{'fraction_non_alphanumeric': 0.038406263937757076, 'fraction_numerical': 0.033797512265226225, 'mean_word_length': 4.6733202136631995, 'pattern_counts': {'":': 0, '<': 0, '<?xml version=': 0, '>': 0, 'https://': 0, 'lorem ipsum': 0, 'www.': 0, 'xml': 0}, 'pii_count': 0, 'substrings_counts': 0, 'word_list_counts': {'cursed_substrings.json': 1, 'profanity_word_list.json': 0, 'sexual_word_list.json': 0, 'zh_pornsignals.json': 0}}
Enhancement of adsorption capacity of low cost mesoporous MCM-41 and their antibacterial and antifungal activities

This work aims to the enhancement of low cost MCM-41 adsorption capacity of copper and iron ions separately and as a mixture from solution and subsequently their use in antibacterial and antifungal activities. MCM-41mesoporous were synthesized from used spent glass as source of silicon and aluminum. The hybrid MCM-41 mesoporous were obtained by impregnation of 8-hydroxyquinoline 5-sulfonic acid on the MCM-41 pores under different mass ratios (5, 10, 15, 20 and 25%). The hybrid solids were characterized by x-ray diffraction (XRD), and the presence of 8-hydroxyquinoline 5-sulfonic acid in hybrid MCM-41 is verified by thermogravimetric analysis and infrared spectroscopy. The effect of contact time, initial pH of a solution, heavy metal concentrations and 8-hydroxyquinoline 5-sulfonic acid content on the adsorption efficiency were investigated. Pseudo-first/second order isotherms are applied to determine the efficiency of hybrid solid. The experimental data fitted well with the pseudo-second order model for Cu2+ and Fe2+ adsorption. Maximum yields for Cu2+ and Fe2+were 94% and 95% respectively. However, the extraction yield for both ion metals seems to be increase to reach 98.24% and 95.10% for iron and copper respectively when both solutions are mixed together. The hybrid MCM-41 with higher extraction yield for both metal ions and for mixture are applied as antibacterial inhibitors against Gram-negative (E. coli ATCC 25922, P. aeruginosa ATCC 27853, ), Gram-positive (S. aureus1 ATCC 25923, S.aureus2 ATCC 43300) bacteria and also as antifungal against Candida albicans ATCC 10231. The obtained results of the application of hybrid MCM-sox Cu, Fe and Cu/Fe as antibacterial and antifungal inhibitors seem to be very promising material in the adsorption and antimicrobial fields.


Introduction
The main causes of environmental pollution are linked to heavy metals and pathogenic microorganisms. Heavy metals are a serious hazard to the environment, such as the aquatic ecosystem, due to their accumulated in an ecological system to induce irreversible pollution or in the human body. In addition, microbial contamination has always been a challenge that threatens the health of humans. Many types of bacteria can cause serious lifethreatening infections in humans. Therefore, it is important and necessary to develop an efficient, inexpensive and environmentally friendly material capable of either adsorbing or trapping these metals and has both an antibacterial and an antifungal effect. From a health, environmental and economic point of view the elimination of these toxic metals is very important and has a crucial issue. Diverse processes were improved to minimize this environmental problem, such as chemical precipitation [1], heavy metal chelating precipitation [2,3], membrane filtration [4], activated carbon [5], reverse osmosis [6], and ion exchange treatment [7,8], all of which can be effective in removing copper and iron from aqueous system. Unfortunately, the high cost and complexity of procedures is diverting researchers to other procedures to separate these metals from the environment. and to make them useful for potential antibacterial activities [9,10]. Many studies used phyllosilicates [11,12] and microporous materials in the adsorption of different metals ions [13,14] due to their higher cationic exchange capacity instead of mesoporous materials which have drawbacks in terms of cation exchange capacity (CEC) and exorbitant costs. In spite of all these troublesome characteristics, the mesoporous materials have other advantages, such as identical mesoporous sieves ranging from 2 to 10 nm, and higher surface areas up to 1000 m 2 g −1 [15][16][17]. This paper will describe the procedure for low-cost synthesis of MCM-41 mesoporous materials from spent waste and how they will be used as adsorbed and antimicrobial metal promoters. On the basis of a literature review, there is only a few documents [18] on the use of 8-hydroxyquinoline for the elaboration of fluorescent materials. This study treats the use of 8-hydroxyquinoline mesoporous MCM-41 hybrid (MCM-sox) for simultaneous investigation of the removal of copper and iron metals ions and their applications in antimicrobial activities. The mesoporous MCM-41 were prepared from waste spent glass as silicon and aluminium sources instead of lab reagents such as Ludox and sodium aluminates respectively to reduce significantly the synthesis cost of MCM-41 to be used as trap of ion metals for an antibacterial and antifungal possible activities.

Adsorption reagents
The Cu (II) and Fe (II) (0.1 g l −1 ) solutions were prepared from their corresponding salt (CuCl 2 .2H 2 O, FeCl 2 .4H 2 O) in deionised water. NaCl and HCl were also used. Spent glass was used as silicon and aluminium sources for the synthesis of MCM-41 according to the process given by Adjdir et al [19]. To extract the Si and Al needed to synthesis MCM-41 from waste spent glass, a fusion process at 550°C was adopted which consisted of a treatment of sodium hydroxide with waste spent glass under a mass ratio of 1:1.2, waste spent glass: NaOH to obtain a fused mass which was cooled at room temperature overnight then mixed with water at mass ratio fused mass: H 2 O (1:6) and stirred overnight at room temperature. After centrifugation of the mixture, liquid solution obtained is called supernatant its elemental compositions are given in table 2. The synthesis procedure of Al-MCM-41 from the supernatant was given as follows [19]. 0.867g of hexadecyltrimethylammonium bromide (C 16 TMABr), different mass ratios 5, 10, 15, 20 and 25% of 8-hydroxyquinoline 5-sulfonic acid (sox), 15 ml water and 0.75 g NH 4 OH were combined with 40 ml of supernatant separately and stirred at room temperature then an appropriate amount of acid acetic was added. The obtained hydrogels were treated at 100°C in glass tube instead of autoclave for 48 h. The solids obtained were called WSG-MCM-41-sox (scheme 1).

Characterization methods
Inductively Coupled Plasma Optical Emission spectrometer (ICP-OES) was used to determine elemental composition of supernatant solutions. Formation and structure of Al-MCM-41 was checked by XRD. Diffraction patterns were recorded in the 2θ range of 1-70°with a step of 0.02°2θ and a step time of 5 s on a Bruker D5000 diffractometer with CuKα (λ=1.5406 Å ) radiation (40 kV, 40 mA). The copper and iron ions concentrations were determined by Perkin-Elmer flame atomic absorption spectrometer, Model 2380.

Metal extraction procedure
In batch experiments at 25°C, the adsorption of Cu (II) and Fe (II) (0.1 g l −1 ) was performed. 0.1 g of MCM-41sox samples was mixed mechanically in polypropylene tubes with 10 ml of aqueous metal solution during 180 min separately. The equilibrium pH e was determined after phase separation. The concentrations of metal ions were calculated by atomic absorption spectroscopy on a Perkin-Elmer 2380 spectrophotometer.

Kinetics adsorption procedure
The kinetic study was carried out under the following experimental conditions: 0.1 g of MCM-41-sox mesoporous material is suspended in 10 ml of Cu(II) and Fe(II) solutions at 25°C for contact times ranging from 0 to 360 min separately. Two kinetic models pseudo-first and pseudo-second order have been applied to understand the adsorption behaviour.

Cu/Fe selectivity separation
To study the adsorption selectivity between iron and copper ions, an appropriate amount of MCM-41-sox solid was mixed with 100 mg l −1 of a solution containing Cu (II) and Fe (II) at pH i 4 corresponding to Cu (II) and Fe (II) solutions respectively.

Preparation of bacterial cultures
The same method as presented in previous work [10] was used to prepare the bacterial medium. The adsorbents materials MCM-sox, MCM-sox-Cu15%, MCM-Sox-Fe15% and MCM-sox-Fe/Cu15% were tested on the inhibition of bacteria. A same amount of these materials are deposited on the surface of solid mass medium seeded with pure bacterial culture. The studied pathogenic bacterias are Staphylococcus aureus ATCC 25923, Escherichia coli ATCC 25922, Staphylococcus aureus ATCC 43300, Pseudomonas aeruginosa ATCC 27853 and for antifungal activity against Candida albicans ATCC 10231 was used. 0.5 ml culture (10 8 cell ml −1 ) acquired after incubation at 37°C for 24 h was mixed with 10 ml of medium (PDA) liquid at 40°C. This last is melted by heating and then cooled before placing in contact with the microbial suspension. The mixture was deposed in Petri dishes of 90 mm. Discs materials exchanged by copper, iron and both copper and iron previously sterilized at 180°C for 30 min, and are then putted in the medium containing the bacteria. The antimicrobial activity is determined after incubation of the dishes in an oven at 37°C for 24 h for bacteria and 48 h at 30°C for Candida albicans. The inhibition zone for bacterial growth was detected visually and photographed. The ICP-OES analysis (table 2) reveals differences between supernatant resulting from waste spent glass and Bentonite [20,21]. The amount of silicon drawn by the alkaline fusion method of waste spent glass is about 26 450 mg l −1 which seems much higher than that extracted from Bentonite 10 600 mg l −1 , and the difference is around 46%. By contrast, the amount of aluminum drawn from Bentonite [20] is ca 645 mg l −1 . higher to that found from waste spent glass is 145 mg l −1 . The huge amount of silicon extracted from the waste spent glass can be explained either by the element composition of glass, where the main element that constitutes the waste spent glass is silica.

X-rays diffraction
The powder XRD patterns of the Al-MCM-41 synthesized from waste spent glass are depicted in scheme 2 and figure 1(a). The XRD pattern of all samples display a higher crystalline order and present the same reflections which consist of one very strong peak (100) and two weak reflections corresponding to (110), and (200) at 2θ ranging from 2°to 6°. The (100) reflection which characterized a hexagonal pore structure of Al-MCM-41 was observed in the low-angle x-ray patterns [19,22,23]. Based on the XRD of both samples in figure 2(b), it can be noted that the sample synthesized from waste spent glass has a better crystallinity in comparison to that one synthesized from Bentonite [24]. This is related to the aluminum content in Bent-MCM framework Si/Al ca. 16 [20]. According to the XRD of the samples, it is concluded that the samples synthesized from waste spent glass present an additional distinct peaks in the region of 2θ ranging from 20°to 25°, these peaks are attributed to the crystalline NaNO 3 . The existence of this new phase, that do not belong to MCM-41 phase, is due to the interaction of HNO 3 acid added in the synthesis step to decrease the pH of the supernatant with the excess of Na + from the alkaline fusion step. In this work the excess of Na ions are generated into the new crystalline NaNO 3 phase. However, the Gaussian confirms the existence of an amorphous silica phase. This indicates that the amount of silica used in the synthesis could be greater than the necessary amount.

Infrared spectroscopy analysis
The FTIR spectrum of MCM-41-sox shows a broad band in the region 3438-3414 cm −1 attributed to the surface elongation vibrations of the silanol groups (Si-OH) [25]. The peaks at 2925 and 2854 cm -1 are attributed to C-H stretching vibration of cetyltrimethylammonium and 8-hydroxyquinoleine5-sulfonic acid (sox). A strong peak in the region 1245-1020 cm −1 denotes C-O stretching vibrations. The MCM-41-sox shows the asymmetric and symmetric S=O stretching vibration in the region 1390-1368 cm −1 and 1168-1150 cm −1 . the peak at 1620 cm −1 is attributed to C=C stretching in aromatic nuclei of 8-hydroxyquinoline 5-sulfonic acid (sox) [18].

Scanning electron microscopy
The SEM images of the particle morphology and size of the WSG-MCM-41 sample was presented in ( figure 3).
The WSG-MCM-41 sample exhibits a silica fibers or nanotubes. This evidently, the detailed experimental conditions such as the amounts of silicon and aluminum and the acid concentration in the self-assembly reaction play an important role in the determination the particle shape and the particle size. The obtained morphology is similar to that found by Adjdir and coworker [19] where they stated that when the content of aluminum into MCM-framework decrease, the obtained morphology tends to a nanotube shape. In the Bent-MCM-41 sample, the morphology is more spherical than nanotube, This is due to aluminum, which seems to block the Si polymerization sites, thus leading to a reduced growth in all dimensions. This nanotube morphology is also observed when the Si-MCM-41 is synthesized from laboratory reagents in absence of aluminum. This phenomenon can be explained by the process of polymerization between different silica species which leads to the strengthening of the silica walls and to the improvement in the long-range ordering. this result is confirmed by XRD.

Metal extraction
The reaction of divalent metals adsorption by MCM-sox-15% is given below [11]

Effect of stirring time and kinetic of adsorption
The determination of the effect of stirring time on the extraction yields at pH4 was studied and given in figure 4. It can be noticed from this plot that the maximum of extraction yield are around 93.87% for Fe (II) and 81.41% for Cu (II) and it is reached after 60 min. Therefore, the contact time of 60 min was adopted for subsequent studies of both ion metals. For the kinetic adsorption, two models are chosen the pseudo-first order expressed in equations (3), (4) and the pseudo-second order given in equations (5), (6) to investigate the kinetic order of the extraction process [28].
For a pseudo-first order reaction (figure 5), the rate law is expressed by equation (3): The rate law for pseudo-second order reaction (figure 6) is expressed by equation (5) = dq dt k q q 5 t e t 2 2 Where k 2 is the rate constant (g/mmol.min) Equation (6) is rearranged and given as follow: The rate constants and correlation coefficients were determined by plotting Ln (q e -q t ) as a function of time (t) for pseudo-first order and t/q t versus time (t) for pseudo-second order. The results are summarized in table 3 and shown in figures 5 and 6.
The experimental results are in excellent agreement with the theoretical results given in table 3. After comparison of the correlation coefficients for both ions and both models, it is noted that the experimental results coincide with the pseudo-second order kinetic model. According to this model, the amounts of metal ion extracted at equilibrium are calculated (table 3). These results are in agreement with those found by many researchers [11,29,30].

Effect of equilibrium pH
The adsorption of metal ions depends highly on the pH [31][32][33][34][35]. Stock solutions of Cu (II) and Fe (II) (0.1 g l −1 ) were prepared according to the initial pH from 3 to 6. The pH range for each metal ions is taken to avoid hydroxide precipitation at significant pH values. Copper (II) and iron (II) extraction percentages as a function of equilibrium pH (pH e ) are summarized in table 4.
Moderate extraction percentage was observed at pH 3 around 55.25% and 66.03% for Cu(II) and Fe(II) respectively. At pH 4, an exponential increase in metal extraction for both metal ions is observed, where the extraction of copper(II) reached 96.35% and iron(II) was 98.29% slightly higher than that found for copper. This difference can be attributed to their reciprocal ionic radius where Cu(II) displays an ionic radius about 73 pm and Fe(II) is 70 pm. The extraction gap between copper (II) and iron (II) becomes bigger as the pH increase.

Effect of the sox mass ratio on the adsorption
First experiment consists to mix 0.1 g of MCM-41-sox with different mass ratios in 10 ml of Cu(II) and Fe(II) (100 mg L −1 ) solutions separately. In the second experiment the same amount of MCM-41-sox added to 10 ml of Cu(II) and Fe(II) (100 mg l −1 ) previously mixed together at 25°C, teq=60 min and pH 4. The results are illustrated in table 5.
The obtained results clearly shown that, in general, the retention of Cu(II) increases as the mass ration of the sox increases. These results are in agreement with those find by many researches and can be related to the nature of the sox. Moeller et al [36] stated that the pore structure of granular activated carbon and chemistry of the ligand molecule (as chelating agents) probably contribute significantly towards uptake of copper ions and concluded that sox ligand behaves as a bidentate (N, O) ligand and thus could chelate effectively with metal ions like copper and iron. However, the best results are attributed to Fe(II), where de retention yields are higher in all mass ratios.

Adsorption selectivity effect of Cu(II) and Fe(II) by MCM-41-sox 15%
Two solutions containing copper and iron were prepared at 100 mg l −1 separately then mixed together for a while. An amount of MCM-41-sox was added to the mixture under stirring for 60 min at 25°C for pH4. From the results given in table 6 both ions are practically extracted at pH e 4. MCM-41-sox seems to have an affinity

Antimicrobial and antifungal tests
The antibacterial activity against Gram-negative (E. coli ATCC 25922, P. aeruginosa ATCC 27853, ), Grampositive (S. aureus1 ATCC 25923, S.aureus2 ACC 43300) bacteria and also as antifungal against Candida albicansATCC 10231 for the adsorbents was evaluated as showed in the figure 7. The diameters of inhibition zones were recorded in table 7. MCM-soxpresents no antibacterial activity versus the microorganisms. The same result was also observed in the case of zeolites and clay mineral used alone [37][38][39]. The adsorbents samples MCM-sox-Cu15% and MCM-sox-Fe15% presented the excellent antibacterial activity against gram-positive bacteria. However, in the case of Gram-negative bacteria only the antibacterial activity of MCM-sox-Fe15% adsorbent was observed. In the case of MCM-sox-CuFe15%, the antibacterial activity has been greatly improved and has shown an obvious synergistic antibacterial effect, this is probably due to both copper and iron ions which show some antibacterial activity [39,40], but also to attack targets against microorganisms may be  different from each other. A weak antibacterial activity was observed for the adsorbents studied against Escherichia coliATCC 25922. This shows a very great resistance of this bacteria. However, MCM-sox-Cu15% presents no activity antifungal against Candida albicansATCC 10231. Unlike the result found by MCM-sox-Cu15%, MCM-sox-Fe15% presents an activity antifungal. This activity seems to be increased when MCM sox contained both metal ions (MCM-sox-CuFe15%).

Conclusion
The summary of this work was the removal of divalent metals using hybrid MCM-41-sox mesoporous materials and their uses against antibacterial and antifungal. In this study, the removal of Cu 2+ and Fe 2+ using hybrid MCM-41-sox mesoporous materials type synthesized from used spent glass is successfully undertaken. Hybrid MCM-41 with different mass ration of sox were synthesized, the intercalation of the sox molecules in the pores of the mesoporous during the synthesis did not affect the structure of the MCM-41. The adsorption of Cu 2+ and Fe 2+ from aqueous solutions on MCM-41-sox 15% is well described and fit with the pseudo-second order kinetic model. The remediation yield of bivalent metals copper and iron is up to 90% for both ions. The hybrid MCM-sox-Cu15% and MCM-sox-Fe15% presented an excellent antibacterial activity. In the case of MCM-sox-CuFe15%, the antibacterial activity has been greatly improved and has shown an obvious synergistic antibacterial effect. However, MCM-sox-Cu15% presents no activity antifungal against Candida albicansATCC 10231. Unlike the result found by MCM-sox-Cu15%, MCM-sox-Fe15% presents an activity antifungal very promising. This activity seems to be increased when MCM sox contained both metal ions (MCM-sox-CuFe15%).