{'fraction_non_alphanumeric': 0.03383793410507569, 'fraction_numerical': 0.005342831700801425, 'mean_word_length': 4.793814432989691, 'pattern_counts': {'":': 0, '<': 0, '<?xml version=': 0, '>': 0, 'https://': 0, 'lorem ipsum': 0, 'www.': 0, 'xml': 0}, 'pii_count': 0, 'substrings_counts': 0, 'word_list_counts': {'cursed_substrings.json': 0, 'profanity_word_list.json': 0, 'sexual_word_list.json': 0, 'zh_pornsignals.json': 0}}
Effect of Poling Atmosphere on Pb (Zr, Ti)O3 / Pb(Zr, Ti) O3 Sol-gel Composite

In the Pb(Zr,Ti)O3/Pb(Zr,Ti)O3 sol-gel composite, the influence of humidity and the influence of atmosphere during poling treatment were investigated. There were three atmospheric conditions to be surveyed. There are three states: a high humidity state where the atmosphere is not controlled, a humidity control state by injecting nitrogen gas, and a humidity control state by injecting dry air. When poling in a high humidity condition where the atmosphere is not controlled, the piezoelectric constant d33 was confirmed to be as small as a number [pC/N]. On the other hand, when the poling was performed while the humidity was controlled by injecting nitrogen gas or dry air, a relatively large value of several tens [pC/N] was confirmed. Also, the ultrasonic response of these samples was measured. As a result, it was confirmed that the ultrasonic response was clearer when the humidity was controlled by injecting nitrogen gas or dry air than when the poling was performed in a high humidity state where the atmosphere was not controlled.