{'fraction_non_alphanumeric': 0.04212299915754002, 'fraction_numerical': 0.016849199663016005, 'mean_word_length': 5.6, 'pattern_counts': {'":': 0, '<': 0, '<?xml version=': 0, '>': 0, 'https://': 0, 'lorem ipsum': 0, 'www.': 0, 'xml': 0}, 'pii_count': 0, 'substrings_counts': 0, 'word_list_counts': {'cursed_substrings.json': 0, 'profanity_word_list.json': 0, 'sexual_word_list.json': 0, 'zh_pornsignals.json': 0}}
Effects of Valence States of Working Cations on the Electrochemical Performance of Sodium Vanadate.

Supercapacitors have received much attention as large-scale energy storage devices for high power density and ultralong cycling life. In this work, sodium vanadate Na0.76V6O15/poly(3,4-ethylenedioxythiophene) (PEDOT) nanocables with deficient bridge oxygen at the interface (denoted Vo••-PNVO) have been tailored for supercapacitors through the in situ polymerization of 3,4-ethylenedioxythiophene and studied using three different electrolytes. Experiments and theoretical calculations reveal that all Na+, Zn2+, and Al3+ ions appear as hydrates in aqueous solutions but insert into the crystal structure as Na+ ions and Zn2+-H2O and Al3+-H2O hydrates, respectively. In comparison with the Zn2+-H2O and Al3+-H2O hydrates, Na+ ions with a smaller radius diffuse more quickly in Vo••-PNVO. Thus, Vo••-PNVO delivers better charge storage capability and stability when an electrolyte with Na+ ions is used. The results strongly suggest that an electrostatic interaction is significant in determining transport properties and storage capacities, rather than hydrate radii or valence states.