{'fraction_non_alphanumeric': 0.026840490797546013, 'fraction_numerical': 0.02223926380368098, 'mean_word_length': 4.878378378378378, 'pattern_counts': {'":': 0, '<': 0, '<?xml version=': 0, '>': 0, 'https://': 0, 'lorem ipsum': 0, 'www.': 0, 'xml': 0}, 'pii_count': 0, 'substrings_counts': 0, 'word_list_counts': {'cursed_substrings.json': 0, 'profanity_word_list.json': 0, 'sexual_word_list.json': 0, 'zh_pornsignals.json': 0}}
[Coordination and local structure of Si and Al in silicate glasses and melts: X-ray absorption spectroscopic study].

The coordination and local structure of Si and Al in silicate glasses and melts have been studied using Si and Al K-edge X-ray absorption spectroscopy for the first time. It has been verified that in SiO2-P2O5 and Na2O-SiO2-P2O5 join phosphate silicate glasses, Si atoms remains tetrahedrally coordinated with oxygen when the content of P2O5 is below 32 mol%, but partial Si atoms become octahedrally coordinated with oxygen when the content of P2O5 increases above 32 mol%, and the proportion of the octahedrally coordinated Si atoms increases with the increasing content of P2O5. It has also been demonstrated that Al remains four-fold coordinated with oxygen in ambient NaAlSi2O6-NaAlSi3O8 glasses, but in the same composition glasses quenched at 4.4 GPa and 1,575 degrees C, partial Al atoms becomes five- and six-fold coordinated with oxygen, and at the same pressure and temperature, the proportions of five- and six-fold coordinated Al atoms increases with the increasing content of NaAlSi2O6 in the glasses. Thus, the pressure-induced coordination change of Al in aluminosilicate glasses and melts has been observed for the first time by Al K-edge X-ray absorption spectroscopy.