{'fraction_non_alphanumeric': 0.033817204301075265, 'fraction_numerical': 0.01881720430107527, 'mean_word_length': 4.789293495175848, 'pattern_counts': {'":': 0, '<': 0, '<?xml version=': 0, '>': 0, 'https://': 0, 'lorem ipsum': 0, 'www.': 0, 'xml': 0}, 'pii_count': 0, 'substrings_counts': 0, 'word_list_counts': {'cursed_substrings.json': 1, 'profanity_word_list.json': 0, 'sexual_word_list.json': 0, 'zh_pornsignals.json': 0}}
Anodic Stripping Voltammetric Determination of Copper Traces in Carbonate Minerals and Fly Ash Extracts Using a Screen-Printed Electrode Modified In Situ with Antimony Film

A simple and inexpensive anodic stripping voltammetric procedure for the determination of copper in dolomite, limestone and fly ash extracts is proposed. The method applies an antimony film electrode deposited in situ on a screenprinted graphite substrate. In the optimal conditions: 0.01 M acetate buffer (pH 4.5), 0.01 M KNO3, 0.25 mgL -1 Sb(III) and after 120 s of accumulation at a potential of -1.0 V, the procedure exhibits linear behavior from 4 to 200 μg L-1 Cu(II) with satisfying reproducibility (5%) and an LOD of 0.2 μg L-1.


Introduction
Copper belongs to trace elements essential for biological systems, but it is toxic at higher concentrations [1]. The natural levels of copper in surface water, soil and rock vary significantly, but some carbonate rocks are rich in it. For example, the mineral malachite (copper carbonate hydroxide) occurs together with limestone. If either of these materials, after grinding, is used as a soil conditioner or dietary supplement (dolomite only), providing calcium and magnesium for people or animal food, there is a risk of copper contamination. The concentration of copper in nature may also be influenced by anthropogenic emissions, including those from industrial waste. The passage of water or an aqueous solution through porous material (slag or ash heaps) along with the diffusion of contaminants through material may cause the release of toxic substances to the environment. The precise analytical control of copper levels is therefore very important.
To determine low concentrations of copper in minerals, mainly spectrometric methods are used. These methods include electro thermal atomic absorption spectrometry (ET-AAS), inductively coupled plasma optical emission spectrometry (ICP-OES) and inductively coupled plasma mass spectrometry (ICP-MS). However, the determination of copper traces in dolomites, limestone, and fly ash extracts by means of ET-AAS or of ICP-OES may be problematic due to matrix effects caused by the presence of high concentrations of Ca and Mg in the tested samples. Samples containing a high concentration of sulfates may also be problematic; such samples include water extracts of sulfate-rich fly ash produced during the combustion of carbon in a fluidized bed, where lime is added to fuel to prevent the emission of sulfur oxides. The lime reacts with SO 2 to form sulfates, which become part of the fly ash.
In contrast, anodic stripping (ASV) and adsorptive stripping voltammetry, which require relatively inexpensive instrumentation, are sufficiently sensitive for copper quantification in highly concentrated solutions. The hanging mercury drop electrode (HMDE) or the mercury film electrode have been commonly used for the sensitive detection of the above element by means of the ASV technique [2,3]. Unfortunately, the ASV curves of copper in the vast majority of the supporting electrolytes are partly overlapped by the current from the anodic dissolution of mercury,

Insights in Analytical Electrochemistry ISSN 2470-9867
which makes correct measurements of the Cu response at low concentrations difficult. Moreover, due to restrictions in the manipulation and disposal of mercury and its salts in laboratories in some countries, new electrode materials for the preparation of voltammetric sensors have been proposed and tested. Especially bismuth (BiFE) [4] and, subsequently, antimony (SbFE) film electrodes [5,6], both introduced to the analytical practice at the beginning of the present century, have found wide application for the ASV detection of some metal ions (e.g., Pb, Cd, Zn, In, Tl) and organic compounds [7][8][9][10][11]. Unfortunately, the standard potential of copper is more positive than those of Bi or Sb and the anodic Cu oxidation wave is located outside the accessible potential windows of bismuth and antimony film electrodes.
In spite of the above, Wang et al. demonstrated that, using the BiFE working electrode, a split Cu anodic stripping voltammetric signal was observed at the potential more positive than that of the Bi dissolution peak [12]. However, the applicability of the BiFE for the detection of Cu traces in real samples is limited due to the competition of the electrodeposited copper and the bismuth for surface sites [12,13] and the partial overlapping of the Bi and Cu oxidation waves [14][15][16]. The addition of gallium or hydrogen peroxide alleviated these issues [17][18][19]. The application of the antimony film electrodes (SbFE) for the detection of Cu appeared to be more attractive because of the lower sensitivity of the Sb anodic wave in comparison to that of Bi and consequently, its lower influence on the Cu response. Therefore, mainly SbFEs deposited in situ on the glassy carbon [20,21] and carbon paste [22,23] supports have been proposed for the determination of Cu, although the tin film electrode (SnFE) has also been used for this purpose [24]. It was evidenced that the most sensitive Cu signals at the SbFE deposited in situ on the glassy carbon or carbon paste supports were observed in such supporting electrolytes as hydrochloric acid [20,22,23] or potassium tartrate [21]. Due to the insensitive response of Sb in 0.01 M hydrochloric acid, it was possible to determine a relatively low Cu concentration, although the Cu and Sb anodic peaks were almost identical [23]. On the other hand, when potassium tartrate was used as the supporting electrolyte, the differences in peak potentials of Sb-Cu pair amounted to 160 mV, providing good separation of both signals [21].
Glassy carbon and carbon paste have been commonly used as supports for the preparation of metal film electrodes (BiFE, SBFE, SnFE) plated in situ or ex situ [7][8][9][10][11]. Recently, screenprinted electrodes (SPE) have been attracting increasing interest in stripping voltammetry as an alternative substrate for metal film formation because of their many advantages, such as mass production, low cost, small size, lower susceptibility to oxygen interferences, and the possibility of disposal after a single use [25][26][27][28][29][30]. SPEs work with portable, battery-operated electrochemical analysers, making it possible to test the level of toxic metals on site (e.g., stockpiles of raw materials at production sites, in areas contaminated by leakage from industrial installations, ash or slag heaps). SPEs modified with metal layers are a modern type of sensors, and thanks to their advantages they further broaden the scope of applications of electroanalytical methods. The protocols for the determination of Pb and Cd using anodic stripping voltammetry (ASV) employing SPEs have been extensively investigated. However, those describing the determination of Cu are less widespread because of unfavorably positive oxidation potential. Mercury film and gold-sputtered screen-printed electrodes have first been exploited in a voltammetric study of Cu contents [31,32]. So far, only the recently published paper by Arrino et al. has described the application of a modified SPE with an antimony film for the ASV determination of copper [33].
The authors proposed acetate buffer as a suitable supporting electrolyte for the sensitive determination of Cu, Cd and Pb at the SbFE deposited in situ. The attempts to apply SbF-SPEs have so far been focused on the detection of Cu in certified groundwater [34].
The aim of the presented study was to evaluate the possibility of utilizing anodic stripping voltammetry for the determination of copper in carbonate minerals and water extracts of fly ash using the modified screen-printed graphite electrode. To simplify the course of experiment the antimony film was deposited in situ after spiking the examined solution with Sb(III) ions. To obtain the optimal response of the sensing system, it was necessary to test the influence of chemical and instrumental factors on the copper signal and to also evaluate the influence of main constituents of the samples' matrix.

Experimental Reagents
All solutions were prepared using deionized water with resistivity of 18 MΩ (Millipore Simplicity UV, USA). 1 M acetate buffer of pH 4.5 was prepared by mixing appropriate amount of CH 3 COONH 4 with CH 3 COOH solution (Suprapur, Merck). 1 M potassium nitrate was prepared by dissolving appropriate amount of reagent in water. Standard solutions containing Sb(III) or Cu(II) at a concentration of 1 g L -1 were obtained from Merck and diluted as required.

Apparatus
All measurements were performed using an Autolab potentiostat (EcoChemie, The Netherlands) connected to the PC with GPES 4.9 software. The screen-printed electrodes (4 mm in diameter; carbon DRP C110) were provided by Dropsens, Spain. The working electrode used in all experiments was antimony film plated in situ at a screen-printed carbon electrode (SPCE). A coil of platinum wire served as the counter electrode, and an Ag/AgCl electrode (3 M KCl) (Metrohm, Switzerland) was used as the reference electrode. Photolysis was performed using a UV digestion system with a 150 W lamp (Mineral, Poland).

Measurement procedure
The electrochemical investigations were carried out by means of differential pulse anodic stripping voltammetry. The antimony film was deposited in situ at the surface of the screen-printed carbon electrode (SPE). The film-forming Sb(III) was added directly to the examined solution. An aliquot of the analyzed sample was pipetted into the electrochemical cell. After that, the following reagents were added: 0. deionized water was added to the total volume of 10 ml and dissolved oxygen was removed via 7 minutes of argon purging. Afterwards, the potential of 0.5 V was applied for 30 s to clean the surface of the working electrode. Immediately after cleaning, the potential was changed to -1.0 V and maintained for 60 s to deposit the antimony film and, at the same time, accumulate copper on the surface of the working electrode. During cleaning and accumulation, the solution was stirred using a magnetic bar. After 15 s of rest, a differential pulse voltammogram (DP-ASV) was recorded over the range of -0.4 V to 0.2 V. The modulation amplitude was 50 mV and the potential step was 4 mV.

Sample characteristics
Limestone and dolomite: The powdered dolomite and limestone samples (1 g of both) were digested in 10 ml of 65% HNO 3 (Suprapur, Merck) on a hot plate for 30 minutes, then filtered, transferred to a 100 ml flask and UV-irradiated for 2 h. To speed up the photolysis process, 10 µl of 30% H 2 O 2 was added to each 10 ml of the sample.

Evaluation of the performance of unmodified and antimony-plated screen-printed electrodes
Unmodified screen-printed carbon electrodes can be used to record measurable ASV stripping signals of copper, but their shape and sensitivity are inadequate. The copper signal recorded in a solution containing 20 μg L -1 of Cu(II) is very extended -from -0.22 to 0.05 V -and relatively low (Figure 1). Such a distorted peak in pure acetate buffer makes unmodified SPE unsuitable for the analysis of real samples. Moreover, matrix components adversely affect the voltammetric signals. Adding 0.1 mgL -1 of Sb(III) ions to the examined solution made the determination of Cu(II) via ASV possible. During the electrolytic preconcentration of Cu(II) in the presence of Sb(III) ions at -1.0 V, Sb(III) ions were reduced to form the antimony film and, at the same time, copper accumulated on the surface of the SPE working electrode. The copper response recorded using the in-situ plated antimony SPE (SbF-SPE) was well-shaped, more narrow, and more sensitive (three times higher) than that obtained using the unmodified SPE (Figure 1). The potential of copper peak shifted to more positive values by 58 mV in comparison to that obtained using the unmodified SPE.

Optimization of chemical and instrumental variables
To select the optimal concentration of Sb(III) ions, the effect of its concentration on the copper signal was further investigated (Figure 2). At the Sb(III) ion concentration of 0.25 mg L -1 , the copper peak was the highest and was 3.7 times higher than the copper signal recorded using the unmodified SPE. A small peak originating from antimony oxidation was also observed at a potential 0.1 V more negative than that of the copper peak. Increasing the Sb(III) concentration further resulted in a slight drop in the copper peak current (Figure 2A and 2B). In addition, the antimony signals recorded in solutions with a concentration higher than 0.25 mg L -1 partially distorted the copper signal.
The Cu(II) signals recorded in solutions with acetate buffer concentrations ranging from 0.005 to 0.05 M did not differ to a considerable extent (the RSD of their peak currents was equal to 5.3%; Figure 2C). When increasing the concentration of acetate buffer within the investigated range, the potential of the Cu response shifted to more negative values, by 68 mV per 10 mM. Further experiments were therefore performed in 0.01 M acetate buffer containing 0.25 mg L -1 of Sb(III).
The pH of the supporting electrolyte has a profound effect on the preconcentration efficiency of metals and on the width of the potential window. The influence of the acetate buffer pH was investigated in the range 3.6 to 5.5 by adding the appropriate amount of NaOH. The highest, most narrow and most symmetrical copper signals were recorded in the acetate buffer with the pH of 4.5. In the case of solutions with a pH lower than 4.5, copper and antimony peaks overlapped; when the pH was higher than 4.5, copper peaks were lower and not symmetrical.
The DPV mode was found to be optimal for Cu(II) determination.   The SWV and LSV techniques were not sufficiently sensitive to provide satisfactory signals of Cu(II). The influence of the deposition potential, one of the most important parameters affecting the efficiency of metal ion accumulation, was investigated in the range from -1.2 to -0.2 V. The copper signal increased from -1.2 V up to -1.0 V; less negative accumulation potentials caused the copper signal to decrease. The highest copper signal was obtained for the accumulation potential of -1.0 V, and this value was chosen for further investigations (Figure 2).

Insights in Analytical Electrochemistry
The results of tests performed at the antimony-plated SPE after accumulation at -1.0 V in a solution of 20 µg L -1 of copper showed a linear increase in the copper signal in the accumulation time range of 0 -180 s. For the majority of further experiments, the accumulation time of 60 s was used as a compromise between sensitivity and the duration of the procedure. In some experiments, accumulation was prolonged to 120 s to increase the sensitivity of the copper signal (Figure 3). c acetate buffer / M R 2 =0.99). The loss of linearity at concentrations higher than 200 µg L -1 was likely due to the partial saturation of the electrode surface. The detection limit for an accumulation time of 120 s estimated from 3 times the standard deviation for the lowest concentration of Cu(II) was equal to 0.2 µg L -1 . The reproducibility estimated for 10 subsequent curves was satisfactory (RSD=5%) for voltammograms recorded in the solution containing 4 µg L -1 of Cu(II).

Analytical performance
To validate the proposed protocol, Cu(II) was determined in the reference material (Reference Material for Measurement of Elements in Surface Waters SPS-SW2 Batch 129). Three subsamples were analyzed by applying the optimized chemical and instrumental parameters. The results of copper determination obtained using the in-situ SbF-SPE (96.6 ± 2.2 µg L -1 ) were in good agreement with the certified value of 100.0 ± 1 µg L -1 ( Figure 5).

Interferences
All examined samples were rich in calcium ions; the fly ash Cu(II) appeared for a NaCl concentration as low as 0.2 mM, and became progressively worse up to 0.011 M, at which point the copper peak retained only 15% of its initial value. Consequently, nitric acid was used to digest the solid limestone and dolomite samples.

Application
The investigated in-situ SbF-SPE was applied for the determination of Cu(II) in the digested dolomite and limestone samples, and fly ash extracts. To determine the Cu(II) concentration, the standard additions procedure was used ( Figure 5). Quantification was performed for three aliquots of each investigated sample. The results are presented in Table 1. In the case of fly ash extracts, the components of the solution matrix heavily influenced the Cu(II) response. The copper signals recorded in the pure supporting electrolyte were higher than those recorded in copper-spiked (20 μg L -1 ) samples of fly ash extracts. This signal suppression was observed in 20-fold diluted samples (45% and 21% drop in the copper signal for fly ash 1 and fly ash 2, respectively) and was more pronounced in the less diluted sample solutions. To assess if the suppressing effect was caused by the presence of organic matter originating from unburned carbon compounds, UVphotolysis was performed again for these samples. After 12 hours of photolysis, it was possible to record measureable copper peaks for the extract of fly ash 1. Unfortunately, the copper signal was still not present in the voltammograms recorded for the extract of fly ash 2. In this case, it was only possible to perform recovery studies after spiking the sample with 20 μg L -1 of Cu(II) ( Table 1).

Conclusions
The introduction of Sb(III) ions into the acetate buffer for antimony film formation improved the sensitivity of the voltammetric determination of copper and the quality of the signals recorded using SPEs in terms of symmetry and peak width. Under the optimized conditions, the copper signal recorded using the SbF-SPE was 3.7 times higher than that observed when unmodified SPEs were used. The procedure offers one of the lowest limits of detection (0.2 μg L -1 ) and a linear response over a wide concentration range (4-200 μgL -1 ) when compared with other procedures employing SPEs. It was demonstrated that the proposed method is suitable for the determination of trace copper content in both inorganic natural (carbonate minerals) samples and materials produced by human activity (fly ash). The method is simple and fast, offers sufficient sensitivity, and utilizes relatively inexpensive electrochemical instrumentation. These features make it suitable for the future application in the on-site determination of trace levels of copper.