{'fraction_non_alphanumeric': 0.03570555147957936, 'fraction_numerical': 0.024985734083312953, 'mean_word_length': 5.089600397120874, 'pattern_counts': {'":': 0, '<': 1, '<?xml version=': 0, '>': 0, 'https://': 0, 'lorem ipsum': 0, 'www.': 0, 'xml': 0}, 'pii_count': 0, 'substrings_counts': 0, 'word_list_counts': {'cursed_substrings.json': 0, 'profanity_word_list.json': 0, 'sexual_word_list.json': 0, 'zh_pornsignals.json': 0}}
Nanofiber-enrich activated carbon coin derived from tofu dregs as electrode materials for supercapacitor

In this study, the activated carbon with enriched nanofiber obtained from free-binder materials. It was conducted tofu dregs carbon nanofiber as electrode material for supercapacitor without the addition of pVdF/PTFE. The chemical impregnation of NaOH, ZnCl2 and H3PO4 at hightemperature pyrolysis in an N2-CO2 environment converted the tofu dregs into carbon coin. Subsequently, the physical properties including, microcrystalline, morphology, element analysis, and electrochemical properties of specific capacitance were investigated. The morphological structure of activated carbon showed high nanofiber density and was decorated by sponge-like pores. In addition, the nanofiber contains oxygen content of 12.70% which can act as self-doping due to the pseudo-capacitance properties. Furthermore, the two-electrode system obtained a specific capacitance of 163 F g in 1 M H2SO4 electrolyte. The results showed that tofu dregs-based activated carbon coins are sustainable and efficient to obtain high-dense nanofiber structure as electrode materials for energy storage applications.


Introduction
Supercapacitors are considered as one of the relatively ideal energy storage that can be applied to a variety of digital equipment, electric vehicle, cranes, and laser systems [1,2]. This is due to its relatively easy-to-understand principles, short charge-discharge process, almost unlimited life cycle, and high durability [3]. For almost two decades, improving performance has been inextricably linked with advances in nanotechnology, especially in the fields of materials science and nanomaterials. These fields provide a variety of electrodebased materials including carbon [4], graphene [5], and synthetic polymers [6]. Furthermore, they are provided in various nanometer-scale sizes including nanofibers, nanotubes, nanowire, nanosphere, and nanosheet. Among these various materials, carbon nanofiber has shown remarkable performance in improving energy storage for supercapacitors and other devices such as lithium batteries, fuel cells, water purification applications, and medical applications [7,8]. However, the synthesis is complicated because of the difficulty to obtain a high-density fiber structure.
Biomass and bio-waste are the most popular carbon-based materials recently used in supercapacitor electrode applications. This is due to their abundant availability, easy production process, cost-effectiveness, and high surface area. Furthermore, they allow the presence of nanoscale morphological structures including nanofibers, nanotubes, and nanosheets [9,10]. Biomass can easily be converted to activated carbon through heat treatment in a certain gaseous environment (Ar/N2/CO2/H2O), chemical impregnation (KOH, NaOH, ZnCl2, H3PO4), or a combination of both [11,12]. The main constituent components include lignocellulose consisting of hemicellulose, cellulose, and lignin, which allow the production of activated carbon with tubular [13], rod-like [14], strobili-fiber [15], microsphere [16], nanotube [17], and nanosheet [18] morphologies. Meanwhile, chemical impregnation with high-temperature pyrolysis in a certain gas environment can optimize the fibrils and cellulose in the biowaste components to produce high-density nanofibers [19]. This is due to its hemicellulose, cellulose, and lignin composition, which are connected by b-1-4-linkages and hydrogen bonds [20]. The bond can be removed in the component framework through a pyrolysis process to produce carbon nanofibers. For example, activated carbon nanofiberbased on acacia leaves waste has been successfully obtained through a chemical KOH impregnation and physical activation, with a capacity of 113 F g -1 [21]. In addition, several result was found in other studies [22]. However, biowaste and biomass do not always produce a nanofiber structure on activated carbon as raw materials. Therefore, it is necessary to select the types that contain an effective percentage of lignocellulose content.
One of the bio-wastes that have the potential to be used as a carbon nanofiber-based material is tofu dregs. In the food industry, tofu has an important role because of its high protein content [23], and the development of increasingly sophisticated industrial technology has led to large quantities of production. This is also followed by the number of dregs, which are commonly called tofu dregs. The residual protein contained can offer a nitrogen component and high lignocellulose content for carbon materials [24]. Furthermore, the chemical impregnation process and the right pyrolysis temperature can produce activated carbon with a nanofiber morphological structure.
This study synthesized activated carbon nanofiber through facile with chemical impregnation at N2-CO2 pyrolysis. This method is cost-effective, and without polymers from tofu biowastefor supercapacitor electrodes. Furthermore, activated carbon was synthesized using chemical impregnation of NaOH, ZnCl2, and H3PO4 followed by pyrolysis at a high temperature of 850 °C in an N2-CO2 gas environment. To maintain the real conductivity of the basic material, the activated carbon electrode was prepared in the form of a coin without the addition of PVDF/PTFE. The morphological structure confirms the presence of high nanofiber with carbon and oxygen contents of 87.88% and 12.70% respectively. Moreover, the electrochemical feature has a high specific capacitance of 163 F g -1 in 1 M H2SO4 electrolyte. These results suggest that tofu dregs-based activated carbon coins are sustainable and efficient to obtain high-density nanofiber structure by being chemically impregnated at hightemperature pyrolysis as electrode materials for supercapacitors.

Synthesis of activated carbon coins nanofiber
The basic material of tofu dregs is obtained from the production house of medium-sized businesses in Pekanbaru city. Meanwhile, chemical substances including ZnCl2, NaOH, and H3PO4 with purity of ±98% were obtained from Merck KGaA, 64271 Darmstadt. The tofu dregs were washed, cleaned for further pre-carbonization, and chemically activated in 0.5 m L -1 using three different reagents as ZnCl2, NaOH, and H3PO4. For comparison, a sample without chemical impregnation was provided as a sample powder in a heterogeneous form <60μm. Furthermore, it was converted into solid coin form without the addition of any adhesive component such as polyvinyl or others. The pyrolysis process was conducted in a furnace tube using N2 and CO2 gas atmosphere at a maximum high temperature of 850 °C, and the coin samples were then neutralized in DI water (pH = 7).

Characterizations
Carbon nanofiber coins were characterized by several methods including density changes, crystallinity, surface morphology, chemical elements confirmed, and capacitive properties of supercapacitor cells. The change in density ρ was evaluated by measuring the mass, diameter, and height of the carbon coins, and was calculated twice, before and after the pyrolysis process using standard equations [25]. ρ = m/V  Furthermore, the crystallinity properties were confirmed by X-ray diffraction with Cu Kα radiation in 2θ angel of 15°-65° at V=40.0kV and I=30mA using the Shimadzu-7000L instrument. The surface morphology and chemical elements in the sample were reviewed through the SEM-EDS method using the JEOL-JSM-360LA instrument. Moreover, electrochemical properties such as specific capacitance, specific energy, and power were evaluated by using cyclic voltammetry (CV) and galvanostatic charge-discharge (GCD) techniques. The supercapacitor cells were prepared in the form of sandwich layers consisting of two carbon nanofiber coins-based electrodes, an organic separator, and a stainless steel current collector. Meanwhile, the CV method was applied to a 0-1 constant voltage window with various scan rates of 1,2,5 and 10 mV s -1 and the specific capacitance (Csp) was evaluated using the following equation (2) [26]: Furthermore, the GCD technique was evaluated at a constant current density of 1 A g -1 with the capacitive behavior (Csp) determined according to the following equation (2) [26,27]: Specific energy (Esp) and specific power (Psp) were evaluated using standard formulas (3,4) [16,28]:

Density analysis of carbon coin nanofiber
The chemically activated carbon samples include NaOH, ZnCl2, and H3PO4 in the form of solid coins without adhesive materials at high-temperature pyrolysis. They require initial confirmation to evaluate the success of converting biomass into porous activated carbon coins with a nanofiber structure. This initial confirmation is conducted by evaluating the dimensions of mass, thickness, and diameter in the pyrolysis process which is accumulated in the density changes based on equation . Figure 1 shows the changes in density before and after the pyrolysis process with N2-CO2 stages. All samples showed a reduction in density after pyrolysis, and this is natural because high temperature can decompose and evaporate volatile elements and water content. Furthermore, it may also break down hemicellulose, cellulose, and lignin compounds in the form of CO, CO2, and NH4 gases [29]. The final process creates empty spaces in the coin sample and allows the presence of multiple pore structures to reduce their density. Furthermore, N2-CO2 integrated pyrolysis allows more breakdown of the hemicellulose and lignin [30] attached to the cellulose, and it indicates the presence of a nanofiber structure in the sample [15]. These physical structures favor porous activated carbon to improve the electrochemical properties of the supercapacitor. In addition, this analysis was further confirmed by SEM micrographs and CV/GCD profiles. Before pyrolysis, each sample of TD-Inactivation, TD-NaOH, TD-ZNCl2, and TD-H3PO4 had a density of 0.9328, 0.9510, 1.0144, 0.9472 g cm -3 , respectively.
Meanwhile, after pyrolysis with N2-CO2 level at a high temperature of 850 °C, the density drastically decreased reaching 59.72%, 47.57%, 24.63%, and 11.99% in TD-ZnCl2, TD-NaOH, TD-H3PO4, and TD-Inactivation respectively. The ZnCl2 Impregnation shows the greatest density reduction compared to NaOH and H3PO4. This is because ZnCl2 is a dehydrating agent in biomass-based that reacts faster at 600 °C pyrolysis temperature and oxidizes as well as evaporates impurities. Furthermore, ZnO as an impregnation co-product allows the etching of carbon to form a pore framework on the surface of the sample [31]. The basic reaction between carbon and ZnCl2 was shown in equation  These results showed that the chemical impregnation on N2-CO2 integrated pyrolysis was successful in converting tofu dregs to porous activated carbon coins.

Microstructure features
The microstructural features of activated carbon nanofiber were examined using the XRD technique as shown in figure 2 This is because the ZnCl2 impregnation produces a relatively more random combination of micropores and mesoporous [36] and it corresponds to the data shown in the previous density reduction. In addition, a small number of sharp peaks were found at a 2θ angle of 37.47° which confirmed the presence of crystalline compounds from CaCO3 [14]. The analysis was also confirmed by the EDS data shown in the subsection below, and the appearance of CaCO3 compounds was speculated from the basic constituent elements of tofu dregs which are not completely decomposed by N2-CO2 pyrolysis. Table 1 shows the average interlayer spacing of d002 and d100 of TD-NaOH, TD-ZnCl2, and TD-H3PO4, which was evaluated by using Bragg's Law. The d002 exhibited value in the range of 3.440-3.936 Å while d100 presented the value of 2.060-2.058 Å and were increased by15% compared to normal graphite structures. These values are also similar to others reported by using different raw materials such as pineapple crown [37] and an empty fruit bunch of palm oil [38]. Table 1 also shows the microcrystalline dimension such as stack height (Lc), and width (La) was evaluated by the Debye-Scherrer equation [39]. TD-ZnCl2 sample has the lowest Lc value than TD-NaOH, and TD-H3PO4 samples, while the ratio between Lc and La was decreased. Furthermore, each microcrystalline dimension can be used as a reference to determine the specific surface area of the sample. The relationship between stack height Lc and specific surface area is shown in the empirical formula SSAxrd=2/ρxrdLc [40,41]. Based on this, the highest surface area discovered in the TD-ZnCl2 sample was predicted with TD-NaOH and TD-H3PO4. This speculation is consistent with the density reduction analysis discussed above and it greatly improved the capacitive properties of the supercapacitor electrodes.  Figure 3 illustrates that the morphological structure of the activated carbon coins nanofiber was evaluated using SEM techniques. The micrographs in figure 3 perform the surface morphology of TD-NaOH, TD-ZnCl2, and TD-H3PO4 samples. Furthermore, they were pyrolyzed in an N2-CO2 gasses environment of high temperature 850 °C. The TD-NaOH sample displayed dense nanofiber structures with diameters ranging from 54-285 nm. NaOH impregnation and high-temperature pyrolysis optimized the fibril and cellulose in the lignocellulosic component of biomass to produce highdensity nanofibers. This is due to the composition of tofu dregs which contain hemicellulose, cellulose, and lignin connected by b-1-4-linkages and hydrogen bonds [8,20]. This bond can be removed in the framework through the pyrolysis process of N2-CO2 to produce carbon nanofibers with different surface morphologies. During high-temperature pyrolysis, biomass that has a complex organic structure undergoes decomposition in stages. This begins with the evaporation of water vapor and volatile elements followed by the breakdown of complex compounds including hemicellulose, cellulose, and lignin [19]. Furthermore, the pyrolysis process of N2-CO2 separates and breaks the chemical bonds of functional groups from cellulose [13]. The resulting thermochemical reaction is released in the form of oxygen and carbon monoxide to produce pure carbon and nanofibers [42]. This nanofiber structure improves the performance of the supercapacitor electrode as energy storage due to its high surface area, tunable porosity, and high mechanical and structural stability. In addition, it has a diameter lower than 500 nm with high thermal and electrical conductivity as well as a good loading efficiency [43,44]. In the enlarged area selection, there is a combination of nanofiber and pore interconnection for the TD-ZnCl2 sample, and the resulting fiber diameter ranges from 83-162 nm in size. ZnCl2 as a dehydrating agent directly erodes the constituent components of the sample including cellulose. Therefore, it reduces the density of the fibers, aggregations, and the formation of hierarchically connected pores, which were visible on the surface of the sample. The impregnation of ZnCl2 on carbon coin provided a sponge-like pore structure which allowed activated carbon to have a combination of various sizes including micropores, mesopores, and macropores [45]. These pores store more ionic charges at the electrode/electrolyte interface while providing a 3D ion diffusion pathway [46,47]. Furthermore, they can increase and maintain the energy and power density of the supercapacitor. These properties caused the TD-ZnCl2 sample to have relatively higher electrochemical behavior compared to others as confirmed in the CV and GCD profiles discussed below.

Morphological analysis
Moreover, H3PO4 impregnation followed by hightemperature pyrolysis displayed the surface morphology covered by larger aggregations in the size range of 1.2-2.3μm as shown in figure 3c. Also, H3PO4 as a strong acid reduced the nanofibers on the surface of the sample as confirmed by the enlarged selection area in the SEM micrograph. The visible pores showed a larger size range, and their expansion reduced the porosity and surface area of the carbon electrode as well as the capacitive properties of the sample.

Element status of carbon coin nanofiber
The elemental composition of the TD-NaOH, TD-ZnCl2 and TD-H3PO4 samples was analyzed using energy dispersive spectroscopy (EDS). Table 2 summarizes the elements present in carbon coins nanofiber at different chemical activation of NaOH, ZnCl2, and H3PO4. It has the highest percentage for all carbon monolith samples. A high percentage implies that most of the volatile and non-carbon content has been removed during the activation process [48]. The ZnCl2 impregnation indicates an increasing percentage of carbon. It showed that the decomposition of non-carbon compounds such as organic acids, volatile, and tar occurs effectively [49]. This analysis is confirmed by the reduction of the density of the coin described previously. At TD-NaOH, and TD-H3PO4 samples, the percentage of carbon is reduced slightly with the addition of more oxygen components. This is beneficial to provide wettability of the samples and exhibited the presence of pseudo-capacitance in the electrode material [50,51] as confirmed in the CV profile. Therefore, the NaOH and H3PO4 are more likely to form more oxygen bonds than carbon atoms. Furthermore, low levels of magnesium, calcium, phosphorus, and potassium come from the organic material [52] and the carbon element is almost similar to other biomass/waste-based studies as shown in table 3.

Electrochemical analysis
A The electrochemical performance of tofu dregs-based carbon coins nanofiber from TD-NaOH, TD-ZnCl2, and TD-H3PO4 was evaluated through a two-electrode system in a 1 M H2SO4 aqueous electrolyte. Figure 4 performs a typical CV profile for TD-NaOH, TD-ZnCl2, and TD-H3PO4 samples at a constant voltage of 0.0-1.0V with a low scan rate of 1 mV s -1 . Furthermore, the profile confirmed a distorted rectangular shape for all samples identifying the normal electrochemical properties of the double-layer capacitor (EDLC) due to the ionic charge which undergoes a rapid charge and discharge process [53]. Few samples showed a pair of redox peaks in the 0.3-0.6V voltage range characterizing the presence of pseudocapacitive features due to the faradaic reaction [54,55]. This is because oxygen acts as self-doping in the electrochemical reaction of the sample, especially TD-NaOH and TD-ZnCl2. However, these properties faded in the TD-H3PO4 and TD-Inactivation samples. The largest closed area CV profile found in TD-ZnCl2 confirmed the highest capacitive properties which were followed by TD-NaOH, TD-H3PO4, and TD-Inactivation samples. Based on equation (2), the specific capacitance produced by the CV technique is 15, 145, 148, 127 F g -1 for TD-Inactivation, TD-NaOH, TD-ZnCl2, and TD-H3PO4 samples, respectively. Furthermore, chemically activated samples were able to enhance the specific capacitance by almost 10 times, especially in the ZnCl2 activator agent which showed the highest specific capacitance of 148 F g -1 . The increase in the TD-ZnCl2 samples was due to the combination of the morphological structure of the nanofiber and sponge-like pore. This allows the electrode to have high conductivity, high porosity, and diverse pore distribution to provide all-directional ion transport paths on the surface of the sample [45,56]. Based on the empirical formula of SSAxrd, TD-ZnCl2 is predicted to have a larger specific surface area. This allows the storage of more ionic charges at the electrode/electrolyte interface. In addition, TD-NaOH has capacitive properties that are similar to TD-ZnCl2 of 145 F g -1 even though it does not confirm the pore in the morphological structure. This is because NaOH impregnation provides a nanofiber structure that dominates the surface of the sample. Therefore, it has high conductivity properties and maintains a relatively smooth ion transport pathway for electrolyte ion diffusion. However, H3PO4 impregnation has relatively lower capacitive properties than ZnCl2 and NaOH at 127 F g -1 due to the reduction of the nanofiber on the sample surface. Through equations (3) and (4) the energy and power density of TD-Inactivation, TD-NaOH, TD-ZnCl2, and TD-H3PO4 were also evaluated with the values of 2.08, 20.14, 20.55, and 17.07 Wh kg -1 , as well as the power density of 7.49, 72.57, 74.07, and 63.56 W kg -1 , respectively. Figure 5 shows the specific capacitance to the scan rate increasing from 1 mV s -1 to 10 mV s -1 . Furthermore, all samples showed reduced capacitive properties which were influenced by the expanding pore structure. However, the TD-ZnCl2 maintained a specific capacitance of 54.42%. Therefore, the TD-ZnCl2 sample has better capacitive properties than TD-NaOH and TD-H3PO4 which are only around 48% and 51%. To further validate the electrochemical properties of the activated carbon nanofiber, a two-electrode system was tested using the GCD technique at a constant current density of 1 A g -1 . The GCD profiles for TD-Inactivation, TD-NaOH, TD-ZnCl2, and TD-H3PO4, samples showed a nearly symmetric triangular shape with a slight curvature. It characterizes normal electric double-layer capacitor properties followed by pseudocapacitance [57] as shown in figure 6. This is consistent with the CV analysis that has been discussed previously. Furthermore, activated carbon nanofiber impregnated with ZnCl2 showed the longest charge-discharge time indicating higher capacitive properties followed by TD-NaOH, TD-H3PO4, and TD-Inactivation. This trend data is relatively positive with the CV profile shown in figure 4. Based on equation (3), the specific capacitances generated from GCD are 13, 159, 163, and 134 F g -1 for TD-Inactivation, TD-NaOH, TD -ZnCl2, and TD-H3PO4 samples respectively. In addition, ZnCl2 impregnated coin carbon effectively showed the best capacitive properties compared to NaOH, and H3PO4. This is because it provides high surface area, best amorphous properties, and high conductivity due to the combination of nanofiber and sponge-like pore structure. Based on the GCD profile, iR drop is also evaluated for all samples where the internal resistance of TD-Inactivation, TD-NaOH, TD-ZnCl2, and TD-H3PO4 is 76mΩ, 34mΩ, 21mΩ, and 10mΩ, respectively. However, TD-H3PO4 does not have the best capacitive properties because of its very low resistance. The pore expansion that occurs on the carbon surface provides an unobstructed ion transport path [58]. In addition, power and energy density are also evaluated using the GCD technique using equations (4) and (5). The energy densities for TD-Inactivation, TD-NaOH, TD-ZnCl2, and TD-H3PO4 were 1.81, 22.08, 22.63, 18.61 Wh kg -1 respectively. Meanwhile, the power densities were 6.52, 79.56, 81.54, and 67.06 W kg -1 , respectively. These results are consistent with the analysis obtained from CV data. Furthermore, the capacitive properties obtained were compared with some of the materials for activated carbon electrodes as shown in table 3.

Conclusion
In summary, a simple approach has been proposed to obtain the waste-based porous carbon nanofiber without the addition of synthetic materials such as PTFE, PVP, or PVdF. Furthermore, activated carbon was prepared from tofu dregs with high nanofiber density. A combination of nanofiber and sponge-like pores morphology that allows for various pores including micro, meso, and macropores was featured by ZnCl2 impregnation. These allowed the sample to have more active sites for ionic charges to diffuse at the electrode/electrolyte interface. In addition, a seamless ion diffusion path covering all directions on the sample surface was provided. Carbon coins nanofiber contain oxygen content. It has wettability and hydrophilicity properties due to the presence of pseudocapacitance in the two-electrode system. Moreover, the electrochemical behavior results showed that the carbon coins nanofiber from tofu dregs exhibited excellent capacitive performance. This was particularly evident in the TD-ZnCL2 sample, which produced a high specific capacitance 163 F g -1 at a constant current density of 1 A g -1 . The specific capacitance was still retained at approximately 54.42% in scan rate of 10 mV s -1 . In addition, the excellent electrochemical capacitive behaviors were mainly attributed to the unique nanofiber and sponge-like pores structure. This study developed a facile approach to obtain porous carbon coins material with high performance for supercapacitor application.