{'fraction_non_alphanumeric': 0.036616161616161616, 'fraction_numerical': 0.022727272727272728, 'mean_word_length': 4.746376811594203, 'pattern_counts': {'":': 0, '<': 0, '<?xml version=': 0, '>': 0, 'https://': 0, 'lorem ipsum': 0, 'www.': 0, 'xml': 0}, 'pii_count': 0, 'substrings_counts': 0, 'word_list_counts': {'cursed_substrings.json': 0, 'profanity_word_list.json': 0, 'sexual_word_list.json': 0, 'zh_pornsignals.json': 0}}
Organic field-effect transistors containing a SiO2 nanoparticle thin film as the gate dielectric.

In this article, we report the fabrication of organic field-effect transistors using self-assembled SiO2 as a gate dielectric material and pentacene as a semiconductor. The dielectric layer was self-assembled with 10 layers of SiO2 nanoparticles 45 nm in diameter, and its breakdown field was larger than 0.57 MV/cm. Being a low-cost and low-temperature process, the layer-by-layer self-assembly is particularly suitable for organic field-effect transistor fabrication. The pentacene was thermally evaporated on the substrate under high vacuum at the room temperature. The fabricated transistor has a threshold voltage of 0.3 V, field-effect mobility of 0.05 cm2/Vs, and slope of 1.4 V/decade.