{'fraction_non_alphanumeric': 0.030483271375464683, 'fraction_numerical': 0.013382899628252789, 'mean_word_length': 5.289719626168225, 'pattern_counts': {'":': 0, '<': 0, '<?xml version=': 0, '>': 0, 'https://': 0, 'lorem ipsum': 0, 'www.': 0, 'xml': 0}, 'pii_count': 0, 'substrings_counts': 0, 'word_list_counts': {'cursed_substrings.json': 0, 'profanity_word_list.json': 0, 'sexual_word_list.json': 0, 'zh_pornsignals.json': 0}}
Green synthesis and characterization of zero-valent iron nanoparticles using stinging nettle (Urtica dioica) leaf extract

Abstract For the first time, aqueous leaf extract of Urtica dioica was used as a sustainable source of reducing and capping agents to synthesize iron nanoparticles (INPs). In this regard, zero-valent INPs were produced and entrapped in a biologic coating. INPs were characterized by transmission electron microscopy (TEM), particle size analysis, Fourier transform infrared (FTIR) spectroscopy, X-ray diffractometer, vibrating sample magnetometer, thermogravimetric analysis (TGA), and differential TGA. Based on the results, the prepared INPs were completely composed of zero-valent iron atoms without any iron oxide impurities. Nanoparticles were spherical in shape with diameters ranging from 21 nm to 71 nm with a mean particle size of 46 nm. Particles were entrapped in a biologic coating which resulted in formation of complexes ranging from 117 nm to 605 nm. High zeta potential value of these complexes (−82.6 mV) and the presence of hydrophilic groups on the biologic coating provided a stable colloid system. Prepared INPs were non-crystalline (amorphous) having a low magnetization value of 0.14 emu/g. The prepared particles are of significant interest in a wide range of scientific and technical applications.