{'fraction_non_alphanumeric': 0.029290768471285172, 'fraction_numerical': 0.016661181504031595, 'mean_word_length': 5.023042616451932, 'pattern_counts': {'":': 0, '<': 0, '<?xml version=': 0, '>': 0, 'https://': 0, 'lorem ipsum': 0, 'www.': 0, 'xml': 0}, 'pii_count': 0, 'substrings_counts': 0, 'word_list_counts': {'cursed_substrings.json': 0, 'profanity_word_list.json': 0, 'sexual_word_list.json': 0, 'zh_pornsignals.json': 0}}
Synthesis and Characterization of a Chitosan/PVA Antimicrobial Hydrogel Nanocomposite for Responsive Wound Management Materials

Copyright: © 2016 Rinehart SJ, et al. This is an open-access article distributed under the terms of the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original author and source are credited.


Introduction
Hydrogels are networks of hydrophilic polymers that form welldefined three dimensional structures that are ideal for modification and functionalization [1]. The water insolubility of hydrogels and high swelling capability has led to their use in the design of biomaterials for applications such as tissue engineering, drug release systems, and wound management materials [2][3][4][5][6][7][8]. Hydrogels made from natural biopolymers are ideal for biomaterial applications owing to their intrinsic properties such as non-cytotoxicity and biodegradability [9,10]. Chitosan, which is a biopolymer produced as a byproduct of crustacean shells, is widely used as a backbone of hydrogels for such applications. In addition to the aforementioned properties, chitosan is often sought out for use in antimicrobial hydrogels for its inherent antibacterial property [11,12]. Although there has been extensive work highlighting the advantages of chitosan hydrogels, there are still some functional limitations.
The use of chitosan alone has shown to limit the mechanical strength of the hydrogel during swelling [13]. It has been reported that polymer blending can be used to improve physicochemical properties such as mechanical strength [14][15][16]. For example, Yang et al reported that chitosan based hydrogels cross-linked with polyvinyl alcohol (PVA) showed an increased mechanical strength compared to their chitosan only counterparts [14]. This and related work has led to the development of structurally stable hydrogels for many applications.
In recent years, significant attention has been focused on the use of chitosan based hydrogels for burn wound management [17][18][19]. Chitosan-based hydrogels are biocompatible, can maintain a moist healing environment that provides a scaffold for cell growth while acting as a protective barrier from microorganisms to prevent secondary infections. Furthermore, they have shown to assist in absorbing excess wound exudates, meeting the requirements of an ideal wound dressing [19][20][21]. In efforts to increase structural rigidity and improve the antimicrobial efficiency (AME) without compromising the biocompatible integrity of these hydrogels, many studies have focused on the integration of antimicrobial silver (Ag) and Ag functionalized semiconductor particles into their matrices [22,23].
Ionic Ag and Ag-based compounds have been widely accepted as bacterial growth inhibitors since the 19th century due to their notable biocidal properties against several types of bacteria, including Escherichia coli and Staphylococcus aureus [24][25][26]. However, Ag + can be difficult to uniformly distribute throughout the hydrogel matrix. Therefore, Ag coated semiconductor particles offer an alternative incorporation approach. When a solid support, such as titanium dioxide (TiO 2 ), functionalized with Ag is placed in a suspension, the Ag + released from the surface can kill bacteria [27,28]. This allows for the gradual release of Ag + , which has shown to increase the longevity

Abstract
The development of novel wound management materials must address several challenges to be most efficacious. Successful wound management should include the ability to adhere to wound surfaces, absorb wound exudates, and enhance bactericidal effectiveness. Few current biomaterials address all of these characteristics and in addition often have poor structural rigidity leading to a lack of protection and support to ensure proper cell growth. The focus of this study was to develop a multifunctional biomimetic nanocomposite system that will improve mechanical stability, effectively eliminate E. coli and S.aureus biofilm propagation, and serve as a scaffold for effective adult human dermal fibroblast (HDFa) growth. Synthetic parameters, such as the ratio of chitosan to PVA concentration and deposition method for the incorporation of Ag + -functionalized nanoparticles into the final nanocomposite, were optimized. It was determined the deposition reaction pH and Ag + concentration played a key role in the control of post reaction particle size and zeta potential. It was also determined that the concentration of Ag + functionalized nanoparticle incorporated into the nanocomposite must be greater than 5 mM to achieve optimal control of biofilm formation. The prepared hydrogel nanocomposites demonstrated effective bacterial inhibition when exposed to cultures of E. coli, S. aureus, and MRSA. Lastly, human dermal fibroblast test results revealed that when PVA concentration increased in the system, there was no appreciable cell growth. On the other hand, when the ratio of biomimetic chitosan and PVA is optimized to reduce the overall amount of synthetic polymer (PVA), there was healthy cell growth. These results directly speak to a key finding that reveals the importance of the correct balance or the removal of synthetic polymer from the system. of the substrate. The application of this ideology to current hydrogel technology can allow for the development of burn wound management materials with increased rigidity and sustainability. This paper reports the synthesis and characterization of a nanocomposite chitosan/PVA hydrogel matrix coupled with photochemically prepared antimicrobial nanoparticles (Ag/TiO 2 ). The addition of Ag-functionalized nanoparticles to the hydrogel matrix has shown to improve structural rigidity without compromising the rate of fluid uptake (i.e. swellabilty) as well provides a site for controlled release (i.e. no static ion leaching) of Ag + necessary for bacterial disinfection. Upon optimization of the synthetic parameters (i.e. balance of biopolymer and synthetic polymer) the nanocomposite has shown excellent biocompatibility with human dermal fibroblasts.

Pre-coated Nanoparticle Synthesis
Modification to a previously reported method were used to prepare Ag-functionalized TiO 2 nanoparticles by irradiating suspended TiO 2 in aqueous solution with ultraviolet light (UV) to reduce Ag + onto the TiO 2 surface. Ethanol (ETOH) was added to the system to fill the electron hole and prevent charge recombination. Aeroxide® anatase (80%) TiO 2 nanoparticles (Evonik Industries) with an approximate diameter of 25 nm were used as the core particle for all systems presented in this work. Nanoparticle dispersions, in water, were prepared by adding 0.1 wt.% TiO 2 and 1.0 wt.% ethanol to a 250 mL Pyrex flask. The resultant dispersion was ultrasonicated (Branson Instruments) for 30 minutes to break up any weak aggregates that may have occurred upon core nanoparticle addition. The post-sonication dispersion was transferred to a 500 ml 3-neck Pyrex round bottom flask and placed in the photoreactor chamber (Luzchem) with an irradiation wavelength centered at 254 nm. A second solution containing the desired concentration of Ag + (1 mM, 5 mM, 10 mM) was prepared and placed into a separatory funnel fixed above the round bottom flask. The solution was allowed to slowly drip (approximately 3.0 mL/min) into the reaction vessel while exposed to UV light under constant nitrogen purge for 1 hour. After reaction, the particles were dialyzed for 48 hours using dialysis tubing with a molecular weight cutoff 12,000-14,000 (Carolina Supplies) to remove any unreacted Ag + . Using Dynamic Light Scattering (DLS) (Malvern Instruments) the average particle size was determined (post-reaction/post-dialysis) for a representative sample (3.0 ml) of photo-reacted nanoparticle dispersion. Additionally the isoelectric point was determined via pH sweeps (adjusted with 0.05M HNO 3 and 0.1M NaOH) and the zeta potential (approximately 1 ml sample) was measured at each condition using the Malvern Zetasizer (Malvern Instruments).

Nanocomposite Hydrogel Synthesis
Due to solubility limitations of both chitosan and PVA, 2.0 wt.% stock solutions were prepared in 4% aqueous acetic acid. The nanocomposite hydrogels were prepared by adding 0.01% TiO 2 as a substrate for the photo-reduction of Ag to varied ratios of the stock solutions (10:90, 15:85, and 20:80 chitosan:PVA) and treated in an ultrasonic bath (Branson Instruments) for 30 minutes to break up any aggregates. The chitosan solution was then added to the PVA/TiO 2 dispersion and stirred for 15 minutes. A 1 mL aliquot of glutaraldehyde was slowly added to the PVA/chitosan/TiO 2 mixture to promote the effective crosslinking of the nanocomposite hydrogel matrix [30,31]. Upon standing for 10 minutes, the gel-like dispersion was poured into a petri dish and allowed to set for 24 hours. The resultant gel was washed with 12% NaOH followed by deionized water and dehydrated in a furnace at 140ºC until dry.
After dehydration, gel samples are photo-reacted in-situ using 10 mM silver nitrate (AgNO 3 ) with two different methods. The first method involves soaking the gel samples in Ag for 30 minutes and then photo-reacting for an additional 30 minutes. The second method involves soaking the gel samples in AgNO 3 while simultaneously photo-reacting for 30 minutes under a constant a nitrogen (N 2 ) purge. The Ag coated gels are stored in a freezer to prevent from hardening.

Swelling studies
The fluid absorbing capacity (swellability) of the hydrogel is one of the important criteria for maintaining a moist wound environment. The initial mass of the as prepared hydrogel nanocomposite will be recorded and a 2 cm in size hydrogel disk will be placed in aqueous media. The hydrogel will be exposed to the fluid under different conditions (pH, time, temperature) that will attempt to mimic the physiological environment of the wound. The hydrogel absorbing capacity or degree of swelling (DOS) will be calculated using the following equation: where W 0 and W t are the weights of the nanocomposite before exposure to buffer solution and the weight of the swollen nanocomposite. Observation of the DOS as a function of time at controlled temperature the equilibrium concentration as well as the rate of swellability can be determined.

Antimicrobial testing
Cultures of both E. coli (ATCC-25922) and S. aureus (ATCC-6538) were grown at 37°C in a standard tryptic soy broth (TSB) to an optical density (OD 660 ) of 0.5. Each liquid bacterial culture was then aseptically swabbed onto a Mueller-Hinton (MH) Agar plate, and sections of each hydrogel (approximately 1.0 cm 2 ) were then placed onto each plate. Following incubation for 18 hours at 37°C, the zone of inhibition (ZOI) around each hydrogel was measured to quantify AME.

Cell culture
Adult human dermal fibroblasts (HDFa) were routinely maintained in 25 cm 2 flasks in supplemented medium 106 with LSGS Kit (Invitrogen) containing 10 ml of fetal bovine serum (FBS), 1.5 µg/ml recombinant human basic fibroblast growth factor/5 mg/ml heparin, 1 mg/ml hydrocortisone, 1 ml gentamicin/amphotericin B, 5.0 µg/ml recombinant human epidermal growth factor and kept at 37°C in a 5% CO 2 /95% air humidified incubator. Initial seeding was done following the determination of viable cell density. A seeding density of 5 × 10 3 viable cells/cm 2 was confirmed by combining 5 µl of HDFa cells with 5 µl of trypan blue (Invitrogen) into a hemacytometer. The contents of the cell vial (1.0 ml) was diluted to a concentration of 2.5 × 10 4 viable cells/ml using the supplemented medium 106. 5 ml of cell suspension was placed into four 25 cm 2 flasks, swirled to distribute cells evenly and left undisturbed for 72 hours at 37°C in a 5% CO 2 /95% air humidified incubator.
Culture medium was changed every other day until cells reached 80% confluency. At that time cells were subcultured by removing all medium from the flasks and rinsing with 5 ml of Dulbecco's Phosphate Buffered Saline (DPBS, Invitrogen) without calcium and magnesium. Following removal of DPBS, 3 ml of TRYPLE Express with phenol red (TrypLE) was added to flasks and placed in incubator for 10 minutes to remove cells. After all cells were dislodged, 5 ml of medium 106 was added to flasks and the entire volume was collected in a 50 mL conical tube. Cell suspension was spun at 100 × g for 9 minutes forming a cell pellet. The supernatant was discarded and the cells were re-suspended with fresh medium 106. Concentration of viable cells was determined; cells were diluted and placed in new 25 cm 2 flasks.
After four successful passages, cells were subcultured (above) and placed into a flask that contained one of twenty-four different unlabeled biomimetic hydrogels or no hydrogel (control). This was repeated 3 times for each hydrogel. The flasks were returned to the incubator and left undisturbed for 24 hours. After 24 hours, cell growth was examined using a Nikon Eclipse TS100 inverted fluorescent microscope. A live/ dead cell imaging kit 488/570 (Molecular Probes, Invitrogen) was used to assess cell viability in the flask and in proximity to the hydrogel. Equal amounts of Live Green and Dead Red vials were added to an equal amount of cells and incubated for 15 minutes.

Effect of Reaction pH on Ag-functionalized Nanoparticle Size
Synthetic modulation of the Ag-functionalized nanoparticle size is a critical attribute with respect to hydrogel matrix stability and the overall AME. It is believed the size of the nanoparticle will play a major role in the hydrogen-bonding network formation that is essential for the hydrogel matrix to exhibit the desired structural properties as well as the ability to achieve the desired swelling efficiency. Previous work has also suggested that smaller nanoparticles exhibit enhanced antimicrobial properties as a function of the effective surface area available for bacteria cell interactions. Figure 1 is a summary of the effect of reaction pH on the size of the Ag-functionalized nanoparticle after photo-deposition and post-dialysis. As pre-reaction pH of the dispersion increases the surface charge of the core TiO 2 nanoparticle approaches its soelectric point (measured in reaction mixture to be pH=5.3), which results in the charge destabilization of the core particle and the subsequent formation of aggregates of the functionalized particle. At lower pH there is significant charge repulsion of the core particles, which modulates the degree of aggregation and results in lower average particle size post-reaction. While lower pH is desired for the formation of smaller post-reaction particles the ability of the deposited Ag 0 to undergo dissolution to Ag + in the acidic media is possible. In order to control this effect the post-reaction dispersion underwent dialysis (48-hours) in neutral pH=6.0 deionized water to neutralize the acidic environment and quench the ability of the deposited Ag 0 to ionize. Figure 1 clearly indicates that the pH=2.5 reaction condition shows little deviation between the post-dialysis and post-reaction particle size. Validation of the aggregation effect can be seen at the pH of 5.5 condition where there is severe aggregation of the particle post-dialysis indicating reduced Ag surface coverage that results in the ability of the core nanoparticles to form large aggregates.

Effect of [Ag + ] on Ag-functionalized Nanoparticle Size
Using the desired reaction conditions (pH=2.5 and 48-hour dialysis) the effect of pre-reaction Ag + concentration was evaluated to determine its effect on particle size and the isoelectric point of the functionalized particle. The results indicate that the particle size increases slightly upon the deposition of 1 mM Ag and trends upward as a function of concentration (5 and 10 mM). This clearly shows that upon irradiation in the presence of Ag + the surface of the core TiO 2 nanoparticle is being modified. As increased amounts of Ag + are added to the reaction mixture there is apparent surface saturation reached which may result in a slight increase of postreaction particle aggregation. To further validate Ag-functionalization on the surface of the core TiO 2 nanoparticles the isoelectric point of the post-dialysis dispersions were measure and compared against a naked TiO 2 nanoparticle. The results in Table 1 validate that as deposition onto the surface of the core nanoparticle occurs there is a shift in the isoelectric point as a function Ag concentration increased. Adding Ag to the surface of TiO 2 changes the surface structure of the core particle, which results in the observed isoelectric point shifts. Additionally these results support the surface saturation hypothesis at 5 mM because there is a minimal isoelectric point shift demonstrating no further Ag was deposited. Based on this result it was determined that the optimal [Ag + ] for particle size balance is centered on the 5 mM region.

Antimicrobial Efficiency (AME) of Ag-functionalized Nanoparticles
Disk diffusion tests were conducted using the optimal synthetic pathway to determine the effect of pre-reaction [Ag + ] on the effective ZOI. As previously stated, Ag-functionalized nanoparticle samples were pressed into uniform pellets, placed over a bacteria-coated plate, and incubated for 18 hours. Figure 2 is a summary of the ZOI for cultures of E. coli and S. aureus as a function of Ag concentration. It must be noted that the functionalized nanoparticle size for the various concentrations remained relatively constant as to decouple the size and concentration effects. Against both bacteria, there appears to be a clear increase in the ZOI from the naked nanoparticle versus the addition of 1.0 mM Ag to the particle. This is further validation of the claim that  0" 292" ± "15" 5.3" ± "0.2" 1" 344" ± "41" 5.5" ± "0.3" 5" 397" ± "28" 6.3" ± "0.1" 10" 443" ± "31" 6.4" ± "0.2"    the addition of Ag results in the effective inhibition of bacterial growth. As the concentration of the Ag increased, there was no increase in the effective ZOI, which indicates the functionalized nanoparticle contains the necessary surface concentration to effectively inhibit the growth of both E. coli and S. aureus. It should be noted that this concentration occurred around the 5.0 mM region, thus matching the optimal concentration for particle size control.

Optimization of PVA/Chitsoan Nanocomposite Hydrogel Degree of Swelling
There has been a significant amount of work conducted to describe the kinetic and thermodynamic of the fluid uptake (swelling) of various hydrogel systems. Swelling has been described as the transition from an unsolvated state to a state where the pores of the hydrogel nanocomposite are swollen (solvated) with fluid. More specifically this has been reported as the diffusion of solution into the polymeric matrix of the hydrogel resulting in expansion and retention of the external fluid. This work adds an extra level of complexity to the swelling process via the incorporation of functionalized nanoparticles within the polymeric matrix. The hydrogel nanocomposite system was optimized by evaluating the ratio of biopolymer (chitosan) and swelling agent (PVA) in the presence of core TiO 2 nanoparticles to determine the concentration that produce maximum swell capacity without compromising the structural integrity of the nanocomposite. Figure  3 is the summary of the effect of additive ratios at fixed nanoparticle concentration (0.1 wt%) on the overall degree of swelling. The results clearly show the balance needed to achieve maximum swelling requires a high level of PVA to ensure effective hydrogen bonding in the hydrogel matrix. The addition of increased level of chitosan created a more fiber like structure, which resulted in a reduced degree of swelling and furthermore comprised the structural integrity of the gel. The final phase of optimization was to explore the effect of the Ag-functionalization method (pre-coated vs. in-situ) on the degree of swelling. Figure 4 shows the effect of deposition method on the degree of swelling for the optimized hydrogel synthesis pathway (pH=2.5 and 5 mM Ag). It is clear that the addition of Ag-functionalized nanoparticles using the in-situ deposition method produced swelling effectiveness similar to that of the unmodified core particle. The preparation of hydrogel nanocomposites using the pre-coated nanoparticles showed a significant decrease in overall swelling effectiveness. This decrease is attributed to the reduction of effective incorporation of the functionalized nanoparticle into the hydrogel matrix. More specifically shifting the surface energy (hydrophobic/hydrophilic interactions) of the particle resulted in a reduction of effective crosslinking (hydrogen bonding) that impacted the structural integrity of the gel. Figure 5 is a summary of the ZOI for cultures of E. coli and S. aureus for the various methods of nanoparticle functionalization using the optimized synthesis parameters (15% PVA / 85% Chitosan and 5 mM [Ag]). These data suggest that either method of nanoparticle functionalization will provide effective inhibition of bacterial growth, although it is proposed that the greatest inhibition can be obtained via the in-situ method of deposition. This may be related to the ability of the particle to be functionalized uniformly through the depth of the hydrogel matrix and thus would have an impact on the effective transport of the necessary Ag + to the bacterial cell wall. Additionally this can be coupled with the fact that the structural integrity of the hydrogel produced using the in-situ method as well as its effective degree of swelling results in more efficient ion transport to result in cell lysis. Further validation of the effective antimicrobial properties of the optimized hydrogel nanocomposite can be seen in Figure 6. A culture of Methicillin-resistant Staphylococcus aureus (MRSA) was exposed for 18 hours to the optimized hydrogel nanocomposite at two levels (5.0 and 10.0 mM) of in-situ Ag-functionalization [29]. The ZOI results clearly show effective inhibition of MRSA growth indicating the nanocomposite hydrogels effectiveness in the presence of a clinically relevant multi-drug resistant bacterial species. Figure 7 is a representative summary of adult human dermal fibroblast (HDFa) growth in the presence of different ratios of additives (PVA/Chitosan) with constant in-situ functionalized nanoparticle concentration (5mM Ag with 0.1 wt.% core particle). HDFa were grown in culture containing a biomimetic hydrogel constructed of either 50% PVA / 50% Chitosan (A), 10% PVA / 90% Chitosan (B), 20% PVA / 80% Chitosan (C), and 15% PVA / 85% Chitosan (D). Fibroblasts with a bipolar appearance that are dispersed evenly on the flask bottom demonstrate successful cell growth (B-D), whereas clumped circular cells are evidence of cell death (A). To further investigate cell viability, a live (green)/ dead (red) protein stain was added in culture. Figure 7 shows significantly higher cell death in the presence of higher concentration of PVA (A). In addition, the ability of human dermal fibroblasts to proliferate on and adjacent to varying hydrogels was determined. Photomicrographs taken of HDFa in culture showed proliferating HDFa growth directly below and adjacent to hydrogels optimized to 15% PVA / 85% Chitosan (Figure 8). Flasks containing a higher concentration of PVA either inhibited fibroblast growth completely or impeded growth near the hydrogel.

Conclusion
This work developed a photochemical method to prepare Ag +functionalized TiO 2 nanoparticles at a controlled particle size and observe the resulting antimicrobial activity E. coli and S. aureus. A synthetic protocol was developed implementing a pre-reaction sonication and slow-drip method to minimize the amount of aggregates formed during the photo-reduction process. The effect of reaction pH and Ag concentration on the overall particle size and antimicrobial effectiveness was studied. Furthermore, the antimicrobial effect of both nanocomposites and nanoparticle dispersions was observed. The antimicrobial activity of the prepared nanocomposites clearly shows