{'fraction_non_alphanumeric': 0.01916646474436637, 'fraction_numerical': 0.020147807123818754, 'mean_word_length': 4.755595844083397, 'pattern_counts': {'":': 0, '<': 0, '<?xml version=': 0, '>': 0, 'https://': 0, 'lorem ipsum': 0, 'www.': 0, 'xml': 0}, 'pii_count': 0, 'substrings_counts': 0, 'word_list_counts': {'cursed_substrings.json': 11, 'profanity_word_list.json': 0, 'sexual_word_list.json': 0, 'zh_pornsignals.json': 0}}
Experimental Characterization and Deterministic Prediction of In-Plane Formability of 3rd Generation Advanced High Strength Steels

The objective of the current study is to develop a practical, deterministic approach to the prediction of the in-plane formability of two third generation advanced high-strength steels (AHSS) of 980 and 1180 MPa ultimate tensile strength using only quasi-static mechanical property data. The hardening response to large strains was experimentally measured with the use of simple shear and tensile tests and validated in tensile simulations. The process-corrected limit strains in the Nakazima and Marciniak tests were compared to various analytical Forming Limit Curve (FLC) models for in-plane stretching. It was observed that the widely-used Marciniak–Kuczynski model can adequately predict the experimental FLC in biaxial stretching but significantly underestimated the limit strains in uniaxial stretching for both third generation AHSS. The observed through-thickness shear fracture mode in biaxial stretching was reasonably well-captured by the Bressan–Williams (BW) instability model for the 1180 MPa steel. A proposed extension of the BW model to uniaxial tension by adoption of the maximum in-plane shear stress criterion (BWx model) provided superior experimental correlation relative to the zero-extension model of Hill that was too conservative. Finally, a linearized version of the modified maximum force criterion (MMFC) was proposed that markedly improved the correlation with the process-corrected FLC for in-plane stretching of AHSS. The developed framework for FLC prediction was then applied to a DP980 AHSS and an AA5182 aluminum alloy from the literature. The DP980 corroborated the observed trend for the two third generation AHSS whereas the MK and the BWx models performed best for the AA5182 with its saturation-type hardening behavior and non-quadratic yield surface.


Introduction
The automotive industry has been aggressively pursuing the development and incorporation of new grades of advanced high strength steel (AHSS) for vehicle lightweighting and enhanced crash performance. A light weight of the vehicle structure is constrained by strength requirements for anti-intrusion into the cabin as well as the local ductility of the material for energy absorption. The replacement of conventional steels with advanced high strength steels (AHSS) can reduce component weight by reducing the thickness while increasing strength [1]. The recent development of the so-called third generation of AHSS provides significant improvements in formability compared to the first generation of AHSS [2] due to their complex microstructures and retained austenite that transforms to martensite during deformation [3]. The formability of a third generation 980 MPa steel can be comparable to a conventional 590 MPa or 780 MPa AHSS grade [4]. There are many variants of The focus of the present study is on the experimental characterization and deterministic prediction of the forming limit strains for two third generation AHSS with a nominal ultimate tensile strength of 980 MPa and 1180 MPa by only using quasi-static mechanical property data. Calibration of an analytical formability model with prior knowledge of limit strains, even just the FLC 0 , is prohibitive from an experimental standpoint and also raises questions of calibration bias in the resulting FLC predictions. To remove uncertainty with respect to the influence of the hardening model extrapolation using tension test data, the novel experimental methodology of Rahmaan et al. [20] using simple shear and tension tests will be adopted. The formability of both 3rd Gen AHSS will be characterized using both Marciniak and Nakazima tests to demonstrate the influence of the process-effects on the Nakazima FLC. The formability predictions of the MK model, the MMFC model, and two variants of the Bressan-Williams (BW) [21] critical shear stress model will be compared with the corrected Marciniak and Nakazima FLC data. Extensions to the MMFC model and BW models were proposed to enhance the predictive accuracy while not introducing any new calibration parameters. Finally, to evaluate the proposed framework for FLC prediction for a larger range of automotive sheet metals, a DP980 and aluminum AA5182 alloy are also considered that were characterized for in-plane formability by Noder and Butcher [18].

Characterization of Anisotropy
The two third generation steels considered in this study are commercially available and were provided by steel member companies of the Automotive Program of the American Iron and Steel Institute (AISI) (Washington, DC, USA). The identity of the suppliers was kept blind to the parties involved, including the authors. Two third generation advanced high-strength steels (AHSS), denoted as 3rd Gen 980 and 3rd Gen 1180, with 1.4 mm nominal thickness and nominal ultimate tensile strength (UTS) of 980 MPa and 1180 MPa were selected for this study. The mechanical properties of both steels were characterized in uniaxial tension with the JIS No. 5 specimen geometry ( Figure 1a) and simple shear with the geometry of Peirs et al. [22] shown in Figure 1b. Disc compression tests with a diameter of 5 mm were performed according to the procedure of Tian et al. [23] at strain levels up to approximately 19% to determine the biaxial R-value. Tensile tests were conducted in five orientations in 22.5 • increments with respect to the rolling direction with vertical and horizontal gage lengths of 50 mm and 25 mm, respectively. The shear tests were extracted such that the principal stress directions are initially aligned in the rolling (RD) and transverse directions (TD). DIC strain measurement was performed using the Vic-3D ® 7 software (Correlated Solutions Inc., Irmo, SC, USA). The virtual strain gage length (VSGL) is commonly reported and provides a measure for the local region used for strain computation in the DIC analysis. In the shear tests, the VSGL of 0.3 mm was computed from the product of the step size (7), filter size (5 pixel), and camera resolution (0.0085 mm/pixel).
The shear test geometry has a nominal gage length of 3.0 mm to determine the shear stress which is relatively homogeneous in the adopted shear geometry. Additional details on DIC analysis and validation of the shear geometry for constitutive characterization can be found in Rahmaan et al. [20]. Table 1 provides a summary of the mechanical data retrieved from tensile tests in the TD. The material yield strength was obtained from a 0.2% offset of the equivalent strain that was obtained from a 50 mm virtual extensometer. The Considère [24] criterion was adopted for identification of the uniform elongation. Surface roughness measurements performed with a profilometer and a characteristic length of 2.5 mm revealed similar average roughness values for both steel grades. The anisotropy parameters are summarized in Table 2. The tensile R-values were determined by Figure 1. Geometric dimensions of adopted geometries to characterize the material behavior in uniaxial tension using the JIS No. 5 tensile geometry (a) and shear loading using the miniature shear geometry proposed by Peirs et al. [22] (b). All dimensions are in milimeters. Table 1 provides a summary of the mechanical data retrieved from tensile tests in the TD. The material yield strength was obtained from a 0.2% offset of the equivalent strain that was obtained from a 50 mm virtual extensometer. The Considère [24] criterion was adopted for identification of the uniform elongation. Surface roughness measurements performed with a profilometer and a characteristic length of 2.5 mm revealed similar average roughness values for both steel grades. The anisotropy parameters are summarized in Table 2. The tensile R-values were determined by averaging the DIC strain field in an area of 25 × 50 mm over a range of true strain from 0.05-0.15 and 0.03-0.08 for the 3rd Gen 980 and the 3rd Gen 1180, respectively, which approximately corresponds to the range of uniform deformation. The limiting direction for both steels was in TD and the plastic work and equivalent plastic strain at the onset of diffuse necking corresponded to 164.7 MJ/m 3 and 0.15 respectively for the 3rd Gen 980 and 88.4 MJ/m 3 and 0.07 respectively for the 3rd Gen 1180. The dimensionless stress ratios of the tensile and shear stress with respect to the stress in RD were determined at the limiting plastic work level.  . Geometric dimensions of adopted geometries to characterize the material behavior in uniaxial tension using the JIS No. 5 tensile geometry (a) and shear loading using the miniature shear geometry proposed by Peirs et al. [22] (b). All dimensions are in milimeters.

Determination and Calibration of the Isotropic Hardening Behavior up to Large Strains
Analytical predictions of formability can be very sensitive to the selection of the hardening law particularly in biaxial stretching where the equivalent limit strains can far exceed the necking strain in uniaxial tension. If only uniaxial tension data is available, then the accuracy of the predictions depends upon the unverified accuracy of the post-uniform extrapolation [25]. In order to obtain the hardening response to higher strains to remove uncertainty in the limit strain prediction, biaxial bulge tests can be performed. Hydraulic bulge tests require specialized test equipment and accurate extraction of the hardening curve requires careful analysis of the DIC data as detailed by Min et al. [16]. Simple shear tests are an attractive alternative for materials that exhibit isotropic hardening since they can be readily performed on a universal test frame along with the tensile tests. Shear tests are not limited by a tensile instability as in uniaxial tension or bulge tests so that very large strain levels can be obtained prior to fracture. A novel experimental methodology to use simple shear to obtain the isotropic hardening behavior has been developed by Rahmaan et al. [20] and is utilized in the present study for the two steels. The method converts the uniaxial and shear stress responses to be in terms of the plastic work. The tensile hardening response is used until the onset of diffuse necking and the shear stress ratio at this work level is used to convert the shear stress to an equivalent tensile stress. Figure 2 serves to show the approximately stable stress conversion ratio by the plastic work level corresponding to the tensile instability that justifies the assumption of isotropic hardening for the studied steel grades. Next, the equivalent plastic strain is calculated from the plastic work. A limitation of the methodology is that it does not account for shear anisotropy due to the material frame rotation, but it can be readily accounted for by using the procedure of Abedini et al. [26] that requires shear tests to be performed in different orientations. For a DP980 and DP1180 steel, Abedini et al. [26] reported that the error associated with neglecting material frame rotation in the determination of the hardening response was on the order of 2% for the AHSS but was 5% for AA5182 aluminum and 15% for an AA6063-T6 aluminum extrusion. Based upon the results of Rahmaan et al. [20] for a DP600 steel along with the DP980 and DP1180 of Abedini et al. [26], only one shear test was performed to obtain the hardening response. The use of a single shear test is considered to be at least first-order accurate for the hardening response of the 3rd Generation steels and only adds a single test to be performed alongside the basic tensile characterization. The hardening response for the tensile and shear tests for both steels are shown in Figure 3. The validity of the experimental hardening curve obtained using the tensile and shear tests is evaluated in Section 2.4 using 3D simulations of the tensile test where large strains develop due to localization.
hardening response to higher strains to remove uncertainty in the limit strain prediction, biaxial bulge tests can be performed. Hydraulic bulge tests require specialized test equipment and accurate extraction of the hardening curve requires careful analysis of the DIC data as detailed by Min et al. [16]. Simple shear tests are an attractive alternative for materials that exhibit isotropic hardening since they can be readily performed on a universal test frame along with the tensile tests. Shear tests are not limited by a tensile instability as in uniaxial tension or bulge tests so that very large strain levels can be obtained prior to fracture.
A novel experimental methodology to use simple shear to obtain the isotropic hardening behavior has been developed by Rahmaan et al. [20] and is utilized in the present study for the two steels. The method converts the uniaxial and shear stress responses to be in terms of the plastic work. The tensile hardening response is used until the onset of diffuse necking and the shear stress ratio at this work level is used to convert the shear stress to an equivalent tensile stress. Figure 2 serves to show the approximately stable stress conversion ratio by the plastic work level corresponding to the tensile instability that justifies the assumption of isotropic hardening for the studied steel grades. Next, the equivalent plastic strain is calculated from the plastic work. A limitation of the methodology is that it does not account for shear anisotropy due to the material frame rotation, but it can be readily accounted for by using the procedure of Abedini et al. [26] that requires shear tests to be performed in different orientations. For a DP980 and DP1180 steel, Abedini et al. [26] reported that the error associated with neglecting material frame rotation in the determination of the hardening response was on the order of 2% for the AHSS but was 5% for AA5182 aluminum and 15% for an AA6063-T6 aluminum extrusion. Based upon the results of Rahmaan et al. [20] for a DP600 steel along with the DP980 and DP1180 of Abedini et al. [26], only one shear test was performed to obtain the hardening response. The use of a single shear test is considered to be at least first-order accurate for the hardening response of the 3rd Generation steels and only adds a single test to be performed alongside the basic tensile characterization. The hardening response for the tensile and shear tests for both steels are shown in Figure 3. The validity of the experimental hardening curve obtained using the tensile and shear tests is evaluated in Section 2.4 using 3D simulations of the tensile test where large strains develop due to localization. Recent work by Noder and Butcher [18] highlighted the importance of the calibration procedure used in the hardening model and how it can significantly influence analytical formability predictions. A constrained calibration must be performed to enforce the Considère criterion [24] for the beginning of diffuse necking in uniaxial tension, which occurs when the hardening rate is equivalent to the major principal stress such that Metals 2020, 10, 902 6 of 33 Failure to enforce the Considère constraint of Equation (2) upon the hardening model at the experimentally measured plastic strain for the uniform elongation will result in shifting of the FLC 0 in analytical formability models. It is particularly problematic for the MK model since the imperfection factor will then be adjusted to compensate for the shifted FLC 0 leading to a false conclusion that the imperfection factor has a strong dependence upon the hardening model. Butcher et al. [17] showed that the simple enforcement of the Considère constraint can effectively remove the dependence of the MK imperfection factor upon the selection of hardening model.
where σ is the flow stress, ε is the equivalent plastic strain, and C1-5 are calibration parameters.
The MHS coefficients were calibrated using a constrained least squares minimization in MATLAB ® software using the fmincon subroutine and are tabulated in Table 3. The Considère constraint of Equation (2) was enforced at the true plastic strain corresponding to the uniform elongation determined in the tensile tests stated in Table 1. The constraint was enforced to a tolerance of 1 × 10 −8 . A comparison of the MHS model calibrations with the tensile and converted shear data and the computed hardening rate are illustrated in Figure 3. It should be noted that since all of the formability tests were conducted in the TD, the hardening response was characterized in the TD. In the anisotropic yield function that uses the rolling direction as the reference, the TD hardening data was converted to the RD by the uniaxial stress ratios given in Table 2 and the MHS model coefficients are  provided in Table 3.     The present study has adopted the modified Hockett-Sherby (MHS) model of Noder and Butcher [18] in Equation (3) which is flexible enough to satisfy the constraint of Equation (2) and does not saturate at high strains like the regular Hockett-Sherby model. The MHS model is defined as where σ is the flow stress, ε is the equivalent plastic strain, and C 1-5 are calibration parameters. The MHS coefficients were calibrated using a constrained least squares minimization in MATLAB ® software using the fmincon subroutine and are tabulated in Table 3. The Considère constraint of Equation (2) was enforced at the true plastic strain corresponding to the uniform elongation determined in the tensile tests stated in Table 1. The constraint was enforced to a tolerance of 1 × 10 −8 . A comparison of the MHS model calibrations with the tensile and converted shear data and the computed hardening rate are illustrated in Figure 3. It should be noted that since all of the formability tests were conducted in the TD, the hardening response was characterized in the TD. In the anisotropic yield function that uses the rolling direction as the reference, the TD hardening data was converted to the RD by the uniaxial stress ratios given in Table 2 and the MHS model coefficients are provided in Table 3.

Calibration of the Yld2000 Anisotropic Yield Function
The choice of yield function was shown by Barlat [27] and Lian et al. [28] to significantly influence the MK formability predictions through the yield surface shape and the ratio of the yield strength in plane strain to equal-biaxial tension. The adoption of a quadratic yield surface tends to significantly overestimate the biaxial limit strains in the MK model. To account for the influence of anisotropy on the formability predictions, the non-quadratic plane stress Yld2000 model of Barlat et al. [29] was adopted for both 3rd Gen steels. The Yld2000 model contains eight calibration parameters, a 1-8 , and an exponent, m. For steels with a Body Centered Cubic (BCC) crystal structure an initial estimate for the yield exponent is 6. The equivalent stress in the Yld2000 model is where X i and X i " are the principal deviatoric stresses from two linear transformations defined by, X = L : σ and X = L : σ. The eight anisotropy parameters are embedded within the two fourth-order transformation tensors L and L . For brevity, the reader is referred to Barlat et al. [29] for a detailed description of the yield function and its derivation. Least squares optimization was performed in MATLAB ® with the twelve experimental data points in Table 2. The calibrated anisotropy parameters and yield exponents are tabulated for both steels in Table 4. Note that for the 3rd Gen 1180, better experimental agreement was obtained with a slightly lower yield exponent of 4.7 that correlated well with the study of Kuwabara and Nakajima [30] who used yield exponents ranging from 4-6 for DP980. A comparison of the calibrated yield surfaces with respect to the von Mises yield criteria is presented in Figure 4 along with the predictions of the tensile stress ratios and R-values in Figures 5 and 6, respectively. Although the Yld2000 model is over-constrained with more experimental data points than parameters, it is able to accurately describe the anisotropy of both steels with the exception of shear where the yield stress is underestimated. For the present study where the focus is on the prediction of formability in tensile loading, the error in the predicted shear stress is acceptable. Future work could consider more advanced yield functions such as the Drucker-based model by Yoshida et al. [31] to improve the overall accuracy in shear stress states.           The plane strain yield strength is important for the prediction of the FLC0. The normalized plane strain yield strengths were predicted by the Yld2000 model to be 1.11 and 1.146 for the 3rd Gen 980 and the 3rd Gen 1180 in the TD, respectively. For equal-biaxial stretching where no yield stress data was available, the predicted biaxial stress ratio was 0.995 and 1.005 for the 3rd Gen 980 and the 3rd Gen 1180, respectively.

Validation of the Hardening Model in Tensile Simulations
Accurate calibration of the hardening model is paramount for reliable model predictions of the material formability. To highlight the applicability of the experimentally-based method to obtain the hardening behavior to large strains using shear and tensile tests to the AHSS, the uniaxial tensile tests The plane strain yield strength is important for the prediction of the FLC 0 . The normalized plane strain yield strengths were predicted by the Yld2000 model to be 1.11 and 1.146 for the 3rd Gen 980 and the 3rd Gen 1180 in the TD, respectively. For equal-biaxial stretching where no yield stress data was available, the predicted biaxial stress ratio was 0.995 and 1.005 for the 3rd Gen 980 and the 3rd Gen 1180, respectively.

Validation of the Hardening Model in Tensile Simulations
Accurate calibration of the hardening model is paramount for reliable model predictions of the material formability. To highlight the applicability of the experimentally-based method to obtain the hardening behavior to large strains using shear and tensile tests to the AHSS, the uniaxial tensile tests were simulated with the identified hardening parameters in Table 3 using the Finite Element (FE) solver LS-DYNA ® (LSTC, Livermore, CA, USA) with an implicit time integration scheme. In order to capture the post-uniform behavior associated with strain localization, the specimen sheet thickness was discretized with a total of 10 fully integrated solid elements (Type-2 in LS-DYNA ® ), resulting in brick elements of 0.3 × 0.3 × 0.14 mm 3 . Unfortunately, the use of 3D elements to capture localization within the neck precludes the use of the plane stress Yld2000 model used in the formability predictions. For simplicity and in light of the mild tensile anisotropy in TD recorded in Table 2, the isotropic von Mises yield surface was adopted for the 3D tensile simulations. A velocity-controlled boundary condition with a test speed of 0.05 mm/s was applied and degrees of freedom in the specimen gripping area were constrained in accordance with clamping in the experiments.
Model predictions for both steels are shown in Figure 7 and were in good agreement with the global stress-strain response in the tests until just prior to fracture where the isotropic model did not capture localization as well. For the analytical prediction of formability, the hardening models obtained with the tensile and shear tests appears to be sufficiently accurate.
The plane strain yield strength is important for the prediction of the FLC0. The normalized plane strain yield strengths were predicted by the Yld2000 model to be 1.11 and 1.146 for the 3rd Gen 980 and the 3rd Gen 1180 in the TD, respectively. For equal-biaxial stretching where no yield stress data was available, the predicted biaxial stress ratio was 0.995 and 1.005 for the 3rd Gen 980 and the 3rd Gen 1180, respectively.

Validation of the Hardening Model in Tensile Simulations
Accurate calibration of the hardening model is paramount for reliable model predictions of the material formability. To highlight the applicability of the experimentally-based method to obtain the hardening behavior to large strains using shear and tensile tests to the AHSS, the uniaxial tensile tests were simulated with the identified hardening parameters in Table 3 using the Finite Element (FE) solver LS-DYNA ® (LSTC, Livermore, CA, USA) with an implicit time integration scheme. In order to capture the post-uniform behavior associated with strain localization, the specimen sheet thickness was discretized with a total of 10 fully integrated solid elements (Type-2 in LS-DYNA ® ), resulting in brick elements of 0.3 × 0.3 × 0.14 mm. Unfortunately, the use of 3D elements to capture localization within the neck precludes the use of the plane stress Yld2000 model used in the formability predictions. For simplicity and in light of the mild tensile anisotropy in TD recorded in Table 2, the isotropic von Mises yield surface was adopted for the 3D tensile simulations. A velocity-controlled boundary condition with a test speed of 0.05 mm/s was applied and degrees of freedom in the specimen gripping area were constrained in accordance with clamping in the experiments.
Model predictions for both steels are shown in Figure 7 and were in good agreement with the global stress-strain response in the tests until just prior to fracture where the isotropic model did not capture localization as well. For the analytical prediction of formability, the hardening models obtained with the tensile and shear tests appears to be sufficiently accurate.

Marciniak and Nakazima Tests
The Marciniak and Nakazima experiments were conducted in accordance with the ISO12004-2 standard to explore strain paths from approximately uniaxial to equal-biaxial stretching by varying the width of the test specimen from 25.4 mm to 203.2 mm, shown in Figure 8 and recorded in Table 5.
All specimens were extracted and tested in the TD.
Tool sets for both Marciniak and Nakazima tests correspond to the ISO 12004-2 standard with toolset dimensions shown in Figure 9. The Nakazima test uses a hemispherical punch with a 101.6 mm diameter whereas a cylindrical punch was used for the Marciniak test with the same diameter and 12 mm radius at the edge of the punch. The Nakazima tooling had a 106 mm inner diameter with a 6.35 mm entry radius and for the Marciniak tooling, a 119 mm inner diameter and a 16 mm die entry radius. The lockbead on both toolsets have a 4.7 mm height and a clamping force of 640 kN was adopted. For biaxial Marciniak tests done on 3rd Gen 1180, an alternate punch with a 25 mm profile radius was used due to the less ductile properties of 3rd Gen 1180 as radius fracture would occur with the standard punch. The punch velocity was 0.25 mm/s and layers of 0.1 mm thick circular Teflon ® sheets (two small circles and three large circles) lubricated with petrolatum were placed in between the sample and the punch to aid in promoting center fracture on the specimen. For the Marciniak tests, the Teflon ® sheets were placed between the punch and carrier blank.

Marciniak and Nakazima Tests
The Marciniak and Nakazima experiments were conducted in accordance with the ISO12004-2 standard to explore strain paths from approximately uniaxial to equal-biaxial stretching by varying the width of the test specimen from 25.4 mm to 203.2 mm, shown in Figure 8 and recorded in Table  5. All specimens were extracted and tested in the TD.  Table 5.
Tool sets for both Marciniak and Nakazima tests correspond to the ISO 12004-2 standard with toolset dimensions shown in Figure 9. The Nakazima test uses a hemispherical punch with a 101.6 mm diameter whereas a cylindrical punch was used for the Marciniak test with the same diameter and 12 mm radius at the edge of the punch. The Nakazima tooling had a 106 mm inner diameter with a 6.35 mm entry radius and for the Marciniak tooling, a 119 mm inner diameter and a 16 mm die entry radius. The lockbead on both toolsets have a 4.7 mm height and a clamping force of 640 kN was adopted. For biaxial Marciniak tests done on 3rd Gen 1180, an alternate punch with a 25 mm profile radius was used due to the less ductile properties of 3rd Gen 1180 as radius fracture would occur with the standard punch. The punch velocity was 0.25 mm/s and layers of 0.1 mm thick circular Teflon ® sheets (two small circles and three large circles) lubricated with petrolatum were placed in between the sample and the punch to aid in promoting center fracture on the specimen. For the Marciniak tests, the Teflon ® sheets were placed between the punch and carrier blank.  Table 5.  The choice of carrier blank is important for the Marciniak tests since they are used to achieve the in-plane stretching and promote localization of the blank over its central hole. A 0.9 mm thick 1004 cold-rolled mild steel (MS) that was sand-blasted was initially selected for the carrier blank material for both steels. The carrier blanks were square with a side length of 203.2 mm with a 32 mm diameter hole located in the center that was machined by laser cutting. However, due to the relatively high formability of the 3rd Gen 980, a more ductile stainless steel (SS) carrier blank (27 mm hole diameter and 1.2 mm sheet thickness) was selected for biaxial strain paths to inhibit premature failure at the hold edge. The carrier blank materials for each specimen width in the Marciniak tests are listed in Table 5.   The choice of carrier blank is important for the Marciniak tests since they are used to achieve the in-plane stretching and promote localization of the blank over its central hole. A 0.9 mm thick 1004 cold-rolled mild steel (MS) that was sand-blasted was initially selected for the carrier blank material for both steels. The carrier blanks were square with a side length of 203.2 mm with a 32 mm diameter hole located in the center that was machined by laser cutting. However, due to the relatively high formability of the 3rd Gen 980, a more ductile stainless steel (SS) carrier blank (27 mm hole diameter and 1.2 mm sheet thickness) was selected for biaxial strain paths to inhibit premature failure at the hold edge. The carrier blank materials for each specimen width in the Marciniak tests are listed in Table 5.

DIC Settings and Limiting Strain Methodology
Stereoscopic full-field DIC and the software Vic-3D 7 ® (Correlated Solutions Inc., Irmo, SC, USA) with a step size of 2, strain filter size of 9 pixels, a resolution of 0.057 mm/pixel and a subset of 35 pixels, corresponding to a VSGL of approximately 1.0 mm, were adopted for formability strain analysis. In order to capture a minimum of 300 images per test for both 3rd Gen steels, a frame rate of 5-6 images per second was utilized.
Limit Strain Detection: ISO12004-2 The DIC-based methodology within the ISO12004-2 was followed to determine the limit strains in all tests. For each specimen, five DIC line slices were extracted oriented perpendicular to the location of fracture where five limit strains were determined and averaged to determine the limit strain. The ISO12004-2 standard fits parabolas to the thickness strain and major strain distribution and uses volume conservation to acquire the minor strain. Consequently, the minor strain may not lie on the measured strain path at the necking location. In order to correct this inconsistency, the procedure by Noder and Butcher [18] was followed where the minor strain was selected from the measured DIC strain path when the major limit strain was reached. Figures 10 and 11 provide the strain path and superimposed limit strains obtained from Marciniak and Nakazima tests for both steel grades. The limiting strains for all tests are tabulated in Appendix A. Non-linear strain paths are evident from Nakazima tests shown in Figures 10a and 11a for which the hemispherical dome induces an equi-biaxial pre-stretch prior to transitioning to the target strain path. Contrary, tests performed with the flat Marciniak punch do not exhibit non-linearity in the strain path. procedure by Noder and Butcher [18] was followed where the minor strain was selected from the measured DIC strain path when the major limit strain was reached. Figures 10 and 11 provide the strain path and superimposed limit strains obtained from Marciniak and Nakazima tests for both steel grades. The limiting strains for all tests are tabulated in Appendix A. Non-linear strain paths are evident from Nakazima tests shown in Figure 10a,11a for which the hemispherical dome induces an equi-biaxial pre-stretch prior to transitioning to the target strain path. Contrary, tests performed with the flat Marciniak punch do not exhibit non-linearity in the strain path.

Fracture Modes
Localization within the Marciniak tests for both steels followed a similar trend; localization occurred at an angle in uniaxial tension and transitioned to be perpendicular to the principal stretching direction for plane strain to biaxial tension. The localization behavior in terms of the major principal strain prior to fracture is shown for the 3rd Gen 1180 AHSS in Figure 12. In the Nakazima tests, the hemispherical punch geometry promoted localization and fracture to occur perpendicular to the principal stretching direction for all test conditions. Figure 10. Strain paths to fracture superimposed with limit strains obtained using the ISO12004-2 standard for 3rd Gen 980 obtained from Nakazima tests (a) and Marciniak tests (b). Figure 11. Strain paths to fracture superimposed with limit strains obtained using the ISO12004-2 standard for 3rd Gen 1180 obtained from Nakazima tests (a) and Marciniak tests (b).

Fracture Modes
Localization within the Marciniak tests for both steels followed a similar trend; localization occurred at an angle in uniaxial tension and transitioned to be perpendicular to the principal stretching direction for plane strain to biaxial tension. The localization behavior in terms of the major principal strain prior to fracture is shown for the 3rd Gen 1180 AHSS in Figure 12. In the Nakazima tests, the hemispherical punch geometry promoted localization and fracture to occur perpendicular to the principal stretching direction for all test conditions. Cross-sections of the failed Marciniak samples for the two steels were then inspected for the fracture mode through an optical microscope. Specimens with a strain path of approximately uniaxial tension, plane strain tension, and balanced biaxial stretching are shown in Figure 13. The local thinning near the fracture surface for the 3rd Gen 980 steel is indicative of preceding necking prior to  Cross-sections of the failed Marciniak samples for the two steels were then inspected for the fracture mode through an optical microscope. Specimens with a strain path of approximately uniaxial tension, plane strain tension, and balanced biaxial stretching are shown in Figure 13. The local thinning near the fracture surface for the 3rd Gen 980 steel is indicative of preceding necking prior to fracture. Contrary, the 3rd Gen 1180 steel experienced significantly less necking and samples appear to have failed in a through-thickness shear fracture mode.

Process Corrections of the Limiting Strains
Direct comparison of analytical formability predictions under proportional in-plane stretching conditions in Section 5 requires the correction of the measured necking strains for process effects such as curvature, non-linear strain path, and through-thickness stress due to tool contact. Contrary to Nakazima tests, Marciniak tests do not require correction for contact pressure due to the presence of a carrier blank and curvature effects are negligible due to the use of the cylindrical punch. The strain paths in the Marciniak test are fairly linear (see Figures 10b and 11b) with the only non-linearity arising from the transition to plane strain tension during localization. Thus, the non-linear strain path corrections for the Marciniak tests are expected to be minor. For the Nakazima tests, the process effects can be significant and the methodology of Min et al. [19] was adopted for this study and will be summarized for brevity.
For simplicity, the elastic strains are neglected by assuming a rigid-plastic material such that the DIC strains are taken as plastic strains. In light of the large radius of the Nakazima punch and the thin sheet gauges of the steels considered, the strain gradient through the thickness of the sheet caused by bending is assumed to be a second-order effect with respect to the influence of the contact pressure and non-linear strain path (NLSP). A procedure to account for the influence of curvature in both the major and minor strain directions and its influence on the through-thickness strain gradient in Nakazima tests was provided by Min et al. [19]. For more severe bending scenarios, such as the adoption of smaller punch radii, curvature corrections should be considered. The small degree of curvature due to crowning of the blank in Marciniak tests was shown by Min et al. [19] to have a negligible influence on the through-thickness strain gradient. The critical layer of material for necking in the Nakazima tests was taken as the inner layer that is in contact with the punch that will experience a compressive stress that will delay localization. The convex (outer) surface of the blank is in plane stress while the inner layer is in a three-dimensional state of stress.
The instantaneous principal strain ratio, exp ρ , can readily be computed from the ratio of the

Process Corrections of the Limiting Strains
Direct comparison of analytical formability predictions under proportional in-plane stretching conditions in Section 5 requires the correction of the measured necking strains for process effects such as curvature, non-linear strain path, and through-thickness stress due to tool contact. Contrary to Nakazima tests, Marciniak tests do not require correction for contact pressure due to the presence of a carrier blank and curvature effects are negligible due to the use of the cylindrical punch. The strain paths in the Marciniak test are fairly linear (see Figures 10b and 11b) with the only non-linearity arising from the transition to plane strain tension during localization. Thus, the non-linear strain path corrections for the Marciniak tests are expected to be minor. For the Nakazima tests, the process effects can be significant and the methodology of Min et al. [19] was adopted for this study and will be summarized for brevity.
For simplicity, the elastic strains are neglected by assuming a rigid-plastic material such that the DIC strains are taken as plastic strains. In light of the large radius of the Nakazima punch and the thin sheet gauges of the steels considered, the strain gradient through the thickness of the sheet caused by bending is assumed to be a second-order effect with respect to the influence of the contact pressure and non-linear strain path (NLSP). A procedure to account for the influence of curvature in both the major and minor strain directions and its influence on the through-thickness strain gradient in Nakazima tests was provided by Min et al. [19]. For more severe bending scenarios, such as the adoption of smaller punch radii, curvature corrections should be considered. The small degree of curvature due to crowning of the blank in Marciniak tests was shown by Min et al. [19] to have a negligible influence on the through-thickness strain gradient. The critical layer of material for necking in the Nakazima tests was taken as the inner layer that is in contact with the punch that will experience a compressive stress that will delay localization. The convex (outer) surface of the blank is in plane stress while the inner layer is in a three-dimensional state of stress.
The instantaneous principal strain ratio, ρ exp , can readily be computed from the ratio of the second principal to the first principal strain measured from DIC. Adoption of an associated flow rule provides the principal in-plane normal stress ratio, α: The through-thickness stress ratio, χ, can be approximated from the equation provided by Min et al. [19] where R 1 and R 2 represent the principal curvature on the convex (outer) surface. Since strain localization for the two AHSS considered occurred at locations in close proximity to the specimen apex, the 50.8 mm Nakazima punch radius was selected for the curvature in both principal directions. Material thinning was approximated from Equation (8) where t 0 and t refer to the initial and instantaneous sheet thickness, respectively. The equivalent plastic strain, ε, at the initiation of necking can be computed by integration of the equivalent strain utilizing the incremental plastic work balance, where σ corresponds to the material flow stress and k represents the stress ratio of the first principal stress to the equivalent stress, σ eq , which is dependent upon the selection of yield function such that The strain-path corrected principal strains, ε linear 1 and ε linear 2 , are obtained through linearization of the equivalent plastic strain using the instantaneous stress and strain state when the limit strain is reached as ε linear In order to correct for the through-thickness stress caused by tool contact in the Nakazima test, Min et al. [19] adopted a phenomenological mapping from a 3D to a 2D stress state under the assumption of a constant in-plane stress ratio. The in-plane stress ratio of the triaxial stress state is utilized to determine the equivalent stress related to the in-plane stresses as, σ PS eq , in Equation (13). The corresponding equivalent plastic strain due to the in-plane loading, ε PS , is determined from inversion of the hardening law such that σ PS (ε PS ) = σ PS eq . An effective in-plane strain ratio, ρ PS , is then calculated based upon the flow rule using only the in-plane stress ratio as follows ρ PS (α) = dε 2 dε 1 = ∂σ PS eq /∂σ 2 ∂σ PS eq /∂σ 1 (14) The principal limit strains for the effective plane stress state are readily determined from decomposition of the equivalent plastic strain as This phenomenological mapping procedure of the limit strains between 3D and plane stress states under a constant in-plane stress ratio was first suggested by Smith et al. [32]. Matin and Smith [33] reported that the methodology is sensitive upon the selection of hardening model and Noder and Butcher [18] showed that materials with low hardening rates are predicted to have limit strains that are strongly dependent upon the contact stress.
In the process correction methodology, the influence of the NLSP effects are first removed followed by the contact pressure. As expected, the NLSP corrections in Marciniak tests are minor as seen in Figure 14. Given the small magnitude of the NLSP correction and when weighed against the additional complexity introduced into the analysis and error associated with assuming a yield function and flow rule to integrate the equivalent strain, the NLSP could be neglected for the Marciniak tests.
The principal limit strains for the effective plane stress state are readily determined from decomposition of the equivalent plastic strain as This phenomenological mapping procedure of the limit strains between 3D and plane stress states under a constant in-plane stress ratio was first suggested by Smith et al. [32]. Matin and Smith [33] reported that the methodology is sensitive upon the selection of hardening model and Noder and Butcher [18] showed that materials with low hardening rates are predicted to have limit strains that are strongly dependent upon the contact stress.
In the process correction methodology, the influence of the NLSP effects are first removed followed by the contact pressure. As expected, the NLSP corrections in Marciniak tests are minor as seen in Figure 14. Given the small magnitude of the NLSP correction and when weighed against the additional complexity introduced into the analysis and error associated with assuming a yield function and flow rule to integrate the equivalent strain, the NLSP could be neglected for the Marciniak tests. In contrast to the relatively linear in-plane deformation encountered in the Marciniak tests, Nakazima tests are characterized by out-of-plane stretching. Due to the hemispherical punch, initial deformation is approximately biaxial bending which shifts the limit strains such that the FLC0 does not occur at zero minor strain. The NLSP correction is on the order of up to 0.04 average major strain for both 3rd Gen AHSS shown in Figure 15. The limit strains are shifted up and to the left which restores the lowest limiting strains to occur at approximately zero minor strain in plane strain tension. In contrast to the relatively linear in-plane deformation encountered in the Marciniak tests, Nakazima tests are characterized by out-of-plane stretching. Due to the hemispherical punch, initial deformation is approximately biaxial bending which shifts the limit strains such that the FLC 0 does not occur at zero minor strain. The NLSP correction is on the order of up to 0.04 average major strain for both 3rd Gen AHSS shown in Figure 15. The limit strains are shifted up and to the left which restores the lowest limiting strains to occur at approximately zero minor strain in plane strain tension.
Due to tool contact in the Nakazima test, the limit strains need to be corrected for the induced stress through the sheet thickness. Figure 16 demonstrates that the pressure corrections can be quite significant with a reduction in the average major strain of 0.04 to 0.07 for the 3rd Gen 980 and 0.06-0.10 for the 3rd Gen 1180 with respect to the NLSP corrected limit strains. Referring to Figure 3b, the 3rd Gen 1180 exhibits a lower hardening rate relative to the 3rd Gen 980 that directly affects the pressure corrections owing to the inversion of the hardening law. Due to tool contact in the Nakazima test, the limit strains need to be corrected for the induced stress through the sheet thickness. Figure 16 demonstrates that the pressure corrections can be quite significant with a reduction in the average major strain of 0.04 to 0.07 for the 3rd Gen 980 and 0.06-0.10 for the 3rd Gen 1180 with respect to the NLSP corrected limit strains. Referring to Figure 3b, the 3rd Gen 1180 exhibits a lower hardening rate relative to the 3rd Gen 980 that directly affects the pressure corrections owing to the inversion of the hardening law. A direct comparison of the corrected limiting strains acquired from the Marciniak and Nakazima tests for both AHSS are shown in Figure 17. Overall, the process-corrected limiting strains of the two test methodologies are in good agreement, particularly around plane strain tension and on the draw side of the FLC.  Due to tool contact in the Nakazima test, the limit strains need to be corrected for the induced stress through the sheet thickness. Figure 16 demonstrates that the pressure corrections can be quite significant with a reduction in the average major strain of 0.04 to 0.07 for the 3rd Gen 980 and 0.06-0.10 for the 3rd Gen 1180 with respect to the NLSP corrected limit strains. Referring to Figure 3b, the 3rd Gen 1180 exhibits a lower hardening rate relative to the 3rd Gen 980 that directly affects the pressure corrections owing to the inversion of the hardening law. A direct comparison of the corrected limiting strains acquired from the Marciniak and Nakazima tests for both AHSS are shown in Figure 17. Overall, the process-corrected limiting strains of the two test methodologies are in good agreement, particularly around plane strain tension and on the draw side of the FLC. A direct comparison of the corrected limiting strains acquired from the Marciniak and Nakazima tests for both AHSS are shown in Figure 17. Overall, the process-corrected limiting strains of the two test methodologies are in good agreement, particularly around plane strain tension and on the draw side of the FLC.

MK Model
The well-known MK model is based upon deformation of a sheet metal in plane stress that has a thickness imperfection in the form of a band inclined at an angle, θ , visualized in Figure 18.
Deformation is proportional and homogeneous in the region outside of the imperfection band,

MK Model
The well-known MK model is based upon deformation of a sheet metal in plane stress that has a thickness imperfection in the form of a band inclined at an angle, θ, visualized in Figure 18. Deformation is proportional and homogeneous in the region outside of the imperfection band, denoted with subscript 'a', and the material inside the imperfection band, denoted with subscript 'b'. Deformation is prescribed upon the homogeneous zone and deformation within the band is governed by the equilibrium and compatibility equations at the boundary of the band that lead to where the components of stress and strain are denoted with a subscript, nn for normal to the band, tt, for tangential to the band and nt to denote shear in the band. The thickness imperfection factor, f, evolves with deformation as Localization has occurred when the equivalent plastic strain increment in the imperfection band is 10 times greater than the equivalent plastic strain in the homogenous zone. The Newton-Raphson solution procedure of Butuc [34] to integrate the MK model was adopted in the present work. For each proportional stress state, the limit strains were evaluated for band angles in 2 degrees increments and the lowest strains for all of the bend angles were taken as the limit strains. Predicted limit strains by the MK model can be highly sensitive to the selection of the imperfection factor as shown by Ratchev et al. [35]. Barlat and Jalinier [36] reported an imperfection factor of 0.996 to be reasonable based on imperfections of commercial sheet metals that was adopted in this study. The thickness imperfection factor can also be approximated from the surface roughness (refer to Table 1) which yielded an imperfection factor of 0.9992 and 0.9993 for the 3rd Gen 980 and the 3rd Gen 1180, respectively. The imperfection factor is often calibrated based upon a best-fit calibration to the FLC or can be calibrated using only the limit strain in plane strain using the solution of Soare [10]. These strategies are not considered in the present study because the MK predictions are no longer deterministic and require a priori knowledge of the limit strains. Predicted limit strains by the MK model can be highly sensitive to the selection of the imperfection factor as shown by Ratchev et al. [35]. Barlat and Jalinier [36] reported an imperfection factor of 0.996 to be reasonable based on imperfections of commercial sheet metals that was adopted in this study. The thickness imperfection factor can also be approximated from the surface roughness (refer to Table 1) which yielded an imperfection factor of 0.9992 and 0.9993 for the 3rd Gen 980 and the 3rd Gen 1180, respectively. The imperfection factor is often calibrated based upon a best-fit calibration to the FLC or can be calibrated using only the limit strain in plane strain using the solution of Soare [10]. These strategies are not considered in the present study because the MK predictions are no longer deterministic and require a priori knowledge of the limit strains.

MMFC Model
The MMFC model was proposed by Hora et al. [9] and is based upon the model of Swift [37] for the initiation of diffuse necking. Hora et al. [9] introduced a second term in Equation (21) to describe the change in the first principal stress with respect to the strain ratio to account for the change in the stress and strain state towards plane strain tension where an acute neck has formed such that The derivative of the major stress with respect to the strain ratio is The limit strains in the MMFC model are identified when the strain state has transitioned to plane strain tension corresponding to ρ = 0. The limit strains are therefore obtained under a non-linear path which is in contrast with the experimental limit strains that have been corrected for NLSP and process effects. This is an inconsistency in the MMFC model that does not appear in the MK model since the strains outside of the band are reported as the limit strains. Therefore, a linearized version of the MMFC model is required for consistency with the FLC test data and comparison with other analytical models. The average strain path was selected for linearization of the MMFC predictions by averaging the strain history ρ, that is computed by integrating the equivalent plastic strain as The average stress ratio, α, is then determined from the flow rule using ρ and the linearized principal strains are obtained following Equations (15) and (16).

Bressan-Williams-Hill Model
Bressan and Williams [21] postulated an instability criterion where localization occurs through the thickness of the sheet in plane stress biaxial stretching at the angle of zero-extension, φ, which correlated well with the post-test fracture surfaces for the 3rd Gen 1180 in Figure 13. The zero-extension direction during biaxial stretching is illustrated in Figure 19 where a strain transformation yields the through-thickness localization angle as correlated well with the post-test fracture surfaces for the 3rd Gen 1180 in Figure 13. The zeroextension direction during biaxial stretching is illustrated in Figure 19 where a strain transformation yields the through-thickness localization angle as In the BW model, it is assumed that the through-thickness instability will occur when the local shear stress reaches a critical shear stress as The critical shear stress is taken as a material constant. In the present study, the critical shear stress is identified in plane strain tension from the maximum force criterion of Swift [37] which is also identical to the solution of Hill [38] for plane strain tension. The formation of an acute neck in the zero-extension model of Hill [38] is predicted to occur when    In the BW model, it is assumed that the through-thickness instability will occur when the local shear stress reaches a critical shear stress as The critical shear stress is taken as a material constant. In the present study, the critical shear stress is identified in plane strain tension from the maximum force criterion of Swift [37] which is also identical to the solution of Hill [38] for plane strain tension. The formation of an acute neck in the zero-extension model of Hill [38] is predicted to occur when The critical shear stress for the BW model in Equation (27) is determined by evaluating Equation (28) in plane strain with α identified from the yield function corresponding to ρ = 0. The BW model is restricted to biaxial stress states so that Hill's [38] zero-extension model of Equation (28) is used for uniaxial stretching to form the so-called BWH model proposed by Alsos et al. [39]. Localized necking occurs in-plane at the zero-extension angle shown in Figure 18 and is denoted by BWx Model The BWH model is consistent in terms of its formulation based upon localization along the zero-extension direction but is inconsistent in that the limit strains in biaxial tension are based upon a critical shear stress whereas this parameter is excluded in uniaxial stretching. Therefore, we can propose a simple extension of the BW model, denoted as BWx, that also uses the critical shear stress for the draw side of the FLC instead of the Hill solution such that This BWx model could alternatively be viewed as a modification of the maximum normal stress model used by Hance and Huang [40] to predict the formability of 3rd Gen AHSS. The maximum normal stress model is equivalent to idealizing a stress-based FLC to be a flat line that is independent of the minor stress which is visualized in Figure 20a. To visualize the representation of the stress-based FLC in principal space, a power law hardening material with n = 0.15 and the von Mises yield function were arbitrarily adopted to generate Figure 20b. It is important to note that for plane stress states from uniaxial to biaxial tension, the maximum shear stress and maximum normal stress only differ by a factor of two, and thus would predict the same FLC if the model was defined in terms of the normal stress or shear stress. Therefore, we will refer to the model of Hance and Huang [40] as a maximum shear stress criterion for consistency with the BW model. The BWx model retains the critical shear stress for the draw side as done by Hance and Huang [40] but instead uses the BW model for biaxial stress states where localization occurs through-thickness. No new parameters are introduced into the BWx model. model used by Hance and Huang [40] to predict the formability of 3rd Gen AHSS. The maximum normal stress model is equivalent to idealizing a stress-based FLC to be a flat line that is independent of the minor stress which is visualized in Figure 20a. To visualize the representation of the stressbased FLC in principal space, a power law hardening material with n = 0.15 and the von Mises yield function were arbitrarily adopted to generate Figure 20b. It is important to note that for plane stress states from uniaxial to biaxial tension, the maximum shear stress and maximum normal stress only differ by a factor of two, and thus would predict the same FLC if the model was defined in terms of the normal stress or shear stress. Therefore, we will refer to the model of Hance and Huang [40] as a maximum shear stress criterion for consistency with the BW model. The BWx model retains the critical shear stress for the draw side as done by Hance and Huang [40] but instead uses the BW model for biaxial stress states where localization occurs through-thickness. No new parameters are introduced into the BWx model.

MK Model Predictions
The analytical FLC predicted by the MK model using the imperfection factor of 0.996 proposed by Barlat and Jalinier [36] can well describe the limit strains in biaxial stretch but underestimates the limit strains in uniaxial tension for both steels shown in Figure 21. Using alternate imperfection factors based on the surface roughness did not lead to improved predictions for either steel since the entire FLC was shifted upwards that led to a marked overprediction of the biaxial limit strains. A marginal increase in the draw side limit strains was observed but was not sufficient to appreciably improve the agreement. The larger effect of the choice of imperfection factor for biaxial strain paths relative to the draw side of the FLC was also noted by Chan et al. [41] and Ratchev et al. [35]. It has been reported in literature that MK model predictions on the draw side are significantly more sensitive upon strain-rate effects relative to the biaxial side [42]. Zhang et al. [43] reported a 73% increase in the limit strains for uniaxial tension whereas the biaxial FLC only increased by 12% when the strain rate index was increased from 0.01 to 0.04. For consistency with the other quasi-static analytical models considered in the study, no strain rate sensitivity has been included in the MK model.

MMFC Model Predictions
A comparison of the MMFC model by Hora et al. [9] and its linearized form is depicted in Figure 22. For both steels, the predicted FLC 0 limit strain is in very good agreement with the process-corrected limit strains. The differences between the two MMFC variants are prominent on biaxial stretching where the strains are largest and the NLSP effects are magnified. The MMFC predictions are somewhat higher and represent the upper limit of the experimental limit strains whereas the linearized version shows better correlation with the overall FLC trend for each material. Most importantly, the linearized version of the MMFC is more consistent with the underlying assumption of a linear strain path and does not introduce any calibration parameters into the model. been reported in literature that MK model predictions on the draw side are significantly more sensitive upon strain-rate effects relative to the biaxial side [42]. Zhang et al. [43] reported a 73% increase in the limit strains for uniaxial tension whereas the biaxial FLC only increased by 12% when the strain rate index was increased from 0.01 to 0.04. For consistency with the other quasi-static analytical models considered in the study, no strain rate sensitivity has been included in the MK model.

MMFC Model Predictions
A comparison of the MMFC model by Hora et al. [9] and its linearized form is depicted in Figure  22. For both steels, the predicted FLC0 limit strain is in very good agreement with the processcorrected limit strains. The differences between the two MMFC variants are prominent on biaxial stretching where the strains are largest and the NLSP effects are magnified. The MMFC predictions are somewhat higher and represent the upper limit of the experimental limit strains whereas the linearized version shows better correlation with the overall FLC trend for each material. Most importantly, the linearized version of the MMFC is more consistent with the underlying assumption of a linear strain path and does not introduce any calibration parameters into the model.

BWH and BWx Model Predictions
A comparison of the predicted FLC using the BWH and BWx models for each steel is shown in Figure 23. In biaxial tension for which both models are equivalent and follow the BW criterion, the predictions are conservative for the 3rd Gen 980 and excellent for the 3rd Gen 1180 steel. This is consistent with the experimental observations of the fracture modes in Section 3.3 where the 3rd Gen 1180 displayed marginal necking with through-thickness shear fracture compared to the 3rd Gen 980, which showed more necking. The MK model based on tensile localization was better able to predict the biaxial limiting strains for the 3rd Gen 980 and slightly overestimated the limit strains for the 3rd Gen 1180 AHSS.
On the draw side, the limit strains predicted by Hill's zero-extension criterion in the BWH model are similar to the MK model and significantly underestimated the formability of both steels. The BWx model predictions show a marked improvement over the Hill model, particularly for the 3rd Gen 1180. It is interesting that the rather simple BWx model can predict the FLC to such good agreement to be comparable to the more sophisticated MMFC and MK models. Overall, the BWx model appears to provide improved predictions on the draw side of the FLC compared to the BWH model and can accurately predict the biaxial limit strains for materials that exhibit a strong sensitivity to throughthickness localization such as the 3rd Gen 1180 steel. Otherwise, the predicted biaxial limit strains will be underpredicted using the BW model for materials that have more tensile localization and thinning such as the 3rd Gen 980 steel.

BWH and BWx Model Predictions
A comparison of the predicted FLC using the BWH and BWx models for each steel is shown in Figure 23. In biaxial tension for which both models are equivalent and follow the BW criterion, the predictions are conservative for the 3rd Gen 980 and excellent for the 3rd Gen 1180 steel. This is consistent with the experimental observations of the fracture modes in Section 3.3 where the 3rd Gen 1180 displayed marginal necking with through-thickness shear fracture compared to the 3rd Gen 980, which showed more necking. The MK model based on tensile localization was better able to predict the biaxial limiting strains for the 3rd Gen 980 and slightly overestimated the limit strains for the 3rd Gen 1180 AHSS.
On the draw side, the limit strains predicted by Hill's zero-extension criterion in the BWH model are similar to the MK model and significantly underestimated the formability of both steels. The BWx model predictions show a marked improvement over the Hill model, particularly for the 3rd Gen 1180. It is interesting that the rather simple BWx model can predict the FLC to such good agreement to be comparable to the more sophisticated MMFC and MK models. Overall, the BWx model appears to provide improved predictions on the draw side of the FLC compared to the BWH model and can accurately predict the biaxial limit strains for materials that exhibit a strong sensitivity to through-thickness localization such as the 3rd Gen 1180 steel. Otherwise, the predicted biaxial limit strains will be underpredicted using the BW model for materials that have more tensile localization and thinning such as the 3rd Gen 980 steel.
to be comparable to the more sophisticated MMFC and MK models. Overall, the BWx model appears to provide improved predictions on the draw side of the FLC compared to the BWH model and can accurately predict the biaxial limit strains for materials that exhibit a strong sensitivity to throughthickness localization such as the 3rd Gen 1180 steel. Otherwise, the predicted biaxial limit strains will be underpredicted using the BW model for materials that have more tensile localization and thinning such as the 3rd Gen 980 steel.

Discussion
Three analytical models to predict the FLC using only material property data have been evaluated for both 3rd Gen AHSS. It is now instructive to compare the most successful variants of each model to evaluate their predictive accuracy. To draw conclusions on the models across a larger data set, an aluminum alloy, AA5182, and a dual phase steel, DP980, characterized by Noder and Butcher [18] will also be revisited with the linearized MMFC, MK model, and the BWx model. The AA5182 will be shown to be provide an interesting counterpart to the three AHSS as a consequence of its saturation-type behavior at large strains and higher or non-quadratic yield functions representative of a Tresca-type yield function.

Comparison of Analytical FLC Predictions for 3rd Gen AHSS
A comparison of the three analytical models with the in-plane limit strain data is presented in Figures 24 and 25 for the 3rd Gen 980 and the 3rd Gen 1180, respectively.

Discussion
Three analytical models to predict the FLC using only material property data have been evaluated for both 3rd Gen AHSS. It is now instructive to compare the most successful variants of each model to evaluate their predictive accuracy. To draw conclusions on the models across a larger data set, an aluminum alloy, AA5182, and a dual phase steel, DP980, characterized by Noder and Butcher [18] will also be revisited with the linearized MMFC, MK model, and the BWx model. The AA5182 will be shown to be provide an interesting counterpart to the three AHSS as a consequence of its saturation-type behavior at large strains and higher or non-quadratic yield functions representative of a Tresca-type yield function.

Comparison of Analytical FLC Predictions for 3rd Gen AHSS
A comparison of the three analytical models with the in-plane limit strain data is presented in Figures 24 and 25 for the 3rd Gen 980 and the 3rd Gen 1180, respectively. In biaxial stretching, the MK and linearized MMFC models predicted similar limit strains that are in excellent agreement with the experiment values while the BWx model systematically underpredicted the biaxial limit strains. On the draw side of the FLC, the MK model predictions are conservative while the MMFC and BWx models can both predict the limit strains within the variation of the test data. While the MMFC and BWx models both accurately predict the FLC0 from the diffuse necking limit in plane strain, the MK model will always predict a lower FLC0 value due to the imperfection factor [10].
For the 3rd Gen 1180 AHSS, the BWx and the linearized MMFC models provided the best overall  In biaxial stretching, the MK and linearized MMFC models predicted similar limit strains that are in excellent agreement with the experiment values while the BWx model systematically underpredicted the biaxial limit strains. On the draw side of the FLC, the MK model predictions are conservative while the MMFC and BWx models can both predict the limit strains within the variation of the test data.
While the MMFC and BWx models both accurately predict the FLC 0 from the diffuse necking limit in plane strain, the MK model will always predict a lower FLC 0 value due to the imperfection factor [10].
For the 3rd Gen 1180 AHSS, the BWx and the linearized MMFC models provided the best overall agreement while the MK significantly underestimated the draw side limit strains and slightly overestimated the biaxial strains. The simple BWx model was able to accurately describe the FLC which is consistent with the observed sensitivity of the 3rd Gen 1180 to shear failure. The MMFC and MK models that cannot account for through-thickness shear failure both tended to overestimate the biaxial limit strains as a result. However, the MMFC model did provide accurate predictions on the draw side of the FLC while the MK predictions were very conservative, which might be attributed to the absence of a strain-rate dependent constitutive model.

Application to DP980 and AA5182
To evaluate the proposed framework for FLC characterization and prediction to a larger range of automotive alloys, the AA5182 aluminum and DP980 AHSS of Noder and Butcher [18] who reported Marciniak and process-corrected Nakazima FLC data, are revisited. The limit strains were determined from a modified linear best fit (LBF) method by Volk and Hora [44].
Detailed characterization data for plastic anisotropy for the two alloys was not provided so the DP980 is assumed to follow the isotropic Hosford yield criterion with an exponent of 6 and an exponent of 8 for the AA5182. The AA5182 hardening model was calibrated to strain levels beyond the diffuse necking limit obtained in tensile tests while reflecting the plastic uniform elongation using the modified Generalized Voce model defined as The MHS model hardening model in Equation (3) was used for the DP980 steel. The calibrated material coefficients are summarized in Tables 6 and 7.

3rd Gen 1180
Process corrected limting strains Figure 25. Analytical FLC variants with the best overall agreement overlaid with process-corrected limiting strains for 3rd Gen 1180.

Application to DP980 and AA5182
To evaluate the proposed framework for FLC characterization and prediction to a larger range of automotive alloys, the AA5182 aluminum and DP980 AHSS of Noder and Butcher [18] who reported Marciniak and process-corrected Nakazima FLC data, are revisited. The limit strains were determined from a modified linear best fit (LBF) method by Volk and Hora [44].
Detailed characterization data for plastic anisotropy for the two alloys was not provided so the DP980 is assumed to follow the isotropic Hosford yield criterion with an exponent of 6 and an exponent of 8 for the AA5182. The AA5182 hardening model was calibrated to strain levels beyond the diffuse necking limit obtained in tensile tests while reflecting the plastic uniform elongation using the modified Generalized Voce model defined as The MHS model hardening model in Equation (3) was used for the DP980 steel. The calibrated material coefficients are summarized in Tables 6 and 7.  The critical shear stress in the BWx model was also determined from the hardening model and assumed yield functions of the DP980 and AA5182. The same MK imperfection factor of 0.996 was also employed and the MMFC model contains no calibration parameters.
The FLC predictions of the three models for the DP980 are consistent with the observations for the 3rd Gen AHSS as shown in Figure 26. On the draw side, the MMFC and BWx models provide excellent agreement with the limit strains whereas the MK model is very conservative. For biaxial stretching, all of the models predict similar limit strains that are in good overall agreement with the measured limit strains. The BWx model is slightly conservative with the linearized MMFC providing the best overall predictions. For AHSS, the linearized MMFC appears to be preferable or the simple BWx if the steel is sensitive to through-thickness shear fracture in biaxial stretching. The MK model systematically underestimated the draw side of the FLC for the three AHSS considered in the paper and is better suited for the biaxial limit strains.
Metals 2020, 10, x FOR PEER REVIEW 26 of 34 measured limit strains. The BWx model is slightly conservative with the linearized MMFC providing the best overall predictions. For AHSS, the linearized MMFC appears to be preferable or the simple BWx if the steel is sensitive to through-thickness shear fracture in biaxial stretching. The MK model systematically underestimated the draw side of the FLC for the three AHSS considered in the paper and is better suited for the biaxial limit strains. Figure 26. Comparison of the linearized MMFC, the MK model, and the extended BWx model with the process-corrected limiting strains for DP980. Note that the limit strains were obtained from Noder and Butcher (2019) [18].
A comparison of the predicted FLCs for the AA5182 is presented in Figure 27. The linearized MMFC model did not predict the aluminum FLC as accurately as it did for the AHSS. The shape of the FLC does not resemble the experimental FLC and the limit strains are systematically overestimated. For the AA5182, the termination criterion of the MMFC model based on the strain path reaching plane strain appears problematic although it worked very well for the three AHSS considered. It is possible that this can be attributed to the omission of strain-rate sensitivity in the analysis. AHSS have positive rate sensitivity that stabilizes the neck and slows the transition to plane strain. The termination criterion of reaching plane strain while neglecting rate dependence may be offsetting the error for the AHSS within the MMFC model such that good limit strain predictions were still obtained. For the AA5182, which has been reported to exhibit negative rate sensitivity at room temperature [45], the localization process would be accelerated and the termination criterion of reaching a plane strain condition may not be appropriate.
In contrast to the MMFC model, the MK and BWx models are both able to predict the FLC of the AA5182 with excellent agreement in biaxial stretching. The limit strains generated by the MK model in the biaxial region are widely known to be dependent upon the yield exponent and in particular the ratio of the plane strain yield strength to the biaxial yield strength [27]. The high yield exponent of 8 for the aluminum in the Hosford model reduces this critical ratio compared to the quadratic von Mises yield function and enabled the correct prediction of the shape and magnitude of the FLC in

DP980
Process corrected limiting strains Figure 26. Comparison of the linearized MMFC, the MK model, and the extended BWx model with the process-corrected limiting strains for DP980. Note that the limit strains were obtained from Noder and Butcher (2019) [18].
A comparison of the predicted FLCs for the AA5182 is presented in Figure 27. The linearized MMFC model did not predict the aluminum FLC as accurately as it did for the AHSS. The shape of the FLC does not resemble the experimental FLC and the limit strains are systematically overestimated. For the AA5182, the termination criterion of the MMFC model based on the strain path reaching plane strain appears problematic although it worked very well for the three AHSS considered. It is possible that this can be attributed to the omission of strain-rate sensitivity in the analysis. AHSS have positive rate sensitivity that stabilizes the neck and slows the transition to plane strain. The termination criterion of reaching plane strain while neglecting rate dependence may be offsetting the error for the AHSS within the MMFC model such that good limit strain predictions were still obtained. For the AA5182, which has been reported to exhibit negative rate sensitivity at room temperature [45], the localization process would be accelerated and the termination criterion of reaching a plane strain condition may not be appropriate.

Conclusions
From the current study of three variants of AHSS and a disparate aluminum alloy, an objective and deterministic approach to analytically predict forming limit strains has been developed. Different variants of the commonly used analytical FLC models for in-plane stretching were considered with modifications proposed for the MMFC and BW models to improve their predictive accuracy without adding new calibration parameters. Only mechanical property data from tensile and shear tests was required to objectively predict the FLC for in-plane stretching to avoid calibration bias. The following conclusions can be drawn from this study: 1. Finite element simulations of uniaxial tensile tests confirmed that the experimental shear conversion methodology proposed by Rahmaan et al. [20] provides a reliable technique to accurately obtain the material hardening response of AHSS to large strains that is suitable for formability prediction. 2. Nakazima forming limit curves should be corrected for process effects associated with outof-plane deformation to be consistent with analytical formability models for proportional plane stress loading. 3. The MK model, when evaluated deterministically using an assumed imperfection factor of 0.996, predicted the biaxial limit strains to good agreement but were too conservative for the uniaxial tension of the three AHSS. The best performance of the MK model was found for the AA5182 aluminum. 4. The BWH model was found to be unsatisfactory on the draw side of the FLC due to its reliance upon the Hill model. The proposed extension to the BW model to employ the maximum shear stress criterion on the draw side (BWx model) led to superior formability predictions without adding any new parameters. Aside from its simplicity, the BWx model is particularly attractive for materials sensitive to through-thickness shear such as the 3rd Gen 1180 and performed well for AA5182. 5. Among the studied analytical models, the linearized MMFC [9] proposed in this study showed a superior correlation with experiments for the three AHSS but overestimated the formability of the AA5182. The predicted necking strain in the MMFC was linearized over the average strain path to be more consistent with the process-corrected forming limit strains for in-plane stretching.

AA5182
Process corrected limiting strains Figure 27. Comparison of the linearized MMFC, the MK model, and the extended BWx model with the process-corrected limiting strains for AA5182. Note that the limit strains were obtained from Noder and Butcher (2019) [18].
In contrast to the MMFC model, the MK and BWx models are both able to predict the FLC of the AA5182 with excellent agreement in biaxial stretching. The limit strains generated by the MK model in the biaxial region are widely known to be dependent upon the yield exponent and in particular the ratio of the plane strain yield strength to the biaxial yield strength [27]. The high yield exponent of 8 for the aluminum in the Hosford model reduces this critical ratio compared to the quadratic von Mises yield function and enabled the correct prediction of the shape and magnitude of the FLC in biaxial stretching. Similarly, the BWx model also captures this effect since there will be a smaller difference in the limit strains based on a critical shear stress as the yield surface becomes flatter with higher exponents. On the draw side of the FLC there is some variation within the measured limit strains with both the BWx and MK models describing the upper and lower bounds of the data, respectively. Although additional aluminum alloys should be investigated to support these conclusions, the MK and BWx models appear to be preferable for the aluminum while the linearized MMFC and BWx performed well for the AHSS with the MK better suited for the biaxial limit strains.

Conclusions
From the current study of three variants of AHSS and a disparate aluminum alloy, an objective and deterministic approach to analytically predict forming limit strains has been developed. Different variants of the commonly used analytical FLC models for in-plane stretching were considered with modifications proposed for the MMFC and BW models to improve their predictive accuracy without adding new calibration parameters. Only mechanical property data from tensile and shear tests was required to objectively predict the FLC for in-plane stretching to avoid calibration bias. The following conclusions can be drawn from this study:

1.
Finite element simulations of uniaxial tensile tests confirmed that the experimental shear conversion methodology proposed by Rahmaan et al. [20] provides a reliable technique to accurately obtain the material hardening response of AHSS to large strains that is suitable for formability prediction.

2.
Nakazima forming limit curves should be corrected for process effects associated with out-of-plane deformation to be consistent with analytical formability models for proportional plane stress loading. 3.
The MK model, when evaluated deterministically using an assumed imperfection factor of 0.996, predicted the biaxial limit strains to good agreement but were too conservative for the uniaxial tension of the three AHSS. The best performance of the MK model was found for the AA5182 aluminum. 4.
The BWH model was found to be unsatisfactory on the draw side of the FLC due to its reliance upon the Hill model. The proposed extension to the BW model to employ the maximum shear stress criterion on the draw side (BWx model) led to superior formability predictions without adding any new parameters. Aside from its simplicity, the BWx model is particularly attractive for materials sensitive to through-thickness shear such as the 3rd Gen 1180 and performed well for AA5182.

5.
Among the studied analytical models, the linearized MMFC [9] proposed in this study showed a superior correlation with experiments for the three AHSS but overestimated the formability of the AA5182. The predicted necking strain in the MMFC was linearized over the average strain path to be more consistent with the process-corrected forming limit strains for in-plane stretching.

Conflicts of Interest:
The authors declare no conflict of interest.   Table A7. Forming limit strains and process corrected limit strains for the 152.4 mm wide 3rd Gen 980 samples.   Table A15. Forming limit strains and process corrected limit strains for the 139.7 mm wide 3rd Gen 1180 samples.