{'fraction_non_alphanumeric': 0.034968770545693625, 'fraction_numerical': 0.018450032873109798, 'mean_word_length': 4.868579696165903, 'pattern_counts': {'":': 0, '<': 2, '<?xml version=': 0, '>': 0, 'https://': 0, 'lorem ipsum': 0, 'www.': 0, 'xml': 0}, 'pii_count': 0, 'substrings_counts': 0, 'word_list_counts': {'cursed_substrings.json': 1, 'profanity_word_list.json': 0, 'sexual_word_list.json': 0, 'zh_pornsignals.json': 0}}
On the improved electrochemistry of hybrid conducting-redox polymer electrodes

The electrochemistry of poly(2,5-dihydroxyaniline) (PDHA), a novel hybrid molecular configuration with redox active sites and electrical charge conduction along the polymer chain, has been recently reported. The theoretical capacity of this material is estimated at 443 mAh g−1, with high power performances being proposed given the intrinsic electrical conductivity. However, the initial results were below the expectations: only half the theoretical capacity attained, poor cycling stability and modest power behavior calling for further investigations on improving these performances. Herein we detail the optimized chemical synthesis and electrode formulation for poly(2,5-dihydroxyaniline) resulting in improved cycling stability, power performances and defined electrochemical response. We also detail the alternative electrochemical synthesis and activation route for PDHA and compare the results with the chemical approach.

estimated at 443 mAh g −1 . Given the relatively high electrical conductivity of 100 mS cm −1 15 , PDHA was also advanced with potential for high power performances.
Despite the promising estimated energy metrics, the performances attained were below the expectations. The developed methodology did not allow us to reach the theoretical gravimetric capacity of the PDHA yet, a charge storage capacity of 270 mAh g −1 was still possible to attain. Other limitations were related to poor cycle life as well as to ambiguous electrochemical response. As for the capacity extraction, Poizot et al. 28 postulated that structural aspects can induce the redox process to be limited to one-electron redox per BQ instead of the theoretical two. Furthermore, even though polyaniline is the oldest known synthetic conjugated polymer, its molecular structure is still matter of debate. The fact that polyaniline and its derivatives are displaying structures markedly influenced by the synthetic conditions is not helping to overcome this situation.
In this respect, the present work aims to get a better understanding of the limitations at play with PDHA in order to bring its performances to a higher level, particularly regarding the specific capacity and the capacity retention upon cycling. Therefore, the focus was set on several aspects that have not been explored in our first publication regarding the electrode formulation but also the material synthesis and processing. More specifically, we are now presenting parameters that have been reconsidered for the chemical demethylation step of poly-2,5-dimethoxyaniline (PDMA CHEM ) in the chemical synthesis approach of PDHA CHEM . Additionally, we also explore and discuss the all-electrochemical synthesis route for PDHA E-CHEM 29-32 : electro-polymerization of the poly-2,5-dimethoxyaniline (PDMA E-CHEM ), followed by electro-oxidative demethylation. Eventually, our attention has been focused on improving the active material-additives slurry formulation and electrode processing.

Results and Discussion
Synthesis. First, the results of the electrochemical synthesis of PDHA E-CHEM are detailed. The motivation for this approach was that it can directly afford PDMA (and potentially PDHA) as an electrode, i.e. the pure deposited material without any additives (carbon, binder). Not only would this grant electrochemical cells with higher energy densities, but it also makes for a very simple and straightforward procedure. The electrodeposition conditions on stainless steel substrate (potential window, voltage sweep rate, number of scans) were first screened to obtain homogeneous, compact and adherent PDMA films.
A series of typical samples and associated cyclic voltammograms for the electro-polymerization and the demethylation steps are shown in Fig. 2. The voltammogram in Fig. 2b shows progressive current increase with each cycle, significative of an increased amount of polymer being electrodeposited for each subsequent cycle. The porosity and thus the surface area increase allows for more monomer to be electro-oxidized, leading to a signal increase at every cycle. However, excessive deposition resulted in delamination of the PDMA film upon washing and drying, this step thus requiring further optimization. Films obtained after 10 scan cycles were found to be optimal (photographs A, B in Fig. 2a). A scan rate of 5 mV/s was also found optimal; for faster scan rates, non-uniform deposits were obtained (photographs B, C, D in Fig. 2a). Finally, the optimal scan potential window was determined to be −0.2 to 0.85 V vs. Ag/AgCl. The cyclic voltammogram of the electro-polymerization (Fig. 2b) displays a broad anodic peak around 0.8 V vs. Ag/AgCl, corresponding to the oxidation of the monomer and the electro-polymerization. The second anodic peak (0.3 V vs. Ag/AgCl) and the associated cathodic peak (0.2 V vs. Ag/AgCl), which are less visible at the beginning but become more pronounced with each cycle, are ascribed to the oxydo-reduction of the formed polymer. The most conclusive result (photograph A in Fig. 2a) in terms of homogeneity and structural integrity of the film was thus achieved with the following parameters: −0.2 to 0.85 V vs. Ag/AgCl, 5 mV s −1 , 10 cycles. Subsequent analysis was carried out on PDMA E-CHEM samples synthesized using these parameters.
After electro-polymerization, the samples were washed to remove any trace of monomer and electrochemical demethylation was tested. The conditions were similar to those of the polymerization except for the absence of monomer: voltammetry scans in 0.5 mol.L −1 H 2 SO 4 aqueous electrolyte. The potential scan window was limited to −0.2-0.7 V vs. Ag/AgCl at a scan rate of 1 mV s −1 (Fig. 2c). Two sets of redox peaks can be distinguished on the voltammogram. The reversible waves at 0.2 and 0.3 V vs. Ag/AgCl are characteristic of the polymer backbone redox (leucoemeraldine -emeraldine couple). The peak at 0.65 V vs. Ag/AgCl is indicative only of an irreversible process that we assign to the oxidative demethylation of the PDMA. It should be noted that the emeraldine -(per) nigraniline redox potential in acidic solution was reported to be in the range of 0.65-0.85 V vs. Ag/AgCl with this process being partially reversible and leading to chain degradation when in presence of oxygen [33][34][35] . It is thus Scientific RepoRts | 7: 4847 | DOI:10.1038/s41598-017-05063-z possible that the oxidative demethylation and the redox of the backbone are concurrent processes, leading to difficulties in precisely quantifying the specific contribution of each. Moreover, both processes can account for the irreversible chain degradation. It should also be noted that the peak at 0.65 V did not entirely vanish, even after extended scanning, which would have been expected in the case of complete demethylation of PDMA without interference of the emeraldine -(per)nigraniline redox process. Besides, the possibility of the chain degradation is supported by the global decrease of the whole signal after each voltammetry cycle. The physico-chemical and electrochemical characterizations that are following are providing some insight about the nature and the extent of the processes occurring during this synthetic approach.
Regarding our second approach, consisting in the chemical demethylation of PDMA CHEM , its yield was most comprehensively tuned by the amount of BBr 3 equivalents as well as the reaction time. The demethylation yield was evaluated through elemental analysis (see the characterization section) and the capacity extracted from electrochemical measurements in coin cells (see the electrochemical characterization section). For one equivalent of methoxy groups, the yield increased significantly from 1.5 up to 3 equivalents of demethylating agent; going up from 3 equivalents, the yield gain was much less pronounced. Regardless of the excess of BBr 3 , the reaction is relatively slow, and a total time of 72 hours was finally retained to ensure a maximum demethylation yield.
Characterization. The electroactive polymers synthesized using both chemical and electrochemical methods were first characterized to determine the chemical composition and molecular structure. In both cases, the precursor polymer and the product of demethylation exhibited IR peaks around 1520 cm −1 (marked with * in Fig. 3)stretching mode of the benzenoid ring -and 1590 cm −1 (marked with ** in Fig. 3) -stretching mode of the quinoid ring. The presence of the respective vibration modes supports the polymeric formula with polyaniline backbone in emeraldine oxidation state 36 . The N-H stretching peak (3300 cm −1 ) (marked with *** in Fig. 3) of the secondary amines of the polymer backbone is distinguishable for both PDMA CHEM/E-CHEM and PDHA CHEM/E-CHEM . It is however more intense for PDMA E-CHEM and PDHA E-CHEM , which hinders the observation of the O-H peak (marked with **** in Fig. 3) in the spectrum of PDHA E-CHEM (Fig. 3d). This is not the case for the chemical synthesis route, and the O-H for PDHA CHEM is clearly distinguishable (Fig. 3b), confirming the success of the demethylation reaction. This analysis suggests a higher demethylation yield for the chemical approach (PDHA CHEM ).
To quantify the demethylation extent in PDMA CHEM /PDHA CHEM , elemental analysis was employed (Table 1)   demethylation is the decrease of C/N and C/O ratios, accompanied by C/H ratio increase. The C/N, C/O and C/H ratios closest to the expected values were measured for PDHA CHEM samples with the following demethylation conditions: 72 h at −5 °C with 3 or more equivalents of BBr 3 . However, the demethylation yield derived from this analysis shows rather important variations (55 to 130%) depending on the ratio on which we base our calculations (C/N, C/O or C/H). This lack of precision is most certainly due to the contamination from the substrate during the mechanical film peeling, as well as the limited amount of material available per single batch. The yields derived from the galvanostatic discharge capacities were in that regard more conclusive, as will be illustrated in the electrochemical characterization section.
Finally, SEM analysis was carried out on PDHA E-CHEM electrodes given that particle delamination was noticed during the electropolymerization (Fig. 4a,b). The polymer film is composed of nano-and micro-particles (1-10 μm) with indeed loosely bound particles present on the surface. The bulk film remains compact with no significative porosity being detected by SEM. The polymer film can however be easily swelled by a solvent, implying a mesoporous morphology. By allowing an easy access of the electrolyte to the active material, this should have a favorable impact on the electrochemical performances/properties that have to be studied next.

Electrochemical characterization in non-aqueous electrolytes. With both materials (PDHA CHEM
and PDHA E-CHEM ) synthesized and characterized, we entailed electrochemical characterization in non-aqueous Li-half-cell configuration (Fig. 5a). Similarly to what was previously reported 15 , the half-cells typically had an open circuit potential of 2.8-3.2 V vs. Li/Li + and required an initial cathodic polarization scan. The electrodes made of PDHA CHEM display reversible behavior with two pairs of peaks centered at 2.3 and 2.7 V vs. Li/Li + , which are ascribed to the 2 electrons of the redox process, typical for quinone redox in aprotic electrolytes 6 . The absence of such peaks in pristine PDMA CHEM electrodes 15 constitutes an indication of successful demethylation. For comparison, the CV of the previously reported PDHA CHEM material 15 is shown in Fig. 5b. A visible improvement concerning the definition of the redox response is observable, implying a higher demethylation yield obtained using the current method than with the previous reaction parameters. This also corroborates the higher capacities obtained on galvanostatic cycling of PDHA CHEM synthesized in this work, involving higher activation of quinone redox moieties.  In contrast, the electrochemical analysis of PDHA E-CHEM shows a different behavior from PDHA CHEM . Two redox waves-centered at 2.8 and 3.2 V vs. Li/Li + -can be distinguished (Fig. 5c). The processes are reversible, with a slight decrease in intensity of the peak at 2.8 V observed with increasing cycle number. It should be noted that others have also attempted the electrochemical synthesis of PDHA for charge storage applications [29][30][31][32] . However, we find a lower redox activity window for PDHA E-CHEM : 2.5 to 3.6 V vs. Li/Li + compared to the 3.0-4.0 V vs. Li/Li + window previously reported. The assigned redox peak values are also not consistent with the electrochemistry of benzoquinone in non-aqueous electrolytes. The redox process centered at 3.2 V vs. Li/Li + is characteristic of the redox reaction of the electroactive polyaniline chain (refer also to Fig. 2b,c) 37,38 . While the peak centered at 2.8 V vs. Li/Li + could be assigned to PDHA redox, the absence of the second associated redox peak (typically located between 2.0 and 2.6 V vs. Li/Li + as seen in Fig. 5a,b) could be an indication that we are confronted with a different redox process than the classical quinone redox couple.
The explanation for this could be the high anodic polarization required for PDMA demethylation that also increases the redox state within the polyaniline chain. When in presence of oxygen, the (per)nigraniline has been reported unstable with irreversible degradation of the polymer matrix. The additional presence of methoxy/hydroxyl groups here could lead to complex electrochemical stability -response interplay requiring further investigation. Overall, this analysis suggests that the electrochemical synthesis route of PDHA requires further optimization to reach results similar to the chemical demethylation approach.
Lastly, galvanostatic cycling tests were run on PDHA CHEM assembled electrodes to determine the attainable reversible capacities and cycling stability. PDHA CHEM half-cells were cycled within a potential range from 1.8 to 3.0 V vs. Li/Li + . The voltage window was preliminarily determined by CV (Fig. 5a) and the upper limit was set to 3 V to avoid any overlap with the polyaniline backbone redox. The specific capacities, directly linked to the demethylation yields, varied with the demethylation conditions, as illustrated in Table 2. Higher excesses of BBr 3 demethylating agent and longer reaction times allow for an improved conversion of methoxy groups, and thus a higher amount of hydroxy chemical functions accessible for the electrochemical process. Accordingly, we observe an uptake of the specific capacity when these two reaction parameters are increased.
The best demethylation conditions led to an initial discharge capacity of 290 mAh g −1 (Fig. 6a). This constitutes the highest to date capacity for this class of materials, and is attributed to improved synthesis, limited exposure to air of the demethylated material and storage in controlled atmosphere prior utilization.
Another major improvement is the enhancement of the capacity retention (Fig. 6a,b). For instance, 90% of the initial capacity (270 mAh g −1 ) was lost in the first three cycles for the highest capacity PDHA previously reported 15 . As illustrated in Fig. 6b, the PDHA CHEM electrodes analyzed here retain more than 50% of the initial capacity after more than 30 cycles. These ameliorations are the result of an improved synthesis method, an adequate current collector implementation (carbon-coated aluminum foil here vs. nickel foam in ref. 15), and an improved adhesion of the coated electrodes.
The coulombic efficiency for the PDHA CHEM electrodes is also illustrated in Fig. 6b, with initial values above 100%. High reversibilities of carbonyl groups have been reported before for other organic electrode materials, with associated good coulombic efficiencies 9,24,25,39,40 . In this case, the excessive values obtained for a current density of 16 mA g −1 (C/20) are ascribed to irreversible redox processes in the polymer backbone. With cycling, the coulombic efficiency values stabilizes at 100%, which implies limited irreversible redox of the backbone.
Lastly, the power performances of PDHA CHEM have also been measured. Figure 7 displays the stable reversible capacity obtained -the electrodes delivered specific capacities of 160, 130, 110 and 100 mAh g −1 at 16 (C/10), 32 (C/5), 80 (C/2) and 160 mA g −1 (1C), respectively. Moreover, after the power-rate evaluation, the PDHA CHEM retained most of the initial capacity of 125 mAh g −1 , thus 80% of the initial value. For comparison, the best rate performances achieved in our previous report are also shown. Despite a lower initial value at C/10 (160 mAh g −1 vs. 190 mAh g −1 ), the capacities delivered at C/2 (110 mAh g −1 vs 85 mAh g −1 ) and 1C (100 mAh g −1 vs 60 mAh g −1 ) are significantly higher in current work. These improved power properties are ascribed to optimized synthesis and formulation parameters, and notably to the change of current collector with carbon-coated aluminum foil used this time instead of Ni foam.

Conclusion
To summarize, this work details the chemical and electrochemical synthesis of poly(2,5-dihydroxyaniline) coupled to electrochemical analysis of the synthesized materials. Full and reversible capacity utilization in this hybrid redox-conductive polymer still remains elusive with however some important insights being presented in this work. The electrochemical method was tested as it can provide pure PDMA (and potentially PDHA) electrodes to truly benefit from intrinsic electrical conductivity, electrolyte insolubility and high capacity of this material. Nevertheless, the electroanalytical analysis of PDHA E-CHEM points towards a mechanism differing from the demethylation, with possible enhanced degradation given the high anodic polarization required. Further improvement of the electrochemical demethylation method is thus required for it to deliver more satisfactory results. The optimization of the chemical synthesis, electrode processing and assembly protocol in turn has led to clear improvements in terms of first cycle capacity, cycle capacity retention and power performance. This work is expected to lead to further progress in this direction by enabling full capacity utilization in PDHA and gives guidelines for new alike hybrid redox-conductive polymers materials for energy storage.

Methods
Materials and reagents. The  Electrochemical synthesis approach. The electrochemical synthesis was carried out in a one-compartment three-electrode cell. A polished stainless steel disk (SS-304) was used as the working electrode, a platinum wire as the counter electrode and an Ag/AgCl electrode as reference electrode. All the experiments were performed using an Arbin instruments BT -2043 multichannel potentiostat. PDMA E-CHEM films were deposited by means of cyclic voltammetry from an aqueous solution containing 0.05 mol L −1 DMA and 0.5 mol L −1 H 2 SO 4 . The potential range, the scan rate and the number of scans were optimized in order to obtain adherent and homogeneous deposits. After the electro-polymerization, the films were rinsed with water and dried. For the oxidative demethylation (yielding PDHA E-CHEM ), the obtained PDMA E-CHEM films on stainless steel substrates were used as the working electrode and exposed to cyclic voltammetry polarization scans in a 0.5 mol L −1 H 2 SO 4 aqueous solution. After several optimization tests, the following parameters were found as optimal: the potential was cycled between −0.2 and 0.7 V vs. Ag/AgCl with a scanning rate of 1 mV s −1 . The mechanism for the electrochemical demethylation reaction (Fig. 8) proceeds through the oxidation of PDMA E-CHEM (schematized here for the 2 electrons reaction per monomer unit), followed by the elimination of two methyl cations.
Chemical demethylation of PDMA E-CHEM was also tested but unsatisfactory results have been obtained. During the reaction in conditions similar to above, the stainless-steel disk displayed signs of corrosion (progressive appearance of a dark-brown film/deposit) accompanied by delamination of the PDMA film.
Chemical synthesis approach. The previously reported chemical synthesis of PDHA was reconsidered here 15 . The method consists in (i) oxidative polymerization of 2,5-dimethoxyaniline using ammonium persulfate as oxidizing agent to obtain PDMA, followed by (ii) chemical demethylation of PDMA with boron tribromide to give PDHA 15 (Fig. 9).
The PDMA CHEM was obtained following the literature reports 33,41,42 . In short, DMA (0.03 mol L −1 ) was dissolved in 1 mol L −1 HCl aqueous solution followed by slow addition of ammonium persulfate ((NH 4 ) 2 S 2 O 8 , 1.5 equivalents) as oxidizing agent at 0 °C. The reaction was further stirred for 4 h at 0 °C. The obtained PDMA CHEM  For the chemical hydrolysis of the methoxy groups, the reaction time, temperature and the amount of demethylating agent were screened to find the optimal conditions. First, PDMA CHEM was basified with an ammonium hydroxide solution (NH 4 OH 0.1 mol L −1 ) then dried overnight under reduced pressure at 35 °C. The PDMA CHEM was then dispersed in dichloromethane (with also partial dissolution) and the solution was cooled to −5 °C. Afterwards, boron tribromide (BBr 3 ) (1.5 to 5 equivalents) was added dropwise over 1 hour. The reaction time varied from 24 to 72 hours while maintaining the temperature at −5 °C. The reaction was quenched with deionized water, recovered by vacuum filtration and washed with 0.1 mol L −1 HCl and diethyl ether. The obtained product (PDHA CHEM ) displayed the expected green color (acidified form of polyanilines) and solid consistency, whereas the solubility in water and acetonitrile considerably decreased compared to the PDMA CHEM precursor.
Physico-chemical characterization. FTIR spectra of PDMA/PDHA CHEM/E-CHEM products were acquired with a Bruker Equinox 55 spectrometer by mixing the powders with KBr. Elemental analysis was performed by soliciting Medac Ltd services, with a stated absolute precision of 0.3%. Scanning Electron Microscopy (SEM) images were acquired using a LEO 982 FEG-SEM.
Electrode formulation and electrochemical testing. To prepare the electrodes, PDHA CHEM was first ball-milled with carbon black (SC45, Timcall, MTI). It should be mentioned that similarly to our previous work, carbon black was primarily used as reinforcement filler material to enhance the structural integrity of the coatings. Without added carbon black, coatings were found to crack and delaminate from current collectors even in presence of excess amount of binder. Two binder formulations have been tested: PVDF-NMP (poly(vinylidene fluoride) dissolved in N-methylpyrrolidone) and CMC/SBR-water (aqueous solution of carboxymethyl cellulose and styrene-butadiene rubber). The best results in terms of coating integrity during manipulation as well as post-cycling analysis were obtained using the formulation containing PDHA CHEM :SC45:PVDF − 30:60:10 (mass ratio) coated on carbon-coated aluminum foil (EQ-CC-Al-18u-260, MTI) as current collector. Attempts were made to reduce the proportion of carbon, but resulted in an important loss of integrity of the electrode during handling, cycling, and first cycle irreversible capacity loss.
Pure PDHA electrodes were prepared by means of electrochemical synthesis as detailed in the synthesis section. The PDHA E-CHEM on SS disks were used as such without any further processing or additive incorporation. PDHA CHEM/E-CHEM electrodes were tested in half-cell configuration using lithium metal (Gelon) as reference and counter electrode. A porous polyethylene membrane (Celgard) was used as separator. A mixture of ethylene carbonate (EC), diethyl carbonate (DEC) and dimethylcarbonate (DMC) with a 1:1:1 volume ratio with 1 mol L −1 of lithium hexafluorophosphate (LiPF 6 ) was used as electrolyte (Solvionic). Electrochemical cells were assembled in nutlock-type cells (X2 Labwares). The assembly was made under protective argon atmosphere (<0.1 ppm H 2 O, <0.1 ppm O 2 ) in a MBraun glovebox. All the galvanostic cycling experiments were performed using an Arbin BT -2043 multichannel potentiostat.