{'fraction_non_alphanumeric': 0.015912897822445562, 'fraction_numerical': 0.0, 'mean_word_length': 5.096938775510204, 'pattern_counts': {'":': 0, '<': 0, '<?xml version=': 0, '>': 0, 'https://': 0, 'lorem ipsum': 0, 'www.': 0, 'xml': 0}, 'pii_count': 0, 'substrings_counts': 0, 'word_list_counts': {'cursed_substrings.json': 0, 'profanity_word_list.json': 0, 'sexual_word_list.json': 0, 'zh_pornsignals.json': 0}}
Analysis of Single Particle Attrition during Impact Experiments†

Particle breakage can be characterised as attrition, chipping, fracture, abrasion and wear. All these types of breakage mechanisms are the effect of the damage caused to these particles. These mechanisms can be differentiated not just on the basis of magnitude and direction of the force but also by the damage caused to the particles. The damage is measured by change in the size distribution and the change in shape of the particles. In the current research, experiments were performed on the newly developed Repeated Impact Test. The unique feature of this test is that about hundred particles can be subjected simultaneously to a monitored number of impacts, without particle‐particle interactions at regulated velocities. The preliminary experiments were performed with single crystalline particles of different shapes and sizes. After fixed number of impacts, the images of the particles were taken. The volume and shape of the particles were determined by image analysis. It was observed that the rate of attrition was very high when the particles are irregular. The rate decreased as the particles became more spherical.