{'fraction_non_alphanumeric': 0.0404270798513479, 'fraction_numerical': 0.018463535009929803, 'mean_word_length': 4.922673809246535, 'pattern_counts': {'":': 0, '<': 17, '<?xml version=': 0, '>': 1, 'https://': 0, 'lorem ipsum': 0, 'www.': 0, 'xml': 0}, 'pii_count': 0, 'substrings_counts': 0, 'word_list_counts': {'cursed_substrings.json': 0, 'profanity_word_list.json': 0, 'sexual_word_list.json': 0, 'zh_pornsignals.json': 0}}
Mineralogy of Zirconium in Iron-Oxides: A Micron- to Nanoscale Study of Hematite Ore from Peculiar Knob, South Australia

Zirconium is an element of considerable petrogenetic significance but is rarely found in hematite at concentrations higher than a few parts-per-million (ppm). Coarse-grained hematite ore from the metamorphosed Peculiar Knob iron deposit, South Australia, contains anomalous concentrations of Zr and has been investigated using microanalytical techniques that can bridge the micron- to nanoscales to understand the distribution of Zr in the ore. Hematite displays textures attributable to annealing under conditions of high-grade metamorphism, deformation twins (r~85˚ to hematite elongation), relict magnetite and fields of sub-micron-wide inclusions of baddeleyite as conjugate needles with orientation at ~110˚/70˚. Skeletal and granoblastic zircon, containing only a few ppm U, are both present interstitial to hematite. Using laser-ablation inductively coupled plasma mass spectrometry (LA-ICP-MS) spot analysis and mapping, the concentration of Zr in hematite is determined to be ~260 ppm on average (up to 680 ppm). The Zr content is, however, directly attributable to nm-scale inclusions of baddeleyite pervasively distributed throughout the hematite rather than Zr in solid solution. Distinction between nm-scale inclusions and lattice-bound trace element substitutions cannot be made from LA-ICP-MS data alone and requires nanoscale characterization. Scandium-rich (up to 0.18 wt. % Sc2O3) cores in zircon are documented by microprobe analysis and mapping. Using high-angle annular dark field scanning transmission electron microscopy imaging (HAADF-STEM) and energy-dispersive spectrometry STEM mapping of foils prepared in-situ by focused ion beam methods, we identify [011]baddeleyite epitaxially intergrown with [22.1]hematite. Lattice vectors at 84–86˚ underpinning the epitaxial intergrowth orientation correspond to directions of r-twins but not to the orientation of the needles, which display a ~15˚ misfit. This is attributable to directions of trellis exsolutions in a precursor titanomagnetite. U–Pb dating of zircon gives a 206Pb/238U weighted mean age of 1741 ± 49 Ma (sensitive high-resolution ion microprobe U–Pb method). Based on the findings presented here, detrital titanomagnetite from erosion of mafic rocks is considered the most likely source for Zr, Ti, Cr and Sc. Whether such detrital horizons accumulated in a basin with chemical precipitation of Fe-minerals (banded iron formation) is debatable, but such Fe-rich sediments clearly included detrital horizons. Martitization during the diagenesis-supergene enrichment cycle was followed by high-grade metamorphism during the ~1.73–1.69 Ga Kimban Orogeny during which martite recrystallized as granoblastic hematite. Later interaction with hydrothermal fluids associated with ~1.6 Ga Hiltaba-granitoids led to W, Sn and Sb enrichment in the hematite. By reconstructing the evolution of the massive orebody at Peculiar Knob, we show how application of complimentary advanced microanalytical techniques, in-situ and on the same material but at different scales, provides critical constraints on ore-forming processes.

the current maximum deposition ages for these rocks (~1750 Ma [19]) suggests they are more likely equivalents to the Wallaroo Group metasediments of the Yorke Peninsula. Intrusive rocks recognized within the basement complex include the foliated 1691 ± 25 Ma Engenina Adamellite and the weaklyto non-foliated 1584 ± 18 Ma Balta Granite, affiliated with the~1.6 Ga Hiltaba Suite [20].
The metamorphic history of the Mount Woods Inlier has been extensively debated but is nevertheless important in the context of understanding and constraining sequences of mineralization at Peculiar Knob ( Figure 1B). The metamorphic grade within the Mount Woods Inlier is suggested to increase from greenschist facies in the south to granulite facies in the north [28]. Granulite facies metamorphism occurred coincident with early stages of the~1.73-1.69 Ga Kimban Orogeny ( [29] and references therein), based on a 1736 ± 14 Ma SHRIMP (sensitive high-resolution ion microprobe) U-Pb age of interpreted metamorphic zircon [20].
Metamorphic ages of~1. 59 Ga are reported from throughout the Mount Woods Inlier [19,26,27]. Recent monazite CHIME (chemical Th-U-total Pb isochron method) dating, combined with P-T pseudosection modeling of a sample of Skylark Metasediments, provided evidence for a granulite facies metamorphic event that peaked at~1595 Ma [22]. This sample, however, derived from a location some distance northwest from Peculiar Knob. A potentially still younger overprint is indicated by metamorphic rims dated at 1576.2 ± 7 Ma from a leucogabbro from drillhole PKN1 adjacent to the deposit [27].
The deposit is buried beneath 12-35 m of the flat-lying Cretaceous sediments (Bulldog Shale) and was mined between 2011 and 2015. The deposit consists of a zone of high-grade hematite mineralization, roughly 1 km in length,~35 m wide and up to~300 m deep ( Figure 1C). The orebodies are steeply NW-dipping and occur as two NE-striking, sub-parallel elongated lensoidal bodies, which are off-set by at least four cross-cutting faults. These are hosted within a sequence of iron-rich units and various high-grade metamorphosed rocks and granitoids. Ultramafic/mafic lithologies within the sequence can be inferred by the presence of altered, chlorite-rich rocks. Similar lithologies are also known associated with BIF sequences from the Middleback Ranges deposits [6]. The ores comprise massive specular hematite and have been considered to represent the metamorphosed hydrothermally-altered equivalents of Fe-rich sediments, including chemical precipitates (BIFs), in several previous studies [10,15,30], and also in the most recent resource report [11]. Early studies also acknowledge the impact on the ores from the adjacent Balta Granite (e.g., [31]). More recently, other authors have speculated on the possible relationships between iron deposits such as Peculiar Knob and IOCG systems of the eastern Gawler Craton (e.g., [32]), although little direct evidence is available to support such a hypothesis.

Methodology
The present study was carried out on a sample of massive hematite ore ( Figure 2) collected from the Peculiar Knob open pit. The sample was assayed by Intertek Genalysis (Adelaide, Australia). Methodology for the whole-rock analysis and element minimum detection limits (MDL) are provided in Supplementary Material A. All the below mentioned microanalytical instrumentation are housed at Adelaide Microscopy, The University of Adelaide (Adelaide, Australia). Petrographic observations were made on a one-inch polished block using reflected-light optical and scanning electron microscopy (SEM). A FEI Quanta 450 SEM equipped with an energy dispersive X-ray spectrometer (EDS) was used for further µm-scale observations, detection of compositional zonation within hematite and zircon, and for back-scattered electron (BSE) imaging. Analytical conditions for SEM work were 20 kV acceleration voltage and a beam current of 10 nA.
Trace element concentrations in hematite were measured with a RESOlution excimer laser ablation system (Applied Spectra Inc., Fremont, SA, USA) coupled to an Agilent 7900x Quadrupole ICP-MS using a frequency of 10 Hz, fluence of 3.5 J/cm 2 and a spot diameter of 60 µm. Laser ablation element maps were performed using a laser frequency of 10 Hz, fluence of~3 J/cm 2 , and a spot diameter and scan speed of 7 µm and 7 µm/s, respectively. 57 Fe was used as an internal standard element for quantification of hematite assuming ideal stoichiometry. External reference materials used were the synthetic basalt glass standard GSD-1G glass (USGS; [33]) and the NIST-610 glass [34]. "GLITTER" software [35] was used for data reduction. To avoid element contamination from trace minerals included in hematite, only those intervals within individual spot analyses showing flat signals were selected during the data reduction process. Time-resolved depth profiles were used to further assess trace element data quality and to ensure negligible influence from included minerals during analysis. Average minimum detection limits (MDL) for the analyzed elements are also provided in the same appendix. Laser ablation element maps were constructed using "Iolite" software [36]. See Supplementary Material A for full details of analytical methods.
Zircon compositions were quantitatively determined using a Cameca SX-Five Electron Microprobe (Adelaide Microscopy) running "PeakSite" software and equipped with five wavelength-dispersive X-Ray detectors. Calibration and data reduction were carried out using "Probe for EPMA" software. Analytical conditions, elements measured, average MDL, peak/background positions, count times, and standards are listed in Supplementary Material A.
Minerals 2019, 9, x FOR PEER REVIEW 5 of 27 provided in the same appendix. Laser ablation element maps were constructed using "Iolite" software [36]. See Supplementary Material A for full details of analytical methods. Zircon compositions were quantitatively determined using a Cameca SX-Five Electron Microprobe (Adelaide Microscopy) running "PeakSite" software and equipped with five wavelength-dispersive X-Ray detectors. Calibration and data reduction were carried out using "Probe for EPMA" software. Analytical conditions, elements measured, average MDL, peak/background positions, count times, and standards are listed in Supplementary Material A. A FEI-Helios nanoLab Dual Focused Ion Beam (FIB) SEM was used for preparing foils for transmission electron microscopy (TEM) study. Procedures for extracting and thinning (to <100 nm) of foils by beam (Ga + ) milling and attachment to Cu grids followed those outlined previously [37]. High-angle annular dark field-scanning transmission electron microscopy (HAADF-STEM) imaging and energy-dispersive X-ray spectrometry (EDS)-STEM mapping were performed on a highresolution, probe-corrected, FEI Titan Themis S/TEM equipped with the X-FEG Schottky source and Super-X EDS geometry, operated at 200 kV.
Cathodoluminescence (CL) imaging to characterize core-rim relationships and zonation patterns within granular zircon interstitial to hematite was performed on a FEI Quanta 600 MLA SEM (Adelaide Microscopy) equipped with a tungsten filament electron source. In-situ U-Pb dating of zircon was performed with the high-resolution ion microprobe (SHRIMP-II) at the John de Laeter Centre, Bentley, Curtin University, Western Australia. Analytical methods used broadly follow those described by Compston et al. [38] and Williams [39]. Further details are given in Supplementary Material A.

Petrography
The massive ore consists of mm-sized, polyhedral grains of hematite with granoblastic texture (Figure 2). Gangue minerals (mostly quartz and minor siderite) are located at hematite grain boundaries or concentrated along trails within the hematite ( Figure 2B). Mutual grain boundaries, often with triple junctions at 120˚, exhibit both straight and serrated margins ( Figure 3A,B). A FEI-Helios nanoLab Dual Focused Ion Beam (FIB) SEM was used for preparing foils for transmission electron microscopy (TEM) study. Procedures for extracting and thinning (to <100 nm) of foils by beam (Ga + ) milling and attachment to Cu grids followed those outlined previously [37]. High-angle annular dark field-scanning transmission electron microscopy (HAADF-STEM) imaging and energy-dispersive X-ray spectrometry (EDS)-STEM mapping were performed on a high-resolution, probe-corrected, FEI Titan Themis S/TEM equipped with the X-FEG Schottky source and Super-X EDS geometry, operated at 200 kV.
Cathodoluminescence (CL) imaging to characterize core-rim relationships and zonation patterns within granular zircon interstitial to hematite was performed on a FEI Quanta 600 MLA SEM (Adelaide Microscopy) equipped with a tungsten filament electron source. In-situ U-Pb dating of zircon was performed with the high-resolution ion microprobe (SHRIMP-II) at the John de Laeter Centre, Bentley, Curtin University, Western Australia. Analytical methods used broadly follow those described by Compston et al. [38] and Williams [39]. Further details are given in Supplementary Material A.

Petrography
The massive ore consists of mm-sized, polyhedral grains of hematite with granoblastic texture (Figure 2). Gangue minerals (mostly quartz and minor siderite) are located at hematite grain boundaries or concentrated along trails within the hematite ( Figure 2B). Mutual grain boundaries, often with triple junctions at 120 • , exhibit both straight and serrated margins ( Figure 3A,B). Polysynthetic twinning, following one or two crystallographic directions, is a common feature of hematite ( Figure 3A-C). Small grains, from <1 µm to a few µm in size, of magnetite are ubiquitous throughout the hematite ( Figure 3D-I). The morphology of these grains varies from thin lamellae to (sub)-euhedral grains of hexagonal to octagonal shape in cross-section. Magnetite is closely associated with the twin planes in hematite, either at their margins, along, or slightly offset/across them ( Figure 3E-G). Pressure gashes filled with gangue minerals (quartz and siderite) and tiny blebs of magnetite are observed along microfractures crosscutting the twin planes ( Figure 3I). Polysynthetic twinning, following one or two crystallographic directions, is a common feature of hematite ( Figure 3A-C). Small grains, from <1 µm to a few µm in size, of magnetite are ubiquitous throughout the hematite ( Figure 3D-I). The morphology of these grains varies from thin lamellae to (sub)-euhedral grains of hexagonal to octagonal shape in cross-section. Magnetite is closely associated with the twin planes in hematite, either at their margins, along, or slightly offset/across them ( Figure 3E-G). Pressure gashes filled with gangue minerals (quartz and siderite) and tiny blebs of magnetite are observed along microfractures crosscutting the twin planes ( Figure 3I). Rounding and replacement of coarser magnetite by gangue is also observed at junctions of microfractures ( Figure 3H). More advanced reworking of hematite is observed along the trail of gangue minerals that runs through the middle part of the polished block. This includes brecciation within twin planes associated with small displacements of finer sets of twins ( Figure 3J) and deformation of smaller hematite grains ( Figure 3K). Rounding and replacement of coarser magnetite by gangue is also observed at junctions of microfractures ( Figure 3H). More advanced reworking of hematite is observed along the trail of gangue minerals that runs through the middle part of the polished block. This includes brecciation within twin planes associated with small displacements of finer sets of twins ( Figure 3J) and deformation of smaller hematite grains ( Figure 3K).
One of the unusual characteristics of the hematite is the presence of fields comprised of micron to sub-micron inclusions with bright appearance on BSE images ( Figure 4A-C). These are identified from the nanoscale study (see below) as baddeleyite (monoclinic ZrO 2 ). Such fields are, however, absent in some grains ( Figure 4A), or are effectively invisible, at least at this scale of observation. The baddeleyite inclusions display bleb, or more often needle-like morphologies, are generally <3 µm in length and <1 µm in width and are preferentially oriented in two or three directions. The obtuse/acute angles between two arrays of inclusions are~110 • /70 • . One of the unusual characteristics of the hematite is the presence of fields comprised of micron to sub-micron inclusions with bright appearance on BSE images ( Figure 4A-C). These are identified from the nanoscale study (see below) as baddeleyite (monoclinic ZrO2). Such fields are, however, absent in some grains ( Figure 4A), or are effectively invisible, at least at this scale of observation. The baddeleyite inclusions display bleb, or more often needle-like morphologies, are generally <3 µm in length and <1 µm in width and are preferentially oriented in two or three directions. The obtuse/acute angles between two arrays of inclusions are ~110°/70°. The baddeleyite arrays can cross over grain boundaries ( Figure 4A), form locally denser domains within the same grain ( Figure 4B), or be present within/along twin planes, remarkably with the same preferential orientation as elsewhere ( Figure 4C). Some of the twins in hematite are also visible on The baddeleyite arrays can cross over grain boundaries ( Figure 4A), form locally denser domains within the same grain ( Figure 4B), or be present within/along twin planes, remarkably with the same preferential orientation as elsewhere ( Figure 4C). Some of the twins in hematite are also visible on BSE images ( Figure 4C). Zircon is also present in the sample and displays morphology varying from skeletal ( Figure 4D-F) to granular ( Figure 4G-I). The skeletal zircon, restricted to grain boundaries in hematite or between hematite and quartz, features marginal alteration and tiny inclusions of hematite and xenotime-(Y) ( Figure 4D,E). A transition from skeletal to granular morphology is observed towards the boundaries with quartz ( Figure 4F). The granular zircon form aggregates towards larger quartz pockets ( Figure 4G). Larger, single grains of zircon occur within hematite and these are surrounded by radial cracks ( Figure 4H,I). Such grains display asymmetric cores and rims with brighter bands marking the two domains on BSE images. Fluorapatite, xenotime-(Y) and pores are noted particularly within the cores or towards corroded margins in zircon ( Figure 4I).
Both hematite and quartz display textures indicative of fluid percolation ( Figure 5A,B). Pores and inclusions of siderite and magnetite mark zones of microbrecciation within sets of twin lamellae ( Figure 5A). Coarser quartz grains with partially resorbed/hooked boundaries display rotational textures comprising sub-µm size grains of hematite and acicular Ti-oxides (probably rutile) ( Figure 5B-D). Hematite aggregates nucleate within pores in such quartz ( Figure 5C). Siderite is present between hematite lamellae and also forms interstitial pockets with quartz ( Figure 4E,F). Rotational textures between the two minerals are observed in the latter case ( Figure 5F). Sub-rounded grains of fluorapatite are also noted within hematite ( Figure 5G). skeletal ( Figure 4D-F) to granular ( Figure 4G-I). The skeletal zircon, restricted to grain boundaries in hematite or between hematite and quartz, features marginal alteration and tiny inclusions of hematite and xenotime-(Y) ( Figure 4D,E). A transition from skeletal to granular morphology is observed towards the boundaries with quartz ( Figure 4F). The granular zircon form aggregates towards larger quartz pockets ( Figure 4G). Larger, single grains of zircon occur within hematite and these are surrounded by radial cracks ( Figure 4H,I). Such grains display asymmetric cores and rims with brighter bands marking the two domains on BSE images. Fluorapatite, xenotime-(Y) and pores are noted particularly within the cores or towards corroded margins in zircon ( Figure 4I). Both hematite and quartz display textures indicative of fluid percolation ( Figure 5A,B). Pores and inclusions of siderite and magnetite mark zones of microbrecciation within sets of twin lamellae ( Figure 5A). Coarser quartz grains with partially resorbed/hooked boundaries display rotational textures comprising sub-µm size grains of hematite and acicular Ti-oxides (probably rutile) ( Figure  5B-D). Hematite aggregates nucleate within pores in such quartz ( Figure 5C). Siderite is present between hematite lamellae and also forms interstitial pockets with quartz ( Figure 4E,F). Rotational textures between the two minerals are observed in the latter case ( Figure 5F). Sub-rounded grains of fluorapatite are also noted within hematite ( Figure 5G).

Whole-Rock Data
Whole-rock geochemical data for the studied ore sample shows it is composed predominantly of Fe2O3 (Table 1). A minor amount of SiO2 is present, which is represented mainly by quartz. Other components are TiO2, P2O5 and CO2, the latter two likely resulting from fluorapatite and carbonates, respectively. The oxides Al2O3, MgO, CaO, K2O and MnO are present in concentrations <0.05 wt. %.

Whole-Rock Data
Whole-rock geochemical data for the studied ore sample shows it is composed predominantly of Fe 2 O 3 (Table 1). A minor amount of SiO 2 is present, which is represented mainly by quartz. Other components are TiO 2 , P 2 O 5 and CO 2 , the latter two likely resulting from fluorapatite and carbonates, respectively. The oxides Al 2 O 3 , MgO, CaO, K 2 O and MnO are present in concentrations <0.05 wt. %.
A suite of trace elements was measured at notable concentrations ( Table 1). The chalcophile element Sb measured 7.5 ppm whereas typically associated As measured only 1 ppm. The transitional elements Cr and V are both present at concentrations ≥25 ppm. Besides relatively high TiO 2 (0.26 wt. %), other high-field strength elements (HFSE) that were measured, albeit at lower concentrations (<6 ppm), include Nb and Hf. Zirconium concentration in whole-rock is 94 ppm. Typical granite-related elements Sn (4 ppm) and W (4 ppm) are also present. With the exception of La, Ce, Y and Nd, rare-earth elements occur at concentrations <1 ppm (ΣREE = 12.8 ppm). The chondrite-normalized REE fractionation trend shows LREE enrichment (La CN /Yb CN = 10.31) and no Ce-or Y-anomaly ( Figure 6). A suite of trace elements was measured at notable concentrations ( Table 1). The chalcophile element Sb measured 7.5 ppm whereas typically associated As measured only 1 ppm. The transitional elements Cr and V are both present at concentrations ≥25 ppm. Besides relatively high TiO2 (0.26 wt. %), other high-field strength elements (HFSE) that were measured, albeit at lower concentrations (<6 ppm), include Nb and Hf. Zirconium concentration in whole-rock is 94 ppm. Typical granite-related elements Sn (4 ppm) and W (4 ppm) are also present. With the exception of La, Ce, Y and Nd, rare-earth elements occur at concentrations <1 ppm (ΣREE = 12.8 ppm). The chondrite-normalized REE fractionation trend shows LREE enrichment (LaCN/YbCN = 10.31) and no Ce-or Y-anomaly ( Figure 6).  (Table 2). Aluminum, Si, Cr, V and P Figure 6. Chondrite-normalized REE fractionation trends for whole-rock and hematite. Chondrite values from [40]. Note the marked differences for LREE (high in whole-rock, low in hematite) and the negative Y-anomaly for hematite. These features are attributable to presence of Zr-minerals and fluorapatite.

Trace Element Concentrations and Grain-Scale Distribution in Hematite
LA-ICP-MS trace element compositional data for hematite show the presence of several elements that likely account for a large portion of the whole-rock budget (Table 2). Aluminum, Si, Cr, V and P measured in the tens to hundreds ppm. Antimony is present at a concentration more than an order of magnitude higher than As. Tin and W both measured~5 ppm. Among the HFSE, Ti and Zr were measured at high concentrations, i.e., average~1490 ppm and~250 ppm, respectively; Nb and Hf measured at~5 ppm. Zirconium concentration varies, as expected, depending upon the presence or absence of visible baddeleyite inclusions on the surface of the polished block, i.e., between 68 ppm up to 600 ppm. However, given the nm-size of baddeleyite inclusions, these are not observable as fluctuating signals for Zr on the time-resolved depth profiles for individual LA-ICP-MS spot analyses ( Figure 7).
The concentrations of all other trace elements were <1 ppm. The chondrite-normalized REE fractionation trend for a mean analysis of hematite shows relative LREE depletion and HREE enrichment (La CN /Yb CN = 0.049), noticeable negative Ce-, Eu-anomalies and a strong negative Y-anomaly ( Figure 6). The differences between the whole-rock and hematite data are attributable to the role of Zr-minerals (particularly Y) and fluorapatite (LREE).
Trace element LA-ICP-MS maps of hematite reveal grain-scale compositional zoning ( Figure 8). This is expressed by relative enrichment in elements such as Zr, Hf, Ti and Cr in hematite cores and respective depletion of these elements on grain margins. The latter are, however, enriched in Nb, Sb, W and Sn. Although the fields with baddeleyite are visualized on the LA-ICP-MS element maps (Zr in Figure 8A), Zr is relatively homogenously distributed throughout hematite grain cores, as also shown by time-resolved depth profiles, with measurable, still high concentrations of Zr in hematite grains that are apparently free of baddeleyite (Figure 7). The maps also show that Zr and Hf are depleted along the margins of hematite wherever granular zircon is present ( Figure 8B). Zircon grains on the maps illustrated in Figure 8B show rims that are enriched in U relative to cores.

Zircon Electron Microprobe Data
Electron microprobe spot analysis ( Table 3) and mapping of the various zircon textures show distinct compositional differences between the cores and rims of granular and skeletal zircon (Figures 9 and 10). Besides ZrO 2 and SiO 2 , all textural variants of zircon contain measurable concentrations of MgO (~0.02 wt. %) and HfO 2 (~1.5 wt. %). The cores of granular zircon, however, contain higher concentrations of Al 2 O 3 (~0.2 wt. %), P 2 O 5 (~0.5 wt. %) and Y 2 O 3 (0.05 wt. %) relative to the rims of the same grains and also the skeletal zircon. Additionally, Sc 2 O 3 (~0.1 wt. %) was measured in zircon cores whereas rims and skeletal zircon measured below detection limit.
The core and rim textures in granular zircon are well-marked on the maps, particularly by the presence of Sc (Figure 9). The boundary between the core and rim is marked by depletion in P, but enrichment in U corresponding to the bright and dark zones on BSE and CL images, respectively ( Figure 9). The highest concentrations of P, Al and Y occur along the grain boundaries and cracks suggesting secondary element remobilization from zircon. Occurrence of xenotime-(Y) along the margin of zircon is common (e.g., the BSE image in Figure 10). The area mapped for the skeletal zircon ( Figure 10) can be considered as transitional toward the granular texture. This shows comparable trace element enrichment as in the granular type but with a patchy appearance, also due to the much smaller size of the map. Notable is the marginal enrichment in P, Al and Y on one side of the zircon.

Zircon Electron Microprobe Data
Electron microprobe spot analysis ( Table 3) and mapping of the various zircon textures show distinct compositional differences between the cores and rims of granular and skeletal zircon ( Figures  9 and 10). Besides ZrO2 and SiO2, all textural variants of zircon contain measurable concentrations of MgO (~0.02 wt. %) and HfO2 (~1.5 wt. %). The cores of granular zircon, however, contain higher concentrations of Al2O3 (~0.2 wt. %), P2O5 (~0.5 wt. %) and Y2O3 (0.05 wt. %) relative to the rims of the same grains and also the skeletal zircon. Additionally, Sc2O3 (~0.1 wt. %) was measured in zircon cores whereas rims and skeletal zircon measured below detection limit.
The core and rim textures in granular zircon are well-marked on the maps, particularly by the presence of Sc (Figure 9). The boundary between the core and rim is marked by depletion in P, but enrichment in U corresponding to the bright and dark zones on BSE and CL images, respectively ( Figure 9). The highest concentrations of P, Al and Y occur along the grain boundaries and cracks suggesting secondary element remobilization from zircon. Occurrence of xenotime-(Y) along the margin of zircon is common (e.g., the BSE image in Figure 10). The area mapped for the skeletal zircon ( Figure 10) can be considered as transitional toward the granular texture. This shows comparable trace element enrichment as in the granular type but with a patchy appearance, also due to the much smaller size of the map. Notable is the marginal enrichment in P, Al and Y on one side of the zircon.    -

Nanoscale Mineral Study
The nanoscale study was carried out for identification of: (i) Zr-rich needles as baddeleyite; and (ii) the core and rim texture in granular zircon mapped in Figure 9.

Baddeleyite
One of the typical fields with inclusions of baddeleyite was selected for the nanoscale study ( Figure 11A). Two areas containing needle-like inclusions were assessed by FIB cross-sectioning ( Figure 11B-D). Needles present beneath the surface were observed and the presence of two sets of lamellae with orientation at ~110˚/70˚ measured on the surface of the polished block could also be confirmed at depth ( Figure 11D).
HAAD-STEM imaging and EDS mapping/spectra of the foil obtained from cut #1 (Figures 11  and 12) show one of the widest (~60 nm) and longest (~3 µm) needles that were identified as baddeleyite, the monoclinic polymorph of ZrO2. High-resolution imaging was performed with the sample tilted on the [ 22 . 1 ] zone axis in hematite. Baddeleyite and host hematite are crystallographically oriented along lattice directions with ~3.7 Å repeats in each case, i.e., (011)baddeleyite parallel to (10. 2 )hematite ( Figure 12B-D). In closer detail, stepwise defects are observed to occur that adjust the ~2˚ misfit between the lattice vectors (012)^(10.-2)~86˚ and (100)^(011)~84˚ on [22 . 1]hematite and [01 1]baddeleyite zone axes, respectively ( Figure 12D). The bright dots on the atomic-scale images correspond to Fe and Zr atoms in hematite and baddeleyite, respectively, with stacking corresponding to crystal structure models on each respective zone axis ( Figure 12E,F).
STEM-EDS element maps of baddeleyite show the major elements Zr and O, with minor Hf and trace concentrations of Si, U and Ti, confirming that the chemistry of the nm-scale Zr-bearing phase in hematite as ZrO2 ( Figure 13A). Relative variation in major and trace elements between the needle and host hematite is shown on the EDS profiles ( Figure 13B). We note the relatively high concentration of Ti in baddeleyite (monoclinic) relative to hematite (rhombohedral) (Figure 13C), inferring preferential partitioning during needle crystallization. Titanium affinity for monoclinic ZrO2 (so-called baddeleyite-TiO2) has been documented from synthetic studies at the nanoscale [41].  (Figure 9). In this case, P, Al and Y show strongest enrichment on one side of the zircon. Despite the low resolution of these images, Sc is nonetheless notable as spots of higher concentration corresponding to patchy areas of enrichment in the other mapped elements. Scales in wt. %.

Nanoscale Mineral Study
The nanoscale study was carried out for identification of: (i) Zr-rich needles as baddeleyite; and (ii) the core and rim texture in granular zircon mapped in Figure 9.

Baddeleyite
One of the typical fields with inclusions of baddeleyite was selected for the nanoscale study ( Figure 11A). Two areas containing needle-like inclusions were assessed by FIB cross-sectioning ( Figure 11B-D). Needles present beneath the surface were observed and the presence of two sets of lamellae with orientation at~110 • /70 • measured on the surface of the polished block could also be confirmed at depth ( Figure 11D).
HAAD-STEM imaging and EDS mapping/spectra of the foil obtained from cut #1 (Figures 11 and 12) show one of the widest (~60 nm) and longest (~3 µm) needles that were identified as baddeleyite, the monoclinic polymorph of ZrO 2 . High-resolution imaging was performed with the sample tilted on the [22.1] zone axis in hematite. Baddeleyite and host hematite are crystallographically oriented along lattice directions with~3.7 Å repeats in each case, i.e., (011) baddeleyite parallel to (10.2) hematite ( Figure 12B-D). In closer detail, stepwise defects are observed to occur that adjust the~2 • misfit between the lattice vectors (012)ˆ(10.  Figure 12D). The bright dots on the atomic-scale images correspond to Fe and Zr atoms in hematite and baddeleyite, respectively, with stacking corresponding to crystal structure models on each respective zone axis ( Figure 12E,F).
STEM-EDS element maps of baddeleyite show the major elements Zr and O, with minor Hf and trace concentrations of Si, U and Ti, confirming that the chemistry of the nm-scale Zr-bearing phase in hematite as ZrO 2 ( Figure 13A). Relative variation in major and trace elements between the needle and host hematite is shown on the EDS profiles ( Figure 13B). We note the relatively high concentration of Ti in baddeleyite (monoclinic) relative to hematite (rhombohedral) (Figure 13C), inferring preferential partitioning during needle crystallization. Titanium affinity for monoclinic ZrO 2 (so-called baddeleyite-TiO 2 ) has been documented from synthetic studies at the nanoscale [41]. showing the Bdy needles and their relative orientations at depth. Note that more needles are aligned along two directions in cut #2, closer to the fracture, and also that the orientation of these needles is different at depth and in FIB cut #2.

Zircon
A second foil, obtained from one of the granular zircon grains was prepared from a slice cut across the core to rim boundary ( Figure 14A,B). Imaging of the foil in both BF and HAADF-STEM modes does not show this boundary, even though a number of spotty trails and streaks are present, more abundant within the core than the rim ( Figure 14C). No lattice defects or other structural changes could be identified by imaging and no chemical difference could be detected by STEM-EDS spot analysis or mapping. It is most likely that the intensity variation observed on both the BF and HAADF-STEM images is due to cumulative effects of trace element contents, even if the concentrations of individual elements are below the detection limit of the detectors. High-resolution imaging was performed with the specimen tilted on the [001] zone axis in zircon ( Figure 14D,E). The core and rim domains are parts of the same grain (single crystal with the same orientation throughout the foil) and the zircon lattice is generally free of defects. Bright spots on the HAADF-STEM images correspond to positions of overlapping Zr and Si atoms on the [001] zone axis in zircon ( Figure 14D).

Zircon
A second foil, obtained from one of the granular zircon grains was prepared from a slice cut across the core to rim boundary ( Figure 14A,B). Imaging of the foil in both BF and HAADF-STEM modes does not show this boundary, even though a number of spotty trails and streaks are present, more abundant within the core than the rim ( Figure 14C). No lattice defects or other structural changes could be identified by imaging and no chemical difference could be detected by STEM-EDS spot analysis or mapping. It is most likely that the intensity variation observed on both the BF and HAADF-STEM images is due to cumulative effects of trace element contents, even if the concentrations of individual elements are below the detection limit of the detectors. High-resolution imaging was performed with the specimen tilted on the [001] zone axis in zircon ( Figure 14D,E). The core and rim domains are parts of the same grain (single crystal with the same orientation throughout the foil) and the zircon lattice is generally free of defects. Bright spots on the HAADF-STEM images correspond to positions of overlapping Zr and Si atoms on the [001] zone axis in zircon ( Figure 14D).
STEM-EDS element mapping shows a relative enrichment in Sc within the grain core ( Figure  15A) but no direct correlation between chemistry and the bright streaks/spots on the HAADF image. A profile across the mapped area also shows notable Y, and interestingly, the contact between the rim and core domains is marked by an increase in Y and less pronounced increase in Sc concentration over a distance of 1 µm ( Figure 15B). This information complements other data about the distinct chemistry of the core and rim zones, the rims appearing depleted in P on EPMA maps, and are seen to be enriched in U on BSE and CL images (Figure 9). Such chemical variation suggests that the core and rim domains in granular zircon result from an overprint event traceable down to the nanoscale rather than primary growth. STEM-EDS element mapping shows a relative enrichment in Sc within the grain core ( Figure 15A) but no direct correlation between chemistry and the bright streaks/spots on the HAADF image. A profile across the mapped area also shows notable Y, and interestingly, the contact between the rim and core domains is marked by an increase in Y and less pronounced increase in Sc concentration over a distance of 1 µm ( Figure 15B). This information complements other data about the distinct chemistry of the core and rim zones, the rims appearing depleted in P on EPMA maps, and are seen to be enriched in U on BSE and CL images ( Figure 9). Such chemical variation suggests that the core and rim domains in granular zircon result from an overprint event traceable down to the nanoscale rather than primary growth.

U-Pb SHRIMP Zircon Geochronology
Cathodoluminescence imaging of zircon aggregates interstitial to hematite and displaying rounded textures shows that the grains lack oscillatory growth zonation typical of magmatic zircon. The grains instead feature core-rim relationships more representative of hydrothermal growth (Figure 16 and Supplementary Figure S1).

U-Pb SHRIMP Zircon Geochronology
Cathodoluminescence imaging of zircon aggregates interstitial to hematite and displaying rounded textures shows that the grains lack oscillatory growth zonation typical of magmatic zircon. The grains instead feature core-rim relationships more representative of hydrothermal growth ( Figure 16 and Supplementary Figure S1).
Eight spot analyses were collected from the zircon grains. A single grain contained high U (25 ppm), low Th (4.3 ppm), and large discordance (300%) and was not considered for further calculation. Another two grains had 206 Pb/ 238 U ratios <0.3 and were also not considered further. The remaining five analyses contained low concentrations of U and Th (from ~2-3.5 ppm and ~7-27 ppm, respectively; Table 4). One analysis is reversely discordant (−13) while the remaining four had discordance ranging from 6 to 32%. When anchored to a common-Pb upper intercept at 4500 ± 50 Ma, the data form a discordia line with a lower intercept age of 1731 ± 50 Ma (MSWD = 0.024). A 206 Pb/ 238 U weighted mean age was used due to the presence of common-Pb affecting the 207 Pb/ 206 Pb weighted mean and yielding an artificially old age. The three most concordant grains were used to obtain a 206 Pb/ 238 U weighted mean age of 1741 ± 49 Ma (MSWD = 0.86), which is interpreted to reflect the timing of zircon formation. Eight spot analyses were collected from the zircon grains. A single grain contained high U (25 ppm), low Th (4.3 ppm), and large discordance (300%) and was not considered for further calculation. Another two grains had 206 Pb/ 238 U ratios <0.3 and were also not considered further. The remaining five analyses contained low concentrations of U and Th (from~2-3.5 ppm and~7-27 ppm, respectively; Table 4). One analysis is reversely discordant (−13) while the remaining four had discordance ranging from 6 to 32%. When anchored to a common-Pb upper intercept at 4500 ± 50 Ma, the data form a discordia line with a lower intercept age of 1731 ± 50 Ma (MSWD = 0.024). A 206 Pb/ 238 U weighted mean age was used due to the presence of common-Pb affecting the 207 Pb/ 206 Pb weighted mean and yielding an artificially old age. The three most concordant grains were used to obtain a 206 Pb/ 238 U weighted mean age of 1741 ± 49 Ma (MSWD = 0.86), which is interpreted to reflect the timing of zircon formation.

Recognition of Metamorphic Textures
Hematite displays textures attributable to annealing under conditions of high-grade metamorphism, e.g., 120 • triple junction "foam" textures comparable with those observed in many metamorphosed massive pyrite ores [42]. This is concordant with an interpretation in which the Peculiar Knob ore underwent metamorphism at T > 680 • C based on the thermoremanent magnetization history of comparable coarse hematite [12]. Although no fine-scale lamellar microstructure is observed in samples studied here, the presence of twins and tiny inclusions of magnetite are common features of the coarse hematite at Peculiar Knob and are analogous to those reported by Schmidt et al. [12]. In addition, we show that, although no metamorphic silicates are present, the gangue minerals also exhibit fabrics indicative of metamorphism, e.g., rotational patterns within quartz, or imbricate intergrowths between siderite and quartz. Nonetheless, superimposed textures in hematite, including decussate boundaries, microfractures, pressure gashes, porosity are evidence for deformation associated with fluid percolation during retrograde metamorphism or to a later tectono-magmatic event.
This is the first report of high Zr (hundreds of ppm) and Ti (1,500 ppm) concentrations in hematite from Peculiar Knob. We show that only Ti can be inferred as lattice-bound, whereas sub-µm inclusions of baddeleyite can account for the Zr content as measured by LA-ICP-MS. Formation of such Zr-and Ti-bearing hematite cannot be reconciled with chemical precipitation alone in a BIF environment, as had been previously considered (e.g., [10]).

Bridging Micron-to Nanoscale Observations in Hematite: Reconstruction of Ore Evolution
Nanoscale twinning has been shown in hematite grown from acicular goethite [43], a mechanism we consider feasible during diagenesis. Nonetheless, the studied hematite is markedly coarse-grained and the twinning is most likely related to syn-metamorphic deformation, in which case accommodation of strain takes place along glide planes ( [44], and references therein). The~85 • angle between twins and crystal elongation in some hematite grains (Figure 3b) is comparable to the 84-86 • angle between the reciprocal lattice vectors in epitaxial intergrowths of baddeleyite and hematite, i.e., (011)* baddeleyite II (10.2)* hematite and (100)* baddeleyite II (01.2)* hematite ( Figure 12). Rhombohedral ("r") type twins in metamorphosed hematite were measured relative to the parent crystal by a rotation of 85 • about the r = (0221) direction [44], equivalent to the (0112)* direction in reciprocal space (indicated as (01.2)* on Figure 12C). This implies that twinning in hematite can be correlated with the fine adjustment of epitaxial intergrowths with baddeleyite during the same syn-deformational metamorphic event.
On the other hand, the angle between baddeleyite needles is distinct, by~15 • , from the "r" twin angle discussed above, with conjugate set of needles at~110 • /70 • ( Figure 4A-C and Figure 11D). These values correspond to the obtuse/acute angles between (111)ˆ(111) and (111)ˆ(111) pairs of lattice vectors, respectively, in magnetite, and such crystallographic directions are often marked by trellis exsolutions formed during cooling of titanomagnetite (Ti-Mt) (e.g., [45], and references therein). The 15 • offset is observed between the crystal orientations of some relict magnetite grains relative to the twin planes in hematite in which they are located ( Figure 3F). Whereas relict magnetite can be preserved within hematite, the two minerals share equilibrium boundaries on f O 2 − f S 2 phase diagrams over temperature ranges of many geological environments, ilmenite is not stable with hematite. However, knowing that ilmenite is a good host for Zr relative to magnetite [46], decomposition of ilmenite could have led to: (i) exsolutions of baddeleyite within magnetite undergoing transformation into hematite; and (ii) subsequent relative enrichment of Ti in that hematite.

Zirconium Mineralogy: Geological Evolution at Peculiar Knob
Metamorphic differentiation can lead to migmatite formation, thus accounting for segregation of mafic and felsic minerals in a pre-existing lithology via sub-solidus remobilization and/or partial melting. For example, based on zircon geochronology indicating the presence of detrital zircon, the Warramboo magnetite gneisses in the southeastern Gawler Craton, which was previously considered an Archean BIF, has been reinterpreted as a package of Fe-rich sediments that underwent deformation and granulite facies metamorphism during the Kimban Orogeny [47]. An increase in Fe content and the large-scale structural architecture of the Warramboo deposit was ascribed to melt loss and deformation during metamorphism. Such a process of iron-oxide concentration is, however, unlikely, by itself, to explain formation of hematite-rich orebodies at Peculiar Knob considering their high-grade, deposit size and the absence of metamorphic silicates (pyroxene, amphibole, garnet, etc.) at least not in the studied ore, among other arguments.
A potential source for the hematite protore could therefore be detrital titanomagnetite sourced from mafic/ultramafic rocks and deposited within a sedimentary basin. Such heavy mineral horizons could have been of sufficient volume to have formed an Fe-rich sediment with or without chemical precipitates. This hypothesis would also explain the Cr concentrations in hematite. A diagenesis-uplift cycle typical of Fe-rich sediment packages of this type could have led to transformation of magnetite into martite (pseudomorphic replacement of magnetite by hematite) with subsequent granoblastic coarsening and annealing during a high-grade metamorphic event such as the Kimban Orogeny. Ilmenite has been recognized as an important source of Zr during granulite facies metamorphism and baddeleyite associated with magmatic ilmenite in mafic granulites was interpreted as an exsolution product [48]. This infers that, ilmenite, although no longer present, may have been the source of Zr in the studied hematite. The age yielded by U-Pb SHRIMP analysis of zircon reported here, although not well constrained (1741 ± 49 Ma), is nevertheless similar to the age reported for the Kimban Orogeny with peak metamorphism at granulite facies (1736 ± 14 Ma; [24]).
The zircon cannot be readily linked to formation of baddeleyite in the same sample given the lack of similarity in the geochemical signature between the two Zr-minerals (e.g., Ti in baddeleyite, Sc in zircon), difference in both size and grain morphology, as well as lack of any observable relationships between the two minerals. A detrital origin was considered for Sc-bearing zircon found in association with pretulite (ScPO 4 ) and xenotime-(Y) in an Ordovician apatite-rich, oolitic ironstone from the Armorican Massif, France [49]. Low-temperature, P-bearing hydrothermal fluids were considered responsible for mineral reactions leading to Zr remobilization to form the Sc-phosphate during diagenesis and low-grade metamorphism. Scandium-rich zircon was also reported from xenotime-rich veins attributed to percolation of acidic, volatile-rich fluids, possibly granite-derived, through porous arkose units in the Browns Ranges REE deposit, Western Australia [50].
Although detrital zircon from a granitic source is an option, both the metamorphic age obtained, and the very low U concentrations represent arguments against a granitic source. Nonetheless, the association between Sc and P, as well as the inclusions of fluorapatite within the zircon cores ( Figure 9) could be indicative of comparable low-T, P-and Si-bearing, acidic fluids that could have locally interacted with inclusions of ilmenite/baddeleyite within the titanomagnetite at the time of martitization, producing the observed Sc-bearing cores in the granular zircon. Scandium could have been remobilized by such fluids from the same Fe-Ti-oxides, since magmatic ilmenite can carry tens of ppm Sc (e.g., [7]). Baddeleyite can also be converted to zircon as a result of increased silica activity [51]. Recent assessment of the P-T conditions controlling zircon behavior during metamorphism indicates that growth occurs during late-stage exhumation/cooling, whereas prograde metamorphism is responsible for zircon dissolution ( [52], and references therein). Therefore, growth of the granular zircon with Sc-P-Al-bearing cores during uplift could have been followed by zircon partial dissolution resulting in the skeletal zircon, locally preserving granular morphology with Sc-bearing domains preserved ( Figure 10).
The distinct Sc-free rims in zircon with a narrow Sc-and Y-rich boundary depicted at the nanoscale ( Figure 11B), are attributable to later fluid percolation, possibly associated with granite-derived hydrothermal fluids associated with the~1.6 Ga Hiltaba Suite intrusions intersected in drillholes at depth beneath the deposit ( Figure 1A). The modest recrystallization along the margins of hematite grains, featuring a conspicuous Sn-W-Nb-Sb trace element signature is consistent with hydrothermal overprinting associated with Hiltaba magmatism [5,53].

Conclusions and Implications
The measured Zr concentration in hematite of average~260 ppm is directly attributable to nm-scale inclusions of baddeleyite. These are likely pervasively distributed throughout the sample based on the inclusions observed beneath the surface and with smaller size. A distinction between such nm-scale inclusions and lattice-bound trace element substitutions cannot be made from LA-ICP-MS data alone and can only confirmed by nanoscale sample characterization [54].
The evidence presented here suggests that multiple events contributed to formation of the massive orebody at Peculiar Knob. Detrital titanomagnetite is considered to have been a source for Zr, Ti, Cr and Sc in a sedimentary environment via erosion of mafic rocks. The Fe-rich sedimentary package underwent diagenesis, followed by uplift and supergene ore enrichment leading to desilicification, compaction and martitization. This was followed by subsequent burial, deformation and high-grade metamorphism during the Kimban Orogeny. Later interaction with Hiltaba granitoids and distal hydrothermal fluids associated with those granites, led to W, Sn and Sb enrichment in hematite.
Zirconium mineralogy and geochemistry, the presence and distribution of Zr in iron-oxides and of Sc in zircon could represent potential indicators of ore formation. Similar characteristics might be anticipated in other Fe-rich prospects in South Australia and elsewhere. This study further demonstrates that observations bridging the micron-to nanoscales, using complimentary advanced microanalytical techniques, can provide critical constraints on ore-forming processes [12].