{'fraction_non_alphanumeric': 0.03284652831155521, 'fraction_numerical': 0.01921598770176787, 'mean_word_length': 5.023456790123457, 'pattern_counts': {'":': 0, '<': 4, '<?xml version=': 0, '>': 0, 'https://': 0, 'lorem ipsum': 0, 'www.': 0, 'xml': 0}, 'pii_count': 0, 'substrings_counts': 0, 'word_list_counts': {'cursed_substrings.json': 0, 'profanity_word_list.json': 0, 'sexual_word_list.json': 0, 'zh_pornsignals.json': 0}}
Biomechanical development and evaluation of a new framework for all-on-four rehabilitation

Abstract Introduction For complete rehabilitation of fully edentulous mandibles, the option for immediate loading determines the use of temporary prostheses that splint the installed implants. Although temporary prostheses with reinforcement provide rehabilitations with biomechanical benefits, the non-adoption of this recommendation coexists in different studies on immediate restorations. Objective This study evaluates a type of prosthesis to restore jaws by the all-on-four concept. Material and method: The mechanical behavior of prostheses with the modified framework was evaluated in vitro, under a cantilever mechanical unilateral bending test. Two representative groups were included in the all-on-four concept, with a G1 test group (n = 10) containing modified frameworks and a G2 control group (n = 10) that included full acrylic prostheses. The samples were submitted to thermal cycling with 500 cycles (5° ± 2 °C for 30 s, and 55° ± 2° for 30 s) and to the mechanical bending test on the cantilever. Result The Mann-Whitney test revealed a significant difference between G1 and G2 (p <0.001). In the descriptive evaluation, G1 averaged 830.50 N until the initial resin fracture, while the control group presented a mean of 403.58N. The maximum resistance until complete fracture was recorded in G1, with a mean of 903.03N, while in G2, a mean of 435.20N was recorded. The linear vertical component of the flexion was 0.68 mm and 0.39 mm until the initial fracture of the bar, respectively for G1 and G2. Conclusion The modified framework for the all-on-four protocol determined better mechanical performance when compared to the same full acrylic prosthesis model.


INTRODUCTION
The all-on-four concept (Nobel Biocare, Gothenburg, Sweden), a rehabilitation modality that combines axial anterior and angled posterior implants with immediate load on the mandible, has been validated by longitudinal studies 1,2 . Since it was developed by Maló et al. 3 , the surgicalprosthetic technique has shown excellent results and predictable success rates 4-6 .
After 5-year and 10-year follow-ups, implant success rates of 98.1% and 94.8%, respectively, were observed. Excellent results were also obtained in biomechanical evaluations of prosthetic rehabilitation of the edentulous mandible, by means of the all-on-four concept 2 . By using four implants, balanced by greater spacing among them, the expected polygonal setup is maintained, ensuring sufficient biomechanical stability to the prosthesis, and appropriate force distribution to bone 5,[7][8][9] .
Advantages of this concept include the possibility of using long implants and the reduced need for bone graft 8 . The prevention of long cantilevers, as well as the possibility of increasing the distance between anterior and posterior pillars, characterize the significance of the proposal 9,10 .
Other advantages include a lower cost and easier cleaning, due to the reduced number of implants 5,11 .
However, different studies report on prosthetic complications and temporary acrylic prosthesis breaks during the post-surgery recovery phase 4,5,9,10 . The choice to prepare the temporary prosthesis without internal reinforcement contributes to the occurrence of complications varying between 10.8%, according to Hinze et al. 5 , and 30% reported on Maló et al. 3 study, whereas the temporary prostheses, with internal reinforcement, are considered to be the golden standard as they offer biomechanical advantages 11 . The metal framework promotes rigid splinting and maintains implant micromovements below the critical threshold, favoring osseointegration 12 . The prosthesis metal reinforcement hinders fracture and may also reduce bending forces, decreasing bone stress and favoring the required hardness during the implant scarring phase 8 .
However, a quality metal reinforcement, ensuring a passive fit of the prosthesis, requires more time and adds to the financial costs of rehabilitation 1 . Alternatives for planning effective frameworks have been discussed in several studies 8,[12][13][14][15] . Despite the advances, no evidence has been observed 4,6,8,11 that complement the simplicity proposed by Maló et al. 2,3 .
The present study proposes a new type of immediate prosthesis for the all-on-four protocol, consisting of non-welded metal structure, designed to offer an in vitro view of mechanical behavior of these prostheses regarding their fracture resistance, when compared to fully acrylic prostheses without internal reinforcement.

MATERIAL AND METHOD
Two sets of test specimens have been compared, one test group named G1 (n = 10), and the other, G2 (n = 10). G1 included prostheses with a metal framework in non-welded cobalt-chromium alloy, cast and machined separately from the support cylinder and later combined with machined and pre-fabricated titanium cylinders during the acrylic press. G2 consisted of fully acrylic prostheses for the all-on-four protocol.
Previous waxing and mounting of the acrylic teeth were performed in order to reproduce the ideal tooth distribution, in a full Brånemark protocol mandibular prosthesis, allowing for the adjustment of the implant geometry and positioning. Based on this waxing, a diagnostic model was developed, in heat activated acrylic resin, containing four analogs of mini conical pillars with a 4.1-mm platform, a 3-mm band, and 20-degree convergence (Neodent, Curitiba, PR, Brazil). The two anterior analogs were positioned perpendicularly to the areas corresponding to the cingulum of the lateral incisors, and the two posterior analogs were positioned in the second pre-molar region, in accordance with Maló et al. 3 protocol. To simulate the immediate post-surgical clinical status, after inserting the prosthetic mini-pillars, the diagnostic model posterior analogs were inserted without inclination for the prosthetic platform parallel to the occlusal plane to represent the distal implant angle (30 degrees).
By means of a transference index (Figure 1a), with molding components consisting of metal stems connected by low contraction acrylic, the position of prosthetic components was transferred to a carbon steel metal disc, constituting the metal master model (MM) (Figure 1b). The MM was prepared to also be coupled to the trial machine, working as a support for the mechanical test. With the aid of the AutoCAD 2007 software (Autodesk, California, USA), a metal structure was prepared for prosthetic reinforcement that was compatible with the all-on-four protocol (Figure 1c), adopting the following dimensions: 2.0-mm gingival-occlusal width, 6.8-mm vestibular-lingual width, and 10-mm cantilever. Four circular 4.9 mm diameter drills were designed to insert the support cylinders (Neodent, Curitiba, PR, Brazil). With this diameter, the framework ran through the conical shape of the cylinders, with a cervical shoulder fit and a 0.6-mm support around the entire opening. After the layout was completed, the framework was printed in 3D with the support of a SD 300 Pro printer (SKA, Tel Aviv, Israel). From the prototype, it was possible to develop a metal matrix (M0) designed to reproduce the resin patterns under press (Pattern Resin LS GC, Tokyo, Japan) for the future metal frameworks ( Figure 2a). After dimensions have been checked with the help of a caliper, 20 acrylic frameworks were selected to constitute both experimental groups. For the G1, ten frameworks have been processed and cast in cobalt-chrome (Co-Cr) alloy ( Figure 2b). For the G2, ten acrylic patterns were reserved, free of any processing.
The prosthesis section designed to press the resin was reproduced over two other matrices (M1 and M2) (Figure 2a). The M1 enabled the positioning of the G1 frameworks, and M2 was prepared to control the G2. The M1 was different as it spaced the framework at 1.5 mm from the cylinder shoulder, whereas in M2, the structures came in contact with each other. Both matrices bore implant analogs to be bolted to the cylinders when the prostheses are mounted.
Both matrices allowed for the mounting of the prototypes in wax, with a 6.8-mm vestibular-lingual width and a 6.9-mm cervical-occlusal height, including titanium frameworks and cylinders (Figures 2c and 2d). In M1, rubber rings were inserted (1.5 mm) over the titanium cylinder shoulder to ensure homogeneity between the spacing and the bars (Figure 2c). After being verified with a caliper, the prototypes were bolted onto twenty models, constituting copies of the MM model, with titanium analogs and bases in type IV gypsum stone (Herostone, Vigodente, RJ, Brazil). In sets of four units, the models with their respective prototypes were included in muffle. After a gypsum press time of approximately 30 minutes, the muffle was taken to a microwave oven (LG 1200W, LG Electronics, SP, Brazil) for one minute and twenty seconds to melt the wax. After full wax removal, the pre-fabricated cylinders were cleaned with a brush and blasted with 125-micrometer particles of aluminum oxide, and once again bolted to the models included in the muffles. G1 frameworks were also blasted with aluminum oxide. Microwave power activated resin powder and liquid (VipWave, Vip, São Paulo, SP, Brazil) were proportioned according to the manufacturer's instructions and deposited inside the muffle, which was pressed at 1 ton for 20 minutes. Following manufacturer's instructions for full acrylic polymerization, in the initial stage, the muffle was maintained for 20 minutes at a 10% to 20% power in a microwave oven, and in the final stage, for 5 minutes at a 30% to 40% power.
The spacing between the support cylinder metal bar and the shoulder in the G1 group, after polymerization, enabled the formation of a resin collar that connected these structures. After unmuffling, the test specimens were cleaned with a brush and stored in water at 37° ± 1 °C until thermal cycling.
The test specimens were bolted to a different model, also originated from the MM, and ten-unit groups were subjected to 500 cycles in a thermocycler (MSCT/3e-ELQUIP, São Paulo, SP, Brazil). Each cycle consisted of 30-second baths, alternating in water at 5° ± 2 °C and 55° ± 2 °C. When the thermal cycling was completed, the test specimens were evaluated visually by means of a stereoscopic magnifier, STEMI 2000-C (Zeiss, Germany), 20x magnification, by a duly calibrated examiner, who did not observe apparent damages in the test specimens. After the thermal cycling, the test specimens were stored again in water at 37° ± 1 °C.
The MM was coupled to a universal tester (EZTest 5kN, EZ-L, Shimadzu, Japan); here the G1 and G2 test specimens were individually bolted at 20N torque in each titanium bolt. A loading piston was positioned over the right cantilever, 5 mm apart from the bar distal edge, exerting a compressive axial force with a maximum limit of 1,000N. The applied speed was 0.5 mm/minute until the test specimen was fractured, or until it reached the maximum load ( Figure 3). The mechanical behavior data for the sample were recorded, and the analysis was performed using the software SPSS version 13.0 for Windows (SPSS Inc., Chicago, IL). Descriptive statistical analyses were developed for the following dependent variables: maximum supported load until the initial resin fracture, linear extension of deformation, and maximum withstood load until full fracture.

RESULT
Thermal cycling, under evaluation with a magnifier, produced no apparent damages in the test specimens. The bending test caused full fractures in the test specimen cantilevers that propagate through the vestibular-lingual interface, adjacent to the distal cylinder, in a cross section of the bar (Figure 3). Initial fractures (FI) occurred in the resin, which, as the test progressed, became full of fractures (FC), characterized by the sudden tension drop recorded by the trial machine software. Figure 4 presents the deformation charts (%) and applied load (N) generated in the Universal Tester, with evidence of initial fracture (FI) and complete fracture (CF). Table 1 presents the descriptive analysis of the dependent variables. The Mann Whitney test revealed statistical significance in the inter-group comparison for the withstood load until initial resin fracture (p<0.001), maximum applied load (p<0.001), as well as in the vertical-linear component of the cantilever bending (p<0.001).

DISCUSSION
The success of the all-on-four concept has been clinically reviewed for the survival rate of implants 2,3,5,9,10,12,16 , despite the occurrence of prosthetic complications, ranging from 10.8% to 30% in full temporary prostheses, for edentulous mandible rehabilitation 1,3,5,9,10 . The highest occurrence rates were found in works that used no reinforcement structure for the prostheses 1,3 .
Similarly, in the present study, bending load resistance differences between G1, with metal framework, and G2, without such reinforcement, were significant. Figure 4 shows that, in G1, there was greater load absorption, with a lower percentage of deformation. At the start of deformation, the lines corresponding to each test specimen are noticeably steeper, when compared to G2. The behavior in G1 reveals greater hardness, as the N/m ratio is higher when compared to G2 17 .
Although Maló et al. 3 have reported that the prosthetic failures recorded were repairable and had no effect on survival rates, this study detected full fractures on the cantilever end. When they occur clinically, full fractures require unbolting the prosthesis for repair, within the scarring period between 4 and 6 weeks, when operating with an immediate load 18 . Early removal may lead to counter-torque exceeding the resistance of the bone being remodeled, and may interfere in osseointegration 2,12 . Therefore, the metal framework reviewed in this study, may contribute to the elimination of future prosthetic problems.
Several studies 1,5,9,10 make no reference to the use of metal framework, nor do they discuss the evidence obtained from excluding the reinforcement. The decision made may arguably have been influenced by the difficulty in developing, during the immediate post-surgical period, a quality, low-cost framework that allows for resistance and passive adaptation.
Bending resistance is known to evaluate the maximum bending the material may withstand before fracture 19 . Taking into account the occurrence of free distal extension, subjected to the masticatory function, bending resistance becomes a relevant clinical factor in all-on-four rehabilitations.
The proposal of a design that would provide spacing between the metal bar and the support cylinder shoulder, allowing, after pressing, for the formation of a resin collar that would join these structures, sought greater occlusal load absorption and better dissipation among the implants, avoiding direct contact between metals. Studies that evaluated stress concentrations on full prosthesis upon the edentulous mandible revealed an overload on the distal implant 4,6 . Even when distal angled implants were selected, with the possibility of a stress concentration reduction of up to 17%, the stress accumulation for cantilever adjacent implants still persists 20 .
The metal bar design with structural modification allowed for the assembly to reach a bending linear-vertical component of 0.68 mm up to the initial fracture for G1 test specimens. An increase in this bending linear extension reached 74.36%, which was deemed satisfactory when compared to the G2. All fractures, however, occurred in the distal interface of the last implant, which confirms the stress concentration shown in findings from Begg et al. 6 on distal implant biomechanics.
In designs, including a bar isolated from the cylinders, exhibiting relative spatial freedom between them and the framework, the resistance element under observation in this study becomes the interface between the resin, the cylinder, and the metal bar. Therefore, this study proposed the evaluation of all bars with resin subjected to thermal cycling 21 , simulating the assembly thermal fatigue. Even with thermal aging, the results of absorbed load up to the initial fracture were higher than those of the control group, and higher than the average observed in other studies 4,6 .
The prosthesis evaluated in G1 withstood the occlusal load on the cantilever (830.50N) up to the initial resin fracture. Taking into account that the occlusal load recorded on the molar region in patients with implant treatment showed a variation ranging between 112.5N and 450N [22][23][24] , the resistance increment for the framework proposed in this study may be valued. Similarly, the G2 control group withstood the bending load (403.58N), a value close to those found in previous works 1,5,9,10 regarding the occlusal load and may explain a greater occurrence of failure in prosthesis without reinforcement bars.
The bar allowed for the exclusion of metal welding 12,13 , as they were cast in a single block.
Casting the structure, independently from the cylinders, contributed to the absence of influence of metal alloy cooling contraction and casting failures inherent to the process of obtaining conventional frameworks in prosthetic adaptation in the present study, considering the connection to the cylinders took place during the pressing phase. During this stage, placing the cylinders over the master model provided better control of its position.
In the present study, the master model copy (M1) was the basis for pressing the prostheses. The cylinders and the metal bar were fastened to this model, ensuring fidelity to the MM after pressing. Therefore, for the clinical use of this proposal, it would be important to obtain faithful models of the implant distribution in the mouth. The option to use the transference index with auxiliary metal bars and low acrylic contraction was based on work showing satisfactory results with this technique 25 .
The G2 group exhibited initial fractures under lower loads other than those observed in the G1 group. The lowest mechanical resistance observed in the fully acrylic bar proves the findings in the clinical study conducted by Maló et al. 3 Despite the fracture rates reported in different studies and this control group behavior, structures that are not fully acrylic are still mentioned in restoration protocols for the edentulous mandible 5,9,10,26 .
Only two clinical post-surgical moments are required to install the temporary acrylic prosthesis, associated with the non-welded bar, and to put it into operation. In addition, the opportunity of not using welds or cement to join the cylinders to the bar offers effective results at a low cost, showing simplicity and speed. Due to its mechanical properties, the metal reinforced temporary acrylic prosthesis may be used for a longer period beyond the scarring period, and may also be used as a lower cost final prosthesis 3,12 .
This study presented limitations, especially due to the low number of samples tested and due to the fact that it was an in vitro study. In vivo longitudinal studies are warranted to achieve clinical results that allow for a comparison to this in vitro study.

CONCLUSION
Results have confirmed that the metal reinforcement increased the final resistance of temporary acrylic prostheses. The connection resin interface between the metal bar and the cylinders increased the resistance to the bending load.