{'fraction_non_alphanumeric': 0.027106658809664112, 'fraction_numerical': 0.008249852681202121, 'mean_word_length': 5.530769230769231, 'pattern_counts': {'":': 0, '<': 0, '<?xml version=': 0, '>': 0, 'https://': 0, 'lorem ipsum': 0, 'www.': 0, 'xml': 0}, 'pii_count': 0, 'substrings_counts': 0, 'word_list_counts': {'cursed_substrings.json': 0, 'profanity_word_list.json': 0, 'sexual_word_list.json': 0, 'zh_pornsignals.json': 0}}
Improved adhesion between nickel–titanium SMA and polymer matrix via acid treatment and nano-silica particles coating

Shape memory alloy (SMA) composites are the desirable candidate for smart materials that used in intelligent structures. However, the overall mechanical performance of SMA composites depends immensely on the quality of the interaction between SMA and polymer matrix. Therefore, it is necessary to find out an approach to enhance the interfacial property of this composite. In this paper, we modified nickel–titanium SMA wire with nano-silica particles before and after acid treatment. The modification effect on the interfacial strength between SMA and epoxy resin was evaluated. Contact angle analysis, scanning electron microscopy (SEM) observation, and single fiber pull-out test were carried out. The bonding characteristics between modified wire and liquid/cured resin were investigated. We then embedded SMA wire into woven glass fabric/epoxy composite laminates, and manufactured this hybrid composites via vacuum assisted resin transfer molding processing. Three-point-bending test of the hybrid composites was performed to validate the modification effect. Fiber pull-out experiment demonstrates that the interfacial shear strength increases by 6.48% by nano-silica particles coating, while it increases by 52.21% after 8 h acid treatment and nano-silica particles coating simultaneously. For hybrid composites, flexural strength of the two specimens increases by 19.8 and 48.2%, respectively. In SEM observation, we observed large debonding region in unmodified composites, while interfacial adhesion between modified wire and epoxy keeps strong after flexural damage.