{'fraction_non_alphanumeric': 0.0387038703870387, 'fraction_numerical': 0.018901890189018902, 'mean_word_length': 5.177777777777778, 'pattern_counts': {'":': 0, '<': 0, '<?xml version=': 0, '>': 0, 'https://': 0, 'lorem ipsum': 0, 'www.': 0, 'xml': 0}, 'pii_count': 0, 'substrings_counts': 0, 'word_list_counts': {'cursed_substrings.json': 0, 'profanity_word_list.json': 0, 'sexual_word_list.json': 0, 'zh_pornsignals.json': 0}}
Influence of low-energy electron beam irradiation on defects in activated Mg-doped GaN

The effect of low-energy electron beam irradiation (LEEBI) on residual hydrogen impurities and native defects in activated metalorganic vapor phase epitaxy-grown Mg-doped (p-type) GaN layers was studied by cathodoluminescence (CL) microanalysis and spectroscopy at temperatures between 80 and 300 K. The LEEBI treatment dissociates (Mg–H)0 complexes producing (i) at 300 K, a significant increase in a free-to-bound transition (e,Mg0) centered at 3.26 eV and (ii) at 80 K, a substantial decrease in a H–Mg donor–acceptor pair emission at 3.27 eV. In-plane and depth-resolved CL imaging reveals a direct correlation between the spatial distribution of the injected carriers and the depth and lateral distribution of activated Mg acceptors. This finding strongly suggests that hydrogen dissociation results from electron-hole recombination at hydrogen defect complexes rather than heating by the electron beam. The results at 80 K indicate that the process of dissociation of hydrogen from (Mg–H)0 complexes is accompanied...