{'fraction_non_alphanumeric': 0.02826379542395693, 'fraction_numerical': 0.020188425302826378, 'mean_word_length': 5.305084745762712, 'pattern_counts': {'":': 0, '<': 0, '<?xml version=': 0, '>': 0, 'https://': 0, 'lorem ipsum': 0, 'www.': 0, 'xml': 0}, 'pii_count': 0, 'substrings_counts': 0, 'word_list_counts': {'cursed_substrings.json': 0, 'profanity_word_list.json': 0, 'sexual_word_list.json': 0, 'zh_pornsignals.json': 0}}
X-ray Diffraction Study of the Ultrathin Al2O3 Layer on NiAl(110)

Ultrathin Al2O3 layers on alloys are used as templates for model catalysts, tunneling barriers in electronic devices, or corrosion-resistant layers. The complex atomic structure of well-ordered alumina overlayers on NiAl(110) was solved by surface x-ray diffraction. The oxide layer is composed of a double layer of strongly distorted hexagonal oxygen ions that hosts aluminum ions on both octahedral and tetrahedral sites with equal probability. The alumina overlayer exhibits a domain structure that can be related to characteristic growth defects and is generated during the growth of a hexagonally ordered overlayer (Al2O3) on a body-centered cubic (110) substrate (NiAl).