{'fraction_non_alphanumeric': 0.027673896783844427, 'fraction_numerical': 0.011219147344801795, 'mean_word_length': 4.792207792207792, 'pattern_counts': {'":': 0, '<': 0, '<?xml version=': 0, '>': 0, 'https://': 0, 'lorem ipsum': 0, 'www.': 0, 'xml': 0}, 'pii_count': 0, 'substrings_counts': 0, 'word_list_counts': {'cursed_substrings.json': 0, 'profanity_word_list.json': 0, 'sexual_word_list.json': 0, 'zh_pornsignals.json': 0}}
Magnesium Solubility in Primary α-Al and Heat Treatment Response of Cast Al-7Si-Mg

Magnesium and silicon concentrations in the interior of primary α-Al of Al-7Si-Mg alloys were studied at temperatures in the liquid-solid range and just after solidification was completed. Analysis of the results showed that the magnesium concentration in the interior of primary α-Al is very low in the temperatures range from the liquidus to the start of the Al-Si eutectic reaction. Formation of silicon-rich phases during eutectic reactions, such as eutectic silicon and β-Al5FeSi, phases trigger a significant increase in the magnesium concentration in the interior of primary α-Al, when sufficient time is allowed for solid-state diffusion to occur. When fast cooling rates are applied during the Al-Si eutectic reaction, most of the magnesium is retained in π-Al8FeMg3Si6 and Mg2Si phases formed during solidification. Semi-solid Al-7Si-Mg castings were produced with varying magnesium contents, and the mechanical properties were evaluated in the as-cast, T5 and T6 conditions. It was found that the 0.2% offset yield strength of the semi-solid Al-7Si-Mg castings in the T5 and T6 conditions increases linearly with the square root of the magnesium concentration in the interior of the α-Al globules formed during the slurry preparation process.