{'fraction_non_alphanumeric': 0.031082028511334424, 'fraction_numerical': 0.032640024927942664, 'mean_word_length': 4.586597040905135, 'pattern_counts': {'":': 0, '<': 1, '<?xml version=': 0, '>': 1, 'https://': 0, 'lorem ipsum': 0, 'www.': 0, 'xml': 0}, 'pii_count': 0, 'substrings_counts': 0, 'word_list_counts': {'cursed_substrings.json': 0, 'profanity_word_list.json': 0, 'sexual_word_list.json': 0, 'zh_pornsignals.json': 0}}
Nitrate-Melt Synthesized HT-LiCoO2 as a Superior Cathode-Material for Lithium-Ion Batteries

An electrochemically-active high-temperature form of LiCoO2 (HT-LiCoO2) is prepared by thermally decomposing its constituent metal-nitrates at 700 ºC. The synthetic conditions have been optimized to achieve improved performance with the HT-LiCoO2 cathode in Li-ion batteries. For this purpose, the synthesized materials have been characterized by powder X-ray diffraction, scanning electron microscopy, and galvanostatic charge-discharge cycling. Cathodes comprising HT-LiCoO2 exhibit a specific capacity of 140 mAhg-1 with good capacity-retention over several charge-discharge cycles in the voltage range between 3.5 V and 4.2 V, and can sustain improved rate capability in contrast to a cathode constituting LiCoO2 prepared by conventional ceramic method. The nitrate-melt-decomposition method is also found effective for synthesizing Mg-/Al- doped HT-LiCoO2; these also are investigated as cathode materials for Li-ion batteries.


Experimental
Powder samples of LiCoO 2 were prepared by rapidly heating the mixture of LiNO 3 and Co(NO 3 ) 2 .6H 2 O in the molar ratio of 1.1:1 with an excess of lithium stoichiometry (10 mol %) added to compensate for the lithium losses during the synthesis. In a typical preparation, 3.87 g of LiNO 3 and 14.87 g of Co(NO 3 ) 2 ·6H 2 O were taken in a sintered alumina crucible and introduced to a preheated furnace at 350 ºC. Subsequently, the furnace was programmed for rapid heating to 700 ºC and held there for 1 h. The furnace was then fast cooled to 350 ºC in about 10 min and the crucible removed from the furnace. The sample was crushed and ground well to obtain a fine powder of LiCoO 2. Similarly, Mg-or Al-doped HT-LiCoO 2 with respective compositions of LiCo 0.95 Mg 0.05 O 2 and LiCo 0.95 Al 0.05 O 2 were prepared by taking corresponding metal nitrates in the required stoichiometry with 10 mol % extra lithium nitrate, followed by heating at 700 ºC for 1h. For comparison, HT-LiCoO 2 was also prepared using the conventional solid-state method [9]; this sample is referred to as LiCoO 2 -SS in the text.
Powder X-ray diffraction patterns for the prepared samples were recorded using X'pert PRO-PANalytical Diffractometer with CuK α radiation. The morphology of the powder samples were examined under a Scanning Electron Microscope (HITACHI Model S-3000H). Chemical analyses of the samples were carried out using Perkin-Elmer Atomic Absorption Spectrometer (AAS). Electrochemical tests were conducted using Swagelok-type TM cells assembled in an argon-filled glove box. The positive electrode comprised the ball-milled mixture of 85 wt.% active material with 15 wt.% Super-P Li Carbon (Timcal Belgium) as the conducting additive. Lithium electrode was prepared by pressing a piece of lithium metal onto a thin stainless steel disc. Electrolyte used was 1M LiPF 6 solution in a mixture of ethylene carbonate and dimethyl carbonate in 1:1 ratio by volume. The cells thus fabricated were cycled galvanostatically between 3.5 V and 4.3 V versus lithium using a VMP3Z (Biologica) multi-channel potentiostat/galvanostat.

Results and Discussion
Figures 1(a-d) show the powder X-ray diffraction patterns for the products formed by heating the mixed-metal nitrates of lithium and cobalt in a 1.1:1 molar ratio at varying temperatures between 600 ºC and 900 ºC for 4 h. The diffraction pattern for the product obtained at 600 ºC could be indexed as rhombohedral R 3 m LiCoO 2 along with small amounts of lithium-deficient LiCoO 2 crystallizing in cubic Fm3m structure. X-ray powder diffraction pattern for the product obtained by heating at 700 ºC shows single-phase LiCoO 2 as indexed on the basis of α-NaFeO 2 structure (space group: R 3 m). The lattice parameters obtained by Rietveld refinement of LiCoO 2 -700 sample agree well with those prepared by conventional solid-state method [21] and are given in Table 1. All diffraction patterns show clear (006)/(102) peaks and (018)/(110) split peaks indicating a perfect layered-structure for LiCoO 2 [21]. The diffraction patterns of samples prepared at 800 ºC and 900 ºC comprise a major LiCoO 2 phase crystallizing in rhombohedral structure with a small Co 3 O 4 spinel phase marked with (*) in Figure 1 (c) and (d); the latter arising due to lithium evaporation from the parent compound at high temperatures. I (003) /I (104) intensity ratio decreases with increasing calcination temperature and is sensitive to the degree of cation mixing [22] that influences electrochemical properties substantially. It is clear from the aforesaid X-ray diffraction studies that 700 ºC is the optimal temperature for obtaining pure LiCoO 2 in ordered rock-salt superstructure. In order to determine the optimal duration, the synthesis was carried out with varying heating durations between 15 min and 4 h at 700 ºC. The Xray diffraction patterns for the products formed at different time intervals are presented in Figure 2. It is seen from the diffractograms that the sample prepared at 700 ºC for as low as 15 min matches well with HT-LiCoO 2 pattern with R 3 m space group; the intensity ratio of I (003) /I (104) <1.2 indicating a considerable extent of cation mixing in the crystal lattice. By contrast, the samples synthesized at 700 ºC for 1 h (or more) exhibit I (003) /I (104) >1.2 indicating the absence of cation mixing. On increasing the heating duration beyond 1 h, little change is observed in the diffraction pattern with increase in overall peak intensity owing to the improved crystallinity of the sample.
The increase in crystallinity of the sample with longer heating duration is further corroborated from morphological studies by scanning electron microscopy (SEM). The SEM image for the samples heated at 700 ºC for 1 h shown in Figure 3(a) depicts agglomerates of smaller crystallites of ~1 μm. The sample obtained by heating at 700 ºC for 4 h shows well defined crystals of platelet-like morphology of ~ 50 μm [ Figure 3(b)]. The chemical compositions of the prepared samples obtained from AAS analysis of Li and Co suggest cation stoichiometry to be strongly dependent on the synthesis temperature. LiCoO 2 prepared at 600 ºC shows a slight excess of lithium stoichiometry corresponding to Li 1.09 CoO 2 and closure to the initial stoichiometry of nitrates taken, suggesting little loss of Li during heating. It is noteworthy that impurity peaks corresponding to lithium salts are absent in the X-ray diffractogram. The sample prepared at 700 ºC has its nominal composition as LiCoO 2 while the samples prepared at 800 ºC and above reflect Co 3 O 4 as impurity in the diffractogram albeit the use of 10 mol % excess Li salt in the synthesis. This suggests substantial amount of Li loss at high temperatures. Chemical analyses of these samples were not possible owing to the insolubility of Co 3 O 4 in acids. From the fore going, it is clear that the synthetic conditions have a seminal role in controlling structural as well as compositional aspects of LiCoO 2 that affect its electrochemical activity.  The metal-nitrates-melt decomposition method has added advantage in relation to solution methods as the former results in homogeneously mixed metal ions leading to their effective substitution in the end product. It has been possible to synthesize about 5-6 atom % of Mg-or Al-doped LiCoO 2 . Figure 4 shows powder X-ray diffraction patterns for LiCo 0.95 Mg 0.05 O 2 and LiCo 0.95 Al 0.05 O 2 samples along with the XRD pattern for pristine LiCoO 2 . All these XRD patterns could be indexed to a layered ( b ) ( a ) 10 Table 1 which agrees well with those reported in the literature for similar compositions [23][24]. Substitution of Co 3+ by larger Mg 2+ -ion increases the a and c lattice parameters with c/a ratio of 4.99 while substitution by smaller Al 3+ -ion decreases the alattice parameter and increases the c-lattice parameter resulting in an increased c/a ratio of 5.004. The electrochemical performances of all the LiCoO 2 samples, prepared at different temperatures with varying heat durations, have been evaluated using Swagelok-type cells. The voltage-composition curves for galvanostatic charge/discharge cycling of Li/LiCoO 2 -700 cells at 1 Li/5 h in different voltage ranges are shown in Figures 5(a) and (b) as representative examples.
The smooth charge-discharge curves between 3.5 V and 4.2V show the absence of spinel-phase formation during cycling with the plateau due to Co 3+ /Co 4+ redox process at ~3.9 V. A higher capacity of 150 mAhg -1 is obtained when the cells are cycled between 3.5 V and 4.3 V but the irreversible capacity loss, polarisability and capacity fade are higher compared to cells cycled between 3.5 V and 4.2 V. This is probably due to the change in crystal structure associated with the higher lithium extraction during higher voltage windows. 10 Figure 6 shows the specific capacity values versus cycle number for Li/LiCoO 2 cells with LiCoO 2 samples prepared at different temperatures. The first charge/discharge capacities of the samples prepared at 600 °C, 700 °C and 800 °C are 106/91, 132/122 and 131/114 mAhg -1 , respectively. As obvious from the data, the sample obtained by heating at 600 ºC shows lower capacity and retains only 92% of its initial capacity after 25 cycles, presumably due to the absence of perfect-layered structure as revealed by its X-ray diffraction pattern. By contrast, the sample prepared at 700 °C shows a maximum capacity with an irreversible capacity loss of about 10 mAh/g; the sample retains a capacity value of ∼ 116mAhg -1 after 25 cycles with a capacity loss of only ~ 5%. The initial charge capacity for the sample synthesized at 800 °C is comparable to the sample prepared at 700 °C but its irreversible capacity loss in the first cycle is 17 mAhg -1 that pushes its specific capacity to ~114 mAhg -1 . This is due to the Li-deficiency in the sample brought about by lithium loss at higher temperature. Accordingly, the sintering temperature clearly affects electrochemical behavior of the samples. In this study, the optimum electrochemical performance is observed for stoichiometric LiCoO 2 prepared at 700 °C. In order to compare the electrochemical performance of HT-LiCoO 2 prepared by nitrate-melt method with conventionally prepared samples, the cells of LiCoO 2 prepared by solid state (LiCoO 2 -SS) and nitrate-melt (LiCoO 2 -700) methods have been subjected to cycling at varying rates. The capacity Vs cycle number plot is shown in Figure 7. The data reflect that the sample derived by nitrate-melt method exhibits higher capacity and better rate capability as compared to the sample prepared by conventional ceramic method.  The Mg-doped samples show good reversibility during charge/discharge cycling with first cycle capacity as high as 146 mAhg -1 , a value comparable to un-doped LiCoO 2 . As expected, Mg doping enhances the structural stability with good capacity retention between 3.5 V and 4.3 V in relation to pristine LiCoO 2 . Interestingly, Li/LiCo 0.95 Al 0.05 O 2 cell shows very high initial capacity of ∼ 154 mAhg -1 but has poor capacity retention We have demonstrated that nitrate-melt-decomposition route leads to electrochemically active pristine and doped LiCoO 2 . Although, synthesis of electrochemically active LiCoO 2 through nitrate precursors followed by combustion, sol-gel or flame pyrolysis methods have been reported previously [18][19][20], these methods require a fuel or chelating agent in addition with metal precursors. Generally, the product obtained using these methods have residual carbonaceous matter which requires high-temperature heating for long duration. Besides, in many cases, the product formed is amorphous and requires further calcination for crystallization. In this context, the metal-nitrate-meltdecomposition route is attractive and new. The method is simple as well as cost effective for synthesizing battery grade LiCoO 2 in bulk.

Conclusions
Electrochemically active HT-LiCoO 2 has been prepared by heating nitrate precursors for duration as short as 15 min. LiCoO 2 prepared using this method exhibits varying degrees of cation mixing and crystallinity depending on the synthetic conditions. The samples prepared at 700 ºC for shorter durations are nano-crystalline in nature and exhibit increased rate capability. On increasing the reaction temperature above 700 ºC, samples are found to be lithium deficient. HT-LiCoO 2 obtained by nitrate-melt decomposition at 700 ºC results in a superior cathode material for lithium-ion batteries. The method is also effective for synthesizing Mg-or Al-doped LiCoO 2 . The nitrate-melt decomposition method is simple, cost effective and convenient for large-scale synthesis of LiCoO 2 with better electrochemical performance.