{'fraction_non_alphanumeric': 0.024288107202680067, 'fraction_numerical': 0.0033500837520938024, 'mean_word_length': 5.9476744186046515, 'pattern_counts': {'":': 0, '<': 0, '<?xml version=': 0, '>': 0, 'https://': 0, 'lorem ipsum': 0, 'www.': 0, 'xml': 0}, 'pii_count': 0, 'substrings_counts': 0, 'word_list_counts': {'cursed_substrings.json': 0, 'profanity_word_list.json': 0, 'sexual_word_list.json': 0, 'zh_pornsignals.json': 0}}
Surface modification of neural stimulating/recording electrodes with high surface area platinum-iridium alloy coatings

High-surface area platinum-iridium alloys were electrodeposited by on Pt and Au microelectrodes using a potential sweep technique. Detailed investigations of the structure and morphology and the electrochemical properties of the electrodeposited Pt-Ir alloy coatings were performed. Scanning electron microscopy (SEM) and energy dispersive spectroscopy (EDS) were used for the determination of the surface morphology and the chemical composition of the Pt-Ir coatings, respectively. The elemental analysis by EDS showed a nearly 60–40% Pt-Ir composition of the coatings. The electrochemical properties of the Pt-Ir coatings were evaluated using cyclic voltammetry (CV) and electrochemical impedance spectroscopy (EIS). CV and EIS measurements revealed that the Pt-Ir coated electrodes exhibit significantly increased charge storage capacity and real surface area compared to uncoated Pt electrodes. Charge injection experiments of the Pt-Ir coated microelectrodes revealed low potential excursions, indicating high charge injection capabilities within safe potential limits.