{'fraction_non_alphanumeric': 0.036731657419174855, 'fraction_numerical': 0.026068627754874306, 'mean_word_length': 4.391377005347594, 'pattern_counts': {'":': 0, '<': 0, '<?xml version=': 0, '>': 0, 'https://': 0, 'lorem ipsum': 0, 'www.': 0, 'xml': 0}, 'pii_count': 0, 'substrings_counts': 0, 'word_list_counts': {'cursed_substrings.json': 0, 'profanity_word_list.json': 0, 'sexual_word_list.json': 0, 'zh_pornsignals.json': 0}}
Simple and scalable growth of AgCl nanorods by plasma-assisted strain relaxation on flexible polymer substrates

Implementing nanostructures on plastic film is indispensable for highly efficient flexible optoelectronic devices. However, due to the thermal and chemical fragility of plastic, nanostructuring approaches are limited to indirect transfer with low throughput. Here, we fabricate single-crystal AgCl nanorods by using a Cl2 plasma on Ag-coated polyimide. Cl radicals react with Ag to form AgCl nanorods. The AgCl is subjected to compressive strain at its interface with the Ag film because of the larger lattice constant of AgCl compared to Ag. To minimize strain energy, the AgCl nanorods grow in the [200] direction. The epitaxial relationship between AgCl (200) and Ag (111) induces a strain, which leads to a strain gradient at the periphery of AgCl nanorods. The gradient causes a strain-induced diffusion of Ag atoms to accelerate the nanorod growth. Nanorods grown for 45 s exhibit superior haze up to 100% and luminance of optical device increased by up to 33%.

Efforts to fabricate nanostructures on rigid substrates include top-down methods such as photo- 16,17 , laser interference- 18 and e-beam lithography 19 ; and bottom-up methods such as synthesis of semiconductor nanorods (NRs) by vapour-liquid-solid (VLS) [20][21][22] , chemical vapour deposition (CVD) 23,24 and thermal oxidation 25 . However, most of these method are not suitable for fabricating nanostructure on flexible substrates. Lithography techniques use photoresists; their removal entails use of solvents that can damage a polymer film 26,27 . VLS, CVD and thermal oxidation require growth temperatures 4500°C [28][29][30] , but most plastic substrates cannot tolerate temperature 4150°C 31 .
To realize fabrication of nanostructures on flexible substrates, it will require simple fabrication methods that can be conducted at low temperature. Due to the chemical and thermal fragility of the polymer, indirect nanostructure-transfer methods such as nanoimprint lithography (NIL) [32][33][34] , and Langmiur-Blodgett methods 35,36 are widely used to fabricate nanostructures on plastic substrates. Recently, NIL has been used to form sub-wavelength structure with period of 250 nm and depth of 50 nm on polyethylene terephthalate (PET) films; because this structure minimized the waveguide mode in the substrate, OLEDs had 84% higher power efficiency than a device fabricated on planar film 37 . However, NIL has limited applicability to ultraviolet or thermal resins such as polymethyl methacrylate and polydimethylsiloxane [32][33][34] . Also, the method has low throughput, is complex and expensive, and uses master moulds that may deform after repeated use. The Langmiur-Blodgett process can transfer nanostructures with targeted density and thickness by immersing the substrates in a solution, but requires nanoparticles that have been functionalized with surfactant, and a subsequent careful dipping-pulling process. In addition, NRs fabricated by this method can be aligned only in lateral directions 38 , so the spatial density of NRs on the surface is low. Such problems could be solved by developing a plasma-assisted method to induce strain relaxation, which is the driving force of NR growth on polymer substrate. A polymer substrate flexes convexly during the growth of NRs, so migration of Ag atoms is accelerated by strain-induced diffusion; as a result, NRs grow rapidly on the polymer substrate.
Here, we demonstrate the growth of single-crystalline AgCl NRs by using a Cl 2 plasma source. Vertically well-aligned AgCl NRs were grown by a strain-relaxation process on several kinds of transparent substrate. To understand the growth procedures of AgCl NRs on Ag film, synchrotron radiation X-ray photoelectron spectroscopy (XPS) and X-ray diffraction (XRD) data were systematically examined with respect to plasma exposure time and various kinds of substrates. Spontaneous flexion of substrates during growth increases both the supply of Cl radicals and diffusion of Ag. From the off-axis phi-scan analysis and high-resolution transmission electron microscopy (HR-TEM) images, we propose a detailed growth structure, that is, AgCl NRs (200) grow epitaxially in cube-on-hexagon geometry on Ag (111) to minimize the strain energy.

Results
Fabrication of AgCl NRs on various substrates. Singlecrystalline AgCl NRs were grown on the transparent substrate with deposited Ag layer by introducing a chlorine plasma source. We deposited 300-nm-thick Ag on 100-mm-thick colourless polyimide (PI) film, then exposed the Ag to Cl 2 plasma (Fig. 1). During the plasma treatment, Ag atoms reacted with highly reactive Cl radicals on the surface of Ag film; as a result AgCl formed, as confirmed by XRD ( Supplementary Fig. 1).
The plasma condition has an important influence on the morphology of the AgCl nanostructures, so we optimized the plasma power (P) and process pressure (p) to produce well-defined AgCl NRs ( Supplementary Figs 2 and 3). At P ¼ 50 W, surface morphology of Ag was almost unchanged, because Cl radicals did not have sufficient energy. At P ¼ 200 W, the surface began to develop nanodots; at P ¼ 350 W, AgCl NRs were grown successfully, but at P4350 W, they began to shrink and aggregate. We then optimized p while maintaining P ¼ 350 W (Supplementary Fig. 3). At p ¼ 2 mTorr, NRs produced were short due to insufficient supply of Cl radicals. At p ¼ 10 mTorr, sufficient amount of Cl radicals led to longer NRs. However, at p ¼ 10 mTorr the NRs began to aggregate because of excessive supply of Cl radicals. Therefore, we identified P ¼ 350 W and p ¼ 10 mTorr for optimal growth of AgCl NRs.
Plasma exposure time can also affect the morphology of AgCl NRs (Fig. 2a). When Ag on PI film was exposed for 15 s, numerous AgCl nanodots were produced. At exposure time of 30 s, the nanodots began to grow to form NRs with length of 1 mm. Then, their length gradually increased until 60 s. As the exposure time increased over 90 s, the NRs became severely deformed to hierarchical structures. This simple method of NR growth could be applicable to any substrates including PET (film thickness ¼ 130 mm) (Fig. 2b) and soda-lime glass (700 mm) (Fig. 2c), but the growth rates strongly depends on the type of substrate. The growth behaviour of AgCl NR on PET film was similar to that on PI film, but the NRs grew slowly on 700-mm-thick glass (Fig. 2c).
Optical properties of AgCl NRs. The size and optical properties of the NRs can be controlled by changing Ag thickness (t Ag ) ( Fig. 3a). At t Ag ¼ 10 nm, AgCl nanostructures were parabolic. As t Ag increased, AgCl NRs became aligned orthogonal to the substrate. The surface morphology was examined with t Ag and plasma exposure time and summarized in Supplementary Fig. 4. The distributions of period and diameter were plotted and an Ag-coated substrates were exposed to Cl 2 plasma. During plasma treatment, Ag was reacted completely to produce AgCl nanorods on flexible plastic substrates. This growth method is compatible with roll-to-roll processing. ARTICLE NATURE COMMUNICATIONS | DOI: 10.1038/ncomms15650 average period and the average diameters were determined ( Supplementary Fig. 5). As t Ag increased from 10 to 500 nm, the average period changed linearly from 60 to 690 nm (Fig. 3b). The average diameter increased until t Ag ¼ 200 nm, then saturated (Fig. 3c).
The optical properties of size-tunable AgCl NRs were examined by using an integrating sphere to measure total transmittance (T total ) and Haze (H) (Fig. 3d,e). Over the wavelength range 400rlr800 nm, the as-received PI film had average T total ¼ 89.4% and H ¼ 0.22%. The sub-wavelength scale AgCl (t Ag ¼ 10 nm) had the highest average T total ¼ 93.2% and average H ¼ 0.27%, by providing gradually changed refractive index and allowing only zeroth-order transmitted light 39,40 . In contrast, the T total of the other AgCl structures decreased and H increased as t Ag increased. H was B100% at t Ag 4300 nm. The wavelength-scale structures induced high-order diffraction modes of transmitted waves, and thereby increased H. These AgCl NRs are suitable for substrates in OLED-illumination applications because high H causes scattering, which improves the outcoupling efficiency of confined wave-guided light in the substrates. T total and H were also measured as functions of t Ag and Cl 2 plasma time ( Supplementary Fig. 4b,c). Consequently, the light-scattering characteristics can be managed from haze-free to fully scattering by controlling the size of the AgCl nanostructures, which can be tuned simply by adjusting t Ag .
Surface analysis of AgCl NRs. The Ag 3d spectrum of as-deposited Ag film showed peaks centred at 374.0 eV and 368.0 eV (Fig. 4a), which are ascribed to Ag 3d 5/2 and Ag 3d 3/2 , respectively. These two peaks could each be separated into two groups. The peaks at 374.0 and 368.0 eV could be assigned to metallic Ag 0 (refs 41,42), and the peaks at 373.6 and 367.6 eV could be attributed to Ag þ of native silver oxide 43,44 . After Ag was exposed to the Cl 2 plasma for 45 s, peaks centred at 373.7 and 367.7 eV appeared; these can be ascribed to Ag þ of the AgCl (refs 45,46). The Cl 2p spectrum (Fig. 4b) showed no signal before the plasma exposure, but afterward the spectrum showed peaks centred at 199.4 and 197.8 eV, which are ascribed to Cl 2p 3/2 and Cl 2p 1/2 , respectively 47 .
To investigate electrical properties during the transition from Ag to AgCl, we measured current-voltage (I-V) curves of plasmaexposed Ag film on sapphire as a function of the Cl 2 plasma exposure time (Fig. 4c). In all cases, I increased linearly with V; in as-deposited Ag film, the resistance (inverse of slope) was 1.97 O. The resistance gradually increased with the plasma exposure time and reached 8.32 Â 10 10 O at 90 s. This trend is evidence that Cl 2 plasma treatment converts the Ag conducting layer to an AgCl insulating layer. These results suggest that treatment for 90 s caused the Ag to react completely to produce AgCl.
Crystallography of the AgCl NRs. The crystal structures of the AgCl NRs (Fig. 5a) were characterized using transmission electron microscopy (TEM). Selected area electron diffraction (SAED) patterns (inset) showed a few defects; they were caused by decomposition of AgCl to polycrystalline Ag under the high-energy electron beam 48,49 . HR-TEM images of the AgCl NRs show well-aligned rock salt single crystals (Fig. 5b,c). The NR grew along the [200] direction. The measured interplanar distances were 2.77 and 3.20 Å, which are consistent with those of (111) and (200) AgCl planes, respectively.
The growth direction of the NRs was also confirmed by XRD; the patterns ( Fig. 5d) of as-deposited Ag on the PI film and Cl 2 plasma-treated Ag were measured in the Bragg-Brentano configuration (y-2y geometry). In as-deposited Ag film, only Ag peaks exist and the peak of (111) crystallographic plane was dominant. After plasma treatment, only AgCl peaks existed, and diffraction on the (200) planes reached its maximum intensity. The Bragg-Brentano scan represents only crystallographic planes of the film that are parallel to the substrate, so these results indicate that large amounts of (200) planes of AgCl were parallel to the PI film. Because the NRs were aligned vertically on the substrate, their growth direction of the NRs was determined to be perpendicular to the (200)  To further confirm the epitaxial relationship between Ag and AgCl, off-axis phi scans (azimuthal scan) were performed. XRD phi scan was used to determine the crystal orientations of Ag and AgCl. To measure off-axis phi scans, we choose an arbitrary reflection plane which is not surface normal plane. To allow interpretation of the in-plane relationship, c-Sapphire was used instead of PI film. The surface normal planes of c-sapphire, Ag and AgCl are (006), (111) and (200) respectively. Thus, we performed phi scans along the c-sapphire (113) plane with psi of the phi scan and the surface normal plane of sample. In the phi scan, Ag film exhibited six-fold symmetry on c-sapphire substrates with coincidence in angular positions (Fig. 5e). This result reveals that Ag film was deposited on c-sapphire with (111)-preferred orientation. After Cl 2 plasma treatment, Ag changed to AgCl. Ag maintains the six-fold symmetry, but AgCl exhibits 12-fold symmetry with 30°intervals (Fig. 5f). Ag and AgCl had the same angular positions. AgCl (200) with 12-fold symmetry has three types of cubic domains, which are aligned on hexagonal Ag (111) planes with 60°azimuthal rotation (Fig. 5g). The phi scan confirmed that the growth direction of AgCl NRs was (200), which is in good agreement with HR-TEM observation (Fig. 5b).
Driving force of growth of AgCl NRs. On the basis of these results, we proposed a growth mechanism of the AgCl NRs (Fig. 6). When Ag was deposited, the face-centred-cubic Ag film tended to grow with the preferred orientation of (111) (Fig. 5d). During the initial stage of growth, Ag atoms on the surface of Ag film reacted with Cl radicals from the Cl 2 plasma (Fig. 6a). Conversion of Ag to AgCl nanodots imposes a large strain because of the lattice mismatch between Ag (lattice constant a Ag ¼ 4.079 Å 3 ) and AgCl (a AgCl ¼ 5.545 Å) (Fig. 6b). To minimize the strain energy, the nucleated AgCl nanodots had (200) orientation, which has the smallest lattice mismatch with Ag (111) film. Because the AgCl nanodots acted as a seed for the growth of AgCl NRs, the Ag atoms reacted with adsorbed Cl radicals at the interface of the NRs with Ag film (Fig. 6c). At that time, the AgCl underwent a compressive strain from the remaining Ag (Fig. 6e); to relieve this strain, NRs grew vertically. As a result, the basal plane of the NR was subjected to less strain than the surface area of AgCl between the NRs, so a strain gradient developed in the AgCl layer. This strain gradient induced strain-induced diffusion of Ag atoms in Ag film to the basal plane of the NR (Fig. 6f); this migration allowed selective growth of NRs at the bottom of the nucleated AgCl nanodot. In this mechanism, the supply of Cl radicals is constant, independent of the kind of substrate. Thus, diffusion of Ag atoms to the base of NRs determines their growth rates.     The growth mechanism of AgCl NRs on flexible film. The AgCl NRs grew rapidly as the substrate became thin (Fig. 2). To investigate the dependence of growth characteristics on the kind of substrate, XRD was measured on Ag-deposited PI film (Fig. 7a), glass (Fig. 7b) and c-sapphire ( Supplementary Fig. 6) as a function of plasma time. As-deposited Ag film showed only metallic Ag peaks. As the plasma exposure time increased, AgCl peaks began to appear and the Ag peaks weakened. The ratio of AgCl (Fig. 7c) (that is, [area of AgCl peak]/[total areas of AgCl and Ag peaks]) reached 1.0 within 20 s on the PI film but it took 120 s on both glass and on c-sapphire; that is, AgCl grew six times faster on PI film than on the glass and on the c-sapphire. This fast growth on PI is due to the spontaneous bending with convex shape during the Cl 2 plasma treatment (Fig. 7d). During NR growth, the flexible thin PI could bend to minimize the strain energy induced by lattice mismatch between Ag and AgCl, but the inflexible thick polycarbonate (PC) film and glass did not bend. This difference occurs because the PI film has the smallest bending radius due to its low thickness (d) and low Young's modulus (E) from the Stoney equation 50 (PI film: d PI ¼ 100 mm, E PI ¼ 2.5 GPa; glass: d glass ¼ 700 mm, E glass ¼ 74 GPa). The details are described in Supplementary Table 1.
To further investigate the effect of substrate bending on the growth of NRs, we conducted finite element method analysis on rigid glass (Fig. 7e) and flexible PI film (Fig. 7f). The reaction of Ag with Cl causes to expand the volume of Ag layer because a AgCl ¼ 5.545 Å is greater than a Ag ¼ 4.079 Å. This causes convex bending of PI film, but not of the stiff glass. The bending relaxes the strain, so flexion of the PI film caused strain distribution to vary rapidly at the Ag/AgCl interface ( Supplementary Fig. 7b) because the bending relaxes the strain. As a result, the strain gradient of 11.0 mm À 1 was localized near the edge of the NRs in the PI film (Fig. 7f). However, in the case of glass, there was no strain gradient ( Supplementary Fig. 7a) because of the high stiffness of the glass. The strain gradient on the glass was calculated to be only 0.79 mm À 1 (Fig. 7e). The strain gradient was calculated on the various substrates such as PI, PET, PC film, glass and sapphire. The elastic properties of substrates are summarized in Supplementary Table 1. The bending radius of substrates were calculated using the Stoney equation 51 and normalized to that of PI (Supplementary Table 1). The strain gradient at the edge of NRs was plotted as a function of relative bending radius ( Supplementary Fig. 8). As the degree of convex flexion increased, the strain gradient became increasingly localized at the edge of the NRs. The localization of strain gradient can increase the strain-induced diffusion of Ag atoms as 25,52 where J is the atomic flux, C is the atomic concentration, O is the atomic volume, D is the local diffusion coefficient, E is Young's modulus, k B is Boltzmann's constant, T is absolute temperature and e is the strain. In general, strain-induced diffusion is more dominant than that induced by the concentration gradient at low temperatures 53 , so the concentration gradient was neglected (Supplementary Table 2). Because the strain gradient was localized at the edge of the NRs on the PI film, strain-induced diffusion drove facilitated diffusion of Ag atoms toward the bases of the NRs, so NRs growth was accelerated on the PI film.
To test this hypothesized mechanism of rapid growth on PI, we attached the Ag-coated PI film to a rigid substrate (that is, the sample chuck in the plasma chamber) using double-sided kapton tape, so that the substrate could not bend under lattice-mismatch strain. Then the sample was exposed to Cl 2 plasma for 45 s (Fig. 8). It was found that no NRs were grown on the fixed PI film, as in the case of the rigid glass substrate. On the basis of this experiment, we conclude that the substrate bending critically contributes to the rapid growth of NRs, due to strain-induced diffusion. Experimental results provide evidence that Ag atoms diffuse to the bases of the NRs and react with Cl radicals until Ag is completely consumed, leading to the formation of single-crystal AgCl NRs.
Application of the AgCl NRs in OLEDs. These AgCl NRs could be applied to OLEDs. To investigate the effect of AgCl NRs on light extraction of the OLEDs, AgCl NRs on the backside of PI film were used as substrates. The device structure was WO 3 (36 nm)/Ag (12 nm)/WO 3 (3 nm)/WO 3 :CBP (230 nm)/CBP (10 nm)/Ir(ppy) 3 :CBP (30 nm)/TPBi (45 nm)/LiF (1 nm)/Al (100 nm). The reference device was fabricated on as-received PI film without AgCl nanostructure. The emission wavelength of Ir(ppy) 3 was 510 nm. To enable investigation of the effects of AgCl NRs on antireflection and light scattering, the device was designed to trap a large amount of light.
The current density-voltage (J-V) characteristics of OLEDs based on PI film with AgCl NRs are given in Fig. 9a. The measured operating voltages of a reference device and AgCl device (AgCl on the back of PI film) were ranged from 7.7 to 8.0 V at J ¼ 25 mA cm À 2 ; the difference is negligible. The current efficiency vs. luminance of the OLEDs (Fig. 9b) increased as t Ag increased to 200 nm, but decreased at t Ag ¼ 300 nm. At 1,000 cd m À 2 , the maximum current efficiency was 50.3 cd A À 1 in the reference device, 54.8 cd A À 1 at t Ag ¼ 10 nm, (8.9% increase vs. reference) and 66.9 cd A À 1 at t Ag ¼ 200 nm (33.0% increase vs. reference). The increase of current efficiency at t Ag ¼ 10 nm originated from increased T total due to the refractive index grading effect provided The angular dependence of emission characteristics of the devices varied with t Ag (Fig. 9c). The device with t Ag ¼ 10 nm showed increased emission intensity over a whole range of viewing angles without modifying the emission shape compared to the reference device. The haze-free nanostructure with t Ag ¼ 10 nm did not induce any light scattering, which can affect angular dependency of emission, so the emission pattern of this device was the same as that of the flat device. However, as t Ag increased, the angular emission patterns of AgCl device approached a Lambertian intensity distribution; the change was mainly due to strong scattering of light by AgCl NRs. The emission of the scattered light in all azimuthal directions could contribute to improved angular dependence of colour stability of the OLEDs. The Commission Internationale de l'éclairage (CIE) 1931 colour coordinates of the OLED with t Ag ¼ 200 nm did not change as emission angle increased (Supplementary Fig. 9). These results indicate that the subwavelength-scale AgCl obtained using t Ag ¼ 10 nm is suitable for high-definition display windows by increasing luminance without sacrificing optical clarity, whereas wavelengthscale AgCl obtained using t Ag ¼ 200 nm is suitable for light illumination by increasing light extraction efficiency and improving colour uniformity over all emission angles.
To theoretically study the optical effects of the AgCl NRs on the light extraction efficiency for the OLEDs, two-dimensional finite-difference time-domain (2D FDTD) simulations were performed. Except at the bottom layer, the perfect matched layer was used as the boundary condition to avoid occurrence of an unwanted reflected wave at the edge of the structure. At the bottom layer, the perfect electric conductor boundary condition was used to approximate the metallic mirror at the bottom of the OLEDs. The vertical and horizontal point dipole sources were excited with a wavelength of 510 nm in the active layer. The simulations were performed until steady-state was reached (that is, change of electric field is o0.01% per FDTD time step). The cross-sectional electric field distributions were obtained at steady state by using a discrete Fourier transform (DFT) monitor. The vertical and horizontal dipoles were incoherently combined to get the electric field distribution under an un-polarized dipole source.
The electric field distributions (Fig. 9d) were obtained for the flat device, and for devices with t Ag ¼ 10 nm and with t Ag ¼ 200 nm. In the flat device, the electromagnetic wave was confined in the substrate due to total internal reflection at the interface between air and the PI film. In the device with t Ag ¼ 10 nm, the electric field near the centre (X position ¼ 0) was enhanced compared to that of the flat device (Fig. 9e), because subwavelength scale AgCl provided gradually changed refractive index. Because haze was zero, the field distribution in the air was similar to that on the flat device. However, the device with wavelength-scale (on t Ag ¼ 200 nm) AgCl NRs showed dynamic electric field intensity outside the PI film because the NRs extract the confined wave from the PI substrate, so the field intensity inside the PI film was significantly decreased in the device that had the AgCl NRs. As a result, the calculated light extraction efficiency of the OLED was 46% greater in the device with NRs The AgCl NRs also showed excellent mechanical flexibility. To verify the mechanical stability of the AgCl NRs on PI film, we conducted bending test with various bending radius and bending cycles. The NRs were stable as the bending radius (r) reduced to 1.73 mm (Fig. 10a). No changes in the morphology of NRs and no cracks were found after up to 10,000 bending cycle at r ¼ 1.73 mm (Fig. 10b). Furthermore, the average total transmittance and haze of PI film were sustained even after 10,000 bending cycles (Fig. 10c).

Discussion
We have developed single-crystalline AgCl NRs on various kinds of substrates. By only exposing Ag to Cl 2 plasma, we achieve vertically well-aligned NRs within 1 min, which is the fastest growth ever reported for the growth of single-crystalline NRs. On the basis of experimental observations, we proposed the following growth mechanism of the AgCl NRs, Ag atoms consistently diffuse to the base of NRs and react with incorporated Cl radicals to form AgCl. During the reaction, AgCl is subjected to compressive strain due to volume expansion from Ag to AgCl. During the strain relaxation process, AgCl NRs grow along the [200]-preferred direction on the (111) Ag film to minimize lattice mismatch. XRD reveals that interface relationship between AgCl (200) and Ag (111) is cube-on-hexagon epitaxy. We discussed the effect of bendability of substrate on growth: flexion of the substrate facilitates diffusion of Ag atoms to the base of NRs, thereby promoting their growth. The size of the AgCl nanostructure can be controlled from sub-wavelength scale to wavelength scale simply by changing the thickness of the Ag layer. As a result, light scattering was successfully controlled, which is a critical requirement for nanostructure-based devices. The AgCl NRs on PI film were used in OLEDs. The sub-wavelength AgCl increased OLED luminance by 8.9% compared to as-received PI film, and did not induce blurring or haziness. Due to light scattering, wavelength-scale NRs improved luminance efficiency by 33.0% and reduced the change of colour uniformity over emission angle.
There were a number of reports on the growth of NR using several kinds of growth techniques. Inorganic nanowires can be synthesized by various methods such as VLS, CVD, thermal oxidation and hydrothermal (Supplementary Table 3). However, VLS, CVD and the thermal oxidation methods required high temperature (greater than 400°C), which would damage a polymer substrate. The hydrothermal method can grow NRs at low temperatures (about 100°C), but the growth rate is too slow (less than 1 nm min À 1 ). The high process temperatures and slow rates of the previous methods are serious disadvantages for application to polymer substrates. In this work, we found a way to use a Cl 2 plasma source to grow the single-crystalline and vertically wellaligned AgCl NRs. The advantages of this technique are low temperature process (room temperature) and high-growth rate (about 2,000 nm min À 1 ). Such process condition allows the AgCl NRs to implement the R2R process shown in Fig. 1.
To confirm the applicability of the method to R2R process, we designed a virtual roll-to-roll (R2R) system ( Supplementary  Fig. 10). The plasma exposure time is a critical factor for application to R2R process. The plasma time of 45 s is sufficient to get the NRs (Fig. 2). Because the deposition rate of Ag layer did not have a significant effect on morphology or growth rate of AgCl NRs ( Supplementary Fig. 11), the deposition rate was set to be 20 Å s À 1 .
When the plasma chamber was 90 cm long, and the Ag-deposition chamber was 300 cm long, the feed rate of R2R process was 1.2 m min À 1 , which could be used in a commercial process. As a result, the plasma-induced AgCl NRs could be rapidly fabricated using an R2R process over a large area on several kinds of polymer film because the method does not require lithography, mask moulds or thermal processes. These size-tunable and plasma-induced AgCl NRs can promote the commercialization of highly efficient, inexpensive flexible optoelectronic devices.

Methods
Fabrication of AgCl NRs. The colourless PI films were ultrasonically cleaned with isopropyl alchol for 5 min, then dried under blowing N 2 gas and baked at 110°C for 10 min. The Ag layer was deposited at 1 Å s À 1 on the PI film by using an e-beam evaporator under 1 Â 10 À 6 Torr. Then PI films with Ag layers were treated using Cl 2 plasma. The plasma was induced using 350-W RF power in Cl 2 ambient. The chamber pressure was maintained at 10 mTorr during treatment.
Characterized instrument. The total and diffused transmittance of the AgCl/PI sample were measured using a ultraviolet-visible-NIR spectrophotometer (Cary 4000, Agilent) with a diffuse reflectance accessory. The surface morphology of the AgCl was measured using a field-emission scanning electron microscope (XL30S FEG, PHILIPS) with an 5 kV acceleration voltage and 6 mm working distance, and an atomic force microscope operated in tapping mode on a Veeco nanoscope III. XPS was measured using a synchrotron radiation photoemission spectroscopy with the incident X-ray source at 650 eV and a base pressure of 5 Â 10 À 10 Torr at the 4D beam line at the Pohang Accelerator Laboratory (PAL). The chemical bonding states were separated using a combination of Gaussian and Lorentzian functions. The XRD patterns were measured using a house X-ray source (D2 phaser, Bruker) at 30 kV and 10 mA. Off-axis phi scans using synchrotron radiation were performed at the 3D beamline at PAL. The HRTEM (JEM 2200FS, JEOL) was conducted at 200 kV with a Cs-corrector. The AgCl NRs were sonicated in ethanol and put in a Cu grid. To prevent e-beam decomposition of the AgCl, 10 nm of carbon was deposited on both sides of the Cu grid. The J-V characteristics of the OLEDs were measured using a Kiethley 2400 source metre in N 2 ambient. Luminance characteristics of the OLEDs were measured using a calibrated colorimeter (Qbism HEXA50, McScience) in N 2 atmosphere. The EL spectra of OLEDs were measured using a spectrometer (SM240, Spectral Products) equipped with an optical fibre.
Theoretical modelling and calculation. Two-dimensional finite element method analysis were performed to investigate the effect of bending on growth of AgCl NRs. The simulation tool was commercial software ABAQUS v6.9. The simulation structure consisted of AgCl NRs (E ¼ 20 GPa, u ¼ 0.4), Ag (E ¼ 83 GPa, u ¼ 0.37) 150 nm, and PI (E ¼ 2.5 GPa, u ¼ 0.34) or glass (E ¼ 74 GPa, u ¼ 0.3) substrates, which represented the intermediate state of NR growth. The thickness of the substrate was reduced to 500 nm. On the glass, the bottom of the structure was pinned to represent the rigid glass. The AgCl NRs were set to have period ¼ 300 nm, diameter ¼ 100 nm and height ¼ 600 nm. The reaction of Ag with Cl was assumed to cause volume expansion at the interface of NRs with Ag film. Thus, the top of Ag layer was expanded by 36% and the elastic property of the layer changed from Ag to AgCl. The mesh size of the substrates was 50 nm and the sizes of Ag and AgCl were 25 nm.
Two-dimensional FDTD method with a perfect matched layer was used for numerical analysis of light extraction. The simulation tool was electromagnetic caclulation module (R Soft Fullwave) from commercial software R soft 2014. 09 (Synopsys and R soft Design Group, Inc.) The simulation structure consists of an Aluminium cathode (100 nm), LiF (refractive index n ¼ 1.39) 1 nm, TPBI (n ¼ 1.75) 45 nm, CBP:Ir(ppy) 3 (n ¼ 1.75) 30 nm, CBP (n ¼ 1.75) 10 nm, CBP:WO 3 (n ¼ 1.77) 230 nm, WO 3 (n ¼ 1.92) 3 nm, Ag 12 nm, WO 3 (n ¼ 1.92) 36 nm and PI substrate (n ¼ 1.6) 3 mm. The thickness of the PI substrate was reduced to 3 mm larger than five times the optical wavelength, because the real thickness of PI substrate (100 mm) is too large and consumed too much time in the FDTD simulation. The total width of the structure is 30 mm, which is enough to get saturated extraction efficiency as a function of width. On the basis of analysis of SEM and AFM images, the sub-wavelength AgCl nanostructure was set to have period ¼ 60 nm, diameter ¼ 50 nm and height ¼ 70 nm; and the wavelength-scale AgCl NR was set to have period ¼ 300 nm, diameter ¼ 200 nm and height ¼ 1.5 mm The grid size of the simulation was 10 nm, which is small enough to resolve AgCl nanostructures. Due to this large calculation domain and small grid size, 2D simulation was used to reduce computation time. Horizontal and vertical dipole sources were used. The DFT monitor was used to get the cross-sectional spatial electric field distribution during steady state.
Data availability. The data that support the findings of this study are available from the corresponding author upon request.