{'fraction_non_alphanumeric': 0.03380281690140845, 'fraction_numerical': 0.024413145539906103, 'mean_word_length': 5.833333333333333, 'pattern_counts': {'":': 0, '<': 0, '<?xml version=': 0, '>': 0, 'https://': 0, 'lorem ipsum': 0, 'www.': 0, 'xml': 0}, 'pii_count': 0, 'substrings_counts': 0, 'word_list_counts': {'cursed_substrings.json': 0, 'profanity_word_list.json': 0, 'sexual_word_list.json': 0, 'zh_pornsignals.json': 0}}
Super Tough, Ultrastretchable, and Thermoresponsive Hydrogels with Functionalized Triblock Copolymer Micelles as Macro-Cross-Linkers.

Vinyl-functionalized thermosensitive Pluronic F127 micelles have been used as multifunctional cross-links for the synthesis of super tough, highly resilient and thermoresponsive nanomicelle (NM) hydrogels. Pluronic F127 diacrylate (F127DA) with vinyl groups on both ends self-assembled in aqueous solution into micelles. Such micelles served as multifunctional macro-cross-links to copolymerize with acrylamide (AAm) monomers, generating novel NM hydrogels with extraordinary tensile and compressive properties, without using any chemical cross-linkers. Uniaxial tensile tests demonstrated a fracture strain above 2265%, an ultimate stress of 276 kPa, and a fracture energy of 2.34 MJ/m3. Under compression tests, these hydrogels did not fracture up to 98% strain and 62 MPa stress. Cyclic compressive loading-unloading tests at 90% strain showed no decay of the hyseteresis energy, indicating an unprecedented fatigue resistance.