{'fraction_non_alphanumeric': 0.04320337197049526, 'fraction_numerical': 0.032665964172813484, 'mean_word_length': 4.900621118012422, 'pattern_counts': {'":': 0, '<': 0, '<?xml version=': 0, '>': 0, 'https://': 0, 'lorem ipsum': 0, 'www.': 0, 'xml': 0}, 'pii_count': 0, 'substrings_counts': 0, 'word_list_counts': {'cursed_substrings.json': 0, 'profanity_word_list.json': 0, 'sexual_word_list.json': 0, 'zh_pornsignals.json': 0}}
Large Tunneling Magnetoresistance at Room Temperature Using a Heusler Alloy with the B2 Structure

A Co2Cr0.6Fe0.4Al Heusler alloy film exhibited a B2 structure, which was deposited using a magnetron sputtering system on a thermally oxidized Si substrate at room temperature without any buffer layers. The film exhibited the magnetic moment of 2.04µB per formula unit, nearly the integer number of Bohr magnetons, suggesting a localized nature of ferromagnetism similar to that of many Heusler compounds, which is a necessary condition for half metallicity. A spin- valve-type tunneling junction with a Co2(Cr, Fe)Al Heusler alloy film was fabricated using metal masks, which consists of Co2Cr0.6Fe0.4Al(10 nm)/AlOx (1.8 nm)/CoFe (3 nm)/NiFe (5 nm)/IrMn (15 nm)/Ta (5 nm), deposited on a thermally oxidized Si substrate without a buffer layer. The junction demonstrated large tunneling magnetoresistances of 16% at room temperature and 26.5% at 5 K.