{'fraction_non_alphanumeric': 0.027386541471048513, 'fraction_numerical': 0.015736393670665972, 'mean_word_length': 4.832910750507099, 'pattern_counts': {'":': 0, '<': 1, '<?xml version=': 0, '>': 0, 'https://': 0, 'lorem ipsum': 0, 'www.': 0, 'xml': 0}, 'pii_count': 0, 'substrings_counts': 0, 'word_list_counts': {'cursed_substrings.json': 0, 'profanity_word_list.json': 0, 'sexual_word_list.json': 0, 'zh_pornsignals.json': 0}}
Capacitive properties of zinc oxide thin films by radiofrequency magnetron sputtering

The study focused on the production of zinc oxide (ZnO) thin films as a dielectric material for use in metal–insulator–semiconductor capacitors. The objective of this study has demonstrated the frequency dependence of conductivity and capacity. Zinc oxide (ZnO) was thin films deposited by a silicon wavelength sputtering\magnetron cathode sputtering. The capacitive properties of ZnO zinc oxide were studied at room temperature. The frequency dependence of the conductivity, capacitance and the measured current–voltage (I–V) characteristics of ZnO zinc oxide thin films were studied in the frequency range from 5 kHz to 13 MHz. It is shown that the conductivity is total. Indeed, the measurement of the conductivity in alternating regime obeys the Arrhenius equation. In addition, the measured I–V characteristics of the structures studied at 10 kHz and 10 MHz clearly revealed areas of accumulation, depletion and inversion in the plots. It has been observed that AC conductivity and capacity in the ZnO thin films (ZnO) are frequency dependent. This dependence indicates that the conduction is thermally activated and maintains the correlated barrier of the charge carrier on the localized states as a function of the experimental data. The FBAR (expand) devices with the ZnO films exhibited a pronounced resonance peak centered at 537 MHz with a k2 coupling coefficient of 7%. It found therefore that the impedance matching of the FBAR could be easily achieved simply by controlling the resonance the resonator.


Introduction
Currently, zinc oxide as a dielectric material is the subject of particular attention in the development of micro-and nanotechnologies. Indeed, the determination of its electrical properties in metal-insulator-semiconductor (MIS) capacitors as a dielectric material is much studied [1,2]. Indeed, AC conductivity measurements provide information about the interior of the insulation or semiconductor which is a region of relatively low conductivity, even when the conduction process is limited to the electrode [3,4]. The identification of the conduction mechanism depends on both frequency and temperature dependence of electrical conductivity, and Mahmood et al. [5] studied the electrical properties of ZnO thin films by RF sputtering. It has been found that the electrical conductivity has been thermally activated and dominated by the correlated barrier at low temperature [6].
Indeed, ZnO has the potential for many applications such as gas sensors. [7][8][9]. This material is also interesting because of its simple and economical photocatalytic activity. Wide-band-gap semiconductor, ZnO exhibits interesting optoelectronic properties and spintronic applications [10,11] because of its direct band-gap and large exciton binding energy (60 meV at room temperature) that can be used for UV-blue lasers and diodes [10,12]. UV and visible band emission provides useful information about the electronic properties of ZnO. The UV emissions are usually attributed to the free excitons and donor bound excitons, whereas deep level emissions usually arise from intrinsic defects in ZnO. The zinc oxide usually shows n-type conductivity because of intrinsic defects such as oxygen vacancies and zinc interstitials. Through these mechanisms, ZnO acts as an excellent antibacterial agent [13]. ZnO materials have been synthesized through numerous methods, which include chemical precipitation, sol-gel, pulsed laser deposition technique, microwave radiation and hydrothermal methods [14]. The doping of ZnO materials with different types of metallic ions [11,15,16] enhances its optical, magnetic and conducting properties. This modified ZnO is used as a base material in photocatalysts, dosimeters and biological systems [12]. Furthermore, doping with rare earth elements provides many interesting ZnO properties, including lanthanum-doped ZnO with excellent gas sensitivity and photocatalytic activity [17]. Functional dual TMs doping into ZnO nanostructures could influence the charge carrier recombination rate, optical, structural and interfacial electron-transport rate performance [15].
Also, the determination of the electrical properties of ZnO as a dielectric material in metal-insulator-semiconductor capacitors is more than necessary in the development of nanotechnology devices.
In the literature, the authors have shown that certain properties are determined by the orientation of the crystallites on the substrate. That is, the FWHM width of the ZnO peak along the orientation (002) of the X-ray inclination curve should be less than 0.58 to achieve an effective electromechanical coupling [18,19]. Other studies have shown the frequency dependence of the electrical properties of ZnO sandwich structures [20]. The σ AC test based on the electrical properties of the ZnO thin films showed that in the frequency range of 10 kHz to 10 MHz, electrical conduction is performed by tunneling between the quantum wells. The resistivity of the dielectric material being high, the electrical conductivity of the material can only be achieved by transporting the blasting charge between the particles. In this work, the characteristics of metal-insulator-semiconductor (MIS) capacitors with zinc oxide (ZnO) as a dielectric material were studied. ZnO thin film was analyzed by X-ray diffraction, and the electromechanical coupling coefficient k 2 was measured with network analyzer.

Experimental
The RF magnetron sputtering was used to deposit the thin films of ZnO. Indeed, a target of zinc (99.99%) with a diameter of 51 mm and 6 mm of thickness allowed us to make these deposits. The silicon substrate used is of the p-type with orientation (100). The deposits were carefully cleaned with organic products. The magnetron sputtering is carried out at a gas/argon mixture atmosphere. A power at frequency of 13.56 MHz is supplied to the system. The RF power was about 50 W. The flow rates of argon and oxygen were monitored using a flowmeter (ASM, AF 2600). The spraying pressure was maintained at 3.35 × 10 −3 Torr controlled by a Pirani gauge. Deposition rates covered the range of 0.35-0.53 μm/h. All films were annealed in an atmosphere of helium at 650 °C for 15 min. Indeed, we found that the titanium layer in a Pt/Ti/Si structure annealed at 650 °C for 15 min under an oxygen flow was completely oxidized, while under helium and under the same conditions, the structure exhibited unoxidized titanium layer.
We have previously deposited Ti/Pt as thin inking films on the silicon substrate to facilitate adhesion of the ZnO films. It has been found that a substrate temperature of 100 °C, target/substrate distance of about 70 mm, very low gas pressures of 3.35 × 10 −3 Torr in a mixed argon gas atmosphere and for an oxygen content of 20%, giving to ZnO thin films a good homogeneity and high crystallinity. The thickness measurements of the samples were taken using a DEKTAK_ST high-resolution profilometer. We measured 2.8-3 μm ZnO thin films on samples. We confirmed these thicknesses by the determination of the optical properties. Indeed, the optical properties are a function of the thickness. To do this, we consider that the two envelopes of the measured optical transmittance form a nonlinear system consisting of continuous functions that can be solved by iteration. These continuous functions are the refractive index and the absorption percentage. After deposition of the zinc oxide, silver dot electrodes were evaporated on the Pt/ZnO/Ti/Pt/Si sample using an electron gun evaporation system to render the structure metal-insulator-semiconductor useful for electrical measurements. These were carried out in a vacuum chamber evacuated at about 10 −3 Torr. Measurements of frequency and temperature dependencies of conductivity and capacity were taken using a laboratory configuration for the AC-based electrical test properties. The samples obtained were tested using an alternating current in the frequency range from 5 Hz to 13 MHz (using a capacitance bridge technique) using measurement temperatures of Tp = 30-300 °C, with a Hewlett-Packard LF 4192 A impedance analyzer between silver points and Pt electrode bottom. The temperature was measured with a Doric thermometer (Trendicator 400 K/ °C). To appreciate the nature of our piezoelectric ZnO layers, we determined the coupling coefficient of the complete structure based on frequencies for which the conductance is maximum and the minimum susceptance using a network analyzer (HP 8752 A Network Analyzer) whose pass-band ranges from 300 kHz to 1.3 GHz. This type of device is one of the instruments to define with precision the characteristics of an electric circuit (impedance measurement, electrical admittance, reflection coefficient, etc.).

Conductivity measurements
A different mechanism has been proposed to explain the conductivity σ(ω) in chalcogenide glasses [21][22][23], scandium oxide and glasses [22], zinc oxide [24], ceramic [25] and cobalt ferrite [26]. This mechanism is based on the classic jump of charge carriers between the states located above a potential barrier. This process usually involves phonons, due to the height of the barrier. Consider W M as the energy difference between the ground state of the potential and the ionized (extended) state distant from R. Then, W the potential barrier height of the coulombian type is given by the relationship [22]: where e is the effective dielectric constant.
In the following, only the cases where the jumps between very close sites are the most important were considered. Assuming random spatial distribution of the sites, Pike obtained the expression: with where s is temperature and frequency dependent. Long [27] has discussed the case where an appreciable overlap of the polaron hopping distortion could occur (OLPT), thereby reducing the value of the polaron hopping energy.
According to Elliott, we can show that Eq. (2) can be rewritten as [28]: where τ is minimum relaxation time.
This equation accounts for the variation of σ(ω) with the temperature T, then: The absolute value of this slope decreases as the temperature decreases. This slope also depends on the frequency. For a given temperature, this slope increases when ω decreases.
If we take as a function of temperature, we obtain a straight line that passes through the origin. From this slope, we deduce W M . The value found for W M is to be compared with the activation energies necessary for the hopping of polaron. Holstein showed that at high temperature, the hopping of a small polaron is essentially a transition over the barrier [25], so the Pike model can be applied to the polaron hopping.
The frequency dependence of the conductivity, for the sample grown at 100 °C and for different temperatures, is shown in Fig. 1. The frequency dependence of the capacitance is shown in Fig. 2.
The linear scale was chosen for their presentation in order to determine the mean values of the relaxation times of the permittivity and of the conductivity. Its shown that at the angular frequency: and the dielectric permittivity value decreases twice while the conductivity double its value at higher frequencies. This means that the analysis of the changes in the frequency dependencies is shown in Figs. 1 and 2 which makes it easy  In order to identify the conduction mechanism in these thin films, the frequency exponent s is plotted as a function of temperature and deposition frequency a decrease in s with an increasing frequency as shown in Fig. 3. On the basis of the discussion, the variation of s with the frequency is compatible with the overlap polaron tunnel model (OLPT) for a long polaron ray model developed by Long [27]. The variation of the exponent s with the temperature is illustrated in Fig. 4 for different frequency values. It is observed that s decreases at the temperature of 150 °C, and beyond this temperature, s increases. In addition, the value of s was higher when measured at a lower frequency. The low-temperature results were consistent with calculations based on a model proposed by Holstein (2918) to explain the AC conductivity of amorphous materials. Indeed, it showed that at high temperature, the jump of a small polaron is essentially a transition on the barrier [28,29], so that the Pike model can be applied to the polaron jump. It would therefore seem that the decrease in s with frequency, especially at lower temperatures, is related to a gradual transition between different jump regimes. Therefore, the correlated barrier (CBH) and large polaron ray overlap (OLP) models are suitable for interpreting ZnO data deposited at 100 °C.
To determine activation energy values, Arrhenius plots were plotted for capacity (Fig. 5) and conductivity (Fig. 6) for measuring frequencies of 10 kHz and 10 MHz. The activation energy values determined in relation to these plots in the case of capacity are ΔE C1 ≈ 1.82 meV for the frequency of 10 kHz and ΔE C2 ≈ 0.43 meV for the frequency of 10 MHz. In the case of conductivity for the frequency of 10 kHz, the activation value of the energy is ΔE σ1 ≈ 24.4 meV, while for the frequency of 10 MHz, the value is ΔE σ2 ≈ 2.27 meV.
The electrical conduction of thin films ZnO MIS transistors allowed us to measure the capacitance and the dielectric constant using the following formula:  where C p is the capacitance, ε r is the relative dielectric constant, ε 0 is the dielectric constant of void, A is the active area of the capacitor and d is the thickness of a dielectric layer. The dissipation factor is given by the formula: where tan ϕ is the dissipation factor, σ is the conductivity and ω is the pulsation. This gave an average of 8.5 for the value of the permittivity and a very low dissipation factor of 10 −4 for the sample deposited at 100 °C compared to the samples deposited below and above 100 °C, where the permittivity values are smaller. Similarly, for the dissipation factor, we observe an increase in their values. These capacity data confirm that the ZnO/Si interface does not form a Schottky barrier and that the measurements of the capacity dependence on the film thickness indicate that the relative permittivity of the films is about 8.5. The higher temperature results can be explained by assuming an electron concentration at room temperature and a space-limited conductivity dominated by traps exponentially distributed with energy E under the edge of the web of conduction according to the relation where k B is Boltzmann constant [5]. It results that at low frequency, the electrical capacity of a material containing a potential well is not dependent on the frequency. When the angular frequency ω approaches 1/τ, the value of the electrical capacitance begins to decrease and tends toward a characteristic value of a material which does not contain any potential wells. The relaxation time in this case gives us relation which is exponentially dependent on the temperature [30,31]: where τ 0 is numerical coefficient and ∆E is an activation energy of the relaxation time. The relaxation time is a function of the distance a jumping electron must cover [32]. The distances between the individual particles are also random values from which a random distribution of the relaxation times values occur the thin films of ZnO. The comparative analysis of the dielectric permittivity and conductivity of the direct current indicates that the activation energy of the conductivity is higher than the activation energy of the permittivity. Indeed, we obtain ΔE ε = 3.23 meV (Fig. 5) for the activation energy of the dielectric permittivity and ΔE σ = 91.4 meV (Fig. 6) for the activation energy of the low-frequency conductivity.
The measured C-V characteristics of the studied Pt/ZnO/ Ti/Pt/Si structures are typical for a MIS structure. Figure 7 illustrates this assertion, where the C-V characteristics of the MIS structure with a ZnO thin films deposited at 100 °C at different frequencies and temperatures. The characteristics measured at 10 kHz and 10 MHz clearly revealed the accumulation, depletion and inversion regions in the C-V plots of Fig. 7. The 10 MHz C-V plot measured at room temperature was shifted toward more positive voltages compared with the ideal C-V one. This shift has shown that there is fixed dielectric charge built-up in the ZnO thin films with a density of the order of 10 17 cm −2 , which has a weak tendency to increase with increasing temperature. The related defects were negatively charged, while the fixed oxide charge is always positive in a ZnO-Si MIS structure. One may notice that with decreasing the measurement frequency, the capacitance values become larger in accumulation, depletion and inversion regions as presented in Fig. 7a. The 10 kHz C-V characteristics showed a capacitance maximum in the depletion region, while toward the accumulation region capacitance increased little. The increase by almost one order of magnitude compared with the corresponding capacitance measured at 10 MHz in the depletion region is evidence for the presence of traps at the ZnO-Si interface and of deep levels in Si. The capacitance increase in the accumulation region signals the presence of deep levels in the bulk of ZnO thin films, which capture and emit charge carriers during the voltage sweeps. As illustrated in Fig. 7b, the 10 MHz C-V characteristics measured at 30 °C were shifted toward negative voltages relative to those measured at room temperature. This is an indication of the presence of positively charged traps at the ZnO-Si interface, which contributes to the capacitance values moving the Fermi level toward the Si valence band edge during the temperature decrease from 300 to 30 °C. Therefore, the ZnO-Si interface traps below the middle of the Si energy gap are donor like.
The electrical impedance at the input of the computed from the matrix (13) is [33,34] structure: where Z p , Z 1 , Z 2, respectively, represent the acoustic impedances of the piezoelectric material, settings on the front and rear of the piezoelectric material. k 2 represents the electromechanical coupling coefficient C p is the capacitance of the piezoelectric material and φ is the constant.
To facilitate the study, first look at all the case of a free resonator. The model was developed to account for various losses related to the piezoelectric material [34,35]. We consider, for this, a thin piezoelectric layer, the two sides are metalized, and the electrical impedance is written in this case: Around the resonance, this resonator can be represented by the following equivalent electric circuit. C 0 is dielectric capacitance of the ZnO, L 1 represents the inertia of the (13) circuit structure and the friction losses are R and C 1 is stiffness of the system. The circuit in Fig. 8 is an ideal model to represent the physical characteristics of a free resonator. Indeed, when ω → 0, the parallel resonance frequency (frequency at which the maximum resistance is R) and series (frequency for which the conductance G is a maximum) of the circuit may be written as follows: The IEEE standard [23] shows that the coupling coefficient k 2 is given by The formula can be written in a more explicit form and approximate the error introduced by the approximation which is then less than 1% in the case where k 2 < 0.2, namely: This means that one can calculate the coupling coefficient k 2 by simply raising the maximum of the real parts of the impedance and admittance, i.e., raise the maximum values of the impedance and admittance at the resonant frequency when the imaginary parts are zero. Using the relation (16), we plotted the theoretical evolution of the real and imaginary parts of the electric admittance of the resonator free, thick 5.7 μm, depending on the frequency. Since the modeling was done for the propagation of longitudinal waves of volume, we find a good coupling coefficient k 2 = 7.8%, k = 0.28 for a pure longitudinal mode [33]. Figure 9 shows the variation of the real and imaginary parts of the electric admittance versus frequency. We observe a change in the electrical input admittance of the resonator and the appearance of the produced oscillations superimposed on the general envelope. These oscillations are due to the propagation medium. They reflect changes in real and imaginary parts of the electrical admittance measured. This means that the system reacts to the electrical load with a lag effect. Indeed, the shape of the curves shows that there is interference of waves propagating in the propagation medium which is the silicon substrate.
In support of our study, we also measured changes in the reflection coefficient as a function of frequency on a Smith We observe the presence of the ZnO piezoelectric activity in Fig. 10.
To determine the coupling coefficient of our structure, we placed the fundamental resonance of the resonator, i.e., at frequencies where the real part of the admittance maximum and the minimum susceptance. We performed a piezoelectric resonator using the zinc oxide layer having a resonant frequency of the fundamental mode. The layer of zinc oxide and the delay line are, respectively, 3.8 μm and 380 μm thick. Figure 11 shows the evolution of the effective coupling coefficient k 2 eff versus frequency.

Conclusion
It has been observed that AC conductivity in ZnO films follows a σ(ω) ∝ ω s dependence where s ≤ 1 such behavior appears to indicate that hopping is the predominant conduction process. At low temperature and at high frequencies, observed values of s approach those predicted by the literature that explains the behavior of AC conductivity of amorphous materials. The temperature and frequency dependences of the capacity and conductivity have been tested for a ZnO thin films prepared at a substrate temperature of 100 °C. Frequency dependencies of capacity and conductivity indicate an appreciable overlap of the polaron hopping distortion which could occur (OLPT), thereby reducing the value of the polaron hopping energy. The measured current-voltage characteristics of the Pt/ZnO/Ti/Pt/Si structures studied at 10 kHz and 10 MHz clearly revealed regions of accumulation, depletion and inversion in the plots. This offset showed that there was a fixed dielectric charge in the ZnO thin films with a density of the order of 10 17 cm −2 , hence a low tendency to increase with increasing temperature. The FBAR devices with the ZnO films exhibited a pronounced resonance peak centered at 537 MHz with a k 2 coupling coefficient of 7%.
Open Access This article is distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creat iveco mmons .org/licen ses/by/4.0/), which permits unrestricted use, distribution, and reproduction in any medium, provided you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made.