{'fraction_non_alphanumeric': 0.024088375185393546, 'fraction_numerical': 0.013962051859049762, 'mean_word_length': 4.684302325581395, 'pattern_counts': {'":': 0, '<': 0, '<?xml version=': 0, '>': 0, 'https://': 0, 'lorem ipsum': 0, 'www.': 0, 'xml': 0}, 'pii_count': 0, 'substrings_counts': 0, 'word_list_counts': {'cursed_substrings.json': 0, 'profanity_word_list.json': 0, 'sexual_word_list.json': 0, 'zh_pornsignals.json': 0}}
Potential of calcium carbonate as secondary filler in eggshell powder filled recycled polystyrene composites

Recycling of plastic waste is considered a key intention in regards to the continuous growth of plastic industry. In this work, new composite based on recycled polystyrene (R-PS) was prepared in the presence of eggshell powder (ESP). This was to make a value-added plastic material based on polystyrene. To further extend its performance, calcium carbonate (CaCO 3 ) was used as secondary filler to optimize its performance. It is observed that the stabilization torque of composites decreased with increasing the weight percent of CaCO 3 . Increasing the amount of CaCO 3 has increased the mechanical properties such as Young’s modulus, tensile strength, elongation at break and impact strength of the composites. These findings corresponded well to SEM images. It revealed homogenous dispersions of CaCO 3 throughout R-PS matrix in comparison to ESP alone which formed agglomerations in R-PS matrix. Further evidence on thermal stability has confirmed that CaCO 3 provided better heat resistance over the ESP.


Introduction
Polystyrene is one of the most widely used plastics in many applications i.e., food packaging, home appliance, consumer goods and so forth. Polystyrene is similar to other types of plastic which is non-degradable after use. The abundant of these products has brought to several environmental issues. Therefore, special attention is devoted to recycling, reuse, and making them biodegradable by various approaches [1,2] . The first approach is considered to be most possible way to reduce the discarded polystyrene. To date, the recycling of polystyrene mainly includes mechanical, thermal and chemical methods. The mechanical recycling is one among the methods that has a cost-effective and good environmental option. This technique deals with grinding the polystyrene waste and reprocesses into a new raw material. However, the products obtained from this process still possesses low mechanical properties due to degradation aspect [3][4][5] . Hence, recycled polystyrene with remarkable performance was to develop to overcome this situation while prevailing sustainability.
Introducing fillers to the recycled plastics is another route to increase some properties to the composite. There are two main types of fillers available in the plastic industry which are reinforcing and non-reinforcing fillers. Reinforcing fillers are used to improve the strength and abrasion resistance to the composites [6] . However, for some cases where cost and processability are essential, the use of non-reinforcing fillers are suggested. Calcium carbonate (CaCO 3 ) is a good example of non-reinforcing fillers that has been widely used in plastics. For instance, polypropylene [7] , polyethylene [8] , polystyrene [9] and so forth. It can be said that CaCO 3 is still a filler of choice in plastic industry. However, the advancement of plastic technology introduces a new era in the environmental and industrial field of green research. Therefore, searching for an alternative source of filler that is chemically similar to CaCO 3 is challenging in the near future.
Traditionally, most eggshell waste is discarded to landfills without further processing. For economic aspects, eggshell waste can be used to convert biomaterials into commercial products and creates new values from these waste materials. It is known that eggshell waste contains lots of valuable organic and inorganic components which can be used in many applications. The chemical composition (by weight) of eggshell has been reported to consist mainly of a mineral part (95%) of calcite crystals and a pervading organic matrix (1-3.5% of the remaining material) [10][11][12][13] . Thus, it can be considered a good source of CaCO 3 . Since CaCO 3 is by far an important and the most widely used filler because of its whiteness, low abrasion, availability in wide-size ranges and low cost. Consequently, If the eggshell is prepared properly, it is not only a filler added to reduce costs but today it is the material engineering for the different requirements of modern products Despite replacing the CaCO 3 , the point of application of chicken eggshell waste was to ensure that hybrid fillers based on these two fillers would be able to provide synergistic properties. To date, there has been a limited report on the properties of ESP/CaCO 3 hybrid filled R-PS composites. Due to the above reasons, the effect of ESP/CaCO 3 hybrid fillers on the properties of R-PS composites is thoroughly investigated.

Materials
The materials used for compounding the composites is listed in Table 1. All the materials were used as received except for the eggshell powder (ESP) which was ground until desired particle size.

Preparation of Eggshell Powder (ESP)
The collected chicken eggshell waste was cleaned, washed and dried prior to proceed to the grinding step. The mechanical grinding supplied by Rong Tsong Precision Technology Co. Ltd. was used in the grinding process. The obtained powder form of ESP was sieved using a sieve No. 200 where the size ranging from 30 -150 μm was used for compounding.

Preparation of Composites
The formulation used for preparing ESP/CaCO 3 hybrid filled R-PS composites is listed in Table 2. ESP and CaCO 3 were dried in an oven at 105 °C for 2 h before mixing. All the compounding ingredients were melt-mixed in a Thermo HAAKE PolyDrive internal mixer with co-rotating blades. The compounding was carried out at 180 °C for a total of 8 min with rotor speed of 60 rpm. First, R-PS was charged and ESP and/or CaCO 3 was added after 4 min of mixing. The mixing was continued and left for another 4 min. The mixing torques were recorded until dumping out from the internal mixer. Lastly, resultant compounds were weighed at approximately 30 g and placed inside the mold prior to undergo the compression-molding process using a hydraulic press from GoTech Testing Machines Model KT-7014 A. The compounds were preheated first for 6 min, followed by compression molding for 2 min at a temperature of 180°C. The samples were then cooled under pressure for 3 min at ambient temperature.

Measurement of mechanical properties
Tensile tests were performed using a Universal Testing Machine (UTM) Instron Model 3366 according to the ASTM D638. The samples were pulled at a crosshead speed of 1 mm/min with a constant gauge length of 100 mm. The results of the Young's modulus, tensile strength and elongation at break were discussed. As for the impact test, a sample with the dimension of 64 x 12.7 x 3.2 mm was prepared for un-notched Izod impact test. It was carried out using a Zwick Impact Tester Model 5101 according to ASTM D256.

Scanning electron microscopy
The morphological observation was carried out using a scanning electron microscope (SEM) model Zeiss Supra-35VP. The samples from the tensile and impact fractures were used to captured the image. It was coated with a layer of gold to prevent an electrostatic charge formation prior to scanning.

Thermogravimetric Analysis
Thermogravimetric analysis of the composites were investigated by a Perkin-Elmer Pyris 6 TGA Analyzer. The sample was heated from 25 °C to 600 °C with a heating rate of 10 °C/min under a nitrogen atmosphere. Figure 1 shows the processing torque of the R-PS composites at various weight percent of ESP/CaCO 3 hybrid fillers. At initial stage of mixing, the processing torque increased rapidly due to the shearing action from the solid R-PS pellets. Afterwards, the processing torque gradually reduced, indicating a decrease of viscosity as R-PS pellets melt by continuous mechanical shearing and high processing temperature. Then processing torque increase again after 4 min of mixing. This caused by the addition of the ESP and CaCO 3 into molten R-PS. The melt viscosity increased in the presence of fillers, which reduced the polymer chain mobility in the blend and consequently raised the processing  torque value [14] . The processing torque decreased gradually and the stabilization torque achieved after the composite in homogenized mixture. The similar trend on processing torque was also observed from other literatures with different composites [15,16] . Figure 2 shows the stabilization torque of the R-PS composites at various weight percent of ESP/CaCO 3 hybrid fillers. The results clearly indicate that stabilization torque of composites is decreasing with the increasing the weight percent of CaCO 3 . Such a decrease in stabilization torque could be due to the fine CaCO 3 particles that possesses high dispersibility as compared to ESP. Therefore, CaCO 3 was well-dispersed in molten R-PS, resulting lower viscosity found in the composites containing CaCO 3 . The coarser ESP forms a large network and agglomerates, which required high shear force to disperse the ESP in molten R-PS. Thus, high stabilization torque is observed in the composite based on the ESP alone. Figure 3 shows the tensile strength of the R-PS composites at various weight percent of ESP/CaCO 3 hybrid fillers. From the result obtained, the tensile strength gradually increased upon increasing the weight percent of CaCO 3 . The highest tensile strength was observed for the composite containing 20 wt% of CaCO 3 . The above results indicate that the use of CaCO 3 led to improve the tensile strength of the composites. This is simply related to the well dispersion of CaCO 3 throughout R-PS matrix as compared to ESP which is shown later in SEM images. Strong adhesion between CaCO 3 and polymer interface can cause better stress transfer from one to each other. This has led to a higher tensile strength. Toro et al. [17] , reported that slightly lower tensile strength of the composite containing solely ESP compared to CaCO 3 counterpart can be attributed to its particle size. ESP is normally coaser and bigger size compared with the CaCO 3 . It is easily agglomerated each other, causing to lower the tensile strength eventually. CaCO 3 used in this composite is considered ultra-fine precipitated grade (see Table 1) which has smaller particle size as compared to ESP. The smaller particle size of the filler could produce a maximal interface contact with polymer matrix because of larger specific surface area [18,19] . This will improve the wettability of CaCO 3 by the R-PS matrix. As a result, a high tensile strength is obtained in composites containing more CaCO 3 . The location and behaviour of CaCO 3 throughout the R-PS matrix can be proved in the SEM micrographs of tensile fractured surfaces in the next section.

Mechanical Properties
Elongation at break of the R-PS composites at various weight percent of ESP/CaCO 3 hybrid fillers is also shown in Figure 3. It can be seen that the elongation at break was increased with the increasing the weight percent of CaCO 3 . According to literature [17] , the increment in elongation at break of the composite can be attributed to the formation of stronger filler aggregates. In this case, it is CaCO 3 which is not similar to ESP. ESP is rather found in agglomerated form. The CaCO 3 aggregate has better interfacial adhesions with R-PS matrix, resulting in efficient stress transfer from the matrix to filler, thus increasing the elongation at break. The lower flexibility found for the composite containing more ESP can be attributed to extensive ESP agglomeration as mentioned earlier, which transformed into multiple stress concentration sites. Therefore, the crack propagation across the composite could occur on a large scale, prohibiting the composite from dissipating stress in the form of matrix deformations. Figure 4 shows the Young's modulus of R-PS composites at various weight percent of ESP/CaCO 3 hybrid fillers. Young's modulus of the composites increased as a   function of weight percent of CaCO 3 due to the increase in the composite's stiffness. According to Fu et al. [20] , Young's modulus is known to be less sensitive variation of interfacial adhesion than the tensile strength which is strongly associated with interfacial failure behaviour. This is due to the fact that Young's modulus is measured before any significant plastic deformation takes place. Increase in tensile modulus of some composite samples is attributed to better distribution of small particle size of CaCO 3 in the matrix. A smaller particle size of the CaCO 3 could produce a maximal interface contact because of larger specific surface area. The higher surface area of filler gives better adhesion in composite, thus forming a stiffer material which is attributed to higher modulus. Therefore, small particles and homogeneous distribution are the main contribution to originate a more rigid structure.
As for the impact strength (see Figure 5), similar trend was observed. There was an enhancement in impact strength with the addition of CaCO 3 to the hybrid composite. This behaviour is similar to a result reported by Bashir et al. [21] , considerable improvement in the impact strength of the composite containing CaCO 3 as compared to ESP is mainly due to a well-dispersed CaCO 3 . This has brought to an increase in the interfacial adhesions between filler and polymer matrix. It is then required higher impact force to overcome the strong interfacial adhesions between CaCO 3 within the R-PS matrix. The lower impact strength of the ESP filled composite is simply due to the effect posed by agglomerations of ESP which may act as stress concentration points or points of discontinuity in composites thereby promoting crack initiation and propagation. Figure 6A presents the SEM micrograph of the CaCO 3 . The shape of the CaCO 3 was irregular with various particle sizes. The average particle size of CaCO 3 is ranging from 1 -10 µm. It can be seen that there is smaller than the ESP which is in range of 30 -150 µm (see Figure 6B). This has shown that CaCO 3 possesses high possibility to disperse throughout the matrix when compared to ESP. Figure 7 represents the SEM images obtained from tensile fractured surfaces of ESP/CaCO 3 hybrid filled R-PS composites. Some agglomeration is seen in the composite containing ESP alone (see Figure 7A) and its size was much bigger than the CaCO 3 found in Figures 7B and 7C. The agglomeration of ESP indicates poor dispersion of ESP throughout the R-PS matrix. The agglomerates and bigger particle of ESP may act as stress concentration points or points of discontinuity in composites thereby inhibiting stress   transfer and reduced the tensile strength of ESP composite. Furthermore, the surface was found to be rougher especially at higher weight ratio of CaCO 3 , this reflects less brittle deformation and higher energy absorption is generated. Therefore, a higher tensile strength is obtained in composite containing more CaCO 3 . The SEM results for the tensile fractured surfaces were in good agreement with the results obtained by Siriwardena et al. [22] , who reported that an increase in energy was responsible for the roughness and the matrix tearing line of the fractured surface. Figure 8 demonstrates the SEM images obtained from impact fractured surfaces of ESP/CaCO 3 hybrid filled R-PS composites. Figure 8A shows the SEM image of the R-PS composite containing 20 wt% of ESP. It exhibits a rough surface with bigger particle of ESP, indicating its poor dispersion in R-PS matrix. This may have brought to a stress concentration points or points of discontinuity in composites thereby promoting crack initiation and propagation. Thus the impact strength of composites is reduced. The image also displays several occurrences of voids due to pullingout of the ESP. Comparing with the composites containing higher weight percent of CaCO 3 (see Figures 8B and 8C), it exhibited less void formation, better dispersion and adhesion of CaCO 3 throughout the R-PS matrix. Such remarkable interfacial adhesions of CaCO 3 to the R-PS matrix allowed impact force to be absorbed and transferred more uniformly throughout the composite system, thus providing higher impact strength compared to the composite with ESP alone.

Thermogravimetric Analysis
Thermogravimetric analysis or TGA is a method to determine the rate of the weight changes as a function of temperature at a controlled atmosphere. TGA is primarily used to analyse the compositions and thermal stability of materials [23] . The thermograms (TG) and derivative thermograms (DTG) of ESP/CaCO 3 hybrid filled R-PS composites are shown in Figure 9. The decomposition temperature at 50% (T 50% ) mass loss, maximum mass loss (T max ) and char residue are also listed in Table 3. From the results obtained, there is only one region of the thermogram observed. The degradation started at the temperature around 350 o C and was then completed at about 450 o C. The decomposition was mainly due to the degradation of polystyrene segment where it corresponds to the major peak observed off the DTG curve (see the DTG peaks embedded in Figure 9).
To compare the results, the temperature for 50% mass loss was determined as degradation temperature of the composite. The R-PS composites with 20 wt% of CaCO 3 had a highest degradation temperature of T 50% (425.93 ˚C) as compared to the other composite. This is simply due to the presence of well-dispersed CaCO 3 in R-PS matrix, which is expected to provide a barrier to the diffusion of degradation products, suppressing R-PS mass loss in the composite. The balance set of thermal stability is served for the composite with 10wt% of ESP and CaCO 3 respectively. This is interesting to highlight that the incorporation of ESP with the assistance of CaCO 3 can promote the resistance to heat of R-PS matrix. In addition to that, lowest degradation temperature of T 50% (424.11 ˚C) found in the composite with 20 wt% of ESP may be due to poor dispersion of ESP in R-PS matrix, arising from the formation of agglomerated ESP which reduced thermal stability of the composites.
The amount of residue of R-PS composites with 20 wt% of CaCO 3 is highest (approximately 20.79%) among the  other composite. This residual value of composite is higher than its filler content because the R-PS matrix may contain thermally stable impurities. R-PS composite with 20 wt% of ESP has lower residue content (roughly 19.49%) than 20 wt% of CaCO 3 composite. This is attributed to the loss of organic composition during or after testing.

Conclusions
The processability, mechanical, morphological, and thermal properties of ESP/CaCO 3 hybrid filled R-PS composites were studied with respect to different weight percent of ESP/CaCO 3 hybrid fillers. It is found that the stabilization torque of composites was decreased with the increased of the amount of CaCO 3 . Increasing CaCO 3 content has increased tensile strength, elongation at break, Young's modulus, and impact strength of the composites. The mechanical properties obtained clearly corresponded to SEM images observed. Further evidence on the thermal stability has confirmed that CaCO 3 provided better heat resistance over the ESP alone. Even the CaCO 3 seemed to play important role in the properties of ESP/CaCO 3 hybrid filled R-PS composites. However, the hybridization of ESP and CaCO 3 does show balance set of properties especially the mechanical and thermal properties of ESP/CaCO 3 hybrid filled R-PS composites. It can be concluded that the ESP hybridized CaCO 3 is applicable to prepare the composite based on the R-PS where the ratio of ESP and CaCO 3 at 10/10 (wt%) is highly suggested.