{'fraction_non_alphanumeric': 0.03125, 'fraction_numerical': 0.03987068965517242, 'mean_word_length': 4.664634146341464, 'pattern_counts': {'":': 0, '<': 0, '<?xml version=': 0, '>': 0, 'https://': 0, 'lorem ipsum': 0, 'www.': 0, 'xml': 0}, 'pii_count': 0, 'substrings_counts': 0, 'word_list_counts': {'cursed_substrings.json': 0, 'profanity_word_list.json': 0, 'sexual_word_list.json': 0, 'zh_pornsignals.json': 0}}
Processing and Properties of ZrB2-Cu Composites Sintered by Hot-Pressing Sintering

ZrB2-Cu composite is a new electrical contact materials in the integration of high conductivity, high wear resistance and good mechanical strength. In this paper, ZrB2-Cu composites were prepared by hot-pressing sintering at 800~900 °C under a pressure of 20 MPa.The densification of ZrB2-Cu composites was improved by the addition of nickel using an electroless metal plating technique. X-ray diffraction and scan electron microscopy were used to analyze the phase and microstructure of ZrB2-Cu composites. The results showed that ZrB2-Cu composites with 60 vol % Cu which was sintered at 900 °C had a higher relative density, highest flexural strength of 381 MPa and higher hardness of 2.16 GPa(HV). ZrB2-Cu composites with 50 vol % Cu which was sintered at 900 °C had higher flexural strength of 297 MPa and the highest hardness of 2.66 GPa.