{'fraction_non_alphanumeric': 0.07154340836012862, 'fraction_numerical': 0.03617363344051447, 'mean_word_length': 4.684931506849315, 'pattern_counts': {'":': 0, '<': 0, '<?xml version=': 0, '>': 0, 'https://': 0, 'lorem ipsum': 0, 'www.': 0, 'xml': 0}, 'pii_count': 0, 'substrings_counts': 0, 'word_list_counts': {'cursed_substrings.json': 0, 'profanity_word_list.json': 0, 'sexual_word_list.json': 0, 'zh_pornsignals.json': 0}}
High-temperature proton-exchange-membrane fuel cells using an ether-containing polybenzimidazole membrane as electrolyte.

Herein, poly[2,2'-(p-oxydiphenylene)-5,5'-benzimidazole] (PBI) is synthesized from 3,3'-diaminobenzidine and 4,4'-oxybisbenzoic acid, and the membrane is prepared by solvent casting. The main characteristics of PBI are studied. In the preparation of the PBI/H(3) PO(4) composite membrane, the absorbing temperature of H(3) PO(4) is 120 °C, which leads to a membrane with a high content of H(3) PO(4) . Membrane electrode assemblies (MEAs) are fabricated from PBI/H(3) PO(4) membranes with the catalyst layer made of Pt/C, PBI, and polyvinylidene fluoride (230:12:7 w/w). The fabricated MEA is tested at 150 °C with dry hydrogen and oxygen gas at 0.2 MPa for both anode and cathode feeds. No degradation of voltage is seen during stability testing of the PBI/H(3) PO(4) membrane at a constant current for 100 h. The maximum power density is 1.17 W cm(-2) , and the maximum current density is 6.0 A cm(-2) with a Pt loading of 0.5 mg cm(-2) . The high performance of these membrane materials demonstrates that PBI can be regarded as an alternative membrane material for high-temperature proton-exchange-membrane fuel cells.