{'fraction_non_alphanumeric': 0.02766531713900135, 'fraction_numerical': 0.023616734143049933, 'mean_word_length': 4.638783269961977, 'pattern_counts': {'":': 0, '<': 0, '<?xml version=': 0, '>': 0, 'https://': 0, 'lorem ipsum': 0, 'www.': 0, 'xml': 0}, 'pii_count': 0, 'substrings_counts': 0, 'word_list_counts': {'cursed_substrings.json': 0, 'profanity_word_list.json': 0, 'sexual_word_list.json': 0, 'zh_pornsignals.json': 0}}
In vitro evaluation of coils for endovascular therapy.

PURPOSE
To evaluate the physical characteristics and behavior of coils for endovascular therapy.


METHODS
Mechanically detachable coils were constructed with simple helical (4 mm X 10 cm and 8 mm X 30 cm) and pretzel shapes (4 mm X 5 cm) made from three metals using 0.003- and 0.004-in wire. Stiffness or pliability, frictional resistance, shape memory, and coil stability were evaluated in vitro.


RESULTS
The 0.004-in wire stock coils proved significantly stiffer when compared with the 0.003-in coils. Tungsten coils proved least pliable; platinum coils were intermediate in stiffness; and nitinol coils were softest. Frictional resistance in the catheter was greatest for stiffer coils. The 5-cm pretzel coil consistently created more frictional force than the 10- or 30-cm simple helical coils. Despite a shorter length, the 4-mm simple helical coil exerted more frictional force than the 8-mm coil. Stiffer metal coils constructed of larger-diameter wire (0.004 in) were more stable than softer coils.


CONCLUSION
Stiffer coils exert greater frictional forces within the catheter and a greater resistive force during bending but are more stable after placement. Frictional forces also depend on the complex three-dimensional shape of the coil and the diameter of the turns in that shape rather than coil length. These data suggest that a family of coils of different metals is optimal for varied intravascular needs.