{'fraction_non_alphanumeric': 0.0474792817679558, 'fraction_numerical': 0.026703499079189688, 'mean_word_length': 4.2293108636774, 'pattern_counts': {'":': 0, '<': 0, '<?xml version=': 0, '>': 0, 'https://': 0, 'lorem ipsum': 0, 'www.': 0, 'xml': 0}, 'pii_count': 0, 'substrings_counts': 0, 'word_list_counts': {'cursed_substrings.json': 0, 'profanity_word_list.json': 0, 'sexual_word_list.json': 0, 'zh_pornsignals.json': 0}}
A simple preparation of very high methanol tolerant cathode electrocatalyst for direct methanol fuel cell based on polymer-coated carbon nanotube/platinum

The development of a durable and methanol tolerant electrocatalyst with a high oxygen reduction reaction activity is highly important for the cathode side of direct methanol fuel cells. Here, we describe a simple and novel methodology to fabricate a practically applicable electrocatalyst with a high methanol tolerance based on poly[2,2′-(2,6-pyridine)-5,5′-bibenzimidazole]-wrapped multi-walled carbon nanotubes, on which Pt nanoparticles have been deposited, then coated with poly(vinylphosphonic acid) (PVPA). The polymer coated electrocatalyst showed an ~3.3 times higher oxygen reduction reaction activity compared to that of the commercial CB/Pt and methanol tolerance in the presence of methanol to the electrolyte due to a 50% decreased methanol adsorption on the Pt after coating with the PVPA. Meanwhile, the peroxide generation of the PVPA coated electrocatalyst was as low as 0.8% with 2 M methanol added to the electrolyte, which was much lower than those of the non-PVPA-coated electrocatalyst (7.5%) and conventional CB/Pt (20.5%). Such a high methanol tolerance is very important for the design of a direct methanol fuel cell cathode electrocatalyst with a high performance.

We here present the third trial for this issue (methanol tolerance) that shows a much higher performance than previous methods as well as an easy preparation based on a "polymer-coating" method. We have reported that the electrocatalyst coated with PVPA showed an enhancement in its fuel cell durability 29,30 and blocked methanol absorption on the active Pt nanoparticles (Pt-NPs) 31 , which are important parameters for the cathode side of the DMFC. In this study, we describe the results that after coating with a polymer, the electrocatalyst showed a very high methanol tolerance.

Results and Discussion
The MWNT/PyPBI/Pt and MWNT/PyPBI/Pt/PVPA were prepared according to a previous method ( Fig. 1a) 29,30 . The as-synthesized electrocatalysts were dispersed in water by sonication for 5 min to determine their dispersity in water. As shown in Fig. 1b, the MWNT/PyPBI/Pt/PVPA produced a homogenous solution due to the hydrophilic surfaces of the homogeneous coating of the PVPA layer, while the MWNT/PyPBI/Pt poorly dispersed in water due to the hydrophobic surfaces of the PyPBI. Also, the PVPA layer on the Pt-NPs determined by the HR-TEM shown in Fig. 1c was ~2 nm. The TEM images of the MWNT/PyPBI/Pt and MWNT/PyPBI/Pt/PVPA together with a conventional CB/Pt for comparison are shown in Fig. S1, from which their Pt diameters were determined to be 3.9 ± 0.2, 3.8 ± 0.2 and 3.8 ± 0.6 nm, respectively. The properties of these electrocatalysts were almost the same as those of the previous ones. Briefly, we observed two clear peaks at 71.4 and 75.0 eV that are attributed to the 4f 7/2 and 4f 5/2 of the metal Pt, respectively, and the N 1s peak was observed at ~400 eV in both MWNT/PyPBI/Pt and MWNT/PyPBI/Pt/PVPA that were derived from PyPBI (see Supplementary Information, Fig. S2). The typical P 2p peak due to the PVPA was observed at ~132 eV only in the MWNT/PyPBI/Pt/PVPA, suggesting that the PVPA successfully coated on the prepared electrocatalyst. The decrease in the density of the Pt 4f and N 1s peaks in the MWNT/PyPBI/Pt/PVPA also suggested that the Pt-NPs were covered by PVPA 31 . From the TGA curves (see Supplementary Information, Fig. S3), the Pt contents in the composites decreased from 47.3 wt% to 44.5 wt% due to the additional PVPA, which was 6.0 wt% in the MWNT/PyPBI/Pt/PVPA, that was similar to our previous report 29 , indicating a high controllability and reproducibility of our electrocatalyst, while the previous methanol tolerant electrocatalysts were difficult to synthesize due to their complex structure.
The ORR is the cathodic reaction in an actual fuel cell 32 . During the fuel cell operation in the DMFCs, the methanol crossover is the most serious drawback since it lowers the voltage of the cells, leading to degradation of the FC performance. As shown in Fig. 2, the ORR was measured in the presence of a given concentration of methanol (for rotating disc current densities, see Supplementary Information, Fig. S4, 5 and 6). In the absence of methanol, the mass activities of the CB/Pt, MWNT/PyPBI/Pt and MWNT/PyPBI/Pt/PVPA calculated using the Levich-Koutecky equation, 1/i = 1/i k + 1/i d (where i is the experimentally measured current, and i d is the diffusion-limited current.), were 48.8, 187.0 and 157.7 mA/ mg Pt at 0.85 V vs. RHE, respectively [33][34][35][36] The PVPA-coated electrocatalyst showed a slight decrease in the ORR activity by 15.6% compared to that of the MWNT/PyPBI/Pt due to the polymer-coating of the Pt-NPs. The specific activity was calculated by dividing the mass activity by the electrochemical surface area (ECSA). The ECSAs of the MWNT/PyPBI/Pt and MWNT/PyPBI/Pt/PVPA were 44.7 and 42.3 m 2 / g Pt , respectively, (see Supplementary Information, Fig. S7) 37,38 , and the Pt utilization efficiency of the MWNT/PyPBI/Pt was almost the same as described in our previous report 39 . The specific activities were 0.42 and 0.37 mA/cm 2 Pt for the MWNT/PyPBI/Pt and MWNT/PyPBI/Pt/PVPA, respectively. These obtained values were much higher than that of the commercial CB/Pt (specific activity: 0.08 mA/cm 2 Pt , ECSA: 60.6 m 2 /g Pt ) similar to previous reports 40,41 . Meanwhile, the diffusion-limited current density of the PVPA-coated electrocatalyst (− 5.2 mA/cm 2 , see red line in Fig. 2c) was almost identical to that of the MWNT/PyPBI/Pt (− 5.3 mA/cm 2 , see red line in Fig. 2b), suggesting that the PVPA coating showed a negligible effect on the O 2 accessibility 42 . For the MWNT/PyPBI/Pt, we observed small methanol oxidation peak at 0.9 V vs. RHE in the presence of methanol in the electrolyte (see Fig. 2b). On the contrary, almost no such peak was recognized for the MWNT/PyPBI/Pt/PVPA, indicating the suppression of the methanol oxidation due to effect of methanol absorption caused by the polymer coating 31,43 .
It should be noted that an obvious methanol oxidation peak was observed for the conventional CB/Pt (see Fig. 2a) in the presence of methanol in the electrolyte due to the high ECSA value (see Supplementary  Information, Fig. S7). The MOR peak showed a positive shift and the peak current increased with the increased methanol concentration as shown in Fig. 2a. The half-wave potentials (E 1/2 ) evaluated from the ORR activity of the CB/Pt, MWNT/PyPBI/Pt and MWNT/PyPBI/Pt/PVPA are shown in Table 1 34,44-47 , in which, in the absence of the methanol, the value of the MWNT/PyPBI/Pt was the highest, which is consistent with the analyses of the mass and specific activities. With the increase in the methanol concentration, the E 1/2 of the three electrocatalysts decreased due to the coverage of CO on the Pt-NPs generated during the methanol oxidation reaction. However, in the presence of a high concentration of methanol, the E 1/2 of the CB/Pt and MWNT/PyPBI/Pt sharply decreased by 150 mV and 200 mV (see Table 1), respectively, while for the MWNT/PyPBI/Pt/PVPA, the value decreased only by 80 mV (see Table 1), suggesting that after coating with the PVPA, the presence of methanol showed the lowest effect on the ORR activity. Besides, the E 1/2 was higher than those of the CB/Pt and MWNT/PyPBI/Pt at the same methanol concentration.
Compared to the MWNT/PyPBI/Pt/PVPA (see red and green lines in Fig. 2c, 1.0 mA/cm 2 ), the ORR curves of the CB/Pt (see red and green lines in Fig. 2a) and MWNT/PyPBI/Pt (see red and green lines in Fig. 2b) showed high negative shifts (3.0 and 1.9 mA/cm 2 at 0.85 V vs. RHE for the CB/Pt and MWNT/ PyPBI/Pt, respectively) when 2 M methanol was added to the electrolyte, indicating that the CB/Pt and MWNT/PyPBI/Pt heavily suffered from methanol poisoning 6 . Also, the diffusion limited current density of the MWNT/PyPBI/Pt/PVPA showed a decrease only by 0.7 mA/cm 2 (see Fig. 2c) after adding 2 M methanol to the electrolyte, indicating a slight effect on the O 2 accessibility due to the prevention of methanol absorption on the Pt-NPs by the PVPA coating, while the MWNT/PyPBI/Pt and CB/Pt showed a 1.0 and 2.3 mA/cm 2 -loss (see Fig. 2a,2b) in the diffusion-limited current densities, respectively. Watanabe et al. pointed out that during the ORR, the oxygen molecules were supplied by spherical diffusion to the individual Pt-NPs 48,49 . The present study indicated that after coating with the PVPA, the methanol absorption was partly blocked as shown in Fig. 2d in which the mass current density of the MWNT/PyPBI/Pt/PVPA decreased by ~50% compared to that of the MWNT/PyPBI/Pt due to the coverage of the Pt-NP surfaces. The isolation of the electrocatalyst from the methanol is highly important for prepare a methanol-tolerant electrocatalyst. Meanwhile, the PVPA showed almost no effect on the O 2 diffusion due to the smaller size of the oxygen molecule and easy diffusion. Thus, the oxygen occupied the areas (radial diffusion fields) of the Pt-NPs and was reduced by the Pt-NPs in the MWNT/PyPBI/ Pt/PVPA. As schematically shown in Fig. 3, methanol is predicted to be difficult to absorb on the active Pt-NP surfaces, meanwhile, the possibility of methanol absorption was almost comparable to oxygen for the MWNT/PyPBI/Pt and conventional CB/Pt.
Peroxide (H 2 O 2 ) is an unwanted product during the ORR since it degrades the FC durability via corrosion of the carbon materials 50 . As shown in Fig. 4(a-c), the H 2 O 2 generations of the CB/Pt, MWNT/ PyPBI/Pt and MWNT/PyPBI/Pt/PVPA were calculated using the equation, %H 2 O 2 = 200I R /(NI D + I R ), where I R and I D are the ring and disk currents obtained from the ORR measurement, respectively, and N is the collection efficiency, which corresponds to the I R /I D ratio (0.404) measured in N 2 -saturated 0.1 M KCl and 1 mM K 3 Fe(CN) 6 31 . These values were accelerated with the increase in the methanol concentrations as shown in Fig. 4d, which was attributed to the decrease in the transferred electrons as shown in Fig. 4(e-g)    In order to study the durability of the electrocatalysts, we tested the durability of three electrocatalysts according to the protocol from the Fuel Cell Conference of Japan (FCCJ) in which the carbon corrosion (C+ 2H 2 O→ CO 2 + 4H + + 4e -, 0.207 V vs. RHE) is accelerated. The loss in carbon supporting material leads to degradation of fuel cell performance due to the loss of the Pt-NPs. As shown in Fig. 5a, the ECSA of the CB/Pt lost ~46% after 10,000 cycles from/to 1.0 to/from 1.5 V vs. RHE is due to the lower carbon corrosion resistance. The MWNT/PyPBI/Pt showed an ~10% loss in the ECSA after the potential cycling, while the MWNT/PyPBI/Pt/PVPA showed the highest durability among the three electrocatalysts (~6% loss in the ECSA) due to the high resistance towards carbon corrosion and the PVPA coating, which also reduced the carbon corrosion and Pt agglomeration. The membrane electrode assemblies (MEAs) were fabricated for practical application in DMFC system. The polarization curves of the MEAs measured under 100% relative humidity (RH) at 70 o C are shown in Fig. 5b. Before applying a current to the single cell, the open circuit voltages (OCVs) were 0.66, 0.69 and 0.82 V for the CB/Pt, MWNT/PyPBI/ Pt and MWNT/PyPBI/Pt/PVPA, respectively, in which the observed higher OCV of the MWNT/PyPBI/ Pt/PVPA suggested a higher methanol tolerance. Even though the MWNTs were coated by PyPBI and PVPA, little or no decrease in the electronic conductivity was observed due to the thin layer of the PyPBI (1-2 nm) 51,52 . The maximum power density of the MEA fabricated from MWNT/PyPBI/Pt/PVPA was 187 mW/cm 2 which was ~2.3 times higher than that of the commercial CB/Pt (81 mW/cm 2 ). The MEA fabricated from MWNT/PyPBI/Pt was 165 mW/cm 2 which was lower than that of the MWNT/PyPBI/ Pt/PVPA due to the homogeneous PVPA coating that acted as a proton conductor during the fuel cell measurement.

Conclusions
In conclusion, we have demonstrated that after a simple coating with PVPA, the obtained MWNT/ PyPBI/Pt/PVPA functions as a cathode electrocatalyst of the DMFCs with a high performance. This electrocatalyst has advantages compared to the previously reported electrocatalysts described in the Introduction since its performance is very high and the preparation method is very simple and easy. Such a high performance is due to the coated PVPA layer that blocks the methanol absorption and has no effect on the O 2 diffusion. As a result, the H 2 O 2 generation was highly restricted (only 0.8% even in the presence of 2 M methanol in the electrolyte, which was much lower than those of the MWNT/PyPBI/ Pt (7.5%) and CB/Pt (20.5%). Meanwhile, the power density of the MWNT/PyPBI/Pt/PVPA was ~2.3 times higher than that of the commercial CB/Pt (81 mW/cm 2 ).
The present study provides a new strategy for the design a practically applicable electrocatalyst as a DMFC cathode with a high methanol tolerance.

Method
Materials. H 2 PtCl 6 ·6H 2 O, 2-propanol, N,N-dimethylacetamide (DMAc), ethylene glycol (EG) and poly(vinylphosphonic acid) (PVPA, 30 wt%) were purchased from Wako Pure Chemical Industry, Ltd. Commercial CB/Pt (Pt amount: 37.9 wt%) was obtained from Tanaka Kikinzuku Kogyo KK. Perchloric acid (70%) was purchased from EMD Millipore Chemical Co., Ltd. Methanol was purchased from Kanto Chemical Co., Inc. All the chemicals were used as received without any purification. The MWNTs with a ~20 nm diameter were kindly provided by Nikkiso Co., Ltd. Gas diffusion electrode (GDE) fabrication. The GDE was fabricated as follows. The electrocatalyst was dispersed in 50 mL of a 2-propanol aqueous solution by sonication for 1 h, then filtrered using a gas diffusion layer (GDL) as a filter paper. The Pt loading amount on the GDL was controlled at 2 mg/ cm 2 . The obtained GDE was dried overnight under vacuum at room temperature to remove any residual solvent.

Synthesis of MWNT/PyPBI
Membrane electrode assembly (MEA) fabrication. The MEA was prepared by hot pressing the prepared GDE and a Nafion 117 membrane. The active area of the MEA was 1 cm 2 .
Characterization. The X-ray photoelectron spectroscopy (XPS) spectra were measured using an AXIS-ULTRA DLD (Shimadzu) instrument. The TGA measurements were conducted using an EXSTAR 6000, Seiko, Inc., instrument at the heating rate of 5 ºC/min under 100 mL/min of air. The TEM micrographs were measured using a JEM-2010 (JEOL, acceleration voltage of 120 kV) electron microscope, in which a copper grid with a carbon support (Okenshoji) was used.
Electrochemical measurement. The electrochemical measurements were performed using a rotating ring disk electrode attached to an RRDE-3 (Bioanalytical Systems, Inc.) with a conventional three-electrode configuration in a vessel at room temperature. A glassy carbon electrode (GCE) with a geometric surface area of 0.196 cm 2 was used as the working electrode. A Pt wire and an Ag/AgCl were used as the counter and reference electrodes, respectively. The potential of the electrode was controlled by an ALS-Model DY2323 (BAS) potentiostat. The electrocatalyst suspension was typically prepared as follows. The electrocatalyst (1.0 mg) was ultrasonically dispersed in an 80% aqueous EG solution (2.0 mL) to form a homogeneous dispersion. A portion of the dispersion was then cast on a GCE to provide an electrocatalyst film, which was air-dried on which the Pt-NPs (14 μ g/cm 2 ) were deposited. The CVs of the electrocatalysts were carried out at a scan rate of 50 mV/s in N 2 -saturated 0.1 M HClO 4 solutions to determine the ECSA values. The oxygen reduction reaction (ORR) was conducted in O 2 -saturated 0.1 M HClO 4 and the given concentration of methanol using a rotation ring disk electrode (RRDE) system (BAS, Inc). MOR evaluation. The methanol oxidation reaction (MOR) was evaluated before and after the durability test using N 2 -saturated 1 M-methanol and 0.1 M HClO 4 at the scan rate of 50 mV/s at room temperature without rotation. The electrode was the same as that used for the ECSA measurements. The Pt loading amounts were controlled at 14 μ g/cm 2 . Before the MOR measurements, 50 cycles were carried out to activate the electrocatalysts.
Durability testing. The carbon corrosion was severely tested using the protocol of the Fuel Cell Commercialization Conference of Japan (FCCJ) 53 (measured in N 2 -saturated 0.1 M HClO 4 at room temperature without rotation), in which the potential was maintained at 1.0 V vs. RHE for 30 s, then applied Scientific RepoRts | 5:12236 | DOi: 10.1038/srep12236 to 1.5 V vs. RHE at the scan speed of 0.5 V/s followed by a potential-return to 1 V vs. RHE. This procedure was cycled, and after every 1000 cycles, ECSA measurements were carried out (see Supplementary  Information, Fig. S8).
Fuel cell testing. The FC performance of the assembled MEAs was evaluated at 70 °C using a computer-controlled fuel cell test system (Model 890e, Scribner Associate, Inc.). The polarization and power density curves were obtained at the atmospheric pressure by flowing 8 M methanol (flow rate = 9 mL/min) and 100% relative humidified air (flow rate = 200 mL/min) to the anode and cathode, respectively.