{'fraction_non_alphanumeric': 0.025951557093425604, 'fraction_numerical': 0.010380622837370242, 'mean_word_length': 5.92814371257485, 'pattern_counts': {'":': 0, '<': 0, '<?xml version=': 0, '>': 0, 'https://': 0, 'lorem ipsum': 0, 'www.': 0, 'xml': 0}, 'pii_count': 0, 'substrings_counts': 0, 'word_list_counts': {'cursed_substrings.json': 0, 'profanity_word_list.json': 0, 'sexual_word_list.json': 0, 'zh_pornsignals.json': 0}}
Structure and peculiarities of nanodeformation in Ti–Zr–Ni quasi-crystals

Ti–Zr–Ni samples with a substantial predominance of icosahedral quasicrystalline phase were produced by the melt-spinning technique. Their structure and mechanical properties were studied by X-ray diffraction and nanoindentation methods. The quasicrystalline phase was found to have a primitive lattice with the quasicrystallinity parameter a q = 0.5200–0.5210 nm. Quasicrystalline deformation behaviour under nanoindentation versus phase composition and structure is discussed in comparison with single crystal W–12 wt% Ta. The estimated elastic modulus E of the quasicrystalline phase shows no correlation with the element composition. The nanohardness was shown to increase with increasing quasicrystalline-phase perfection. Load–displacement curves of Ti–Zr–Ni quasicrystals (QCs) show stepwise character with alternation of elastic and plastic sections. Such non-uniform plastic flow in QCs might be caused by the localization of plastic deformation in shear bands. The non-uniformity of the plastic deformation increases with the increasing quasicrystalline phase perfection.