{'fraction_non_alphanumeric': 0.03393014382154388, 'fraction_numerical': 0.026240093924273556, 'mean_word_length': 4.486634460547504, 'pattern_counts': {'":': 0, '<': 1, '<?xml version=': 0, '>': 3, 'https://': 0, 'lorem ipsum': 0, 'www.': 0, 'xml': 0}, 'pii_count': 0, 'substrings_counts': 0, 'word_list_counts': {'cursed_substrings.json': 0, 'profanity_word_list.json': 0, 'sexual_word_list.json': 0, 'zh_pornsignals.json': 0}}
Fabrication of Ga2O3 Schottky Barrier Diode and Heterojunction Diode by MOCVD

In this article, we reported on a Ga2O3-based Schottky barrier diode and heterojunction diode from MOCVD. The Si-doped n-type Ga2O3 drift layer, grown by MOCVD, exhibited high crystal quality, flat surfaces, and uniform doping. The distribution of unintentional impurities in the films was studied. Then nickel Schottky barrier diode and p-NiO/n-Ga2O3 heterojunction diode were fabricated and measured. Without any electric field management structure, the Schottky barrier diode and heterojunction diode have specific resistances of 3.0 mΩ·cm2 and 6.2 mΩ·cm2, breakdown voltages of 380 V and 740 V, thus yielding power figures of merit of 48 MW·cm−2 and 88 MW·cm−2, respectively. Besides, both devices exhibit a current on/off ratio of more than 1010. This shows the prospect of MOCVD in power device manufacture.

In semiconductor devices, a high-quality film with stable electrical properties is an important factor in ensuring the device's performance. Ga 2 O 3 films can be grown by molecular beam epitaxy (MBE) [26,27], low-pressure chemical vapor deposition (LPCVD) [14], halide vapor phase epitaxy (HVPE) [28,29], mist-chemical vapor deposition (mist-CVD) [13], and metal-organic chemical vapor deposition (MOCVD) [12,15]. Currently, HVPE is the dominant method for Ga 2 O 3 epitaxial wafers due to faster growth rates and lower carbon impurity. However, since the fast growth rate will lead to contamination and a rough surface of the film, chemical mechanical polishing (CMP) is necessary to achieve a smooth surface. At the same time, other impurities will be introduced into the film during the CMP [16]. Compared with HVPE, the growth rate of MOCVD is slower, but the surface of the Ga 2 O 3 film tends to show a uniform step flow mode, making epitaxial wafers unnecessary to polish. In addition, MOCVD also has advantages in precise doping and low background carrier concentration, which makes MOCVD have great potential in growing Ga 2 O 3 films [16,18]. In the current reports, the fabrications of Ga 2 O 3 SBDs and HJDs are mostly based on HVPE Ga 2 O 3 epitaxial wafers [4,5,19,20,24]. However, there are few reports on Ga 2 O 3 power diodes from MOCVD [18].
In this paper, the homoepitaxy of the Ga 2 O 3 drift layers was performed on the (001) Ga 2 O 3 substrate by MOCVD, and the nickel SBD and p-NiO/n-Ga 2 O 3 HJD were fabricated.

Film Characterization
The characterization results of Ga 2 O 3 films are shown in Figure 1. From the XRD in Figure 1a,b, it can be found that the Ga 2 O 3 film exhibits a strong preferred orientation along the <001> direction. The full width at half maximum (FWHM) of the rocking curve of the (002) diffraction plane is 36.7 arcsec, basically close to the 28.6 arcsec of the substrate, indicating low dislocation density. From the FESEM and AFM images shown in Figure 1c,d an obvious step-flow growth pattern with consistent direction can be seen on the film surface. Besides, the film surface is smooth and uniform, and the root mean square (RMS) roughness is 0.95 nm. These characterizations indicate the high crystal quality of the films. Figure 2 shows the characterization of NiO films. Figure 2a,b shows the surface of NiO film grown on Ga 2 O 3 films. The NiO film has a dense surface with an RMS roughness of about 1.07 nm. The optical properties of NiO grown on the sapphire and Ga 2 O 3 wafers were characterized by transmittance spectroscopy, as shown in Figure 2c. All the films exhibited a high transmittance rate (>80%) in the energy range of 1.5-3.5 eV. Figure 2d is the Tauc plot. The band gaps of Ga 2 O 3 and NiO were obtained by linear extrapolation to be 4.75 eV and 3.54 eV, respectively. Besides, by Hall measurement at room temperature, the NiO film exhibited a resistivity of 5.0 Ω·cm with a hole concentration and mobility of 5 × 10 18 cm −3 and 0.47 cm 2 /V·s, respectively.  Figure 2 shows the characterization of NiO films. Figure 2a,b shows the surface of NiO film grown on Ga2O3 films. The NiO film has a dense surface with an RMS roughness of about 1.07 nm. The optical properties of NiO grown on the sapphire and Ga2O3 wafers were characterized by transmittance spectroscopy, as shown in Figure 2c. All the films exhibited a high transmittance rate (>80%) in the energy range of 1.5-3.5 eV. Figure 2d is the Tauc plot. The band gaps of Ga2O3 and NiO were obtained by linear extrapolation to be 4.75 eV and 3.54 eV, respectively. Besides, by Hall measurement at room temperature, the NiO film exhibited a resistivity of 5.0 Ω•cm with a hole concentration and mobility of 5 × 10 18 cm −3 and 0.47 cm 2 /V•s, respectively. To investigate the impurity contamination on the film surface and the distribution of unintentional doping elements, the SIMS was performed on N, H, and O, as shown in Figure 3. It can be found that the content of C and H is relatively high on the film surface. H is present only in the depth range of ~20 nm on the surface, while the penetration depth of C and N is ~0.2 μm. Since the content of all three elements decays rapidly to the detection limit after 0.2 μm away from the film surface, it can be inferred that the impurity elements originate from the adsorption of impurities in the environment and contamination. However, surface impurities will significantly change the surface state of the film, including interface state density, charge accumulation, and surface barrier, thereby affecting the performance of the device [19]. Therefore, the exposure time to air needs to be To investigate the impurity contamination on the film surface and the distribution of unintentional doping elements, the SIMS was performed on N, H, and O, as shown in Figure 3. It can be found that the content of C and H is relatively high on the film surface. H is present only in the depth range of~20 nm on the surface, while the penetration depth of C and N is~0.2 µm. Since the content of all three elements decays rapidly to the detection limit after 0.2 µm away from the film surface, it can be inferred that the impurity elements originate from the adsorption of impurities in the environment and contamination. However, surface impurities will significantly change the surface state of the film, including interface state density, charge accumulation, and surface barrier, thereby Figure 3. It can be found that the content of C and H is relatively high on the film surface. H is present only in the depth range of ~20 nm on the surface, while the penetration depth of C and N is ~0.2 μm. Since the content of all three elements decays rapidly to the detection limit after 0.2 μm away from the film surface, it can be inferred that the impurity elements originate from the adsorption of impurities in the environment and contamination. However, surface impurities will significantly change the surface state of the film, including interface state density, charge accumulation, and surface barrier, thereby affecting the performance of the device [19]. Therefore, the exposure time to air needs to be minimized to reduce the adsorption of impurities.  The electron concentration of the Ga 2 O 3 drift layer was characterized by the capacitancevoltage (C-V) measurement at room temperature under 500 kHz due to the conductive substrate. The plot of electron concentration with depth is shown in Figure 4. It can be seen intuitively that the values of N d -N a are all stable at around 3.5 × 10 16 cm −3 at different depths, which indicates the superiority of MOCVD in doping accuracy. The C-V relationship is shown in the inset. In the voltage range of 0 V to −5 V, the depletion layer ranges from 200 nm to 450 nm and is not completely depleted [32]. In addition, the MOCVD-grown Ga 2 O 3 films with this electron concentration value have an electron mobility of~140 cm 2 /V·s, according to our prior work [33]. The electron concentration of the Ga2O3 drift layer was characterized by the capacitance-voltage (C-V) measurement at room temperature under 500 kHz due to the conductive substrate. The plot of electron concentration with depth is shown in Figure 4. It can be seen intuitively that the values of Nd-Na are all stable at around 3.5 × 10 16 cm −3 at different depths, which indicates the superiority of MOCVD in doping accuracy. The C-V relationship is shown in the inset. In the voltage range of 0 V to −5 V, the depletion layer ranges from 200 nm to 450 nm and is not completely depleted [32]. In addition, the MOCVD-grown Ga2O3 films with this electron concentration value have an electron mobility of ~140 cm 2 /V•s, according to our prior work [33].    Figure 5 shows the structure and the forward characteristic of the devices. From Figure 5b, the turn-on voltages (V on ) of SBD and HJD are about 1.0 V and 2.0 V, respectively. The R on, sp of the SBD and HJD are 3.0 mΩ·cm 2 and 6.2 mΩ·cm 2 , obtained by the derivative of the curve. Higher electron concentration and lower drift layer thickness enable the device to achieve low R on, sp . From the logarithmic scale forward characteristic curve in Figure 5c, both SBD and HJD exhibit a current on/off ratio of more than 10 10 at 3 V. Besides, the ideality factor and subthreshold swing (SS) of a diode can be calculated according to the following relationship:

Devices Measurement
where J represents the current density, k is the Boltzmann constant, and n is the ideality factor [34]. The ideality factor and SS are shown in Figure 5d. In the near-linear barriercontrolled region, the ideality factor of SBD can be maintained at about 1.1~1.2, suggesting a dominant thermionic emission model [35]. In contrast, the ideality factor of HJD is stably maintained around 1.7, which has been reported to be related to interface recombination caused by large lattice mismatch [36,37]. The minimum SS of SBD and HJD fluctuate, ranging from~63 mV to~90 mV, respectively. A current change of 6 orders of magnitude can be achieved before the SS increases to 200 mV, which indicates a low density of trap states at the interface. In addition, the average SS of SBD is significantly lower than that of HJD, indicating a faster switching speed.  Through the one-dimensional Poisson equation and the assumption of the planar junction, the SBD and HJD depletion width is calculated to be 3.4 μm and 4.8 μm when the BVs are applied. Since 3.4 μm and 4.8 μm are smaller than the drift layer thickness, this indicates that the devices are non-punch-through, mainly caused by the higher electron concentration of the film and electric field crowding at the anode edge. Furthermore, since the film surface is exposed to air for a long time and has not been treated, the adsorption of impurities can also cause an increase in devices leakage current. Etching away the Ga2O3 film with a thickness of ~200 nm from the surface by dry etching and then repairing the surface damage will greatly improve the ideality factors and BVs of the devices [19].  Through the one-dimensional Poisson equation and the assumption of the planar junction, the SBD and HJD depletion width is calculated to be 3.4 µm and 4.8 µm when the BVs are applied. Since 3.4 µm and 4.8 µm are smaller than the drift layer thickness, this indicates that the devices are non-punch-through, mainly caused by the higher electron concentration of the film and electric field crowding at the anode edge. Furthermore, since the film surface is exposed to air for a long time and has not been treated, the adsorption of impurities can also cause an increase in devices leakage current. Etching away the Ga 2 O 3 film with a thickness of~200 nm from the surface by dry etching and then repairing the surface damage will greatly improve the ideality factors and BVs of the devices [19].
indicates that the devices are non-punch-through, mainly caused by the higher electron concentration of the film and electric field crowding at the anode edge. Furthermore, since the film surface is exposed to air for a long time and has not been treated, the adsorption of impurities can also cause an increase in devices leakage current. Etching away the Ga2O3 film with a thickness of ~200 nm from the surface by dry etching and then repairing the surface damage will greatly improve the ideality factors and BVs of the devices [19]. The benchmark relationship between Ga2O3 BV and Ron, sp is shown in Figure 7, which also lists the prior reports on three types of different devices, including SBDs, HJDs, and heterojunction barrier Schottky diodes (HJBSDs) fabricated by different growth methods. The benchmark relationship between Ga 2 O 3 BV and R on, sp is shown in Figure 7, which also lists the prior reports on three types of different devices, including SBDs, HJDs, and heterojunction barrier Schottky diodes (HJBSDs) fabricated by different growth methods. From the figure, although there are few vertical power diodes based on MOCVD, according to existing research, the performance of diodes from MOCVD has achieved higher P-FOM with thinner thickness [18]. In this work, the diodes have lower BVs due to a larger leakage current caused by a high electric field. Therefore, by appropriately increasing drift layers thickness, reducing the electron concentration, and adding edge terminations or surface electric field management structures, the performance of the device will be further improved. This shows the promise of MOCVD in Ga 2 O 3 power devices. From the figure, although there are few vertical power diodes based on MOCVD, according to existing research, the performance of diodes from MOCVD has achieved higher P-FOM with thinner thickness [18]. In this work, the diodes have lower BVs due to a larger leakage current caused by a high electric field. Therefore, by appropriately increasing drift layers thickness, reducing the electron concentration, and adding edge terminations or surface electric field management structures, the performance of the device will be further improved. This shows the promise of MOCVD in Ga2O3 power devices. Figure 7. Plot of the specific on-resistance and breakdown voltage for reported Ga2O3 power diodes [4,5,18,19,23,[37][38][39][40][41][42][43][44][45].

Discussion
The homoepitaxy of n-Ga2O3 films on (001) substrate was achieved. Various characterizations demonstrated the films' high crystal quality and stable electrical properties. On this basis, Ga2O3 SBD and HJD were fabricated and measured. In terms of the forward characteristics, the Ron, sp of SBD is 3.0 mΩ•cm 2 , which is smaller than that of HJD. Besides, HJD exhibits a large ideal factor because of the complex current transport mechanisms caused by the lattice mismatch and the adsorption of impurities at the interface. In terms of reverse characteristics, the BVs of the SBD and HJD are 380 V and 740 V, respectively, which indicates that HJD has significantly better blocking characteristics than SBD. The P-FOM of the SBD and HJD are 48 MW•cm −2 and 88 MW•cm −2 , comparable to reported SBD and HJD with the same structure. However, the high electric field at the anode edge

Discussion
The homoepitaxy of n-Ga 2 O 3 films on (001) substrate was achieved. Various characterizations demonstrated the films' high crystal quality and stable electrical properties. On this basis, Ga 2 O 3 SBD and HJD were fabricated and measured. In terms of the forward characteristics, the R on, sp of SBD is 3.0 mΩ·cm 2 , which is smaller than that of HJD. Besides, HJD exhibits a large ideal factor because of the complex current transport mechanisms caused by the lattice mismatch and the adsorption of impurities at the interface. In terms of reverse characteristics, the BVs of the SBD and HJD are 380 V and 740 V, respectively, which indicates that HJD has significantly better blocking characteristics than SBD. The P-FOM of the SBD and HJD are 48 MW·cm −2 and 88 MW·cm −2 , comparable to reported SBD and HJD with the same structure. However, the high electric field at the anode edge will result in large leakage currents at high reverse bias voltages. Therefore, appropriate edge termination or electric field management structures, such as implanted edge termination, field plates, field limiting rings, etc., will increase device BV further.

Conclusions
SBD and HJD based on high-quality homoepitaxial Ga 2 O 3 films from MOCVD were reported. Without any electric field management structure, the SBD achieves a R on, sp of 3.0 mΩ·cm 2 and a BV of 380 V, compared to 6.2 mΩ·cm 2 and 740 V for the HJD. Due to the relatively high electron concentration of the film and the electric field concentration effect at the anode edge of the devices, the devices are non-punch-through. Therefore, appropriately reducing the electron concentration of the films while the field management structure or punch-through design is the next research direction.

Data Availability Statement:
The data presented in this study are available on request from the corresponding authors.

Conflicts of Interest:
The authors declare no conflict of interest.