{'fraction_non_alphanumeric': 0.010954616588419406, 'fraction_numerical': 0.004694835680751174, 'mean_word_length': 5.2745098039215685, 'pattern_counts': {'":': 0, '<': 0, '<?xml version=': 0, '>': 0, 'https://': 0, 'lorem ipsum': 0, 'www.': 0, 'xml': 0}, 'pii_count': 0, 'substrings_counts': 0, 'word_list_counts': {'cursed_substrings.json': 0, 'profanity_word_list.json': 0, 'sexual_word_list.json': 0, 'zh_pornsignals.json': 0}}
An Investigation of Hardness Homogeneity and Microstructure in Pure Titanium Processed by High Pressure Torsion

High-pressure torsion (HPT) was conducted on disks of commercial purity Ti under applied pressures of 3 and 6 GPa. Measurements of the Vickers microhardness showed improving hardness homogeneity with increasing numbers of HPT turns. Transmission electron microscopy demonstrated that a higher HPT pressure leads to a smaller grain size after straining and these grains contain a high dislocation density with arrays of twins. This is consistent with the higher hardness of the Ti samples processed by HPT under 6 GPa pressure.