{'fraction_non_alphanumeric': 0.03443429374560787, 'fraction_numerical': 0.012649332396345749, 'mean_word_length': 4.836065573770492, 'pattern_counts': {'":': 0, '<': 2, '<?xml version=': 0, '>': 0, 'https://': 0, 'lorem ipsum': 0, 'www.': 0, 'xml': 0}, 'pii_count': 0, 'substrings_counts': 0, 'word_list_counts': {'cursed_substrings.json': 0, 'profanity_word_list.json': 0, 'sexual_word_list.json': 0, 'zh_pornsignals.json': 0}}
On the origin of the cobalt particle size effects in Fischer-Tropsch catalysis.

The effects of metal particle size in catalysis are of prime scientific and industrial importance and call for a better understanding. In this paper the origin of the cobalt particle size effects in Fischer-Tropsch (FT) catalysis was studied. Steady-State Isotopic Transient Kinetic Analysis (SSITKA) was applied to provide surface residence times and coverages of reaction intermediates as a function of Co particle size (2.6-16 nm). For carbon nanofiber supported cobalt catalysts at 210 degrees C and H(2)/CO = 10 v/v, it appeared that the surface residence times of reversibly bonded CH(x) and OH(x) intermediates increased, whereas that of CO decreased for small (<6 nm) Co particles. A higher coverage of irreversibly bonded CO was found for small Co particles that was ascribed to a larger fraction of low-coordinated surface sites. The coverages and residence times obtained from SSITKA were used to describe the surface-specific activity (TOF) quantitatively and the CH(4) selectivity qualitatively as a function of Co particle size for the FT reaction (220 degrees C, H(2)/CO = 2). The lower TOF of Co particles <6 nm is caused by both blocking of edge/corner sites and a lower intrinsic activity at the small terraces. The higher methane selectivity of small Co particles is mainly brought about by their higher hydrogen coverages.