{'fraction_non_alphanumeric': 0.035164835164835165, 'fraction_numerical': 0.02783882783882784, 'mean_word_length': 5.26605504587156, 'pattern_counts': {'":': 0, '<': 0, '<?xml version=': 0, '>': 1, 'https://': 0, 'lorem ipsum': 0, 'www.': 0, 'xml': 0}, 'pii_count': 0, 'substrings_counts': 0, 'word_list_counts': {'cursed_substrings.json': 0, 'profanity_word_list.json': 0, 'sexual_word_list.json': 0, 'zh_pornsignals.json': 0}}
Porosity‐Controlled TiNb2O7 Microspheres with Partial Nitridation as A Practical Negative Electrode for High‐Power Lithium‐Ion Batteries

Titanium niobium oxide (TiNb2O7) has been recognized as a promising anode material for lithium‐ion batteries (LIBs) in view of its potential to operate at high rates with improved safety and high theoretical capacity of 387 mAh g−1. However, it suffers from poor Li+ ion diffusivity and low electronic conductivity originated from its wide band gap energy (Eg > 2 eV). Here, porous TiNb2O7 microspheres (PTNO MSs) are prepared via a facile solvothermal reaction. PTNO MSs have a particle size of ≈1.2 μm and controllable pore sizes in the range of 5–35 nm. Ammonia gas nitridation treatment is conducted on PTNO MSs to introduce conducting Ti1−xNbxN layer on the surface and form nitridated PTNO (NPTNO) MSs. The porous structure and conducting Ti1−xNbxN layer enhance the transport kinetics associated with Li+ ions and electrons, which leads to significant improvement in electrochemical performance. As a result, the NPTNO electrode shows a high discharge capacity of ≈265 mAh g−1, remarkable rate capability (≈143 mAh g−1 at 100 C) and durable long‐term cyclability (≈91% capacity retention over 1000 cycles at 5 C). These results demonstrate the great potential of TiNb2O7 as a practical high‐rate anode material for LIBs.