{'fraction_non_alphanumeric': 0.042226397369657116, 'fraction_numerical': 0.028088304368248003, 'mean_word_length': 4.573560209424084, 'pattern_counts': {'":': 0, '<': 0, '<?xml version=': 0, '>': 0, 'https://': 0, 'lorem ipsum': 0, 'www.': 0, 'xml': 0}, 'pii_count': 0, 'substrings_counts': 0, 'word_list_counts': {'cursed_substrings.json': 1, 'profanity_word_list.json': 0, 'sexual_word_list.json': 0, 'zh_pornsignals.json': 0}}
Selective surface modification in bimodal mesoporous CMK-5 carbon

Ordered, bimodal mesoporous CMK-5 carbon is prepared by using mesoporous SBA-15 silica as a structural mold. The carbon material is chemically modified by oxidative treatment with acidic persulfate solution. This leads to the creation of oxygen-containing functionalities at the pore walls of the carbon (up to 13 wt% oxygen), as confirmed by IR spectroscopy. The oxidative treatment is carried out before removal of the silica mold which ensures that only one of the two distinct modes of mesopores (namely, the intra-tubular pores) is affected; the other mode (inter-tubular pores) is protected from oxidation by the presence of the silica mold. This is proven by water vapor physisorption analysis. The oxidatively treated (intra-tubular) pores are significantly more polar and, hence, better wettable than the untreated (inter-tubular) pores.


Introduction
Ordered mesoporous carbon materials with regular pore architectures and uniform pore sizes are frequently prepared by the structure replication (nanocasting) method, 1-4 using mesoporous silica as structural molds. 5,6 The carbon material is created inside the pores of the silica (e.g. by carbonization of sucrose or furfuryl alcohol). If the entire pore volume of the silica matrix is lled with carbon, then subsequent removal of the silica by chemical etching (using NaOH or HF solution) will yield an exact carbon 'replica' of the original silica pore system. For example, SBA-15 silica 7 with its 2D hexagonal array of linear, cylindrical mesopores will yield mesoporous CMK-3 carbon, 8 which basically consists of carbon rods in a 2D hexagonal parallel arrangement. By varying the synthesis parameters it is possible to not completely ll the pores of the silica matrix with carbon, but to create only a layer of carbon at the pore walls; the center of the cylindrical pores remains hollow. Aer removal of the silica matrix the resulting carbon material, frequently termed CMK-5, 9,10 then consists of cylindrical rods that are hollow ('tubes'), therefore constituting two distinct types of mesopores: (i) inter-tubular pores (between adjacent rods; these pores are present in both CMK-3 and CMK-5) and (ii) intratubular pores (i.e., the hollow interior of the rods; this type of pores is missing in CMK-3).
In general, nanoporous carbon phases are promising materials for numerable applications, including in batteries, [11][12][13] as capacitors, 14,15 as sorbents for biomolecules, 16,17 in chromatography, 18,19 wastewater cleaning, 20,21 and catalysis. [22][23][24] For the latter, porous carbon may serve as a support material for catalytically active species or carry organic functionalities covalently attached to the carbon framework. CMK-5 carbon, with its above-described bimodal mesoporosity, offers particular chances, since the two distinct pore modes can be addressed separately and independently, which opens up an opportunity to create materials with dual functionality. During the synthesis of CMK-5 the intra-tubular pores are formed upon carbonization of the precursor compound (furfuryl alcohol) within the silica mold. At this stage, the inter-tubular pores are still blocked by the silica matrix; they become accessible only aer the removal of silica by chemical etching. This means that the intra-tubular pores can be modied selectively (before removal of silica) without affecting the inter-tubular pores (Scheme 1). 25,26 This concept offers new opportunities, for example in the eld of heterogeneous catalysis using bifunctional catalysts. Bifunctional catalysts combine two distinct types of catalytically active sites (guest species and/or functional groups) in one material, thereby facilitating fast and effective catalytic one-pot reactions. Recent reports include mesoporous silica and/or carbon materials containing combinations of various kinds of catalyst species in their mesopore channels. [27][28][29][30][31][32][33][34] Multiple functionalization is also interesting for phase-boundary catalysis, i.e. catalytic processes that involve reactants immiscible in the same solvent; 35 single-phase catalysts which exhibit polar and nonpolar surfaces at the same time have been shown to improve such processes. 36,37 For some catalytic reactions, however, it might be advantageous to immobilize the two active species in distinct pore systems of the same material, for example in order to prevent them from inactivating each other. 38,39 This latter option is available with bimodal mesoporous CMK-5 carbon, as described above.
Here we present a straightforward method to functionalize the intra-tubular pores of CMK-5 carbon selectively without affecting the inter-tubular pore system. Acidic ammonium persulfate solution is used as an oxidation agent, selectively for the intra-tubular pores, while the inter-tubular pore system remains unchanged.

Results and discussion
Elemental carbon was created in the cylindrical pores of mesoporous SBA-15 silica by carbonizing furfuryl alcohol and oxalic acid as described in the Experimental section. The employed synthesis protocol leads to a coating of the pore walls with a homogeneous layer of carbon while the center of the pores remains hollow. 9 Aer selective removal of the silica by etching with HF solution a mesoporous carbon material results which is frequently referred to as CMK-5. 10 As mentioned in the Introduction, mesoporous CMK-5 is a particularly interesting material as it exhibits two distinct types (modes) of mesopores. It can be described as a regular array of hollow, tubular 'nanorods': (i) the voids between adjacent rods constitute one mode of mesopores; they originate from the removal of the silica matrix (and they also exist in other types of mesoporous carbon materials prepared by nanocasting, such as CMK-3). In the following, we will refer to this type of mesopores as 'inter-tubular pores'. (ii) In addition, since the rods in CMK-5 are hollow, a second mode of mesoporosity results, in the following denoted as 'intra-tubular pores'. These intra-tubular pores are unique in CMK-5; they already exist before removal of the SBA-15 silica matrix, i.e. in the CMK-5@SBA-15 composite material right aer carbonization. Hence, the intra-tubular carbon pores can be modied (e.g. lled with guest species or functionalized at the pore walls) independently before the removal of the silica matrix (see Scheme 1), as will be shown in the following.
We have subjected the CMK-5@SBA-15 carbon/silica composite to oxidative treatment by dispersing the material in a persulfate solution and stirring at room temperature for a dened duration between 1 h and 10 h. The oxidative treatment does not affect the long-range structural order of the nal CMK-5 carbon materials, as conrmed by powder X-ray diffraction (see ESI section, Fig. S1 †). This is worth noticing, since treatment under harsher oxidative conditions has previously been observed to compromise the structural integrity of mesoporous CMK-3 or CMK-5 carbon. [40][41][42] FT-IR spectra of the (silica-free) CMK-5 carbon samples treated for 0 h, 1 h, 6 h, and 10 h, respectively, are shown in Fig. 1. For a semi-quantitative analysis the spectra were normalized with respect to the intensity of the band at ca. 1582 cm À1 (aromatic C-C ring stretching mode [43][44][45] ). The oxidative treatment results in the occurrence of a band at ca. 1730 cm À1 which increases in intensity upon longer treatment. This band can be attributed to the carbonyl C]O stretching mode in a keto or carboxyl function. [43][44][45] Likewise, a band at ca. 1220 cm À1 also appears upon oxidation; this corresponds presumably to a C-O stretching mode. 44,45 (The band at ca. 1150 cm À1 is assigned to a C-C stretching mode. [43][44][45] ) Hence, it can be concluded that the treatment with persulfate solution creates oxygen-containing polar surface functions (which, in turn, leads to an increase in hydrophilicity, as will be shown below). This is conrmed by elemental analysis. The initial oxygen content in the untreated CMK-5 carbon material is 3.8 wt%; the value gradually increases to 13.0 wt% aer 10 hours of oxidative treatment (see Table 1). It should be noted again that only the intra-tubular pores were modied, since the oxidative treatment was performed before the removal of the silica phase. The inter-tubular pores of CMK-5 carbon were not accessible to the persulfate solution at this stage. Fig. 2 (le) shows the N 2 physisorption isotherms of the (silica-free) CMK-5 samples that previously (i.e. before removal of the silica) underwent oxidative treatment for 0 h, 1 h, 6 h, and 10 h, respectively. All isotherms exhibit a shape of the IV(a) type, 46 indicating uniform mesopores. The BJH pore size distribution curves (Fig. 2, right) reveal an asymmetric peak between ca. 3.0 nm and 4.5 nm. This peak is attributable to both modes of mesopores, the inter-tubular pores with an average diameter of ca. 4.0 nm and the intra-tubular pores with an average diameter of ca. 3.5 nm. The two pore modes are not resolved in the pore size distribution curves, but the existence of the intra-tubular pores (3.5 nm) will be substantiated below (Fig. 4); they are responsible for the tailing of the asymmetric peak on the le-hand side. Oxidative treatment leads to a slight decrease of the specic pore volume to ca. 90% of its initial value (from 1.55 cm 3 g À1 to 1.39 cm 3 g À1 ); the BET surface area reduces to ca. 89% (from 1073 m 2 g À1 to 954 cm 2 g À1 ). The decrease in pore volume and BET surface area (both normalized to the sample mass) can be explained by the increase in sample mass as a consequence of the creation of oxygen-containing surface functions. The average pore sizes, however, do not change signicantly and the pore size distribution does not become any broader. These ndings conrm that the oxidative treatment does not affect the structural characteristics of the CMK-5 material. It should be noted that the samples exhibit micropores only to a very small extent, as commonly observed for mesoporous carbon prepared from furfuryl alcohol. 9,10 (Micropores contribute to the BET surface area by only 11 m 2 g À1 in the untreated sample and by 50 m 2 g À1 in the sample treated for 10 h.) Microporosity will therefore be neglected in the following.
Water vapor sorption analysis reveals more signicant differences between oxidatively treated and untreated CMK-5 samples than N 2 sorption analysis does. Fig. 3 shows the respective water sorption isotherms (20 C) for the same samples as in Fig. 2. All isotherms show a clear type-V behavior, 46 as commonly observed for this kind of mesoporous carbon. 47 This isotherm shape is characterized by weak interaction between the sorbent (carbon) and the sorptive (H 2 O). Almost no adsorption occurs at low relative pressure and a steep incline due to pore lling takes place at relative pressures signicantly higher than those for N 2 sorption. Strong hysteresis is observed upon desorption which is attributed to different mechanisms of lling and emptying of the mesopores. Recent studies suggest that the mechanism of pore lling is marked by the formation of adsorbed water clusters. [47][48][49][50] For the CMK-5 carbon samples both the steep incline of the adsorption isotherm and the steep decline of the desorption isotherm occur at variable relative pressure, depending on the relative amount of polar surface functions resulting from oxidative treatment for variable duration. For non-functionalized CMK-5 carbon the mesopore lling occurs at ca. p/p 0 ¼ 0.83 (adsorption   isotherm) and the pore emptying takes place at ca. p/p 0 ¼ 0.76 (desorption isotherm). These values gradually shi towards lower relative pressures for the samples that underwent oxidative treatment for increasing duration. The material treated for 10 h shows pore lling and emptying at ca. p/p 0 ¼ 0.80 and p/p 0 ¼ 0.66, respectively. These data conrm that the pore surface polarity indeed depends on the oxidative treatment. Creating oxygen surface functions renders the pore walls more hydrophilic. In summary, the characterization of the silica-free CMK-5 carbon materials shows that the polar surface functions created by oxidative treatment increase the surface hydrophilicity. However, these surface functions only exist at the walls of the intra-tubular pores. The inter-tubular pore walls are untreated and, thus, hydrophobic. This is an example of a material with dual functionality; the mesoporous carbon materials combine hydrophobic pores with pores that are rather hydrophilic.
The effect of surface functionalization on the hydrophilicity must be expected to be more pronounced in the CMK-5@SBA-15 carbon/silica composite materials, i.e. before removal of the silica, because at this stage the inter-tubular pores are still blocked and, therefore, do not contribute to the overall hydrophobicity. Fig. 4 (le) shows the respective N 2 physisorption isotherms of all samples; the pore size distribution plots are shown in Fig. 4 (right). All samples show IV(a)-type isotherms, similar to the silica-free samples (Fig. 2), but with signicantly lower overall N 2 uptake, corresponding to a lower pore volume (see Table 1). The pore size distribution peak is centered at ca. 3.5 nm. This peak represents the intra-tubular pores; it was also present in Fig. 2b (silica-free CMK-5 carbon samples) where it was only weakly resolved (visible as a shoulder) from the peak corresponding to the inter-tubular pores. (A second, much weaker peak at a pore size of ca. 7.3 nm is also observed in all samples in Fig. 4b; it is absent in the silica-free samples, Fig. 2b, and originates most likely from residual mesopores in the SBA-15 silica matrix that are not lled with carbon.) Oxidative treatment leads to a decrease of the specic pore volume to ca. 73% of its initial value (from 0.33 cm 3 g À1 to 0.24 cm 3 g À1 ); the BET surface area reduces to ca. 59% (from 273 m 2 g À1 to 160 cm 2 g À1 ). The average pore size, however, does not change signicantly and the pore size distribution does not become any broader. These ndings are in line with the respective data for the silica-free samples. The relative decrease in pore volume and BET surface area is more pronounced here because of the altogether lower initial values. Fig. 5 shows the water sorption isotherms for the same samples as in Fig. 4; the isotherms are of type V, similar as for the respective silica-free samples. As in case of N 2 sorption, the overall uptake of water is much lower than for the silica-free materials (Fig. 3), corresponding to a lower pore volume (see Table 1) owing to the absence of inter-tubular pores. As expected, the impact of oxidative treatment is much more visible in this series of samples than in case of the silica-free materials. For the pristine (i.e. non-treated) CMK-5@SBA-15 composite material the lling of the mesopores (adsorption isotherm) occurs in the region of p/p 0 ¼ 0.7-0.9. During desorption two distinct steps are observed. The rst step occurs at ca. p/p 0 ¼ 0.8-0.7; it is present in the same pressure range for all samples aer oxidative treatment and can be explained by the emptying of residual mesopores in the SBA-15 silica, not lled with carbon (as already observed by N 2 sorption analysis). The second step in the desorption isotherm occurs at ca. p/p 0 ¼ 0.56-0.43, corresponding to the emptying of the intra-tubular carbon pores. (This step was already present in the silica-free samples, but less obvious to the naked eye due to the larger scale in Fig. 3. This is shown in the ESI section in Fig. S2. † Interestingly, the step is weaker in the silica-free samples than in the silica-containing samples which cannot be explained in a straightforward way. Apparently, the emptying of the intra-tubular pores seems to be affected by the presence or absence of silica in the adjacent inter-tubular pores. This  phenomenon is currently subject to more elaborate analysis in our lab.) This step is shied signicantly towards lower relative pressure upon oxidative treatment for increasing amounts of time; aer treatment for 10 hours it occurs at p/p 0 ¼ 0.40-0.23. These ndings clearly show that the intra-tubular carbon surface is strongly affected by the oxidative treatment. The presence of oxygen surface functions (carbonyl and carboxyl groups) leads to strongly increased polarity; the carbon pore surface becomes more hydrophilic which explains why water is released from the intra-tubular pores during desorption at signicantly lower relative pressure. [47][48][49][50] The increase in hydrophilicity is supported by the fact that the quotient of the pore volume calculated from N 2 physisorption divided by the value from H 2 O sorption increases with increasing oxidative treatment (see ESI section, Table S1 †). This is attributed to the fact that water has a lower density in conned hydrophobic space compared to a hydrophilic surrounding. 47,51 Experimental Synthesis of SBA-15 silica SBA-15 silica was prepared by a modied literature procedure. 7 A P-123 stock solution was prepared by mixing Pluronic P-123 block co-polymer (167.0 g, Sigma-Aldrich) in water (833.0 g) and stirring overnight. The P-123 stock solution (96.0 g) was diluted with water (385 mL), acidied with hydrochloric acid (48 mL, Stockmeier, 37%), and stirred at 35 C for one hour. Tetraethyl orthosilicate (37.0 mL, ABCR, 99%) was added and the solution was stirred for 24 h at 35 C. The resulting sol was transferred into a glass-lined autoclave and hydrothermally treated at 140 C for 24 h. Aer cooling down to room temperature the product was ltered off, washed with deionized water and dried at 120 C overnight. Finally the powder was calcined in a tube furnace for 6 h with a heating ramp of 2.5 C min À1 at 550 C under owing air.

Synthesis of CMK-5@SBA-15 composite
A composite material of CMK-5 carbon within the pores of SBA-15 (CMK-5@SBA-15) was prepared by a modied literature procedure. 52 Oxalic acid dihydrate (180 mg, ABCR, 98%) was dissolved in furfuryl alcohol (20.0 mL, ABCR, 98%). This solution was mixed with SBA-15 silica to ll the silica pores with a theoretical loading of 130% of the pore volume (incipient wetness) by intensive grinding and subsequent thermal treatment at 60 C for 24 h and 90 C for 48 h in a drying cabinet. Carbonization was completed in a tube furnace at a temperature up to 850 C (heating to 150 C at 2 C min À1 and maintaining at 150 C for 3 h, further heating to 300 C at 1 C min À1 and to 850 C at 5 C min À1 and maintaining at 850 C for 4 h) under vacuum.
Oxidative treatment of the intra-tubular pores of CMK-5 2.30 g of the CMK-5@SBA-15 composite material was dispersed in 63 mL of an acidic solution of ammonium persulfate, (NH 4 ) 2 S 2 O 8 , and stirred for 1 h, 6 h or 10 h, respectively. The persulfate solution was prepared by mixing 33.5 mL concentrated sulfuric acid (96%, Stockmeier) with 300 mL water, followed by addition of (NH 4 ) 2 S 2 O 8 (119.8 g, ABCR, 98%) and further stirring for 10 minutes. The silica/carbon composite samples were denoted as CMK-5@SBA-15(X), where X represents the duration of previous persulfate treatment (in hours).

Removal of the silica matrix
The CMK-5@SBA-15(X) composite materials were treated in aqueous hydrouoric acid (12%, 100 mL, Sigma-Aldrich) for at least 16 h, and washed with deionized water. This procedure was repeated eight times to minimize the residual amount of silica. The silica-free carbon samples were denoted as CMK-5(X), where X represents the duration of previous persulfate treatment (in hours).
Characterization N 2 physisorption analysis was conducted with a Quantachrome Autosorb 6 apparatus. Samples were degassed at 120 C for 12 h. Pore size distributions were calculated by BJH model 53 from the desorption branch of the isotherms. The BET surface areas 54 were calculated in a pressure range of 0.1 # p/p 0 # 0.3. Microporosity was estimated by the t-plot method. Total pore volumes were derived from the second-to-last data point in the adsorption isotherm (ca. p/p 0 ¼ 0.99). Water vapor sorption was performed on a Micromeritics 3Flex apparatus at 20 C. Samples were degassed at 120 C for 12 h. X-ray diffraction was carried out on a Bruker AXS D8 Advance diffractometer with Cu K a radiation (40 kV, 40 mA) with a step size of 2q ¼ 0.0075 and a counting time of 3 s per step. FT-IR spectra were measured on a Bruker Vertex 70 in transmission mode (KBr matrix). Elemental analysis was carried out with an Elementar vario MicroCube.

Conclusions
Bimodal mesoporous CMK-5 carbon was modied by oxidative treatment selectively by temporary blocking of one of the two pore modes. Our data demonstrate that water vapor physisorption analysis provides a versatile method of distinguishing the two distinct modes of mesopores in CMK-5 carbon aer selective modication of pore mode. The pore surface polarity serves as a probe for the increasing quantity of oxygen-containing functionalities formed by oxidative treatment for increased duration. Aer 10 hours of treatment the carbon contains 13.0 wt% oxygen while untreated CMK-5 carbon contains only 3.8 wt% oxygen.