{'fraction_non_alphanumeric': 0.045338908339840306, 'fraction_numerical': 0.0316112944258331, 'mean_word_length': 4.891378542810506, 'pattern_counts': {'":': 0, '<': 3, '<?xml version=': 0, '>': 1, 'https://': 0, 'lorem ipsum': 0, 'www.': 0, 'xml': 0}, 'pii_count': 0, 'substrings_counts': 0, 'word_list_counts': {'cursed_substrings.json': 0, 'profanity_word_list.json': 0, 'sexual_word_list.json': 0, 'zh_pornsignals.json': 0}}
Photoresponsive Porphyrin Nanotubes of Meso-tetra(4-Sulfonatophenyl)Porphyrin and Sn(IV) meso-tetra(4-pyridyl)porphyrin

Porphyrin macrocycles and their supramolecular nanoassemblies are being widely explored in energy harvesting, sensor development, catalysis, and medicine because of a good tunability of their light-induced charge separation and electron/energy transfer properties. In the present work, we prepared and studied photoresponsive porphyrin nanotubes formed by the self-assembly of meso-tetrakis(4-sulfonatophenyl)porphyrin and Sn(IV) meso-tetra(4-pyridyl)porphyrin. Scanning electron microscopy and transmission electron microscopy showed that these tubular nanostructures were hollow with open ends and their length was 0.4–0.8 μm, the inner diameter was 7–15 nm, and the outer diameter was 30–70 nm. Porphyrin tectons, H4TPPS42- : Sn(IV)TPyP4+, self-assemble into the nanotubes in a ratio of 2:1, respectively, as determined by the elemental analysis. The photoconductivity of the porphyrin nanotubes was determined to be as high as 3.1 × 10−4 S m−1, and the dependence of the photoconductance on distance and temperature was investigated. Excitation of the Q-band region with a Q-band of SnTPyP4+ (550–552 nm) and the band at 714 nm, which is associated with J-aggregation, was responsible for about 34 % of the photoconductive activity of the H4TPPS42--Sn(IV)TPyP4+ porphyrin nanotubes. The sensor properties of the H4TPPS42-- Sn(IV)TPyP4+ nanotubes in the presence of iodine vapor and salicylate anions down to millimolar range were examined in a chemiresistor sensing mode. We have shown that the porphyrin nanotubes advantageously combine the characteristics of a sensor and a transducer, thus demonstrating their great potential as efficient functional layers for sensing devices and biomimetic nanoarchitectures.


INTRODUCTION
The self-organization of tetrapyrroles in the form of molecular aggregates is known in biological systems for its role in light harvesting, energy transformation, and electron transport. The properties and functions of natural chlorophyll pigments, which in the composition of the chloroplasts carry out the photosynthesis, and hemes, which in the composition of hemoglobin carry out oxygen transport, in the composition of myoglobin-its storage, and in the composition of cytochromes-catalysis of biological redox reactions, inspired wide use of porphyrins and their molecular assemblies as biomimetic materials in systems replicating photosynthesis, electron transport, and enzymatic catalysis. Therefore, the self-assembly of porphyrin macrocycles, whose nanostructures have interesting electronic and optical properties, is being used in search for new nanoscale materials in the field of reversible binding and (photo)catalysis, biomimetic sensors, solar energy conversion, and electrically active components in various nanodevices (Fukuzumi and Imahori, 2008;El-Khouly et al., 2014;Fuhrhop, 2014;Guo et al., 2014;Ou et al., 2014;Zhang et al., 2015;Chen et al., 2016;Koposova et al., 2016a;Mirkovic et al., 2017;Paolesse et al., 2017). Particular attention has been given in the past to the watersoluble porphyrins. The synthesis of the first J-aggregates of a water-soluble porphyrin, 5,10,15,20-tetra(4-sulphonatophenyl) porphyrin, formed in acidified aqueous solutions, provided the stimulus for the investigations of the self-assembled porphyrin nanostructures (Pasternack et al., 1972;Ohno et al., 1993;Mchale, 2012). Fine-tuning the properties of a metallo-porphyrin complex by varying its different components, such as the molecular skeleton, peripheral substituents, coordinated metal as well as pH and ionic strength of the solutions, allows the creation of self-assembled nanostructures of various shapes with different properties. Self-assembly of porphyrin tectons into nanostructures is controlled by a multiplicity of non-covalent interactions such as hydrogen bonds, electrostatic and π-π interactions, axial coordination, and van der Waals forces (Guldi and Imahori, 2004;Martin et al., 2010Martin et al., , 2013Würthner et al., 2011).
The electrical and photoconductivity properties of aromatic π-conjugated porphyrin macrocycles and their nanoarchitectures are intensively studied. The π-conjugated porphyrin macrocycles absorb the visible light energy, which may lead to the intermolecular transfer or delocalization of the excitation energy in porphyrin aggregates and arrays making them photoconductive under application of electric field (Weigl, 1957;Golubchikov and Berezin, 1986;Kobayashi et al., 1993;Chou et al., 2000;Drain, 2002;Schwab et al., 2004;Yeats et al., 2008;Kocherzhenko et al., 2009;Friesen et al., 2010;Martin et al., 2010;Riley et al., 2010;Cai et al., 2014;Adinehnia et al., 2016;Koposova et al., 2016bKoposova et al., , 2018Borders et al., 2017). So far, electrical properties of porphyrin nanostructures and the mechanisms of charge transport in their aggregates have not been investigated and explained in details. Photoconductivity was reported in J-aggregates of free-base porphyrins (Schwab et al., 2004;Yeats et al., 2008;Friesen et al., 2010;Riley et al., 2010), whereby most studies so far have dealt with the selfassembled nanorods of 5,10,15,20-tetra(4-sulphonatophenyl) porphyrin. Later on, Adinehnia et al. (2016) and Borders et al. (2017) studied photoconductive properties of porphyrin nanostructures composed of oppositely charged free-base porphyrins: 5,10,15,20-tetra(4-sulfonatophenyl)porphyrin with 5,10,15,20-tetra(N-methyl-4-pyridyl)porphyrin, TPPS 4 :TMPyP, (Adinehnia et al., 2016) or 5,10,15,20-tetra(4-pyridyl)porphyrin, TPPS 4 :TPyP, (Borders et al., 2017). Martin et al. (2010) described photoconductive microscale clover-shaped structures self-assembled from the water-soluble metalloporphyrins Zn(II)TPPS 4− as a donor and Sn(IV)T(N-EtOH-4-Py)P 4+ as an acceptor. The authors discussed the observed photoconductivity of the nanostructures in terms of exciton delocalization and charge-transfer exciton theory based on a model of the electron-donor-acceptor chargetransfer complex tetrathiafulvalene-tetracyanoquinodimethane (TTF-TCNQ) (Ferraris et al., 1973). By analogy with TTF-TCNQ, the authors proposed an arrangement of individual electron donor, Zn(II)TPPS 4− , and acceptor, Sn(IV)T(N-EtOH-4-Py)P 4+ , porphyrin molecules in segregated stacks, whereby the charge carriers produced by photoexcitation can move along the stacks, when an electric potential is applied in the direction of the stacks. Formation of heteroaggregates with charge-transfer interactions was also found earlier in the assembly of electron-attracting Au(III) porphyrin and electron-releasing Zn(II) porphyrin (Segawa et al., 1989). Segawa et al. (1992b) reported photoinduced electron-transfer reactions in porphyrin heteroaggregates of the water-soluble Au(III) and Zn(II) porphyrins and formation of the contact radical ion pair as a result of photoexcitation. Recently, photoinduced charge separation has been observed for the ion-pairs obtained from water-soluble cationic and anionic porphyrins ZnTMePyP 4+ or H 2 TMePyP 4+ and ZnTPPS 4− or H 2 TPPS 4− (Natali and Scandola, 2016). In this system, the porphyrins of cationic character were reduced, while the porphyrins of anionic character were oxidized. Collman et al. (2000) reported a series of bis(metalloporphyrin) sandwich complexes as charge-transfer materials and their conductivities. Porphyrins as molecular acceptors form donor-acceptor systems with other molecular donors (Segawa et al., 1992a;Jana et al., 2017). The above studies give an evidence for the electron-donor-acceptor charge-transfer complex mechanism of the photoconductivity of the porphyrin dimers, aggregates, arrays, and nanostructures. However, a better knowledge of the supramolecular non-covalently bonded porphyrin nanoaggregates and their properties is required to understand natural macrocycles assemblies, evaluate their utility as electrical components in nanodevices, and advance the exploitation of their properties, such as excited state delocalization, energy and electron transfer, and photoconductivity in bio-mimicking materials in the fields of photodetectors, solar energy applications, catalysis, and sensors. Earlier, we reported on the self-assembly and photoconductivity of the porphyrin nanostructures in systems of meso-substituted Co(III) and Sn(IV) porphyrins as well as meso-substituted Co(III) and free-base porphyrins. In this report, we present the morphological, spectral, electrochemical properties, and photoconductivity phenomenon of self-assembled porphyrin nanostructures of meso-tetra(4-sulfonatophenyl)porphyrin and Sn(IV) meso-tetra(4-pyridyl)porphyrin, which shows the highest photoconductivity of the last systems.

Chemicals
Sn(IV) meso-tetra(4-pyridyl)porphyrin dichloride and mesotetra(4-sulfonatophenyl)porphyrin dihydrochloride were obtained from Frontier Scientific (>95% purity) and used as received, (Figure 1). All other chemicals were from Sigma-Aldrich. Diamond (1 µm) and alumina (0.05 µm) polishing suspensions and the corresponding polishing pads were from ALS Co. All solutions were prepared using distilled water. Sodium hydroxide and hydrochloric acid solutions were used to adjust the pH.

Nanotube Synthesis
The porphyrin nanotubes were prepared using equal volumes of the 10 µM stock solutions of individual porphyrins (an equimolar, 1:1 concentration ratio) and adjusting the pH of the mixture to pH 2, 6, and 10.5. The formation of colloids started immediately at pH 2, while at pH 6 and 10.5 no nanostructure formation was observed. The nanostructures were also prepared using 1:5

Characterization of the Structure and Composition
The nanostructures were characterized by scanning electron microscopy using a Gemini 1550 VP SEM (Carl Zeiss, Jena, Germany). To prepare the samples for SEM, 50 µL of the nanostructures solutions were dropped on the Si substrates, and the samples were left to dry for 12 h. After that, the samples were washed with 0.01 M HCl, water, and left to dry. The transmission electron microscopy (TEM) images were obtained using a FEI Tecnai G2 F20 microscope operated at 200 kV. EDX analysis was performed using a JEOL 840 A. The samples of the nanostructures for the EDX analysis were concentrated in a 0.02 M HCl by centrifugation (10,000 rpm 7 min) and washing several times until a transparent supernatant solution was obtained to remove not self-assembled porphyrins. Fifty microliter of the nanostructures solutions were dropped on the Si/SiO 2 substrates, and the samples were left to dry. This procedure was repeated four times. After that, the samples were washed with 0.01 M HCl, water, and left to dry. The AFM measurements of the nanostructures on the Si/SiO 2 substrates were performed using a MultiMode scanning probe system (Bruker) in a tapping mode. The samples were prepared as described above for the SEM samples. The optical spectra were obtained on a PerkinElmer Lambda 900 spectrometer. Quartz cuvettes with a path length of 10 and 5 mm were used. Individual porphyrin solutions for spectra measurements were prepared by dissolving Sn(IV)TPyP 4+ in acidified water (pH = 2.0) and H 4 TPPS 2− 4 in water. The samples of the nanostructures for the UV-vis spectrometry were concentrated in a 0.02 M HCl by centrifugation (10,000 rpm 7 min) and washing several times until a transparent supernatant solution was obtained to remove not self-assembled porphyrins.
The ratio of S:N atoms was found using an elemental analysis, which determines the absolute element content. The samples of the nanorods for the elemental analysis were prepared by centrifugation (10,000 rpm 7 min) and washing of the nanorods solutions with subsequent drying of the collected sediments and analyzed by the "vario El cube" (Elementar) with a thermal conductivity detector.

Electrochemical Methods
Electrochemical experiments were performed with a potentiostat (Autolab PGSTAT100, The Netherlands) controlled by the Nova 2.1 software. The experimental setup for recording the cyclic voltammograms included a three-electrode electrochemical cell. A coiled platinum wire was used as a counter electrode. A glassy carbon electrode (BASi Inc.) with a diameter of 3 mm was used as a working electrode. The potentials were controlled relative to a double junction Ag/AgCl, Metrohm, Ag | AgCl | KCl 3 M::0.5 M KCl reference electrode. The solution in the bridge of the reference electrode was replaced after each measurement to avoid contaminations of the electrochemical cell. Measurements were carried out under Ar in the dark at room temperature (21 ± 1 • C). Glassy carbon electrodes were cleaned before each electrochemical measurement as described below: the electrodes were polished with diamond (1 µm) and then alumina (0.05 µm) slurry on the respective polishing cloths. Immediately after polishing, the electrodes were rinsed with distilled water and sonicated in a mixture of water and ethanol for about 10 s to remove polishing residues from the electrode surface. The electrodes were then thoroughly rinsed with distilled water and dried with nitrogen.

Electrophotoresponse Measurements
To measure the (photo)conductance of the porphyrin nanorods, two types of thin-film gold electrodes were used: gold electrode pairs with an electrode gap of 400 nm, (Figure S1), and interdigitated electrode arrays with a 2 µm spacing between the electrode lines and an electrode line thickness of 2 µm. The electrodes were produced on a Si substrate with a silicon dioxide layer of 1,000 nm thickness using electron beam lithography, liftoff process, and thin-film technologies in an ISO 5 cleanroom as described in detail in Muratova et al. (2016). Thin metal layers of titanium for adhesion (10 nm) and gold (50 nm) were deposited by means of an electron beam evaporation using a Pfeiffer PLS 500 equipment. After fabrication, the electrodes were cleaned in acetone and isopropanol. After that, the electrodes were treated with oxygen plasma (≪Plasma system FEMTO≫). Finally, the electrodes were rinsed with ethanol and distilled water. Two microliter of the porphyrin nanostructures solution was pipetted onto the electrodes and the samples were allowed to dry in the dark for 2 h. The samples were then rinsed with 0.01 M HCl, water, and allowed to dry for 24 h. The measurements were also performed using an equimolar solution of TPPS 4 and Sn(IV)TPyP 4+ of pH 6 instead of the nanostructure solution. The device was prepared in a similar way as for the nanostructures, namely, 2 µL of the solution of porphyrins was pipetted onto the electrodes and the device was allowed to dry in the dark for 2 h. The device was then rinsed with water and allowed to dry for 24 h.
The (photo)conductance was recorded with a Keithley 4200 SCS semiconductor analyzer using a two-probe configuration. Applied potential was 0.5 V. The gold electrodes were connected to the external circuit by contacting the bond pads with tungsten

Nanotube Morphology
Sn(IV)TPyP 4+ and H 4 TPPS 2− 4 solutions produced brown precipitates in a self-assembly reaction at pH 2. It should be noted that that for a concentration ratio of 5:1 (Sn(IV)TPyP 4+ : H 4 TPPS 2− 4 ), a very small amount of the nanostructures is formed in a self-assembly reaction, which makes them not very suitable for practical use. SEM, TEM, and AFM analyses revealed that these two porphyrins form the tubular nanostructures, (Figures 2-4) and (Figures S2, S3).
TEM images show that the tubular nanostructures are hollow with open ends. These structural details are clearer at the edges of the round formed conglomerates, because the material layers overlap at the places with a higher density of nanotubes. Additionally, the open ends of the nanotubes can be seen in some of the SEM images, e.g., (Figure S2B). The nanotubes have a length of 0.4-0.8 µm, an inner diameter of 7-15 nm, and an outer diameter of 30-70 nm, (Figures 2-4) and (Figures S2, S3).
Interestingly, SEM and AFM investigations indicated a presence of two types of the nanostructures in a system, where the porphyrins were taken in a 1:5 (Sn(IV)TPyP 4+ : H 4 TPPS 2− 4 ) concentration ratio, (Figures 2C,D, 4C,D) and (Figures S2, S4). One kind of the nanostructures is similar to the nanostructures in the systems, where the porphyrins were taken in 1:1 and 5:1 (Sn(IV)TPyP 4+ and H 4 TPPS 2− 4 ) concentration ratios, while the presence of much thinner nanorods of about 10 nm diameter and patches (unrolled pieces of nanorods) of about 6 nm thickness is observed in a 1:5 (Sn(IV)TPyP 4+ : H 4 TPPS 2− 4 ) system, (Figures 2C,D) and (Figures S2, S4). We assume that these thinner and segregated nanostructures are H 4 TPPS 2− 4 self-assembled nanorods formed due to the excess of this porphyrin because of the structural and optical absorption similarity (see below). The thin nanorods and patches were observed to be located under the thicker Sn(IV)TPyP 4+ -H 4 TPPS 2− 4 nanotubes and on the edges of the layers formed by the thick Sn(IV)TPyP 4+ -H 4 TPPS 2− 4 nanotubes, (Figures 2C,D) and ( Figure S2). One may conclude that the excess of H 4 TPPS 2− 4 results in a larger dispersion of the nanostructures, which is also supported by the AFM investigation below, producing at least two types of the nanostructures. These segregated thin nanorods and patches do not form, however, continuous layers like the thick Sn(IV)TPyP 4+ -H 4 TPPS 2− 4 nanotubes form.
An interesting feature of the nanostructures self-assembled in a system, where the porphyrins were taken in a 5:1 (Sn(IV)TPyP 4+ : H 4 TPPS 2− 4 ) concentration ratio, in comparison with other two systems at pH 2 was a transparency of the nanotubes, (Figures 2E,F) which is probably related to their thickness or non-dense structure.
AFM analysis showed that the nanostructures selfassembled from equimolar solutions of two porphyrins produced smoother layers, (Figures 4A,B), while the nanostructures obtained from 1:5 (Sn(IV)TPyP 4+ : H 4 TPPS 2− 4 ) solutions formed more rough layers, (Figures 4C,D), which might be explained by the presence of the nanostructures of two types. Additionally, AFM showed a different morphology of the nanotube surfaces formed in a system, where the porphyrins were taken in a 5:1 (Sn(IV)TPyP 4+ : H 4 TPPS 2− 4 ) concentration ratios. One can observe a nodular or twisted surfaces of the nanotubes, (Figures 4E,F). This feature requires, however, further investigations. The nanotubes in the TEM images appear in round formed agglomerates, being connected together by one edge and diverging in different directions from one place. The appearance of the round nanostructure conglomerates may emerge either in the solution during synthesis after the formation of individual nanotubes which then stick together or after deposition of the nanotubes on a solid substrate and subsequent water evaporation. Thus, SEM, TEM, and AFM analyses show that the structural features of the H 4 TPPS 2− 4 -Sn(IV)TPyP 4+ binary nanotubes differ essentially from those of the self-assembled H 4 TPPS 2− 4 nanorods. The latter are well-segregated nanorods with an essentially smaller outer diameter of about 10-15 nm, as it is shown in Figure S5. The smaller nanostructures in the system, where the porphyrins in the solution were taken in a concentration ratio of 1:5 (Sn(IV)TPyP 4+ : H 4 TPPS 2− 4 ), were probably the result of self-assembly mainly H 4 TPPS 2− 4 because of its excess. A synergy of various intermolecular interactions and structural features of individual porphyrin tectons (Agranovich and Bassani, 2003; Guldi and Imahori, 2004;Medforth et al., 2009;Koposova et al., 2016bKoposova et al., , 2018 are responsible for a great multiplicity of the observed 1D to 3D geometries of porphyrin molecular aggregates formed by self-assembly. The self-assembly of the H 4 TPPS 2− 4 : SnTPyP 4+ porphyrin nanotube (2.4:1 mol mol −1 ) was first shown by Shelnutt and co-workers . The self-assembly was highly pH dependent, since the protonation states of the porphyrin molecules determined the balance of molecule charges for the assembly Franco et al., 2010). At pH = 2.0, partially dissociated sulfonato-groups (pK a = 2.6 for benzenesulfonic acid), a protonated center of H 4 TPPS 2− 4 (pK a = 4.9), and protonated pyridyl groups of Sn(IV)TPyP 4+ (pK a = 5.2 for pyridine) participate in the molecular assembly. Influence of the pH on the porphyrin molecular assembly was also documented in the study of the Sn(IV)TPPS 4 -Co(III)TPyP nanostructures, where the Sn:Co atomic ratio was found to be 1:1.15 at pH 2.7 and 1:3 at pH 4.8 (Koposova et al., 2016b). These molecule ratios were due to the neutralization of anionic and cationic porphyrin species at different pH. Accordingly, pH plays an important role in the self-assembly, since it determines the electrostatic interactions of the porphyrin tectons.
In our study, TPPS 4 and Sn(IV)TPyP 4+ taken in a 1:1 concentration ratio did not self-assembly into the nanostructures at pH 6 and 10.5, where TPPS 4 is predominantly in its deprotonated H 2 TPPS 4− 4 form. This indicates that the presence of the protonated center of H 4 TPPS 2− 4 and its assembly into the slipped face-to-face configuration is a driving force for the self-assembly process, while the Sn(IV)TPyP 4+ tectons, which do not produce the nanostructures by its own, co-assembly in this self-assembly process. In these cases, the optical absorption spectra, (Figure 5), of Sn(IV)TPyP 4+ and TPPS 4 taken in 1:1 concentration ratio at pH 6 and 10.5 are practically overlap of the optical absorption spectra of the individual porphyrins at the same pH and are not indicative for the formation of new species. In addition, as it was mentioned earlier, a very small amount of nanostructures was formed if the initial molar ratio of H 4 TPPS 2− 4 : SnTPyP 4+ in solution was 1:5, pH 2. Altogether, these observations indicate that H 4 TPPS 2− 4 represents the driving force for self-assembly in this porphyrin couple, while SnTPyP 4+ is rather included due to its cationic nature.
The UV-visible absorption spectrum of the H 4 TPPS 2− 4 nanorods demonstrates a sharp J-band at 491 nm red-shifted from the monomer absorption and distinguished by its narrowness and high extinction coefficient together with a band at 706 nm in a Q-region typical for the J-aggregates of H 4 TPPS 2− 4 , (Figure 5). Absorption spectrum of the H 4 TPPS 2− 4 -SnTPyP 4+ nanotubes prepared using different molar ratios of the porphyrins in the solutions at pH 2 in our study, Figures 5A,C, indicates presence of the J-aggregates in the Sn(IV)TPyP 4+ -H 4 TPPS 2− 4 selfassembly according to the characteristic absorption bands at λ = 500-516 nm and λ = 714-726 nm. The bands are red-shifted and broadened compared to the absorption bands of the H 4 TPPS 2− 4 nanorods (dark yellow line), (Figures 5A,C). Interestingly, that in the case of a system, where SnTPyP 4+ and H 4 TPPS 2− 4 porphyrins were taken in a concentration ratio of 1:5 (green line), (Figure 5C), the J-band at about 500-516 nm is splitted, which may support existence of two types of nanostructures in this system, as it was discussed above. The presence of J-aggregate bands indicates that excitons may be delocalized over multiple molecules (Torres and Bottari, 2013). Thin nanotubes formed by self-assembly of the metal-free porphyrin H 4 TPPS 2− 4 into slipped face-to-face columnar arrangements as well as the mechanism of their formation have been presented and discussed in a series of studies (Ohno et al., 1993;Maiti et al., 1995;Würthner et al., 2011;Mchale, 2012). Inclusion of the hexacoordinated Sn(IV)TPyP 4+ metalloporphyrin with a heavy metal results in thicker nanotubes with larger sizes saving stack configuration in the assembly and interrupting the usual dipole coupling that  lead to broadening of J-bands (Franco et al., 2010). Unlike H 4 TPPS 2− 4 , Sn(IV)TMPyP 4+ does not form homoaggregates on its own (George et al., 2010). This may be explained by the presence of the obligate axial ligands of the Sn(IV) porphyrin, which is expected to inhibit macrocycle stacking due to the lack of a cationic center (Ohno et al., 1993;Franco et al., 2010). The Sn 4+ ion with the axially coordinated Cl − ions hinder the faceto-face geometry, preventing its own J-aggregates but allowing electrostatic interaction between H 4 TPPS 2− 4 and SnTPyP 4+ via the cationic and anionic peripheral groups (Rosaria et al., 2008), which is another force of the assembly process. In Koposova et al. (2016b), a cationic center of the H 4 TPPS 2− 4 dianion was replaced with a metal cation, which resulted in a network-like nanostructures prepared by self-assembly of two metalloporphyrins, Sn(IV)TPPS 4 -Co(III)TPyP, instead of wellformed nanorods characteristic for the H 4 TPPS 2− 4 self-assembly. Thus, the central metal affects the assembly dimension (Rosaria et al., 2008), which is useful for modulating the aggregate size and properties. Based on previous literature and our experiments above, we assume that the main driving force of self-assembly in this porphyrins pair is assembly of the TPPS 4 dianion, H 4 TPPS 2− 4 , with a slipped face-to-face stacking with inclusion of a six-coordinated tin porphyrin, which do not form aggregates by its own. However, exact relative molecular arrangement of both porphyrins in these nanostructures remains under discussion Franco et al., 2010). In the present study, EDX spectroscopy showed a presence of both porphyrins (according to the presence of both sulfur and tin elements) in the self-assembled nanotubes, (Figure 6 and Figure S6). Because of the poor accuracy of quantitative EDX analysis, we used chemical elemental analysis to estimate the presence of both porphyrins in the nanotubes. Since a very small amount of the nanostructures is formed in a 5:1 (Sn(IV)TPyP 4+ : H 4 TPPS 2− 4 ) solution, and system 1:5 (Sn(IV)TPyP 4+ : H 4 TPPS 2− 4 ) produced at least two different kinds of nanostructures, we performed an elemental analysis of the nanostructures self-assembled from the equimolar porphyrin solutions at pH 2, Figure S7, which indicated a H 4 TPPS 2− 4 : SnTPyP 4+ molar ratio in the nanostructures of 2:1.

Photoconductivity
The electrophotoresponse of the H 4 TPPS 2− 4 -SnTPyP 4+ porphyrin nanotubes was measured in the dark (dark current) and after photoexcitation with visible light, (Figure 7). Photoexcitation resulted in a photocurrent in case of the H 4 TPPS 2− 4 -SnTPyP 4+ porphyrin nanotubes as one can see in Figure 7. Photoresponse of a device, where an equimolar solution of TPPS 4 and SnTPyP 4+ porphyrins (pH 6) was dropcasted onto the device and prepared for the measurements in the same way as for the nanostructures (see section Electrophotoresponse Measurements) is also shown. However, no photocurrent was observed in this case probably due to the absence of a permanent layer of porphyrins in the gap between the contact electrodes in the conditions of experiments and a lower photoconductivity of the individual porphyrin molecular layers.
After subtracting the dark current, the apparent photoconductivity of the H 4 TPPS 2− 4 -Sn(IV)TPyP 4+ nanotubes at 23 • C was estimated as (3.1 ± 0.9)×10 −4 S m −1 (n = 5). Slightly lower and less reproducible value, (2.2 ± 1.0) × 10 −4 S m −1 , was found for the nanostructures prepared in a solution with a Sn(IV)TPyP 4+ : H 4 TPPS 2− 4 concentration ratio of 1:5. We assume that this might be due to the presence of several types of the smaller nanostructures formed by H 4 TPPS 2− 4 , which do not form a continuous layer over hundreds of nm distances, (Figures 2C,D and Figure S5), and contact area with the metal electrodes. The latter value is thus not a characteristic of one type of nanostructures, but rather characterizes a nonhomogeneous mixture of the nanostructures obtained in this system. Amounts of the nanostructures prepared in a solution with a Sn(IV)TPyP 4+ : H 4 TPPS 2− 4 concentration ratio of 5:1 was practically very small for the accurate measurements of photoconductivity, giving a similar approximate value of (1.8 ± 0.8) × 10 −4 S m −1 (n = 2). Identical spectral features of the nanostructures prepared at pH 2, (Figure 5C), are in agreement with similar values of photoconductivities in these systems.
The value of the apparent photoconductivity of the H 4 TPPS 2− 4 -Sn(IV)TPyP 4+ nanotubes is lower than for the FIGURE 7 | Visible light photoresponse of the H 4 TPPS 2− 4 -SnTPyP 4+ nanotubes prepared in an equimolar solution at pH 2, electrode gap 400 nm, V app = 0.5 V. A dark blue curve shows a visible light photoresponse of a device with no nanostructures. The device was prepared by dropcasting an equimolar solution of TPPS 4 and SnTPyP 4+ (pH 6) onto the chip as described in experimental section Electrophotoresponse Measurements.
porphyrin-acetylene-thiophene polymer wires synthesized in Li et al. (2004), which, had, however, covalent nature, ( Table 1). On the other hand, the apparent photoconductivity of the H 4 TPPS 2− 4 -Sn(IV)TPyP 4+ nanotubes is higher by several orders of magnitude than for similar systems, (Table 1), and corresponds to the conductivity region of semiconductors Naarman, 2012). As can be seen in Table 1, the photoconductivities of the porphyrin films and porphyrin self-assembled nanostructures were demonstrated in a range of 10 −10 -10 −3 S m −1 (Golubchikov and Berezin, 1986). 1 | Conductivity and photoconductivity of different self-assembled and covalently bonded porphyrin systems.

Porphyrin system σ , S m −1 References
Tetraphenylporphine (TPP) film a 1.5 × 10 −9 Weigl, 1957 Oxygen-doped (air) ZnTPP thin film b <10 −9 Kobayashi et al., 1993 Charge-transfer complexes of Lanthanide(III) bis ( Chlorophyll-a a,e (0.2-1.0) × 10 −8 Jones et al., 1983 Protoporphyrin IX dimethyl ester 1.5 × 10 −5  (Segawa et al., 1992a). d The photoconductivity in this study is defined as the conductivity divided by the light intensity. e Photoconductivity parallel to the plane of the multilayer, in-plane photoconductivity, 50 W m −2 of white light, 5 V bias. f At 405 nm excitation, 10 kW m −2 , 2 V bias. g At 445 nm excitation, 10 kW m −2 , 2 V bias. h At 445 nm excitation, 1.0 W cm −2 , 5 V bias. i Visible light, Xe lamp, 0.25 kW m −2 , bias 0.5 V. Figure 6A shows that the photocurrent of the self-assembled H 4 TPPS 2− 4 -Sn(IV)TPyP 4+ nanotubes decreases over the µm distances. The dependence of the photroconductance of the H 4 TPPS 2− 4 -SnTPyP 4+ nanostructures on temperature was investigated in the range from 23 to 70 • C, (Figure 6B). Increasing the temperature resulted in a decrease in the photocurrent, dσ/dT<0. At the highest temperature, 70 • C, a decrease in the dark current was also observed. The metal-like character of the dependence of the photoconductivity of the H 4 TPPS 2− 4 -SnTPyP 4+ nanotubes on temperature was also observed earlier for the H 4 TPPS 2− 4 -Co(III)T(4-Py)P self-assembled nanostructures (Koposova et al., 2018). Furthermore, the photoconductivity of the Sn(IV)TPPS 4 -CoTPyP nanostructures was characterized by the decrease in both photocurrent and dark current at the elevated temperature (Koposova et al., 2016b). The observed dependence may be explained by overcoming the energy of intermolecular interactions with increased disorder, as well as the recombination of electrons and holes at elevated temperatures. A similar metal-like character of the conductance was also observed in a TTF-TCNQ complex in a narrow range of temperature (Ferraris et al., 1973) and arrayed iodine-doped metallo-macrocycles (Schramm et al., 1980;Hoffman and Ibers, 1983;Golubchikov and Berezin, 1986). After cooling down to the initial temperature, the conductance properties recovered and photoconductance even increased slightly, (Figure 6B) (dotted line). This indicates that the destruction of the nanostructure assembly does not occur during heating.
Photoinduced charge transfer in self-assembled porphyrin nanomaterials can be described in terms of charge-transfer exciton theory, where two neighboring porphyrin molecules with different electronic characteristics form an electron-donoracceptor charge-transfer complex (Segawa et al., 1989(Segawa et al., , 1992bKnoester and Agranovich, 2003;Scholes and Rumbles, 2006;Zhu et al., 2009;Martin et al., 2010;Natali and Scandola, 2016). This theory assumes that the charge-transfer excitons in the electron-donor-acceptor complexes are generated by absorption of light, and that these are essential for the creation of free carriers (Knoester and Agranovich, 2003). The locations of the hole and electron on different porphyrin molecules due to their different electron donating and electron accepting properties (Knoester and Agranovich, 2003;Martin et al., 2010;Natali and Scandola, 2016) increases the electron and hole separation distance and the probability of a free charge-carrier formation. An applied electric field may favor the charge separation (Scholes and Rumbles, 2006) and result in a photocurrent. Exciton theory has been applied to biomolecular aggregates in the lightharvesting systems of plants and several types of green bacteria, which absorb sunlight and transport the excitation energy to the reaction centers (Knoester and Agranovich, 2003).
As it was mentioned in the introduction section, Martin et al. (2010) described the photoconductance of the microscale clovershaped assemblies of two metalloporphyrins Zn(II)TPPS 4− and Sn(IV)T(N-EtOH-4-Py)P 4+ in terms of the charge-transfer excitons produced in the photoexcited nanostrucutres. ZnPs were considered donors and Sn(IV)Ps were considered acceptors because of the redox potentials estimations based on the literature data for the Zn and Sn(IV)OEPs. The segregated stacking of molecules similar to that in a classical donor-acceptor organic solid TTF-TCNQ was supposed. In this configuration, the excitation with light resulted in electrons on acceptor porphyrin in columns of positive charges of the pyridinium groups, and the holes remained on porphyrin with a donor character with channels formed by the negative charges of the sulfonate groups.
The donor and acceptor character of the nanorod tectons can be estimated from the energy levels of each component. This can be approached using cyclic voltammetry, which reveals the first oxidation and reduction potentials and, as a result, the relative location of the porphyrin energy levels (Mairanovsky, 1987;Bouvet and Simon, 1990;Rieger, 1994;Kadish and Van Caemelbecke, 2003;Martin et al., 2010). Under defined conditions (Delahay, 1954;Rieger, 1994), the half-wave potentials of the compounds can be taken as an approximation to the standard potentials and it is expected that their values correlate with the electron affinity of the compounds. The electron affinity is expected to be related to the energy of the lowest unoccupied molecular orbital. We carried out cyclic voltammetry of TPPS 4 and Sn(IV)TPyP 4+ , (Figure 7 and Table 2). Measurements were performed at pH=2.0 and 3.5 for SnTPyP 4+ , and at pH = 4.0 for H 4 TPPS 2− 4 (dimerization, self-assembly) and pH = 6.9 for H 2 TPPS 4− 4 , respectively. On the one hand, the measurements at higher pH were impeded by a poor solubility of Sn(IV)TPyP 4+ . On the other hand, H 4 TPPS 2− 4 forms dimers, J-aggregates, and nanotubes in neutral and acidic media (pH < 4.8), respectively, and the redox peaks were very sluggish and poorly defined. In general, adsorption also complicates the electrochemical measurements of TPPS 4 and Sn(IV)TPyP compounds. Therefore, we used a negative shift of 0.030 V pH −1 for the first reduction of SnTPyP (found from the values taken at pH 2.0 and 3.5) to estimate E red 1/2 of about −0.534 V for SnTPyP at pH 6.9. It is lower in energy than that found for H 2 TPPS 4− 4 at this pH. The oxidation peak could be resolved only for H 2 TTPS 4− 4 at pH 6.9. The oxidation peak of Sn(IV)TPyP is at more positive potentials interfering with the decomposition of the aqueous solutions. The CV of the NS adsorbed overnight on a GCE (washed thoroughly with water before measurements) revealed a broad feature corresponding presumably to the reduction of the Sn(IV)TPyP species at a lower potential window of about −0.6 to −0.4 V (Ag/AgCl). It also revealed a reduction process at a higher energy of about −0.7 V (Ag/AgCl), (Figure 7), presumably corresponding to the reduction processes of the TPPS 4 species. However, it was shown that the redox potentials of the porphyrins may be shifted due to their interactions, e.g., as shown for the porphyrin ion-paired porphyrin dimers (Natali and Scandola, 2016). Altogether, the data suggest that Sn(IV)TPyP can be considered as a molecule with more acceptor properties and TPPS 4 as a molecule with more donor properties in this couple. Indeed, this is in agreement with the fact that the Sn(IV) complex is considered one of the most electropositive metalloporphyrins (Fuhrhop et al., 1973;Koposova et al., 2016a). While it is stable against electrophilic attack, it is very reactive with reducing agents (Fuhrhop et al., 1973). Moreover, the Py substituents of the porphyrin ring have more electron-withdrawing properties than 4-sulfonatophenyl substituents, contributing to lowering the reduction potential of Sn(IV) porphyrins with Py substituents of the macrocycle and the stability of a π-radical anion of Sn(IV)P (Jahan et al., 2012;Koposova et al., 2016a). It is worth mentioning that the CV of the adsorbed nanostructures indicates that the energy levels of individual molecules may be changed in the nanostrucutres, as shown for the porphyrin ion pairs (Natali and Scandola, 2016). Thus, applying this principle to the couple under investigation and based on the cyclic voltammetry data we can assume that photoirradiation may lead to exciton delocalization in the H 4 TPPS 2− 4 -Sn(IV)TPyP 4+ porphyrin nanotubes, where Sn(IV)TPyP porphyrin possesses an acceptor character and H 4 TPPS 2− 4 porphyrin possesses a donor character in this couple, although, the positions of LUMO and HOMO for Sn(IV)TPyP 4+ and H 4 TPPS 2− visible light in a semiconductor range of (3.1 ± 0.9) × 10 −4 S m −1 . The temperature dependence of the photoconductance of the nanotubes showed a metal-like character of decreasing current with increasing temperature. The photocurrent decreased over the µm distances. It was found that excitation of the Q-band region with a Q-band of Sn(IV)TPyP 4+ (550-552 nm) and the J-band of the nanostructures at 714 nm is responsible for about 34% of the photoconductance activity of the H 4 TPPS 2− 4 -Sn(IV)TPyP 4+ -porphyrin nanotubes. The sensor properties of the nanotubes in a chemiresistor mode were tested to demonstrate a perspective of the self-assembled porphyrin nanorods as functional layers for the sensor devices and biomimetic nanoarchitectures.

DATA AVAILABILITY
All datasets generated for this study are included in the manuscript and/or the Supplementary Files.

AUTHOR CONTRIBUTIONS
EK made substantial contributions to design, acquisition, analysis, and interpretation of data, and participated in drafting the article. AO and YE made substantial contributions to conception, analysis, and interpretation of data, and participated in drafting the article. YM made substantial contributions to conception, design, acquisition, analysis, and interpretation of data, and participated in drafting the article. All authors gave final approval of the submitted manuscript.

FUNDING
This research did not receive any specific grant from funding agencies in the public, commercial, or not-for-profit sectors.