{'fraction_non_alphanumeric': 0.04475421863536317, 'fraction_numerical': 0.025678650036683785, 'mean_word_length': 4.804255319148936, 'pattern_counts': {'":': 0, '<': 0, '<?xml version=': 0, '>': 0, 'https://': 0, 'lorem ipsum': 0, 'www.': 0, 'xml': 0}, 'pii_count': 0, 'substrings_counts': 0, 'word_list_counts': {'cursed_substrings.json': 0, 'profanity_word_list.json': 0, 'sexual_word_list.json': 0, 'zh_pornsignals.json': 0}}
Vanadium Nitride Supported on N-Doped Carbon as High-Performance ORR Catalysts for Zn–Air Batteries

It is desirable to prepare low-cost non-noble metal catalysts using a simple and efficient method. Herein, we display for the first time that nitrogen-doped hierarchical porous carbon-supported vanadium nitride (VN/NC/C-x) catalysts can be regulated by dicyandiamide (DCDA). The introduction of DCDA not only effectively controls the pore structure, but also plays an important role in adjusting oxygen vacancies and d-electrons. In addition, DCDA is not only a significant raw material for the N-doped carbon, but also a nitrogen source for the preparation of vanadium nitride. The VN/NC/C-3 catalyst was prepared after optimization of the preparation parameters, and the macro/micro structure demonstrates a superior ORR performance in alkaline media with a positive onset potential of 0.85 V and a half-wave potential of 0.75 V, the limiting current density is as high as 4.52 mA·cm−2, and the Tafel slope is only 75.54 mV·dec−1. The VN/NC/C-3-based Zn–air battery exhibits a highest peak power density (161.82 mW∙cm−2) and an excellent energy density (702.28 mAh·kgZn−1 and 861.51 Wh·kgZn−1). This work provides a valuable synthetic approach for the preparation of other transition metal nitride catalysts with a relative economic value and high performance.