{'fraction_non_alphanumeric': 0.03423438691636302, 'fraction_numerical': 0.030251673586984155, 'mean_word_length': 4.665866538646183, 'pattern_counts': {'":': 0, '<': 0, '<?xml version=': 0, '>': 0, 'https://': 0, 'lorem ipsum': 0, 'www.': 0, 'xml': 0}, 'pii_count': 0, 'substrings_counts': 0, 'word_list_counts': {'cursed_substrings.json': 1, 'profanity_word_list.json': 0, 'sexual_word_list.json': 0, 'zh_pornsignals.json': 0}}
COMPOSITIONS AND THERMO-CHEMICAL ANALYSIS OF BOVINE AND CAPRINE BONES

Studies have been carried out on bovine bone due to its abundance and large quantity of hydroxyapatite (HAP) in it while caprine bone has been understudied. In this study, locally sourced bovine and caprine bones were washed in distilled water, defatted at 120°C for 1.5 hr in a pressure pot, ball-milled, sieved to 150 µm particle size and characterised. The X-ray fluorescence (XRF) and Energy dispersive X-Ray Spectroscopy (EDS) analysis revealed calcium, phosphorus and carbon as the main components. Both bones contained carbon and oxygen due to the presence of organic collagen but the quantity in caprine bone was a bit higher as revealed by the Fourier Transform Infrared Spectroscopy (FTIR) and EDS spectra. A slight difference in thermal decomposition patterns was recorded while X-Ray diffraction analysis (XRD) revealed the presence of identical functional phases. The microstructures showed needle-like and pebble-like shapes for bovine and caprine respectively, also on visual examination of the Scanning Electron Micrograph (SEM), the bovine samples tended to have particle surface roughness more than caprine. Consequently, the chemical properties of both bone raw samples were insignificantly different from each other except for collagen composition and morphology.


INTRODUCTION
The abundant quantity and high quality of hydroxyapatite (HAP) in mammalian bones have made significant inroad in biomedical applications due to its biocompatible and noninflammatory properties. It is also non-toxic, non-immunogenic and bioactive, which make it able to form a bond with the surrounding tissue after bone grafting (Rana et al., 2017). All these properties have made HAP useful in other applications including its use as a drug carrier (Kano et al., 1994) to selectively take drugs to the diseased cells in the body, replacement of bone tissues (Tang et al., 2009), reconstruction of skull defects (Staffa, et al., 2007), tissue engineering, biosensors (Salman et al., 2008), removal of heavy metals (Reichert et al., 2008) and as an important material in artificial bone synthesis (Hirata et al., 2008) because of its chemical and mineral phase that is closely related to bones and teeth, which is the reason for it use as titanium implantation coat in the body as it enables the body system to see the implantation as a natural bone (Mohammed, 2015). Moreover, collagen, which is the organic component of the bone extracellular matrix is also an auspicious biomaterial due to its excellent biocompatibility, cell affinity and biodegradability and consequently, the composite of HAP and collagen scaffolds has been reportedly used to chemically and structurally mimic the natural bone with excellent performance (Sun et al, 2018). Thus, researchers have studied and derived HAP from different sources majorly from mammalian bones (bovine, horse and camel). Feng (2009) stated that bones consist of ~60% inorganic component (HAP), ~30% organic (Collagen) and ~10% water. Among the natural sources that are currently being evaluated for HAP include marine sources (fish bone and fish scale), shell sources (seashell and eggshell) and mineral sources (limestone) (MohdPu'ad et al., 2019). However, fish bone and scales are not as abundant as mammalian bones. Furthermore, as revealed in the literatures, extraction of HAP from shell and limestone sources takes a longer process and use of chemicals as larger percentage of its calcium is in carbonate form and not phosphate. Pig bones can also be used as a source of HAP, but religious sentiments are often associated with it (Venkatesan and Kim, 2013). There are many natural sources that have been studied and bovine bone remains the most well-established source due to its abundance. In the Guardians, (April 08, 2018), it was stated that Lagos State (A state in Southwest Nigeria) residents consume over 8000 cows per day.
Based on calculation by Omole and Ogbiye (2013), 900 tons of bone is yielded daily from slaughtered cows constituting a huge environmental pollution. This situation appears to be similar in other parts of the world. However, for sustainable development, wastes of any class must be processed for value addition (Malla et al., 2020). Caprine bone has been understudied despite it availability. Also having no religion sentiment associated with it making anything 58 Ojo et al., derived from it acceptable by the society (Ramesh et al., 2018). Giving the bovine bones more attention than the others in research domains could be misconstrued as having superior chemical properties to others. This study is carried out to examine their compositions and thermochemical properties to confirm if there are significant differences between the two bone samples. The bovine and caprine bones were obtained from ~ 36 months old and 30-36 months old animals respectively. The bones were thoroughly washed to remove dirt, blood on the surfaces and soaked for 96 hr in water to break the strongly adhering tissues, meat and other impurities.

Preparation of bovine and caprine bone particles
Each of the bones were mechanically broken to 4-10 cm length while a hammer and anvil was used to remove the marrow. This was followed by defatting of the bones in a 10-litre Quink® pressure pot into which 4 L of preheated water was poured and heated to 120°C for 1.5 hr. On cooling, the hot water with fat was poured into a sieve to collect the fat which was weighed when the water has completely drained. It was then oven dried for 8 hr at 80°C.
After oven drying, each of the samples were hammer milled using Broyeur Clero® model 13634, 1.5 kV, France. This process facilitated the bones size reduction to less than 10 mm.
Then the bones particles were subjected to ball milling using a Faure® machine; model 28A20:92, France. The machine has a 5 kg-ceramic of 10-20 mm diameter milling balls with a 10-litre milling barrel. Ball milling was carried out at 40 rpm for 24 hr followed by sieving to 150 µm prior to characterisation.

Chemical and Morphological characterisation
The phase composition of the samples was performed on an EMPYERN XRD-600 Diffractometer (45 kV, 40 mA) with a CuKα (λ=1.54). Radiation over the scanning range (2θ) from 5° to 75° and a step size of 0.026°. To confirm the functional groups present in the raw bone samples, Agilent Technologies® (USA) FTIR analyzer was used to achieve this in the range of 4000-650 cm -1 . Thermogravimetric analysis was carried out using PerkinElmer® TGA Q500 (USA) to analyze the stages in composition and thermal stability of the bovine and caprine bones.The heating started from 30°C to 950°C at 10°C /minute. The raw bovine and Kufa Journal of Engineering, Vol. 12, No. 3, July 2021 59 caprine bones samples were examined using SEM; model Phenom® Eindhoven, Netherlands.
The EDS employed in this study was equipped with the SEM.

General Observations
In the course of defatting, it was observed that the bovine and caprine bones released 6.57 g and 10.57 g of fat per kilogram of the bones respectively. This indicated that caprine bone holds more adsorbed fat than that of bovine. During milling, as shown in Fig. 1, it was observed that bovine bone samples turned grey from yellowish-white, in contrast, the caprine sample that remained unchanged in colour. This may be attributed to heat generated due to attrition during the milling process.

Thermal Decomposition Characteristics
The mass loss curve for the two bone samples are shown in Fig. 2 with mass loss around 100°C, which is associated with loss of moisture (Mkukuma et al., 2004). Between 200°C to 520°C, both samples suffered mass loss associated with decomposition of the organic materials present in the bones. This is mainly collagen and some other organic materials like lipids, chondroitin and keratin sulphate (Manalu et al., 2015). The decomposition temperature of collagen is between these two temperature ranges. There was a slight difference in thermal decomposition patterns of the bone in the range 300°C to 470°C owing to the difference in the quantity of their organic contents.

60
Ojo et al., There was no significant mass loss in the samples beyond 600 o C as most organic substances appeared to have decomposed. Calcium carbonate decomposes above 750°C to give off carbon dioxide (CO2) and any slight change in mass beyond this temperature was attributed to CO2 released (Karunadasa et al., 2019) leaving Calcium oxide (CaO). About 17.8% and 5.2% of bovine and caprine weight percent respectively remained at the end of the analysis. This showed that the organic content was more in raw caprine bone sample.

Constituent Compounds in the Bones
The results of XRF analysis of the raw bovine and caprine bone samples are presented in Table   1. As shown in the

Functional Groups Present in the Bones
The FTIR spectra are a combination of that of HAP and collagen, which are the major constituents of raw bones. On the average, bone samples consist of ~ 60% inorganic component (HAP), 30% organic component and 10% water (Feng 2009). The spectra showed the presence 62 Ojo et al., of Phosphate (PO4 3-), Carbonate (CO3 2-) absorbed water, Amide I and II in both raw samples.
The PO4 3stretching bands in bovine and caprine bone samples appear at wavelength 1018 and 1010 cm -1 respectively (Malla et al., 2020). The characteristic bands for CO3 2were assigned at 1446, 1409, 872 cm -1 for both bovine and caprine samples. The absorbed water in bovine sample appears in bands 2922 and 3276 cm -1 and 2851, 2922 and 3284 cm -1 for caprine sample (Rana et al., 2017). Also, the Amide I and Amide II bands were 1640 and 1543 cm -1 in bovine, and 1636 and 1543 cm -1 in caprine sample respectively, the Amide peaks could be attributed to the presence of protein (Collagen) macromolecules in the raw bones (Al-Sokanee et al., 2009, Bano et al., 2017. The hydroxyl (OH -) band (3568 cm −1 ) was absent in both samples; this may be attributed to the overlapping of impurity bands over the OHband (Malla et al., 2020). Some of the functional groups bands in the two bone samples appeared in the same wavelength while others were in very close wavelength, Table 2. Contrarily, there was variation in the transmittance percentage especially in the collagen band because of difference in the quantity of the organic substances present in each of them. This reflected that caprine sample contains more of organic substance as the transmittance percentage was lower than that of bovine at collagen band. This is in agreement with the spectra reported by Ramesh et al., (2018), also with the EDS result. The positions and intensities of the respective absorption bands can be influenced by changes in the molecule's environment of the samples (Rana et al., 2017).

Crystallographic Phases in the Bones
Fig . 5 shows the X-ray difraction patterns of raw bovine and caprine bone with HAP and collagen peaks. The XRD parameters of the two bone samples showed they have identical phases present. They reflect some of the characteristic peaks correspond to HAP (Piga et al., 2013). Also, the characteristic peaks of collagen were obtained as weak diffraction peak around  samples. The bovine sample seems to have needle-like shape while caprine's was pebble-like.
The particles size of caprine sample appeared to be coarser than that of bovine. This might be as a result of caprine bone having more collagen which means more toughness as stated earlier and consequently, more resistance to milling. On visual examination of the SEM, the bovine sample particles surface appeared rougher than that of caprine bone samples. The particle size, shape and surface roughness tend to have effect on the properties of the particles. The particle