{'fraction_non_alphanumeric': 0.04509073134966701, 'fraction_numerical': 0.030854768741980815, 'mean_word_length': 4.56734693877551, 'pattern_counts': {'":': 0, '<': 0, '<?xml version=': 0, '>': 0, 'https://': 0, 'lorem ipsum': 0, 'www.': 0, 'xml': 0}, 'pii_count': 0, 'substrings_counts': 0, 'word_list_counts': {'cursed_substrings.json': 1, 'profanity_word_list.json': 0, 'sexual_word_list.json': 0, 'zh_pornsignals.json': 0}}
Synthesis of Hierarchical Porous Carbon in Molten Salt and Its Application for Dye Adsorption

Hierarchical porous carbon was successfully synthesized from glucose in a molten salt at 800 °C for 2 h. It was amorphous and contained numerous oxygen containing functional groups on its surface. The porous carbon with 1.0 wt% Fe(NO3)3·9H2O oxidizing agent showed the highest specific surface area of 1078 m2/g, and the largest pore volume of 0.636 cm3/g, among all of the samples. Raman and TEM results revealed that it had more defects and pores than other as-prepared carbon materials. The adsorption capacities of as-prepared porous carbon for methylene blue (MB) and methyl orange (MO) were 506.8 mg/g and 683.8 mg/g, respectively. The adsorption isotherms fit the Langmuir model and the adsorption kinetics followed the pseudo-second-order kinetic model.


Introduction
Dyes have long been used in plastic, paper, leather, textile, and other industrial sectors. Wastewaters discharged from these industrial sectors often contain a certain amount of dyes, especially water-soluble organic dyes, due to their low biodegradability [1][2][3]. The conventional biological treatment processes fail to effectively treat these dye wastewaters, due to which, several physical or chemical processes, including osmosis [4], electro flotation [5], chemical oxidation [6], ion exchange [7], and filtration [8], have been developed in recent years. Unfortunately, these processes are not economically-viable and are still not sufficiently effective for treating a wide range of dye wastewaters [9]. Physical adsorption has become the most popular method so far for removing dyes from wastewaters, owing to its low cost, high efficiency, easy operation, diversity in adsorbents, and high stability towards the adsorbents.
Porous carbon materials have been widely applied for removing dyes and other organic and inorganic pollutants from drinking water due to their high specific surface area [10][11][12]. In particular, those with hierarchical porosities (micro-/meso-/macropore) exhibit enhanced dye adsorption performance. This is because that the hierarchical pore structures can provide various functions: Micropores provide high surface area and large adsorption capacity, mesopores facilitate dye transporting, and macropores act as reservoirs for dye molecules.
Several techniques, mainly physical or chemical activation combined with templating, have been used to synthesize hierarchical porous carbon materials [13][14][15]. However, they exhibited some disadvantages, such as high carbonization temperature, multiple steps, low carbon yield, vessel corrosion, and environmental pollution. Recently, molten salt synthesis methods have become applicable to the preparation of a wide range of nanomaterials, including binary, ternary/multinary oxides [16][17][18][19][20][21][22][23][24][25], hydroxide [26], non-oxides [27], and porous carbon materials [28][29][30][31]. For example, Liu et al. synthesized porous carbon and carbon sheets in molten LiCl/KCl containing different oxysalts (such as Fe(NO 3 ) 3 ·9H 2 O, KClO 3 , and K 2 CO 3 ), which facilitated pore formation in the final porous carbon [32]. Deng et al. prepared nitrogen-doped hierarchically porous carbon materials with high specific surface area in molten ZnCl 2 [33]. Despite these studies, there have been few studies on the preparation of porous carbon with high specific surface area by using a combined activator, ZnCl 2 and Fe(NO 3 In this work, hierarchical porous carbon was synthesized in ZnCl 2 -KCl molten salt using a low-cost and eco-friendly glucose carbon source and an Fe(NO 3 ) 3 ·9H 2 O oxidizing agent. The effects of additional amounts of Fe(NO 3 ) 3 ·9H 2 O on the specific surface area of as-prepared samples were investigated, as were their adsorption capacities for methylene blue (MB) and methyl orange (MO).

Raw Materials and Sample Preparation
The main starting materials included: Glucose (C 6  In a typical preparation process, 2 g glucose and different amounts of Fe(NO 3 ) 3 ·9H 2 O (0-2.0 wt% Fe of carbon amount, the samples are referred to as 0 Fe, 0.5 Fe, 1.0 Fe, 1.5 Fe, and 2.0 Fe, respectively) were milled together and further combined with 20 g of KCl and ZnCl 2 (in the weight ratio of 1:2. The eutectic point of the binary salt is 234 • C.). The mixed powder was contained in an alumina crucible and heated at 2 • C/min to 800 • C and soaked for 2 h in an alumina tube furnace protected by flowing Ar (99.999 vol% pure). The reacted sample was subjected to repeat water-washing before being oven-dried for 12 h at 80 • C.

Adsorption Test
Adsorption processes were investigated using MB and MO. Typically, 20 mg of as-prepared sample (porous carbon) powder was added into 50 mL MB aqueous solution with a concentration ranging from 0 to 500 mg/L. The suspension was then homogenized for 30 min at 25 • C using a magnetic stirrer. After centrifugation, the solution part was examined using a UV-visible spectrophotometer.
To study the adsorption kinetics, 60 mg of as-prepared porous carbon were added to 150 mL aqueous dye solution (100 mg/L) in a beaker. The suspension was stirred using a magnetic stirrer. After a certain time period, 5 ml of the solution was taken and centrifuged for UV-vis examination. The maximum adsorption wavelengths of 665 nm and 464 nm, in the cases of MB and MO, were used respectively for calculation.
The equilibrium adsorption amount of the porous carbon materials was determined based on the following equation: where q e (mg/g) is the equilibrium adsorption amount, c 0 (mg/L) is the initial concentration of dye solution, c e (mg/L) is the equilibrium concentration of dye solution, v (L) is the volume of dye solution, and m (g) is the mass of porous carbon.

Characterization
Powder X-ray diffraction (XRD) analysis was carried out using a Philips X'Pert PRO diffractometer (Xpertpro, PHILIPS, Hillsboro, The Netherlands) at 40 mA and 40 kV and with a Cu Kα radiation (λ = 0.1542 nm). The scan range was between 10 • and 90 • (2θ) at 40 mA and 40 kV and the scan rate was 2 • /min with a step size of 0.05 • . Microstructure and phase morphologies of as-prepared samples were examined by using a field-emission scanning electron microscope (FE-SEM; Nova400NanoSEM, 15 kV, Philips, Amsterdam, The Netherlands) and a transmission electron microscope (TEM) JEM-2100UHRSTEM, 200 kV (JEOL, Tokyo, Japan) along with an energy dispersive spectrometer (EDS) Penta FET X-3 Si (Li) (EDS, IET 200, Oxford, UK). The specific surface area of as-prepared samples was calculated based on Brunauere Emmette Teller (BET) nitrogen adsorption/desorption analysis carried out using a gas sorption analyzer Autosorb-1-MP/LP (Quantachrome, Boynton Beach, FL, USA). Functional groups on the surface of a sample were identified by Fourier Transform Infrared Spectroscopy (FTIR) VERTEX 70 (Bruker, Karlsruhe, Germany). The adsorption of MB or MO was examined by Ultraviolet-visible spectroscopy UV-2550 (Shimadzu Corporation, Kyoto, Japan). Raman spectra were recorded using a Horiba Jobin-Yvon Labram-HR800 Raman spectrometer (Raman, Paris, France) with an excitation wavelength of 532 nm.

Microstructural Characterization of As-Prepared Porous Carbon
Powder X-ray diffraction patterns of samples resultant from 2 h firing in molten salt at 800 • C are shown in Figure 1a   Scanning electron microscope images of as-prepared carbon samples resulting from 2 h firing at 800 • C in the molten salt with various amounts of Fe(NO 3 ) 3 ·9H 2 O are shown in Figure 2, and reveal the formation of irregular carbon particles and carbon sheets. With increasing Fe content, the morphology of the carbon particles changed very little. The carbon particles resulted from the decomposition of glucose and the nucleation of intermediates and their subsequent growth during carbonization, whereas the carbon sheets were formed via the merging and growing of carbon particles facilitated by highly reactive lithium, potassium, and chloride ions in the molten salt medium [37,38]. the largest specific surface area. Figure 3b shows the pore size distribution curves derived from the 142 desorption isotherms using the Barret-Joner-Halenda (BJH) method, which reveal the formation of N 2 adsorption-desorption isotherms of as-prepared carbon samples, along with the derived pore size distributions are presented in Figure 3. Similar type I isotherms were seen in all cases, and the adsorption amounts within different relative pressure ranges reflected different pore structures (micropores (P/P 0 between 0−0.1), mesopores (P/P 0 between 0.1−0.8), and macroporous (P/P 0 between 0.8-1.0) [39,40]. Therefore, the N 2 sorption profiles evidently reveal that the as-prepared carbon materials possessed a hierarchical micro-/mesoporous structure. From Figure 3a, it can be seen that the sample with 1.0 wt% Fe showed the maximum adsorption volume, indicating it has the largest specific surface area. Figure 3b shows the pore size distribution curves derived from the desorption isotherms using the Barret-Joner-Halenda (BJH) method, which reveal the formation of mainly microand meso-porosities in as-prepared carbon materials. The porosity parameters of as-prepared porous carbon materials are listed in Table 1. As can be seen from Table 1, the BET specific surface areas of all of the samples with Fe(NO 3 ) 3 ·9H 2 O increased compared to the sample without Fe(NO 3 ) 3 ·9H 2 O, and upon increasing the amount of Fe(NO 3 ) 3 ·9H 2 O to 1.0 wt%, the sample showed the highest BET specific surface area of 1078 m 2 /g and the highest pore volume of 0.636 cm 3 /g. Furthermore, the mesoporous volume percent reached up to 60% with increasing the Fe amount to 1.0-1.5 wt%, which was probably mainly due to the decomposition of Fe(NO 3 ) 3 ·9H 2 O during carbonization [41]. as-prepared porous carbon materials are listed in Table 1. As can be seen from Table 1 Figure 4 presents Raman spectra of porous carbon materials prepared at 800 • C for 2 h with various amounts of Fe. Two main peaks at 1350 and 1590 cm -1 were respectively assigned to the D band and G band [42]. With the increase of the Fe amount, the value of I D /I G increased initially and then decreased, demonstrating the existence of many defects in the as-prepared porous carbon.  Based on the above test results, it can be concluded that addition of 1.0 wt% Fe(NO 3 ) 3 ·9H 2 O, resulted in the largest specific surface area. In order to compare and further reveal the effectiveness of Fe(NO 3 ) 3 ·9H 2 O, samples using respectively FeCl 3 ·6H 2 O and Zn(NO 3 ) 2 as oxidizing agents were also prepared under similar processing conditions to those in the case of using 1.0 wt% Fe(NO 3 ) 3 ·9H 2 O. Amorphous carbon was also formed in these two cases ( Figure S1). For the sample with added FeCl 3 ·6H 2 O, one peak at about 36.2 • appeared, which was corresponded to Fe 3 O 4 . As shown in Figure S2, porous carbons prepared using FeCl 3 and Zn(NO 3 ) 2 as oxidizing agents were mainly comprised of carbon particles. Different from the case of using Fe(NO 3 ) 3 ·9H 2 O, carbon sheets were only occasionally seen. FTIR identified the existence of some oxygen containing functional groups and C-H groups on the surface of as-prepared porous carbon ( Figure S3). The specific surface areas of the samples prepared with FeCl 3 and Zn(NO 3 ) 2 were 534 and 654 m 2 /g, respectively ( Figure S4), which are even lower than that of the sample prepared without using any oxidizing agents (Table 1), indicating that neither FeCl 3 nor Zn(NO 3 ) 2 was useful for increasing the specific surface area. The sample with Zn(NO 3 ) 2 had a higher surface area than in the case of using FeCl 3 , which was attributed to the oxidizability of Zn(NO 3 ) 2 . The samples prepared with Fe(NO 3 ) 3 ·9H 2 O showed the highest surface area, since Fe(NO 3 ) 3 ·9H 2 O can act as an effective oxidizing agent during carbonization [43]. It reacts with glucose and releases some gaseous phases, such as NO x , CO, and CO 2 , facilitating the formation of micro/mesopores [41]. Comparison of the Raman results ( Figure S5 and Figure 4) also reveals that the samples with Fe(NO 3 ) 3 ·9H 2 O had a higher I D /I G value, suggesting the existence of more defects in them.
In order to further reveal the porous structures of the as-prepared carbon materials, Figure 5, as an example, shows TEM images and EDS results of the sample prepared with 1.0 wt% Fe. As seen from Figure 5a,b, the as-prepared carbon contained a large number of mesopores, which were consistent with the BET results ( Figure 3). EDS of the selected region in Figure 5a indicated that the sample was mainly composed of C, Fe, and O elements. seen from Figure 5a,b, the as-prepared carbon contained a large number of mesopores, which were 185 consistent with the BET results ( Figure 3). EDS of the selected region in Figure 5a indicated that the 186 sample was mainly composed of C, Fe, and O elements.

Adsorption Performance of As-Prepared Porous Carbon for Methylene Blue and Methyl Orange
The adsorption behaviors of porous carbon materials prepared with various amounts of Fe (Figures 1-5) were also examined using MB and MO as adsorbates, and the adsorption isotherms were simulated using the Langmuir and Freundlich models expressed as follows: Freundlich isotherm : where q e (mg/g) is the equilibrium adsorption amount, Q 0 (mg/g) is the maximum adsorption amount, b (L/mg) is the constant term related to the energy of adsorption, c e (mg/L) is the equilibrium concentration of dye solution, and k F and n are the Freundlich constants. The calculated adsorption parameters and correlation coefficients (R 2 ) (Tables 2 and 3) suggest that the Langmuir model fits the data better than the Freundlich model. The maximum monolayer adsorption capacity (Q 0 ) of the as-prepared porous carbon (1.0 Fe) for MB and MO were calculated to be 506.8 and 683.8 mg/g, respectively, which was mainly attributed to the much larger specific surface area of the hierarchical porous carbon materials and the oxygen containing functional groups existing on their surfaces. Table 4 compares the adsorption capacity for dyes of hierarchical porous carbon materials and other adsorbents. The high adsorption capacity of hierarchical porous carbon materials prepared in this work indicates their feasibility in dye removal. The following pseudo-first-order and pseudo-second-order kinetic models [1] were also used to assist understanding the relevant adsorption mechanism: Pseudo-first-order model : Pseudo-second-order model : where q t (mg/g) is the adsorption amount at time t, k 1 and k 2 (g·mg −1 ·min −1 ) are respectively the pseudo-first-order and pseudo-second-order rate constants. As indicated by the results listed in Tables 2 and 3, the pseudo-second-order model shows a good linearity, with correlation coefficients (R 2 ) ≥ 0.99, suggesting that the adsorption kinetics of as-prepared porous carbon follow this model ( Figure 6).
where qt (mg/g) is the adsorption amount at time t, k1 and k2 (g·mg -1 ·min -1 ) are respectively the 223 pseudo-first-order and pseudo-second-order rate constants.

225
As indicated by the results listed in Table 2 Table 3, the pseudo-second-order model shows a 226 good linearity, with correlation coefficients (R 2 ) ≥ 0.99, suggesting that the adsorption kinetics of 227 as-prepared porous carbon follow this model ( Figure 6).

Conclusions
A simple molten salt method was used to synthesize hierarchical porous carbon at 800 • C for 2 h. Glucose and ZnCl 2 -KCl were used as the carbon source and reaction medium, respectively. Numerous oxygen containing functional groups existed on the surface of the as-prepared porous carbon. The porous carbon prepared with 1.0 wt% Fe(NO 3 ) 3 ·9H 2 O addition showed the highest specific surface area of 1078 m 2 /g and the largest pore volume of 0.636 cm 3 /g, which were attributed to Fe(NO 3 ) 3 ·9H 2 O acting as an oxidizing agent during carbonization, favoring the formation of micro/mesopores. The adsorption capacities of as-prepared hierarchical porous carbon for methylene blue and methyl orange were respectively 506.8 mg/g and 683.8 mg/g. The adsorption isotherms fit the Langmuir model and the adsorption kinetics followed the pseudo-second-order kinetic model.