{'fraction_non_alphanumeric': 0.02452697967764541, 'fraction_numerical': 0.014716187806587245, 'mean_word_length': 5.4324324324324325, 'pattern_counts': {'":': 0, '<': 0, '<?xml version=': 0, '>': 0, 'https://': 0, 'lorem ipsum': 0, 'www.': 0, 'xml': 0}, 'pii_count': 0, 'substrings_counts': 0, 'word_list_counts': {'cursed_substrings.json': 0, 'profanity_word_list.json': 0, 'sexual_word_list.json': 0, 'zh_pornsignals.json': 0}}
Constructing the Efficient Ion Diffusion Pathway by Introducing Oxygen Defects in Mn2O3 for High-Performance Aqueous Zinc-Ion Batteries.

Mn-based cathodes are admittedly the most promising candidate to achieve the practical applications of aqueous zinc ion batteries because of the high operating voltage and economic benefit. However, the design of Mn-based cathodes still remains challenges due to the vulnerable chemical architecture and strong electrostatic interaction that lead to the inferior reaction kinetics and rapid capacity decay. These intrinsic drawbacks need to be fundamentally addressed by rationally decorating the crystal structure. Herein, an oxygen-defective Mn-based cathode (Ocu-Mn2O3) is designed via doping low-valence Cu-ions strategy. The oxygen-defect can modify internal electric field of material and enhance substantial electrostatic stability by compensating for the non-zero dipole moment. With the merits of oxygen deficiency, the Ocu-Mn2O3 electrode exhibits the significant diffusion coefficient in the range from 10-6 to 10-8, and good rate performance. In addition, the Ocu-Mn2O3 maintains the highly reversible cyclic stability with the capacity retention of 88 % over 600 cycles. The charge storage mechanism is explored as well, illustrating that the oxygen defects can improve the electrochemical active sites of H+ insertion, achieving the better charge storage capacity than Mn2O3.