{'fraction_non_alphanumeric': 0.03524229074889868, 'fraction_numerical': 0.011747430249632892, 'mean_word_length': 5.39906103286385, 'pattern_counts': {'":': 0, '<': 0, '<?xml version=': 0, '>': 0, 'https://': 0, 'lorem ipsum': 0, 'www.': 0, 'xml': 0}, 'pii_count': 0, 'substrings_counts': 0, 'word_list_counts': {'cursed_substrings.json': 0, 'profanity_word_list.json': 0, 'sexual_word_list.json': 0, 'zh_pornsignals.json': 0}}
Preparation of Nitrogen-Doped Carbon-Based Bimetallic Copper-Cobalt Catalysis Based on Deep Learning and Its Monitoring Application in Furfural Hydrogenation

In the field of catalysis, the support of the catalyst is often composed of hollow carbon materials. In order to monitor the preparation of nitrogen-doped carbon-based bimetallic copper-cobalt catalysis and its hydrogenation reaction in furfural, using m-aminophenol as the nitrogen source, formaldehyde as a carbon source, and P123 as a template agent, a nitrogen-doped bimetallic copper-cobalt mesoporous carbon catalyst Cu-Co@N-MPC-500 was synthesized by the hydrothermal method. The morphology, structure, and chemical composition of the catalyst were analyzed by means of TEM, XRD, BET, and XPS, respectively. The results show that the nitrogen-doped mesoporous carbon has a stable structure, uniform pore size distribution, and the nano-copper-cobalt particles are uniformly dispersed in the mesoporous carbon surface. Through furfural hydrogenation, the catalyst selectivity and cycle stability were discussed. Under the furfural conversion rate of 96.1%, the yield of cyclopentanone could reach 76.2%. After 5 cycles, the catalytic efficiency of the catalyst did not decrease significantly. It shows that Cu-Co@N-MPC-500 has excellent application prospects in the field of industrial production.