{'fraction_non_alphanumeric': 0.04680290046143705, 'fraction_numerical': 0.028345418589321027, 'mean_word_length': 4.5, 'pattern_counts': {'":': 0, '<': 0, '<?xml version=': 0, '>': 1, 'https://': 0, 'lorem ipsum': 0, 'www.': 0, 'xml': 0}, 'pii_count': 0, 'substrings_counts': 0, 'word_list_counts': {'cursed_substrings.json': 0, 'profanity_word_list.json': 0, 'sexual_word_list.json': 0, 'zh_pornsignals.json': 0}}
Effect of different root canal obturating materials on push-out bond strength of a fiber dowel.

PURPOSE
During dowel space preparation, the instrumentation forms a thick smear layer along with sealer-occluded dentinal tubules. The purpose of this study was to evaluate the effect of different obturating materials on push-out bond strength of a fiber dowel.


MATERIALS AND METHODS
Fifty human uniradicular teeth were decoronated and prepared using the step-back technique. The specimens were divided into five groups on the basis of obturating materials: group I received no obturation; group II (ZOE) gutta-percha and zinc oxide eugenol sealer; group III (ZOAH) gutta-percha and AH plus sealer; group IV (GF) GuttaFlow; and group V (RE) with Resilon Epiphany system. Dowel spaces were made with manufacturer's provided drills, and a fiber dowel was luted. Horizontal slices were obtained from the middle third, and push-out bond strength (S) was evaluated. Statistical analysis was carried out using one-way ANOVA and post hoc Tukey's test.


RESULTS
The push-out bond strength values in the control group, ZOE, ZOAH, GF, and RE were 9.303 ± 0.565 MPa, 8.859 ± 0.539 MPa, 8.356 ± 0.618 MPa, 9.635 ± 0.435 MPa, and 8.572 ± 0.256 MPa, respectively. There was no statistically significant difference between the S values of all the groups (p > 0.05).


CONCLUSION
There was no effect of different tested obturating materials on the push-out bond strength of fiber dowels; however, further studies should be conducted.