{'fraction_non_alphanumeric': 0.025210084033613446, 'fraction_numerical': 0.007469654528478058, 'mean_word_length': 5.160919540229885, 'pattern_counts': {'":': 0, '<': 0, '<?xml version=': 0, '>': 0, 'https://': 0, 'lorem ipsum': 0, 'www.': 0, 'xml': 0}, 'pii_count': 0, 'substrings_counts': 0, 'word_list_counts': {'cursed_substrings.json': 0, 'profanity_word_list.json': 0, 'sexual_word_list.json': 0, 'zh_pornsignals.json': 0}}
Anisotropic electric-field-enhanced electron emission from deep-level defects in GaAs

Strongly anisotropic electric-field enhancements of the thermal emission rates of electrons from the EL3 and EL5 deep-level defects in n-type GaAs crystal have been revealed with the double-correlation deep-level transient spectroscopy. The results, analysed by taking into account both the Poole–Frenkel and phonon-assisted tunnel effects, evidence a strong coupling of the defects to the lattice vibronic modes. The defect potential anisotropy of EL3 is consistent with the defect identification as an off-centre substitutional oxygen on the arsenic site. The revealed surprising break-down of the emission-rate enhancement, for the electric field applied along the ⟨1 0 0⟩ crystallographic direction, is interpreted as resulting from a possible reorientation of the EL3 defect, owing to a jump of the oxygen ion into a neighbouring lattice site, driven by a strong electric field. On the other hand, a close pair divacancy complex is suggested to be responsible for the EL5 defect.