{'fraction_non_alphanumeric': 0.037717601547388784, 'fraction_numerical': 0.012572533849129593, 'mean_word_length': 4.686813186813187, 'pattern_counts': {'":': 0, '<': 0, '<?xml version=': 0, '>': 0, 'https://': 0, 'lorem ipsum': 0, 'www.': 0, 'xml': 0}, 'pii_count': 0, 'substrings_counts': 0, 'word_list_counts': {'cursed_substrings.json': 0, 'profanity_word_list.json': 0, 'sexual_word_list.json': 0, 'zh_pornsignals.json': 0}}
Characterization of GaN p-n Junction Grown on Si (111) Substrate by Plasma-Assisted Molecular Beam Epitaxy

In this report, the growth of GaN p-n junction on Si (111) substrate by plasma-assisted molecular beam epitaxy (PAMBE) is demonstrated. Doping of the GaN p-n junction has been carried out using Si and Mg as n-type and p-type dopants, respectively. Silicon substrate is used to grow the GaNpn-junction. In order to improve the crystalline quality of the nitride based junction, AlN is used as a buffer layer. The optical properties of the sample have been characterized by photoluminescence (PL) and Raman spectroscopy.PL spectrum shows a strong band edge emission of GaN at ~364nm, indicating good quality of the sample.The presence of peak ~657cm-1 in Raman measurement has exhibited asuccessful doping of Mg in the sample. The structural properties are measured by high-resolution x-ray diffraction (HR-XRD) and scanning electron microscopy (SEM). The cross section of the SEM image of the sample has shown sharp interfaces.