{'fraction_non_alphanumeric': 0.037, 'fraction_numerical': 0.021, 'mean_word_length': 4.623595505617978, 'pattern_counts': {'":': 0, '<': 0, '<?xml version=': 0, '>': 0, 'https://': 0, 'lorem ipsum': 0, 'www.': 0, 'xml': 0}, 'pii_count': 0, 'substrings_counts': 0, 'word_list_counts': {'cursed_substrings.json': 0, 'profanity_word_list.json': 0, 'sexual_word_list.json': 0, 'zh_pornsignals.json': 0}}
Type-II GaSb quantum dots grown on InAlAs/InP (001) by droplet epitaxy

GaSb quantum dots (QDs) have been grown by droplet epitaxy within InAlAs barrier layers on an InP (001) substrate. The droplet growth mode facilitates a larger size (average height ∼4.5 nm) and a lower density (∼6.3 × 109 cm-2) for the QDs than would be expected for the 4% lattice mismatch between GaSb and InAlAs. A type-II band alignment between the GaSb QDs and the InAlAs barriers is revealed by photoluminescence (PL) through a prominent blue-shift of ∼0.11 eV resulting from a six orders of magnitude increase in excitation power. Further confirmation of the type-II nature of these QDs is found through time-resolved PL studies showing a biexponential decay with a long carrier lifetime of ∼10.9 ns. These observations reveal new information for understanding the formation and properties of GaSb/InAlAs/InP QDs, which may be an optimum system for the development of both efficient memory cells and photovoltaic devices.