{'fraction_non_alphanumeric': 0.04779969650986343, 'fraction_numerical': 0.025796661608497723, 'mean_word_length': 4.941441441441442, 'pattern_counts': {'":': 0, '<': 0, '<?xml version=': 0, '>': 0, 'https://': 0, 'lorem ipsum': 0, 'www.': 0, 'xml': 0}, 'pii_count': 0, 'substrings_counts': 0, 'word_list_counts': {'cursed_substrings.json': 0, 'profanity_word_list.json': 0, 'sexual_word_list.json': 0, 'zh_pornsignals.json': 0}}
[Effect of 2-methacryloyloxyethyl phosphorylcholine on the protein-repellent property of dental adhesive].

OBJECTIVE
To evaluate the effect of 2-methacryloyloxyethyl phosphorylcholine (MPC) and nanoparticles of amorphous calcium phosphate (NACP) on the protein-repellent property of dental adhesive.


METHODS
MPC and NACP were incorporated into SBMP as the test group. Scotchbond Multi-Purpose (SBMP) was used as control group. Human dentin shear bond strengths were measured. Protein adsorption onto samples was determined by micro bicinchoninic acid (BCA) method. A dental plaque microcosm biofilm model with human saliva as inoculum was used to investigate biofilm viability.


RESULTS
The dentin bond strength of modified group was (28.7±2.2) MPa, which was not significantly different from that of the SBMP control group. The amount of protein adsorption in the modified group and the SBMP control group were (0.21±0.02) µg/cm(2) and (4.17±0.45) µg/cm(2) respectively. Lactic acid production of biofilms in modified group and SBMP control were (7.71 ± 1.01) mmol/L and (19.18 ± 2.34) mmol/L repectively.


CONCLUSIONS
MPC-NACP based dental adhesive greatly reduce the protein adsorption and bacterial adhesion, without compromising dentin shear bond strength. This novel bonding agent may have wide application.