{'fraction_non_alphanumeric': 0.037037037037037035, 'fraction_numerical': 0.021164021164021163, 'mean_word_length': 5.376404494382022, 'pattern_counts': {'":': 0, '<': 0, '<?xml version=': 0, '>': 0, 'https://': 0, 'lorem ipsum': 0, 'www.': 0, 'xml': 0}, 'pii_count': 0, 'substrings_counts': 0, 'word_list_counts': {'cursed_substrings.json': 0, 'profanity_word_list.json': 0, 'sexual_word_list.json': 0, 'zh_pornsignals.json': 0}}
Pore-Filled PEMs from Poly(Phenylene Sulfonic Acid)s and Electrospun Poly(Phenylene Sulfone) Fiber Mats

A novel, composite, non-PFSA-based fuel cell membrane has been fabricated using a pore filling technique. The membrane consists of a mechanically stabilizing skeleton from an electrospun poly(phenylene sulfone) (PPSU) fiber mat and a thermally crosslinkable poly(phenylene sulfonic acid) (cPPSA) proton conducting ionomer that fills the interfiber voids. cPPSA copolymer was synthesized using Ullmann coupling copolymerization of 4,4-dibromobiphenyl 3,3-disulfonic acid with 1,4-dibromobenzene-2,5-disulfonic, followed by grafting a certain fraction of backbone sulfonic acid groups with biphenyl linker. The PPSU fiber mat was electrospun from NMP/acetone solution. Pore-filling was carried out by pouring a solution of cPPSA in methanol over the mat, followed by heating at 70oC to evaporate solvent. The cPPSA was crosslinked by an additional heating step, in a vacuum oven at 210oC for 5 hours. The resultant membrane had excellent proton conductivity, 5 times greater than that of Nafion® 211 in the 40-90% RH range at 80oC.