{'fraction_non_alphanumeric': 0.04142011834319527, 'fraction_numerical': 0.03057199211045365, 'mean_word_length': 5.34375, 'pattern_counts': {'":': 0, '<': 0, '<?xml version=': 0, '>': 0, 'https://': 0, 'lorem ipsum': 0, 'www.': 0, 'xml': 0}, 'pii_count': 0, 'substrings_counts': 0, 'word_list_counts': {'cursed_substrings.json': 0, 'profanity_word_list.json': 0, 'sexual_word_list.json': 0, 'zh_pornsignals.json': 0}}
Upconversion Luminescence and Temperature Sensing of InNbO4:Er3+/Yb3+ Phosphors

Er3+/Yb3+ co-doped InNbO4 phosphors were synthesized using solid state reaction method. Crystal structure was characterized using X-ray diffraction (XRD), which confirm all obtained phosphors had a monoclinic-wolframite structure and no impurity phase
 was introduced upon doping. Upon 980 nm excitation, upconversion (UC) emission from Er3+ ions was observed in green and red range. UC emission was obviously enhanced after co-doping Yb3+ ions and reached the maximum for 10 mol% Yb3+ ions. The relation between
 emission intensity and pump power was performed, revealing that the UC emission result from two-photon processes. Optical temperature sensing property was investigated by exploiting fluorescence intensity ratio (FIR) between 2H11/2 and 4S3/2 levels
 of Er3+ ions. Its maximum value of absolute sensitivity obtained was 0.0091 K-1, suggesting InNbO4:Er3+/Yb3+ phosphors show potential application in optical thermometry.