionic radii have larger hydrated radii so they hold on their hydration shells. On the other hand, larger radii ions are less strongly hydrated; therefore, they able to break off their hydration shells during the insertion into the ZnHCF lattice. Similar CVs of the Fig. 7 for monovalent and divalent ions are available as supporting information.

Conclusions
Films of zinc hexacyanoferrate have been deposited on a glassy carbon electrode with a specific protocol aimed at ensuring reproducible electrode characteristics. The morphology of the electrodeposited material has been further studied by SEM and ATR-FTIR spectroscopy confirming the occurrence of the Fe II -C-N-Zn II structural unit. A full electrochemical characterization suggested a good stability of the film and the capacity to intercalate several both monovalent and divalent cations. Kinetics of the intercalation/deintercalation process has been also addressed. Overall, the low-toxicity and cheapness zinc make zinc hexacyanoferrate films a promising candidate for application in ion exchange system.

Author contribution
All authors contributed to the study conception and design. Material preparation, data collection, and analysis were performed by Rosalinda Sciacca. The first draft of the manuscript was written by Rosalinda Sciacca and Marco Giorgetti, and all authors commented on previous versions of the manuscript. All authors read and approved the final manuscript.
Funding Open access funding provided by Alma Mater Studiorum -Università di Bologna within the CRUI-CARE Agreement.
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http:// creat iveco mmons. org/ licen ses/ by/4. 0/.