{'fraction_non_alphanumeric': 0.03996017437166999, 'fraction_numerical': 0.02241537053979872, 'mean_word_length': 4.422880490296221, 'pattern_counts': {'":': 0, '<': 0, '<?xml version=': 0, '>': 0, 'https://': 1, 'lorem ipsum': 0, 'www.': 1, 'xml': 0}, 'pii_count': 0, 'substrings_counts': 0, 'word_list_counts': {'cursed_substrings.json': 1, 'profanity_word_list.json': 0, 'sexual_word_list.json': 0, 'zh_pornsignals.json': 0}}
Sustainable Electrochemical NO Capture and Storage System Based on the Reversible Fe 2+ /Fe 3+ -EDTA Redox Reaction

: The removal of nitric oxide (NO), which is an aggregation agent for ﬁne dust that causes air pollution, from exhaust gas has been considered an important treatment in the context of environmental conservation. Herein, we propose a sustainable electrochemical NO removal system based on the reversible Fe 2+ /Fe 3+ -ethylenediamine tetraacetic acid (EDTA) redox reaction, which enables continuous NO capture and storage at ambient temperature without the addition of any sacriﬁcial agents. We have designed a ﬂow-type reaction system in which the NO absorption and emission can be separately conducted in the individual reservoirs of the catholyte and anolyte with the continuous regeneration of Fe 2+ -EDTA by the electrochemical reduction in Fe 3+ -EDTA. A continuous ﬂow reaction using a silver cathode and glassy carbon anode showed that the concentrations of Fe 2+ and Fe 3+ -EDTA in the electrolyte were successfully maintained at a 1:1 ratio, which demonstrates that the proposed system can be applied for continuous NO capture and storage.


Introduction
Recently, the removal of nitric oxide (NO) in exhaust gas generated by the combustion of fossil fuels has been considered an important treatment to ensure a clean atmospheric environment [1][2][3]. NO is not only an aggregation agent for fine dust, which causes air pollution, but it also provokes acid rain and the depletion of the ozone layer. Although the NO concentration in exhausted gas is as low as approximately 500 ppm, NO emission without proper treatment is severely restricted around the world because of the high environmental toxicity [4][5][6]. Thus, selective non-catalyst reduction (SNCR), which involves spraying an ammonia or urea solution at 1000 • C to the exhaust gas to convert NO to N 2 and water (4NH 3 + 6NO → 5N 2 + 6H 2 O) [7,8], has been used industry wide for the NO removal. However, SNCR causes some issues: (i) unreacted hot ammonia solution is frequently released into the air, causing yellow smoke with odor; and (ii) the ammonium salts formed by side reactions cause clogging of the pipelines and act as an aggregation agent for the fine dust. Alternatively, selective catalyst reduction (SCR), which catalytically converts NO to N 2 by using V 2 O 5 , TiO 2 , WO 3 , or MoO 3 catalysis, can be used for NO removal [9,10]. However, the high maintenance cost for the frequent replacement of catalysts due to the poor stability in the given reaction conditions with NO is a major drawback for practical use [10]. Therefore, the development of new solutions that can overcome these issues of SCR and SNCR is required.
NO absorption using Fe complexes has attracted significant attention as an alternative solution for the NO removal [11]. For example, the Fe 2+ -ethylenediamine tertaacetic acid (EDTA) complex can be combined with NO as Fe 2+ -EDTA-NO (Equation (1)) [12]. The equilibrium constant (K c ) and rate constant (k) for this reaction are substantially high, namely K c = 3.48 × 10 6 at 311 K and k = 6.0 × 10 7 M −1 s −1 at 298 K [13], respectively, which demonstrates that NO can be easily and quickly captured by Fe 2+ -EDTA and stably exist as a liquid phase in the Fe 2+ -EDTA solution. In this manner, the solubility of NO in water can significantly be increased from 56 mg/L to the equivalent amount of Fe 2+ -EDTA dissolved in water. In addition, the liquid-phased NO does not only have many benefits in terms of handling and transport compared to NO gas, but also has further possibilities to be converted to value-added chemicals such as ammonia by post-reactions. Nevertheless, due to the poor resistance of Fe 2+ -EDTA to being oxidized to Fe 3+ -EDTA by O 2 in the air, the practical use of Fe 2+ -EDTA for NO removal is still challenging because Fe 3+ -EDTA has no absorption ability. Thus, research efforts have been focused on reducing Fe 3+ -EDTA to Fe 2+ -EDTA in NO removal systems by using a reducing agent or microorganism system [14][15][16][17]. However, the continuous addition of reducing agents is not a promising solution [14], and microorganism systems exhibited very slow reduction speeds and required the repeated addition of nutrients for metabolism [15][16][17]. Meanwhile, a fuel-cell type electrochemical system using the Fe-EDTA mediated NO capture and release has been reported, in which the Fe 2+ /Fe 3+ -EDTA reduction and oxidation reactions with NO gas were paired with the methanol oxidation to CO 2 and the O 2 reduction to water, receptivity, in a dual electrochemical cell [18]. However, this study focused only on utilizing NO mediated Fe-EDTA conversion reaction for the electricity generation, so that their fuel-cell was designed to release NO to the air after the Fe 2+ -to Fe 3+ -EDTA oxidation reaction without any consideration of the environmental hazard of NO gas.
Recently, as the share of renewable energy sources such as solar and wind power in global electricity generation is continuously increasing, chemical synthesis and pollutant treatment through electrochemical methods have rapidly emerged [19][20][21][22][23]. This is an inevitable trend to develop diverse electrochemical processes that can be directly powered by renewables without the loss of energy through conversion to heat or pressure. The performance of an electrochemical system is strongly dependent on the electrode materials and operating conditions. Consequently, engineering the reaction environment such as tuning the electrolyte composition and pH [24], modifying the reactor design and compartment [25], and the altering reactant [26] has become an important factor that significantly affects the product yield and Faraday efficiency of the electrochemical reaction. In this respect, the innovative design of conventional reaction systems could provide new opportunities to extend the usability of electrochemical methods.
In this study, we propose a sustainable electrochemical NO removal system based on the reversible Fe 2+ /Fe 3+ -EDTA redox reaction, which enables the continuous NO capture and storage at ambient temperature without the addition of any sacrificial agents. We designed a flow-type reaction system in which strong NO absorption and fast NO emission was separately conducted in the individual reservoirs of the catholyte and anolyte with the continuous regeneration of Fe 2+ -EDTA by the electrochemical reduction in Fe 3+ -EDTA (Scheme 1a). This system consisted of four steps (Scheme 1b): (i) NO absorption in the Fe 2+ -EDTA solution (Equation (1)); (ii) the electrochemical oxidation of Fe 2+ -EDTA-NO to Fe 3+ -EDTA to release NO from Fe 2+ -EDTA (Equation (2)); (iii) electrochemical regeneration of Fe 2+ -EDTA by the reduction of Fe 3+ -EDTA (Equation (3)); and (iv) repeated NO absorption using the regenerated Fe 2+ -EDTA solution (Equation (1)).
(i, iv) Fe 2+ -EDTA (l) + NO (g) → Fe 2+ -EDTA-NO (l) (1) To enhance the efficiency of the NO capture and storage system, we performed electrode screening to identify the most reactive element for the electrochemical Fe 2+ /Fe 3+ -EDTA redox reaction with strong stability under the given electrolyte conditions. In addition, five different Fe 2+ -complexes were prepared, and their NO absorption capacity and oxidation resistance ability were compared to those of Fe 2+ -EDTA to examine which Fe-complex is most suitable for this NO removal system. The individual conversions of Fe 2+ -EDTA to Fe 3+ -EDTA and Fe 3+ -EDTA to Fe 2+ -EDTA using a half-cell reaction system with glassy carbon cathode and anode were completely conducted with conversion and Faraday efficiencies higher than 90%. Furthermore, in the full-cell reaction system with the silver cathode and glassy carbon anode, the concentration of Fe 2+ and Fe 3+ -EDTA in the electrolyte was maintained at approximately 1:1 ratio for 10 h, which demonstrates that the proposed system can be applied for continuous NO capture and storage. The novelty of our system is that (i) NO capture can be performed semi-permanently without the addition of consumable compounds and degradation of catalysts; (ii) side reactions involving harmful fumes and pipe blockage do not occur; (iii) it is an energy-efficient process compared to SNCR and SCR because electrical energy can be directly consumed by the NO capture reaction; and (iv) valuable NO-derived chemicals such as ammonia or nitric acid can be easily synthesized by post-treatment. Although the NO removal efficiency of the full-cell reaction was not sufficient for practical use, we ensured that the concept of using the reversible electrochemical Fe-complex redox cycle at ambient temperature and pressure could be a promising and environmentally friendly NO removal method that is an alternative to SCR and SNCR.

Preparation of Fe-Complex Solutions
Fe 2+ -EDTA: The Fe 2+ -EDTA solution was prepared by mixing 10 mM FeSO 4 ·7H 2 O and 10 mM Na 2 EDTA·2H 2 O in deionized water. The water was purged with N 2 for 15 min at least before mixing to remove dissolved oxygen. The pH of the as-prepared Fe 2+ -EDTA solution was 2.7. The Fe 3+ -EDTA solution was prepared by exposing the as-prepared Fe 2+ -EDTA solution to air for 24 h.
Synthesis of MPMAA and DPPETS and preparation of Fe 2+ MPMAA and Fe 2+ -(DPPETS) 2 : The (methyl-pyridine-2-ylmethyl-amino)-acetic acid (MPMAA) was synthesized with ethyl sarcosine hydrochloride and pyridine-2-carboxaldehyde. Furthermore, 12.28 g of ethyl sarcosine hydrochloride was dissolved in 400 mL of methanol at 0 • C. Then, 88 mmol pyridine-2-carboxaldehyde in 40 mL methanol and 68.9 mmol solid sodium cyanoborohydride was added to the solution at 0 • C. The resulting clear yellow solution was stirred at room temperature for 18 h. HCl (12.1 M) was added to the solution, and the yellow suspensions were stirred for 2 h. The solvent was removed under vacuum and the residue was basified with saturated aqueous sodium bicarbonate. The resulting mixtures were extracted with methylene chloride, and the organic layer was dried over magnesium sulfate, followed by evaporation of the organic layer under vacuum. The product was purified by chromatography on 250 g of silica gel with 2% triethylamine in ethyl acetate as the eluent. Then, 50.76 mmol of the product was added to 56 mL of 1 M NaOH at 0 • C. The orange suspension was stirred for 3 h at room temperature, washed with benzene (200 mL), and neutralized with 56 mL of 1 M HCl. After stirring for 30 min, the solution was washed with 200 mL of methylene chloride, and the aqueous phase was evaporated under vacuum to dryness. The residue was slurried using absolute ethanol, sonicated, and filtered. The filtrate was evaporated to yield a yellow oil. (9.1 g, 63% overall yield). m-Sulfonated 1,2-bis (diphenylphosphino) ethane (DPPETS) was synthesized using 1,2-bis (diphenylphosphino) ethane (DPPE) and oleum. The DPPE was slowly added to oleum (18−24% SO 3 ) and stirred at 0 • C for 72 h. Then, 25% NaOH (pH 8.5) was added to the solution at 0 • . The aqueous solution was evaporated to reduce the volume to 4 mL.
A methanol was added to the solution to separate DPPETS from reaction residues and for easy evaporation. The mixture was refluxed for 1 h. After hot filtration, the solution was washed with 4MeOH/H 2 O to remove Na 2 SO 4 . The solution was filtered under dry conditions and a white crystalline solid was crystallized from 10 MeOH/H 2 O.

Characterizations
Materials characterizations: The morphology of electrodes was monitored using a FEI Inspect F field emission-scanning electron microscopy (FE-SEM) with an accelerating voltage of 15 kV. The elemental analysis was performed with an energy dispersive spectroscopy (EDS) accessory attached to the FE-SEM equipment. The X-ray diffraction (XRD) patterns of electrodes were obtained using a Panalytical Empyrean XRD with the fixed theta-two theta scan.
Fe 2+ and Fe 3+ concentrations in the Fe-complex solutions: Colorimetry analysis using 1,10-phenanthroline was used to determine the Fe 2+ and Fe 3+ ratios in the Fe-complex solutions. UV/Vis absorbance spectra of the 1,10-phenanthroline added Fe-complex solution after reaction were obtained by using an Agilent Cary 5000 UV-Vis-NIR spectrophotometer. The intensity of the characteristic absorbance of Fe 2+ at 510 nm, which was determined from the as-prepared fresh Fe 2+ -complex solution, was used as the reference for 100% Fe 2+ . The fresh Fe 3+ -complex solution showed almost zero absorbance at 510 nm.
No absorption capacity and oxidation resistance of Fe-complex solutions: 1 mM NO gas was purged into the 5 mM Fe 2+ -complex solutions in the N 2 purged air-tight vial. As each Fe-complex solution showed characteristic absorbance at wavelength between 400 and 600 nm due to NO absorption, NO purging was repeatedly performed until the characteristic absorbance intensity was saturated. The oxidation resistance was analyzed by exposing the as-prepared Fe 2+ -complex solutions to an air condition for 24 h. The concentration of remaining Fe 2+ in the solution was determined by colorimetry analysis using 1,10-phenanthroline.

Electrochemical Measurement
Preparation of electrodes: The surface of the glassy carbon plate was polished with a polishing pad and alumina beads (10 µm and 0.05 µm) to remove native oxide layers. The surfaces of all metal foils and foams were also cleaned by sonication in a 0.5 M H 2 SO 4 solution for 15 min. The foils and foams were subsequently washed with distilled water and dried with N 2 blow.
Cyclic voltammetry (CV) measurements: CV measurements were conducted using a Biologic VSP potentiostat with a three-electrode system composed of a K 2 SO 4 saturated Hg/Hg 2 SO 4 reference electrode (E 0 = 657 mV vs. NHE) and a Pt mesh counter electrode. The surface cleaned glassy carbon plate or metal foils were used for the working electrode. A geometric surface area of all the working electrodes exposed to the electrolyte was 1 cm × 1 cm. The electrolyte was prepared by dissolving 10 mM Fe 2+ -complexes in a N 2 purged 0.1 M Na 2 SO 4 aqueous solution. The pH of the as-prepared Fe 2+ -EDTA solution was 2.7, and the pH of other Fe 2+ -complexes was adjusted to 2.7 by adding 0.5 M H 2 SO 4 or NaOH solution. All the CV curves were obtained at a scan rate of 10 mV s −1 . Electrochemical active surface area (ECSA) of the electrodes was obtained by dividing the double layer capacitance by the intrinsic capacitance of silver (30 µF/cm 2 ) or glassy carbon (33 µF/cm 2 ). The double layer capacitances were determined by CV measurement with different scan rates (10-160 mV/s) in the region of non-Faradaic potential in a 0.1 M Na 2 SO 4 solution (pH 2.7).
Fe-EDTA conversion using half-cell and full-cell systems: A two-electrode system based on a Micro Flow Cell purchased from ElectroCell was used for the continuous Fe-EDTA conversion test. The inner gaskets of the flow cell were modified to reduce the distance between the working and counter electrodes. The glassy carbon foam and Ag foam with a geometric area of 3.2 cm × 3.2 cm were used as working or counter electrodes for this Fe-EDTA conversion test. Nafion 117 was used as the ion-conducive membrane dividing the cathode and anode compartments. Two 80 mL Teflon reservoirs for 10 mM Fe 2+ -and Fe 3+ -EDTA dissolved in a 0.1 M Na 2 SO 4 aqueous solution were connected to the flow cell with silicon tubing. The Fe-EDTA solutions were purged with N 2 for 30 min before the flow was started. The flow rate of the Fe-EDTA solution was controlled at 4 mL min −1 using an EMS Tech EMP-600G2 peristaltic pump. Linear sweep voltammetry (LSV) and chronoamperometry measurements were performed using the glassy carbon or Ag foam working electrode to perform the reduction reaction of Fe 3+ -EDTA to Fe 2+ -EDTA. For the half-cell test, the anolyte and catholyte were individually circulated without mixing each other (Figure 3a). For the full-cell test, a mixed solution of Fe 2+ -EDTA and Fe 3+ -EDTA in a 1:1 ratio was filled into the reservoirs, and the electrolyte was cross-circulated from the reservoir to the cell compartment (Figure 4a). The Fe 2+ -and Fe 3+ -EDTA concentrations in the electrolyte after the reaction were determined by colorimetric analysis using 1,10phenanthroline.
NO absorption and emission tests using the Fe 2+ -EDTA full-cell system: The NOabsorbed Fe 2+ -EDTA (Fe 2+ -EDTA-NO) solution was prepared by purging NO gas. The two-electrode full-cell reaction was performed using an Fe 2+ -EDTA-NO solution. The gas sampling bag was connected to the top of the anolyte reservoir to collect the desorbed NO by the oxidation of Fe 2+ -EDTA-NO. The NO concentration in the captured gas was monitored using a ThermoFisher Scientific NOx analyzer. The ammonia concentration in the Fe-EDTA solution was determined using the indophenol blue method. A 20% v/v sodium hypochlorite solution is dissolved in the citrate solution (20% w/v sodium citrate and 1% w/v sodium hydroxide in water). The Fe-EDTA electrolyte was added to the oxidized citrate solution mixed with the phenol solution (11.1% v/v phenol in ethanol) and the sodium nitroprusside solution (0.5% w/v sodium nitroprusside in water). The mixed solution was stabilized for 6 h. Subsequently, UV/Vis absorbance measurements were performed to determine the ammonia concentration.

Electrochemical Redox Property of Fe-EDTA Solution
The Fe-EDTA complex solution was prepared by dissolving 10 mM FeSO 4 and 10 mM Na 2 EDTA in a 0.1 M Na 2 SO 4 aqueous solution. Na 2 SO 4 was used as a supporting electrolyte because the Na + and SO 4 2− ions did not show any electrochemical reactivity with the working and counter electrodes (Figure 1a) or any side reactions with the Fe-EDTA complex under the given conditions [27,28]. The pH of the 10 mM Fe 2+ -EDTA solution was 2.7. The electrochemical properties of Fe 2+ -EDTA were examined using a glassy carbon electrode (Figure 1a). The cyclic voltammetry (CV) curve before dissolving the Fe 2+ and EDTA 2− precursors did not show any redox wave in the potential range of −0.2-0.8 V vs. RHE. However, the Fe 2+ -EDTA solution clearly showed the reversible redox wave with the oxidation onset of Fe 2+ to Fe 3+ at 0.20 V vs. RHE and the reduction onset of Fe 3+ to Fe 2+ at 0.35 V vs. RHE. The diffusion-limited peak currents of the oxidation and reduction reactions were almost identical at approximately 0.3 mA/cm 2 . This reversible redox feature of the Fe 2+ /Fe 3+ transition was stably maintained until 200 cycles of CV measurement (inset of Figure 1a), which demonstrates that the Fe-EDTA complex system in an aqueous condition can be applied to a sustainable NO capture and storage system. We note that the overall shape of the CV curve in Figure 1a was almost identical to the CV curve drawn using a glassy carbon working electrode and Fe 2+ -EDTA solution at pH 2.2 in the previous study [29]. Moreover, the reversible electrochemical redox property of Fe-EDTA was examined using a variety of metal foils (Ni, Ti, Ag, Cu, Fe, Pt, and W) to find an electrode with a higher reactivity than that of glassy carbon. Ni and Ti showed reversible redox waves in their CV curves; however, Ni was not stable at pH 2.7 and Ti showed a substantial overpotential and low current density for the Fe 2+ /Fe 3+ -EDTA redox reaction (Figure 1b). Ag, Cu, and Fe showed capacitive features for the reduction reaction of Fe 3+ -EDTA to Fe 2+ -EDTA, whereas the oxidation current corresponding to the Fe 2+ -EDTA to Fe 3+ -EDTA transition was linearly generated due to electrode dissolution in the oxidative environment (Figure 1c), which indicates that these electrodes were limited to the reduction reaction only. However, Cu and Fe were not available for the reduction reaction because Cu was gradually dissolved at a pH 2.7 condition and the Fe surface quickly corroded immediately after the redox reaction was initiated. Although Pt and W showed a clear redox wave with a lower overpotential and higher current density for the Fe 2+ /Fe 3+ -EDTA redox reaction than that of glassy carbon, several reaction peaks were observed in addition to the Fe 2+ /Fe 3+ -EDTA redox curve (Figure 1d). This is because Pt and W react with EDTA molecules directly, which results in the degradation of the Fe-EDTA complex structure. This indicates that Pt and W are not available for the sustainable Fe-EDTA redox reaction. Based on these examinations, we discovered that Ag was the only available option for the reduction reaction, in addition to glassy carbon.

NO Absorption Capacity and Electrochemical Redox Property of Diverse Fe-Complexes
As the Fe 2+ -EDTA complex can be easily oxidized to Fe 3+ -EDTA in air, we prepared additional Fe complexes with five different ligand chemicals, namely sodium 2,3-dimercaptopropanesulfonate (DMPS), cysteic acid (CA), (methyl-pyridine-2-ylmethylamino)-acetic acid (MPMAA), triphenylphosphine-3,3 ,3"-trisulfonic acid trisodium (TPPTS), and m-sulfonated 1,2-bis(diphenylphosphino)ethane (DPPETS) to find a replacement for EDTA. These chemicals can stabilize the Fe 2+ state under aqueous conditions by forming a complex molecular structure. All the Fe complexes prepared with these chemicals showed excellent resistance to oxidation by air ( Table 1). The NO absorption capacity of Fe-complexes can be determined through UV/Vis absorbance measurements as each Fe complex showed a characteristic absorbance wavelength due to NO absorption on the Fe 2+ center. All the Fe-complexes, except Fe 2+ -(TPPTS) 2 , can absorb an equivalent amount of NO to the ligand chemical combined with Fe 2+ , which is comparable to the performance of the Fe-EDTA. Although Fe 2+ -(CA) 2 showed the highest NO absorption among all Fe complexes, the precipitation of Fe ions spontaneously proceeded with NO absorption. This indicates that the NO-combined Fe 2+ -(CA) 2 structure is not stable. The electrochemical redox properties of the Fe complexes were examined with a glassy carbon electrode in a 0.1 M Na 2 SO 4 aqueous solution. The Fe 2+ -DMPS and -(CA) 2 showed a clear redox wave corresponding to the Fe 2+ /Fe 3+ transition without any side reactions at the potential ranges between 0.5 to 1.0 V vs. RHE. This was anodically shifted compared to that of Fe 2+ -EDTA (Figure 2a). However, Fe 2+ -(CA) 2 was not available because of the Fe precipitation. In addition, the Fe 2+ -DMPS showed an asymmetrically large oxidation wave for the oxidation reaction of Fe 2+ to Fe 3+ , suggesting that an equilibrium corresponding to the ratio Fe 2+ :Fe 3+ would be difficult to achieve in the continuous redox reaction system because the reactivity for oxidation is substantially higher than that for reduction. Fe 2+ -MPMAA, -(TPPTS) 2 , and -(DPPETS) 2 showed additional reaction peaks in their redox wave curves as the ligands reacted with the electrode (Figure 2b). Fe 2+ -MPMAA and -TPPTS have a corresponding reaction peak near the onset of Fe 2+ oxidation, and Fe 2+ -(DPPETS) 2 showed a reaction peak after the peak current of the Fe 2+ oxidation. Because these side reactions can eventually cause the decomposition of complex molecular structures, MPMAA, TPPTS, and DPPETS are not suitable for a sustainable redox reaction system. These results suggest that Fe-EDTA is the only available option for the proposed sustainable NO removal system.

Fe-EDTA Conversion Using a Half-Cell Reaction System
The continuous electrochemical Fe-EDTA conversion in a flow-type cell was examined using GC and Ag foam to increase the reactivity by maximizing the surface area without modifying the intrinsic catalytic property; therefore, the conversion time could be reduced. The Fe-EDTA conversion using the half-cell reaction, where the oxidation of Fe 2+ -EDTA to Fe 3+ -EDTA and the reduction of Fe 3+ -EDTA to Fe 2+ -EDTA were individually conducted without mixing the catholyte and anolyte in the flow cell (Figure 3a), was first conducted for a clear evaluation of the oxidative and reductive conversion performance of each electrode. The GC foam electrode showed a redox wave identical to that of the GC plate electrode (Figure 3b). The peak current density for the oxidation and reduction reaction was increased up to 6 mA cm −2 by using GC foam, which was approximately 20-fold higher than those by GC plate. The GC foam also showed 500 mV lower onset potentials for the oxidation (0.15 V vs. RHE) and reduction reaction (0.40 V vs. RHE) than those exhibited by the GC plate. The linear sweep voltammetry (LSV) curves for Fe 3+ -EDTA reduction using GC foam in the flow-type cell showed that the reduction reaction started from the cell voltage of −1.50 V and can be conducted without reducing the supporting electrolyte and water until −2.3 V (Figure 3c). The oxidation LSV curve also demonstrated that the Fe 2+ -EDTA oxidation could be safely conducted up to a cell voltage of 2.0 V without the oxidation of the electrolyte (Figure 3d). Based on these results, the half-cell test using GC foam electrodes was performed by applying a cell voltage of −2.0 V at the GC cathode (working electrode). The cell current density started from at −6 mA cm −1 and rapidly decreased to approximately 0 mA cm −1 in 30 min, which indicates that the reductive conversion of Fe 3+ -EDTA to Fe 2+ -EDTA was almost completed in that period (Figure 3e). A charge of 72.7 C was applied during this reaction for an hour. As Fe 2+ -EDTA has a characteristic absorbance peak at a wavelength of 525 nm, whereas Fe 3+ -EDTA does not show any absorbance in the range of 450 to 600 nm, the conversion ratio of Fe-EDTA can be evaluated by UV/Vis absorbance measurements. By comparing the intensity of the absorbance peak at 525 nm between the catholyte and the reference Fe 2+ and Fe 3+ peaks obtained from the as-prepared 100% Fe 2+ -EDTA and Fe 3+ -EDTA solutions, we confirmed that 90% of the Fe 3+ -EDTA in the catholyte was successfully converted into the Fe 2+ -EDTA (Figure 3f). A comparison of the characteristic absorbance peak of the anolyte with the reference peaks demonstrated that 95% of Fe 2+ -EDTA of 95% was oxidized to Fe 3+ -EDTA during the conversion reaction. Considering that the theoretical charge amount for the full conversion of Fe 2+ -EDTA to Fe 3+ -EDTA is 77 C, the Faraday efficiency of this half-cell reaction using GC foam cathode and anode was 95.3% for reductive conversion and 101.2% for the oxidative conversion of Fe-EDTA (the reason for the Faraday efficiency being higher than 100% is explained in the next paragraph).
Furthermore, the half-cell reaction was performed using an Ag foam electrode as a cathode because Ag is the only element that can be limited to the Fe-EDTA reduction reaction without any issues. The Ag cathode showed a 300 mV lower onset potential and 1 mA cm −1 lower current density at −2.0 V for the Fe 3+ -EDTA reduction compared to those of the GC cathode (Figure 3g). Although the LSV curve of the Ag cathode was slightly bumpy, no side reactions that could cause the degradation of the Fe-EDTA solution or Ag stability were observed. The LSV curve of Fe 2+ -EDTA oxidation using the GC anode in the Ag cathode-GC anode system also showed an almost identical shape to that of the GC anode in the GC cathode-anode system (Figure 3f). The constant potential half-cell reaction was performed by applying a cell potential of −1.5 V to the Ag cathode because the GC anode showed a 500 mV lower onset potential for the electrolyte oxidation (dotted line in Figure 3h) compared to that given by the LSV curve of the GC anode in the GC cathodeanode system. Thus, the starting current density was approximately −2.0 mA cm −1 , which was −4.0 mA cm −1 lower than that of the GC cathode in the GC cathode-anode system. The current density was gradually decreased to −0.3 mA cm −1 for an hour, and the charge of 50.6 C was passed during this reaction. The conversion ratio determined by the UV/Vis measurement was 74% for the reduction of Fe 3+ -EDTA to Fe 2+ -EDTA and 92% for the oxidation of Fe 2+ -EDTA to Fe 3+ -EDTA (Figure 3j). The lower reduction conversion rate (74%) compared to that of GC cathode-anode system (90%) is possibly due to the low current density because the feasible applied potential was limited to less than −1.5 V. In addition, the electrochemical active surface area (ESCA) analysis demonstrated that the Ag foam had approximately 7-fold higher ESCA compared to that of the GC foam ( Figure S1), which indicates that the GC has a higher intrinsic electrochemical catalytic reactivity for the Fe 3+ -EDTA to Fe 2+ -EDTA reduction than the Ag foam. We also note that the 18% difference between the reduction, oxidation, and conversion rates in this Ag cathode-GC anode system implies that the Fe 3+ -EDTA to Fe 2+ -EDTA conversion is more difficult than Fe 2+ -EDTA to Fe 3+ -EDTA conversion and/or Fe 2+ -EDTA can be spontaneously converted to Fe 3+ -EDTA without applying any electrochemical energy input. This feature was also observed in the GC cathode-GC anode system; the oxidative conversion ratio was 5% higher than the reductive conversion ratio, which resulted in a Faraday efficiency higher than 100% for the oxidative conversion. The linear sweep voltammetry (LSV) curves of (c) 10 mM Fe 3+ -EDTA reduction and (d) 10 mM Fe 2+ -EDTA oxidation using GC foam cathode and anodes in the half-cell system. (e) J-t and C-t curves of the constant potential half-cell reduction reaction at −2.0 V using GC foam as a working electrode in the half-cell system. (f) UV/Vis absorption spectra to determine of Fe 2+ and Fe 3+ ratio in the electrolyte after the constant potential half-cell reaction (solid lines). The dotted lines represent reference UV/Vis spectra corresponding to 100% of Fe 2+ and Fe 3+ ratio. The linear sweep voltammetry (LSV) curves of (g) 10 mM Fe 3+ -EDTA reduction using Ag foam cathode and (h) 10 mM Fe 2+ -EDTA oxidation using GC foam anode in the half-cell system. (i) J-t and C-t curves of the constant potential half-cell reduction reaction at −1.5 V using Ag foam as a working electrode in the half-cell system. (j) UV/Vis absorption spectra of electrolyte after the constant potential half-cell reaction. All the LSV curves were obtained with a scan rate of 10 mV s −1 . The flow rate of electrolyte circulation was 4 mL min −1 .

NO Absorption and Emission Using Fe-EDTA Solution in a Full-Cell System
The Fe-EDTA conversion in the full-cell system performed by mixing the catholyte and anolyte was conducted using the GC-GC and Ag-GC electrode configurations (Figure 4a). Full-cell Fe-EDTA conversion without NO absorption and release was first performed to determine whether the equilibrium between Fe 2+ -EDTA and Fe 3+ -EDTA concentrations can be consistently maintained with the given electrode configuration and potential. Changes in the Fe 2+ -EDTA ratio in the reservoirs were monitored every 2 h for 10 h. The J-t curve of constant potential conversion with the GC cathode (as the working electrode)-GC anode system under −2.0 V showed the gradual decrease of the current density to approximately −1.1 mA cm −1 (Figure 4b). Furthermore, the Fe 2+ -EDTA ratio was gradually increased from 50% to 80% during the reaction. We assume that this continuous increase in the Fe 2+ -EDTA concentration is possibly because the GC electrode has a higher reactivity for the reduction reaction than the oxidation (Figure 3c,d); therefore, the equilibrium state would be difficult to sustain for a long period. The full-cell Fe-EDTA conversion using the Ag cathode (as the working electrode)-GC anode system was also performed by applying a cell potential of −1.5 V for 12 h. Although the starting current density was lower than that of the GC cathode-anode system, a steady current density of approximately −0.4 mA cm −1 was continuously maintained for 8 h. Moreover, the initial Fe 2+ -EDTA concentration of 50% was successfully maintained until the end of the reaction. These results demonstrate that Ag cathode-GC anode is a better combination for achieving a sustainable Fe-EDTA redox system because the reactivity between the reduction by Ag and oxidation by GC can be matched to an equivalent level in the given reaction system. The stability of electrodes was examined using SEM and XRD measurement. The microporous morphology of GC foam was fully maintained after the full-cell reaction, and the smooth surface of frame was not changed (Figure S2a,b). The Ag foam also showed identical microporous morphology before and after the reaction ( Figure S2c,d); however, the smooth semicircular surface was slightly changed with the creation of small particles on the surface. Considering that the elemental ratio of oxygen on the Ag foam was increased after the full-cell reaction (Table S1), this morphological change in Ag surface is possibly due to the creation of silver hydroxides or oxides during the reaction. Nevertheless, the surface morphology change does not indicate that the Ag cathode is unstable in the given reaction conditions because the reduction reactivity of Ag cathode was stably maintained during the reaction (Figure 4c). Furthermore, the strong crystallinity of Ag foam was identically maintained before and after reaction ( Figure S3a).
The NO removal performance was examined using a full-cell reaction system with Ag cathode-GC anode in a NO-saturated 30 mM Fe 2+ -EDTA solution (Fe 2+ -EDTA-NO). An identical applied potential of −1.5 V was applied to the Ag cathode for 24 h. The J-t curve slightly fluctuated between −2.5 to −1.5 mA cm −1 for the first 8 h and a steady current of approximately −1.8 mA cm −1 was stably generated for the last 16 h (Figure 4d). The NO emitted by the oxidation of Fe 2+ -EDTA-NO was captured in the gas sampling bag connected to the anolyte reservoir. The amount of NO was 2.28 mM, which was 7.6% of that absorbed onto the 30 mM Fe 2+ -EDTA. We discovered that a large amount of the absorbed NO was directly converted to NH 4 + by the reduction of the Ag cathode. This is possibly because the reaction kinetics of NO reduction to NH 4 + by the Ag cathode is much faster than that of the oxidation to emit NO by the GC anode. This results in a significant difference between the amount of emitted NO and produced NH 4 + . We note that since the NO absorption to Fe 2+ -EDTA is a thermodynamic reaction, and not an electrochemical reaction, the NO absorption reservoir can be operated separately from the electrochemical cell. This method would be advantageous to improve the energy efficiency of the electrochemical cell because if the NO absorption speed to the Fe 2+ -EDTA solution is not fast enough to instantaneously spread throughout the solution in the anodic compartment, the Fe 2+ -EDTA oxidation and the Fe 3+ -EDTA reduction reactions will be conducted without involving the NO capture and release.

Conclusions
In conclusion, we proposed and demonstrated a sustainable electrochemical NO removal system using a reversible Fe 2+ /Fe 3+ -EDTA redox reaction under aqueous conditions. We designed a flow-type reaction system in which the NO absorption and emission can be separately conducted in the individual reservoirs of the catholyte and anolyte with the continuous regeneration of the Fe 2+ -EDTA by the electrochemical reduction of Fe 3+ -EDTA.
We discovered that although the reduction reactivity of Ag was lower than that of GC, the Ag cathode-GC anode electrode configuration stabilized the Fe 2+ -and Fe 3+ -EDTA ratio to 1:1 for a long period. NO was successfully captured by the Fe 2+ -EDTA solution by creating Fe 2+ -EDTA-NO in the liquid phase, and 7.6% of the adsorbed NO was emitted by the oxidation reaction of Fe 2+ -EDTA-NO in the flow-type reaction system. The low efficiency of NO emission is possibly due to the reaction kinetics of NO reduction to NH 4 + by the Ag cathode, which is much faster than oxidation to emit NO by the GC anode. This imbalance between the anodic and cathodic reactions must be overcome for practical use. However, the proposed concept is innovative because the gas removal process can be conducted semi-permanently without the addition of any consumable compounds or harmful side reactions at ambient temperature and pressure, enabling energy-efficient and environmentally friendly NO capture and storage. Therefore, we expect that this gas treatment system using electrochemical metal-complex redox reactions will be applicable to diverse pollutant-gas treatments.
Supplementary Materials: The following are available online at https://www.mdpi.com/article/10 .3390/catal12010079/s1, ESCA, SEM, EDS, and XRD analysis of Ag and GC foam electrodes are in the Supplementary Materials. Figure S1, Electrochemical active surface area (ECSA) analysis foam electrodes, Figure S2, SEM images of GC and Ag foam electrodes before and after reaction of full-cell system, Figure S3, XRD patterns of (a) Ag and (b) GC foam electrodes before and after reaction of full-cell, Table S1, Elemental analysis of GC and AG foam electrode before and after reaction of full-cell.