{'fraction_non_alphanumeric': 0.04251968503937008, 'fraction_numerical': 0.004724409448818898, 'mean_word_length': 4.834862385321101, 'pattern_counts': {'":': 0, '<': 0, '<?xml version=': 0, '>': 0, 'https://': 0, 'lorem ipsum': 0, 'www.': 0, 'xml': 0}, 'pii_count': 0, 'substrings_counts': 0, 'word_list_counts': {'cursed_substrings.json': 0, 'profanity_word_list.json': 0, 'sexual_word_list.json': 0, 'zh_pornsignals.json': 0}}
Magnetic and Electric Properties in C/Mn/C/Si Multilayers

We have investigated the magnetic and electric properties of C/Mn/C/Si multilayers and found that annealing at temperatures above 590 K causes ferromagnetism at room temperature in the C/Mn/C/Si multilayers, although the as-deposited multilayers are not ferromagnetic. No known ferromagnetic compound is observed in the C/Mn/C/Si multilayers. Electrical resistance of the C/Mn/C/Si multilayers increases as temperature decreases for a current-flow perpendicular to the film plane (CPP). The changes in the resistance indicate that the C/Mn/C/Si multilayers are semiconductive.