{'fraction_non_alphanumeric': 0.0329605650382578, 'fraction_numerical': 0.02118893466745144, 'mean_word_length': 4.743243243243243, 'pattern_counts': {'":': 0, '<': 0, '<?xml version=': 0, '>': 0, 'https://': 0, 'lorem ipsum': 0, 'www.': 0, 'xml': 0}, 'pii_count': 0, 'substrings_counts': 0, 'word_list_counts': {'cursed_substrings.json': 0, 'profanity_word_list.json': 0, 'sexual_word_list.json': 0, 'zh_pornsignals.json': 0}}
Li-ion and Na-ion transportation and storage properties in various sized TiO2 spheres with hierarchical pores and high tap density

Titanium oxide (TiO2) has attracted great interest as a promising anode material for lithium (Li) ion batteries (LIBs) and sodium (Na) ion batteries (SIBs). However, the key factors that dictate the Li-ion and Na-ion storage and transportation in TiO2 remain unclear. Herein, we report a facile hydrolysis route to crafting a variety of high tap-density TiO2 spheres with controllable size and hierarchical pores. The Li-ion and Na-ion storage properties based on these TiO2 spheres were systematically investigated. The pore distribution and the size of TiO2 spheres were found to exert profound influence on the Li-ion and Na-ion storage and transportation. The Li-ion storage and transportation in dense TiO2 spheres was dependent mainly upon the micropore distribution and volume and independent of the size of spheres. In contrast, the excellent Na-ion storage and transportation in TiO2 spheres was enabled by the loose structure with a large macroscopic pore volume and shortened Na-ion diffusion length. High tap-density TiO2 spheres (1.06 g cm−3) with superior Li-ion and Na-ion storage properties were produced, exhibiting a Li-ion storage specific capacity of 189 mA h g−1 at 1C and a high capacity retention of 88.1% after 100 cycles, and a Na-ion storage specific capacity of 184 mA h g−1 at 1C and capacity retention of 90.5% after 200 cycles. The ability to understand the critical factors controlling the Li-ion and Na-ion storage in high tap-density TiO2 spheres enables their implementation for practical applications in Li-ion and Na-ion batteries.