{'fraction_non_alphanumeric': 0.033393501805054154, 'fraction_numerical': 0.0388086642599278, 'mean_word_length': 4.867724867724868, 'pattern_counts': {'":': 0, '<': 0, '<?xml version=': 0, '>': 0, 'https://': 0, 'lorem ipsum': 0, 'www.': 0, 'xml': 0}, 'pii_count': 0, 'substrings_counts': 0, 'word_list_counts': {'cursed_substrings.json': 0, 'profanity_word_list.json': 0, 'sexual_word_list.json': 0, 'zh_pornsignals.json': 0}}
Extended-short-wavelength infrared AlInAsSb and InPAsSb detectors on InAs

We have fabricated and characterized AlInAsSb- and InPAsSb-absorber nBn infrared detectors with 200 K cutoff wavelengths from 2.55 to 3.25 μm. Minority-carrier lifetimes determined by microwave reflectance measurements were 0.2-1.0 μs in doped n-type absorber materials. Devices having 4 μm thick absorbers exhibited sharp cutoff at wavelengths of 2.9 μm or longer and softer cutoff at shorter wavelengths. Top-illuminated devices with n+ InAs window/contact layers had external quantum efficiencies of 40-50% without anti-reflection coating at 50 mV reverse bias and wavelengths slightly shorter than cutoff. Despite the shallow-etch mesa nBn design, perimeter currents contributed significantly to the 200 K dark current. Dark currents for InPAsSb devices were lower than AlInAsSb devices with similar cutoff wavelengths. For unoptimized InPAsSb devices with 2.55 μm cutoff, 200 K areal and perimeter dark current densities at -0.2 V bias in devices of various sizes were approximately 1x10-7 A/cm2 and 1.4x10-8 A/cm, respectively.