{'fraction_non_alphanumeric': 0.043050255020151945, 'fraction_numerical': 0.022684310018903593, 'mean_word_length': 4.717373572593801, 'pattern_counts': {'":': 0, '<': 1, '<?xml version=': 0, '>': 0, 'https://': 0, 'lorem ipsum': 0, 'www.': 0, 'xml': 0}, 'pii_count': 0, 'substrings_counts': 0, 'word_list_counts': {'cursed_substrings.json': 1, 'profanity_word_list.json': 0, 'sexual_word_list.json': 0, 'zh_pornsignals.json': 0}}
Axial Coordination Site-Turned Surface Confinement, Electron Transfer, and Bio-Electrocatalytic Applications of a Hemin Complex on Graphitic Carbon Nanomaterial-Modified Electrodes

Understanding the relation between the chemical bonding and the electron-transfer (ET) reaction of surface-confined hemin (a five-coordinated Fe-porphyrin-with-chlorine complex) is a special interest in the biomimicking studies of heme proteins. Owing to the difficulty in ET function, scanty electrochemical reports of hemin in aqueous solution were reported. It has been noticed that in most of the reported procedures, the sixth axial coordination position of the hemin complex has been unknowingly turned by attaching with water molecules (potential cycling in alkaline conditions or heating), solvents such as ethanol and dimethyl sulfoxide, and nitrogen-donating compounds that have helped for the heme ET reaction. In this work, a systematic effort has been taken to find out the contribution of hemin and its axial bond coordination with π–π interaction, hydrogen bonding, and hydrophobic binding systems toward the ET reaction. Various graphitic carbons such as graphitized mesoporous carbon (GMC), mesoporous carbon-hydrophilic and hydrophobic units, graphite nanopowder, graphene oxide, single-walled carbon, multiwalled carbon nanotube (MWCNT), and carboxylic acid-functionalized MWCNT (as a source for π–π interaction, hydrogen bonding, and hydrophobic environment) along with the amino functional group of chitosan (Chit; as an axial site coordinating system) have been tested by modifying them as a hemin hybrid on a glassy carbon electrode (GCE). In addition, a gold nanoparticle (Aunano) system was combined with the above matrix as a molecular wiring agent, and its role was examined. A highly stable and well-defined redox peak at an apparent formal potential (Eo′) of −320 mV versus Ag/AgCl with the highest surface excess of 120 × 10–10 mol cm–2 was noticed with the GCE/Aunano–GMC@hemin–Chit hybrid system, wherein all interactive features have been utilized. Omitting any of the individual interactions resulted in either decreased (with Aunano) or nil current response. As applications, efficient bio-electrocatalytic reduction and sensing of dissolved oxygen and hydrogen peroxide have been demonstrated.


INTRODUCTION
Hemin, a five-coordinated Fe-porphyrin-with-chlorine complex (Scheme 1), is a derived active site of the heme-containing proteins and enzymes such as hemoglobin (Hb), cytochrome C, horseradish peroxidase, and catalase. 1 It is produced endogenously in the human body during the turnover of red blood cells (RBCs). 2 Indeed, it forms inappropriately as a result of vascular (vessels that carry blood) injury or hemolysis (rupture or destruction of RBCs) in the physiological system. 3 It has been revealed that the endogenously formed hemin helps in intracellular generation of reactive oxygen species (ROS) such as hydrogen peroxide, singlet oxygen, hydroxyl radicals, and superoxide. 4 At the same time, this hemin has the capacity to interact with the peroxide and oxygen molecules and facilitates their bio-electrocatalytic reduction to water by mediated electron-transfer (ET) reaction mechanism (at specific operating potentials). 5 Note that meticulous ROS production in human cells assists in energy production 6 and apoptosis 7 and supports to combat pathogens. Indeed, abandoned ROS leads to permanent damage of the cell organelles and tissues. 8 Biomimicking the ET function of the hemin and probing the mysteries of its biological function are a continued research interest. In this regard, fixing hemin as a surface-confined species similar to the natural system is an important step. Unfortunately, there is no clear and systematic information about ET of surface-confined hemin complex covering π−π and hydrogen bonding and axial ligand coordination, in the literature. The electro-inactive character of hemin on solid electrodes is a prime reason for the limitation. Herein, we report a meticulously designed heminconfined carbon nanomaterial (graphitic base)/chitosan (Chit) chemically modified electrode, designated as glassy carbon electrode (GCE)/carbon@hemin−Chit, for an efficient ET and mediated reduction of dissolved oxygen and hydrogen peroxide in a physiological system.
With the aim of biomimetic studies, since 1928, there has been significant interest on the ET feature of hemin (homogenous condition) in organic and semiaqueous mediums. 9−12 In 1967, Bednarski and Jordan first reported the adsorption and ET study of hemin on the dropping Hg electrode in 0.1 M KOH solution and stated that hemin forms a soluble dimer, which undergoes a two-electron reversible reduction to yield a ferroheme monomer (wherein two water molecules are attached on the two axial positions). 12 Following this, there were several studies on hemin complex with Hg systems. 13,14 In 1990, Bianco et al. reported adsorption of hemin on a pyrolytic graphite electrode (PGE) and showed an ET reaction at E o ′ ≈ −0.55 V versus Ag/AgCl with a surface excess of Γ hemin = 11 × 10 −10 mol cm −2 in pH 7 phosphate buffer solution (PBS). 15 In their preparation procedure, the PGE was simply exposed to hemin solution containing 30% ethanol/borate buffer of pH 11. It has been claimed that the π−π interaction between the graphitic sites and hemin is responsible for the adsorption and ET feature. In a similar fashion, hemin was adsorbed on a multiwalled carbon nanotube (MWCNT) via π−π interaction and showed E o ′ = −0.34 V versus Ag/AgCl and Γ hemin = 27 × 10 −10 mol cm −2 . 16 Later on, a covalently immobilized hemin on an amino-functionalized M W C N T -m o d i fi e d e l e c t r o d e v i a 1 -e t h y l -3 -( 3dimethylaminopropyl)carbodiimide (EDC) (E o ′ ≈ −0.5 V vs Ag/AgCl in pH 1 buffer) was reported. 17 Recently, heminimmobilized graphene oxide (GO)-(a hemin−NaOH solution heated at 70°C was used; E o ′ = −0.15 V vs Ag/AgCl; Γ hemin ≈ 1 × 10 −10 mol cm −2 ) 18 and gold nanoparticle−GO (a mixture of ethanolic solution of hemin−GO−Au nano was used; E o ′ = −0.4 V vs Ag/AgCl, Γ hemin ≈ 2 × 10 −10 mol cm −2 )-19 based chemically modified electrodes were reported in the literature. All of those studies emphasize the π−π interaction for the ET process. Meanwhile, there were few reports on hemin surfaceconfined gold self-assembled monolayer electrodes utilizing nitrogen-containing biomolecules such as histidine and guanine quadruplex (G4) complexes with E o ′ = −0.22 to −0.35 V versus Ag/AgCl and Γ hemin = 0.0016−2.2 × 10 −10 mol cm −2 . These above reports highlight the importance of the planar orientation and axial ligand interactions for the ET activity. 20,21 In this report, π−π interaction, axial ligand coordination, and multihydrogen bonding were collectively tuned for the enhanced ET reaction of the hemin on a carbon nanomaterial/Chit-modified electrode system. Importance of the axial ligand coordination in the ET of hemin was first reported by Richard

ACS Omega
Article hemin derivatives and pK a of the axial ligands had been shown. Further, it was stated that nitrogen-and sulfur-containing solvents such as dimethyl sulfoxide and dimethylformamide are capable of coordinating with hemin (in the sixth position) and assisting the ET feature. 22 Surprisingly, in many of the previous studies with hemin-surface confined systems, the axial position of the hemin has been unknowingly turned. 18,19,21 For instance, water molecules attachment in the axial positions by electrochemical treatment in alkaline solution and heating, 18 and using organic solvent or compounds like ethanol and EDC as a coordinating ligand in the preparation procedure. 18,19,21 In this report, to understand the role of the sixth vacant axial position of the hemin site in association with other chemical interactions, a systematic effort has been taken by providing a control environment using Chit, graphitic carbon nanomaterials, especially graphitized mesoporous carbon (GMC), and gold nanoparticles to confinement of the hemin complex. The GMC provides not only a graphitic environment for π−π interaction but also a mesoporous space (∼50 nm) 23,24 and oxygen functional groups for the entrapment and hydrogen bonding. Similarly, the amino functional group of the Chit helps for the sixth vacant axial position coordination, and gold nanoparticles support as an internal ET linker (wiring). Previously, it has been shown that Chit, a linear polysaccharide-based biopolymer obtained from shrimp cells, 23 is effective for complexation with the iron site 25−27 and gold nanoparticles as a linker for the electrical wiring of biomolecules. 28−30 Several control experiments were carried out utilizing different carbon nanomaterials such as mesoporous carbon (CM)-hydrophobic unit, CMhydrophilic unit, GO, graphite nanoparticles (GNPs), singlewalled carbon nanotube (SWCNT), MWCNT, and carboxylic group-functionalized MWCNT (f-MWCNT) to find the contribution of the π−π and oxygen functional group influences on the ET feature of the hemin. In addition, owing to its biological relevance, 4−8 dissolved oxygen and hydrogen peroxide reduction reactions mediated by the surface-confined hemin in a physiological system have been studied as model systems.

CV Study of GCE/Au nano −Carbon@Hemin−Chit.
Initial experiments were carried out using GMC as a standard system. At first, the hemin complex is adsorbed on a bare GCE surface and subjected to CV study in N 2 -purged pH 7 PBS. As can be seen in Figure 1A, curve a, a featureless voltammetric response was noticed. This observation is the same when the hemin is modified on GCE/GMC as GCE/GMC@hemin ( Figure 1A, curve b) (Scheme 1A−C). Note that, even after providing a graphitic environment by GMC, which can support π−π interaction, there is no specific redox signal for hemin. This is the reason why, in previous reports, hemin surfaceconfined graphene and GO/gold nanoparticle systems failed to show any marked characteristic redox peak at an apparent electrode potential of E o ′ = −0.320 V versus Ag/AgCl in neutral pH solution, 32,33 affirming that graphitic interaction alone could not be a prime factor for the ET reaction. Interestingly, when a dilute solution of Chit polymer which contains an amino functional group is coated on GCE/GMC@ hemin, as GCE/GMC@hemin−Chit, a well-defined redox peak at E o ′ = −380 ± 5 mV versus Ag/AgCl with a surface coverage (Γ hemin ) = 62 × 10 −10 mol cm −2 appeared because of the ET of the surface-confined hemin ( Figure 1A, curve c). Meanwhile, a 1% Nafion (Nf) polymer, a characteristic cationic exchange polymer without any amino functional group, is casted on GCE/GMC@hemin, as GCE/GMC@hemin−Nf, and tested (Supporting Information Figure S1). In addition, hemin adsorbed on the Chit-modified electrode, that is, GCE/ Chit@hemin, was also tested (data not included). There is no formation of the redox peak in the previous cases. These observations highlight the important role of the amino functional group along with the graphitic environment for the redox tuning of the hemin. In the literature, the amino group in Chit has been referred to as a good coordinating site. Our group utilized Chit for the complexation with the iron site buried in the pristine MWCNT. 26 Similarly, Chit−iron(III)modified smectites, 34 a [Fe(CN) 5 (NH 3 )] 3− complex-incorporated Chit hybrid film, 35 and an Fe(III)−Chit complex 36 have been reported in the literature utilizing complexation of the amino functional group with the iron site. In this work, it is expected that the amino functional group of Chit is bounded on the sixth vacant position of the hemin (axial bond) and helped the ET process.
With an aim to improve the performance and literature reports based on molecular wiring systems, 16,29,30,37−39 Au nano particles were chosen as a wiring agent and incorporated in the optimal electrode as a GCE/Au nano −GMC@hemin−Chit configuration. The preparation procedure was optimized as casting a dilute solution of Au 3+ ion on the GCE as the first step followed by other modification procedures. During the electrochemical potential cycling experiment, the Au 3+ ion was in situ reduced as Au nano particles and molecularly wired in the matrix (Scheme 1H,I). 31 Figure 1A (curve d) shows a typical CV response of GCE/Au nano −GMC@hemin−Chit, showing the redox peak at E o ′ = −320 ± 2 mV versus Ag/ AgCl with a 2-fold enhancement in the Γ hemin value (120 × 10 −10 mol cm −2 ). Further, E o ′ noticed here is about 70 mV positive than the value obtained without the Au nano particlemodified electrode (−390 mV), supporting the molecular wiring within the matrix. The E o ′ value (−320 mV) is matching with previous reports on hemin-modified electrodes, for example, hemin-MWCNT (E o ′ = −0.34 V vs Ag/AgCl), 16 Au nano −GO−hemin (E o ′ = −0.4 V vs Ag/AgCl), 19 and heminself-assembled gold monolayers via histidine and guanine quadruplex (G4) complexes (E o ′ = −0.22 to −0.3 V vs Ag/ AgCl). 20,21 The calculated peak-to-peak separation value (ΔE p ) is 40 mV at v = 10 mV s −1 , indicating a fast ET process. It is noteworthy that the Γ hemin value noticed in this work is the highest compared to the previous literature reports on the hemin-surface-confined system such as PGE@hemin (11 × 10 −10 mol cm −2 ), 15 MWCNT@hemin (27 × 10 −10 mol cm −2 ), 16 and N-doped GO@hemin (13 × 10 −10 mol cm −2 ). 39 In continuation, Nf polymer-coated GCE/Au nano −GMC@ hemin (GCE/Au nano −GMC@hemin−Nf) was also examined for the redox activity (data not enclosed) (Scheme 1D). However, nil redox response was noticed, confirming the specificity of Chit for the axial coordination ET process. On the basis of the results, it has been proposed that π−π interaction, axial coordination, hydrogen bonding (oxygen and hydrogen functional groups between hemin, GMC, and Chit), and internal linking (wiring) factors have been collectively involved in the effective ET process in this work.
From the CV study of the effect of scan rate (v), it is confirmed that ET of GCE/Au nano −GMC@hemin−Chit is surface-confined in nature (anodic and cathodic peak currents i pa and i pc vs v are linear starting from the origin) (Figure 2A,B). The ratio of the cathodic and anodic peak currents, i pc /i pa , is found to be nearly unity, obeying the reversible nature of the ET process. The heterogeneous rate constant k s was calculated from the Laviron's model at condition ΔE p < 200 mV using the equation k s = mnFv/RT, where m is a dimensional-less parameter relating to ΔE p and transfer coefficient value (α), n is the number of ET (n = 1), v is the scan rate, and other symbols have their own significance. 40 Priorly, the values E pc − E f /E pa − E f = 1 and ΔE p = 99 mV at v = 100 mV s −1 ( Figure  2C) were applied in the Laviron's working plots, 40 Figure 2D). The plot of E pa versus pH is linear with a slope of −36 mV pH −1 , indicating the non-Nernstian behavior (expected slope = −58 mV pH −1 ). 26 Previously, a similar kind of observation was made with several Hb-modified electrodes: Hb-polymer-grafted MWCNT (−42 mV pH −1 ) 44 and Hb−CNT−HA (−38 mV pH −1 ) systems. 45 Partial protonation of ligands is the likely reason for this observation. 46 At this stage, it is difficult to predict the exact molecular orientation of the hemin in this new system. Further, because the modified electrode is complex in nature and the concentration of the immobilized species is at the nanogram level, it is not convenient to use conventional characterization techniques such as nuclear magnetic resonance and mass spectroscopy to identify the active site. On the other hand, from the control experiments and physicochemical characterization studies, the possible structure and orientation of the surface-confined hemin system can be predicted.
The concept of immobilizing hemin is extended to other carbon nanomaterials as well. Figure 1B  Possibly, there may be electrostatic repulsions between the oxygen functional groups (hemin-COOH, pK a ≈ 3.8) 22 and hence avoid the communication. Indeed, a fraction of the carbon's oxygen functional groups helped for the hydrogen bond formation. (iv) The MWCNT structure is better than the single-walled structure, which may be due to the highly porous nature. (v) The graphitic structure along with the porous site provided by the GMC is the best option for the stable entrapment of the hemin system. Overall, it is obvious that tuning of π−π interaction, hydrophobic interaction, hydrogen bonding, and axial ligand coordination is necessary for the effective ET reaction. Partial or incomplete tuning of the interactions may result in either poor or nil ET process. 17,18,28,47−49 Because of the well-defined redox peak response, highest Γ hemin , and low material cost, GMC has been chosen as a model system in this work.
In order to find out the interaction of Au nano on the hemin functional group, control experiments were carried out with other forms of hemin derivative, hematin, modified electrodes, that is, GCE/Au nano −GMC@hematin−Chit and GCE/GMC@ hematin−Chit (without Au nano ). The hematin electrodes were prepared similar to GCE/Au nano −GMC@hemin−Chit and tested. Figure 3 (curves a and b) shows the typical CV responses of GCE/Au nano −GMC@hematin−Chit (curve b) and GCE/GMC@hematin−Chit (curve a) in N 2 -purged pH 7 PBS at v = 50 mV s −1 . Unlike the hemin case with a 50% increment in the Γ hemin value ( Figure 1A, curve c), there is no significant effect of Au nano on the redox feature of the hematin (Figure 3, curves a and b). Both Au nano -modified and unmodified hematin electrodes showed almost similar redox peaks signals (Figure 3). Note that, both hemin and hematin have the same molecular structure and varies only in the fifth axial ligands, where in, chloride (Cl) with hemin and hydroxide (OH) with hematin (Scheme 1). From these results, it can be revealed that Au nano has a positive interaction with the chloride ligand of hemin (likely chemisorption) as {Fe−Cl···Au nano } (molecular wiring) in turn for the enhanced communication.
2.2. Physicochemical Characterizations. Transmission electron microscopy (TEM) images of Au nano −GMC@hemin− Chit and GMC@Chit systems are shown in Figure 4. There is no marked change in the structural feature, except for black shades on the graphitic structure and fine dots of ∼20−40 nm in size with Au nano −GMC@hemin−Chit. These preliminary observations may support π−π interaction between the hemin and the graphitic structure of GMC and the presence of some nanoparticles in the matrix. Extended experiment with TEM− energy-dispersive X-ray spectrometry (EDXS) showed signals corresponding to Cu (because of the copper grid), Au, and Fe atoms (Supporting Information Figure S2). This observation confirms the existence of hemin-Fe and Au systems on the modified electrode. Supporting Information Figure S3 shows comparative Raman spectroscopic responses of Au/GMC@ hemin−Chit and unmodified GMC displaying specific D and G bands corresponding to the graphitic (hexagonal sp 2 carbons) and disordered structure (sp 3 carbons), respectively. 46 The calculated intensity ratio between D and G bands, I D /I G , for Au/GMC@hemin−Chit (0.214) is less than that for the unmodified GMC (0.2707). These data indicate an improvement in the graphitic structure of GMC by the hemin surface confinement through π−π interaction. Although the porphyrin rings have π bonds, because of the improper orientation, they may not be completely aligned on the six-membered π structure of the GMC-graphitic units. On the other hand, the alkene tail in hemin is expected to have positive π−π interaction with the graphitic structure (Scheme 1). UV−vis spectroscopic characterization was also used for the structural identification in this work. For that, respective GCE-modified electrode was sonicated with 500 μL of PBS and filtered with a microsyringe. Figure 5A shows a typical UV−vis response of  Au nano −GMC@hemin−Chit, hemin, and Au 3+ solution (precursor). Specific absorption signals at λ max ∼405 and 534 nm were noticed. Compared with the control hemin and Au 3+ solution and the data from the literature related to hemin−GO hybrid (λ max = 413 nm) 28 and Au nano (λ max = 520−535 nm; 20− 70 nm-sized particles), 50 the UV−vis signals can be identified as hemin (hybrid) and Au nano particles, respectively. Figure    2116, 1736, and 1134 cm −1 ), hemin (2994, 1705, 1200−1390, 928, and 708 cm −1 ), and Chit (3315 and 1639 cm −1 ). 31,52,53 The information supports the existence of various functional group interactions such as π−π, hydrophilic, and hydrogen bonding within the new chemically modified electrode.
2.3. Bio-Electrocatalytic Reduction of Dissolved Oxygen and Hydrogen Peroxide. Figure 6A shows the CV response of GCE/Au nano −GMC@hemin−Chit with (10 ppm) and without oxygen gas saturation in pH 7 PBS at v = 10 mV s −1 . A N 2 gas-purged pH 7 PBS was used as an electrolyte. A well-defined oxygen reduction signal at an onset potential, 0.25 V versus Ag/AgCl with peak current maximums at 0 and −0.38 V versus Ag/AgCl, where the hemin redox peak exists, was noticed. A control experiment with a hemin unmodified electrode, GCE/Au nano −GMC−Chit showed a reduction signal about 300 mV higher negative potential and about twice lesser in the peak current value than that of the optimal electrode. This observation denotes the hemin redox-mediated reduction of the dissolved oxygen. A pre-reduction peak at about 0 V versus Ag/AgCl noticed with the optimal working electrode is due to immobilization of the hemin at energetically different surfaces such as pores and valleys/asperities of the GMC and its interaction with analytes. 43 Presumably, hemin trapped at the pores of the GMC, which provide significant π−π and hydrogen bonding, is responsible for the low-potential peak observation in this work. Figure 6B shows the effect of dissolved oxygen concentration on the mediated oxygen reduction current signals. The dissolved oxygen concentration was measured discreetly by a DO meter (the inset of Figure  6B). A systematic increment in the peak current against the increase in the dissolved oxygen concentration was noticed. The plot of peak current versus dissolved oxygen concentration was linear in a range of 0−8 ppm with a current sensitivity value of 0.794 μA ppm −1 ( Figure 6C). This result highlights the potential use of the new system for dissolved oxygen sensor development.
In addition, electrocatalytic reduction of hydrogen peroxide was also demonstrated with this new hemin-modified electrode system, as in Figure 6D. The H 2 O 2 reduction signal was noticed at an onset potential of −0.38 V versus Ag/AgCl with peak maximums at −0.05 and −0.4 V, similar to the case of the oxygen reduction reaction, due to the mediated reduction by the surface-confined hemin sites. The plot of the reduction peak current signal i ( ) μM H 2 O 2 at an applied potential of 0 V was analyzed (Supporting Information Figure S4C). There is no significant alteration in the reduction current signals upon spiking the aforementioned interfering biochemicals. This observation indicates the selective H 2 O 2 electrochemical interaction and reduction similar to the heme-based protein/enzymatic systems. GCE/Au nano −GMC@hemin−Chit is found to be stable at room temperature for 30 days and beyond (Supporting Information Figure S5), unlike the enzymatic systems, which have poor stability.

CONCLUSIONS
Highly redox active hemin-complex surface-confined carbon nanomaterial/Chit/Au nano chemically modified electrodes have been prepared by a simple drop-casting technique within 18 ± 2 min. Cyclic voltammetric investigation of the modified electrode showed a well-defined redox peak at E o ′ = −320 ± 2 mV versus Ag/AgCl with peak-to-peak separation and surface excess values of 40 mV (10 mV s −1 ) and 120 × 10 −10 mol cm −2 , respectively, in N 2 gas-purged pH 7 PBS because of the facile ET behavior of the iron site in the hemin. Control experiments with the absence of Chit and graphitic carbon nanomaterial resulted in nil redox peak response. The new hemin-modified electrode was subjected to several physicochemical characterization studies using TEM, EDXS, Raman spectroscopy, UV− vis, and FTIR. The collective results revealed that the axial coordination bonding of amino functional groups of the Chit with sixth vacant site of the hemin is a key step for the ET process of the hemin-surface-confined carbon nanomaterial systems. Incorporating gold nanoparticles in the matrix improved the ET function through molecular wirings. As an electrochemical application, electrocatalytic reductions of dissolved oxygen and hydrogen peroxide in N 2 -purged pH 7 PBS have been demonstrated. The new modified electrode showed about 300 mV reduction in the overpotential and two times increment in the reduction peak current signals over the respective unmodified electrode, GCE/Au nano −GMC−Chit. Extension of the new system toward sensor applications of dissolved oxygen and H 2 O 2 without interference from common biochemicals was also demonstrated. Unlike the enzymatic systems, the hemin surface-confined carbon nanomaterial system showed redox stability over 30 days at room temperature.

Apparatus.
Electrochemical experiments were carried out using a portable Biologic (USA) instrument with a threeelectrode system comprising hemin chemically modified GCE (GCE/GMC@hemin−Chit) as a working electrode (0.0707 cm 2 ), platinum as a counter electrode, and Ag/AgCl with 3M KCl as a reference electrode with a 10 mL working volume of N 2 -purged pH 7 PBS. Raman spectroscopy analyses were carried out using AZILTRON, PRO 532, (USA) with a 532 nm laser excitation source. UV−vis analysis was done by using a UV−vis NIR spectrophotometer, JASCO V-670, Japan. FTIR analysis was done with a JASCO 4100 spectrophotometer by KBr method. A portable dissolved oxygen meter (HI9142) from Hanna Instruments, USA, was used to measure the dissolved oxygen concentration.
4.3. Fabrication of a Hemin Chemically Modified Electrode. First, the GCE (3 mm in diameter) was subjected to a series of chemical, mechanical, and electrochemical cleaning procedures, as reported in the literature. 26 For the preparation of GCE/Au nano −GMC@hemin−Chit, the clean surface of GCE was first casted with Au 3+ solution (5μL; 1000 ppm), followed by drying at room temperature for 2 ± 1 min. Then, 5 μL of GMC or other carbon nanomaterial−ethanol suspension (2 mg mL −1 ) was casted and air-dried (2 ± 1 min). Following this, 5 μL of hemin−NaOH (0.1 M) solution (2 mg mL −1 ) was dropped on the surface of the above modified electrode (GCE/Au nano −GMC) and left to dry in an incubator (40 ± 2°C) for 5 ± 1 min. As a last step, 5 μL of 0.5% Chit− acetic acid solution was overlayer-coated and air-dried for 2 ± 1 min. In total, within 18 ± 2 min, the modified electrode can be prepared. The modified electrode was potential-cycled in pH 7 PBS at a window −0.8 to 0.4 V versus Ag/AgCl for 20 scans at v = 50 mV s −1 (Scheme 1). During this process, the Au 3+ ions were in situ reduced as Au nanoparticles and stabilized by the amino functional group of Chit in the modified electrodes (Scheme 1H,I). 31 For Raman spectroscopic characterization, SPCE-coated GMC and Au nano −GMC@hemin−Chit were used. UV−vis spectroscopy measurements were carried out by stripping out the hemin site from the GCE-modified electrode by sonicating the electrode with 500 μL of pH 7 PBS followed by microfiltration. To perform a typical FTIR characterization, respective GCE-modified electrodes were peeled off with a doctor's syringe needle (1 mm × 4 cm), mixed with KBr as a pellet, and subjected to the analysis. Electrocatalytic reduction of dissolved oxygen and H 2 O 2 was carried out by exposing GCE/Au nano −GMC@hemin−Chit to saturated DO (10 ppm, measured by a standard DO meter) taken in N 2 -purged pH 7 PBS and 500 μM H 2 O 2 .