{'fraction_non_alphanumeric': 0.019157088122605363, 'fraction_numerical': 0.0007662835249042146, 'mean_word_length': 5.433497536945813, 'pattern_counts': {'":': 0, '<': 0, '<?xml version=': 0, '>': 0, 'https://': 0, 'lorem ipsum': 0, 'www.': 0, 'xml': 0}, 'pii_count': 0, 'substrings_counts': 0, 'word_list_counts': {'cursed_substrings.json': 0, 'profanity_word_list.json': 0, 'sexual_word_list.json': 0, 'zh_pornsignals.json': 0}}
Laser-promoted nanostructure evolution and nanoparticle alignment

A cone microstructure has been used as a template to generate nanotips and to promote nanoparticle alignment. A quasi-periodic array of nanotips is produced when the laser-induced cone microstructure is subject to chemical etching due to tapering of the cone tips. Nanoparticles can be produced on the surface of a silicon specimen by irradiating it in the presence of an inert gas atmosphere. The backscattered material that is re-deposited on the substrate, upon irradiation at fluences close to the melting threshold, is composed of a thin film intermixed with extremely small nanoparticles. Further irradiation promotes film clustering and nanoparticle formation. In the presence of cones, the nanoparticles become aligned into straight and long (~1 mm) lines whose spacing is close to the laser wavelength. This result suggested an ordering mechanism similar to that occurring for laser-induced periodic surface structures. The relation between nanoparticle line spacing and angle of incidence of the radiation supported this similarity. Nanoparticle ordering also was promoted by laser-enhanced chemical vapor deposition (LCVD) using polarized light, when a laser-induced periodic surface nanostructure was present in the substrate.