{'fraction_non_alphanumeric': 0.041742286751361164, 'fraction_numerical': 0.011796733212341199, 'mean_word_length': 5.162011173184357, 'pattern_counts': {'":': 0, '<': 0, '<?xml version=': 0, '>': 0, 'https://': 0, 'lorem ipsum': 0, 'www.': 0, 'xml': 0}, 'pii_count': 0, 'substrings_counts': 0, 'word_list_counts': {'cursed_substrings.json': 0, 'profanity_word_list.json': 0, 'sexual_word_list.json': 0, 'zh_pornsignals.json': 0}}
What Limits the Open-Circuit Voltage of Bromide Perovskite-Based Solar Cells?

High band gap Pb bromide perovskite (APbBr3)-based solar cells, where A is a mixture of formamidinium, methylammonium, and Cs, show significantly higher, relative, VOC losses than their iodide analogs. Using photoluminescence-, quantum efficiency-, and surface photovoltage-spectroscopy measurements, we show the absence of any significant electronically active tail states within the bulk of the (FA0.85MA0.1Cs0.05)PbBr3 absorber. All methods confirm that EG = 2.28 eV for this halide perovskite, HaP. Contact potential difference measurements for this HaP, on different substrates, reveal a Z-shape dependence between the substrate work functions and that of the HaP, deposited on it, indicating that the HaP is relatively low doped and that its Fermi level is affected by the substrate onto which it is deposited. We confirm results from electron beam-induced current (EBIC) and other measurements that most voltage loss of cells, made with these HaP films, is at the HaP/selective-contact interface, specifically the...