{'fraction_non_alphanumeric': 0.021638330757341576, 'fraction_numerical': 0.0020607934054611026, 'mean_word_length': 5.305194805194805, 'pattern_counts': {'":': 0, '<': 0, '<?xml version=': 0, '>': 0, 'https://': 0, 'lorem ipsum': 0, 'www.': 0, 'xml': 0}, 'pii_count': 0, 'substrings_counts': 0, 'word_list_counts': {'cursed_substrings.json': 0, 'profanity_word_list.json': 0, 'sexual_word_list.json': 0, 'zh_pornsignals.json': 0}}
Production of Single Tracks of Ti-6Al-4V by Directed Energy Deposition to Determine the Layer Thickness for Multilayer Deposition.

Directed Energy Deposition (DED), which is an additive manufacturing technique, involves the creation of a molten pool with a laser beam where metal powder is injected as particles. In general, this technique is employed to either fabricate or repair different components. In this technique, the final characteristics are affected by many factors. Indeed, one of the main tasks in building components by DED is the optimization of process parameters (such as laser power, laser speed, focus, etc.) which is usually carried out through an extensive experimental investigation. However, this sort of experiment is extremely lengthy and costly. Thus, in order to accelerate the optimization process, an investigation was conducted to develop a method based on the melt pool characterizations. In fact, in these experiments, single tracks of Ti-6Al-4V were deposited by a DED process with multiple combinations of laser power and laser speed. Surface morphology and dimensions of single tracks were analyzed, and geometrical characteristics of melt pools were evaluated after polishing and etching the cross-sections. Helpful information regarding the selection of optimal process parameters can be achieved by examining the melt pool features. These experiments are being extended to characterize the larger blocks with multiple layers. Indeed, this manuscript describes how it would be possible to quickly determine the layer thickness for the massive deposition, and avoid over or under-deposition according to the calculated energy density of the optimum parameters. Apart from the over or under-deposition, time and materials saving are the other great advantages of this approach in which the deposition of multilayer components can be started without any parameter optimization in terms of layer thickness.