{'fraction_non_alphanumeric': 0.024158757549611734, 'fraction_numerical': 0.0, 'mean_word_length': 5.590909090909091, 'pattern_counts': {'":': 0, '<': 0, '<?xml version=': 0, '>': 0, 'https://': 0, 'lorem ipsum': 0, 'www.': 0, 'xml': 0}, 'pii_count': 0, 'substrings_counts': 0, 'word_list_counts': {'cursed_substrings.json': 0, 'profanity_word_list.json': 0, 'sexual_word_list.json': 0, 'zh_pornsignals.json': 0}}
Mechanism of Enhanced Carbon Cathode Performance by Nitrogen Doping in Lithium–Sulfur Battery: An X-ray Absorption Spectroscopic Study

Lithium–sulfur batteries have drawn much attention in advanced energy storage development due to their high theoretical specific capacity; however, several obstacles hinder their applications, including rapid capacity loss due to dissolution of polysulfide into the electrolyte. Nitrogen-doped mesoporous carbon cathode materials were found to effectively immobilize sulfur species and minimize the sulfur loss. In this work, we use X-ray absorption near-edge structure (XANES) spectroscopy to probe the coordination structures of C, O, and N in a carbon cathode before and after the sulfur loading in order to better understand the effects of nitrogen doping. A significant change in oxygen coordination structure is observed, whereas the carbon and nitrogen chemical environments remain unaltered. In addition, the significant change in S K-edge XANES spectra is also observed after sulfur was loaded on nitrogen-doped carbon cathode material. These observations reveal that strong interaction between the nitrogen-dop...