{'fraction_non_alphanumeric': 0.01906158357771261, 'fraction_numerical': 0.0036656891495601175, 'mean_word_length': 5.6911764705882355, 'pattern_counts': {'":': 0, '<': 0, '<?xml version=': 0, '>': 0, 'https://': 0, 'lorem ipsum': 0, 'www.': 0, 'xml': 0}, 'pii_count': 0, 'substrings_counts': 0, 'word_list_counts': {'cursed_substrings.json': 0, 'profanity_word_list.json': 0, 'sexual_word_list.json': 0, 'zh_pornsignals.json': 0}}
Study on Steady Shear, Morphology and Mechanical Behavior of Nanocomposites based on Polyamide 6

Nanocomposites of two different grades of polyamide 6 (PA6) with organically modified nanoclay were prepared via melt compounding in a twin‐screw extruder. The rheological behavior, morphology and mechanical properties of the nanocomposites were studied using a capillary rheometer, x‐ray diffraction (XRD), tapping‐mode atomic force microscopy (AFM), and tensile and flexural tests. XRD patterns indicate that the organically modified layered silicate was well dispersed in the PA6 matrix. From the AFM images the surface roughness of PA6 slightly increases with addition of organoclay. The rheological studies showed that the prepared nanocomposites have shear thinning behavior, obeying the power law equation. Addition of organoclay increases the shear stress and shear viscosity. At high rate of shear deformation the viscosity of nanocomposites are comparable to those of the pure polyamides. The activation energy of flow decreases with increasing nanoclay content. For most of the prepared nanocomposites the activation energy values increase with increasing shear rate. The tensile strength and flexural modulus and strength of the nanocomposites increase with increase of nanoclay content, but the extension at yield decreases with increasing clay loading.