{'fraction_non_alphanumeric': 0.028304674112155054, 'fraction_numerical': 0.01849553861608462, 'mean_word_length': 4.932001402032948, 'pattern_counts': {'":': 0, '<': 0, '<?xml version=': 0, '>': 0, 'https://': 0, 'lorem ipsum': 0, 'www.': 0, 'xml': 0}, 'pii_count': 0, 'substrings_counts': 0, 'word_list_counts': {'cursed_substrings.json': 0, 'profanity_word_list.json': 0, 'sexual_word_list.json': 0, 'zh_pornsignals.json': 0}}
PRODUCTION AND ANALYSIS OF FUNCTIONAL SEBS NANOFIBERS BY ELECTROSPINNING

Thermoplastic elastomers (TPE) offers wide design opportunities because of its rapid prototyping that provides researchers with the acquisition of many different material properties from softness and jelly-like properties to hardness and rigidity. In this regard, poly(styrene-b-(ethylene-cobutylene)-b-styrene) (SEBS) triblock copolymer has many positive aspects and is very promising when the design and requirements of devices for different applications are considered. The combination of thermoplastic and elastomeric properties of SEBS triblock copolymer makes it one of the potential materials in the production of large-scale materials. In this study, highly elastic and functional nanofibers from SEBS triblock copolymer with the diameters of 286±93 nm were produced successfully by electrospinning for the first time, to the best of our knowledge. We believe that SEBS-based functional electrospun nanofibers will find widespread applications in medicine and water purification in the near future.


Introduction
Thermoplastic elastomers have excellent processing properties at high temperatures and demonstrate physical properties of elastomers at the working temperature. TPEs can be classified as a multi-phase material comprising rigid thermoplastic and soft rubbery phase. At the working temperature, the rigid thermoplastic phase coalesces to form small areas that function as physical cross-links between the soft blocks. Over the glass transition temperature (Tg) or melting temperature (Tm) of the thermoplastic phase, the physical cross-links disappear and the material becomes melt-processable (Ismail et al., 2016). TPEs can be produced by blending different compounds and this allows the adjustment of several processing properties and improvements in the material specifications, performance and functionality while also reducing the cost.
Since their introduction to the market, many different TPEs have been produced. The major share of the TPE market is composed of elastomers with basic structures of polystyrene (PS) block copolymers and poly(styrenebutadiene-styrene) (SBS) or poly(styrene-isoprene styrene) (SIS). In SBS and SIS, the rubbery phase is more susceptible to degradation than that of PS. This is due to the presence of reactive double bonds present in the rubbery phase and low glassy-rubbery transition temperatures. To improve the degradation resistance, the 2nd generation of PS-elastomer block copolymers with hydrogenated midblock using SEBS copolymers were released to the market after 10 years of the commercial introduction of SBS (White et al., 2011). SEBS triblock copolymers are composed of physically cross-linked soft polybutadiene and hard polystyrene segments. The soft parts of the SEBS are responsible for elastomeric properties and high resistance to thermal degradation. The hard parts are responsible for both thermoplastic performance (crystal formation) and mechanical strength (Latko et al., 2017). It is widely used due to the coexistence of soft elastomer and hard polystyrene phases. The styrenic block copolymer has remarkable mechanical properties such as ease of deformation at ambient temperature, excellent elongation and elasticity before the breaking. SEBS is also an easily processable and blendable polymer, hence finds widespread use in different applications, including coatings, adhesives, sealants and impact plastics in engineering applications (Li et al., 2017). The molecular structure of SEBS is shown in Figure 1 (Zhou et al., 2010). SEBS copolymer is also widely used in medical applications. For example, Shi et al. investigated the release of ascorbic acid and lecithin from core-shell nanofibers in contact with blood to reduce long-term hemolysis of erythrocytes and used SEBS copolymer in their experiments. As a result, mechanical and oxidative damage to erythrocyte membrane was reduced . In another study, glycidyl methacrylatehyaluronic acid was prepared and covalently-grafted onto the SEBS surface by light-initiated polymerization to obtain biocompatible matrices. By doing so, biological performance of the modified base, including platelet adhesion and cell responses, was investigated (Li et al., 2013).
Shi et al. obtained D-α-tocopheryl polyethylene glycol succinate / polyethylene oxide (TPGS / PEO) core-shell nanofibers on the SEBS surface grafted with polyethylene glycol (PEG) chains by coaxial electrospinning technique. Here in this study TPGS released from nanofibers acts as an antioxidant to protect erythrocytes from oxidative damage and reduces mechanical damage to erythrocytes in PEGgrafted layers. The grafted PEG chains provide a hydration layer on the surface of the SEBS to reduce the collision between the erythrocytes and the SEBS surface and prevents sticking of the erythrocytes, resulting in reduced mechanical damage to the erythrocyte membrane. This study proves to be useful for the production of long-term anti-hemolytic in vitro biomaterials-a new pathway for the development of non-plasticized polymers for erythrocyte protection .
There are handful number of research carried out with SEBS-based polymers in the field of medicine and there is almost no study that showed the production of the nano-sized fibers of SEBS triblock copolymers by using electrospinning or any other technique. It is possible to obtain nano-sized fibers since the first half of the 20 th century with various morphology, properties and compositions by applying the electrospinning technique (Avci et al., 2013;Calisir et al., 2016;Gergeroglu et al., 2017). Previously Rungswang et al. (2013) and Kurusu et al. (2015) have showed how to produce fibers at micron level by electrospinning method by using SEBS polymer. Here, it is the first time, we report the production of nano-sized fibers of SEBS triblock copolymers by using electrospinning technique. Morphology and mechanical analysis were also performed to assess its performance and results were compared with thermoplastic polyurethane (TPU) based nanofibers.
We believe that the produced SEBS-based nanofibers are versatile and will soon find effective usage in medical and water purification applications.

Material and Electrospinning Process
SEBS triblock copolymer was supplied as granules from Kraton Inc. with the trademark of G1652 E (Mw ~ 82,000 g mol -1 ) and has a styrene content of 30% by weight. Dimethylformamide (DMF) and toluene were used as the solvents of TPU and SEBS, purchased from Sigma Aldrich. TPU (Elastollan C95A) was also obtained from BASF. The optimum electrospinning solution was determined by varying the concentration from 7 wt% to 24 wt%.

Microwave Treatment
A microwave oven at a low power level of about 250watt power with the frequency of 2.45 GHz was used for the SEBS triblok copolymer solution to completely dissolves, leaving no remaining polymer.

Morphology Analysis
Scanning Electron Microscope (SEM) characterization of the nanofibers was performed by using the JEOL JSM 5600 instrument. All samples were first coated with 5 nm of Au and Pd under an inert gas atmosphere for SEM characterization. The average fiber diameters of the produced nanofibers were calculated using the Image J program and the measurements were taken from at least 50 different sites.

Mechanical Analysis
Mechanical analysis was carried out using Shimadzu AGS-X instrument. In the analysis, a force applied to the specimens with the dimension of 20 mm x 10 mm at a crosshead speed of 20 mm/min according to ASTM standard of D882 and D535 (Kumar and Vasita, 2017). As a result of the test, modulus of elasticity (E), tensile strength and elongation at break were investigated.

SEM Characterization and Optimization of SEBS Nanofibers
It is well known that the changes in solution concentration, viscosity and surface tension are important parameters affecting the fiber formation. Fibers with beaded structure can be formed due to the low surface tension of the solution with low concentration while the formation of fiber due to higher viscosity can be seen with the solution of the higher concentration (Subbiah et al., 2005). In the first trial, toluene solvent mixtures containing 7 wt% and 14 wt% SEBS were prepared, and these two solutions were stirred by a magnetic stirrer at 25 °C for 8 hours until colorless solutions were obtained. Later, attempts were made to produce nanofibers from electrospinning solutions transferred into the syringe, but no fiber formation was observed with either solution as seen in Figure 2. During the electrospinning process, the charges on the surface of the jet formed at the tip of the syringe repulse each other. For this reason, extensions occur on the jet. The conductivity of the solution can be increased to carry more load on the solution. If the electrospinning solution does not exhibit sufficient stress, the bead structure can be observed on the collector. To overcome this problem, salt can be added to the electrospinning solution (Zong et al., 2002). Hence, 4 wt% NaCl was added to toluene solvent mixtures containing SEBS concentration of 7 wt% and 14 wt% and electrospinning process was performed again. Although the fiber formation was observed, continuity was not achieved and the solution dripped to the substrate at regular intervals. The reason can be the molecular weight or the concentration of the polymers affects the solution viscosity. It is reported that when the viscosity of the solution used is low, the solution drops by the force of gravity during the process and drops from the needle point, thus preventing the production (Deitzel et al., 2001). For this reason, further experiments were carried out with the higher concentration of the polymer in the solution. In addition, during the electrospinning process, the solvent in the solution must evaporate rapidly. In course of the jet thinning, phase separation is formed. Some of the most important parameters for the electrospinning process include the evaporation rate and the vapor pressure of the solvent in the solution. It has been reported that the average fiber diameter of the nanofibers obtained from the solutions prepared using higher concentration of DMF decreases. It is also known that more uniform and dense fiber can be obtained by using highly volatile solutions (Subbiah et al., 2005;Ramarkrisha et al., 2005).
On the other hand, DMF-Toluene (1:1 v/v) solvent mixture containing 15 wt% SEBS concentration was stirred at 500 rpm at 50 ˚C but turbidity was observed. Therefore, a mixture of DMF-toluene (3:7 v/v) containing 15 wt% SEBS was prepared and stirred until completely dissolved at 500 rpm at 50 °C temperature in which a colorless electrospinning solution was obtained. The electrospinning of the prepared solution was carried out at room temperature under a voltage of 15 kV and a flow rate of 1 mL/hr at syringe tip-collector distance of 10 cm. As seen in Figure 3A, the beaded structures were observed. It is reported in the literature that if the solution viscosity is low, bead-like structures can be observed and the liquid jet breaks during the production. As viscosity increases, the beaded structures become ellipse-like structure from spherical (Deitzel et al., 2001).

Figure 3. SEM images of the fiber morphologies produced under different conditions by using DMF-toluene (3:7 v/v) solution. A. 15 wt% SEBS (Scale bar is 10 μm). B. 18 wt% SEBS (Scale bar is 2 μm). C. 21 wt% SEBS (Scale bar is 1 μm). D. 24 wt% SEBS (Scale bar is 1 μm).
DMF-Toluene (3:7 v/v) solution containing 18 wt% SEBS concentration was then prepared and mixed until completely dissolved at 400 rpm at 50 ˚C to obtain a colorless solution. The electrospinning of the prepared solution was carried out at a temperature of 18 °C with a humidity of 39.6% at a distance of 10 cm under a voltage of 17 kV and a flow rate of 12 μL/min. It is clearly seen that although there is a high bead density, the fiber structure started to form as follow ( Figure 3B). This is a strong indication that the increase in solution viscosity leads to the formation of uniform fiber structure under optimized conditions. Therefore, the polymer concentration was further increased to 21 wt%. After many trials, the electrospinning of the prepared solution was fixed under about 17 °C with applying the voltage of 17 kV and at a flow rate of 10 mL/hr with a distance of 10 cm under 47% humidity. As can be seen in Figure 3C, further improvement of the fiber structure was observed.
In order to fabricate the electrospun fibers with desired morphologies and smaller diameters, the concentration of 24 wt% SEBS was prepared. Uniform and nano-sized fiber formation was obtained under the electrospinning conditions of 10 cm distance at a flow rate of 10 mL/hr at 17 °C, 18 kV applied voltage under 47% humidity. As seen in Figure 3D, improved fiber structure and morphology were obtained uniformly with the average fiber diameter of about 357 n Besides the influence of solution concentration on the fiber structure, the effect of other parameters such as humidity was also investigated. It is stated in the literature that if the relative humidity of the environment is greater than 60%, it can prevent the formation of nanofibers (Subbiah et al., 2005). In addition, as the relative humidity increases, the fiber diameter also increases, which is due to the electrical charging on the surface of the polymer solution (Kozanoğlu et al., 2006). Therefore, in our experiment, further re-optimization steps were necessarily carried out. In order to improve on the nanofiber structures, 24 wt% SEBS triblock copolymer solution was microwaved for 105 seconds in total while power level was kept at about 250-watt with the frequency of 2.45 GHz for 20 -25 -40 -20 seconds. It was then stirred at 25 ° C in a magnetic stirrer until a colorless level was achieved at 600 rpm. The dissolved solution was successfully transformed to the nanofibers at an average diameter of 286 ± 93 nm upon the application of 18 kV voltage with a flow rate of 2 mL/hr at a distance of 10 cm ( Figure 4A). As reported previously, the dissolution of some natural and synthetic polymers can be facilitated by microwave irradiation (Swatloski et al., 2013). The effect of microwave radiation on the polar solvent of DMF can improve oxygen mobility resulting much faster dissolving process than the conventional methods (Cadafalch Gazquez et al., 2017).

Figure 4. SEM images of the fiber morphologies produced using SEBS (upon microwave treatment) and TPU polymers. A. Electrospun nanofibers by using DMF-Toluene (3:7 v/v) containing 24 wt% SEBS after the microwave oven treatment. B. Electrospun nanofibers by using DMF containing 18 wt% TPU. (Scale bar is 1 μm).
SEBS nanofibers were also compared with TPU nanofibers to demonstrate the relative differences. Uniform TPU nanofibers were obtained with an average diameter of about 314 nm ( Figure 4B). Size analysis was performed using at least 50 different nanofibers from SEM images. The process parameters were fixed at the solution conditions containing 18 wt% TPU, a flow rate of 0.2 mL/hr at a distance of 20 cm under an applied voltage of 24 kV.

Mechanical Analysis
The mechanical properties of the materials used in different fields such as medicine and engineering must meet the requirements for the specific application area. For example, in some cases the elongation at break is important while sometimes the strength is at the foreground. Thus, the mechanical properties of SEBS  Figure  5A and 5B display stress-strain graphs for SEBS and TPU nanofibers, respectively.

Conclusion
In this study, the production of nanofibers from the SEBS triblock copolymer has been successfully accomplished for the first time. SEBS solutions were prepared at different concentrations and the most suitable solution was determined as DMF:Toluene (3:7 (v/v)) containing 24 wt% SEBS. At this specific concentration, nanofibers of about 356 nm in diameter were obtained. In addition, smaller sizes of nanofibers in diameter (286 nm) were obtained by increasing the relative humidity and microwave treatment of the solution.
When the mechanical analysis results are examined, it was found that the elongation at break of SEBS triblock copolymer is much higher than TPU polymer. At the same time, the SEBS nanofiber strength is sufficient enough for use, for example, in medical and filtration fields. It is also clearly understood that the addition of suitable additives to SEBS triblock copolymer has a strong potential to produce wound-dressing materials. Therefore, water filtration and antibacterial tests of SEBS nanofibers with the additives are still continuing.
With further investigations, we hope to develop a new generation nanofibers for different applications; especially for medical and water filtration technologies.