{'fraction_non_alphanumeric': 0.07399103139013453, 'fraction_numerical': 0.05661434977578475, 'mean_word_length': 4.204081632653061, 'pattern_counts': {'":': 0, '<': 5, '<?xml version=': 0, '>': 0, 'https://': 0, 'lorem ipsum': 0, 'www.': 0, 'xml': 0}, 'pii_count': 0, 'substrings_counts': 0, 'word_list_counts': {'cursed_substrings.json': 0, 'profanity_word_list.json': 0, 'sexual_word_list.json': 0, 'zh_pornsignals.json': 0}}
Change in Color and Gloss Parameters of Stained Monolithic Resin-Ceramic CAD/CAM Materials After Simulated Aging: An In Vitro Study.

PURPOSE
To measure the effect of simulated aging on stained resin-ceramic CAD/CAM materials regarding the durability of color and gloss.


MATERIALS AND METHODS
Test specimens (n = 15 per material) were prepared out of CAD/CAM ingots from two resin nanoceramics (Lava Ultimate [LVU], Cerasmart [CER]) and a polymer-infiltrated ceramic (ENA, VITA Enamic) stained with the manufacturer's recommended staining kit using photopolymerization. Control specimens were made of feldspathic ceramic (VITA Mark II [VM2]) and stained by means of ceramic firing. Negative control specimens (n = 15) (no staining) were prepared for each group. Color and gloss measurements were performed before and after each aging cycle by means of mechanical abrasion with a toothbrush. Groups were compared using Kruskal-Wallis test and paired post hoc Conover test. Changes within a group were calculated using Wilcoxon signed-rank test (α = .05).


RESULTS
The color difference (ΔE) was statistically significant for all stained CAD/CAM materials after simulated aging: CER (P < .001, 95% CI: 2.96 to 3.69), LVU (P = .004, 95% CI: 1.09 to 1.46), ENA (P = .004, 95% CI: 0.20 to 0.42), and VM2 (P < .001, 95% CI: 0.29 to 1.08). Aging resulted in a statistically significant increase in gloss in the LVU group (P < 0.001, 95% CI: 13.78 to 17.29), whereas in the ENA (P < .001, 95% CI: 7.83 to 12.72), CER (P < .001, 95% CI: 2.69 to 8.44), and VM2 (P = .014, 95% CI: 0.22 to 1.87) groups, a significant decrease in gloss was noted.


CONCLUSION
Color and gloss of stained resin-ceramic CAD/CAM materials changed significantly after aging by means of toothbrush abrasion in vitro.