{'fraction_non_alphanumeric': 0.032098149006740614, 'fraction_numerical': 0.019080566354006918, 'mean_word_length': 4.8957106812447435, 'pattern_counts': {'":': 0, '<': 0, '<?xml version=': 0, '>': 0, 'https://': 0, 'lorem ipsum': 0, 'www.': 0, 'xml': 0}, 'pii_count': 0, 'substrings_counts': 0, 'word_list_counts': {'cursed_substrings.json': 0, 'profanity_word_list.json': 0, 'sexual_word_list.json': 0, 'zh_pornsignals.json': 0}}
Nanoporous gyroid platinum with high catalytic activity from block copolymer templates via electroless plating

Nanoporous platinum (Pt) with a gyroid nanostructure was fabricated using a nanoporous polymer with gyroid nanochannels as a template. The nanoporous polymer template was obtained from the self-assembly of the degradable block copolymer, polystyrene- b -poly( L -lactide) (PS-PLLA), followed by the hydrolysis of the PLLA blocks. Templated electroless plating can be conducted under ambient conditions to create a precisely controlled Pt gyroid nanostructure with high crystallinity in a PS matrix. After removal of the PS matrix, the well-interconnected nanoporous gyroid Pt can be successfully fabricated. Compared with commercially available catalysts, the nanoporous Pt possesses superior macroscopic stability and peak speci ﬁ c activity, bene ﬁ ting from the well-de ﬁ ned network structure with robust texture and the growth of the low-index crystalline facets of Pt.


INTRODUCTION
Platinum (Pt) materials with a well-defined nanostructure have attracted substantial scientific attention because of their fascinating properties for a variety of applications, including highly active catalysts, 1-3 actuators, 4,5 nanodevices, 6,7 electrodes 8-11 and sensors. [12][13][14] Pt is the most promising electrochemical catalyst to facilitate the reactions at the cathode (oxygen reduction reaction) and the anode (methanol oxidation reaction) of a direct methanol fuel cell. Most Pt catalysts consist of Pt nanoparticles supported by carbon, providing a high electrochemically active surface area (ECSA). The major problems for the practical applications of the carbon-supported Pt nanoparticles are carbon corrosion and aggregation, as well as the Ostwald ripening of the Pt nanoparticle during the electrochemical reaction of the fuel cell. 15 To alleviate the problem and prolong the durability performance, the fabrication of nanoporous Pt is required. Various nanoporous Pt materials composed of nanowire networks, [16][17][18][19] nanotubes, 20,21 nanodendrites [22][23][24] and hollowed nanocrystals [25][26][27] have been fabricated for this purpose. Among them, nanoporous Pt materials with three-dimensional (3D) textures are of significant interest because of the well-defined and well-interconnected networks that provide the required robustness to simultaneously prolong the durability lifetime and increase the residence time of the reactant molecules on the metal surface owing to the confinement effect 28 of the enhancement of the electrochemical reactions. Xia et al. 23 developed a novel method for the fabrication of nanoporous Pt using a truncated Pd seed to grow nanodendrites through epitaxial overgrowth of the Pt branches. Recently, Yang et al. 25 used presynthesized Pt-based 3D nanoparticles to create highly active 3D nanoframes under a spontaneous evolution process in oleylamine ligands. Another straightforward route for the fabrication of nanoporous Pt is to deposit the desired Pt-base materials into templates with defined nanochannels through templated syntheses using mesoporous silica (MCM materials) [29][30][31] or polycarbonate as templates. 32,33 Over recent decades, block copolymers (BCPs) have been extensively investigated because of their ability to self-assemble into one-, two-or 3D periodic nanostructures, according to their compositions and molecular weights. 34,35 Moreover, exploiting the degradable character of BCPs, nanoporous polymer materials can be fabricated by the removal of the components in BCPs through ozonolysis, 36 UV degradation 37 and reactive ion etching. 38 Additionally, polylactidecontaining BCPs (such as polystyrene-b-poly(D,L-lactide) and polystyrene-b-poly(L-lactide) (PS-PLLA)) are supremely suited for the fabrication of nanoporous polymer materials because of the unstable characteristic of the ester group, which can be easily decomposed in a basic aqueous solution. [39][40][41] Among all of the nanostructures resulting from BCP self-assembly, the gyroid is one of the most appealing morphologies for practical applications because of its unique nanostructure, comprising a matrix and two continuous but independent networks in 3D space. [42][43][44] After selective degeneration of one of the constituted blocks, the gyroid nanostructure can be exploited to fully create interconnected nanochannels. Because of the high porosity and large surface area, nanoporous polymer materials can be used as templates for templated synthesis. By exploiting the templating process (that is, nanoreactor concept), certain reactions, such as electroless plating, 45-47 electrochemical deposition [48][49][50] and the sol-gel process, 51,52 can be performed within the BCP templates for the manufacture of nanohybrids because of the freestanding characteristic of the gyroid networks. After removal of the template, nanoporous gyroid materials can be fabricated with a well-defined texture, which is promising for applications such as ceramic membranes, [53][54][55] hybrid solar cells, 45 membrane reactors 56,57 and low refractive index materials. 51,52 In this study, we propose a new approach for the fabrication of nanoporous Pt with a well-defined texture (that is, gyroid-forming nanostructure) using hydrolyzed PS-PLLA (that is, nanoporous PS) as a template for the electroless plating of Pt. A modified electroless plating of Pt is performed to fabricate well-ordered PS/Pt nanohybrids. After removal of the template, nanoporous gyroid Pt can be obtained. In contrast to electrochemical deposition, the process of electroless plating (that is, chemical deposition) does not require any electric current to pass through the solution to form a deposit because the electroless plating is performed and then followed by the nucleation and growth mechanism. Accordingly, no conductive substrates are required during the deposition process of the metallic materials. Additionally, the method is comprehensive because there are many available procedures for the deposition of various metals using electroless plating. However, it is possible to encounter a blocking problem for the growth of Pt from the templated electroless plate. In contrast to the templated synthesis using MCM materials as templates, the blocking problem can be alleviated in the synthesis of Pt using nanoporous PS as a template owing to its larger pore size. Therefore, with the dedicated control of the deposition process of Pt via the modified electroless plating, well-ordered nanoporous Pt can be successfully fabricated. Because of the high porosity and high specific surface area with an open-cell characteristic, the nanoporous gyroid Pt is an excellent catalyst to facilitate electrochemical reactions, especially for use in a direct methanol fuel cell. Compared with commercially available catalysts (PtB (Aldrich, fuel cell grade)) and Pt/C (20 wt % Pt on Vulcan XC-72, E-TEK), the nanoporous gyroid Pt possesses superior macroscopic stability and peak specific activity, benefiting from the well-defined network structure with robust texture and the growth of the low-index crystalline facets of Pt.

EXPERIMENTAL PROCEDURES
Synthesis of PS-PLLA The PS-PLLA was prepared by a sequential living polymerization using a double-headed initiator. Detailed synthetic routes of the PS-PLLA sample have been described in our previously published results. 58,59 The number-average molecular weight and the molecular weight distribution (that is, polydispersity index) of the PS were determined by gel permeation chromatography (GPC). The polydispersity index of PS-PLLA was determined by GPC and the numbers of L-LA repeating units versus styrene repeating units were determined by 1 H nuclear magnetic resonance analysis. The number-average molecular weights of the PS, the PLLA and the polydispersity index of the PS-PLLA are 34 000 g mol − 1 , 27 000 g mol − 1 and 1.21, respectively. The volume fraction of PLLA, f PLLA v , is calculated as 0.37 by assuming that the densities of PS and PLLA are 1.02 and 1.248 g cm − 3 , respectively.

Sample preparation
Bulk samples of PS-PLLA were prepared by solution casting from a dichloromethane (CH 2 Cl 2 ) solution (10 wt % of PS-PLLA with PLLA volume fraction, f PLLA v = 0.37) at room temperature for 2 weeks and then dried in a vacuum oven at 65°C for 3 days. The dry samples were heated to the maximum annealing temperature, T max = 175°C, for 3 min to eliminate the PLLA crystalline residues that were formed during the preparation procedure. After quenching from the microphase-separated ordered melt at 175°C, the samples were prepared for the small-angle X-ray scattering (SAXS) experiments.
Then, the PLLA blocks of the PS-PLLA bulk samples were removed by hydrolysis using a 0.5 M basic solution that was prepared by dissolving 2 g sodium hydroxide in a 40/60 (by volume) solution of methanol/ water. After 3 days of hydrolysis, the hydrolyzed samples were rinsed using a mixture of DI water and methanol and were then used as templates for the subsequent seed growth approach.

Nucleation and growth approach
The nanoporous PS templates with interconnected twisting air networks were soaked in a seeding aqueous solution mixed with methanol (12 ml) and H 2 PtCl 6 (0.01-0.02 g) with stirring at room temperature for several hours. After washing gently with a methanol/ H 2 O solution to remove redundant Pt ions covering the sample surfaces, the pore-filled samples were immersed into a hydrazinium hydroxide (85%, 4 ml) methanol solution for the nucleation of Pt. The diameter of the Pt nuclei is approximately 25-30 nm. By controlling the concentration of the Pt ions, the nucleation density of Pt can be well defined. With the control of sufficiently low Pt ion concentrations, a suitable amount of Pt nuclei within the nanochannels of the template can be formed. Subsequently, a fresh growth aqueous solution consisting of H 2 PtCl 6 (0.03 g), ascorbic acid (1 M, 1 ml) and methanol (12 ml) was prepared, and then the pre-treated templates with a low content of Pt nuclei were immersed into the prepared solution. Accordingly, the Pt ions were reduced to Pt clusters arising from the pre-formed Pt nuclei to gradually develop within the nanochannels through the growth process and eventually forming the PS/Pt nanohybrids with a preserved gyroid texture.

Degeneration for the PS template
To produce the nanostructured Pt materials, the PS template of the PS/Pt nanohybrids was degraded by exposure to UV. The degradation was performed under atmospheric conditions for 24 h using a UV source. The intensity of the UV source was tuned for the efficient degradation of the PS matrix with a wavelength of 254 nm and an intensity of 3 mW cm − 2 . Consequently, the nanostructured Pt materials were easily obtained.

Microscopy (FESEM)
FESEM observations were performed on a JEOL JSM-6700F (JEOL, Peabody, MA, USA) using accelerating voltages of 1.5-3 keV. Prior to the observations, the samples were sputter-coated with 2-3 nm of Pt to avoid the charge effect (the Pt coating thickness was estimated from a calculated deposition rate and experimental deposition time).
Small-angle X-ray scattering (SAXS) SAXS experiments were conducted at the synchrotron X-ray beamline X27C at the National Synchrotron Radiation Research Center (NSRRC) in Hsinchu. The wavelength of the X-ray beam was 0.155 nm. A MAR CCD X-ray detector (Rayonix, L.L.C., Evanston, IL, USA) was used to collect the two-dimensional (2D) SAXS patterns. A one-dimensional (1D) linear profile was obtained by integration of the 2D pattern. The scattering angle of the SAXS pattern was calibrated using silver behenate, with the first-order scattering vector q (q = 4λ − 1 sinθ, where 2θ is the scattering angle) of 1.076 nm − 1 .
Wide-angle X-ray scattering To further confirm the structure of the ordered nanoporous Pt, we collected the powder of nanoporous Pt and performed an X-ray diffraction experiment. The crystal structure of the as-prepared product was characterized by X-ray diffraction using a Rigaku Dmax 2200 X-ray diffractometer (The Woodlands, TX, USA) with Cu KR radiation (λ = 0.1542 nm). The scanning 2θ angle ranged between 20°a nd 120°with a step scanning of 1°for 1 s.

Electrochemical experiments
Electrode preparation. Electrochemical measurements were performed using a glassy carbon rotating disk electrode (Pine Research Instrumentation, Grove City, PA, USA) connected to a PARSTAT 283 potentiostat (Princeton Applied Research, Oak Ridge, TN, USA). A leak-free AgCl/Ag/KCl (3 M) electrode (Warner Instrument, Hamden, CT, USA) was used as the reference. All of the potentials were converted to values with reference to a normal hydrogen electrode. The counter electrode was a Pt mesh attached to a Pt wire. The electrolyte was 0.1 M perchloric acid diluted from 70% (Baker, ACS Reagent grade, Center Valley, PA, USA) using Millipore ultrapure water (Billerica, MA, USA).
Cyclic voltammetry studies. For the Pt/C catalyst (20 wt% 3.2-nm Pt nanoparticles on a Vulcan XC-72 carbon support; E-TEK (Somerset, NJ, USA)), the sample was diluted to 3.3 mg ml − 1 , and then 0.5 μl of the dispersion was transferred onto the rotating disk electrode. Therefore, the loading amount of metal for the Pt/C catalyst was 1.65 μg (that is, 10.57 μg cm − 2 based on the geometric electrode area). For the nanoporous gyroid Pt and Pt black (Aldrich (St Louis, MO, USA), fuel cell grade), the working electrode was prepared using the same procedure, except that the loading amount of the metal was 3.3 μg (that is, 21.5 μg cm − 2 based on the geometric electrode area). Upon drying in air for 2 h, the electrode was covered with 15 μl of 0.05 wt% Nafion solution. After evaporation of water, the electrode was placed under vacuum for 30 min before the measurement. surface (q H ). Subsequently, the specific ECSA was calculated based on the following relationship: where Q H is the charge for H upd adsorption, m is the loading amount of metal, and q H is the charge required for monolayer adsorption of hydrogen on a Pt surface.
Methanol oxidation reaction. In the methanol oxidation reaction studies, all of the prepared samples were transferred to a glassy carbon substrate (geometric area of 1 cm 2 ). The loading density for nanoporous gyroid Pt, PtB and Pt/C was modified by approximately 0.06 mg cm − 2 , 0.25 mg cm − 2 and 0.26 mg cm − 2 , respectively. The CV curves were recorded between 0 and 1.3 V versus normal hydrogen electrode in a nitrogen-purged solution containing 0.5 M CH 3 OH and 0.5 M H 2 SO 4 at the scan rate of approximately 50 mV s − 1 .

RESULTS AND DISCUSSION
Electroless plating of Pt from the BCP template Figure 1a shows Nanoporous gyroid platinum C-F Cheng et al suggesting that the PLLA networks can be selectively removed. Supplementary Figure S1 shows the pore size distribution of the nanoporous PS templates after the hydrolysis of PLLA in PS-PLLA; the average pore size was determined to be approximately 20.4 nm (see SI for details). Therefore, a PS matrix with well-defined, bicontinuous nanochannels can be fabricated and employed as a template for subsequent electroless plating of Pt.
To create the initial stage for the seeding of Pt from electroless plating, the PS template was soaked in a Pt 4+ (H 2 PtCl 4 ) solution mixed with methanol to enhance the wetting tendency of the aqueous solution for pore filling of the PS template through capillary force. The nanoporous template was then immersed into hydrazinium hydroxide (N 2 H 5 OH) (a strong reducing agent for Pt ions) at room temperature to rapidly reduced the Pt ions into nanoparticles inside of the nanochannels (Figure 1b). The nanoparticle size is approximately 20 nm in diameter, as measured from the transmission electron micrographs, equivalent to the diameter of the nanochannel of the template. The nucleation density was calculated from the results of the transmission electron microscopy microtone section with a thickness of 50 nm and estimated as 6 × 10 13 per cubic centimeter (cm 3 ). For the subsequent growth process using the nanoparticle as the nuclei site for the self-catalytic reaction, a relatively weak reducing agent (that is, ascorbic acid) was used. Figure 1c shows the textures of the Pt after a 2-day growth from the reduced nanoparticles in which multibranched Pt can be clearly recognized, indicating successful templating of the gyroid texture from the nucleation and growth processes. After a 5-day growth, as shown in Figure 1d, well-ordered gyroid Pt nanostructures can be successfully fabricated in the PS matrix, reflecting the successful development of gyroid Pt from the branched Pt. Note that the use of a highly active reducing agent may cause blocking of the nanochannels (see Supplementary Figure S2). Therefore, control of the reduction rate is required for the fabrication of a well-interconnected network Pt inside of the PS templates, which can be adjusted and modified by the type and concentration of the reducing agent and the precursor for the nucleation and growth process. Figure 3 shows the [111] and [100] transmission electron microscopy projections of the PS/Pt nanohybrids, suggesting the formation of double gyroid Pt with well-interconnected networks in the PS template after electroless plating. Figure 2c shows the corresponding 1D SAXS profile of the nanohybrids. On the basis of the characteristic reflections for the nanohybrids at the relative q

Nanoporous gyroid Pt
After removal of the PS by UV degradation, a well-ordered network morphology can be found, as shown in Figure 4a. Figure 4b shows the FESEM image with unique gyroid textures, indicating that Pt with well-defined networks and precise control of pore geometry can be prepared. The structure of the nanoporous gyroid Pt can be further identified by SAXS (Figure 2d); the reflections at the relative q values of √6: √8 can be found, suggesting the successful preservation of the gyroid structure after removal of the PS, although the reflections are barely recognizable compared with those in Figure 2c. In addition to the described effects of the Pt on scattering, the smearing of the reflections might be attributed to the deformation and/or the collapse of the Pt network after removal of the template. To examine the crystalline characteristics of the nanoporous gyroid Pt, selected area electron diffraction and wide-angle X-ray diffraction were conducted. The inset of Figure 3a displays the selected area electron diffraction pattern of the PS/Pt nanohybrids. All of the rings can be indexed with the face-centered cubic Pt polycrystals (see Supplementary Figure S3 for details). The wide-angle X-ray diffraction results of the nanoporous gyroid Pt (Figure 4c) are in agreement with the selected area electron diffraction results. All of the diffractions can be indexed as facecentered cubic Pt with the lattice constant a = 3.920 Å, JCPDS card no. 04-0802, corresponding to the reflections of (111), (210), (220), (311) and (220). Furthermore, X-ray photoelectron spectroscopy was used to examine the elemental composition of the nanoporous gyroid Pt. As evidenced by X-ray photoelectron spectroscopy (Supplementary Figure S4), the results show that the C1s peak for the nanoporous Pt is barely detectable compared with that for the PS/Pt nanohybrids, indicating that PS is almost completely removed from the nanoporous gyroid Pt. Moreover, the characteristic peaks of crystalline Pt (binding energy = 70, 314, 331 and 519 eV) remain after the UV exposure, reflecting that the fabricated nanoporous Pt retains its pure metallic character without any impurities. The peak corresponding to O1s (531 eV) can be observed; we speculate that the peak is attributed to the exposure of the metal surface to the air. There is no X-ray photoelectron spectroscopy peak relevant to metal oxides, indicating that the amount of PtO species should be insignificant. Therefore, UV can be used to completely degrade the PS template to yield the nanoporous Pt in its intrinsic form for catalytic applications. Note that metallic materials with fine grains and high purity would exhibit better mechanical strength and catalytic efficiency compared with amorphous materials.

Electrochemical properties of nanoporous Pt
Pt with well-defined nanostructure has been demonstrated to provide superior catalytic activity for electrochemical reactions; for example, Pt with a 1D nanorod structure can be applied to the catalytic electrode in a direct methanol fuel cell by conducting the oxygen reduction reaction (cathode reaction) and the methanol oxidation reaction (anode reaction). 31 For the fabricated nanoporous gyroid Pt, the electronic continuity was probed using cyclic voltammetry. Cyclic  Figure 5a shows the electrocatalytic properties of the nanoporous gyroid Pt compared with commercially available Pt nanoparticle catalysts, including PtB and Pt/C. The CV curves exhibit two distinctive potential regions associated with the adsorption/ desorption of the underpotential deposition of hydrogen (H upd ) between 0 and 0.37 V in the CV curves and the formation of adsorbed hydroxyl species (OH ad ) beyond 0.6 V (see below for details). The ECSA is a quantitative electrochemical property that is sensitively dependent on the size and shape as well as the crystalline interface between the nanostructured Pt and the working environment. The ECSA is estimated using the charge collected in this H upd region between 0 and 0.37 V, based on the hydrogen underpotential deposition charge, Q H,d , after double-layer correction and the assumed value of 210 μC cm − 2 for the desorption of a hydrogen monolayer. On the basis of the CV curves (Figure 5a), the ECSA values are calculated as approximately 15.6, 22.2 and 72.8 m 2 g − 1 for nanoporous gyroid Pt, PtB and Pt/C, respectively. We speculate that the relatively lower ECSA for the nanoporous gyroid Pt catalyst is attributed to its larger Pt size (~20 nm) compared with that of the Pt nanoparticles (~3 nm) in commercially available catalysts. Figure 5b displays the cyclic voltammetry curves of the methanol oxidation reaction catalyzed by the nanoporous gyroid Pt. The entire process was conducted at room temperature in a 0.5 M H 2 SO 4 solution containing 0.5 M methanol. The curves were normalized by experimentally determined ECSA. Two obvious anodic peaks, which is a typical feature of the methanol oxidation reaction, can be clearly identified during the positive sweep. The onset potential (0.63 V) of the nanoporous gyroid Pt was determined for the electrocatalytic oxidation of methanol compared with PtB (0.76 V) and Pt/C (0.79 V). The lower onset potential of the nanoporous gyroid Pt results in a negative shift peak potential, indicating that the methanol oxidation catalyzed by gyroid Pt is substantially easier to trigger. The ratio of the forward anodic peak current density (I f ) to the backward peak current density (I b ), I f /I b value, can be used to investigate the tolerance of the catalyst for carbonaceous species. A low I f /I b value typically indicates poor oxidation of methanol to CO 2 during the forward anodic scan and excessive accumulation of residual carbonaceous species on the catalyst surface. The higher I f /I b value indicates its higher tolerance to the poison. 61,62 As calculated from the results, the I f /I b values are 1.22, 0.96 and 1.26 for the nanoporous gyroid Pt, PtB and Pt/C, respectively. The specific activities of anodic peaks for gyroid Pt, PtB and Pt/C were then calculated as approximately 0.26, 0.24 and 0.12 mA cm − 2 , respectively, demonstrating a better performance in specific activity for nanoporous gyroid Pt compared with that of the commercially available PtB and Pt/C catalysts. The mass activities of the anodic peaks were determined as approximately 40.8, 87.3 and 48.0 mA mg − 1 for the nanoporous gyroid Pt, PtB and Pt/C, respectively. The specific activity of the nanoporous gyroid Pt is more than two times higher than that of Pt/C, whereas the peak mass activity is approximately 47% of Pt/C. Compared with PtB, the nanoporous gyroid Pt exhibits better performance in specific activity but shows a relatively lower value of mass activity. The relatively better performance of the nanoporous gyroid Pt in the specific activity might be attributed to the appearance of low index crystalline facets near the surface of the nanoporous gyroid Pt in addition to the higher specific surface area for electrochemical reaction. As shown in Supplementary Figure S5, based on the high-resolution transmission electron microscopy results, the presence of the low-index crystalline facets can be identified; we speculate that the growth of the low-index crystalline facets is attributed to the confined growth of the Pt within the nanochannels of the PS template. Note that the low-index crystalline facets of Pt would yield a higher catalytic activity. 63 Moreover, based on the X-ray absorption near-edge structure spectra at the Pt L 3 -edge (11 564 eV) (Supplementary Figure S6), nanoporous gyroid Pt shows a relatively lower absorption intensity than PtB and Pt/C, further demonstrating the stabilization of the d orbital electron due to the lower number of unoccupied d-states per Pt atom, resulting in better performance as an electrocatalyst. 64 Therefore, it is reasonable to have a higher specific activity for the nanoporous gyroid Pt than PtB and Pt/C, whereas the relatively lower value of the mass activity of the nanoporous gyroid Pt is attributed to the larger characteristic size of the nanoporous gyroid Pt than the commercially available catalysts.

Performance of durability
Note that the durability of the catalyst materials is a severe problem for practical applications that must be addressed to evaluate their performance. To investigate the durability of the Pt, repeated cycling was conducted in an oxygen-saturated 0.1 M HClO 4 solution by applying voltage from 0 to 1.2 V at the scan rate of 50 mV s − 1 . The decrease of the ECSA with the number of cycling rounds is depicted in Figure 5c. A significant loss of ECSA can be observed for PtB and Pt/C, whereas the ECSA value of the nanoporous gyroid Pt shows only a slight decrease during the CV measurements. After 2000 cycles, the ECSA is reduced to 64 and 49% for PtB and Pt/C, respectively, in contrast to the 13% loss in the nanoporous gyroid Pt. After 3000 cycles, the nanoporous gyroid Pt experiences only approximately 26% loss of ECSA, whereas a significant loss for PtB and Pt/C (75% loss and 65% loss, respectively) can be found (see Supplementary Figure S7 for details). Pt with a 3D network structure was demonstrated to significantly enhance the duration performance. We speculate that the enhancement of the duration performance of Pt is attributed to the well-interconnected network structure that addresses certain problems in the application as electrocatalyst, including particle aggregation and loss of electrical contact, as well as other disadvantages, such as Ostwald ripening.

CONCLUSIONS
In conclusion, nanoporous PS with gyroid nanochannels can be fabricated from the self-assembly of the degradable BCP, PS-PLLA, followed by the hydrolysis of the PLLA blocks. A modified electroless plating method for templated synthesis using the nanoporous PS as a template was demonstrated to prepare well-ordered PS/Pt nanohybrids with a well-defined network morphology by exploiting the nucleation and growth mechanism during the templating process under ambient conditions. After removal of the PS template, nanoporous gyroid Pt can be fabricated and used for electrochemical catalysis. Benefiting from the well-defined network structure with robust texture and the presence of low-index crystalline facets of Pt, the nanoporous gyroid Pt can be used as an electrochemical catalyst possessing superior macroscopic stability and peak specific activity compared with commercially available catalysts.