{'fraction_non_alphanumeric': 0.029817444219066937, 'fraction_numerical': 0.021866125760649086, 'mean_word_length': 4.901604022025377, 'pattern_counts': {'":': 0, '<': 1, '<?xml version=': 0, '>': 0, 'https://': 0, 'lorem ipsum': 0, 'www.': 0, 'xml': 0}, 'pii_count': 0, 'substrings_counts': 0, 'word_list_counts': {'cursed_substrings.json': 0, 'profanity_word_list.json': 0, 'sexual_word_list.json': 0, 'zh_pornsignals.json': 0}}
Phytic acid as alternative setting retarder enhanced biological performance of dicalcium phosphate cement in vitro

Dicalcium phosphate cement preparation requires the addition of setting retarders to meet clinical requirements regarding handling time and processability. Previous studies have focused on the influence of different setting modifiers on material properties such as mechanical performance or injectability, while ignoring their influence on biological cement properties as they are used in low concentrations in the cement pastes and the occurrence of most compounds in human tissues. Here, analyses of both material and biological behavior were carried out on samples with common setting retardants (citric acid, sodium pyrophosphate, sulfuric acid) and novel (phytic acid). Cytocompatibility was evaluated by in vitro tests with osteoblastic (hFOB 1.19) and osteoclastic (RAW 264.7) cells. We found cytocompatibility was better for sodium pyrophosphate and phytic acid with a three-fold cell metabolic activity by WST-1 test, whereas samples set with citric acid showed reduced cell number as well as cell activity. The compressive strength (CS) of cements formed with phytic acid (CS = 13 MPa) were nearly equal to those formed with citric acid (CS = 15 MPa) and approximately threefold higher than for other setting retardants. Due to a proven cytocompatibility and high mechanical strength, phytic acid seems to be a candidate replacement setting retardant for dicalcium phosphate cements.

A couple of studies have demonstrated the bone remodelling capacity of brushite forming cements in various animal models within a time period of 16-18 weeks 20,21 , whereas other studies have indicated a phase conversion of brushite into lower soluble octacalcium phosphate or hydroxyapatite in vivo 22 , which slows down degradation compared to monetite.
Since the crystallization rate of brushite crystals is approximately three orders of magnitude higher than those for hydroxyapatite 23 , setting retarders have to be used in these cements to adjust clinically appropriate setting times of 3-5 min. Most commonly applied setting retarders for brushite cements are citric acid 24,25 , pyrophosphate ions 24,26 , sulfate ions 27 or magnesium ions 28,29 . Among those, citric acid was shown to result in superior physical properties such as mechanical strength, setting time and injectability 30,31 . Although all of these retarders were compounds naturally occurring in tissues 32 , the biological properties of brushite cements were recently demonstrated to be influenced by these additives. Jamshidi et al. showed that the cell attachment to brushite cements is mostly inhibited by using citric acid as retarder 33 . This was attributed to the formation of an amorphous dicalcium citrate phase during setting, which slowly dissolved afterwards in the culture medium during cell experiments. Another study by Kanter et al. 17 revealed that citric acid may also influence the degradation rate of brushite cement in vivo. Even those cement samples, which were not converted into lower solubility octacalcium phosphate remained mostly stable during 10 months of orthotopic implantation, either because the calcium citrate complexes formed in the cement decreased the chemical solubility of the cement matrix or they decreased the metabolic activity of bone resorbing osteoclasts near the implant.
This study aimed to investigate this observation in more detail to identify the effect of different setting retarders on both basic properties of cements as well as on their influence on the cytocompatibility against bone forming and degrading cells. Several possible alternatives to citric acid as setting retarder in brushite cements such as sodium pyrophosphate, sulfuric acid and phytic acid were investigated and compared with citric acid and cements without any setting retardant. Apart from analyzing the influence of these additives on the physico-chemical cement properties such as initial setting time, compressive strength and the exothermic setting reaction, biological investigations concerning cytocompatibility were carried out with a human osteoblastic cell line (hFOB 1.19) and a murine macrophage cell line (RAW 264.7) differentiating into osteoclasts.

Results
Cell proliferation of the osteoblastic cell line hFOB1.19 over a period of 10 days on the surface of set cements revealed cell numbers in the range of the control (cement with no retarding additive, set as 100% at day 4) or above and only those made with citric acid and sulfuric acid as retarder had a large decrease to approx. 27-45% in cell number after 10 days (Fig. 1A). Additionally, cell proliferation assayed by WST-test (Fig. 1B) showed lower cell activity for samples containing citric acid or sulfuric acid compared to the reference without setting retardant. However, more than three-times higher metabolic activity per cell could be reached by the use of sodium pyrophosphate or phytic acid (Fig. 1C). Additionally, cements were seeded with the macrophage cell line RAW 264.7, which were differentiated into osteoclasts after addition of 50 ng/mL RANKL. Surprisingly, cement surfaces prepared with citric acid as setting retardant fully inhibited osteoclast growth during the whole course of the experiment ( Fig. 2A). The cell number of the other retarders was comparable to the reference and increased during culture of 21 days. Cell activity measured by WST-1 test is shown in Fig. 2B. Due to the lack of cells, samples with citric acid had no cell activity. Sulfuric acid had very low activity, which increased during culture period. Cements formed with sodium pyrophosphate and phytic acid were overwhelmingly comparable to the reference, even though the highest activity of the reference on day 21 could not be reached by any other composition (Fig. 2C).
Differentiation of RAW macrophages into multinucleated osteoclasts by addition of RANKL was verified by TRAP staining (Fig. 3). Samples without RANKL addition served as control and were cultured over 21 days resulting in no staining for any cement composition (data not shown). Cement surfaces prepared with citric acid or sulfuric acid as retarder showed hardly any staining and only at day 21, on both surfaces little TRAP staining could be detected. In contrast, cement surfaces prepared with sodium pyrophosphate or phytic acid retarder exhibited continuously increasing TRAP staining during the culture period which was at least comparable or even more than the reference. After 15-21 days, these surfaces were confluently grown with cells.
The solubility of the preset cements was tested using DMEM cell culture medium (Fig. 4) for up to 24 h. All cements showed an adsorption of magnesium ions (2.3-7.3 mg/l) from the medium and a high release of phosphate in the range of 71-89 mg/l. Strong differences were observed regarding calcium ions, where only cements formed with sodium pyrophosphate and phytic acid increased the Ca 2+ concentration of the medium (21-47 mg/l), whereas all other cements adsorbed calcium ions.
Regarding the influence of setting retardants on the mechanical cement properties (Fig. 5A), the highest compressive strength was found for samples set with citric acid (15 MPa) and phytic acid (13 MPa), with both being significantly higher than the reference. In contrast, the use of sodium pyrophosphate and sulfuric acid weakened the cement matrix and compressive strength was significantly lower compared to the reference without setting retardant. Initial setting time was evaluated by the Gillmore needle test (Fig. 5B) indicating a setting time of less than one minute in the absence of any retarder. While sodium pyrophosphate, sulfuric acid and phytic acid increased the setting time to approx. 3-4 min, citric acid had a much stronger influence as retarder and prolonged cement solidification to 5.5 min. Porosity of set cements (Fig. 5C) was found to be in the range 21-23% for the reference as well as citric acid/phytic acid retarder, whereas higher values (29-31%) were obtained for sodium pyrophosphate and sulfuric acid. Figure 6 shows the temperature evolution during cement setting over a period of 60 min and a dot marks the initial setting time measured with Gillmore needle test. As could be already seen at the Gillmore needle test, cement samples set without retardant had the earliest exothermic reaction and highest maximum temperature (45 °C). The maximum peak during setting reaction is shifted to later time points when retarders were employed and also the temperatures achieved during setting decreased by the addition of retarders below 37 °C.  (Fig. 7B), differing in terms of aspect ratio (two-dimensional) and three-dimensional expansion. While cements formed with sodium pyrophosphate and citric acid showed a predominantly needle like structure with a crystal size of 5-10 µm, sulfuric acid as well as phytic acid as retarders led to the formation of plate-like crystals of <5 µm size. A more compact morphology was observed in the absence of any retarder (Fig. 7B). The size distribution of the cement raw materials (Fig. 7D) was monomodal with a medium size of ß-TCP (9.4 µm) and MCPA (14.5 µm).
Phase analysis performed with XRD ( Fig. 7E) exhibited three different phases: brushite (b), the anhydride monetite (m) and the cement raw powder β-TCP (β). The second cement component MCPA was not found in crystalline form after setting. When phytic acid or sulfuric acid were used as retarders, monetite was the predominant phase formed during setting, whereas for all other retardants the formation of mixtures of both brushite and monetite was observed, even though there were residues of β-TCP in all compositions.

Discussion
Dicalcium phosphate crystals are formed during cement setting by a comparatively fast dissolution/precipitation process 5 . The reactants β-TCP and MCPA dissolve in the liquid phase, whereas brushite or monetite precipitates at a pH-value less than 4.2 5 . However, the setting time of dicalcium phosphate cements without any retardant of less than one minute is very short. An extension of the setting time to a clinically applicable time frame requires the use of setting retarders, such as pyrophosphates, sulfates or citrates 24 . These compounds delay the crystal growth rate of the setting product by adsorbing at the active growth sites of dicalcium phosphate crystal faces 34 , leading to both a longer setting time (Fig. 5B) and a decrease in the maximum setting temperature at later time points (Fig. 6B). Among these retarders, citric acid has been proven to simultaneously retard setting and attain excellent material properties such as high compressive strength 31 and good injectability 30 . This was confirmed in the present study demonstrating the highest cement strength and longest setting times compared with all other additives  ( Fig. 5). The only other compound leading to nearly similar cement characteristics was phytic acid, which is known to form Ca 2+ /Mg 2+ chelates with compounds such as α-tricalcium phosphate, ß-tricalcium phosphate or trimagnesium phosphate [35][36][37] and which acts as a regulator of brushite and hydroxyapatite crystal growth 38 .
Although for all cements a constant powder to liquid ratio was used, porosity as a strength determining parameter 39,40 was found to vary in the range from 21-31% (Fig. 5C). These porosity differences likely correlate with strength variation as those cements with the lowest porosity (citric acid, phytic acid, no retarder) had the highest strength, whereas the Ca 2+ chelating capacity of citric acid and phytic acid may have further contributed to the mechanical performance. In addition, the observed variation in brushite crystal morphology may be a regulating parameter for cement strength as it is also known for hydroxyapatite forming cements 41 . Examination of surface morphology of the different setting retardants via SEM revealed three types of crystal shapes. Plates and needles could be detected due to a non-centrosymmetric monoclinic crystallization structure as reported elsewhere 42,43 . Furthermore, paving stone like structures were found having a more compact structure with a lower aspect ratio compared to plates and needles. In most cases, the morphology of cement samples was a mixture of these three types since the complex kinetics influenced by numerous factors may play a decisive role in crystallization leading to a variety of crystal morphologies. In terms of the mechanical cement properties, the predominant needle like character of brushite crystals formed by the addition of citric acid are thought to result in a better entanglement of crystals compared to the compact morphology of brushite crystals without setting retarder (Fig. 7).
Despite of the excellent cement material properties, recent studies indicated a reduced cell attachment on cement surfaces 33 and a strongly delayed degradation in vivo 17 for citric acid modified brushite cements. Especially the latter is surprising, since the authors did not observe any phase changes during 10 months of orthotopic implantation for low porosity brushite cements. This anomalous behavior may have two reasons: firstly, the calcium citrate complexes formed in the cement may generally decrease the solubility of the cement and/or secondly, the calcium citrate complexes are not only affecting the proliferation/activity of osteoblasts but also those of bone resorbing osteoclasts. Regarding the cement solubility, cements formed with citric acid showed a similar dissolution behavior like cements with sulfuric acid or without setting retarder (Fig. 4). The release of phosphate in conjunction with the adsorption of Ca 2+ and Mg 2+ is related to the well know tendency of brushite cements to convert into calcium phosphate phases with a higher Ca: P ratio [44][45][46][47] . Surprisingly, sodium pyrophosphate and phytic acid behaved differently and expressed both Ca 2+ and phosphate ions. However, since the release was measured only at an early time point, an absence or a retarded phase transformation of brushite into lower soluble phases in a long term implantation regime is speculative.
The biological part of our study confirmed recent results of Jamshidi et al. 33 regarding the low cytocompatibility of brushite cements formed with citric acid retarder. The human fetal osteoblast cell line hFOB used here is likely more suitable for bone models than tumor derived MG63 exhibiting numerous karyotypic alterations 48 . Cell number of hFOB was measured via cell counting on day 4, 6 and 10 ( Fig. 1) showing that most cement samples were in the range of the retardant free reference with a slight tendency to higher cell numbers for sodium pyrophosphate modification. Citric acid, in contrast, had decreasing cell numbers, especially on day 10. Cell activity measurements confirmed the tendency suggested for cell number and activity on citric acid and sulfuric acid modified cements was even lower than for the reference tracing back to a reduced cell metabolism. In contrast, the addition of sodium pyrophosphate or phytic acid enhanced cell activity up to three times indicating a metabolism activating influence on osteoblasts.
Complementary to osteoblast cell tests, osteoclast precursor cells RAW264.7 were cultured on cement surfaces over 21 days (Fig. 2). This cell line is an established model to study bioceramic dissolution for both sintered hydroxyapatite or tricalcium phosphate ceramics 49 as well as for low temperature cements 50 . The effect of citric acid on osteoclasts was even more striking than for osteoblastic cells showing practically no cell growth or cell activity during the whole culture period. Sulfuric acid also showed very low cell number and cell activity in the first eleven days but increased until day 21. Sodium pyrophosphate and phytic acid were almost comparable to the reference and showed no inhibiting effect on osteoclast proliferation and activity. To prove differentiation of precursor cells into multinucleated osteoclasts by supplementation of RANKL to the medium, staining with TRAP was performed (Fig. 3). On surfaces with citric acid and sulfuric acid, no staining could be found which is in accordance with cell number and cell activity. In contrast, on samples with sodium pyrophosphate and phytic acid all cells differentiated within 15 days and stayed vital until day 21. The results clearly support the hypothesis that citric acid used as a retarder in brushite cements alters the degradation ability of the cement in vivo, most likely because of a cytotoxic effect on osteoclastic cells. However, brushite cements in the current study contained a relatively high concentration of citric acid (0.5 M), since this concentration provided the maximum effect on cement material properties. Previous experiments with other citrate modified cements were performed with 10 times lower concentrations of 0.05 M and showed medium activity of osteoclasts. This demonstrates that citrate ions are not generally cytotoxic for osteoclasts and hence this may open the possibility for further cement optimization regarding cytocompatibility and material properties. The mechanism by which citrate ions inhibit osteoclast formation and activity is however still unclear. A recent study by Drager et al. 51 has shown a strong effect of iron chelators on osteoclast function, as iron is needed for mitochondrial biogenesis during osteoclastic differentiation. Since citrate has also the capacity to form iron-chelates 52 , the formation of such complexes from dissolved calcium citrate from the cement might have provoked iron chelation with the observed inhibition of osteoclast formation. Although also phytic acid is a strong chelating agent for iron 53 , we assume, that the calcium-phytate complexes formed during cement setting are stable under in vitro neutral pH conditions as demonstrated by Gosselin et al. 54 and Grynspan et al. 55 in contrast to calcium citrate which dissolves in this environment 56 . It is then likely that for phytic acid as setting retarder, the free iron concentration is maintained within the cell culture (and hence osteoclast activity), which is not the case for citric acid retarder due to the solubility of calcium citrate.

Conclusion
An in vitro cytocompatibility test with both osteoblastic (hFOB1.19) and osteoclastic (RAW264.7) cell lines revealed a very low cell number and activity for citric acid as a common dicalcium phosphate cement setting retardant. To overcome this drawback, we analyzed the retarders sodium pyrophosphate, sulfuric acid and phytic acid, whereas the best in vitro performance was achieved with phytic acid with a high cell proliferation and cell activity. The mechanical properties were investigated with a compression test, showing that cements with sodium pyrophosphate (CS = 3.2 ± 0.7 MPa) and sulfuric acid (CS = 4.7 ± 1.2 MPa) were mechanically much weaker than cements formed with phytic acid (CS = 13.2 ± 1.9 MPa) or citric acid (CS = 15.0 ± 1.6 MPa). Altogether, phytic acid as a novel setting retardant for dicalcium phosphate cements seemed to be promising in terms of material properties as well as biological behavior. Nevertheless, further knowledge has to be gained by in vivo tests, since complex organisms always have a different behavior compared to mono-cultures.

Materials and Methods
Sample preparation. β-TCP was made of an equimolar mixture of CaHPO 4 and CaCO 3 (both Merck, Darmstadt, Germany) by sintering for 14 h at 1400 °C followed by 6 h at 1000 °C. Crushing with mortar and pestle followed by grinding for 10 min in a planetary ball mill (PM400, Retsch, Germany) resulted in a medium particle size of 9.4 µm. Monocalcium phosphate anhydrate (MCPA) was used as phosphate source. MCPA (LOT: MV3272, Budenheim) was mixed in a stoichiometric ratio of 0.755:1 with β-TCP within a coffee mill (Privileg, type: PCML2012, Quelle GmbH, Fürth, Germany). The setting retardants citric acid monohydrate (Sigma-Aldrich, LOT: SZBB2010V), sulfuric acid (Merck, LOT: 318 K19691813) and phytic acid (Sigma-Aldrich, LOT: BCBH8997V) were added to the liquid phase, whereas tetra-sodium pyrophosphate decahydrate (Merck, LOT: F1061091 139) was added to the powder. The concentrations were 0.5 mol/L citric acid (0.5 M ca), 5.4 wt% sodium pyrophosphate (5.4 wt% sp), 0.1 mol/L sulfuric acid (0.1 M sa) and 0.1 mol/L phytic acid (0.1 M pa). All samples had a powder to liquid ratio of 3 g/mL and were produced in silicon molds. Samples were set for 1 h at 37 °C and 100% humidity prior to testing.
Characterization. Particle sizes of raw powders were measured with a laser diffractometer (Horiba LA 300 Wet, Horiba, Japan) in ethanol. Characterization of the cement morphology was performed by cross beam scanning electron microscopy (SEM; CB 340, Zeiss, Germany) where the samples were sputtered with 4 nm platinum prior to imaging. The SEM operated at 3 kV with a 2000-fold magnification. For mechanical testing, cuboid samples of 6 mm × 6 mm × 12 mm (n = 12) were prepared and stored in water at 37 °C for 24 h. The mechanical testing device (Zwick GmbH & Co.KG, Ulm, Germany) was operated in compression mode with a 10 kN load cell at a testing speed of 1 mm/min. The solubility of preset cement samples was tested by immersion in 10 ml DMEM cell culture medium for 24 h at 37 °C. Ion concentrations in the immersion liquids were quantified by inductively coupled plasma mass spectrometry (ICP-MS; Varian, Darmstadt, Germany) against standard solutions of 5 and 10 mg/mL (Merck, Darmstadt, Germany). To measure the initial setting time, a Gillmore needle test was performed within a chamber at 37 °C and 100% humidity. Exothermic behavior of isolated samples of 1.5 g cement (n = 5) within 60 min was recorded by a thermometer (Data-Logger Thermometer 306, Conrad Electronic GmbH, Hirschau, Germany). Statistical analysis was calculated with ANOVA using the program SigmaPlot 12.5 (Systat Software, Inc., 2011). The porosity of the cement samples (6 mm × 6 mm × 12 mm) was measured according to Unosson et al. 57 , by solvent resaturation (n = 12). Therefore, the weight of water saturated samples was recorded followed by drying under vacuum at room temperature. The porosity Φ in percent was calculated according to Eq. (1), where m sat and m dry are the weight of saturated and dry samples, respectively, ρ w is the density of water and V is the apparent volume of the sample. . Cement samples (n = 4) and polystyrene plates serving as reference were placed in 24-well plates and seeded with a cell density on cement surfaces of 10 5 cells/ well and 5 · 10 4 cells/well on polystyrene. The seeded samples were incubated at 34 °C and 5% CO 2 and cell activity and cell number were evaluated at day 4, 6 and 10. Samples were incubated for 30 min with WST-1 reagent (dilution of 1:10) and the cell activity was measured twice with a spectrometer (Tecan SpectraFluor Plus, Tecan, Maennedorf, Switzerland). Cell number was evaluated by a cell counter (Casy, Roche innovates AG, Bielefeld, Germany) after detaching cells from the surface by 12 min incubation with Accutase (PAA, Cat. No.: L11-007). Cell counting was performed in isotonic liquid with a dilution of 1:100. Furthermore, cell tests with the murine macrophage cell line RAW 264.7 were performed to investigate the influence of retardant addition on activity of bone degrading cells. RAW cells were used up to passage 18 and were cultured in Dulbecco's Modified Eagle's Medium (DMEM; ATCC), supplemented with 1% Penicillin-Streptomycin (Gibco, Cat. No.: 15140-122) and 10% FCS (Gibco, Cat. No.: 10270-106). Therefore, samples (n = 4) with a diameter of 5 mm and a height of 2 mm were placed in 96-well plates, seeded with 6.4 · 10 3 cells/well and incubated at 37 °C and 5% CO 2 . After 24 h of culture medium was supplemented with 50 ng/mL receptor activator of the nuclear factor κB ligand (RANKL) to induce differentiation to multinucleated osteoclasts and culture medium was changed every 2-3 days. Osteoclast differentiation was evaluated by tartrate resistant acid phosphatase (TRAP) staining after 5, 11, 15 and 21 days by using a commercial TRAP-staining kit (Sigma, Cat. No. 387). Moreover, cell number of osteoclasts was determined using Auto T4 cell counter (Nexcellom Bioscience, Lawrence, Massachusetts, USA) after detaching cells from cement surface by incubation with Accutase (PAA, Cat. No.: L11-007) for 45 min. Similar to hFOB cell tests, activity of osteoclasts was measured by WST-1 reagent also over 21 days.