{'fraction_non_alphanumeric': 0.0372820558054747, 'fraction_numerical': 0.020699185557613714, 'mean_word_length': 4.868184955141477, 'pattern_counts': {'":': 0, '<': 0, '<?xml version=': 0, '>': 0, 'https://': 0, 'lorem ipsum': 0, 'www.': 0, 'xml': 0}, 'pii_count': 0, 'substrings_counts': 0, 'word_list_counts': {'cursed_substrings.json': 1, 'profanity_word_list.json': 0, 'sexual_word_list.json': 0, 'zh_pornsignals.json': 0}}
3D-printing of dynamic self-healing cryogels with tuneable properties†

We report a novel synthetic and processing methodology for the preparation of doubly dynamic, selfhealing, 3D-printable macroporous gels. 3D-printable oxime hydrogels were prepared by cross-linking poly(n-hydroxyethyl acrylamide-co-methyl vinyl ketone) (PHEAA-co-PMVK) with a bifunctional hydroxylamine. 3D-printed oxime hydrogels were subjected to post-printing treatment by thermally induced phase separation (TIPS), which facilitated the formation of hydrogen bonding and oxime cross-links, and dramatically increased the mechanical strength of soft oxime objects in a well-controlled manner by up to ∼1900%. The mechanical properties of the cryogels were tuned by freezing conditions, which affected the microstructure of the cryogels. These doubly dynamic 3D-printed cryogels are macroporous, exhibit outstanding swelling performances, and can fully, rapidly and autonomously self-heal.


Introduction
Self-healing materials possess a unique capability to recover from damage, thereby restoring their structure and function. Owing to their self-healing properties these nature-mimicking materials also derive the benefit of a prolonged lifetime and offer alternative solutions for damage repair. 1,2 The development of self-healing materials has attracted a lot of attention, [2][3][4][5] however, very few studies focus on their processability. 6,7 Three-dimensional printing (3DP) has emerged as a promising technology for advanced manufacturing of objects fabricated layer-by-layer from a digital model. [8][9][10] Potential applications of 3DP have been successfully explored in a myriad fields, such as tissue engineering, [11][12][13][14] catalysis, 15 actuation, 16 and sensing. 17 To expand the utility of 3DP, development of new printable materials is highly desirable and is becoming a topic of significant scientific interest. 10,15 A particularly intriguing group of materials is functional hydrogels. These materials can be exploited as actuators and shape morphing devices, 6,16,18 act as biomimetic tissue engineering scaffolds, 8,11,12,14 or exhibit self-healing capabilities. 6 Retaining large volumes of solvent, these 3D polymer networks are usually prone to poor mechanical robustness. 2,19 Moreover, 3DP by commonly used extrusion-based technologies imposes additional restrictions on the mechanical strength and structural integrity of 3D-printed gels, making this process extremely challenging. 6 To be extrusion compliant, inks must be formulated within a well-specified rheological parameter range, 6,9,12 making them even less versatile and softer than their non-printable analogues. To overcome these limitations, numerous techniques have been developed to reinforce soft 3D-printed objects. Well-known approaches include secondary ( post-printing) cross-linking with ultraviolet (UV) light, 8,11,12,14 chemical or physical cross-linking by covalent or ionic cross-linkers, 6,8,19 evaporation induced curing, 20 and thermally induced gelation. 21,22 Despite their popularity, these methods rely on the addition of external compounds, such as photo-initiators or small molecules, 8 or require a sophisticated design of polymers, which can exhibit concentration or temperature triggered self-assembly. [20][21][22] Herein, we explore thermally induced phase separation (TIPS) as a post-printing reinforcement technique, which enables the fabrication of macroporous 3D-printed objects. Post-printing freeze-thaw cycles induce thermodynamically driven cross-linking of the polymer rich phase, resulting in well-controlled mechanical stabilization of soft gels. The macroporous structure of cryogels contributes to their improved mechanical strength. 23 Recently, TIPS in combination with 3DP was reported as a useful approach to tailor the surface morphology of polymeric scaffolds. 24 In this work, TIPS is explored as a novel tool for post-printing reinforcement of soft 3D-printable gels. More importantly, the mechanical properties of these self-healing cryogels are tuneable and can be modulated via the conditions of the freeze-thaw process. We design a doubly dynamic self-healing network by the synthesis of poly(n-hydroxyethyl acrylamide-co-methyl vinyl ketone) (PHEAA-co-PMVK). The ketone groups are harnessed to form oxime bonds with a bifunctional hydroxylamine crosslinker, and therefore enable the formation of stable dynamic covalent bonds, making the gel self-healable. PHEAA has been chosen owing to its excellent water solubility, eliminating the need for organic solvents. More importantly, the amide and the hydroxyl groups of HEAA units have a strong ability to form hydrogen bonds, which enable physical cross-linking during TIPS and make the self-healing cryogels doubly dynamic. First, oxime gels are formed. These soft self-healing gels can fully and autonomously recover from damage, 3,25 and are 3D-printable. Post-printing TIPS treatment makes these gels doubly dynamic by facilitating the formation of hydrogen bonds, and improves the mechanical robustness of the soft objects in a well-controlled manner.

Instrumentation
Size exclusion chromatography (SEC) was performed on a Shimadzu Liquid Chromatography system equipped with a Shimadzu RID-10 refractometer (λ = 633 nm) and a Wyatt 3-angle light scattering detector, with three Waters Ultrahydrogel columns in series ((i) 250 Å porosity, 6 μm diameter bead size; (ii) and (iii) linear, 10 μm diameter bead size) for separation. Milli-Q water with 0.1 vol% TFA was used as an eluent. Average molecular weights (M n and M w ) and the polydispersity index (Đ) were calculated based on polyethylene glycol calibration standards. Nuclear Magnetic Resonance ( 13 C-and 1 H-NMR) was performed on a Varian 400 MHz spectrometer. A refrigerated thermostatic bath (Alpha RA series) filled with water and ethylene glycol was operated at −10°C or −20°C for gel freezing. Rheological studies were conducted on a controlled stress rheometer with 40 mm diameter parallel plate geometry (AR-G2, TA Instruments). For 3Dprinting, a 3D-Bioplotter (Developer Series, EnvisionTec, Germany) with Bioplotter RP software for file processing was used. Printing parameters: ambient temperature printing with 0.6 mm nozzle diameter, pressure of 4.0 bar, print head speed: 7.0 mm s −1 , or high temperature printing (80°C) with 0.4 mm nozzle diameter, pressure of 3.0 bar, print head speed: 12.0 mm s −1 . Fourier transform infrared (FTIR) spectroscopy was performed on a Varian 7000 model, ATR mode. Confocal laser scanning microscopy (CLSM) was performed on a Nikon A1R+ microscope with a 40× objective using a laser excitation wavelength of 561 nm. Data analysis was conducted with NIS elements viewer software. Thermogravimetric analysis (TGA) was conducted on a PerkinElmer Diamond instrument (Pyris Diamond TG-DTA).

Synthesis of PHEAA-co-PMVK
PHEAA-co-PMVK was synthesized by free radical polymerization. HEAA (3.0 g, 26.057 mmol), MVK (1.9 g, 27.464 mmol) and AIBN (0.007 g, 0.0426 mmol) were combined in a 100 mL round bottom flask and sealed with a rubber septum. The mixture was placed in an ice bath, degassed by nitrogen bubbling for ∼30 min, sealed under nitrogen and placed in an oil bath heated to 60°C. The mixture was left to react with stirring for 17 h. The reaction was quenched by placing the flask in an ice bath. The solid-like contents of the flask were diluted with methanol and precipitated into diethyl ether. The product was collected, dried, and dissolved in deionized water. The aqueous solution was dialyzed, followed by freeze-drying, after which a solid product was obtained.

Synthesis of tetraethylene glycol bishydroxylamine (TEG-BHA)
The synthesis was performed according to a reported procedure. 26 Preparation of 3D-printable self-healing oxime gels (G oxime ) PHEAA-co-PMVK (1.0 g, 10.44 mmol) was dissolved in 10.0 mL deionized water and allowed to stir at room temperature until a fully homogeneous solution was obtained. TEG-BHA (6.0 mg, 0.02 mmol) was slowly introduced to the polymer solution under rigorous stirring and mixed for 10 min. The gelation was indicated by a standard inversion test.
Preparation of self-healing oxime gels with alternating degrees of cross-linking For the preparation of oxime cross-linked gels, PHEAA-co-PMVK (0.1 g, 1.04 mmol) was dissolved in 1.0 mL deionized water and allowed to stir at room temperature until a fully homogeneous solution was obtained. TEG-BHA (0.9 mg, 0.003 mmol) was slowly introduced to the polymer solution under rigorous stirring and mixed for 10 min. To obtain a lower degree of cross-linking, PHEAA-co-PMVK (0.1 g, 1.04 mmol) was dissolved in 0.9 mL deionized water and allowed to stir at room temperature until a fully homogeneous solution was obtained. TEG-BHA (3.0 mg, 0.01 mmol) was dissolved in 1.0 mL deionized water. Afterwards, 0.1 mL of TEG-BHA solution was introduced to the PHEAA-co-PMVK solution, stirred and allowed to set.
The gelation of the samples was indicated by a standard inversion test.
Preparation of doubly dynamic self-healing cryogels 0.7 mL fractions of freshly prepared G oxime were loaded into a syringe and cast into glass vials to form uniform gel discs (diameter: 20.0 mm, thickness: 5.0 mm). The vials were sealed and allowed to stabilize overnight at ambient temperature. After overnight solidification, the gels were transferred to a cooling bath set to −10°C or −20°C for 24 h. Afterwards, the gels were removed from the bath and allowed to thaw for 3 h at room temperature. Each freeze-thaw cycle was repeated as specified. These conditions were applied unless stated otherwise.
For the study of the effect of cryogelation time on the mechanical properties of the gels, each freezing cycle was conducted at −10°C for 4 h, followed by thawing at room temperature for 3 h.

Rheological characterization
A time sweep was applied to measure the storage and loss modulus of the gels. The measurements were conducted at a constant temperature of 25°C, an angular frequency of 6.283 rad s −1 , and 0.5% strain. 6 The measurements were repeated in triplicate. The degree of reinforcement (R) was evaluated using formula (1): where G′ n represents the average storage modulus of a gel after n freeze-thaw cycles, and G′ 0 represents the initial storage modulus of G oxime (without freeze-thaw treatment). The self-healing characteristics of the gel were assessed using an increased strain ramp conducted at 25°C and an angular frequency of 6.283 rad s −1 . The flow properties of the gel (shear moduli as a function of stress, and apparent viscosity) were determined at 25 and 80°C and an angular frequency of 6.283 rad s −1 . A gelation kinetic study of G oxime was conducted by dissolving 0.1 g of PHEAA-co-PMVK in 1.0 mL deionized water. Afterwards, 0.6 mg of TEG-BHA was added to the vial and stirred for a few minutes until fully homogenized. The contents of the vial were immediately transferred to the rheometer plate, followed by time sweep experiments conducted at 25°C, 0.5% strain and an angular frequency of 6.283 rad s −1 .
Frequency sweep was performed by examining the gel in the range of 0.01-10.0 Hz at 25°C and 1.0% strain.

Mechanical testing 27
Compression tests were performed on an Instron (Micro Tester 5848) equipped with a 5.0 kg load cell. Gel samples (20.0 mm diameter, 5.0 mm thickness) were placed between the compression discs and deformed at a constant strain rate of 60% per minute. Young's (compression) modulus was extracted from stress-strain curves, by determining the slope of the curves in the low strain linear region (0-10% strain). 27 All the measurements were performed 3 times.

Degree of swelling
The gels were dried under vacuum for 24 h, until no further change in their weight was observed. The weight of the samples was monitored. After drying, the gels were submerged in deionized water overnight, gently wiped to remove excess surface water and weighed. The degree of swelling (S) was calculated according to formula (2): 19,27 where W d and W s represent the weight of the dry and the swollen gels, respectively.
To examine the effect of pH on the degree of swelling, the same procedure was repeated with an acid (aqueous HCl solution, pH = 4.5) and a base (aqueous KOH solution, pH = 8.5) instead of deionized water.

Porosity
The evaluation of porosity (P) was performed using the solvent replacement method. 28 Briefly, the gels were dried under vacuum to constant weight. The dry weight was monitored. Afterwards, the dry gels were submerged in absolute ethanol overnight, wiped to remove excess solvent and weighed.
The porosity was calculated according to formula (3): where W d and W s are the weight of the dry and the swollen gel, respectively, V is the volume of the gel, and ρ is the density of absolute ethanol.

Morphological characterization
The morphology of the gels was characterized by CLSM to retain the hydrated state of the gels and to prevent pore collapse under vacuum. The gels were soaked in an aqueous solution of Rhodamine B (0.09 mg mL −1 ) overnight. Afterwards, the gels were soaked in a deionized water reservoir and thoroughly washed several times to remove any excess dye. The pore size and wall thickness of the cryogels (average ± stdev) were analysed using the NIS elements software.
3D-printing of G oxime G oxime was loaded into a disposable syringe equipped with a 0.6 mm nozzle and compressed until a good contact between the gel and the lid of the syringe was obtained and air evacuated. The syringe was placed into the 3D-Bioplotter machine, followed by standard purging and calibration procedures. Printing conditions ( print head speed and pressure combination) were optimized to produce a stable, continuous and shape retaining filament strand (optimal printing conditions: 4.0 bar pressure, 7.0 mm s −1 print head speed, 25°C). In addition to ambient conditions, G oxime was also printed at 80°C (stainless steel cartridge was used instead of a disposable plastic syringe). Optimal printing parameters: 0.4 mm nozzle diameter, 3.0 bar pressure, 12 mm s −1 printing speed.
Post-printing (secondary) reinforcement by TIPS G oxime scaffolds (100% infill, 2.0 cm diameter, 0.5 cm thickness) were 3D-printed onto a glass slide and placed on the bottom of a glass vessel. After sealing, the vessel was placed in a thermoset controlled water bath set to −10°C or −20°C and subjected to a specified number of freeze-thaw cycles.

Thermal stability analysis
The thermal stability of PHEAA-co-PMVK was assessed by TGA. 6.9 mg of PHEAA-co-PMVK were placed in an alumina crucible and the sample was heated at a constant rate of 10°C min −1 from 40°C to 600°C under a nitrogen flow of 200 mL min −1 .

Results and discussion
Engineering doubly dynamic, self-healing and 3D-printable gels requires a strategic design of a polymer system with mul-tiple functionalities and well-defined properties. A facile free radical copolymerization of cheap and accessible HEAA with MVK (∼40% yield, M n = 284 kDa, Đ = 2.39) enabled the synthesis of a multi-functional platform in which the ketone groups of MVK act as reactive sites to form oxime cross-links (see Fig. S1-S3 † for the 1 H-NMR and 13 C-NMR of PHEAA-co-PMVK, Fig. S4 † for SEC traces of PHEAA-co-PMVK, and Fig. S5 † for 1 H-NMR and a detailed synthesis procedure of TEG-BHA). Oxime chemistry has been chosen owing to its high hydrolytic stability 29,30 and the ability to autonomously selfheal. 3,31 The HEAA units of PHEAA-co-PMVK add a second dynamic functionality to the system by facilitating the formation of physical cross-links via hydrogen bonding during the cryogelation process. The excellent water solubility of HEAA eliminates the need for organic solvents and enables hydrogel formation in non-toxic aqueous media. The generalized method for the formation of 3D-printable, doubly dynamic, self-healing cryogels is presented in Scheme 1.
To be printable, gels must possess a good balance between the ability to flow and the ability to retain their 3D structure without collapsing. Therefore, a delicate rheological balance is required to formulate inks with optimal 3D-printing characteristics. 6,12 Unlike commonly reported printing of non-covalently Scheme 1 A schematic of the methodology used to form 3D-printable, doubly dynamic self-healing cryogels. 3D-printing of oxime gels is followed by post-printing cryogelation, which induces the formation of macropores and physical cross-links by hydrogen bonding, and reinforces the object. The inset demonstrates the chemical structure of the cryogels and their macroporous morphology.

Polymer Chemistry Paper
This cross-linked gels and polymer assemblies, 11,13,21 3DP of covalently cross-linked gels has the potential to be a challenging task due to a higher strength of covalent bonds, yet it remains desirable for the printing of materials requiring higher stability and diverse functionalities. The adjustment and optimization of oxime ink formulations was conducted according to an established approach. 6 G oxime was selected as an optimal formulation for 3DP in the current work. Rheological characterization of G oxime confirms its suitability for extrusion based 3DP (Fig. 1). The apparent viscosity measurements of G oxime indicate that the gel exhibits shear thinning behaviour, an essential criterion for extrudeability, and exhibits a good fit to a power law model 32 (Fig. S6 †). The increase in temperature from 25°C to 80°C resulted in a significant decrease in apparent viscosity, enabling the printing at more moderate pressures. Similar printing performances were obtained at 25°C and 80°C. Printing at high temperatures was achievable due to the high thermal stability of PHEAA-co-PMVK, as indicated by the TGA (Fig. S7 †).
Other important parameters for formulating extrudeable materials are the storage modulus and the point of flow associated with the yield stress. The applied shear stress generated in the print head must exceed the yielding point of the gel in order to induce flow. 9 At ambient temperature, G oxime starts flowing at ∼1000 Pa and its storage modulus is 82 Pa. At 80°C, the stress required to induce G oxime flow decreases to ∼400 Pa and the storage modulus to 40 Pa (Fig. 1b). The G oxime formulation is in an appropriate rheological range for successful 3Dprinting, and its rheological parameters are in agreement with previously reported values. 6,9,11,12 The extrusion of G oxime resulted in the formation of well-structured and stable filamentous strands, suitable for layer-by-layer deposition (Fig. 1c). After the extrusion-induced shear was stopped, printed filaments exhibited fast shape recovery to well-defined self-supporting shapes. Although the 3DP of G oxime allowed fabricating only simple architectures, 3D-printed objects successfully retained their structure without collapsing, and enabled subsequent mounting of multiple ink layers on top of each other without spreading (Fig. 1d). Owing to the fast fusion of the filaments, solid and fully symmetrical infill patterns (100% infill mesh), the printing directionality had no effect on the gels' properties.
Rapid, full and autonomous recovery from damage is a significant advantage for self-healing systems as they eliminate any need for the application of an external stimulus to fully heal the damage. The evaluation of G oxime and the cryogels' self-healing performance was conducted by using rheology measurements and induction of macroscopic cuts. Rheological analysis of G oxime shows that at high strains (∼2200%) the network is destroyed. This trend is indicated by a sharp decrease in storage modulus, and the intersection of G′ and G″. The self-healing (dynamic) response of the gel is indicated by the immediate recovery of G′ to its initial values at low strain (Fig. 2a). Frequency sweep experiments revealed that G oxime exhibits frequency dependent behaviour, which is a characteristic of (albeit not unique to) self-healing gels (Fig. S8 †). 4,33 Finally, G oxime and the cryogel recovery from macroscopic cuts was examined. After the induction of a scalpel cut, the 2 halves of the gels were immediately brought into contact and the recovery of the gel to a single unit was followed ( Fig. 2b-d and S9 †). After ∼3 hours at ambient temperature, and without any external additives, the damaged gels were healed and were able to support themselves under gravity. Owing to the dynamic nature of G oxime and its instant recovery, extrusion through a nozzle did not affect the gel. While oxime bonds can be disrupted by the printing shear, their ability to instantly recover from high mechanical strains enables them to retain their intact properties.
In addition to the 3D-printable G oxime , we have examined the effect of alternating degrees of cross-linking on the mechanical and self-healing properties of the gels (Fig. S10 †). As expected, with the increase in the wt% of TEG-BHA, stiffer gels were formed. The examined gels retained their selfhealing ability, and fully recovered from high-strain network destruction. However, these gels were not suitable for 3DP and were either too soft and spreadable, or densely cross-linked and therefore prevented a smooth mass flow during their extrusion.
The effect of post-printing treatment of soft G oxime by TIPS was explored and a structure-property investigation was conducted. Subjecting G oxime to subsequent freeze-thaw cycles was found to be an efficient method to increase the strength of Fig. 1 Rheological characterization and the 3DP performance of G oxime : (a) apparent viscosity curves of G oxime at 25°C (black squares) and 80°C (red triangles). The gel exhibits shear thinning behaviour, suitable for 3DP. (b) Shear yielding of G oxime at 25°C (black squares) and 80°C (red triangles). (c) A stable, shape-retaining extruded filament of G oxime . (d) 3D-printed hollow structure (6 layers of G oxime ink printed at 80°C on top of a glass substrate). The structure did not collapse upon substrate inversion, indicating its structural integrity. The inset demonstrates a caption taken from the top of the same hollow object.
G oxime in a well-controlled manner. The approach enabled a sensitive tuning of the mechanical properties through the precise control over TIPS conditions, such as freezing temperature, the number of cycles and the cycle's duration. The effect of TIPS treatment is demonstrated in Fig. 3. With the increasing number of cryogelation cycles a significant increase in storage modulus is observed, indicating the reinforcement effect of TIPS. Moreover, the reinforcement rate was highly dependent on the freezing temperature. When the freezing temperature was −10°C, a higher reinforcement at a faster rate was achieved compared to freezing at −20°C, (Fig. 3a and  b, respectively). Freezing at −20°C increased the storage modulus by up to ∼500% after 5 cycles. Freezing at −10°C resulted in a much more drastic storage modulus increase of up to ∼1900% after the same number of cycles. In both cases, the method allowed a very significant and gradual increase in the mechanical strength of G oxime , demonstrating the advantages of this method in the reinforcement of soft materials. To investigate the effect of cryogelation time on the mechanical properties of G oxime the freezing time has been decreased from 24 to 4 h. As expected, a longer cryogelation time resulted in a more significant reinforcement effect by enabling more time for the cross-links to form (Fig. S11 †).
After TIPS treatment (3 cycles or more at −10°C or 5 cycles at −20°C), the storage modulus of the cryogels becomes similar (or higher) to that of the previously reported non-printed self-healing gels. 4,5,34 More importantly, unlike soft G oxime , the cryogelated objects could be easily handled, lifted and displaced from the substrate without spreading. After TIPS treatment the objects were reinforced, and therefore the cryogels are not printable. However, the cryogels remained complaint to some degree of deformation and shaping. The reinforcement effect of TIPS was also supported by compression tests, which are in good agreement with the rheological data, and indicate a gradual increase in Young's (compression) modulus with the increasing number of TIPS cycles (Fig. S12 †). The reinforcement effect can be attributed to the formation of hydrogen bonding ( physical) cross-links induced by the cryogelation process. It is well-known that cooling aqueous solutions containing cryogel precursors to subzero temperatures generates cryo-concentrated microphases, surrounded by ice crystals. 35,36 These polymer rich zones facilitate interactions between polymer chains which can form physical cross-links. 33,35 Since the polymer system contains multiple hydrogen bonding motifs, we hypothesized that the cryogelation process can facilitate physical cross-linking between the G oxime chains, and hence introduce a second dynamic functionality to the self-healing system. FTIR analysis of G oxime and the cryogels supports this hypothesis (Fig. S13 †). The FTIR spectra indicate that after cryogelation, a significant broaden-  ing and an increase in signal intensity of bound hydroxyl (2957-3687 cm −1 ) and carbonyl (1637 cm −1 ) groups occur. Moreover, the bound hydroxyl peak has shifted from 3367 to 3342 cm −1 as a result of cryogelation. These results provide evidence for hydrogen bonding enhancement by TIPS. In addition to the formation of physical cross-links by TIPS, it has recently been reported that low temperatures can actually increase the rate of oxime ligation. 37 Agten et al. demonstrated that freezing can catalyse the formation of oxime ligation. 37 Therefore, repeated freezing of G oxime may also account for the increased strength of G oxime after freezing cycles.
To investigate the stabilization of G oxime , gelation kinetic studies were conducted. Rheological data indicate that the solto-gel transition occurs within 1 h (Fig. S14a †). Re-examination of the same sample after overnight stabilization (16 h) revealed that G′ values remained unchanged. This provides evidence of the full completion of the TEG-BHA cross-linking reaction under ambient conditions (Fig. S14b †).
Unlike traditional types of cryogel precursors such as colloidal dispersions, monomeric, or polymeric precursors, 35 the method described herein allows the formation of cryogels from gels and therefore represents a novel approach towards the formation of macroporous materials from solid, crosslinked precursors.
The changes in the degree of swelling of oxime cryogels provide additional evidence to confirm the formation of crosslinks by cryogelation. With an increasing number of freezethaw cycles, a decrease in swelling was observed (Fig. 3c). Moreover, an inverse correlation between the storage modulus and the degree of swelling of all the prepared cryogels was also observed (Fig. 3d). As expected, with the increasing number of subsequent cryogelation cycles, more cross-links are formed, which results in an increased mechanical strength and decreased swelling capabilities. The results are in good agreement with the literature. 33 G oxime and doubly dynamic selfhealing cryogels exhibit an extremely high degree of swelling. G oxime increased in weight by ∼11 000% by water uptake, G oxime was subjected to 5 freeze-thaw cycles at −10°C and swelled by ∼1000%, and G oxime was subjected to 5 freeze-thaw cycles at −20°C and swelled by ∼3000%. The observed differences between the swelling capacities of the cryogels indicate that the cross-links remain stable and do not get disrupted by interactions with water. The swelling of G oxime and the cryogels in the acid and base was studied in order to assess their response to alternating pH values. When the gels were introduced to the acid ( pH = 4.5) and base ( pH = 8.5) their degrees of swelling decreased compared to the degrees of swelling in deionized water (Fig. S15a †). In agreement with these observations, rheological examination of the gels confirmed the increase in their storage modulus in the acid and base (Fig. S15b †). These results indicate that the acid and base can enhance the cross-linking of the gels and affect their interactions with water. The presence of an acid can catalyse the formation of oxime bonds 38 by the protonation of ketone groups, making them more prone to nucleophilic attack by the unreacted TEG-BHA. Basic conditions had a similar effect on the gels. The understanding of the observed results under basic conditions requires a more detailed future investigation.
Rheological characterization of the cryogels indicates that the self-healing properties of the gels were not affected by TIPS, and the cryogels retained the ability to recover from network destruction (Fig. S16 †). Interestingly, the recovery tendency of G oxime and the cryogels were very similar and all the gels exhibited an immediate recovery. This similarity can be attributed to the methodological sensitivity, which does not provide a sufficient resolution to distinguish between these differences, especially when the recovery is instant and full. However, despite the similarity in the self-healing behaviour (recovery time and %), the rheological response of the gels to the applied strain was different and strongly dependent on the mechanical strength of the gels. Soft gels (G′ ∼ 100 Pa) with a low degree of cross-linking (G oxime and the cryogel prepared by 2 freeze-thaw cycles at −20°C, Fig. 2a and S16b, † respectively) can withstand high strains (∼2000%) before reaching a failure point. Highly cross-linked and stiffer cryogels (G′ ∼ 1000 Pa, cryogels prepared by 4 freeze-thaw cycles at −10°C, Fig. S16a †), on the other hand, fail at much lower strains (∼60%). Similar behaviour of soft and strong gels has been previously observed by Rutz et al. 12 These differences can be explained by the fact that the polymer chains of softer gels (less cross-linked) are less constrained, and therefore have more freedom to deform and disentangle, requiring higher strains to reach their failure.
The differences between the degree of cross-linking and therefore the mechanical performance of oxime cryogels prepared at −10°C and −20°C can be explained by the cryogel microstructure. At lower freezing temperatures, the freezing rate is faster, and therefore the water crystalizes more rapidly, resulting in smaller crystals. Small water crystals are associated with a smaller pore size and thinner walls, as has been previously reported. 35,36,39 CLSM indicates that the cryogels prepared at −20°C have a smaller pore size and thinner walls than the cryogels prepared at −10°C and are therefore mechanically weaker (Table 1). CLSM analysis of G oxime and the cryogels is presented in Fig. 4 and S17. † While G oxime has a non-porous structure, the cryogels exhibit a sponge-like macroporous structure, which was generated by cryogelation. Ice crystals act as non-toxic and natural porogens, which leave well-defined pores after ice thawing. 36 CLSM morphological analysis shows that a slower freezing rate also enables better control over the freezing process, which is reflected by a more uniform pore shape and size (Fig. 4b). In contrast, an extremely fast freezing rate results in more random pore morphology (Fig. 4c). All the parameters of G oxime and the doubly dynamic cryogels are summarized in Table 1.

Conclusion
We present doubly dynamic and self-healing cryogels with a macroporous structure and tuneable mechanical strength by TIPS. In conjunction with 3DP, this method enables a facile post-printing reinforcement of soft 3D-printed gels, eliminating the need for additional chemicals or UV equipment. Soft 3D-printable gels are able to be reinforced by up to ∼1900%, making soft 3D-printed objects strong and easily handled.
The mechanical strength of TIPS-treated gels can be modulated in a well-controlled manner via a specific choice of freeze-thaw conditions. Different freezing rates resulted in distinct microstructures of the cryogels and therefore different physical and mechanical characteristics. The formation of macroscopic interconnected pores was facilitated by hydrogen bonds between the PHEAA-co-PMVK chains, which could interact in polymer enriched macrophases during cryogelation. It was demonstrated that in addition to conventional cryogel precursors, solid gels can act as cryogel precursors. 3D-printable oxime gels and doubly dynamic cryogels prepared in this work exhibited rapid, full and autonomous recovery from damage (self-healing), making them promising functional materials for applications requiring extensive utilization and prolonged lifetimes. Moreover, their macroporous structure and tuneable mechanical properties make them promising candidates for biomedical applications. More importantly, we envision that the novel approach presented in this work is not limited to PHEAA-co-PMVK, and can be potentially implemented in other functional systems as a generalized reinforcement methodology.

Funding sources
This work has been supported by the Victorian Endowment for Science Knowledge and Innovation (LAC).

Conflicts of interest
The authors declare no conflict of interest. Fig. 4 CLSM morphological characterization of G oxime and the cryogels prepared at different freezing temperatures. (a) G oxime exhibits a nonporous structure. (b) G oxime subjected to cryogelation at −10°C, after 4 subsequent freeze-thaw cycles. The cryogel exhibits a macroporous structure with an average pore size of 16.7 µm and an average wall thickness of 6.5 µm. (c) G oxime subjected to cryogelation at −20°C, after 4 subsequent freeze-thaw cycles. The cryogel exhibits a macroporous structure with an average pore size of 6.5 µm and an average wall thickness of 2.9 µm. Lower cryogelation temperature results in weaker gels with a smaller pore size and wall thickness.

Polymer Chemistry Paper
This