{'fraction_non_alphanumeric': 0.02386634844868735, 'fraction_numerical': 0.028639618138424822, 'mean_word_length': 5.503875968992248, 'pattern_counts': {'":': 0, '<': 0, '<?xml version=': 0, '>': 0, 'https://': 0, 'lorem ipsum': 0, 'www.': 0, 'xml': 0}, 'pii_count': 0, 'substrings_counts': 0, 'word_list_counts': {'cursed_substrings.json': 0, 'profanity_word_list.json': 0, 'sexual_word_list.json': 0, 'zh_pornsignals.json': 0}}
Effects of Sintering Temperature on Microstructure and Phase Formation of Nitrides Bonded MgAl2O4-Crefractory

The microstructure and phase analysis of in situ nitrides formation in MgAl2O4-C refractory were investigated with different temperature. The phase compositions and microstructure of the MgAl2O4-C refractory were investigated by X-ray diffraction (XRD) and scanning electron microscope (SEM). The results show that sintering temperature has a significant influence on the microstructure and phase analysis of MgAl2O4 refractory. As the sintering temperatures are 1450°C and 1500°C, nitride that formed in samples is β-Sialon and the crystal morphology is columnar with short size. With the temperature rise to 1550°C and 1600°C, nitride formed in sample is AlON with the crystal morphology is tabular polymorph with large size.