{'fraction_non_alphanumeric': 0.037516170763260026, 'fraction_numerical': 0.03234152652005175, 'mean_word_length': 5.2926829268292686, 'pattern_counts': {'":': 0, '<': 0, '<?xml version=': 0, '>': 0, 'https://': 0, 'lorem ipsum': 0, 'www.': 0, 'xml': 0}, 'pii_count': 0, 'substrings_counts': 0, 'word_list_counts': {'cursed_substrings.json': 0, 'profanity_word_list.json': 0, 'sexual_word_list.json': 0, 'zh_pornsignals.json': 0}}
Dielectric and Ferroelectric Response of Multiphase Bi‐Fe‐O Ceramics

The structural, dielectric, and ferroelectric characterization of multiphase Bi‐Fe‐O prepared with an excess of Bi up to 20% is reported. It is found that the dominant phase in all samples is the BiFeO3 perovskite in addition to an increasing amount of the Bi‐rich sillenite phases (Bi12.5Fe0.5O19.48/Bi25FeO39) with the Bi excess content. At room temperature, the multiphase Bi‐Fe‐O results in advanced electrical properties, with higher dielectric constant (161 at 1 MHz) and low losses (tanδ = 0.032 at 1 MHz). The ferroelectric character of multiphase ceramics is confirmed by PUND measurements, which shows increased polarization values and coercive field with respect to the single phase ceramics.