{'fraction_non_alphanumeric': 0.0304, 'fraction_numerical': 0.0072, 'mean_word_length': 5.911602209944752, 'pattern_counts': {'":': 0, '<': 0, '<?xml version=': 0, '>': 0, 'https://': 0, 'lorem ipsum': 0, 'www.': 0, 'xml': 0}, 'pii_count': 0, 'substrings_counts': 0, 'word_list_counts': {'cursed_substrings.json': 0, 'profanity_word_list.json': 0, 'sexual_word_list.json': 0, 'zh_pornsignals.json': 0}}
Catalytic Performances of Au–Pt Nanoparticles on Phosphorous Functionalized Carbon Nanofibers towards HMF Oxidation

Herein, we reported the utilization of pre-formed Au–Pt nanoparticles deposited on phosphorus functionalized carbons as effective catalysts for the oxidation of 5-hydroxymethylfurfural (HMF) to furandicarboxylic acid (FDCA). Au–Pt nanoparticles have been prepared by a two-step methodology using polyvinyl alcohol (PVA) as protective agent and a combination of NaBH4 and H2 as reducing agents. Three carbon nanofibers (CNFs) with different graphitization degrees have been functionalized through treatment with an H3PO4–HNO3 mixture at 150 °C, in order to incorporate P groups on carbon surface. Surface and structural properties of the synthesized functionalized materials have been investigated by transmission electron microscopy (TEM), X-ray photoelectron spectroscopy (XPS), and Raman spectroscopy. The structural and surface properties of carbon nanofibers determine the amount of P-functionalities, which is a key parameter affecting the catalytic performances of Au–Pt. Indeed, the highest activity and stability has been achieved for Au–Pt deposited on the sample, which showed the largest amount of P-groups on the surface.