{'fraction_non_alphanumeric': 0.05369595536959554, 'fraction_numerical': 0.05718270571827057, 'mean_word_length': 4.394736842105263, 'pattern_counts': {'":': 0, '<': 0, '<?xml version=': 0, '>': 0, 'https://': 0, 'lorem ipsum': 0, 'www.': 0, 'xml': 0}, 'pii_count': 0, 'substrings_counts': 0, 'word_list_counts': {'cursed_substrings.json': 0, 'profanity_word_list.json': 0, 'sexual_word_list.json': 0, 'zh_pornsignals.json': 0}}
The novel borate Lu5Ba6B9O27 with a new structure type: synthesis, disordered crystal structure and negative linear thermal expansion.

Single crystals of Lu5Ba6B9O27 were obtained by cooling from a melt and polycrystals of the borate were prepared using a multi-step solid-state synthesis. The crystal structure was determined from single-crystal X-ray diffraction data. The borate crystallizes in a new structure type in the monoclinic crystal system in space group C2/c, with cell parameters a = 13.0927 (3), b = 9.9970 (2) and c = 20.4884 (4) Å, β = 106.827 (1)°, V = 2566.86 (9) Å3 and Z = 4. It is described as a framework composed of rings consisting of vertex-sharing [BO3] triangles and [LuO6] octahedra. The Ba atoms are in the cavities of the framework. The structure is disordered: one of the B atoms is surrounded by six O atoms with partial occupancies of 0.5. The thermal properties of Lu5Ba6B9O27 were investigated by thermal analysis and high-temperature X-ray powder diffraction. Its thermal expansion is highly anisotropic. The negative expansion (contraction) is along the b axis, i.e. parallel to the planes of the largest number of [BO3] triangles. The coefficient of negative linear expansion ranges from -1.42 (at 20°C) to -5.57 × 10-6 °C-1 (at 1000°C). Thermal deformation of the ac plane is described in terms of the theory of shear deformation of monoclinic crystals. The Lu5Ba6B9O27 sample melts at 1170°C.