{'fraction_non_alphanumeric': 0.0334855403348554, 'fraction_numerical': 0.0030441400304414, 'mean_word_length': 5.266666666666667, 'pattern_counts': {'":': 0, '<': 0, '<?xml version=': 0, '>': 0, 'https://': 0, 'lorem ipsum': 0, 'www.': 0, 'xml': 0}, 'pii_count': 0, 'substrings_counts': 0, 'word_list_counts': {'cursed_substrings.json': 0, 'profanity_word_list.json': 0, 'sexual_word_list.json': 0, 'zh_pornsignals.json': 0}}
Mg doping affects dislocation core structures in GaN.

Aberration-corrected scanning transmission electron microscopy was used to investigate the core structures of threading dislocations in undoped GaN films with both high and low dislocation densities, and in a comparable high dislocation density Mg-doped GaN film. All a-type dislocations in all samples have a 5/7-atom core structure. In contrast, most (a+c)-type dislocations in undoped GaN dissociate due to local strain variations from nearby dislocations. In contrast, Mg doping prevents (a+c)-type dislocation dissociation. Our data indicate that Mg affects dislocation cores in GaN significantly.