{'fraction_non_alphanumeric': 0.04007869589657111, 'fraction_numerical': 0.041231028667790895, 'mean_word_length': 4.385348872408052, 'pattern_counts': {'":': 0, '<': 5, '<?xml version=': 0, '>': 2, 'https://': 0, 'lorem ipsum': 0, 'www.': 0, 'xml': 0}, 'pii_count': 0, 'substrings_counts': 0, 'word_list_counts': {'cursed_substrings.json': 0, 'profanity_word_list.json': 0, 'sexual_word_list.json': 0, 'zh_pornsignals.json': 0}}
Synthesis, Characterization, and Synergistic Effects of Modified Biochar in Combination with -Fe2O3 NPs on Biogas Production from Red Algae Pterocladia capillacea

This study is the first work that evaluated the effectiveness of unmodified (SD) and modified biochar with ammonium hydroxide (SD-NH2) derived from sawdust waste biomass as an additive for biogas production from red algae Pterocladia capillacea either individually or in combination with hematite α-Fe2O3 NPs. Brunauer, Emmett, and Teller, Fourier transform infrared, thermal gravimetric analysis, X-ray diffraction, transmission electron microscopy, Raman, and a particle size analyzer were used to characterize the generated biochars and the synthesized α-Fe2O3. Fourier transform infrared (FTIR) measurements confirmed the formation of amino groups on the modified biochar surface. The kinetic research demonstrated that both the modified Gompertz and logistic function models fit the experimental data satisfactorily except for 150 SD-NH2 alone or in combination with α-Fe2O3 at a concentration of 10 mg/L. The data suggested that adding unmodified biochar at doses of 50 and 100 mg significantly increased biogas yield compared to untreated algae. The maximum biogas generation (219 mL/g VS) was obtained when 100 mg of unmodified biochar was mixed with 10 mg of α-Fe2O3 in the inoculum.


Introduction
In the recent decades, renewable energy has gained significance largely because of the sources from which it comes [1,2]. Waste-to-energy technologies help process or dispose of less waste while also generating electricity, encouraging the move away from fossil fuels [1,2]. Biomass resources represent an opportunity for sustainable development in bio-based industries, which encompass sectors as diverse as agriculture, food, bio-based chemicals, bio-energy, bio-based textiles, and forestry [3]. In general, initial studies on biomass for energy production have shown that it is a competitive fuel vs. fossil fuels and has a dry matter calorific value of around 17-21 MJ/kg [4]. Biogas may be created from a wide range of sources, as long as they contain organic material. Among these sources are seaweeds, municipal sewage, manure, agricultural waste, and waste dumps [5,6]. The gas composition may vary depending on the source, but methane will always be the significant component [6]. Numerous studies have been conducted to optimize the anaerobic digestion (AD) performance and energy efficiency of biogas-producing technologies to meet global demand for a stable and clean energy source. For example, Europe was striving to achieve one-fifth of renewable energy by 2020 by improving the energy efficiency of existing occurred in the rate of AD for all types of biochar, as confirmed by the thermogravimetric results. The physical properties of the additives, including electrical conductivity and surface area, were found to influence only the rate of AD process and not the biogas production yield [4]. Biochar showed more promising biogas generation results than activated carbon due to its ability to adsorb ammonia nitrogen [4]. Wambugu et al. [5] studied the role of biochar in anaerobic digestion-based biorefinery for food waste, and the results showed that the biogas volume produced by the treatments with the brewery residue hydrochar and treated waste wood pyrochar was lower than the amount of biogas produced by the control with only food waste. These study results indicate that the type of biochar and trace elements concentration in biochar plays a key role in determining the effectiveness of the biochar in enhancing biogas production from food waste.
Biochar modification can enhance the properties associated with the porosity and functional groups and has been identified as an effective way to improve adsorption capacity [30]. The functional groups and surface charge of biochar mainly influence the immobilization of heavy metals, which also depend upon environmental conditions and the type of metals studied for remediation [31]. Recent research has been conducted to determine the role of trace elements and unmodified biochar in the AD of food waste in anaerobic systems, respectively. However, this research did not examine the impact of biochar in conjunction with iron oxide nanoparticles in AD. Additionally, the role of biochar in the continuing AD process has not been reported. Thus, this work aimed to: (i) synthesize, characterize, and modify biochar; (ii) determine the potential of various forms of biochar to increase biogas production, and (iii) determine the influence of biochar in combination with α-Fe 2 O 3 on biogas production. To the authors' knowledge, this is the first study to examine the influence of modified biochar by ammonification on the production of biogas from algae, both singly and in combination with Fe 2 O 3 NPs.

Collection of Red Algae P. capillacea
Red alga P. capillacea was obtained from the Mediterranean coast near Alexandria, gently cleaned with water to eliminate contaminants, and washed multiple times with distilled water and dried in an oven. P. capillacea was dried, processed, crushed to a particle size of approximately 0.5 mm, and stored until usage. According to the literature [32,33], the dry matter has been calculated. By ashing the ground dried samples overnight in a muffle furnace at 550 • C, the ash content was measured. Carbon and nitrogen content was determined from energy dispersive X-ray analysis.

Preparation of Unmodified and Modified Sawdust Raw Materials
The precursors used for the preparation of biochar was sawdust collected from an Egyptian local wood carpentry workshop. It was rinsed numerous times using tap water. Clean sawdust was dried in an oven at 105 • C and then ground and crushed. The crushed sawdust was cooked in a refluxed system for 2 h using a Soxhlet containing 250 g in a 1000 mL solution of 50% H 2 SO 4 (99.999%), then filtered and washed with distilled water until the wash solution became neutral, followed by washing with ethanol. The final result of biochar was dried at 70 • C and then weighed. Modified SD (SD-NH2 ) was prepared by boiling the sawdust (25 g) for 2 h in a refluxed system utilizing a Soxhlet in a 100 mL solution of 25% NH 4 OH (25%), followed by filtration and washing with distilled water and ethanol. The final charcoal product was dried in an oven set to 70 • C [34,35]. H 2 SO 4 and NH 4 OH were obtained from Aldrich Chemicals, Milwaukee, WI, USA.

Characterization and Measurement
The following techniques were used to characterize the samples of α-Fe 2 O 3 NPs and biochar: Fourier transform infrared (FTIR) spectroscopy (platinum ATR) model V-100 VERTEX70, Germany, in the wavenumber range (400-4000 cm −1 ) with resolution values of (4 cm −1 ) and 16 scan, X-ray diffractograms (XRD) using a Bruker Meas Srv (D2-208219)/D2-2082019 diffractometer operating at 30 kV, 10 mA with a Cu tube (λ = 1.54), with a 2θ range of (5-80) for biochar and from  for α-Fe 2 O 3 . Individually, the prepared green nanostructure α-Fe 2 O 3 was characterized using Raman (the sample was exposed to this beam for 1 s at a power of 10 mW and an aperture of 25 1000 mm; three distinct points were measured, and displacement occurred between 100 and 1400 cm −1 ). Transmission electron microscope (TEM) (JEOL, Model JSM 6360LA, Tokyo, Japan), and PSA (the Malvern Mastersizer 3000 is a compact optical system that uses laser diffraction to measure particle size distribution) were used. Thermal analyses of biochar were conducted using SDT650-Simultaneous Thermal Analyzer equipment in the temperature range of room temperature to 900 • C, with a ramping temperature of 5 • C per minute.

Inoculum and Substrates Preparation
Cow excrement was collected from a slaughterhouse in Alexandria, Egypt, sealed in a plastic bag, and stored in a plastic box container until the next day. The cow excrement was diluted 1:1 (w/v) with water.

Biogas Tests
Laboratory tests were conducted on reactors in similar digesters of cylindrical syringes [36][37][38]. The syringes were reversed directly onto the reactor lid [39]. A plastic syringe was used to sample the fuel equipped with a three-way valve and re-injected into the waste. In all tests, 100 mL glass syringes were applied. As feedstock, 1.5 g of milled P. capillacea (dried weight) was used. In each syringe, 20 g (wet weight) of each manure or activated sludge was applied to the untreated and treated P. capillacea. For 10 min, the working volume was flushed with N 2 . For each anaerobic degradation set-up, three replicates were performed. Until no apparent methane was produced, the inoculum was pre-incubated for three days. At 37 • C with continuous shaking at 150 rpm, the digesters were incubated. Table 1 offers an overview of the substrates used in batch experiments to estimate the P. capillacea biogas yield.

Green Synthesis of α-Fe2O3 Nanoparticles
Twenty grams of dried P. capillacea was added to 1.5 L of water and cooked on a hot plate for 20 min at 80 • C. Filtration and storage of the extract solution at 4 • C were performed. Five grams of Fe(NO 3 )3.9H 2 O was dissolved in 30 mL P. capillacea extract and then diluted to 50 mL with distilled water in a beaker. After adding a 6M NaOH solution dropwise to the stirring mixture at room temperature, the product was washed with water and dried at 80 • C for 2 h before being calcified at 450 • C for 2 h [36,40,41].

Kinetics Study and Statistical Analysis
Numerous researchers have used the nonlinear regression models, and the modified Gompertz and logistic function models. Equations (1) and (2) were applied to determine the cumulative biogas production [42][43][44]. In order to compare the accuracy of the studied models, (R 2 ) was calculated using Excel 2010 methods and Origin 2020b.

Chemical Compositions of P. capillacea
As shown in Table 2, the VS content of the investigated P. capillacea is 83.99%. Table 2 shows a C/N ratio of about 5.89%. The majority of the literature recommends a working C/N ratio of between 20 and 30, with a maximum of 25, for anaerobic bacterial growth in the AD system [45], which is still significantly higher than the measured value for P. capillacea. The FTIR spectrum of hematite nanoparticles depicted in Figure 1 demonstrates a series of absorption bands ranging from 400 to 900 cm −1 . The Fe-O vibrational bands of α-Fe 2 O 3 are roughly 627, 580, and 485 cm −1 in this region [46][47][48][49][50]. The vibrational band at 977 cm −1 is due to longitudinal absorptions, but the bands at 538 and 439 cm −1 are due to the transverse absorption of a hematite structure. These bands are seen in Figure 1's FTIR spectrum [51,52]. The FTIR spectrum of the α-Fe 2 O 3 sample exhibits no additional vibrational bands due to the hydration and organic phase used as a capping agent being completely removed after 600 • C calcination.

Raman Spectroscopy
The Raman spectrum of hematite α-Fe2O3 is depicted in Figure 2. It is devoid of peaks associated with maghemite or magnetite. The A1g modes are associated with the 214 and 567 cm −1 peaks [53]. The remaining four peaks at 278, 390, 430, and 616 cm −1 are assigned to the Eg modes [53]. This indicates that heating the initial Fe to 600 °C for four hours will completely convert it to hematite. The data obtained from the FTIR was confirmed by the results obtained from the Raman analysis which proved the formation of the hematite as reported in literature [46][47][48][49][50][51][52][53].

X-ray Diffraction (XRD)
XRD was used to characterize the crystalline structure of the produced α-Fe2O3 nanoparticles. As illustrated in Figure 3

Raman Spectroscopy
The Raman spectrum of hematite α-Fe 2 O 3 is depicted in Figure 2. It is devoid of peaks associated with maghemite or magnetite. The A1g modes are associated with the 214 and 567 cm −1 peaks [53]. The remaining four peaks at 278, 390, 430, and 616 cm −1 are assigned to the Eg modes [53]. This indicates that heating the initial Fe to 600 • C for four hours will completely convert it to hematite. The data obtained from the FTIR was confirmed by the results obtained from the Raman analysis which proved the formation of the hematite as reported in literature [46][47][48][49][50][51][52][53].

Raman Spectroscopy
The Raman spectrum of hematite α-Fe2O3 is depicted in Figure 2. It is devoid of peaks associated with maghemite or magnetite. The A1g modes are associated with the 214 and 567 cm −1 peaks [53]. The remaining four peaks at 278, 390, 430, and 616 cm −1 are assigned to the Eg modes [53]. This indicates that heating the initial Fe to 600 °C for four hours will completely convert it to hematite. The data obtained from the FTIR was confirmed by the results obtained from the Raman analysis which proved the formation of the hematite as reported in literature [46][47][48][49][50][51][52][53].

X-ray Diffraction (XRD)
XRD was used to characterize the crystalline structure of the produced α-Fe2O3 nanoparticles. As illustrated in Figure 3

X-ray Diffraction (XRD)
XRD was used to characterize the crystalline structure of the produced α-Fe 2 O 3 nanoparticles. As illustrated in Figure 3

Transmission Electron Microscopy (TEM)
The TEM micrograph ( Figure 4) revealed that the particles were oval and pyramidshaped, suggesting that they are self-assembled into a large spindle with pores via electrostatic and/or van der Waals forces and aggregated as a result of algal extract solvating and capping the nanoparticles [54]. The particle diameters range from 5.6 to 16.8 nm.

Particle Size Analyzer (PSA) and BET Analysis of the Surface Area
The size distribution is shown in Figure 5 and is defined by PSA for α-Fe2O3 NPs, as a result of detecting α-Fe2O3 hematite in two ranges of size. The range from 6 to 8 nm using a 10° test angle has small size particles and another range of particle sizes around 122 to 691 nm using a 90° test angle; the results indicate the widest size distribution of the α-Fe2O3 nanoparticles. In addition, the dominant sizes of the hematite were about 421 nm. The BET analysis (Table 3) of green α-Fe2O3 shows that the surface area and average pore size of the synthesized magnetite (α-Fe2O3) nanoparticles were 29.29 m 2 /g and 11.92 nm, respectively.

Transmission Electron Microscopy (TEM)
The TEM micrograph ( Figure 4) revealed that the particles were oval and pyramidshaped, suggesting that they are self-assembled into a large spindle with pores via electrostatic and/or van der Waals forces and aggregated as a result of algal extract solvating and capping the nanoparticles [54]. The particle diameters range from 5.6 to 16.8 nm.

Transmission Electron Microscopy (TEM)
The TEM micrograph ( Figure 4) revealed that the particles were oval and pyramidshaped, suggesting that they are self-assembled into a large spindle with pores via electrostatic and/or van der Waals forces and aggregated as a result of algal extract solvating and capping the nanoparticles [54]. The particle diameters range from 5.6 to 16.8 nm.

Particle Size Analyzer (PSA) and BET Analysis of the Surface Area
The size distribution is shown in Figure 5 and is defined by PSA for α-Fe2O3 NPs, as a result of detecting α-Fe2O3 hematite in two ranges of size. The range from 6 to 8 nm using a 10° test angle has small size particles and another range of particle sizes around 122 to 691 nm using a 90° test angle; the results indicate the widest size distribution of the α-Fe2O3 nanoparticles. In addition, the dominant sizes of the hematite were about 421 nm. The BET analysis (Table 3) of green α-Fe2O3 shows that the surface area and average pore size of the synthesized magnetite (α-Fe2O3) nanoparticles were 29.29 m 2 /g and 11.92 nm, respectively.

Particle Size Analyzer (PSA) and BET Analysis of the Surface Area
The size distribution is shown in Figure 5 and is defined by PSA for α-Fe 2 O 3 NPs, as a result of detecting α-Fe 2 O 3 hematite in two ranges of size. The range from 6 to 8 nm using a 10 • test angle has small size particles and another range of particle sizes around 122 to 691 nm using a 90 • test angle; the results indicate the widest size distribution of the α-Fe 2 O 3 nanoparticles. In addition, the dominant sizes of the hematite were about 421 nm. The BET analysis (Table 3) of green α-Fe 2 O 3 shows that the surface area and average pore size of the synthesized magnetite (α-Fe 2 O 3 ) nanoparticles were 29.29 m 2 /g and 11.92 nm, respectively.

Fourier Transform Infrared Spectra (FTIR)
The FTIR spectrum ( Figure 6) was used to qualitatively analyze the chemical structures of biochar modified with H2SO4 and NH4OH. Both samples' FTIR spectra exhibit some similarities. The band between 3388 and 3203 cm -1 corresponds to the -OH and -NH in SD and SD-NH2 biochars, respectively [16,55]. C-H stretching can be attributed to the adsorption peak at 2921 cm -1 . The significant adsorption peak at 1701 cm -1 can be attributed to the carboxyl group's C=O stretching, which was absent in SD and completely absent in SD-NH2 biochars [16,55]. In both SD and SD-NH2 biochars, the band 1581 cm -1 corresponds to the C=O stretching vibration. In SD and SD-NH2 biochars, the peak at 1209-1176 cm -1 represents a rise in C-O-C, while at (1029-1033, 784-792, 615-626) cm -1 represents a Si-O-Si stretching.   The FTIR spectrum ( Figure 6) was used to qualitatively analyze the chemical structures of biochar modified with H 2 SO 4 and NH 4 OH. Both samples' FTIR spectra exhibit some similarities. The band between 3388 and 3203 cm -1 corresponds to the -OH and -NH in SD and SD-NH 2 biochars, respectively [16,55]. C-H stretching can be attributed to the adsorption peak at 2921 cm -1 . The significant adsorption peak at 1701 cm -1 can be attributed to the carboxyl group's C=O stretching, which was absent in SD and completely absent in SD-NH 2 biochars [16,55]. In both SD and SD-NH 2 biochars, the band 1581 cm -1 corresponds to the C=O stretching vibration. In SD and SD-NH 2 biochars, the peak at 1209-1176 cm -1 represents a rise in C-O-C, while at (1029-1033, 784-792, 615-626) cm -1 represents a Si-O-Si stretching.

Fourier Transform Infrared Spectra (FTIR)
The FTIR spectrum ( Figure 6) was used to qualitatively analyze the chemical structures of biochar modified with H2SO4 and NH4OH. Both samples' FTIR spectra exhibit some similarities. The band between 3388 and 3203 cm -1 corresponds to the -OH and -NH in SD and SD-NH2 biochars, respectively [16,55]. C-H stretching can be attributed to the adsorption peak at 2921 cm -1 . The significant adsorption peak at 1701 cm -1 can be attributed to the carboxyl group's C=O stretching, which was absent in SD and completely absent in SD-NH2 biochars [16,55]. In both SD and SD-NH2 biochars, the band 1581 cm -1 corresponds to the C=O stretching vibration. In SD and SD-NH2 biochars, the peak at 1209-1176 cm -1 represents a rise in C-O-C, while at (1029-1033, 784-792, 615-626) cm -1 represents a Si-O-Si stretching.   Figure 7 shows the XRD of the SD and SD-NH 2 biochar. The broad peak in the region of 2θ = 10-30 is indexed as C (002) diffraction peak indicating an amorphous carbon structure with randomly oriented aromatic sheets. There are sharp peaks around 2θ = 27 and 43.65. In the case of SD-NH 2 , sharp peaks around 2θ = 25.8, 43.6, and 63.9 correspond to the miscellaneous inorganic components mainly constituted of quartz and albite, within the structure of SD, which indicated that the original feedstocks were rich in Si, which can be manifested by the Si-O-Si stretching band from FTIR spectra [55].  Figure 7 shows the XRD of the SD and SD-NH2 biochar. The broad peak in the region of 2Ɵ = 10-30 is indexed as C (002) diffraction peak indicating an amorphous carbon structure with randomly oriented aromatic sheets. There are sharp peaks around 2Ɵ = 27 and 43.65. In the case of SD-NH2, sharp peaks around 2Ɵ = 25.8, 43.6, and 63.9 correspond to the miscellaneous inorganic components mainly constituted of quartz and albite, within the structure of SD, which indicated that the original feedstocks were rich in Si, which can be manifested by the Si-O-Si stretching band from FTIR spectra [55].

Thermal Analysis (TGA)
The decomposition of sawdust biochar occurs in three steps, whereas the SD-NH2 biochars decompose in two steps, as illustrated in Figure 8. The first step occurred between 50 and 150 °C as a result of the loss of surface-bound water and moisture present in the sample, resulting in a weight loss of 6.7, 13.21, and 6.7%, respectively, for SD and SD-NH2 [7,34,35]. The second phase results in a 56.30% weight loss at 150-350 °C and a 3.9% weight loss at 150-275 °C for SD and SD-NH2. The third phase results in a 22.55% weight loss at 350-1000 °C and a 30.03% weight loss at 275-1000 °C, for SD and SD-NH2, respectively [7,34,35]. The weight retained by SD-NH2 biochars and the percentages of 2.96% obtained, as well as the DTA curves, indicate that the SD-NH2 biochar amine-modified sample exhibits more stability than the SD biochar [7,34,35]. This enhances the susceptibility to consume SD during anaerobic digestion, which explains why the cumulative amount of biogas produced was greater when SD biochar was used rather than SD-NH2 biochars.

Thermal Analysis (TGA)
The decomposition of sawdust biochar occurs in three steps, whereas the SD-NH 2 biochars decompose in two steps, as illustrated in Figure 8. The first step occurred between 50 and 150 • C as a result of the loss of surface-bound water and moisture present in the sample, resulting in a weight loss of 6.7, 13.21, and 6.7%, respectively, for SD and SD-NH 2 [7,34,35]. The second phase results in a 56.30% weight loss at 150-350 • C and a 3.9% weight loss at 150-275 • C for SD and SD-NH 2 . The third phase results in a 22.55% weight loss at 350-1000 • C and a 30.03% weight loss at 275-1000 • C, for SD and SD-NH 2 , respectively [7,34,35]. The weight retained by SD-NH 2 biochars and the percentages of 2.96% obtained, as well as the DTA curves, indicate that the SD-NH 2 biochar aminemodified sample exhibits more stability than the SD biochar [7,34,35]. This enhances the susceptibility to consume SD during anaerobic digestion, which explains why the cumulative amount of biogas produced was greater when SD biochar was used rather than SD-NH 2 biochars.

BET Analysis of the Surface Area
The parameters of SD and SD-NH 2 biochars, including their BET-specific surface area, total pore volume, and mean pore diameter, are reported in Table 4. Interestingly, the modification enhanced the surface area of SD (2.913) and SD-NH 2 (3.19) biochars.

BET Analysis of the Surface Area
The parameters of SD and SD-NH2 biochars, including their BET-specific surface area, total pore volume, and mean pore diameter, are reported in Table 4. Interestingly, the modification enhanced the surface area of SD (2.913) and SD-NH2 (3.19) biochars.

Impact of Pretreatment on Anaerobic Digestion by Batch
For 40 days, the experimental results of biogas output yields were collected and are shown in Figure 9. When the treated P. capillacea was treated with an SD dose (100, 50 mg/L), the average biogas production yield was marginally increased compared to the biogas production yield without biochar treatment, as shown in Figure 9.

Impact of Pretreatment on Anaerobic Digestion by Batch
For 40 days, the experimental results of biogas output yields were collected and are shown in Figure 9. When the treated P. capillacea was treated with an SD dose (100, 50 mg/L), the average biogas production yield was marginally increased compared to the biogas production yield without biochar treatment, as shown in Figure 9.
A major positive effect on the production of biogas (p < 0.05) was achieved when P. capillacea was treated with 100 mg SD combined with 10 mg α-Fe 2 O 3 . The dosage of 100 mg SD combined with 10 mg α-Fe 2 O 3 produces higher biogas yield with 219 mL/g VS for P. capillacea combined with manure. It is also worth mentioning that when P. capillacea was treated with unmodified SD with different dosages of 50, 100, and 150 mg/L, the biogas was increased more than the control sample, which produces a higher biogas yield with 171, 205, and 169.5 mL/g VS, respectively. It is also clear that modified SD-NH 2 with all higher dosages, except 100 and 150 mg/L, has inhibitory effects on the biogas production.
Biogas output tests have been completed when, as seen in Figure 10, the regular production of biogas is <1% of the total production of most of the tests conducted. It is clear that the biogas output of P. capillacea treated with 50 mg/L of SD-NH 2 is around 169.5 mL/g VS, which is equal to the biogas yield formed by 100 mg/L dosage of unmodified biochar and is higher than the biogas produced from the untreated algae (control), which yields 138 mL/g VS. This may indicate that the little dosages of SD-NH 2 may have no detrimental effect on methane yield of biogas production and the addition effect of biochar in biogas is dosage dependent.  . Average production of cumulative net biogas (mL/g VS) using (a) raw and untreated + raw pretreated with α-Fe2O3, (b) raw and raw pretreated with SD, (c) raw and raw pretreated with SD-NH2, (d) raw and combination of α-Fe2O3 NPs and SD, and (e) raw and combination of SD-NH2 with α-Fe2O3 NPs.
A major positive effect on the production of biogas (p < 0.05) was achieved when P. capillacea was treated with 100 mg SD combined with 10 mg α-Fe2O3. The dosage of 100 mg SD combined with 10 mg α-Fe2O3 produces higher biogas yield with 219 mL/g VS for P. capillacea combined with manure. It is also worth mentioning that when P. capillacea was treated with unmodified SD with different dosages of 50, 100, and 150 mg/L, the biogas was increased more than the control sample, which produces a higher biogas yield with 171, 205, and 169.5 mL/g VS, respectively. It is also clear that modified SD-NH2 with all higher dosages, except 100 and 150 mg/L, has inhibitory effects on the biogas production.
Biogas output tests have been completed when, as seen in Figure 10, the regular production of biogas is <1% of the total production of most of the tests conducted. It is clear that the biogas output of P. capillacea treated with 50 mg/L of SD-NH2 is around 169.5 mL/g VS, which is equal to the biogas yield formed by 100 mg/L dosage of unmodified biochar and is higher than the biogas produced from the untreated algae (control), which yields 138 mL/g VS. This may indicate that the little dosages of SD-NH2 may have no detrimental effect on methane yield of biogas production and the addition effect of biochar in biogas is dosage dependent. Due to the possibility of ammonia accumulation during anaerobic digestion of food waste, its use in industrial biogas facilities is restricted. Sheng et al. [56] investigated the effect of ammonia and nitrate on biogas production from food waste via anaerobic digestion. They discovered that lower ammonia concentrations (1.544 g L −1 ) had no detrimental effect on methane yield, whereas higher TAN concentrations (>3.78 g L −1 ) resulted in severe inhibition of methanogenesis. These findings corroborate our findings that greater doses of SD-NH 2 restrict the formation of biogas from P. capillacea. This inhibitory effect became worse and gave more inhibitory effect when the P. capillacea was treated with SD-NH 2 with a combination with α-Fe 2 O 3 with a dosage of 10 mg/L and the biogas yield was 127, 24, and 9 mL/g VS. The reason for this inhibitory effect may be explained by the releasing of more nitrogen which will be converted into ammonia in the digester according to the following equation: The release of N 2 can alter the C/N ratio, and changes in the C/N ratio can change the pH of a slurry [57]. Increased carbon content results in increased carbon dioxide creation and a lower pH value. In contrast, increased nitrogen content results in increased ammonia gas production, which may raise the pH to the detriment of microorganisms [57].  Figure 10. Average rate of the daily production of the biogas using (a) raw and untreated + raw pretreated with α-Fe2O3, (b) raw and raw pretreated with SD, (c) raw and raw pretreated with SD-NH2, (d) raw and combination of α-Fe2O3 NPs and SD, and (e) raw and combination of SD-NH2 with α-Fe2O3 NPs.
Due to the possibility of ammonia accumulation during anaerobic digestion of food waste, its use in industrial biogas facilities is restricted. Sheng et al. [56] investigated the effect of ammonia and nitrate on biogas production from food waste via anaerobic digestion. They discovered that lower ammonia concentrations (1.544 g L −1 ) had no detrimental effect on methane yield, whereas higher TAN concentrations (>3.78 g L −1 ) resulted in severe inhibition of methanogenesis. These findings corroborate our findings that greater doses of SD-NH2 restrict the formation of biogas from P. capillacea. This inhibitory effect became worse and gave more inhibitory effect when the P. capillacea was treated with SD-NH2 with a combination with α-Fe2O3 with a dosage of 10 mg/L and the biogas yield was 127, 24, and 9 mL/g VS. The reason for this inhibitory effect may be explained by the releasing of more nitrogen which will be converted into ammonia in the digester according to the following equation: Fe2O3 (s) + 2 NH3 (aq) → 2 Fe (s) + N2 (g) + 3 H2O The release of N2 can alter the C/N ratio, and changes in the C/N ratio can change the pH of a slurry [57]. Increased carbon content results in increased carbon dioxide creation and a lower pH value. In contrast, increased nitrogen content results in increased ammonia gas production, which may raise the pH to the detriment of microorganisms [57]. The addition of 10 mg/L α-Fe 2 O 3 resulted in a 12% increase in biogas production over control (138 mL/g VS), which is consistent with the results obtained by Abdelwahab et al. [58], who stated that the addition of 15, 30, and 60 mg/L Fe NPs increases specific biogas production startup by 124.7, 85.1, and 40.3%, respectively. The addition of SD in combination with 10 mg/L α-Fe 2 O 3 increased biogas generation by 40% compared to the control and by 29% compared to the individual SD treatment. These findings are consistent with those of Abdelsalam et al. [59], who discovered that adding 5, 10, and 15 mg/L Fe NPs (20 nm) increases biogas production startup by 250.7, 270.3, and 264.5%, respectively, as compared to using only cattle dung. This discrepancy in results, however, could be explained by the size and concentration of Fe NPs. The size, concentration, and type of NPs have a significant effect in biogas production [38,59]. In our study, the TEM analysis showed α-Fe 2 O 3 NPs in the range of 5-16 nm, which is near the range studied by Abdelsalam [59] (20 nm), which may confirm that the small size of α-Fe 2 O 3 NPs may have a good impact on methanogenesis bacteria. Cumulative specific biogas production results demonstrated a substantial increase (p < 0.05) in cumulative biogas production when α-Fe 2 O 3 NPs and unmodified SD were added to control manure alone, as seen in Figure 9. In this study, the highest biogas yield of 219 mL/g VS was still lower than the results obtained by Hassaan et al. [12], who studied ozonation pretreatment's effect on the biogas production from Ulva lactuca with biogas yield around 499 mL/g VS with higher ozonation time (30 min), but it is still higher than the biogas yield attained by Hassaan et al. [12] when using ozonation time (10 min).
This work can be a good addition to support the circularity of resources due to it having a significant effect on the circular bioeconomy by using red algae P. capillacea as a source of biomass and also to synthesize green α-F 2 O 3 . Another way of using biomass to enhance the bioeconomy is by using the SD waste to synthesize biochar and that will lead to reducing pressure on the environment, and to the creating of new green industries and jobs and boosting economic growth.

Kinetic Study
The data of the gas production kinetic study have been summarized in Tables 5 and 6. It is reported that the Gompertz and logistic feature models matched well the experimental findings, except for 150 SD-NH 2 individually or in combination with α-Fe 2 O 3 with a dosage of 10 mg/L. For the logistic feature model and the modified Gompertz model, Rm of 14.53 and 12.16 mL/g VS, respectively, of biogas production when algae was treated with unmodified SD were observed [42,60]. The modified Gompertz and logistic models' functional received λ values of 0.1 and 0.29 days, respectively. Our work's value is extremely low compared to previously published values [38,61], for both modified Gompertz and logistic function models. The model's reliability was tested by plotting the calculated values for biogas production against the observed values (Figures 11 and 12). Tables 5 and 6 additionally include statistical indicators (R 2 ) to help visualize the kinetics study. According to Nguyen et al. [42], the higher R 2 values (0.999 and 0.994) for modified Gompertz and logistic feature models, respectively, indicated a more appropriate kinetic model. Both models in our analysis have a superior R 2 of 0.997, which is near the same values attained by [12,38].

Conclusions
This study is the first work that studies the impact of nanoparticles with biochar on biogas production from seaweeds. The biomass of the red algae P. capillacea was pretreated with two different types of biochar either individually or combined with α-Fe 2 O 3 for enhancing biogas production in this work. As a result, the unmodified biochar SD with all different dosages increased the biogas ability of the studied red algae P. capillacea compared to untreated P. capillacea. On the other hand, the modified biochar SD-NH 2 has an inhibitory effect on biogas production for higher dosages (100 and 150 mg/L). TEM, Raman, FTIR, PSA, and XRD confirmed the synthesis of α-Fe 2 O 3 NPs. When P. capillacea pretreated with α-Fe 2 O 3 alone and combined with 100 mg/L SD, the biogas increased by 12 and 40%, respectively. The updated Gompertz model and the logistic function model (R 2 = 0.997) were appropriate models to match the calculated biogas production and could be used more reasonably to characterize the kinetics of the AD phase. Moreover, from our results and literature, the type of biochar, trace elements concentration in biochar, and the modification method play a key role in determining the effectiveness of the biochar in enhancing biogas production. The compatibility of the P. capillacea bioprocess, the emission of biogas, techno-economic analysis, and compositional analysis of the used seaweeds should also be studied in a future study. On the basis of our data, the bio-energy is one of the major renewable energy types that demands substantial financial investment. In order to meet the challenge, the Egyptian government should make a significant contribution to the construction of more biogas and biomethane production plants in the coming years.

Conflicts of Interest:
The authors declare no conflict of interest.

AD
Anaerobic digestion NPs Nanoparticles Fe 2 O 3 NPs Hematite nanoparticles SD Sawdust SD+NH 2 Modified sawdust with NH 4 OH FTIR Fourier transform infrared XRD X-ray diffractograms TEM Transmission electron microscopy EDX Energy dispersive X-ray spectroscopy BET Brunauer-Emmett-Teller TGA Thermo gravimetric analysis TS Total solids Rm The maximum biogas production rate VS Volatile solids λ The lag phase time (days)