{'fraction_non_alphanumeric': 0.042735042735042736, 'fraction_numerical': 0.05128205128205128, 'mean_word_length': 4.354285714285714, 'pattern_counts': {'":': 0, '<': 0, '<?xml version=': 0, '>': 0, 'https://': 0, 'lorem ipsum': 0, 'www.': 0, 'xml': 0}, 'pii_count': 0, 'substrings_counts': 0, 'word_list_counts': {'cursed_substrings.json': 0, 'profanity_word_list.json': 0, 'sexual_word_list.json': 0, 'zh_pornsignals.json': 0}}
Micro-structure and properties of Cu-0.5 wt%Ag alloy fine wires with severe cold plastic deformation treatment

In this work, the Cu-0.5 wt% Ag alloy was prepared and then sold solution treated at 760 °C for 4 h and aged at 400 °C for 4 h. The severe cold plastic deformation treatment with a maximum true strain of 11.48 was applied to obtain the Cu-0.5 wt%Ag fine wires with the diameter of 0.087 mm. Then the fine wires were given eight intermediate heat treatments at 300 °C–350 °C for 10–60 min. Properties of the fine wires with different annealing heat treatments were analyzed, results showed that after the annealing process of 350 °C, 20 min was applied to Cu-0.5 wt% Ag fine wires, their conductivity, tensile strength and elongation could reach 98.6%IACS, 367 MPa and 8%, respectively. This demonstrated that the Cu-0.5 wt% Ag processes high strength and high conductivity properties and was a promising conductive material.