{'fraction_non_alphanumeric': 0.03225806451612903, 'fraction_numerical': 0.02729528535980149, 'mean_word_length': 5.1421319796954315, 'pattern_counts': {'":': 0, '<': 0, '<?xml version=': 0, '>': 0, 'https://': 0, 'lorem ipsum': 0, 'www.': 0, 'xml': 0}, 'pii_count': 0, 'substrings_counts': 0, 'word_list_counts': {'cursed_substrings.json': 0, 'profanity_word_list.json': 0, 'sexual_word_list.json': 0, 'zh_pornsignals.json': 0}}
Microstructure and Optical Properties of ZnS:Mn Nanocrystals

Abstract. By using Na2S•9H2O as source precursor and citric acid as stabilizer, ZnS:Mn nanocrystallines were synthesized by solvothermal method. They were annealed at 800 oC in the charcoal powder. The structure, morphology and optical properties were investigated by using X-ray diffraction spectra (XRD), scanning electron microscopy (SEM), and Spectrofluorophotometer respectively. The results showed that all unannealed ZnS:Mn nanocrystallines were about 3~5 nm of particle size and have cubic structure, and all annealed samples were about 30-70 nm of particle size and have mixed structure of the cubic phase and hexagonal phase. Moreover, Mn2+ took the place of Zn2+ in ZnS:Mn. With the increment of Mn2+ content, there occurred a strong emission peak at about 596nm which can be attributed to the Mn2 + leap from 4T1 to 6A1. In addition, the intensity of 596nm emission peak first increased and then decreased with the increment of Mn2+ content, reaching a maximum at about 15% of Mn2+ content. After annealing Mn2+ emission peak intensity is about 20 times that before annealing, and the luminescence peak also showed slightly blue shift.