{'fraction_non_alphanumeric': 0.037624221801167784, 'fraction_numerical': 0.021422218785043114, 'mean_word_length': 4.758628367846804, 'pattern_counts': {'":': 0, '<': 0, '<?xml version=': 0, '>': 0, 'https://': 0, 'lorem ipsum': 0, 'www.': 0, 'xml': 0}, 'pii_count': 0, 'substrings_counts': 0, 'word_list_counts': {'cursed_substrings.json': 0, 'profanity_word_list.json': 0, 'sexual_word_list.json': 0, 'zh_pornsignals.json': 0}}
Crystal-phase engineering of PdCu nanoalloys facilitates selective hydrodeoxygenation at room temperature

Selective hydrodeoxygenation of biomass-derived aromatic alcohols to value-added chemical or fuel is of great importance for sustainable biomass upgrading, and hydrodeoxygenation of 5-hydroxymethylfurfural (HMF) to 2,5-dimethylfuran (DMF) is one of the most attractive reactions. Achieving the conversion of HMF to DMF using H2 at ambient temperature is challenging. In this work, we used PdCu nanoalloys to catalyze the selective hydrodeoxygenation reaction of HMF to DMF using H2 as the reducing agent. The reaction path and the product selectivity are governed by the crystallographic phase of the PdCu nanoalloys. It was discovered that body-centered cubic (BCC) PdCu nanoalloys supported on activated carbon (AC) exhibited outstanding performance with 93.6% yield of DMF at room temperature (PdCu/AC-BCC). A combination of experimental and density functional theory (DFT) studies showed that the tilted adsorption modes of furanic intermediates on PdCu-BCC nanoalloy surfaces accounted for the high selectivity of DMF; however, furan ring was activated on PdCu face-centered cubic (FCC) nanoalloy surfaces. Furthermore, PdCu/AC-BCC could also catalyze the hydrodeoxygenation of other aromatic alcohols at room temperature while maintaining the aromatic structures. This work opens the way for selective hydrodeoxygenation of the aromatic alcohols at room temperature with the aromatic ring intact.

Selective hydrodeoxygenation of biomass-derived aromatic alcohols to value-added chemical or fuel is of great importance for sustainable biomass upgrading, and hydrodeoxygenation of 5-hydroxymethylfurfural (HMF) to 2,5dimethylfuran (DMF) is one of the most attractive reactions. Achieving the conversion of HMF to DMF using H 2 at ambient temperature is challenging. In this work, we used PdCu nanoalloys to catalyze the selective hydrodeoxygenation reaction of HMF to DMF using H 2 as the reducing agent. The reaction path and the product selectivity are governed by the crystallographic phase of the PdCu nanoalloys. It was discovered that body-centered cubic (BCC) PdCu nanoalloys supported on activated carbon (AC) exhibited outstanding performance with 93.6% yield of DMF at room temperature (PdCu/AC-BCC). A combination of experimental and density functional theory (DFT) studies showed that the tilted adsorption modes of furanic intermediates on PdCu-BCC nanoalloy surfaces accounted for the high selectivity of DMF; however, furan ring was activated on PdCu face-centered cubic (FCC) nanoalloy surfaces. Furthermore, PdCu/AC-BCC could also catalyze the hydrodeoxygenation of other aromatic alcohols at room temperature while maintaining the aromatic structures. This work opens the way for selective hydrodeoxygenation of the aromatic alcohols at room temperature with the aromatic ring intact.

INTRODUCTION
Production of commodity chemicals from renewable feedstocks has received significant attention as a promising way to diminish our dependence on fossil resources and construct sustainable chemical industries. [1][2][3][4][5][6] Transition-metal-catalyzed hydrodeoxygenation reaction of oxygenated organic compounds has attracted broad interest in recent years because of their important role in biomass feedstock transformation as well as in pharmaceuticals industry. However, selectively activating and cleaving C-O bonds in lignocellulosic biomass is very difficult. On the one hand, the commonly used noble metal catalysts often have strong hydrogenation ability to C=C bonds and aromatic rings, which are ubiquitous in biomass-derived compounds, resulting in undesirable product. On the other hand, in order to obtain high conversion and product selectivity, a high reaction temperature is often required.
The selective hydrodeoxygenation of 5-hydroxymethylfurfural (HMF), which is considered an important biomass platform chemical, to 2,5-dimethylfuran (DMF) is one of the most attractive reactions in biomass transformation. DMF has been identified as a highly interesting candidate of liquid fuel with high energy densities (30 kJ$cm À3 ) and research octane numbers (RON = 119), holding great potential to substitute for petroleum-based gasoline, and can also be converted to valuable benzene-based chemicals via Diels-Alder reactions. [7][8][9][10][11] Various products, such as 2,5-bis(hydroxymethyl)furan (DHMF), 5-methylfurfural (5-MF), 5-methylfurfurylalcohol (5-MFA), 2,5-bis(hydroxymethyl)tetrahydrofuran (DHTHF), 5-methyltetrahydrofuran-2-methanol (MTHFM), 2-hexanol (HOL), and 2,5-dimethyltetrahydrofuran (DMTHF), are produced in the catalytic HMF hydrodeoxygenation reaction as side products, as shown in Scheme S1. Indeed, different catalytic systems have been used for selective hydrodeoxygenation of HMF to DMF. 12 Bimetallic catalytic systems play an important role in improving DMF selectivity by forming core-shell structure, electronic effect between two metals, and providing multiple sites. 13-16 Pt 3 Co 2 nanoparticles were used in transformation of HMF to DMF with 98% yield at 160 C, and it was modeled as an alloy core covered by a Co 3 O 2 monolayer, in which the Co 3 O 2 layer repelled furan rings to prevent further hydrogenation. 17 Similar to Pt 3 Co 2 core-shell structures, near-ambient-pressure X-ray photoelectron spectroscopy (NAP-XPS) suggested that NiCu 3 nanocrystals involve a Cu-rich core and a 1:1 molar Ni: Cu shell, which exhibited a DMF yield of 98.7% at 180 C. 14 One-hundred percent HMF conversion and 92.9% selectivity to DMF were obtained over Co-alloyed Pt single-atom catalysts under 1.0 MPa H 2 at 180 C, where Pt sites were responsible for H 2 activation and Pt dÀ -Co d+ sites activated C-O bonds. 16 Cobalt and copper bimetallic catalyst on N-graphene-modified Al 2 O 3 could efficiently catalyze the selective hydrodeoxygenation of HMF to DMF at 180 C, and the catalytic performance resulted from the synergistic effect between defects and active metal. 18 Co@Cu/3CoAlO x sequentially catalyzed the C=O hydrogenation and C-OH hydrogenolysis to yield as high as 98.5% DMF at 180 C. 19 It is generally accepted that crystallographic phases of nanoalloy catalysts could also affect the catalytic performance. However, synthesizing nanoalloys with specific crystallographic-phase catalysts to improve the selectivity of hydrodeoxygenation reaction of HMF has not yet been reported. More importantly, although satisfactory DMF yield has been obtained over the catalytic systems that have been reported, the harsh reaction conditions required usually cause serious issues and thus limit their practical applications. It is urgent to explore an efficient catalytic system to achieve the conversion of HMF to DMF under mild conditions, especially at room temperature.
Cu-Pd/reduced graphene oxide could catalyze the selective hydrogenation of HMF to DMF using 2-propanol as the reducing agent. 20 Hydrogen is an ideal reducing agent. However, when hydrogen was used as the hydrogenation agent, only Pd-based catalysts could catalyze the selective hydrodeoxygenation of HMF to DMF at temperatures lower than 100 C, but the addition of acid as promoter is necessary. 21 For example, 96% yield of DMF was obtained over PdAu/C catalyst at 60 C in the presence of HCl. In this work, we synthesized PdCu nanoalloys and achieved the selective hydrogenation reaction of HMF to DMF at ambient temperature using H 2 as the reducing agent. It was discovered that the synthesized body-centered cubic (BCC) PdCu nanoalloys supported on activated carbon (AC) (i.e., PdCu/AC-BCC) displayed outstanding performance for hydrodeoxygenation reaction, with a DMF yield of 93.6% at room temperature. The crystallographic phase of PdCu nanoalloys governed the selectivity of the hydrogenation of HMF. The hydrogenation of furan ring was dominating over face-centered cubic (FCC) PdCu nanoalloys supported on AC (PdCu/AC-FCC) with low selectivity toward DMF. Density function theory (DFT) studies showed that the loose arrangement of surface atoms in PdCu-BCC repelled furan rings, while ring adsorptions were favored by close-packing PdCu-FCC surfaces. Moreover, PdCu/ AC-BCC could also catalyze the hydrodeoxygenation of other aromatic alcohols at room temperature while maintaining aromatic structures.

RESULTS
The PdCu/AC-BCC catalyst was synthesized by an impregnation-reductioncalcination method, the details of which are shown in the section "materials and methods." Figures 1A and S1 show the transmission electron microscopy (TEM) images of the as-prepared PdCu/AC-BCC. Uniform nanoparticles with average diameter of 4.8 nm were immobilized over the AC support. Figure 1B gives an aberration-corrected high-angle annular dark-field (HAADF) scanning  Figure 1C), which is confirmed by the corresponding energy dispersive spectroscopy (EDS) elemental mapping images ( Figure 1D). Inductively coupled plasma atomic emission spectroscopy (ICP-AES) analysis showed that PdCu/ AC-BCC contained 0.54 wt % Pd and 0.31 wt % Cu; i.e., the Pd/Cu atomic ratio was about 1:1. Additional TEM images of PdCu/AC-BCC reveal the uniformity of PdCu nanoalloys ( Figure S2). For comparison, FCC-structured PdCu nanoalloys (PdCu/AC-FCC) at an annealing temperature of 200 C were prepared (using the same precursor and composition as that for PdCu/AC-BCC; see section "materials and methods"). Figure S7 gives the HAADF-STEM image taken from a typical individual PdCu nanoparticle in the PdCu/AC-FCC, which demonstrates the formation of nanoalloy with lattice spacing of 1.99 Å, and the result was consistent with the value of (100) plane of PdCu-FCC nanoalloys. Furthermore, the PdCu nanoalloys crystalline structure was also characterized by X-ray diffraction (XRD) and the results are shown in Figure S8. No obvious diffraction peaks of metallic PdCu were observed in the PdCu/AC-FCC and PdCu/AC-BCC catalysts, mainly because of ultra-small size and good dispersion of the nanoalloys. To get more information about the crystal structure, the PdCu nanoalloys without support were prepared and characterized by XRD ( Figure S8). The XRD peaks of PdCu nanoalloys without support annealed at 200 C can be indexed as FCC structure. The PdCu-BCC (110) and (100) peaks at 42.9 and 62.2 are clearly visible in Figure S8 for the PdCu nanoalloys annealed at 400 C, suggesting the formation of PdCu-BCC structure. Similarly, the results were obtained on the PdCu/AC 10 wt % indicating that the crystal structure can be tuned by the simple annealing treatment ( Figure S9). 22,23 The XPS technique was used to study the electronic structure of Pd and Cu components in different catalysts ( Figure 2). Compared with Pd/AC, PdCu/AC-BCC showed reduced binding energies for Pd 3d, i.e., 341.0 eV (Pd 3d 3/2 ) and 335.7 eV (Pd 3d 5/2 ), suggesting that Pd was slightly negative charged in PdCu/ AC-BCC ( Figure 2A). Likely, Pd receives the electron from Cu in the nanoalloys. The Cu 2p peak exhibits 0.5 eV shift toward higher binding energy in reference to mono-metallic Cu/AC catalyst ( Figure 2B), confirming electron transfer from Cu to Pd. Thus, the addition of Cu to Pd results in enrichment of electron density on Pd, showing the strong electron interaction between Pd and Cu. A similar phenomenon was found in the XPS of PdCu/AC-FCC ( Figure S10). The valence of Cu was further determined by LMM Auger spectra ( Figure S11). Despite the poor signal-tonoise ratio, it can be found that Cu L 3 M 4,5 M 4,5 peak locates in 918 eV, indicating the existence of metallic Cu compared with reported results. 24 The amount of Cl and B in PdCu/AC-BCC were evaluated by ICP mass spectrometry (ICP-MS), both of which were less than 0.01 wt %. Also, XPS showed no residual Cl and B in PdCu/AC-BCC ( Figure S12).
The performance of various catalysts for the hydrodeoxygenation of HMF at different temperatures was studied (Table 1). No target product was formed without any catalysts ( Table 1, entry 1), and AC was inactive in the reaction (Table 1, entry 2). The activity of AC-supported Pd nanoparticles catalyst (Pd/AC, with a similar Pd loading to that of PdCu/AC-BCC) was very low and the yield of DMF was only 6% at 30 C ( Table  1, entry 3). Similarly, AC-supported Cu (Cu/AC) was inactive for the reaction (Table 1, entry 4). To our surprise, a very high DMF selectivity of 93.6% was observed over PdCu/AC-BCC (Table 1, entry 5). These results indicated PdCu/AC-BCC was an outstanding catalyst for hydrodeoxygenation of HMF. The reason for the excellent performance is discussed in the following sections. Interestingly, increasing the reaction temperature to 100 C increased the reaction rate of PdCu/AC-BCC (71.2 h À1 ; Table 1, entry 6), which is much higher than those in previous reports at similar reaction conditions (Table S1). At 160 C, the yield of DMF could reach 97.2% (Table 1, entry 7), demonstrating that further hydrogenation to the furan ring was still inhibited at high temperature. Moreover, the hydrodeoxygenation of HMF to DMF could be carried out under atmospheric pressure and room temperature over PdCu/AC-BCC, and the yield of DMF reached 38.6% (Table 1, entry 8). These results verified that PdCu/AC-BCC is an excellent catalyst for selective hydrogenation of HMF at low temperature. The effect of H 2 pressure and initial HMF concentration were also checked and the results are shown in Table S4. The conversion and DMF yield increased as hydrogen pressure while decreasing as initial HMF concentration (Table S4, entries 1-5). The catalyst loading also affected the catalytic performance and, when the catalyst loading was 0.5 wt %, the HMF conversion and DMF yield were only 56% and 52%, respectively (Table S4, entries 6 and 7).
Very interestingly, the selectivity of DMF depended strongly on the crystallographic phase of PdCu nanoparticles in the catalysts ( Figure 3A and Table S2). The PdCu/AC-BCC catalyzed the hydrodeoxygenation reaction selectively with 93.6% selectivity of DMF. However, the PdCu/AC-FCC promoted the hydrogenation of the furan ring with only 9.0% selectivity to DMF under the same reaction conditions. The effect of reaction time over the PdCu/AC-BCC is shown in Figure 3B. Clearly, for PdCu/AC-BCC, the conversion of HMF increased with the increase of reaction time, reaching a full conversion at around 16 h at 30 C. The selectivity toward DMF of PdCu/AC-BCC increased with the increase of reaction time and reached 93.6% after 20 h, because DMF was formed via intermediates. At a reaction of 20 h, besides DMF and trace amounts of other products, only about 5% DHTHF was detected. Even after the reaction time was extended to 24 h, DMF was not hydrogenated to DMTHF, demonstrating that PdCu/AC-BCC was capable of selectively catalyzing the designated reaction rather than the deep hydrogenation of furan rings to undesired products. As shown in Table S7, the carbon balances of the reaction at different reaction times were all above 94%.
Different from that of PdCu/AC-BCC catalyst, the main product was DHMF with only 18% yield of the desired product DMF, although the conversion of HMF could reach 99.9% in 4 h over PdCu/AC-FCC ( Figure S13). DHTHF became the dominant product with the prolonging reaction time, indicating that DHMF was converted to DHTHF. DMF, MTHFM, 5-MFA, and 5-MF were also detected. The yield of DMF decreased to 8% in 24 h and it was further hydrogenated to DMTHF. These results suggested that the reaction pathways over PdCu/AC-FCC include the hydrogenation of the furan ring and the hydrodeoxygenation reaction. Furthermore, the total yield of DHTHF and DMTHF was much higher than DMF. Throughout the reaction process, no single product could reach a selectivity higher than 50%, showing that PdCu/AC-FCC is not a highly selective catalyst for the hydrodeoxygenation of HMF. To verify the result for the high selectivity to DMF, control experiments using DMF as the substrate were conducted (Table S3). Notably, under the similar reaction conditions, while DMF was fully converted to DMTHF through the hydrogenation of furan ring over PdCu/AC-FCC, the hydrogenation of DMF was almost completely blocked over PdCu/AC-BCC, confirming that the lattice structure of PdCu is responsible for its selectivity. The support also affected the catalytic performance, and PdCu-BCC and PdCu-FCC are inactive for the reaction (Table S5).  Also, no HMF conversion and DMF yield was obtained over PdCu/TiO 2 and PdCu/Al 2 O 3 . As shown in Figure S29, the average sizes of PdCu nanoparticles loaded on Al 2 O 3 and TiO 2 all were above 10 nm, much larger than those in 1 wt % PdCu/AC-BCC, which led to inactivity. Furthermore, The XRD in Figure S9 suggested that the PdCu-FCC phase still existed in the catalyst 10 wt % PdCu/AC-BCC. The hydrogenation of furanic ring was dominant over 10 wt % PdCu/AC-BCC since the FCC-phase PdCu nanoparticles had higher hydrogenation activity than the BCC phase (Table S8).
The DFT calculations were performed to investigate the origin of crystallinephase-controlled selectivity. According to the literature and AC-STEM results, (100) and (111) surfaces were built to represent the exposed facets of PdCu-FCC and BCC nanoparticles ( Figures 4A, S15, and S16). 25 The distance between metal atoms on the top layer in PdCu-BCC is longer than that in PdCu-FCC, which coincides with AC-STEM characterizations. It has been reported that the adsorption modes of HMF were highly sensitive to the microstructure of catalytic surfaces, and it further determined reactants' transformation. 26 Two kinds of adsorption configuration, h adsorptions and s adsorptions, as noted in Figures 4B and  4C, were under discussion in our calculations. The interaction of HMF with PdCu surface involves the h-adsorption modes mainly via the oxygenated pendant functions (aldehyde and hydroxyl groups), while, in s-adsorption mode, the furan ring lies flat on nanoalloy surfaces, as shown in Figure 4C. It is worth noting that dissociated adsorption modes were not taken into comparison. Besides the reactant HMF and the product DMF, the adsorptions of DHMF and MFA as key intermediates during hydrodeoxygenation were explored and the most stable adsorption structures are presented in Figures S17-S20.
HMF adsorbed on BCC (111) and FCC (100) surfaces via s-adsorption modes with À1.00 eV and À0.71 eV, respectively, both of which were stronger than corresponding h-adsorption modes in Figure S17. Although both furan ring and aldehyde group in HMF were activated in s-adsorption mode, either on PdCu-BCC or -FCC, the aldehyde group was first hydrogenated to produce DHMF in our experiment. This is also consistent with the results reported in the literature. 17,18 A discussion of the reaction path of HMF hydrogenation and hydrodeoxygenation over PdCu-BCC below further demonstrates this in theory. When DHMF adsorbed on the same PdCu-BCC surface, the h configuration was favored, and the furan ring was not activated in h adsorption of DHMF. While on PdCu-FCC, DHMF preferred to be adsorbed in s-adsorption configuration, 0.43 eV stronger than its h adsorption. The furan ring was activated in s adsorption on FCC (100), due to the formation of new metal-carbon bonds and the partial rehybridization of ring carbon atoms from sp 2 to sp 3 , which had been reported wildly. 17,27,28 The present chemical interactions between furan rings and FCC (100) surfaces promoted the ring hydrogenations and explained the ring reactivity of PdCu-FCC. The adsorptions of MFA and DMF were also explored both on PdCu-FCC and -BCC, and the results were similar to that of DHMF. MFA s adsorption with ring activation was favored on PdCu-FCC, yet on PdCu-BCC the ring activation was inhibited by h adsorption ( Figure S19). DMF, precluding oxygenated pendant functions, adsorbed on PdCu-BCC (100) surface weakly (À0.33 eV adsorption energy), then the furan ring remained intact. The furan ring in DMF was activated and vulnerable to hydrogenation in s adsorption on FCC (100) with À0.45 eV adsorption energy. Thus, different ring hydrogenation reactivity over PdCu-FCC and PdCu-BCC could be attributed to the different adsorption behaviors of furan rings on these surfaces with corresponding adsorption sites.
The reaction pathway of HMF hydrogenation and hydrodeoxygenation over PdCu-BCC was also confirmed with DFT computations (Figures 5, S22, and S23). The H 2 dissociation barrier was calculated as about 0.2 eV (Figure S21), consistent with previous calculations. 29 Due to the low H 2 dissociation barrier, in the following steps the hydrogen atoms were assumed to adsorb on the surface directly. Hydrogenation of the carbonyl group first takes place on the C atom,   The loose arrangement of surface atoms with PdCu-BCC repelled furan rings of hydrogenation intermediates, while ring adsorptions were favored by close-packing PdCu-FCC surfaces. Our work opened a new insight into the selective hydrogenation of biomass-derived furanics catalyzed by bimetallic nanoparticles. We also investigated the hydrodeoxygenation of other aromatic alcohols, and the results are presented in Table S6. PdCu/AC-BCC could catalyze the hydrodeoxygenation of a series of substrates under mild conditions with high conversions and excellent selectivities to the desired products with the aromatic rings intact.
The recyclability of PdCu/AC-BCC catalyst was evaluated at 100 C and the activity of the catalyst slightly decreased after recycling four times ( Figure S14). As shown in Figure S3, the average diameter of PdCu/AC-BCC after reaction was 5.0 nm, which is similar to the fresh PdCu/AC-BCC catalyst, thus no significant sintering was observed. Also, EDS mapping shows no segregation of Pd or Cu after reactions ( Figure S4). The crystallographic phase was characterized by high-resolution TEM (HRTEM), and the d-spacing of PdCu nanoalloys after reaction was 2.14 Å, corresponding to PdCu-BCC (111) facets, which means that the BCC phase of PdCu was not changed after reaction. Maybe the decrease in catalyst activity is attributed to the inevitable loss of catalyst in the recovery process, since only 16 mg of PdCu/AC-BCC (80% of the original amount) was recovered Report after the fourth run. It can be proved that the yield of the product was nearly the same as that of the first run when 0.24 mmol of HMF (80% of the amount of the first run) was added in the fifth run.

DISCUSSION
In summary, we reported that the introduction of Cu into Pd could tune the electronic structure of Pd through the electron transfer from Cu to Pd. This electronic structure feature greatly promoted the catalytic activity of PdCu nanoalloys for the hydrodeoxygenation of HMF at room temperature. The crystallographic phase of PdCu nanoalloys had a significant impact on their selectivity in the hydrogenation of HMF. On PdCu/AC-BCC, a 93.6% yield toward the desired DMF product could be reached even at room temperature. The lower energy barrier of hydrodeoxygenation of C-OH and C=O than that of furan hydrogenation over PdCu/AC-BCC resulted in the high selectivity of DMF. However, PdCu/AC-FCC preferred to promote the hydrogenation of furan ring with low DMF selectivity. We believe that the PdCu/AC-BCC catalyst has great potential for applications due to its obvious advantages, such as extremely high activity and selectivity, and being easy to prepare. In addition, the findings of this work are useful for designing other efficient catalysts for selective hydrogenation of compounds with two or more unsaturated bonds.

Methods
The PdCu/AC catalysts were synthesized via the co-reduction method and were then annealed at a controlled temperature. In a typical experiment, 0.2 g of AC was dispersed in 50 mL of ultrapure water with sonication for 3 h to get a well-dispersed AC suspension.
Then, 5.0 mL of aqueous solution containing CuCl 2 and H 2 PdCl 4 (with molar ratio of Cu 2+ :Pd 2+ = 1:1) was mixed with AC suspension in an ice water bath. Then fresh aqueous solution containing NaBH 4 was added drop-wise with continuous magnetic stirring under argon atmosphere, and the reaction solution was kept stirring for 3 h to complete the reduction reaction. The obtained black granules were collected by centrifuging and washing with ultrapure water three times (3 3 30 mL) and ethanol twice (2 3 30 mL) and dried in a vacuum oven at 60 C for 12 h. The ground powder was calcined in a tube furnace (Anhui Kemi Machinery Technology; model TFV-1200-50-I-220) for 4 h (reducing gas contains 10 vol % hydrogen and 90 vol % argon) to obtain PdCu/AC. The PdCu/AC-FCC and PdCu/AC-BCC were obtained at annealing temperatures of 200 C and 400 C, respectively. The synthetic conditions for Pd/AC and Cu/AC were similar to those of PdCu/AC-BCC except for changing the ratio of Pd 2+ :Cu 2+ . PdCu/TiO 2 and PdCu/Al 2 O 3 were synthesis with the same method as PdCu/AC-BCC.

Characterization
The TEM and EDS images of the catalysts were obtained using a JEOL-2100F and JEM-200F electron microscope operated at 200 kV. JEM ARM300F equipped with an EDX detector (JEOL) and an energy filter (GATAN) operated at 300 kV was used for aberration-corrected HAADF-STEM images. The XPS measurements were carried out on an ESCALAB 220i-XL spectrometer at a pressure of $3 3 10 À9 mbar (1 mbar = 100 Pa) using Al Ka as the excitation source (hn = 1,486.6 eV) and operated at 15 kV and 20 mA. The binding energies were calibrated with the C1s level of adventitious carbon at 284.8 eV as the internal standard reference. The XPS samples were prepared without exposure to the air. The XRD experiment was performed on Rigaku D/ max 2500 with nickel filtered Cu-Ka (l = 0.154 nm) operated at 40 kV and 20 mA. The contents of different elements in the PdCu/AC catalysts were analyzed by ICP-AES.