{'fraction_non_alphanumeric': 0.02643171806167401, 'fraction_numerical': 0.02026431718061674, 'mean_word_length': 5.491428571428571, 'pattern_counts': {'":': 0, '<': 0, '<?xml version=': 0, '>': 0, 'https://': 0, 'lorem ipsum': 0, 'www.': 0, 'xml': 0}, 'pii_count': 0, 'substrings_counts': 0, 'word_list_counts': {'cursed_substrings.json': 0, 'profanity_word_list.json': 0, 'sexual_word_list.json': 0, 'zh_pornsignals.json': 0}}
Mechanical performance and electromagnetic shielding effectiveness of composites based on Ag-plating cellulose micro-nano fibers and epoxy

Abstract Mechanical and electromagnetic interference shielding composites containing Ag-plating micro-nano cellulose fibers (ANCFs) were prepared as multifunctional materials. ANCFs, as electromagnetic wave reflection filler containing micro-nano cellulose fibers (NCFs) used as the structural component to reinforce the mechanical strength and Ag enhancing electromagnetic shielding effectiveness, were prepared by electroless Ag-plating technology on NCFs surfaces. Ag coating had a thickness of 60 µm without the oxide phase detected. The incorporation of 5 wt % ANCFs into epoxy (EP) substrate yielded impact strength and flexural strength of 1.84 kJ/m2 and 41.6 MPa, which is approximately 2.4 times and 1.41 times higher than EP. The ANCFs-EP composite performed an electromagnetic shielding effectiveness of 34–25 dB at a frequency of 90 kHz in the electromagnetic wave; the EMI shielding effectiveness was improved obviously up to 34 dB, which can meet the requirement of general places.