{'fraction_non_alphanumeric': 0.0343213728549142, 'fraction_numerical': 0.00234009360374415, 'mean_word_length': 6.088397790055248, 'pattern_counts': {'":': 0, '<': 0, '<?xml version=': 0, '>': 0, 'https://': 0, 'lorem ipsum': 0, 'www.': 0, 'xml': 0}, 'pii_count': 0, 'substrings_counts': 0, 'word_list_counts': {'cursed_substrings.json': 0, 'profanity_word_list.json': 0, 'sexual_word_list.json': 0, 'zh_pornsignals.json': 0}}
Biocompatibility, degradability, bioactivity and osteogenesis of mesoporous/macroporous scaffolds of mesoporous diopside/poly(l-lactide) composite

Bioactive mesoporous diopside (m-DP) and poly(l-lactide) (PLLA) composite scaffolds with mesoporous/macroporous structure were prepared by the solution-casting and particulate-leaching method. The results demonstrated that the degradability and bioactivity of the mesoporous/macroporous scaffolds were significantly improved by incorporating m-DP into PLLA, and that the improvement was m-DP content-dependent. In addition, the scaffolds containing m-DP showed the ability to neutralize acidic degradation products and prevent the pH from dropping in the solution during the soaking period. Moreover, the scaffolds containing m-DP enhanced attachment, proliferation and alkaline phosphatase activity of MC3T3-E1 cells, which were also m-DP content-dependent. Furthermore, the histological and immunohistochemical analysis results showed that the scaffolds with m-DP significantly promoted new bone formation and improved the materials degraded in vivo, indicating good biocompatibility. The results suggested that the mesoporous/macroporous scaffolds of the m-DP/PLLA composite with osteogenesis had a potential for bone regeneration.