{'fraction_non_alphanumeric': 0.016865776528460996, 'fraction_numerical': 0.004919184820801124, 'mean_word_length': 5.472727272727273, 'pattern_counts': {'":': 0, '<': 0, '<?xml version=': 0, '>': 0, 'https://': 0, 'lorem ipsum': 0, 'www.': 0, 'xml': 0}, 'pii_count': 0, 'substrings_counts': 0, 'word_list_counts': {'cursed_substrings.json': 0, 'profanity_word_list.json': 0, 'sexual_word_list.json': 0, 'zh_pornsignals.json': 0}}
Surface charge coupling behavior of fluorinated polyimide film under DC and pulse voltage

Polyimide (PI) films have excellent electrical, mechanical and thermal properties in aspect of resisting corona, aging and radiation. However, the pulse voltage combined with dc voltage often causes concentration of local electrical field, which makes the surface charge behaviors more complex and threatens the system. As a means of surface treatment, direct fluorination has been proved as an effective way to improve the polymer properties, without compositing the bulk characteristics. Therefore, this paper intends to reveal the effects of fluorination on surface charge coupling behaviors of the PI films under dc and pulse voltage combination. The PI samples fluorinated for 0, 15, 45 and 60 min were obtained. Surface corona discharging was stressed under the combination of dc and pulse voltage. The surface charge accumulation, decay and distribution were measured coupled with an analysis of trap distribution. The results show the surface charge dynamic behaviors are strongly correlated with the fluorination time, pulse voltage amplitude and polarities of the dc and pulse voltage combination. The trap distribution results imply that the effect of fluorination and charging condition attribute to the change of trap depth and amount. Besides, surface charge behaviors are greatly improved by appropriate fluorination.