{'fraction_non_alphanumeric': 0.029345372460496615, 'fraction_numerical': 0.002257336343115124, 'mean_word_length': 5.616915422885572, 'pattern_counts': {'":': 0, '<': 0, '<?xml version=': 0, '>': 0, 'https://': 0, 'lorem ipsum': 0, 'www.': 0, 'xml': 0}, 'pii_count': 0, 'substrings_counts': 0, 'word_list_counts': {'cursed_substrings.json': 0, 'profanity_word_list.json': 0, 'sexual_word_list.json': 0, 'zh_pornsignals.json': 0}}
Effect of Sunlight/Ultraviolet Exposure on the Corrosion of Fusion-Bonded Epoxy (FBE) Coated Steel Rebars in Concrete

Currently, highway/railway bridges are designed for the service life of more than 100 y. In such reinforced concrete structures, fusion-bonded epoxy (FBE) coated steel rebars are being used in anticipation of delayed initiation of reinforcement corrosion. However, the FBE steel rebars get exposed to sunlight/ultraviolet rays during prolonged storage and delayed/staged construction. This paper presents microanalytical and electrochemical data (Fourier transform infrared spectroscopy, scanning electron microscopy, energy dispersion x-ray diffraction, and electrochemical impedance spectroscopy) and shows the adverse effects of sunlight/UV exposure on the corrosion resistance of FBE-coated steel reinforcement in concrete construction. Based on tests on steel-mortar specimens, the mechanisms of UV-induced chemical changes, shrinkage, and cracking of FBE coating, and the resulting steel corrosion mechanisms are proposed. Also, the adverse effects of sunlight/UV exposure on chloride threshold and reduction in the service life of FBE-coated steel in cementitious systems are presented. The paper recommends to minimize the exposure of FBE-coated steel rebars to sunlight/UV rays to less than one month.