{'fraction_non_alphanumeric': 0.03636363636363636, 'fraction_numerical': 0.02857142857142857, 'mean_word_length': 4.840909090909091, 'pattern_counts': {'":': 0, '<': 0, '<?xml version=': 0, '>': 0, 'https://': 0, 'lorem ipsum': 0, 'www.': 0, 'xml': 0}, 'pii_count': 0, 'substrings_counts': 0, 'word_list_counts': {'cursed_substrings.json': 0, 'profanity_word_list.json': 0, 'sexual_word_list.json': 0, 'zh_pornsignals.json': 0}}
Low-pressure acidic ammonothermal growth of 2-inch-diameter nearly bowing-free bulk GaN crystals

Seeded growth of 2-inch-diameter GaN crystals via low-pressure (∼100 MPa) acidic ammonothermal method is demonstrated. Nearly bowing- and mosaic-free GaN crystals exhibiting full-width at half-maximum values for the 0002 X-ray rocking curves below 20 arcsec were achieved on high lattice coherency c-plane SCAATTM seeds with gross dislocation densities in the order of 104 cm−2. The photoluminescence spectra of the grown crystals exhibited a predominant near-band-edge emission at 295 K, of which intensity was one order of magnitude higher than the characteristic deep-state emission bands. A nearly bowing-free 60 mm × 60 mm c-plane GaN crystal was eventually obtained.