{'fraction_non_alphanumeric': 0.031731706436590734, 'fraction_numerical': 0.03198440489513014, 'mean_word_length': 4.511738957421409, 'pattern_counts': {'":': 0, '<': 0, '<?xml version=': 0, '>': 0, 'https://': 0, 'lorem ipsum': 0, 'www.': 0, 'xml': 0}, 'pii_count': 0, 'substrings_counts': 0, 'word_list_counts': {'cursed_substrings.json': 0, 'profanity_word_list.json': 0, 'sexual_word_list.json': 0, 'zh_pornsignals.json': 0}}
Fabrication of Multilayered Two-Dimensional Micelles and Fibers by Controlled Self-Assembly of Rod-Coil Block Copolymers

Fabricating hierarchical nanomaterials by self-assembly of rod-coil block copolymers attracts great interest. However, the key factors that affect the formation of the hierarchical nanomaterials have not been thoroughly researched. Herein, we have synthesized two diblock copolymers composed of poly(3-hexylthiophene) (P3HT) and polyethylene glycol (PEG). Through a heating, cooling, and aging process, a series of multilayered hierarchical micelles and fibers were prepared in alcoholic solutions. The transition from fibers to hierarchical micelles are strictly influenced by the strength of the π-π stacking interaction, the PEG chain length, and solvent. In isopropanol, the P3HT22-b-PEG43 could self-assemble into hierarchical micelles composed of several two-dimensional (2D) laminar layers, driven by the π-π stacking interaction and van der Waals force. The P3HT22-b-PEG43 could not self-assemble into well-defined nanostructures in methanol and ethanol, but could self-assemble into fibers in isobutanol. However, the P3HT22-b-PEG113 with a longer corona block only self-assembled into fibers in four alcoholic solutions, due to the increase in dissolving capacity and steric hindrance. The sizes and the size distributions of the nanostructures both increased with the increase in polymer concentration and the decrease in solvent polarity. This study shows a method to fabricate the hierarchical micelles.


Synthesis and Characterization of the Block Copolymers
The P3HT 22 -b-PEG 43 and P3HT 22 -b-PEG 113 were synthesized according to our previous report [53], as shown in Scheme S1. The two block copolymers were characterized by proton nuclear magnetic resonance spectroscopy (NMR) and gel permeation chromatography (GPC). The chemical shifts of the block copolymers and the molar ratios of the constituents are shown in Figure S1 and Figure S2, which correspond to the theoretical values. The GPC experiments ( Figure S3) show that the number-average weights (M n ) of the two block copolymers are 7173 g·mol −1 and 9339 g·mol −1 , respectively, which are larger than the M n (3886 g·mol −1 ) of the P3HT 22 block. The corresponding polydispersity index (PDI) values of the two block polymers are 1.07 and 1.05, respectively, which indicate the narrow distributions. The results of 1 H NMR and GPC demonstrate the successful synthesis of the two block copolymers.

The Effect of the PEG Chain Length on the Self-Assembly of the Block Copolymer
In previous studies [53], it was found that the sizes and aspect ratios of the 2D rectangular micelles could be controlled by varying the PEG chain length of the block copolymers with a constant long P3HT chain length. However, the shapes of the assemblies did not change with the variation of the PEG chain length, which did not offer adequate support to help us to understand the formation of the 2D micelles. Thus, in order to further understand the effect of the core-forming blocks and corona blocks on the formation of the 2D hierarchical micelles, the P3HT 22 chain with an intermediate strength of π-π stacking interaction was selected as a constant core-forming block. In this study, the influence of the PEG chain length on the self-assembly of the block copolymers was first studied in i-PrOH at a constant polymer concentration (c = 0.005 mg . mL -1 ). In solution in i-PrOH, the block copolymer P3HT 22 -b-PEG 43 self-assembled into 2D hierarchical micelles, which was confirmed by transmission electron microscopy (TEM) (Figure 1a,b). It was found that these 2D hierarchical micelles were composed of several rectangular 2D laminar layers, which was different from the shape of the regular 2D rectangular micelles self-assembled by P3HT 22 -b-PEG 22 reported in previous studies [53]. The number-average diagonal length (D n ) of these multilayered hierarchical micelles was 2549 nm, which was slightly larger than the size (D n = 2388 nm) of the regular 2D rectangular micelles self-assembled by P3HT 22 -b-PEG 22 [53]. This was probably owing to the imperfect stacking of the 2D laminar layers. Figure 2a shows that the diagonal length of these multilayered 2D hierarchical micelles ranged from 800 to 4700 nm, implying a wide distribution. This wide size distribution was also confirmed by the dispersity (D w /D n = 1.09, D w -the weight-average diagonal length) of these 2D hierarchical micelles. The size of the rectangular 2D laminar layers included in the multilayered 2D hierarchical micelles was also analyzed. The length of the 2D laminar layers ranged from 800 to 3900 nm (Figure 2b), indicating a wide distribution. The number-average length (L n ) of the 2D laminar layers was 2359 nm, which was slightly larger than the length (L n = 2140 nm) of the regular 2D rectangular micelles self-assembled by P3HT 22 -b-PEG 22 [53]. This may have contributed to the broad size distribution of the 2D laminar layers. The dispersity (L w /L n = 1.102, L w -the weight-average length) and the aspect ratio (R= 3.234) of the 2D laminar layers were both larger than the corresponding values of the regular 2D rectangular micelles self-assembled by P3HT 22 -b-PEG 22 [53]. As the PEG chain length increased, the variation of the aspect ratio of the 2D nanostructures formed by P3HT 22 -b-PEG m was in accordance with the corresponding change of the regular 2D rectangular micelles formed by P3HT 43 -b-PEG m [53]. The standard deviation (σ) of the aspect ratio of the 2D laminar layers was 1.328, implying that the shape of the 2D laminar layers was not uniform. The wide size dispersity and the large standard deviation of the aspect ratio of the 2D laminar layers were probably due to the influences of the intermediate π-π stacking interaction and the variation in PEG chain length.
The multilayered structure of the 2D hierarchical micelles was also confirmed by atomic force microscopy (AFM) (Figure 3a). Figure 3b shows that the heights of the adjacent laminar layers were 3.463 nm, 3.075 nm and 5.616 nm, respectively. The difference in the heights of the adjacent layers indicates that the 2D laminar layers should be composed of a thinner nanostructure. To confirm the formation process of the multilayered 2D hierarchical micelles, we studied the morphologies of the assemblies formed by the P3HT 22b-PEG 43 when the temperature of the solution decreased to 45 • C. Figure S4a shows the morphologies of the transition structures, which were composed of a series of linearly arranged fibers. This result demonstrates that the P3HT 22 -b-PEG 43 first self-assembled into fibers, and then the fibers were further reorganized to form the multilayered 2D hierarchical micelles, as shown Figure 4a,b. The length of the 2D laminar layers should be equal to the contour length of the fibers. The formation process of the multilayered 2D hierarchical micelles is the same as that of the regular 2D rectangular micelles [53].  The multilayered structure of the 2D hierarchical micelles was also confirmed by atomic force microscopy (AFM) (Figure 3a). Figure 3b shows that the heights of the adjacent laminar layers were 3.463 nm, 3.075 nm and 5.616 nm, respectively. The difference in the heights of the adjacent layers indicates that the 2D laminar layers should be composed of a thinner nanostructure. To confirm the formation process of the multilayered 2D hierarchical micelles, we studied the morphologies of the assemblies formed by the P3HT22-b-PEG43 when the temperature of the solution decreased to 45 °C. Figure S4a shows the morphologies of the transition structures, which were composed of a series of linearly arranged fibers. This result demonstrates that the P3HT22-b-PEG43 first self-assembled into fibers, and then the fibers were further reorganized to form the multilayered 2D hierar-  The multilayered structure of the 2D hierarchical micelles was also confirmed by atomic force microscopy (AFM) (Figure 3a). Figure 3b shows that the heights of the adjacent laminar layers were 3.463 nm, 3.075 nm and 5.616 nm, respectively. The difference in the heights of the adjacent layers indicates that the 2D laminar layers should be composed of a thinner nanostructure. To confirm the formation process of the multilayered 2D hierarchical micelles, we studied the morphologies of the assemblies formed by the P3HT22-b-PEG43 when the temperature of the solution decreased to 45 °C. Figure S4a shows the morphologies of the transition structures, which were composed of a series of linearly arranged fibers. This result demonstrates that the P3HT22-b-PEG43 first self-assembled into fibers, and then the fibers were further reorganized to form the multilayered 2D hierar- In the i-PrOH solution of the P3HT 22 -b-PEG 113 , there were no 2D micelles. The block copolymer all self-assembled into fibers (Figure 1c,d). The number-average contour length (L n ) of these fibers was 440 nm, which was obviously smaller than the length of the 2D laminar layers included in the 2D hierarchical micelles formed by P3HT 22b-PEG 43 . Figure 2c shows that the contour length of these fibers ranged from 150 to 1050 nm, indicating a broad distribution. The dispersity (L w /L n = 1.172) of the fibers further confirmed the broad distribution. The AFM result (Figure 3c,d) shows that the height of the fibers was 2.946 nm. The width of the fibers was calculated to be 11.0 nm from the TEM and AFM results. According to the estimation of the sizes of the P3HT 22 chain (as shown in Figure S5), the height of the fibers is slightly less than twice the length of side alkyl chain of P3HT, and the width of the fibers is slightly larger than the length of the P3HT 22 chain. This result means that the fibers should be composed of two laminar layers of the P3HT 22 chain, as shown in Figure S6. copolymer all self-assembled into fibers (Figure 1c,d). The number-average contour length (Ln) of these fibers was 440 nm, which was obviously smaller than the length of the 2D laminar layers included in the 2D hierarchical micelles formed by P3HT22-b-PEG43. Figure  2c shows that the contour length of these fibers ranged from 150 to 1050 nm, indicating a broad distribution. The dispersity (Lw/Ln= 1.172) of the fibers further confirmed the broad distribution. The AFM result (Figure 3c,d) shows that the height of the fibers was 2.946 nm. The width of the fibers was calculated to be 11.0 nm from the TEM and AFM results. According to the estimation of the sizes of the P3HT22 chain (as shown in Figure S5), the height of the fibers is slightly less than twice the length of side alkyl chain of P3HT, and the width of the fibers is slightly larger than the length of the P3HT22 chain. This result means that the fibers should be composed of two laminar layers of the P3HT22 chain, as shown in Figure S6.  The above results prove that the morphologies of the nanostructures were greatly influenced by the variation in PEG chain length, which should be due to the influences of the conjugated P3HT block and PEG block. It is known that the strength of π-π stacking interaction decreases with an decrease in P3HT chain length [54]. Meanwhile, the van der Waals interaction force of the block copolymer with a constant P3HT chain length decreases with an increase in PEG chain length. This is because the dissolving capacity increases with the increase in PEG chain length. In addition, the steric hindrance also increases with the increase in PEG chain length, which favors the formation of the fibers. Thus, the intermediate strength of the π-π stacking interaction and the weaker van der Waals interaction force cannot supply enough force to induce the fibers to form 2D micelles in the solution of the P3HT 22 -b-PEG 113 .  The above results prove that the morphologies of the nanostructures were greatly influenced by the variation in PEG chain length, which should be due to the influences of the conjugated P3HT block and PEG block. It is known that the strength of π-π stacking interaction decreases with an decrease in P3HT chain length [54]. Meanwhile, the van der Waals interaction force of the block copolymer with a constant P3HT chain length decreases with an increase in PEG chain length. This is because the dissolving capacity increases with the increase in PEG chain length. In addition, the steric hindrance also increases with the increase in PEG chain length, which favors the formation of the fibers. Thus, the intermediate strength of the π-π stacking interaction and the weaker van der Waals interaction force cannot supply enough force to induce the fibers to form 2D micelles in the solution of the P3HT22-b-PEG113.

The Effect of the Polymer Concentration on the Self-Assembly of the Block Copolymer
The influence of the polymer concentration on the self-assembly of the two block copolymers was also investigated. The self-assembly of P3HT 22 -b-PEG 43 in i-PrOH at different polymer concentrations was studied first. In the solution at c = 0.001 mg . mL −1 , the block copolymer still self-assembled into 2D hierarchical micelles composed of several 2D laminar layers (Figure 5a and Figure S7a). The D n of the 2D hierarchical micelles and the L n of the corresponding 2D laminar layers were 1699 nm and 1570 nm, respectively. The tiny difference in D n of the 2D hierarchical micelles and in L n of the corresponding 2D laminar layers indicates that the stacking of the 2D laminar layers was quite good, which could be further confirmed by the statistical size distributions. The statistical diagonal length of the 2D hierarchical micelles ranged from 700 to 3000 nm (Figure 5d). Meanwhile, the statistical length of the 2D laminar layers ranged from 700 to 2900 nm (Figure 5g). The polydispersity of the 2D hierarchical micelles (D w /D n = 1.074) and the 2D laminar layers (L w /L n = 1.068) implies good size distributions. The sizes of the 2D hierarchical micelles and their 2D laminar layers obtained in the solution (c = 0.001 mg . mL −1 ) were obviously smaller than the corresponding sizes of the nanostructures obtained in the solution (c = 0.005 mg . mL −1 ). As the polymer concentration increased from 0.005 to 0.015 mg . mL −1 , the sizes of the 2D hierarchical micelles (Figure 5b and Figure S7b,c) and the corresponding 2D laminar layers obviously increased. The D n of the 2D hierarchical micelles and the L n of the 2D laminar layers were 2987 nm and 2598 nm, respectively. However, the size distributions of the corresponding nanostructures became broad. Figure 5e shows that the statistical diagonal length of the 2D hierarchical micelles ranged from 900 to 5800 nm. The statistical length of the 2D laminar layers ranged from 600 to 5300 nm, as shown in Figure 5h. The broad distributions were also confirmed by the polydispersity of the 2D hierarchical micelles (D w /D n = 1.173) and the 2D laminar layers (L w /L n = 1.190). When the polymer concentration increased from 0.015 to 0.03 mg . mL −1 , amounts of special hierarchical micelles were found ( Figure 5c and Figure S7d,e). It was easy to find that these special hierarchical micelles were composed of a series of linearly arranged 2D laminar layers. To further confirm the defined structures of these special hierarchical micelles, we studied the morphologies of the transition structures formed by P3HT 22 -b-PEG 43 when the temperature of the solution (c = 0.03 mg . mL −1 ) decreased to 45 • C. Figure S4b shows that the transition structures were composed of a series of linearly arranged fibers. These fibers arranged in a direction that was perpendicular to the length of the fibers. This result further proves that the special hierarchical micelles were formed by the reorganization of the fibers. The length of the linearly arranged 2D laminar layers should be equal to the length of the intermediate fibers. The probable formation process of these special hierarchical micelles is shown in Figure 4c. The D n of the special hierarchical micelles was 4642 nm, which was observably larger than the D n of the hierarchical micelles obtained in solutions with lower polymer concentration. This was due to the linear arrangement of the 2D laminar layers included in the special hierarchical micelles. The size distribution of the special hierarchical micelles was very broad, which could be confirmed by the dispersity (D w /D n = 1.211) and the statistical diagonal length. Figure 5f shows that the statistical diagonal length of the special hierarchical micelles ranged from 1400 to 9300 nm. The L n of these linearly arranged 2D laminar layers was 2155 nm, which was slightly smaller than the L n of the 2D laminar layers included in the hierarchical micelles obtained in the solution (c = 0.015 mg . mL −1 ). This should contributed to the broad length distribution (L w /L n = 1.203) of the 2D laminar layers. Figure 5i shows that the statistical length of the 2D laminar layers ranged from 800 to 5100 nm, further implying a broad distribution. When the polymer concentration was above 0.05 mg . mL −1 , the hierarchical micelles composed of a series of linearly arranged 2D laminar layers could still be found ( Figure S7f). The sizes of these hierarchical micelles and the 2D laminar layers were very large and irregular, so they were difficult to measure. The increase in the sizes of the multilayered hierarchical micelles and the corresponding 2D laminar layers with the increase in polymer concentration is shown in Table 1. Table 1 shows that the aspect ratio (R) and the corresponding standard deviation (σ) of the 2D laminar layers increased with an increase in polymer concentration.
In solution in i-PrOH, the shapes of the nanostructures formed by the P3HT 22 -b-PEG 113 were not influenced by the variation in polymer concentration. The diblock copolymer P3HT 22 -b-PEG 113 all self-assembled into fibers in a wide range of polymer concentrations (Figures 1c and 6a,c,e). However, the sizes of the fibers were distinctly affected by varying the polymer concentration. Figure 6b shows that the contour length of the fibers formed in the solution (c= 0.001 mg . mL −1 ) ranged from 80 to 710 nm. In solution at c = 0.015 mg . mL −1 , the contour length of the fibers ranged from 90 to1200 nm (Figure 6d), which was obviously larger than the lengths of the fibers obtained in the solutions (c = 0.001 and 0.005 mg . mL −1 ). When the polymer concentration increased from 0.015 to 0.03 mg . mL −1 , the contour length of the fibers continued to increase and ranged from 190 to 2200 nm (Figure 6f). Table 2 shows that the number-average contour length (L n ) of the fibers increased with the increase in polymer concentration. The polydispersity (L w /L n ) of all the fibers, ranging from 1.170 to 1.350, reveals that all the fibers have broad size distributions and that the size distribution of the fibers became broader with the increase in polymer concentration.

8 of 14
shows that the aspect ratio (R) and the corresponding standard deviation (σ) of the 2D laminar layers increased with an increase in polymer concentration.  1.203 Dw represents the weight-average diagonal length of the multilayered hierarchical micelles; Dn represents the number-average diagonal length of the multilayered hierarchical micelles; Lw represents the weight-average length of the 2D laminar layers included in multilayered hierarchical micelles; Ln represents the number-average length of the 2D laminar layers included in multilayered hierarchical micelles; R represents the aspect ratios of the 2D laminar layers; σ represents the standard deviations of the R.
In solution in i-PrOH, the shapes of the nanostructures formed by the P3HT22-b-  D w represents the weight-average diagonal length of the multilayered hierarchical micelles; D n represents the number-average diagonal length of the multilayered hierarchical micelles; L w represents the weight-average length of the 2D laminar layers included in multilayered hierarchical micelles; L n represents the number-average length of the 2D laminar layers included in multilayered hierarchical micelles; R represents the aspect ratios of the 2D laminar layers; σ represents the standard deviations of the R.
Polymers 2022, 14, 4125 9 of 15 mg . mL −1 , the contour length of the fibers continued to increase and ranged from 190 to 2200 nm (Figure 6f). Table 2 shows that the number-average contour length (Ln) of the fibers increased with the increase in polymer concentration. The polydispersity (Lw/Ln) of all the fibers, ranging from 1.170 to 1.350, reveals that all the fibers have broad size distributions and that the size distribution of the fibers became broader with the increase in polymer concentration.  The variation in the sizes of the 2D laminar layers and fibers with the increase in polymer concentration could be explained as follows. As the polymer concentration increases, the Gibbs free energy of the system increases. The formation of nanostructures with larger sizes was more beneficial for reducing the Gibbs free energy of the system. Thus, the lengths of the 2D laminar layers and fibers both increase with an increase in polymer concentration. Meanwhile, the self-assembly of the block copolymers become more complicated in a higher polymer concentration, resulting in that the aspect ratio (R) and the corresponding standard deviation (σ) of the 2D laminar layers increased with the increase of the polymer concentration. L w represents the weight-average contour length of the fibers, L n represents the number-average contour length of the fibers.

The Effect of the Solvent on the Self-Assembly of the Block Copolymer
The shapes and sizes of the nanostructures can usually be influenced by the solvent because the dissolving capacity, and the interactions of the conjugated blocks could be influenced by the solvent. Thus, the influence of solvents on the self-assembly of the two block copolymers in different solvents was also studied. Owing to their similar molecular structures, methanol, ethanol, and isobutanol were chosen as the additional selective solvents. In fact, the morphologies of the assemblies formed by the P3HT 22 -b-PEG 43 were strictly influenced by the solvents. In methanol and ethanol, the diblock copolymer could not self-assemble into well-defined nanostructures ( Figure S8a,b). Furthermore, a lot of red precipitates were found in the two solutions during the aging process. In solution in isobutanol (c= 0.015 mg . mL −1 ), the diblock copolymer could only self-assemble into the fibers ( Figure S8c) with a number-average contour length (L n ) of 1355 nm. The contour length of these fibers, ranging from 130 to 4000 nm ( Figure S8d), implies that these fibers have a broad distribution, which was further confirmed by the dispersity (L w /L n = 1.572).
In contrast, P3HT 22 -b-PEG 113 could be dispersed in all three alcohol solutions. The shapes of the nanostructures were not influenced by the variation of the solvent. In methanol, ethanol and isobutanol, the block copolymer all self-assembled into fibers (Figure 7a,c,e). However, the sizes of these fibers were greatly influenced by the variation of the solvent. In solution in methanol (c= 0.015 mg . mL -1 ), the block copolymer self-assembled into very short fibers. Figure 7b shows that contour length of the fibers obtained in methanol, ranging from 30 to 220 nm. In solution in ethanol (c= 0.015 mg . mL −1 ), the contour length of the fibers ranged from 20 to 430 nm (Figure 7d), which was obviously larger than the size of the fibers obtained in methanol. In solution in isobutanol (c= 0.015 mg . mL −1 ), the contour length of the fibers ranged from 140 to 2300 nm. The variation in L n of these fibers formed in three solutions (shown in Table 2) further confirms the influence of the solvent on the sizes of the fibers. The size distribution (L w /L n ) of these fibers also increased with a decrease in solvent polarity, as shown in Table 2.
The influence of the solvents on the self-assembly of the two block copolymers could be explained as follows. The dissolving capacity of the block copolymers P3HT 22 -b-PEG m increased with the decrease in solvent polarity and the increase in PEG chain. In methanol and ethanol, the dissolving capacity of the P3HT 22 -b-PEG 43 was too poor to self-assemble into well-defined nanostructures. In i-PrOH, the dissolving capacity of the P3HT 22 -b-PEG 43 increased. The transition structures (fibers) could be reorganized to form multilayered hierarchical micelles, induced by the π-π stacking interaction and van der Waals force. In isobutanol, the dissolving capacity of the P3HT 22 -b-PEG 43 greatly increased, leading to a decrease in the interactions of the P3HT 22 block. There was no enough force to induce the fibers to form hierarchical micelles. Due to the long PEG chain, the dissolving capacity of the P3HT 22 -b-PEG 113 in the four solvents was quite good. The P3HT 22 -b-PEG 113 could only self-assemble into fibers in all four solvents, due to the increase in dissolving capacity and steric hindrance. The increase in the dissolving capacity of the P3HT 22 -b-PEG m also leads to an increase in the dispersity of the fibers and a decrease in the length of the fibers. The influence of the solvents on the self-assembly of the two block copolymers could be explained as follows. The dissolving capacity of the block copolymers P3HT22-b-PEGm increased with the decrease in solvent polarity and the increase in PEG chain. In methanol and ethanol, the dissolving capacity of the P3HT22-b-PEG43 was too poor to self-assemble into well-defined nanostructures. In i-PrOH, the dissolving capacity of the P3HT22-b-PEG43

Conclusions
In summary, we have prepared a series of multilayered hierarchical micelles selfassembled by P3HT 22 -b-PEG 43 and fibers self-assembled by P3HT 22 -b-PEG 113 . The transition from the fibers to the hierarchical micelles has herein been proven to be influenced by the strength of the π-π stacking interaction, the PEG chain length, and solvent. The dissolving capacity and steric hindrance of the block copolymers both increase with an increase in PEG chain length. Meanwhile, the van der Waals force decreases with an increase in PEG chain length. In i-PrOH of the P3HT 22 -b-PEG 43 , the fibers (the transition structures) could be further reorganized to form multi-layered hierarchical micelles, driven by the intermediate strength of the π-π stacking interaction and the van der Waals force. In contrast, the P3HT 22 -b-PEG 113 with a longer corona block could only self-assemble into fibers in i-PrOH, due to the decrease in van der Waals force and the increase in dissolving capacity and steric hindrance. In addition, the shapes and sizes of the nanostructures could be influenced by the polymer concentration and solvent. In i-PrOH, the P3HT 22 -b-PEG 43 could self-assemble into the hierarchical micelles composed of vertically stacked 2D lamellar layers and the special hierarchical micelles composed of a series of linearly arranged 2D laminar layers, successively, with the increase of the polymer concentration. The P3HT 22 -b-PEG 43 could not self-assemble into well-defined nanostructures in methanol and ethanol, but could self-assemble into fibers in isobutanol. The P3HT 22 -b-PEG 113 could all self-assemble into fibers in methanol, ethanol, and isobutanol. The size and the size distribution of the fibers self-assembled by P3HT 22 -b-PEG 113 both increase with an increase in polymer concentration and a decrease in solvent polarity. This study will offer insight into controlling the morphologies of nanostructures.