{'fraction_non_alphanumeric': 0.048254620123203286, 'fraction_numerical': 0.037987679671457907, 'mean_word_length': 4.6686046511627906, 'pattern_counts': {'":': 0, '<': 1, '<?xml version=': 0, '>': 0, 'https://': 0, 'lorem ipsum': 0, 'www.': 0, 'xml': 0}, 'pii_count': 0, 'substrings_counts': 0, 'word_list_counts': {'cursed_substrings.json': 0, 'profanity_word_list.json': 0, 'sexual_word_list.json': 0, 'zh_pornsignals.json': 0}}
Structure and Microwave Absorption Properties of Ho-Fe-Si Alloys

The Ho2Fe17-xSix (x=0.0, 0.1, 0.2, 0.3) alloys were prepared by arc melting and high energy ball milling method. The influence of the Si substitution on phase structure, morphology and electromagnetic parameters were investigated by X-ray diffraction (XRD), scanning electron microscopy (SEM) and vector network analyzer (VNA), respectively. The results show that the Ho-Fe-Si particles are flaky after the ball milling. The minimum absorption peak frequency shifts towards a lower frequency region with the increasing of Si content. The minimum RL of Ho2Fe16.7Si0.3 reaches-42.96 dB at 9.76 GHz, and the frequency bandwidth of R<-10 dB reaches about 2.64 GHz with the best matching condition d=1.6 mm. The reflection loss with the thickness ranging of 1.2-3.0 mm could reach-10 dB, which indicates the particles be considered as the promising microwave absorbing materials with a good absorption properties.