{'fraction_non_alphanumeric': 0.03973356379502962, 'fraction_numerical': 0.01947682384435404, 'mean_word_length': 4.589302544769086, 'pattern_counts': {'":': 0, '<': 0, '<?xml version=': 0, '>': 26, 'https://': 0, 'lorem ipsum': 0, 'www.': 0, 'xml': 0}, 'pii_count': 0, 'substrings_counts': 0, 'word_list_counts': {'cursed_substrings.json': 0, 'profanity_word_list.json': 0, 'sexual_word_list.json': 0, 'zh_pornsignals.json': 0}}
O-Carboxymethyl Chitosan Supported Heterogeneous Palladium and Ni Catalysts for Heck Reaction

Two polymer catalysts (Pd-OCMCS and Ni-OCMCS) with good reusability were synthesized by coordinating Pd and Ni onto O-carboxymethyl chitosan (OCMCS). The chemical structure and thermal stability of prepared catalysts were determined by Fourier transform infrared (FT-IR) spectra, Energy Dispersive Spectrometer (EDS)analysis, X-ray diffraction (XRD), and thermogravimetric analyzer (TG-DTG), and the analysis results showed that the Pd and Ni ions coordinated onto the OCMCS and formed a ligand with the –COOH group, amino groups, and –OH group on the OCMCS, and the EDS and Inductively Coupled Plasma Optical Emission Spectrometry (ICP-OES) analysis results showed that the loading amounts of Pd and Ni were approximately 8.3% and 8.9%, respectively. In the Heck reaction between aryl halides and n-butyl acrylate catalyzed by the prepared catalyst, the test results showed that the product yield followed the order of aryl iodide > aryl bromide > aryl chloride. Additionally, the product yield for the aryl iodide and aryl bromide could reach up to 99% and 96%, respectively. Moreover, the electron-withdrawing and electron-donating property of the group on the aryl also affected the product yield, and the product yield for aryl halides with electron-withdrawing group p-NO2, p-CH3CO, and p-CHO was higher than that with electron-donating group p-CH3.


Introduction
Heck cross-coupling is an important method for carbon-carbon bond synthesis, and has greatly attracted more and more attention for its wide application in the synthesis of dyes, medicines, natural products, pesticides, perfumes, cinnamic acid derivatives, and new polymer materials [1][2][3][4][5]. The palladium-catalyzed Mizoroki-Heck cross-coupling reaction represents one of the most valuable methods for carbon-carbon bond formation in organic synthesis [6,7]. However, its usage is limited in homogeneous reaction systems due to the difficulties in the separation of the product and catalyst from the reaction mixture and the recycling of catalyst. In order to overcome the aforementioned drawbacks, the heterogenization of catalysts has been studied extensively [4,8,9].
Bio-based polymers have attracted worldwide attention because of their potential biomedical applications, and have served as catalyst carriers in chemical reactions [10][11][12]. Chitosan and its derivatives have highly efficient polymer ligands due to their good metal binding properties [13,14]. Khaled D. Khalil et al. [15] synthesized chitosan-grafted-poly(4-vinylpyridine) beads for Michael additions, and it was a recyclable, environmentally friendly biocatalyst. Hardy et al. [16] synthesized chitosan Schiff bases, prepared a Pd(II) complex, and investigated its catalytic activity in Heck and In the curve of OCMCS, the characteristic adsorption peaks at 1407 and 1644 cm −1 correspond to the symmetric and asymmetrical stretching bands of carboxylate anion, and the second adsorption peak (1644 cm −1 ) overlaps with the N-H bend. In order to investigate the interaction between Pd and Ni ions and OCMCS, infrared spectroscopy in the wavenumber range 1000-2000 cm −1 was observed on a large scale, and the results are shown in Figure 1b. It could be seen that in the spectrum of OCMCS-Pd and OCMCS-Ni, the asymmetric C=O stretching vibration peak shifted to 1654 and 1650 cm −1 , respectively, and C-O symmetric stretching absorption peak were shifted to In the curve of OCMCS, the characteristic adsorption peaks at 1407 and 1644 cm −1 correspond to the symmetric and asymmetrical stretching bands of carboxylate anion, and the second adsorption peak (1644 cm −1 ) overlaps with the N-H bend. In order to investigate the interaction between Pd and Ni ions and OCMCS, infrared spectroscopy in the wavenumber range 1000-2000 cm −1 was observed on a large scale, and the results are shown in Figure 1b. It could be seen that in the spectrum of OCMCS-Pd and OCMCS-Ni, the asymmetric C=O stretching vibration peak shifted to 1654 and 1650 cm −1 , respectively, and C-O symmetric stretching absorption peak were shifted to 1401 and 1403 cm −1 , respectively. Thus, it could be concluded that in OCMCS-Pd and OCMCS-Ni, the Pd and Ni ions bind to the carboxylate groups of OCMCS.
Similarly, the characteristic peaks at 1566 cm −1 belonged to the stretching vibration absorption peak of N-H in the -NH 2 group shifted to 1561 cm −1 in the curve of OCMCS-Pd and 1568 cm −1 in the curve of OCMCS-Ni, and the characteristic peaks at 3426 cm −1 belonged to the stretching vibration absorption peak of O-H in the -OH group shifted to 3415 cm −1 in the curve of OCMCS-Pd and 3418 cm −1 in the curve of OCMCS-Ni. As stated above, in the prepared OCMCS-Pd and OCMCS-Ni catalysts, the palladium and nickel ions also bind to the -NH 2 and -OH groups in OCMCS.

Thermal Analysis
Thermal stability of the prepared OCMCS-Pd and OCMCS-Ni catalyst were tested by TG-DTG measurements under Ar atmosphere, and the results are shown in Figure 2. It can be seen from the DTG curves of OCMCS-Pd and OCMCS-Ni that their exothermic peaks were recorded at 290 • C and 293 • C, respectively, suggesting that the prepared catalyst showed a high thermally stability, and that they could be utilized in the C-C coupling reactions [17]. Similarly, the characteristic peaks at 1566 cm −1 belonged to the stretching vibration absorption peak of N-H in the -NH2 group shifted to 1561 cm −1 in the curve of OCMCS-Pd and 1568 cm −1 in the curve of OCMCS-Ni, and the characteristic peaks at 3426 cm −1 belonged to the stretching vibration absorption peak of O-H in the -OH group shifted to 3415 cm −1 in the curve of OCMCS-Pd and 3418 cm −1 in the curve of OCMCS-Ni. As stated above, in the prepared OCMCS-Pd and OCMCS-Ni catalysts, the palladium and nickel ions also bind to the -NH2 and -OH groups in OCMCS.

Thermal Analysis
Thermal stability of the prepared OCMCS-Pd and OCMCS-Ni catalyst were tested by TG-DTG measurements under Ar atmosphere, and the results are shown in Figure 2. It can be seen from the DTG curves of OCMCS-Pd and OCMCS-Ni that their exothermic peaks were recorded at 290 °C and 293 °C, respectively, suggesting that the prepared catalyst showed a high thermally stability, and that they could be utilized in the C-C coupling reactions [17].

XRD Analysis
The prepared catalyst and OCMCS were characterized by X-ray diffraction (XRD), and the results are shown in Figure 3. An obvious diffraction peak at 2θ = 20.1° was observed in the OCMCS pattern. By comparison, it could be seen that, in the prepared catalyst, the diffraction peak of OCMCS showed a decrease in its diffraction intensity as well as a peak broadening phenomenon, caused by the formation of coordinated ligands between OCMCS and palladium/nickel ions mentioned in the FT-IR analysis [22][23][24]. In addition, in the XRD patterns of the prepared catalyst, new diffraction peaks at 2θ = 28.4°, 40.5° in the pattern of Pd-OCMCS ( Figure 3b) and new diffraction peaks at 2θ = 33.2°, 38.1° in the pattern of Ni-OCMCS ( Figure 3c) were observed, implying that the Pd and Ni ions exist in a crystalline state on the OCMCS [25].
Moreover, according to the following equation, it could be calculated that the OCMCS-Ni catalyst showed higher crystallinity values than the OCMCS-Pd catalyst [26].
In which the I110 was the maximum intensity at 20° and Iam was the intensity of amorphous diffraction at 16°.

XRD Analysis
The prepared catalyst and OCMCS were characterized by X-ray diffraction (XRD), and the results are shown in Figure 3. An obvious diffraction peak at 2θ = 20.1 • was observed in the OCMCS pattern. By comparison, it could be seen that, in the prepared catalyst, the diffraction peak of OCMCS showed a decrease in its diffraction intensity as well as a peak broadening phenomenon, caused by the formation of coordinated ligands between OCMCS and palladium/nickel ions mentioned in the FT-IR analysis [22][23][24]. In addition, in the XRD patterns of the prepared catalyst, new diffraction peaks at 2θ = 28.4 • , 40.5 • in the pattern of Pd-OCMCS ( Figure 3b) and new diffraction peaks at 2θ = 33.2 • , 38.1 • in the pattern of Ni-OCMCS ( Figure 3c) were observed, implying that the Pd and Ni ions exist in a crystalline state on the OCMCS [25].
Moreover, according to the following equation, it could be calculated that the OCMCS-Ni catalyst showed higher crystallinity values than the OCMCS-Pd catalyst [26].
Crystalline index (%) = [(I 110 − I am )/I 110 ] × 100 In which the I 110 was the maximum intensity at 20 • and I am was the intensity of amorphous diffraction at 16 • .

SEM-EDS Analysis
The morphology of OCMCS and prepared catalyst were characterized by SEM, and the results are shown in Figure 4. It could be found that the morphologies and particle size of prepared OCMCS-Pd and OCMCS-Ni catalysts were completely different from those of OCMCS, and the prepared catalysts had more regular morphologies. As mentioned in the FT-IR analysis results, the Pd and Ni ions bind to OCMCS through the -COOH, -NH2, and -OH groups, which resulted in a change of the morphology of OCMCS [27]. The EDS spectra were recorded in order to further confirm the presence of the Pd and Ni ions in the prepared catalyst, and it was obvious that the presence of the Pd element in OCMCS-Pd and the Ni element in OCMCS-Ni was determined. Additionally, their loading amount was determined using ICP-OES spectra, and the results showed that the loading amounts of Pd and Ni were approximately 8.3% and 8.9%, respectively.

SEM-EDS Analysis
The morphology of OCMCS and prepared catalyst were characterized by SEM, and the results are shown in Figure 4. It could be found that the morphologies and particle size of prepared OCMCS-Pd and OCMCS-Ni catalysts were completely different from those of OCMCS, and the prepared catalysts had more regular morphologies. As mentioned in the FT-IR analysis results, the Pd and Ni ions bind to OCMCS through the -COOH, -NH 2 , and -OH groups, which resulted in a change of the morphology of OCMCS [27]. The EDS spectra were recorded in order to further confirm the presence of the Pd and Ni ions in the prepared catalyst, and it was obvious that the presence of the Pd element in OCMCS-Pd and the Ni element in OCMCS-Ni was determined. Additionally, their loading amount was determined using ICP-OES spectra, and the results showed that the loading amounts of Pd and Ni were approximately 8.3% and 8.9%, respectively.

SEM-EDS Analysis
The morphology of OCMCS and prepared catalyst were characterized by SEM, and the results are shown in Figure 4. It could be found that the morphologies and particle size of prepared OCMCS-Pd and OCMCS-Ni catalysts were completely different from those of OCMCS, and the prepared catalysts had more regular morphologies. As mentioned in the FT-IR analysis results, the Pd and Ni ions bind to OCMCS through the -COOH, -NH2, and -OH groups, which resulted in a change of the morphology of OCMCS [27]. The EDS spectra were recorded in order to further confirm the presence of the Pd and Ni ions in the prepared catalyst, and it was obvious that the presence of the Pd element in OCMCS-Pd and the Ni element in OCMCS-Ni was determined. Additionally, their loading amount was determined using ICP-OES spectra, and the results showed that the loading amounts of Pd and Ni were approximately 8.3% and 8.9%, respectively.

Heck Cross-Coupling Reactions
The catalytic activities of the prepared OCMCS-Pd and OCMCS-Ni catalysts were tested by the Heck cross-coupling reactions between various substituted aryl halides and n-butyl acrylate, and the results are shown in Tables 1 and 2. For aryl halides in which the ring was substituted by different halogens, the activity of the halides in reactions catalyzed by OCMCS-Pd and OCMCS-Ni followed the order of iodide > bromide > chloride.
In reactions with aryl iodides and aryl bromides, product yields of up to 99% and 96%, respectively, were obtained (Table 1, entries 3 and 7). However, the highest yield obtained in reactions of aryl chlorides was only 51% ( Table 1, entry 8).
For the same aryl halides, the OCMCS-Pd showed a higher catalytic activity than OCMCS-Ni. As shown in Tables 1 and 2, in reactions of aryl chlorides with catalyst OCMCS-Pd, product yields of up to 51% could be obtained ( Table 1, entry 8). However, in the presence of catalyst OCMCS-Ni, the same aryl chlorides did not react at all under the same reaction conditions ( Table 2, entries 8 and 9). It was also found that the electronic properties of aryl halide substituents influenced the yields of the products. It may be seen from Tables 1 and 2 that product yields were higher when the aryl halides contained electron-withdrawing substituents (e.g., p-NO 2 , p-CH 3 CO and p-CHO) than when they contain electron-donating substituents (e.g., p-CH 3 ); i.e., the catalytic activity was higher when aryl halides containing electron-withdrawing substituents were used. It could be seen from Table 1 (entries 8 and 9) that the withdrawing group p-NO 2 improved the product yield of chlorobenzene catalyzed by OCMCS-Pd by 45%. The catalytic activities of the prepared OCMCS-Pd and OCMCS-Ni catalysts were tested by the Heck cross-coupling reactions between various substituted aryl halides and n-butyl acrylate, and the results are shown in Tables 1 and 2. For aryl halides in which the ring was substituted by different halogens, the activity of the halides in reactions catalyzed by OCMCS-Pd and OCMCS-Ni followed the order of iodide > bromide > chloride.
In reactions with aryl iodides and aryl bromides, product yields of up to 99% and 96%, respectively, were obtained (Table 1, entries 3 and 7). However, the highest yield obtained in reactions of aryl chlorides was only 51% ( Table 1, entry 8).
For the same aryl halides, the OCMCS-Pd showed a higher catalytic activity than OCMCS-Ni. As shown in Tables 1 and 2, in reactions of aryl chlorides with catalyst OCMCS-Pd, product yields of up to 51% could be obtained ( Table 1, entry 8). However, in the presence of catalyst OCMCS-Ni, the same aryl chlorides did not react at all under the same reaction conditions ( Table 2, entries 8 and 9). It was also found that the electronic properties of aryl halide substituents influenced the yields of the products. It may be seen from Tables 1 and 2 that product yields were higher when the aryl halides contained electron-withdrawing substituents (e.g., p-NO2, p-CH3CO and p-CHO) than when they contain electron-donating substituents (e.g., p-CH3); i.e., the catalytic activity was higher when aryl halides containing electron-withdrawing substituents were used. It could be seen from Table 1 (entries 8 and 9) that the withdrawing group p-NO2 improved the product yield of chlorobenzene catalyzed by OCMCS-Pd by 45%. The catalytic activities of the prepared OCMCS-Pd and OCMCS-Ni catalysts were tested by the Heck cross-coupling reactions between various substituted aryl halides and n-butyl acrylate, and the results are shown in Tables 1 and 2. For aryl halides in which the ring was substituted by different halogens, the activity of the halides in reactions catalyzed by OCMCS-Pd and OCMCS-Ni followed the order of iodide > bromide > chloride.
In reactions with aryl iodides and aryl bromides, product yields of up to 99% and 96%, respectively, were obtained (Table 1, entries 3 and 7). However, the highest yield obtained in reactions of aryl chlorides was only 51% ( Table 1, entry 8).
For the same aryl halides, the OCMCS-Pd showed a higher catalytic activity than OCMCS-Ni. As shown in Tables 1 and 2, in reactions of aryl chlorides with catalyst OCMCS-Pd, product yields of up to 51% could be obtained ( Table 1, entry 8). However, in the presence of catalyst OCMCS-Ni, the same aryl chlorides did not react at all under the same reaction conditions ( Table 2, entries 8 and 9). It was also found that the electronic properties of aryl halide substituents influenced the yields of the products. It may be seen from Tables 1 and 2 that product yields were higher when the aryl halides contained electron-withdrawing substituents (e.g., p-NO2, p-CH3CO and p-CHO) than when they contain electron-donating substituents (e.g., p-CH3); i.e., the catalytic activity was higher when aryl halides containing electron-withdrawing substituents were used. It could be seen from Table 1 (entries 8 and 9) that the withdrawing group p-NO2 improved the product yield of chlorobenzene catalyzed by OCMCS-Pd by 45%. The catalytic activities of the prepared OCMCS-Pd and OCMCS-Ni catalysts were tested by the Heck cross-coupling reactions between various substituted aryl halides and n-butyl acrylate, and the results are shown in Tables 1 and 2. For aryl halides in which the ring was substituted by different halogens, the activity of the halides in reactions catalyzed by OCMCS-Pd and OCMCS-Ni followed the order of iodide > bromide > chloride.
In reactions with aryl iodides and aryl bromides, product yields of up to 99% and 96%, respectively, were obtained (Table 1, entries 3 and 7). However, the highest yield obtained in reactions of aryl chlorides was only 51% ( Table 1, entry 8).
For the same aryl halides, the OCMCS-Pd showed a higher catalytic activity than OCMCS-Ni. As shown in Tables 1 and 2, in reactions of aryl chlorides with catalyst OCMCS-Pd, product yields of up to 51% could be obtained ( Table 1, entry 8). However, in the presence of catalyst OCMCS-Ni, the same aryl chlorides did not react at all under the same reaction conditions ( Table 2, entries 8 and 9). It was also found that the electronic properties of aryl halide substituents influenced the yields of the products. It may be seen from Tables 1 and 2 that product yields were higher when the aryl halides contained electron-withdrawing substituents (e.g., p-NO2, p-CH3CO and p-CHO) than when they contain electron-donating substituents (e.g., p-CH3); i.e., the catalytic activity was higher when aryl halides containing electron-withdrawing substituents were used. It could be seen from Table 1 (entries 8 and 9) that the withdrawing group p-NO2 improved the product yield of chlorobenzene catalyzed by OCMCS-Pd by 45%. The catalytic activities of the prepared OCMCS-Pd and OCMCS-Ni catalysts were tested by the Heck cross-coupling reactions between various substituted aryl halides and n-butyl acrylate, and the results are shown in Tables 1 and 2. For aryl halides in which the ring was substituted by different halogens, the activity of the halides in reactions catalyzed by OCMCS-Pd and OCMCS-Ni followed the order of iodide > bromide > chloride.
In reactions with aryl iodides and aryl bromides, product yields of up to 99% and 96%, respectively, were obtained (Table 1, entries 3 and 7). However, the highest yield obtained in reactions of aryl chlorides was only 51% (Table 1, entry 8).
For the same aryl halides, the OCMCS-Pd showed a higher catalytic activity than OCMCS-Ni. As shown in Tables 1 and 2, in reactions of aryl chlorides with catalyst OCMCS-Pd, product yields of up to 51% could be obtained ( Table 1, entry 8). However, in the presence of catalyst OCMCS-Ni, the same aryl chlorides did not react at all under the same reaction conditions ( Table 2, entries 8 and 9). It was also found that the electronic properties of aryl halide substituents influenced the yields of the products. It may be seen from Tables 1 and 2 that product yields were higher when the aryl halides contained electron-withdrawing substituents (e.g., p-NO2, p-CH3CO and p-CHO) than when they contain electron-donating substituents (e.g., p-CH3); i.e., the catalytic activity was higher when aryl halides containing electron-withdrawing substituents were used. It could be seen from Table 1 (entries 8 and 9) that the withdrawing group p-NO2 improved the product yield of chlorobenzene catalyzed by OCMCS-Pd by 45%. The catalytic activities of the prepared OCMCS-Pd and OCMCS-Ni catalysts were tested by the Heck cross-coupling reactions between various substituted aryl halides and n-butyl acrylate, and the results are shown in Tables 1 and 2. For aryl halides in which the ring was substituted by different halogens, the activity of the halides in reactions catalyzed by OCMCS-Pd and OCMCS-Ni followed the order of iodide > bromide > chloride.
In reactions with aryl iodides and aryl bromides, product yields of up to 99% and 96%, respectively, were obtained (Table 1, entries 3 and 7). However, the highest yield obtained in reactions of aryl chlorides was only 51% (Table 1, entry 8).
For the same aryl halides, the OCMCS-Pd showed a higher catalytic activity than OCMCS-Ni. As shown in Tables 1 and 2, in reactions of aryl chlorides with catalyst OCMCS-Pd, product yields of up to 51% could be obtained ( Table 1, entry 8). However, in the presence of catalyst OCMCS-Ni, the same aryl chlorides did not react at all under the same reaction conditions ( Table 2, entries 8 and 9). It was also found that the electronic properties of aryl halide substituents influenced the yields of the products. It may be seen from Tables 1 and 2 that product yields were higher when the aryl halides contained electron-withdrawing substituents (e.g., p-NO2, p-CH3CO and p-CHO) than when they contain electron-donating substituents (e.g., p-CH3); i.e., the catalytic activity was higher when aryl halides containing electron-withdrawing substituents were used. It could be seen from Table 1 (entries 8 and 9) that the withdrawing group p-NO2 improved the product yield of chlorobenzene catalyzed by OCMCS-Pd by 45%. The catalytic activities of the prepared OCMCS-Pd and OCMCS-Ni catalysts were tested by the Heck cross-coupling reactions between various substituted aryl halides and n-butyl acrylate, and the results are shown in Tables 1 and 2. For aryl halides in which the ring was substituted by different halogens, the activity of the halides in reactions catalyzed by OCMCS-Pd and OCMCS-Ni followed the order of iodide > bromide > chloride.
In reactions with aryl iodides and aryl bromides, product yields of up to 99% and 96%, respectively, were obtained (Table 1, entries 3 and 7). However, the highest yield obtained in reactions of aryl chlorides was only 51% (Table 1, entry 8).
For the same aryl halides, the OCMCS-Pd showed a higher catalytic activity than OCMCS-Ni. As shown in Tables 1 and 2, in reactions of aryl chlorides with catalyst OCMCS-Pd, product yields of up to 51% could be obtained ( Table 1, entry 8). However, in the presence of catalyst OCMCS-Ni, the same aryl chlorides did not react at all under the same reaction conditions ( Table 2, entries 8 and 9). It was also found that the electronic properties of aryl halide substituents influenced the yields of the products. It may be seen from Tables 1 and 2 that product yields were higher when the aryl halides contained electron-withdrawing substituents (e.g., p-NO2, p-CH3CO and p-CHO) than when they contain electron-donating substituents (e.g., p-CH3); i.e., the catalytic activity was higher when aryl halides containing electron-withdrawing substituents were used. It could be seen from Table 1 (entries 8 and 9) that the withdrawing group p-NO2 improved the product yield of chlorobenzene catalyzed by OCMCS-Pd by 45%. The catalytic activities of the prepared OCMCS-Pd and OCMCS-Ni catalysts were tested by the Heck cross-coupling reactions between various substituted aryl halides and n-butyl acrylate, and the results are shown in Tables 1 and 2. For aryl halides in which the ring was substituted by different halogens, the activity of the halides in reactions catalyzed by OCMCS-Pd and OCMCS-Ni followed the order of iodide > bromide > chloride.
In reactions with aryl iodides and aryl bromides, product yields of up to 99% and 96%, respectively, were obtained (Table 1, entries 3 and 7). However, the highest yield obtained in reactions of aryl chlorides was only 51% (Table 1, entry 8).
For the same aryl halides, the OCMCS-Pd showed a higher catalytic activity than OCMCS-Ni. As shown in Tables 1 and 2, in reactions of aryl chlorides with catalyst OCMCS-Pd, product yields of up to 51% could be obtained ( Table 1, entry 8). However, in the presence of catalyst OCMCS-Ni, the same aryl chlorides did not react at all under the same reaction conditions ( Table 2, entries 8 and 9). It was also found that the electronic properties of aryl halide substituents influenced the yields of the products. It may be seen from Tables 1 and 2 that product yields were higher when the aryl halides contained electron-withdrawing substituents (e.g., p-NO2, p-CH3CO and p-CHO) than when they contain electron-donating substituents (e.g., p-CH3); i.e., the catalytic activity was higher when aryl halides containing electron-withdrawing substituents were used. It could be seen from Table 1 (entries 8 and 9) that the withdrawing group p-NO2 improved the product yield of chlorobenzene catalyzed by OCMCS-Pd by 45%. The catalytic activities of the prepared OCMCS-Pd and OCMCS-Ni catalysts were tested by the Heck cross-coupling reactions between various substituted aryl halides and n-butyl acrylate, and the results are shown in Tables 1 and 2. For aryl halides in which the ring was substituted by different halogens, the activity of the halides in reactions catalyzed by OCMCS-Pd and OCMCS-Ni followed the order of iodide > bromide > chloride.
In reactions with aryl iodides and aryl bromides, product yields of up to 99% and 96%, respectively, were obtained (Table 1, entries 3 and 7). However, the highest yield obtained in reactions of aryl chlorides was only 51% (Table 1, entry 8).
For the same aryl halides, the OCMCS-Pd showed a higher catalytic activity than OCMCS-Ni. As shown in Tables 1 and 2, in reactions of aryl chlorides with catalyst OCMCS-Pd, product yields of up to 51% could be obtained ( Table 1, entry 8). However, in the presence of catalyst OCMCS-Ni, the same aryl chlorides did not react at all under the same reaction conditions ( Table 2, entries 8 and 9). It was also found that the electronic properties of aryl halide substituents influenced the yields of the products. It may be seen from Tables 1 and 2 that product yields were higher when the aryl halides contained electron-withdrawing substituents (e.g., p-NO2, p-CH3CO and p-CHO) than when they contain electron-donating substituents (e.g., p-CH3); i.e., the catalytic activity was higher when aryl halides containing electron-withdrawing substituents were used. It could be seen from Table 1 (entries 8 and 9) that the withdrawing group p-NO2 improved the product yield of chlorobenzene catalyzed by OCMCS-Pd by 45%. The catalytic activities of the prepared OCMCS-Pd and OCMCS-Ni catalysts were tested by the Heck cross-coupling reactions between various substituted aryl halides and n-butyl acrylate, and the results are shown in Tables 1 and 2. For aryl halides in which the ring was substituted by different halogens, the activity of the halides in reactions catalyzed by OCMCS-Pd and OCMCS-Ni followed the order of iodide > bromide > chloride.
In reactions with aryl iodides and aryl bromides, product yields of up to 99% and 96%, respectively, were obtained (Table 1, entries 3 and 7). However, the highest yield obtained in reactions of aryl chlorides was only 51% (Table 1, entry 8).
For the same aryl halides, the OCMCS-Pd showed a higher catalytic activity than OCMCS-Ni. As shown in Tables 1 and 2, in reactions of aryl chlorides with catalyst OCMCS-Pd, product yields of up to 51% could be obtained ( Table 1, entry 8). However, in the presence of catalyst OCMCS-Ni, the same aryl chlorides did not react at all under the same reaction conditions ( Table 2, entries 8 and 9). It was also found that the electronic properties of aryl halide substituents influenced the yields of the products. It may be seen from Tables 1 and 2 that product yields were higher when the aryl halides contained electron-withdrawing substituents (e.g., p-NO2, p-CH3CO and p-CHO) than when they contain electron-donating substituents (e.g., p-CH3); i.e., the catalytic activity was higher when aryl halides containing electron-withdrawing substituents were used. It could be seen from Table 1 (entries 8 and 9) that the withdrawing group p-NO2 improved the product yield of chlorobenzene catalyzed by OCMCS-Pd by 45%. The catalytic activities of the prepared OCMCS-Pd and OCMCS-Ni catalysts were tested by the Heck cross-coupling reactions between various substituted aryl halides and n-butyl acrylate, and the results are shown in Tables 1 and 2. For aryl halides in which the ring was substituted by different halogens, the activity of the halides in reactions catalyzed by OCMCS-Pd and OCMCS-Ni followed the order of iodide > bromide > chloride.
In reactions with aryl iodides and aryl bromides, product yields of up to 99% and 96%, respectively, were obtained (Table 1, entries 3 and 7). However, the highest yield obtained in reactions of aryl chlorides was only 51% (Table 1, entry 8).
For the same aryl halides, the OCMCS-Pd showed a higher catalytic activity than OCMCS-Ni. As shown in Tables 1 and 2, in reactions of aryl chlorides with catalyst OCMCS-Pd, product yields of up to 51% could be obtained ( Table 1, entry 8). However, in the presence of catalyst OCMCS-Ni, the same aryl chlorides did not react at all under the same reaction conditions ( Table 2, entries 8 and 9). It was also found that the electronic properties of aryl halide substituents influenced the yields of the products. It may be seen from Tables 1 and 2 that product yields were higher when the aryl halides contained electron-withdrawing substituents (e.g., p-NO2, p-CH3CO and p-CHO) than when they contain electron-donating substituents (e.g., p-CH3); i.e., the catalytic activity was higher when aryl halides containing electron-withdrawing substituents were used. It could be seen from Table 1 (entries 8 and 9) that the withdrawing group p-NO2 improved the product yield of chlorobenzene catalyzed by OCMCS-Pd by 45%.

Heck Cross-Coupling Reactions
The catalytic activities of the prepared OCMCS-Pd and OCMCS-Ni catalysts were tested by the Heck cross-coupling reactions between various substituted aryl halides and n-butyl acrylate, and the results are shown in Tables 1 and 2. For aryl halides in which the ring was substituted by different halogens, the activity of the halides in reactions catalyzed by OCMCS-Pd and OCMCS-Ni followed the order of iodide > bromide > chloride.
In reactions with aryl iodides and aryl bromides, product yields of up to 99% and 96%, respectively, were obtained (Table 1, entries 3 and 7). However, the highest yield obtained in reactions of aryl chlorides was only 51% ( Table 1, entry 8).
For the same aryl halides, the OCMCS-Pd showed a higher catalytic activity than OCMCS-Ni. As shown in Tables 1 and 2, in reactions of aryl chlorides with catalyst OCMCS-Pd, product yields of up to 51% could be obtained ( Table 1, entry 8). However, in the presence of catalyst OCMCS-Ni, the same aryl chlorides did not react at all under the same reaction conditions ( Table 2, entries 8 and 9). It was also found that the electronic properties of aryl halide substituents influenced the yields of the products. It may be seen from Tables 1 and 2 that product yields were higher when the aryl halides contained electron-withdrawing substituents (e.g., p-NO2, p-CH3CO and p-CHO) than when they contain electron-donating substituents (e.g., p-CH3); i.e., the catalytic activity was higher when aryl halides containing electron-withdrawing substituents were used. It could be seen from Table 1 (entries 8 and 9) that the withdrawing group p-NO2 improved the product yield of chlorobenzene catalyzed by OCMCS-Pd by 45%. the same aryl chlorides did not react at all under the same reaction conditions ( Table 2, entries 8 and 9). It was also found that the electronic properties of aryl halide substituents influenced the yields of the products. It may be seen from Tables 1 and 2 that product yields were higher when the aryl halides contained electron-withdrawing substituents (e.g., p-NO2, p-CH3CO and p-CHO) than when they contain electron-donating substituents (e.g., p-CH3); i.e., the catalytic activity was higher when aryl halides containing electron-withdrawing substituents were used. It could be seen from Table 1 (entries 8 and 9) that the withdrawing group p-NO2 improved the product yield of chlorobenzene catalyzed by OCMCS-Pd by 45%.

Reusability of Catalysts
After Heck reaction of iodobenzene and n-butyl acrylate, the prepared catalysts were recycled by simple filtration, washing with ethanol, and oven drying, and then the leaking amount of Pd and Ni ions in the filtrate and the catalytic activity of recycled catalyst were tested to evaluate the reusability of prepared catalysts, and the results are shown in Figure 5. Firstly, the results of Inductively Coupled Plasma Optical Emission Spectrometry (ICP-OES) analysis showed that the leaking amount of Pd and Ni ions in the filtrate containing the products were only 0.021 and 0.052 mg/kg, respectively, suggesting that the Pd and Ni were well immobilized on the OCMCS. Secondly, it could be seen from Figure 5 that after recycling the OCMCS-Pd and OCMCS-Ni five times, they still showed high cross-coupling reaction activity, and the cross-coupling reactions for OCMCS-Pd and OCMCS-Ni were still over 90% and 72%, suggesting that the prepared catalyst showed good reusability.

Discussion
In this paper, two polymer catalysts were synthesized by coordinating Pd and Ni onto the O-carboxymethyl chitosan (OCMCS). The FT-IR spectral analysis results showed that the Pd and Ni ions coordinated to OCMCS via the carboxyl, amino, and hydroxyl groups [14]. The thermal analysis results showed that the links formed between carboxymethyl chitosan and the metals in the prepared catalysts have good thermal stability, and hence the catalysts could be utilized in the

Reusability of Catalysts
After Heck reaction of iodobenzene and n-butyl acrylate, the prepared catalysts were recycled by simple filtration, washing with ethanol, and oven drying, and then the leaking amount of Pd and Ni ions in the filtrate and the catalytic activity of recycled catalyst were tested to evaluate the reusability of prepared catalysts, and the results are shown in Figure 5. Firstly, the results of Inductively Coupled Plasma Optical Emission Spectrometry (ICP-OES) analysis showed that the leaking amount of Pd and Ni ions in the filtrate containing the products were only 0.021 and 0.052 mg/kg, respectively, suggesting that the Pd and Ni were well immobilized on the OCMCS. Secondly, it could be seen from Figure 5 that after recycling the OCMCS-Pd and OCMCS-Ni five times, they still showed high cross-coupling reaction activity, and the cross-coupling reactions for OCMCS-Pd and OCMCS-Ni were still over 90% and 72%, suggesting that the prepared catalyst showed good reusability.

Discussion
In this paper, two polymer catalysts were synthesized by coordinating Pd and Ni onto the O-carboxymethyl chitosan (OCMCS). The FT-IR spectral analysis results showed that the Pd and Ni ions coordinated to OCMCS via the carboxyl, amino, and hydroxyl groups [14]. The thermal analysis results showed that the links formed between carboxymethyl chitosan and the metals in the prepared catalysts have good thermal stability, and hence the catalysts could be utilized in the

Reusability of Catalysts
After Heck reaction of iodobenzene and n-butyl acrylate, the prepared catalysts were recycled by simple filtration, washing with ethanol, and oven drying, and then the leaking amount of Pd and Ni ions in the filtrate and the catalytic activity of recycled catalyst were tested to evaluate the reusability of prepared catalysts, and the results are shown in Figure 5. Firstly, the results of Inductively Coupled Plasma Optical Emission Spectrometry (ICP-OES) analysis showed that the leaking amount of Pd and Ni ions in the filtrate containing the products were only 0.021 and 0.052 mg/kg, respectively, suggesting that the Pd and Ni were well immobilized on the OCMCS. Secondly, it could be seen from Figure 5 that after recycling the OCMCS-Pd and OCMCS-Ni five times, they still showed high cross-coupling reaction activity, and the cross-coupling reactions for OCMCS-Pd and OCMCS-Ni were still over 90% and 72%, suggesting that the prepared catalyst showed good reusability.

Discussion
In this paper, two polymer catalysts were synthesized by coordinating Pd and Ni onto the O-carboxymethyl chitosan (OCMCS). The FT-IR spectral analysis results showed that the Pd and Ni ions coordinated to OCMCS via the carboxyl, amino, and hydroxyl groups [14]. The thermal analysis results showed that the links formed between carboxymethyl chitosan and the metals in the prepared catalysts have good thermal stability, and hence the catalysts could be utilized in the

Reusability of Catalysts
After Heck reaction of iodobenzene and n-butyl acrylate, the prepared catalysts were recycled by simple filtration, washing with ethanol, and oven drying, and then the leaking amount of Pd and Ni ions in the filtrate and the catalytic activity of recycled catalyst were tested to evaluate the reusability of prepared catalysts, and the results are shown in Figure 5. Firstly, the results of Inductively Coupled Plasma Optical Emission Spectrometry (ICP-OES) analysis showed that the leaking amount of Pd and Ni ions in the filtrate containing the products were only 0.021 and 0.052 mg/kg, respectively, suggesting that the Pd and Ni were well immobilized on the OCMCS. Secondly, it could be seen from Figure 5 that after recycling the OCMCS-Pd and OCMCS-Ni five times, they still showed high cross-coupling reaction activity, and the cross-coupling reactions for OCMCS-Pd and OCMCS-Ni were still over 90% and 72%, suggesting that the prepared catalyst showed good reusability.

Discussion
In this paper, two polymer catalysts were synthesized by coordinating Pd and Ni onto the O-carboxymethyl chitosan (OCMCS). The FT-IR spectral analysis results showed that the Pd and Ni ions coordinated to OCMCS via the carboxyl, amino, and hydroxyl groups [14]. The thermal analysis results showed that the links formed between carboxymethyl chitosan and the metals in the prepared catalysts have good thermal stability, and hence the catalysts could be utilized in the

Reusability of Catalysts
After Heck reaction of iodobenzene and n-butyl acrylate, the prepared catalysts were recycled by simple filtration, washing with ethanol, and oven drying, and then the leaking amount of Pd and Ni ions in the filtrate and the catalytic activity of recycled catalyst were tested to evaluate the reusability of prepared catalysts, and the results are shown in Figure 5. Firstly, the results of Inductively Coupled Plasma Optical Emission Spectrometry (ICP-OES) analysis showed that the leaking amount of Pd and Ni ions in the filtrate containing the products were only 0.021 and 0.052 mg/kg, respectively, suggesting that the Pd and Ni were well immobilized on the OCMCS. Secondly, it could be seen from Figure 5 that after recycling the OCMCS-Pd and OCMCS-Ni five times, they still showed high cross-coupling reaction activity, and the cross-coupling reactions for OCMCS-Pd and OCMCS-Ni were still over 90% and 72%, suggesting that the prepared catalyst showed good reusability.

Discussion
In this paper, two polymer catalysts were synthesized by coordinating Pd and Ni onto the O-carboxymethyl chitosan (OCMCS). The FT-IR spectral analysis results showed that the Pd and Ni ions coordinated to OCMCS via the carboxyl, amino, and hydroxyl groups [14]. The thermal analysis results showed that the links formed between carboxymethyl chitosan and the metals in the prepared catalysts have good thermal stability, and hence the catalysts could be utilized in the

Reusability of Catalysts
After Heck reaction of iodobenzene and n-butyl acrylate, the prepared catalysts were recycled by simple filtration, washing with ethanol, and oven drying, and then the leaking amount of Pd and Ni ions in the filtrate and the catalytic activity of recycled catalyst were tested to evaluate the reusability of prepared catalysts, and the results are shown in Figure 5. Firstly, the results of Inductively Coupled Plasma Optical Emission Spectrometry (ICP-OES) analysis showed that the leaking amount of Pd and Ni ions in the filtrate containing the products were only 0.021 and 0.052 mg/kg, respectively, suggesting that the Pd and Ni were well immobilized on the OCMCS. Secondly, it could be seen from Figure 5 that after recycling the OCMCS-Pd and OCMCS-Ni five times, they still showed high cross-coupling reaction activity, and the cross-coupling reactions for OCMCS-Pd and OCMCS-Ni were still over 90% and 72%, suggesting that the prepared catalyst showed good reusability.

Discussion
In this paper, two polymer catalysts were synthesized by coordinating Pd and Ni onto the O-carboxymethyl chitosan (OCMCS). The FT-IR spectral analysis results showed that the Pd and Ni ions coordinated to OCMCS via the carboxyl, amino, and hydroxyl groups [14]. The thermal analysis results showed that the links formed between carboxymethyl chitosan and the metals in the prepared catalysts have good thermal stability, and hence the catalysts could be utilized in the

Reusability of Catalysts
After Heck reaction of iodobenzene and n-butyl acrylate, the prepared catalysts were recycled by simple filtration, washing with ethanol, and oven drying, and then the leaking amount of Pd and Ni ions in the filtrate and the catalytic activity of recycled catalyst were tested to evaluate the reusability of prepared catalysts, and the results are shown in Figure 5. Firstly, the results of Inductively Coupled Plasma Optical Emission Spectrometry (ICP-OES) analysis showed that the leaking amount of Pd and Ni ions in the filtrate containing the products were only 0.021 and 0.052 mg/kg, respectively, suggesting that the Pd and Ni were well immobilized on the OCMCS. Secondly, it could be seen from Figure 5 that after recycling the OCMCS-Pd and OCMCS-Ni five times, they still showed high cross-coupling reaction activity, and the cross-coupling reactions for OCMCS-Pd and OCMCS-Ni were still over 90% and 72%, suggesting that the prepared catalyst showed good reusability.

Reusability of Catalysts
After Heck reaction of iodobenzene and n-butyl acrylate, the prepared catalysts were recycled by simple filtration, washing with ethanol, and oven drying, and then the leaking amount of Pd and Ni ions in the filtrate and the catalytic activity of recycled catalyst were tested to evaluate the reusability of prepared catalysts, and the results are shown in Figure 5. Firstly, the results of Inductively Coupled Plasma Optical Emission Spectrometry (ICP-OES) analysis showed that the leaking amount of Pd and Ni ions in the filtrate containing the products were only 0.021 and 0.052 mg/kg, respectively, suggesting that the Pd and Ni were well immobilized on the OCMCS. Secondly, it could be seen from Figure 5 that after recycling the OCMCS-Pd and OCMCS-Ni five times, they still showed high cross-coupling reaction activity, and the cross-coupling reactions for OCMCS-Pd and OCMCS-Ni were still over 90% and 72%, suggesting that the prepared catalyst showed good reusability.

Discussion
In this paper, two polymer catalysts were synthesized by coordinating Pd and Ni onto the O-carboxymethyl chitosan (OCMCS). The FT-IR spectral analysis results showed that the Pd and Ni ions coordinated to OCMCS via the carboxyl, amino, and hydroxyl groups [14]. The thermal analysis results showed that the links formed between carboxymethyl chitosan and the metals in the prepared catalysts have good thermal stability, and hence the catalysts could be utilized in the

Discussion
In this paper, two polymer catalysts were synthesized by coordinating Pd and Ni onto the O-carboxymethyl chitosan (OCMCS). The FT-IR spectral analysis results showed that the Pd and Ni ions coordinated to OCMCS via the carboxyl, amino, and hydroxyl groups [14]. The thermal analysis results showed that the links formed between carboxymethyl chitosan and the metals in the prepared catalysts have good thermal stability, and hence the catalysts could be utilized in the C-C coupling reactions. The EDS analysis and ICP-OES analysis results showed that the loading amount of Pd and Ni on the prepared catalysts were approximately 8.3% and 8.9%, respectively.
The test results of the Heck reaction between aryl halides and n-butyl acrylate catalyzed by the prepared catalyst showed that the product yield was affected by the halogen species and the electron-withdrawing and electron-donating property of groups on the aryl. The product yield for the aryl iodide and aryl bromide could reach up to 99% and 96%, respectively, and the product yields for the aryl halides with electron-withdrawing groups p-NO 2 , p-CH 3 CO, and p-CHO were higher than that with electron-donating group p-CH 3 . After reaction, the ICP-OES analysis results showed that the leaking amount of Pd and Ni ions during the reaction was only 0.021 and 0.052 mg/kg. Additionally, the prepared OCMCS-Pd and OCMCS-Ni catalysts still showed 90% and 72% reaction activity after five times recycling, suggesting that the prepared catalyst possessed good reusability.

Physical Measurements
The FT-IR spectra of samples were performed on a FT-IR spectrophotometer (Nicolet I5 America). The thermal stability of the prepared catalyst was analyzed by a thermogravimetric analyzer (NETZSCH STA 449F3, Selb, Germany) under an argon atmosphere at a heating rate of 10 • C·min −1 . The level of crystallinity of the prepared catalysts and OCMCS was analyzed by X-ray diffraction (XRD, MiniFlex 600, Rigaku, Tokyo, Japan) under a 2θ scan angle from 2.5 • to 60 • . The surface morphologies of the samples were examined using field emission scanning electron microscope (S-4800, Hitachi, Tokyo, Japan), and their EDS spectra were determined by EDAX-Metek. In addition, the loading amounts of Pd and Ni on OCMCS were determined with a plasma optical emission spectrometer (Optima 8000, PerkinElmer, Waltham, MA, USA).

Synthesis of OCMCS-Pd and OCMCS-Ni
Firstly, the PdCl 2 and C 4 H 6 NiO 4 aqueous solutions were prepared by the following procedure: the PdCl 2 (0.35 g) and HCl (0.5 g) were dissolved in 10 mL water and stirred for 1 h at room temperature to obtain a complete aqueous solution. Then, the nickel acetate tetrahydrate (1.24 g) was dissolved in 30 mL water.
Secondly, the OCMCS-Pd catalyst was synthesized. At room temperature, the O-carboxymethyl chitosan (OCMCS, 1.97 g) was added into a KOH aqueous solution (0.4 g KOH, 40 mL water) and stirred at 60 • C for 1 h. Then, the prepared water soluble PdCl 2 aqueous solution was added over 30 min to react with OCMCS for 12 h, and the reaction temperature was 60 • C. Then, the reaction solution was poured into a round-bottomed flask, and the water was removed with a rotary evaporator to obtain the concentrated solution. After cooling to room temperature, the ethanol was added into the concentrated solution to give a precipitate. The mixture was filtered, washed with ethanol, and dried at 60 • C in an oven to give the Pd-OCMCS catalyst.