{'fraction_non_alphanumeric': 0.030076058839427048, 'fraction_numerical': 0.012856646461526582, 'mean_word_length': 4.677772906619904, 'pattern_counts': {'":': 0, '<': 0, '<?xml version=': 0, '>': 0, 'https://': 0, 'lorem ipsum': 0, 'www.': 1, 'xml': 0}, 'pii_count': 0, 'substrings_counts': 0, 'word_list_counts': {'cursed_substrings.json': 2, 'profanity_word_list.json': 0, 'sexual_word_list.json': 0, 'zh_pornsignals.json': 0}}
Coated High ‐ Refractive ‐ Index Barium Titanate Glass Microspheres for Optically Trapped Microsphere Super ‐ Resolution Microscopy: A Simulation Study

: As water is normally used as the immersion medium in optically trapped microsphere microscopy, the high ‐ refractive ‐ index barium titanate glass (BTG) microsphere shows a better imaging performance than the low ‐ index polystyrene (PS) or melamine formaldehyde (MF) microsphere, but it is difficult to be trapped by single ‐ beam optical trapping due to its overly high refractive index. In this study, coated BTG microspheres with a PS coating have been computationally explored for the combination of optical trapping with microsphere ‐ assisted microscopy. The PS coating thickness affects both the optical trapping efficiency and photonic nanojet (PNJ) property of the coated BTG sphere. Compared to the uncoated BTG sphere, the coated BTG sphere with a proper PS coating thickness has a highly improved trapping efficiency which enables single ‐ beam optical trapping, and a better PNJ with a higher optical intensity max I and a narrower full width at half maximum (FWHM) corresponding to better imaging performance. These coated BTG spheres also have an advantage in trapping efficiency and imaging performance over conventional PS and MF spheres. The coated BTG microsphere is highly desirable for optically trapped microsphere super ‐ resolution microscopy and potentially beneficial to other research areas, such as nanoparticle detection.


Introduction
Optical microscopes are widely used in the fields of life science and nano-technology. Due to the optical diffraction limit, conventional optical microscopy has a 200 nm resolution in the visible spectrum which has greatly hampered its applications in many research fields. To break the optical diffraction limit, several techniques have been developed, including a near-field scanning optical microscopy [1], solid immersion lens [2], superoscillatory lens [3] and fluorescent microscopy [4].
In 2011, Wang at al. demonstrated that a traditional optical microscope together with transparent fused silica (SiO2) microspheres (~1.46 n ) can gain a 100-nm resolution in air under white light illumination [5]. Then, a polystyrene (PS) microsphere (~1.59 n ) was used to overcome the optical diffraction limit in both air [6] and water [7]. Darafsheh et al. realized optical super-resolution imaging by using high-refractive-index barium titanate glass (BTG) microspheres (~1.9 2.1 n  ) totally immersed in a liquid environment [8], and they also studied the influence of immersion medium on imaging performance in microsphere-assisted microscopy [9]. This label-free superresolution imaging technique has attracted many research groups across the world, demonstrating sub-diffraction discerning ability in nanostructure detections and biological observations [10][11][12][13]. The super-resolution mechanism of microsphere-assisted microscopy is still a heated topic [14][15][16]. Early in 2004, the dielectric microsphere was regarded as a potential new visible-light super-resolution technique through a phenomenon known as "photonic nanojet"(PNJ), which has a narrow waist and an extraordinarily high optical intensity formed on the shadow-side surface of a plane-waveilluminated dielectric microsphere [17]. The full width at half maximum (FWHM) and the maximum optical intensity ( max I ) of the PNJ are related to the size of the microsphere, the incident wavelength and the refractive index contrast (RIC) between the microsphere and immersion medium [18]. Ultralong PNJ can be obtained by a two-layer dielectric microsphere [19], a graded-index microsphere [20] and a liquid-filled hollow microcylinder [21]. Meanwhile, an ultra-narrow PNJ can be gained by overstepping the upper refractive index [22], a dielectric cylinder, with a glass cuboid [23] and a nanohole-structured mesoscale dielectric sphere [24]. It is responsible for switching the PNJ on and off for a microsphere with an incident focused beam [25]. The PNJ theory is regarded as a part of the super-resolution mechanism, and there is a qualitative relation between PNJ property and imaging performance [26][27][28]. It has been investigated that the PNJ greatly benefits highresolution optical imaging, and the resolution power of PNJ is quantified [29]. We can use the PNJ property of the sphere to characterize the imaging performance, which would help us in selecting a proper microsphere for practical microsphere-assisted microscopy.
To control the position of the microsphere for site-specific imaging and large field-of-view scanning imaging, a non-contact optical manipulation technique of microparticles, named optical trapping (also known as optical tweezers), can be introduced [30]. A schematic of a normal optical system for the combination of single-beam optical trapping with microsphere-assisted microscopy is shown in Figure 1a, including an optical trapping part and an illumination part with the same objective. The laser beam ( 1  ) is highly focused by the objective to trap the microsphere, and the charge-coupled detector (CCD) captures the magnified image of the sample surface through the trapped microsphere under an illumination ( 2  ). The inset in Figure 1a shows the scheme of typical optical trapping of a microsphere in a Gaussian beam. Optically-trapped microspheres have been widely used for imaging applications. Early in 1997, a micro-objective, made of a 25-μm PS microsphere, was manipulated by single-beam optical tweezers to produce locally magnified (or reduced) images of a specific area [31]. Furthermore, Stanescu et al. investigated the magnification property of a laser-trapped PS sphere in water [32]. An optically-trapped SiO2 sphere with a diameter of 8 μm was used to image the sample surface and detected the defect successfully [33]. Recently, our group focused on the selection of microsphere types for the combination of optical trapping with microsphere-assisted microscopy, and finally, the low-index PS sphere and melamine formaldehyde (MF) sphere (~1.68 n ) were optically-trapped for super-resolution imaging of a 139-nm line-width silicon nanostructure grating [34]. Optically-trapped microsphere microscopy holds an advantage in super-resolution imaging through the non-contact optical manipulation of dielectric microspheres.
In optically-trapped microsphere microscopy, the microsphere is not only the object of optical trapping, but also the one to be used for magnified or super-resolution imaging. The refractive index of the sphere is fairly important because it affects both the optical trapping property and the imaging performance of the sphere. On the one hand, for single-beam optical trapping in water, the refractive index of the used sphere is required be less than 1.73 [35], and too high of a refractive index will make it difficult to realize stable optical trapping. For example, the axial force and radial force acting on two index-different spheres as a function of sphere position are illustrated in Figure 1b,c, respectively. The maximum reverse axial force A characterizes the trap strength, which determines whether or not the sphere can be trapped. We can see that the low-index PS sphere in water can be trapped easily, while the high-refractive-index BTG sphere is hard to trap in three dimensions because its high refractive index strongly increases the scattering force, which pushes the sphere away from the focused laser spot. An alternative method to trap high-index spheres has been proposed by counterpropagating optical tweezers in which the scattering forces are eliminated [36], but such a setup is complicated. On the other hand, for imaging applications of microspheres in water, the high refractive index of the BTG sphere is beneficial to produce a sharper PNJ and a better imaging quality (higher resolution and better image contrast) than that of the low-index SiO2, PS and MF spheres.
Even with the same RIC, the BTG sphere in a liquid droplet produces a highly focused PNJ and a better image contrast compared with a low-index soda lime glass sphere (~1.5 n ) in air [9]. There seems to exist a contradiction for the combination of single-beam optical trapping with microsphereassisted microscopy when using high-refractive-index BTG spheres, and existing optically-trapped microsphere microscopy using low-index spheres in water may suffer from poor imaging performance, e.g., inadequate discerning ability and low image contrast.
In this study, high-refractive-index BTG microspheres with uniform PS coatings have been computationally explored for optically trapped microsphere microscopy. An antireflection coating on a high-refractive-index sphere can improve the trapping efficiency of the sphere efficiently [35,37]. From numerical simulations, we found that coating thickness plays an important role and it affects both the optical trapping efficiency and the PNJ property of the coated BTG sphere. Compared to an uncoated BTG sphere, a coated BTG sphere with a proper PS coating thickness in water has a highly improved trapping efficiency, and a better PNJ with a higher max I and a narrower FWHM which corresponds to a better imaging performance. For coated BTG spheres with a specific core radius of 2.5 μm, the maximum axial trapping efficiency can be enhanced over 10-fold by proper PS coating, and the PNJ properties (FWHM and max I ) are also improved by the coating. In addition, coated BTG spheres also have an advantage in trapping efficiency and imaging performance over conventional low-index PS and MF spheres. A coated BTG sphere enables single-beam optical trapping for enhanced trapping efficiency and also produces a better PNJ property related to better imaging performance, making it highly desirable for optically-trapped microsphere super-resolution microscopy.

Model of a Coated Sphere
A model of the coated microsphere is illustrated in Figure 2. The sphere consists of an inner core of radius s R and an outer coating of radius c R . The refractive indices of the inner core and the outer coating are s n and c n , respectively. The coated sphere is totally immersed in a liquid medium with m n . The incident electric field can be a Gaussian beam for optical trapping or a plane wave for PNJ generation.
In the following simulations, s n is set to 1.9 corresponding to the BTG sphere, and deionized of the indices from the core and the medium, and the geometric mean is normally used for an optimal single-layer planar antireflection coating [38]. One should note that the refractive index of the core of the coated sphere is set to 1.9 in numerical simulations; for other high-index spheres with a different refractive index, such as BTG spheres (

Relationship between the Optical Trapping Forces and the Refractive Index Difference Δn
Normally, there are two optical forces acting on a sphere in a focused laser beam: one is the gradient force grad F , which attracts the sphere towards the focus, and the other is the scattering force, which tends to push the sphere away from the focus. A sphere can be trapped if the gradient force is larger than the scattering force. In the Rayleigh regime ( r   ), the gradient force grad where / s m m n n  . A larger gradient force can be generated by spheres with a higher refractive index, attracting spheres more strongly toward the focal region of optical trapping.
However, the scattering force is related to the reflectivity of the sphere, and it is proportional to 2 ( ) n  , the square of the refractive index difference between the refractive index of the sphere and the immersion medium: It is apparent that the scattering force increases more quickly with the refractive index mismatch than the gradient force. Therefore, for spheres with a high refractive index, the scattering force dominates, which pushes spheres away from the focus in the direction of light propagation. This limits the maximum refractive index of spheres that are able to be trapped in single-beam optical tweezers.
In the geometric optics regime ( r   ), by some proper assumptions, such as neglecting interferences and multiple reflections, considering the reflection and refraction of a single light ray incident at an angle 1  with respect to the normal of the sphere surface, researchers also found that the gradient force by a single ray is proportional to the 2 ( ) n  : Furthermore, the corresponding scattering force by the reflected light ray is proportional to n  : Summing the overall light rays preserves the scaling. In the Mie regime ( r   ), including spheres we mainly consider in this research, although the force relations cannot be described correctly by the Rayleigh scattering or geometric approximation, one can still find that for spheres in this regime, the scattering force depends more strongly on the refractive index mismatch n  than on the gradient force.
Antireflection coating on a high-refractive-index sphere serves as a simple and effective way to reduce the scattering force, eventually making high-index spheres trappable by single-beam optical trapping [35,37]. As illustrated in Figure 2 ( ) n  . The sum of the squares is less than the square of the sum, so the total sum of the reflectivity at the two interfaces is smaller than that at the sphere-water interface: The scattering force is proportional to the reflectivity, and it can thus be reduced by the antireflection coating with a refractive index equal to the geometric mean of the indices from the sphere core and the immersion medium.

Optical Trapping Simulations of Coated BTG Spheres with PS Coating
To calculate the optical forces on particles in optical trapping, we used the optical tweezers toolbox [40]. A Gaussian beam with wavelength 1 1064   nm was used as the trapping beam, and it was focused by an objective with NA 1.0. The core radius was set in a range of 0.5 μm-5 μm for a wide enough field of view (FOV) in microsphere-assisted microscopy, and the coating thickness h was varied from  Figure 1b). The dependence of trap strength on sphere size with four different PS coating thickness is shown in Figure 3. The oscillations that appeared in the profiles result from the interference effect [35,41]. For comparison, the force on the uncoated BTG sphere with the same core radius was also calculated, and we can see that uncoated BTG spheres cannot be optically trapped at all sizes. See Video S1 for improvements in axial trapping efficiency z Q and Video S2 for improvements in radial trapping efficiency r Q of coated BTG spheres with varied PS coating thickness. This suggests that the improvement from the coating is not overly sensitive to the coating thickness [35]. This may not be suitable for high-index BTG spheres. When h varies from  Figure 3g. The coating thickness h affects the axial trapping efficiency z Q obviously, and it has a small impact on the radial trapping efficiency r Q . Note that r Q , which normally exceeds z Q broadly, is high enough for stable radial trapping. Therefore, in this research we will pay more attention to the effect of PS coating on axial trapping efficiency z Q .
Through proper PS coating, the optical trapping efficiency of the high-index BTG sphere has been highly improved, which demonstrates that the antireflection coating on a high-index sphere is very useful for single-beam optical trapping. As shown in Figure 4, similar improvements in z Q and r Q have also been demonstrated for a coated BTG sphere with a specific core radius of 2

Electromagnetic Fields in a Multilayered Sphere
where 0 (2 1) / ( 1) n n E i E n n n    . The expansion of the electric fields in the th l region is given by: where is  the angular frequency and  is the magnetic permeability. The expansion coefficients  [43].
The internal electric field in the core region ( 1 l  ) is in the form: ( In the region outside the sphere, the total external fields are considered to be the superposition of the incident field and the scattered field, ; where n a and n b are the scattering coefficients. By comparing equations, we have

PNJ Property of Coated BTG Spheres with PS Coating
The coated BTG sphere with a PS coating in Figure 2 can be regarded as one type of multilayered sphere. Based on the Mie theory, we will now study the intensity distributions of PNJs for coated BTG spheres with a PS coating. For the incident wave, a linearly polarized plane wave ( 2 =600nm  in vacuum) propagates along the z-axial. We suppose that the coated BTG sphere has a core radius of 2.5 μm, the same as the radius in Figure 4, and the thickness of the PS coating is varied from 0 nm to 669 nm. Figure 5 shows the intensity distributions of PNJs generated on the shadow sides of four BTG spheres with different PS coating thicknesses h . The coating thickness affects the focusing performance of the PNJ, as shown in Figure 5a nm as shown in Figure 5b,g) related to better imaging performance. When h was 450 nm, we also obtained a better PNJ with a FWHM of 222 nm (Figure 5i), and the enhancement in max I (Figure 5d) was over 1.45 fold compared to that of the uncoated BTG sphere (Figure 5a). With h of 535 nm, we obtained a better PNJ with a FWHM of 234 nm (Figure 5j), and the enhancement in max I (Figure 5e) was over 1.62 fold compared to that of the uncoated BTG sphere. Figure 6 shows the relative change of FWHMs and max I of PNJs of coated BTG spheres (core radius 2.5 μm) with varied PS coating thickness, and the uncoated BTG sphere with a radius of 2.5 μm is used for comparation. It can be seen that with PS coating, the coated BTG spheres normally show a higher max I (blue line in Figure 6). The wave additionally focuses due to the increase in the curvature of the radiation wave front going through the core, leading to an enhancement in max I at the focal waist of the coated sphere [44]. The increase in max I in our study results from two aspects: (1) the reduction in backscattered light; (2) the increase in the sphere volume. The latter is likely to be the main reason for the rapid increase in max I with a large PS coating thickness (like h above 400 nm). The FWHM varied with the increase in h (red line in Figure 6), and all FWHMs were less than 300 nm ( 2 / 2  ). When h varied from 0 nm to 400 nm, the FWHM of the PNJs showed a random varying trend. Note that once the h leads to a widened FWHM, the increase in corresponding max I is relatively small. When h was in the range of 400 nm to 669 nm, the FWHMs of the coated BTG spheres were always narrower than that of the uncoated BTG sphere, and the relative change in max I was more than 20%.

Proper PS Coating Thickness for Coated BTG Spheres
From numerical simulations for optical trapping and PNJ generation of coated BTG spheres with a PS coating, we can see that the PS coating thickness h affects both the optical trapping ( Figure 4) and the PNJ property ( Figures 5 and 6). A proper PS coating thickness is beneficial to obtain an improved optical trapping efficiency and a better PNJ property of the coated BTG sphere simultaneously, and it is desirable for optically-trapped microsphere microscopy. Actually, the biggest problem of the high-index BTG spheres used for optically-trapped microsphere microscopy is that it cannot be trapped by single-beam optical tweezers. Now, how to decide the proper coating thickness? One simple principle to decide proper PS coating thickness is illustrated as below: first, the selected h should ensure a high trapping efficiency which makes the high-index spheres trappable. Then, once the selected h leads to a better PNJ property, the selected h will be the proper PS coating thickness h .
For the coated BTG sphere with a core radius of 2.5 μm in Figures 4-6, the considered range of PS coating thickness h was set at 90 nm-295 nm and 447 nm-669 nm, corresponding to the highly enhanced z Q (larger than 0.04) above the dashed line in Figure 4a. The value of 0.04 was selected because the average z Q of the PS sphere (which is commonly considered to be trapped easily) with a radius range of 0.5 μm-5 μm in the same condition is no more than 0.04 as shown in Figure 7a. As for the first considered range of h (90 nm-295 nm), we can see that the FWHM of PNJ varies randomly, and the max I is enhanced. Some values of h around 188 nm which lead to a highly these two values being optimized for the BTG sphere with a specific core radius of 2.5 μm, they also work for BTG spheres with other core radii. First, we will compare the trapping performances of the coated spheres with those of the uncoated spheres. Particularly, uncoated low-index PS and MF spheres normally used for opticallytrapped microsphere microscopy are also considered in comparison. The axial trapping efficiency z Q and radial trapping efficiency r Q of different microspheres are illustrated in Figure 7a,b, respectively. As seen in Figure 7a, for uncoated spheres, the overall z Q decreases as the index of sphere increases. With a 188 nm/535 nm PS coating, BTG spheres show much better trapping performance than uncoated BTG spheres, and they also perform better than uncoated low-index PS and MF spheres. The improved trapping performance of the coated high-index sphere is mainly due to the reduced scattering force which originates from the suppression of backscattering by the antireflection coating [45]. Coated BTG spheres indeed possess much higher trapping efficiency which enables single-beam optical trapping. As for PNJ property, it is commonly believed that high-index BTG spheres have an advantage over low-index PS and MF spheres with the same radius in a water medium [8,9], and a high-index sphere is beneficial for producing a PNJ with a smaller FWHM and a higher max I . The coated BTG spheres with proper h possess a better PNJ related to better imaging performance than uncoated BTG spheres. To save computation time, PNJ simulations of related spheres with a wide range of radius are omitted here. For spheres with a specific core radius of 2.5 μm (dotted line in Figure 7), the optical trapping efficiency and the PNJ property of five different spheres (the uncoated PS/MF/BTG spheres and two coated BTG spheres) are summarized in Table 1 It is worthwhile to note that besides the core radius of 2.5 μm, other core radii of coated BTG spheres could be investigated in a similar way to find the ideal coating thickness. The coated BTG sphere with a proper PS coating thickness shows a significant improvement in trapping efficiency and produces a better PNJ, corresponding to an enhanced imaging performance compared to that of the uncoated PS/MF/BTG spheres. This provides us with an opportunity to use coated BTG spheres for optically-trapped microsphere super-resolution microscopy.

Conclusions
There are several comments that can be concluded from above analysis, i.e.: (a) Besides the PS coating, we also used SiO2 material for the coating of BTG spheres. Although the refractive index of SiO2 ( 1.46 n  ) varies by about 0.13 compared to the ideal value of coating, the effects of SiO2 coating on optical trapping efficiency (see Figure S1) and PNJ property (see Figure  S2) of the coated BTG sphere with a core radius of 2.5 μm are similar to that of PS coating. The overall improvement in axial trapping efficiency with an SiO2 coating is smaller than that with a PS coating, and this may be explained by the fact that the refractive index of SiO2 coating deviates from ideal value. With a proper SiO2 coating thickness, we can also obtain a highly enhanced axial trapping efficiency and a better PNJ property (see Table S1). The SiO2 coating provides us with an alternative coating material to fabricate coated BTG spheres, and it also enables us to use single-beam optical tweezers to trap coated BTG spheres for super-resolution microscopy. (b) A BTG sphere with a PS coating or SiO2 coating can be synthesized with existing procedures [46] in future work. The coated sphere enables single-beam optical trapping with a lower NA objective and a much lower laser power [37], and the lower NA objective, in turn, is beneficial to show the enhanced power of microspheres in imaging resolution.
In conclusion, we have computationally studied coated BTG spheres with a PS coating for optically-trapped microsphere super-resolution microscopy. The coating's thickness has an influence on both trapping efficiency and PNJ property of the coated BTG sphere. The PS coating shows a favorable performance in trapping efficiency enhancement as its index is closer to the ideal refractive index (geometric mean of the indices from the BTG core and the water medium). Compared to the uncoated PS, MF and BTG spheres, the coated BTG sphere, with the proper thickness of PS coating, can enhance the trapping efficiency effectively and produce a better PNJ with a narrower FWHM and a higher optical intensity, corresponding to a better imaging performance. The coated high-refractiveindex BTG sphere is highly desirable for optically-trapped microsphere super-resolution microscopy, and potentially useful for other research areas like nanoparticle detection.
Supplementary Materials: The following are available online at www.mdpi.com/xxx/s1, Figure S1: Axial (a) and radial (b) trapping efficiency for a coated BTG sphere with a core radius of 2.5 μm, as the SiO2 coating thickness varies; Figure S2: Relative change of the FWHM and maximum optical intensity of PNJs for a 2.5 μm-core-radius BTG sphere with different SiO2 coating thickness. Table S1: Optical trapping efficiency and PNJ property of five different microspheres in water. Video S1: Axial trapping efficiency with varied PS coating thickness; Video S2: Radial trapping efficiency with varied PS coating thickness.

Conflicts of Interest:
The authors declare no conflict of interest.