{'fraction_non_alphanumeric': 0.03329065300896287, 'fraction_numerical': 0.020486555697823303, 'mean_word_length': 5.409836065573771, 'pattern_counts': {'":': 0, '<': 0, '<?xml version=': 0, '>': 0, 'https://': 0, 'lorem ipsum': 0, 'www.': 0, 'xml': 0}, 'pii_count': 0, 'substrings_counts': 0, 'word_list_counts': {'cursed_substrings.json': 0, 'profanity_word_list.json': 0, 'sexual_word_list.json': 0, 'zh_pornsignals.json': 0}}
Electro-elastic moduli and frequency dependence of KN single crystal

Functional properties of KNbO3 single crystal are characterized. Large polydomain plates cutted from an as-grown KNbO3 crystal (oriented along [001]c (45°-cut) direction) are used. At the fundamental resonance (10 MHz), thickness coupling factor is 65% and frequency dependence is measured with overtone resonances. Its variation is relatively high and reduces to around 45% at 160 MHz. Electro-elastic moduli are also determined by mixing measured parameters (from thickness and lateral modes) and constants already published as initial data. Final constants are obtained by a minimization process to tend toward a self-consistent electro-elastic moduli which is an important condition for numerical modelling.