{'fraction_non_alphanumeric': 0.03363518758085381, 'fraction_numerical': 0.01034928848641656, 'mean_word_length': 5.611111111111111, 'pattern_counts': {'":': 0, '<': 0, '<?xml version=': 0, '>': 0, 'https://': 0, 'lorem ipsum': 0, 'www.': 0, 'xml': 0}, 'pii_count': 0, 'substrings_counts': 0, 'word_list_counts': {'cursed_substrings.json': 0, 'profanity_word_list.json': 0, 'sexual_word_list.json': 0, 'zh_pornsignals.json': 0}}
Augmentation of postswelling surgical sealant potential of adhesive hydrogels.

Two-component hydrogels formed with star polyethylene glycol amine and linear dextran aldehyde polymers (PEG:dextran) show promise as tissue-specific surgical sealants. However, there is a significant loss of adhesion strength to soft tissues following PEG:dextran swelling, which may limit material ability to appose disjoined tissues and prevent leakage from surgical sites. We covalently incorporated the modified amino acid L-3,4-dihydroxyphenylalanine (L-DOPA) into PEG:dextran to enhance postswelling sealant performance. L-DOPA is an essential component of marine animal adhesive plaques and has been used to confer wet adhesion in synthetic materials. As both PEG:dextran cohesion and adhesion are mediated by aldehyde-amine interactions, L-DOPA side-groups make it a potent network modulator with potential to affect multiple material properties. Following 1-h submersion in aqueous media, PEG:dextran doped with 3 mM L-DOPA/M aldehyde on average swelled 50.3% less, had 287.4% greater stiffness, and had 53.6% greater functional adhesion strength compared to the neat hydrogel. Increased concentrations of L-DOPA up to 11 mM L-DOPA/M aldehyde similarly curtailed swelling and mitigated property loss with hydration, but sacrificed initial functional adhesion strength, material modulus, and biocompatibility. Taken together, these data support tailored L-DOPA conjugation as a promising approach to enhance the clinical performance of PEG:dextran sealants.