{'fraction_non_alphanumeric': 0.046532846715328466, 'fraction_numerical': 0.024635036496350366, 'mean_word_length': 4.866310160427807, 'pattern_counts': {'":': 0, '<': 0, '<?xml version=': 0, '>': 0, 'https://': 0, 'lorem ipsum': 0, 'www.': 0, 'xml': 0}, 'pii_count': 0, 'substrings_counts': 0, 'word_list_counts': {'cursed_substrings.json': 0, 'profanity_word_list.json': 0, 'sexual_word_list.json': 0, 'zh_pornsignals.json': 0}}
Lipase Encapsulation onto ZIF‐8: A Comparison between Biocatalysts Obtained at Low and High Zinc/2‐Methylimidazole Molar Ratio in Aqueous Medium

Lipase AK from Pseudomonas fluorescens and Lipase RM from Rhizomucor miehei were encapsulated into a zeolite imidazolate framework (ZIF‐8) by a “one‐pot” synthesis to obtain AK@ZIF‐8 and RM@ZIF‐8 biocatalysts. The effect of a high (1:40) and low (1:4) Zn/2‐methylimidazole molar ratio on the biocatalysts synthesis was investigated. The different Zn/ligand (L) ratios affected both the surface area, the loading, and the specific activity of the biocatalysts. Samples synthesized by using a high Zn/L ratio had high values of surface area whereas those obtained by using a low Zn/L ratio had higher loadings and specific activities. The decrease of pH (from 11.6 to 9.4) during the synthesis at high Zn/L ratio produced ZIF‐8 samples with features similar to those observed for low Zn/L ratio samples. The low Zn/L (1:4) ratio AK@ZIF‐8 biocatalyst retained 99 % activity after storage for 15 days at 5 °C and 40 % activity after five reaction cycles.