{'fraction_non_alphanumeric': 0.01882693700217234, 'fraction_numerical': 0.002172338884866039, 'mean_word_length': 5.115044247787611, 'pattern_counts': {'":': 0, '<': 0, '<?xml version=': 0, '>': 0, 'https://': 0, 'lorem ipsum': 0, 'www.': 0, 'xml': 0}, 'pii_count': 0, 'substrings_counts': 0, 'word_list_counts': {'cursed_substrings.json': 0, 'profanity_word_list.json': 0, 'sexual_word_list.json': 0, 'zh_pornsignals.json': 0}}
Behavior of the bone-titanium interface after push-in testing: a morphological study.

Fourteen titanium dental implants (Tioblast) were implanted singly in the proximal tibia of New Zealand rabbits for 120 days. A bone defect was surgically produced and filled with Bio-Oss around six of these implants. After the animals were sacrificed and their organs harvested, bone segments were fixed and methacrylate embedded after the push-in test had been performed. Microradiography was performed on longitudinal sections of the implants, whereas scanning electron microscope analysis was performed on the remaining embedded half-implants using secondary electrons only. The results showed that the implants were apically and coronally surrounded by bone, whether Bio-Oss was used or not. Fractures were evident through the newly formed bone and between the pre-existing and newly formed bone. Some fracture lines propagated through the bone and stopped at the implant surface without continuing along the bone-titanium interface. Detachment between the implant and the bone occurred at the coronal extremity of the implants and along its cervical region. These results highlight the fact that the bone-titanium interface has a high resistance to loading. It exhibited greater resistance than the newly formed bone and seems to behave in a manner similar to the cement lines of osteons.