{'fraction_non_alphanumeric': 0.02826987231105487, 'fraction_numerical': 0.01946968825491775, 'mean_word_length': 4.756166197649396, 'pattern_counts': {'":': 0, '<': 0, '<?xml version=': 0, '>': 0, 'https://': 0, 'lorem ipsum': 0, 'www.': 0, 'xml': 0}, 'pii_count': 0, 'substrings_counts': 0, 'word_list_counts': {'cursed_substrings.json': 4, 'profanity_word_list.json': 0, 'sexual_word_list.json': 0, 'zh_pornsignals.json': 0}}
COMPARISON OF RESPONSE SURFACE METHODOLOGY (RSM) AND ARTIFICIAL NEURAL NETWORKS (ANN) TOWARDS EFFICIENT OPTIMIZATION OF FLEXURAL PROPERTIES OF GYPSUM-BONDED FIBERBOARDS

In this study, the hydration behavior of gypsum paste mixed with bagasse and kenaf fibers as lignocellulosic material and fiberglass as inorganic material is evaluated. Moreover, the properties of gypsum-bonded fiberboard (GBFB) are examined using bagasse fibers (Saccharum officinarum.L), kenaf fibers (Hibiscus cannabinus.L) and industrial fiberglass. The weight ratios of fiberglass (at three levels 0, 3 and 6%), bagasse fiber (at three levels 0, 7.5 and 15%) and kenaf fiber (at three levels 0, 7.5 and 15%) to gypsum are used to make the gypsum-bonded fiberboard with the nominal density 1.10 g.cm-3 . After preparing the fiberboard, its flexural properties were examined. Response surface methodology (RSM) and artificial neural network (ANN) were used to model the bending strength of gypsum-bonded fiberboard. According to the hydration tests, it was determined that as the extractives in the lignocellulosic materials increased, the temperature of the mixture decreased and its setting time increased. According to the bending test results, it was determined that there is an ideal consistency between the predicted values and the observed data, so that as bagasse and kenaf fiber increased, the modulus of rupture (MOR) increased. Maximum MOR of panel was predicted to be 10.81 MPa and 11MPa by RSM and ANN at optimum condition. Based on the statistical analysis, the training and validation data sets of the studied models were compared by the coefficient of determination (R2), root mean squares error (RMSE) and mean absolute error (MAE). ANN model showed a much more accurate prediction than RSM in terms of the values R2, RMSE and MAE. COMPARISON OF RESPONSE SURFACE METHODOLOGY (RSM) AND ARTIFICIAL NEURAL NETWORKS (ANN) TOWARDS EFFICIENT OPTIMIZATION OF FLEXURAL PROPERTIES OF GYPSUM-BONDED FIBERBOARDS


INTRODUCTION
Panels with mineral binders have extensive applications in flooring, inner lining of walls, ceiling and partition walls. These panels, such as gypsum-bonded fiberboard, have a better linear stability than similar woodbased panels, and when exposed to fire, they show a higher resistance than other wood composite products. Adding cellulose fibers to a certain amount has a strengthening effect, and beyond the certain amount, they have negative effects. Moreover, the way the fibers are distributed in the mixture does not change the results. The comparison of the specimens containing fibers and the control specimens in a research by Rapoport et al. (2005) showed that the cracks observed due to the shrinkage from drying were narrower. For some time, organic fibers were added to gypsum, but artificial fibers were mainly used, such as fiberglass (Eve et al. 2002). Fiberglass increases the flexural load-bearing capacity of the composites (Lempfer et al. 1990). Fiberglass has a proper strength and stiffness, preserves its mechanical properties at high temperatures, has proper resistance to moisture and corrosion and is rather cheap. The relationship between adding natural fibers to gypsum matrix and the mechanical properties of the composites was evaluated (Coutts 1990, Hernández-Olivares et al. 1992. According to the properties of any binder, gypsum and cement improvement must lead to a product with better mechanical properties and higher resistance to moisture. Analysis of the extractives in the organic compounds is very important and can delay the hydration of the mineral binders and hence, it can affect the internal bonding and mechanical properties of gypsum-wood particleboards (Ahn andMoslemi 1980, Simatuupang et al. 1989). In a research on the chemical relationship between wood and cement, Hachmi and Campbel (1990) studied the wood extractives and woodcement setting. Accordingly, extractives are complex compounds that contain resin, fatty acids, terpenes, phenols, tannins and sugars. These elements are largely different in terms of their solubility and their contents are different in different species. The most important constraint for making fiberboard using mineral binders is the highly variable compatibility between wood and mineral binders.
Various factors can affect the compatibility, such as the solubility of the extractives into water or alkaline environment (Hofstrand et al. 1984, Semple et al. 2000, Hachmi and Moslemi 1989, Moslemi and Lim 1984. Species containing more than 7% of the extractives dissolved into hot water can be considered as incompatible materials (Hachmi and Moslemi 1989). Compounds of the extractives can delay the hydration. For reducing the incompatibility, it is suggested that extractives are obtained from wood using hot water and chemical additives (Moslemi et al. 1983, Zhengtian andMoslemi 1985). Conductimetry studies showed that for delaying the gypsum set in the system, the extractives delay the overall reaction. A comparative study of the penetration of acetic acid and phenolic compounds showed that these factors are the main reason of the slow-down of gypsum set. Improvement of mineral binders (cement, gypsum and soil) has become the main issue of concern in recent decades. It is tried to replace mineral reinforcing factors (fiberglass or asbestos fibers) by organic fibers such as sisal and craft pulp, or cellulose fibers (Coutts 1083, Coutts et al. 1994. Natural fibers slow down the gypsum set due to the presence water-soluble compounds (Dalmay et al. 2010). The lack of wood and forest in many countries, cheapness and abundance of lignocellulosic resources during the seasons of the year are some main reasons of using agricultural wastes. Replacement of agricultural wastes with wood can help the improvement of environmental conditions, because resources are used correctly. According to what was mentioned above, many researches are conducted on using agricultural wastes and artificial fibers. Their effects on panel properties will be different due to the different shape of bagasse, kenaf and glass fibers, different chemical compositions and their different morphological and anatomical properties.
As mentioned above, the results obtained from experimental studies showed that many variables significantly affect the bending strength, such as different fiber types and additives. Hence, optimal conditions of manufacturing must be found, which provide a balance between product properties and manufacturing cost. However, it is too costly and time-consuming to determine the influence of each parameter on the bending strength. Thus, most recent researches have been focused on prediction of properties of different composites by modeling tools rather than comprehensive experimental procedures. Artificial neural network (ANN) can give a chance to achieve the logical values of bending properties by doing some experimental treatments because of its capability to determinate complex and non-linear relationship in the data structure (Kalogirou 2001, Zhang et al. 1998). Due to the advantages mentioned, ANN methods are applied in several studies for predicting mechanical and physical properties in the wood-based composites field. Cook and Chiu (1997), Fernandez et al. (2008) Ozsahin (2013) developed an artificial neural network (ANN) model for predicting the effects of some production factors on physical properties of oriented strand board (OSB). Demirkir et al. (2013) employed the same approach for modeling the plywood bonding strength. In literature, the effects of various factors on the mechanical and physical properties of wood-based composites are discussed mostly in detail, and ANN methods are used to predict the properties of these composites. However, it is shown that no information is available to investigate and predict the effects of fibers obtained from different resources on the bending strength of gypsum-bonded fiberboard. Hence in the present study, we aimed to investigate and predict the bending strength of gypsumbonded fiberboard manufactured from different fibrous resources with a proper weight ratio of bagasse, kenaf and glass fiber to gypsum, and determine the best composition for producing gypsum-bonded fiberboard.

Origin of data
Bagasse (Saccharum Ossicinarum L.) was prepared from the southwest regions of Iran. Some worn-out kenaf sacks (Hibiscus cannabinus L.) were prepared also from a warehouse in Zabol. Fiberglass rolls were also prepared and transferred to the laboratory. The mineral binder was Omid-e-Semnan gypsum. The coarse particles of gypsum were first removed by a Mesh 40 Sieve, and fine particles were prepared to make the samples.

Chemical analysis
For chemical analysis of lignocellulosic materials, lignin content, extractives soluble in alcohol-benzene solution and ash and silica of the raw kenaf and bagasse fibers were determined according to TAPPI T 222 om-98 (1998), TAPPI T 204 cm-97 (2004 and TAPPI T 211 om-85 (2009) standards, respectively. Ten specimens were used for each test. The results are shown in Table 1.

Hydration test and compressive strength
The hydration test was performed on the gypsum paste sample using calorimetric method to evaluate the compatibility of the materials used with gypsum by determining the temperature emitted when gypsum was mixed with or without kenaf, bagasse or glass fibers and water containing extractives. The paste's setting time is a good index of the hydration reaction rate. Vicat test was performed to determine the consistency progress of the gypsum paste by recording the initial and final setting times during the change of the penetration depth of the needle of the Vicat apparatus over time. For this purpose, different weight ratios were used including 300g gypsum, 150 ml water and 15 g powder of lignocellulosic material for the treatments c, f and i, respectively, and 300 g gypsum, 150 ml pure water or extractives for the treatments g, a, b, d, e, h, j and k, respectively. For specimens with or without powder of fibers, the initial and final setting times were recorded that are a reliable parameter for determining the hydration speed. From the treatments mentioned above, specimens were also prepared in 20×20×30 mm mould for performing the compressive strength test.

Panel preparation
The effect of independent variables was examined on the modulus of rapture of the boards prepared, including fiberglass at three levels 0, 3 and 6%, bagasse fibers at three levels 0, 7.5 and 15% and kenaf fibers at three levels 0, 7.5 and 15%. Other preparation factors were constant such as the amount of water (40% of dry weight of gypsum), board's density (1.10 g . cm -3 ), press closing speed (4.5 mm . s -1 ), press pressure (15 Kg . cm -2 ), press temperature (25 ºC), press time (24h), board's thickness (10mm) and etc. The preparation process was a semi-dry process. First, water containing citric acid (99.95% water+100% citric acid 0.05) was sprayed on the dry fibers. After moistening the fibers in a laboratory mixer for 5 minutes, gypsum was sprinkled on them and they were remixed in a high speed mixer until a smooth homogeneous mixture of gypsum-fibers was obtained. The mixture was then put into a 30×30 cm wooden mold to prevent from changes in the cake's thickness and density in the final board. The cake was then put under the cold press. The boards were maintained by a clamp for 24 h at a constant pressure. After removing the clamps, the prepared boards were put into plastic bags for 48 h in order to complete the hydration process. Then, after removing the boards from plastic bags, they were exposed to the open air for 5 days in order that the moisture is balanced. After the boards were hardened,

Response surface methodology
After performing bending strength test, the results were analyzed as the response surface using experimental data that presented mathematical relations based on the quadratic regression model. This technique was used for developing a mathematical model as multivariate regression equations for the properties of the boards made. Using the response surface methodology, the independent variables were considered as functions of a mathematical model. The mathematical model is denoted by a general quadratic (regression) Equation 1 for the response surface y (Balasubramanian et al. 2008), where x i and x j are input or independent factors, β 0 is the free term of the equation, the coeffi cients β 1 , β 2 , β i are linear terms; β 11 , β 22 , βii are quadratic terms; β 12 , β 13 , β i-1,j are the interaction terms and the ϵ represents the random error.
variables (percentage of bagasse fi bers, kenaf fi bers and fi berglass) is [3]. When the regression analysis was performed, the response errors were obtained. The number of the independent variables, their codes and levels and the experimental design used are presented in Tables 2 and 4.
All coeffi cients of the cube's central axis were obtained using Expert Design software package. After determining the signifi cance of the coeffi cients (at the level of confi dence 95%), the fi nal model was described only using the coeffi cients (Lakshminarayanan and Balasubramanian 2009). It is recommended that the six-center test is used for three variables (William and Cochran 1992). Hence, based on the equation 2 where n is the number of variables and k is the number of repetitions at the cube's center, the total number of tests required for three independent [3] [4]  Artifi cial neural network ANNs are more powerful techniques in predicting non-linear relationships than the RSM technique, because they require many more experiments than the RSM. However, while the statistical relationships between input and output districts were signifi cant according to the design of experiments (obtained by RSM), ANN methods can also work correctly even with logical small data (Shanmugaprakash and Sivakumar 2013). Therefore, the experimental data achieved by RSM could be adequate to organize ANN model effectively. A MLP was developed in MATLAB (The Mathworks, Inc., R2014a) with three input neurons representing the glass fi ber, kenaf fi ber and bagasse fi ber content, a single hidden layer of neurons, and one output neurons representing the MOR of gypsum-bonded fi berboard. As seen from MLP architecture (Figure 1), the number of neurons required in the hidden layer is determined by adding the weighted inputs and the related bias (Equation 5) and also leading the input data towards a more nonlinear situation; so at least 8 neurons were needed to fi x the fi nal model using the data obtained to develop the RSM, and the addition of more neurons made the model overfi tting possible (Cheok et al. 2012, Madadlou et al. 2009).
The results showed that the fi nal setting time of the gypsum increased at the maximum temperature at the presence of the lignocellulosic material or extractives from washing the lignocellulosic material (Figure 2), and then, the maximum temperature of the mixture decreased. In addition, the increase or decrease of the hydration at different times depends on the type of the lignocellulosic material and the extractives content. Generally, kenaf with less extractives (Table  3) has a higher maximum hydration temperature and lower hydration time.
According to Zhou and Kamdem (2002), the decrease in maximum temperature may be due to the presence of the hygroscopic sponge tissue in pith or extractives in lignocellulosic materials that prevents from heat generation due to water absorption. The results indicate that as raw lignocellulosic material or watersoluble extractives obtained from washing lignocellulosic material are added, the hydration temperature decreases and the fi nal setting time increases. In Figure 2, among the test treatments with two types of lignocellulosic msaterials (bagasse and kenaf) and along with treatments with extractives from washing with hot and cold water, maximum hydration temperature was related to the treatment of gypsum+citric acid 0.05 with kenaf fi ber extractives washed with cold water, showing the temperature 42 ºC and the fi nal setting time 235 min. Since the extractives in bagasse are 1.5 times more [5] To obtain the fi nal model, all experimental data sets were divided evenly into three subsets: 70% of data sets (14 samples) were used for training the network, 15% (3 samples) were used for validation and the last 15% (3 samples) were used for testing sets. The number of neurons in the input layer is determined by the number of inputs, and those in the output layer are determined by the number of outputs (Wang and Wan 2009). The number of neurons in the hidden layer is determined by repetition in testing a number of neural networks until the mean square error (MSE) value of the output reaches a minimum.

Hydration Test
The effect of the type of lignocellulosic material and the water-soluble extractives of these materials was evaluated on hydration process of gypsum paste by measuring the fi nal setting time (t max ) and maximum hydration temperature (T max ) of the gypsum+ lignocellulosic material (bagasse and kenaf) mixture or gypsum+ extractives (from washing the lignocellulosic material with hot and cold water) mixture. T max and t max values of the test samples are given in Table 3. than those in kenaf (Table 1), and washing with hot water contains more extractives, minimum hydration temperature was for the treatment of gypsum+citric acid 0.05 with bagasse fi ber extratives washed with hot water, showing the temperature 38 ºC and the longest fi nal setting time 340 min. Analysis of the results in Tables 1, 3 and Figure  2 shows that washing the lignocellulosic material with hot water results in the solution of more extractives that changes the hydration temperature and setting time of gypsum paste.
During the gypsum hydration process, like calcium hydroxide, calcium sulfate increases the pH of the gypsum paste when adding water to the hydration process. On the other hand, the extractives of plant fi bers are generally acidic and they delay the minerals set due to the presence of sugar and extractives. Therefore, the system pH will change that may change the speed of the hydrated compounds formation; Hence, the hydration process can be negatively affected. Alkaline hydrolysis of hemicellulose and lignin is due to the formation of lignin calcium salts, polysaccaride and decrease of some sugar substances (Singh 1979). These soluble salts or deposits interfere with the hydration of the mineral physically and chemically and even can change the composition and morphology of the hydrated product (Roberts, 1967). In addition, sugar substances of wood are active hydrophilic materials. Besides setting, sugar substances added to water in the mixture of gypsum mineral create a thin layer of densifi ed water on the surface of gypsum grains as impenetrable gel under the effect of absorbency and coherence of the molecule. Although tiny gypsum particles are not compact, they are out of access of water. Therefore, the progress of hydration process is impossible and its speed slows down (Vaickelionis and Vaickelionis 2006).

Vicat
The effect of the type of lignocellulosic material and extractives on the setting time of gypsum paste during the vicat test is shown in fi gure 3.The setting time of the gypsum paste was 40 min without any additive. Acid solvent (citric acid 0.05%) was used to delay the setting speed of the gypsum paste, and the setting time increased to 165 min. Among the test treatments, the lowest setting time was for the mixture of pure gypsum and water followed by the treatment f (gypsum+ citric acid 0.05+kenaf), i.e. 85 min. The reason can be the high volume of fi bers, higher contents of cellulose and lower extractives in the lignocellolosic material (kenaf). In other words, the lower the extractives of the lignocellulosic material in gypsum paste, the shorter the setting time of the paste.
In addition, the paste of the mixture of gypsum and bagasse fi bers has led to water absorption by cell walls due to the low density and bagasse sponge structure. The increase in water absorption increases the concentration of gypsum paste, so that the penetration of vicat needle into the mixture is prevented while gypsum hydration has not completed yet. In fact, bagasse, kenaf and glass fi bers act as fi ller and are the main factor of the decrease in the setting time. The higher content of extractives soluble in the gypsum paste resulting from washing bagasse with hot water can be also an effective factor and delays the gypsum's setting time.

Compressive strength
The results from the compressive strength test are shown in Figure 4. The strengths range from 1 to 7 MPa. The compressive strength of the pure gypsum with water was highest in certain times (3, 8, 24 and 72 h).
The results showed that increasing the time, the compressive strength of the samples increases. The highest strengths were in 72 hours and the highest strength was for the pure gypsum sample (6.5 MPa). Adding citric acid 0.05% as the retarder of dehydration, the compressive strength decreases. The compressive strength of the pure gypsum + water containing citric acid 0.05% decreased to 5.1 MPa after 72 h. This can be due to the delay of the dehydration process and prevents from the formation of gypsum crystal lattice (Sanda 1982). Samples containing extractives have lower strength. The extractives delay the gypsum dehydration process and this can prevent from completion of hydration process and decreases the fi nal strength of the cured mixture.
On the other hand, for a constant wood to gypsum ratio, when the retarder of gypsum paste hydration is used, the compressive strength decreases. Generally, the lowest strength is for gypsum + bagasse or/and kenaf fi bers samples. Values show that when lignocellulosic fi bers are used in the test mixture, there is a lower strength than treatments in which only extractives are applied.

RSM model
The effect of the variables including fi berglass (X 1 ), kenaf fi ber (X 2 ) and bagasse fi ber (X 3 ) on MOR predicted by the RSM model was compared to the experimental data, and the results can be observed in Table 4. The results are plotted in Fgure 5 to provide the coeffi cient of determination (R 2 = 0.9070).
Coeffi cients of each variable in the quadratic model and its estimated multiple regression equation are presented in Table 5 and Equation 5.
ANOVA was used to illustrate which variables are statistically signifi cant in the determination of MOR at the confi dence interval 95% (Table 6). MOR values range from 1.9 to 11 MPa. According to Table 6, the Model F-value of 166.27 shows the model is signifi cant. In fact, there is no chance that a "Model F-Value" is equal to this value due to the noise. Values less than 0.0500 for X 1 , X 2 , X 3 , X 1 X 2 , X 2 X 3 , X 1 2 indicate that these model terms are signifi cant, namely model reduction may improve the model (Table 5). The value 2.65% for the "Lack of Fit F-value" shows that the Lack of Fit is not signifi cant relative to the pure error which it is good. Moreover, a high F value (166.27) with a low probability (p=0.0001) indicates the high ability of the model in predicting the results. The predicted R-squared of 0.9070 is in full agreement with the adjusted R-squared of 0.8812. 150.9, respectively, showing that the slenderness ratio of fi berglass is much higher than that of bagasse and kenaf fi bers. It is observed that the higher the fi berglass used for making gypsum-bonded fi berboard compared to bagasse and kenaf fi bers, the fl exural strength properties (MOR) increase (Figure 7). The reason can be attributed to the strong effective grid produced due to the connections between gypsum particles and fi berglass surface. These fi bers are largely compatible with minerals and lead to a rather strong connection and mix with minerals desirably (Eusebio and Suzuki 1990, Bogue 1964, Hachmi andMoslemi 1990). Fiberglass is resistant to alkalis and signifi cantly affects the composite quality due to its surface activities and hence, it has desirable compatibility with mineral (Eusebio and Suzuki 1990). Due to their high desire to form a bond with minerals, mineral fi bers provide better and stronger bonding conditions for the cohesion between wood, fi bers and cement (Mashima et al. 1994, Eusebio andSuzuki 1990). Findings of Cao et al. (2006) and Ganesan et al. (2007) showed that using fi bers for making fi ber-cement composites improved the mechanical properties, especially the fl exural strength.
They attributed the reason to the high contact surface, formation of a more effective grid and increase in the cohesion of fi bers with cement particles.  The direct effect of three variables on the MOR is shown in fi gure 6. When the content of glass fi ber, kenaf fi ber and bagasse fi ber in the panel varied from 0 to 6%, 0 to 15% and 0 to 15%, respectively, MOR value increased continuously, but the effect of glass fi ber content is greater than others as shown in fi gure 6 and Table 5.
The interactive effects of the variables (bagasse × kenaf fi bers content and kenaf fi bers × glass fi ber) showed that increasing the content of glass, kenaf and bagasse fi bers, the fl exural strength (MOR) also increases ( Figure 7).
The reason can be attributed to the high fl exibility and slenderness ratio of the fi bers (Mashima et al. 1994, Takahashi 1986). This fact affects the brittleness of gypsum composites. Due to their high slenderness ratio, mineral fi bers such as fi berglass also improve the fl exural strength and stiffness of the panels based on mineral binders such as gypsum. This result was in agreement with the previous study that using natural fi bers such as bagasse combined with other lignocellulosic waste materials for making gypsum-bonded particleboard increases the fl exural strength due to their desirable fl exibility (Nazerian and Kamyab 2013). The lowest value of MOR is related to the specimen without any fi ber (Figure 7). According to Table 1, the slenderness ratio of fi berglass, bagasse and kenaf fi bers is ≥ 300, 68.8 and

Artifi cial neural network
In order to determine the suitability of the model, the experimental (actual) values of MOR were compared to those predicted by ANN model. The experimental and predicted values for each experiment were plotted against the run numbers (Figure 8). This fi gure consists of the perfect fi t line y=x (predicted data = experimental data with a high degree of correlation) and best fi t line described by the best linear equation (y = mx + c) with a high coeffi cient of determination (R 2 = 0.9837). In order to predict the MOR values of gypsumbonded fi berboard, the experimental data were grouped into four data sets. The number of hidden neurons between 4 and 10 was selected and evaluated to determine a favorable ANN model. Mean square error (MSE) of the selected hidden neurons in the model was calculated, including 4, 6, 8 and 10 (0.6, 0.065, 0.007 and 0.35, respectively). Hence, 8 hidden neurons were chosen for the model.
The results of MOR value prediction using the developed ANN model are exhibited in Table 4, which included an input layer with three neurons (content of glass fi ber, kenaf fi ber and bagasse fi ber), an output layer with one neuron (MOR value), and 8 hidden neurons. According to the data sets used in the ANN prediction model (Figure 9), the correlation coeffi cient (R) of the predicted values (output) versus the actual values (target) were 0.99946, 0.98783, 0.99942 and 0.99183 for the training, validation, testing and all data sets, respectively.
These R values between experimental response and ANN predicted response showed in all the cases that there was a good correlation between the experimental and predicted values; so the developed ANN model trained using experimental data predicted the studied response (MOR) of panels precisely.
These R values between experimental and predicted values showed in all the cases that there was a good correlation between the actual and predicted values;  and the developed ANN model, which was trained using actual values, predicted the panel MOR precisely. Also, R 2 value suggests that 99.88% of the variation in the actual and predicted values can be explained by the model.

Comparison of RSM and ANN
In order to estimate accurate prediction of the developed models, actual mean MOR values were compared with the mean MOR predicted values of the ANN and RSM models as shown in fi gure 10. It is observed in the fi gure that the prediction of mean MOR in both models is in full agreement with that of actual values; so the experimental values are approximated by trained neural network effi ciently. However, RSM model was slightly accurate. NAZERIAN et al. ANN model predictions fit the line of perfect prediction more than RSM model. Thus, ANN model is more capable of data generalization than RSM model. This higher accuracy of prediction by ANN can be related to its approximation ability through nonlinearity of the system (Maran et al.2013), whereas RSM belongs only to a second-order polynomial (Shanmugaprakash and Sivakumar 2013). However, the negative effect of using ANN technique lies in its limited prediction due to the application of some studied variables and factors through the training process (Rajkovic et al. 2013).

CERNE
the models. The relationships between these values obtained using the CCRD and ANN models are shown in figures 5 and 8, respectively. According to Figure 8, R 2 values in training, validating and testing the data sets for MOR are greater than 0.99%. This result implies that the model designed is capable of explaining at least 0.99% of the measured data. These values also support the applicability of ANN. On the other hand, R 2 values in quadratic model are 90.70% for MOR, which are desirable. These results indicated that the models used in both methods can be selected for accurate predictions, since they both have high explanatory values. However, the normal probability diagram of the measuredpredicted values for ANN and quadratic models show that in the ANN model, data are more closely distributed on straight line ( Figure 8) than those in quadratic model ( Figure 5). This means that the errors in ANN model are distributed more normally. Hence, ANN model is selected as the regression model of MOR. Other studies are carried out about the strength properties of woodbased composites, but R 2 values obtained by ANN and quadratic models in this study are higher compared to other studies (FERNANDEZ et al. 2008, DEMIRKIR et al. 2013, ESLAH et al. 2012. The interactions among three parameters investigated for the bending strength of the panels are examined using three dimensional surface plots (Figure11).
As it can be seen, there is a considerable similarity between Figures 7 and 11. The relationship between the content of kenaf fiber and glass depicted in Figure 7. The figure shows both parameters interact with each other, which significantly affects the MOR value of the panels. MOR value of the panels is highest at the highest kenaf and glass fiber loading. As the loading of both kenaf and glass fibers decreases, MOR value of the panels decreases.
MOR value decreased from over 10.11 MPa to less than 4MPa. Similarly, figure 11 shows MOR value as a function of input parameters including the content of kenaf fiber and bagasse fiber in three dimensional patterns. The lowest MOR value is observed at kenaf fiber content loading 0% and bagasse content 0%. Increasing the content of kenaf and bagasse fibers, MOR value of panels increases; so, MOR value decreased from over 8.9 MPa to less than 2.4MPa.

CONCLUSSION
The study of the hydration process showed that the higher the non-wood extractives, the higher the setting time of the paste containing the extractives. On the other hand, the resulting temperature decreases. ANN predicted values of the experimental samples of MOR and their errors are given in Table  4. The model showed good prediction performance. Moreover, the results indicated that the values predicted by ANN had a low percent of error that is satisfactory for predicting MOR values. R 2 , Adjusted R 2 , RMSE and MAE values used to evaluate the performance of ANN and quadric models developed in this study are given in Table 7. The calculated R 2 and adjusted R 2 of the ANN model were 0.9837 and 0.9619, respectively; however, the determination coefficients and adjusted determination coefficients for RSM models were 0.9070 and 0.8812, respectively.
The high value of R 2 obtained for ANN model is indicative of its better fit (Joglekar and May 1987). The model's generalizability can be verified by its prediction accuracy for a validation data set (Eslah et al. 2012). RMSE and MAE values for ANN were less than those for RSM as shown in Table 1. These results show that the predication of RSM model has a greater deviation than the prediction of ANN model. This also means that the experimental data are fitted with a higher accuracy using the ANN model.
As seen from the results, ANN approach has shown better prediction performance than the quadratic approach based on the evaluation criteria and has a sufficient accuracy level in the prediction of MOR values. The determination coefficient (R 2 ) between the measured and predicted values is used to check the adequacy of Moreover, the longest setting time of the test treatments is related to pure gypsum with water. In addition, among treatments in which only fi bers are used in the gypsum paste, the longest setting time is related to the paste containing bagasse fi bers.
Production of gypsum-bonded fi berboard using bagasse fi bers, kenaf fi bers and fi berglass as the reinforcing fi bers increases the bending strength of the boards. Increasing bagasse and kenaf fi bers when making mineral composites, the MOR increase, but the effect of fi ber glass was higher than others.
The fl exural properties modeling were developed to predict the bending strength. The prediction of not only ANN model but also RSM were found to be in good agreement with experimental data.
The predictive ANN model is found to be capable of better predictions of fl exural properties within the range that they had been trained. The results of the ANN model indicate it is much more confi dent and accurate in estimating the values of bending strength when compared with the response surface model EUSEBIO, D.; SUZUKI, M. Production and properties of plant materials cement-bonded composites, Bulletin of the Experiment Forests, Tokyo University of Agriculture and Technology, v. 27, p. 27-38, 1990.