{'fraction_non_alphanumeric': 0.04103053435114504, 'fraction_numerical': 0.015267175572519083, 'mean_word_length': 4.701086956521739, 'pattern_counts': {'":': 0, '<': 0, '<?xml version=': 0, '>': 0, 'https://': 0, 'lorem ipsum': 0, 'www.': 0, 'xml': 0}, 'pii_count': 0, 'substrings_counts': 0, 'word_list_counts': {'cursed_substrings.json': 0, 'profanity_word_list.json': 0, 'sexual_word_list.json': 0, 'zh_pornsignals.json': 0}}
Structural study of poly(L-lactic acid) spherulites.

Spherulites of poly(L-lactic acid) (PLLA) and of its blends with atactic poly(3-hydroxybutyrate) (a-PHB, from 10 to 75 wt %) were investigated by microfocus X-ray diffraction using synchrotron radiation. Radial scans in 5 microm steps with 3 microm beam diameter were performed. In PLLA, tens of identical diffraction images were collected. The unit cell a-axis was radially oriented, and the other axes lacked any specific orientation. In contrast, all PLLA/a-PHB blends showed a periodic change of diffraction pattern with increasing distance from the spherulite center. In all cases, the a-axis lay along the radius, while the b- and c-axes rotated about a with a defined periodicity. The unit cell twisting frequency increased with a-PHB content and closely matched the band spacing observed by polarized optical microscopy, which changed from 250 to 60 microm when the amount of a-PHB increased from 10 to 75 wt %. Concomitantly, a gradual broadening of all X-ray reflections was observed.