{'fraction_non_alphanumeric': 0.022222222222222223, 'fraction_numerical': 0.01616161616161616, 'mean_word_length': 5.117283950617284, 'pattern_counts': {'":': 0, '<': 0, '<?xml version=': 0, '>': 0, 'https://': 0, 'lorem ipsum': 0, 'www.': 0, 'xml': 0}, 'pii_count': 0, 'substrings_counts': 0, 'word_list_counts': {'cursed_substrings.json': 0, 'profanity_word_list.json': 0, 'sexual_word_list.json': 0, 'zh_pornsignals.json': 0}}
Tribological properties of B4C–TiB2–TiC–Ni cermet coating produced by HVOF

Abstract In this study, B4C–TiB2–TiC–Ni coating was sprayed on the surface of 4130 steel by high velocity oxy-fuel torch. The tribological behavior of samples was studied by ball on disk wear testing. Structural evolution of the coating was analyzed by X-ray diffractometry. The microstructure of the coating, wear track and Al2O3 ball was investigated by scanning electron microscopy, field emission scanning electron microscopy and optical microscopy. Elemental analysis of the wear track was done by energy dispersive X-ray spectroscopy. It was found that a cermet coating containing B4C, TiB2, TiC and Ni phases with good bonding to the 4130 steel substrate with no sign of any cracking or pores was formed. The wear mechanism of the composite coating was delamination. The friction coefficient of samples was decreased with increasing load because of higher frictional heat and creation of more oxide islands.