{'fraction_non_alphanumeric': 0.03519417475728155, 'fraction_numerical': 0.0036407766990291263, 'mean_word_length': 5.6, 'pattern_counts': {'":': 0, '<': 0, '<?xml version=': 0, '>': 0, 'https://': 0, 'lorem ipsum': 0, 'www.': 0, 'xml': 0}, 'pii_count': 0, 'substrings_counts': 0, 'word_list_counts': {'cursed_substrings.json': 0, 'profanity_word_list.json': 0, 'sexual_word_list.json': 0, 'zh_pornsignals.json': 0}}
perpendicular organization of macromolecules: synthesis and alignment studies of a soluble poly(iptycene).

We describe herein a polymeric material that prefers to align perpendicular to a stretch-aligned polymer host in the solid state. Poly(iptycene) poly-1 was synthesized from monomer 1 under hyperbaric techniques via a Diels-Alder polymerization. Polarized excitation spectra of the anthracene end groups in this material in a stretch-aligned, solution-cast poly(vinyl chloride) (PVC) film showed that the poly(iptycene) prefers to align normal (counter aspect ratio) to the stretching direction of the PVC. This is explained by a "threading" mechanism, whereby the PVC intercalates through the internal free volume presented by poly-1, similar to effects observed in small molecule iptycenes under similar conditions.