{'fraction_non_alphanumeric': 0.028346456692913385, 'fraction_numerical': 0.011023622047244094, 'mean_word_length': 5.989010989010989, 'pattern_counts': {'":': 0, '<': 0, '<?xml version=': 0, '>': 0, 'https://': 0, 'lorem ipsum': 0, 'www.': 0, 'xml': 0}, 'pii_count': 0, 'substrings_counts': 0, 'word_list_counts': {'cursed_substrings.json': 0, 'profanity_word_list.json': 0, 'sexual_word_list.json': 0, 'zh_pornsignals.json': 0}}
Evolution of magnetic behaviour in the graphitization process of glassy carbon

We have carried out DC magnetization measurements on spherical glassy carbon exposed to high temperatures and high pressures. The observed magnetic signals clearly depend on the sintering temperature. On the basis of the graphitization temperature (around 1400ºC), the behaviour can be classified into three regions: (1) paramagnetism in the no-graphitization region; (2) ferromagnetism in the near-graphitization region; (3) diamagnetic behaviour after graphitization. The magnetic transitions associated with the process of graphitization are discussed.