{'fraction_non_alphanumeric': 0.01353637901861252, 'fraction_numerical': 0.0, 'mean_word_length': 5.365591397849462, 'pattern_counts': {'":': 0, '<': 0, '<?xml version=': 0, '>': 0, 'https://': 0, 'lorem ipsum': 0, 'www.': 0, 'xml': 0}, 'pii_count': 0, 'substrings_counts': 0, 'word_list_counts': {'cursed_substrings.json': 0, 'profanity_word_list.json': 0, 'sexual_word_list.json': 0, 'zh_pornsignals.json': 0}}
EBSD Investigation on the Primary Recrystallization in Warm Rolled Ti-IF Steel

The nucleus orientations and the nucleation sites at the early stage of recrystallization were studied by EBSD analysis in Ti-IF steel during direct annealing after warm rolling. It is concluded that the formation of the recrystallization texture is dominated by oriented nucleation mechanism. The recrystallized nuclei with γ-orientation emerge preferentially at the beginning of recrystallization and prefer to form inside the γ-oriented deformation bands and on the boundaries between γ and α-oriented bands.