{'fraction_non_alphanumeric': 0.03223263001860788, 'fraction_numerical': 0.023874854133156716, 'mean_word_length': 4.682437275985663, 'pattern_counts': {'":': 0, '<': 1, '<?xml version=': 0, '>': 1, 'https://': 0, 'lorem ipsum': 0, 'www.': 0, 'xml': 0}, 'pii_count': 0, 'substrings_counts': 0, 'word_list_counts': {'cursed_substrings.json': 0, 'profanity_word_list.json': 0, 'sexual_word_list.json': 0, 'zh_pornsignals.json': 0}}
Degradation of inverted architecture CH3NH3PbI3‐xClx perovskite solar cells due to trapped moisture

We explore degradation pathways within encapsulated CH3NH3PbI3‐xClx perovskite devices based on the inverted architecture: ITO/PEDOT:PSS/CH3NH3PbI3‐xClx/PC70BM/LiF/Al. Devices were subjected to more than 670 h of continuous illumination approximating AM1.5, with a Ts80 lifetime of (280 ± 20) hours determined. Devices stored in the dark underwent a similar drop in efficiency over the same time‐period. Using external quantum efficiency, time‐resolved photoluminescence, X‐ray diffraction, scanning electron microscopy and laser beam induced current mapping, we attribute the primary cause of degradation to reactions with residual moisture trapped in the device, resulting in the decomposition of the perovskite.


Introduction
Perovskite solar cells (PSCs) are a promising technology for low-cost photovoltaics. Despite being first realized only 10 years ago [1], PSCs have seen a remarkably rapid rise in power conversion efficiency (PCE), with champion devices now exhibiting efficiencies over 20% [2] -a value that is comparable to crystalline silicon. Notably, PSCs also boast advantages such as being processed from scalable processes such as spray-deposition [3,4] or blade coating [5], together with band gap-tuning by control over composition [6]. It is known, however, that many perovskite materials have relatively limited operational stability (although new classes of perovskite materials appear much more stable [7]). It is therefore important to understand the degradation mechanisms that limit operational stability to mitigate such effects.
To date, most lifetime measurements on PSCs have been conducted on so-called standard architecture devices, in which electron extraction proceeds through a transparent contact positioned on top of the device substrate, with hole extraction occurring via a reflective topcontact. Here, lifetime studies on PSCs utilizing this architecture have included the perovskite materials CH 3 NH 3 PbI 3 and CH 3 NH 3 PbI 3-x Cl x . Here, Chauhan et al. have shown that devices incorporating a CH 3 NH 3 PbI 3- x Cl x mixed halide perovskite within an FTO/TiO 2 / CH 3 NH 3 PbI 3−x Cl x /P3HT/Ag architecture had a T80 lifetime of approximately 200 h and 1100 h under darkstorage [8]. Guarnera et al. used the same structure, but included an additional Al 2 O 3 nanoparticle layer between the perovskite and Spiro-OMeTAD layers [9]. This significantly improved device stability, with a 5% decrease in PCE observed over 350 h. The improvement is attributed to the buffer layer preventing metal atoms migrating into the perovskite layer and increasing current shunt pathways. Recently, Yin et al. demonstrated that CH 3 NH 3 PbI 3 devices incorporating a TiO 2 layer doped with 1% niobium (Nb) retained 89% of their initial PCE after 1200 h [10]. Recent studies have now turned to a study of the stability of multication perovskite materials. In particular, Saliba 3 having remarkably improved stability when held in a nitrogen atmosphere [7]. On illumination, it was found that the PCE decreased by approximately 10% over an initial 250 h period, before then decaying with a half-life of ~5000 h. Further studies have now shown that the stability of caesium-based perovskite devices can be improved through the incorporation of potassium; a result ascribed to the increased phase stability of the reducedvolume lead-halide octahedra [11,12].
We note, however, that relatively few studies have investigated the stability of so-called "inverted architecture" devices. Here, hole extraction occurs through the bottom transparent contact (next to the substrate) with electron extraction occurring via a top reflective contact. Of note, Xie et al. performed a 10 h stability test on unencapsulated ITO/PEDOT:PSS/CH 3 NH 3 PbI 3 /PCBM/PFN-Br/Ag devices in which the devices had either been annealed under vacuum or remained unannealed [13]. It was found that devices that had not been annealed degraded completely within 2 h, whereas annealed devices remained stable. This was attributed to methylammonium chloride within the film absorbing water, enabling the decomposition of the perovskite. Kim et al. also observed complete degradation of unencapsulated CH 3 NH 3 PbI 3 devices within 125 h when stored in air, without illumination [5]. A second "shelflife" study from Kim et al. looked at replacing the PEDOT:PSS hole transport layer with the less hygroscopic copper doped nickel oxide (Cu:NiO x ), resulting in improved stability [14]. Here, the PCE of unencapsulated devices with a PEDOT:PSS hole transport layer decreased by 70% over 250 h, whilst those using Cu:NiO x were reduced by less than 10%. The lower stability of the devices utilizing PEDOT:PSS was speculated to be due to the acidic and hygroscopic nature of the material, resulting in the degradation of the ITO and the perovskite layer.
In this paper, we report a comprehensive study of the operational stability of perovskite solar cells based on the inverted architecture ITO/PEDOT:PSS/CH 3 NH 3 PbI 3-x Cl x / PC 70 BM/LiF/Al. Devices were subjected to 670 h of continuous illumination with JV scans performed every 15 min, whilst being held at open circuit between measurements. Device were also fabricated and stored under dark conditions over a period of 840 h with JV scans measured once a week. External quantum efficiency, time resolved photoluminescence, X-ray diffraction, scanning electron microscopy and laser beam induced current mapping have been used to explore the observed the degradation mechanisms. We find that following a 160 h burn-in period, devices undergo decay characterized by a (stabilized) Ts80 lifetime of approximately 280 h. Devices stored under dark conditions undergo comparable levels of degradation over the same period. Although we cannot rule out additional degradation of the ITO and perovskite due to the acidic nature of the PEDOT:PSS, we speculate that the decomposition of the perovskite is likely to occur via reactions with residual water trapped in the device (most likely within the PEDOT:PSS hole-extraction layer); a process that is likely accompanied by the formation of trap states at the perovskite interface.

Materials and Methods
Perovskite precursor solutions were prepared by mixing PbCl 2 (Sigma-Aldrich, Dorset, UK; 98% pure) and methylammonium iodide (MAI, Ossila Ltd., Sheffield, UK; 99.9% pure) at a ratio of 1.0:2.9 in a N 2 glovebox. Dimethylformamide (DMF, Sigma-Aldrich, 99.8% pure) was added to the mixture to give a total solid content of 660 mg/mL. The solution was left on a hot plate at 70°C overnight to dissolve. Solar cells were fabricated on glass substrates coated by a prepatterned layer of ITO (Ossila Ltd., 20 Ω/□). The substrates were first cleaned by sonication in 5% Hellmanex solution, hot DI water, and isopropyl alcohol (IPA) for 5 min each. Between each sonication the substrates were dump rinsed in hot DI water, and were rinsed with IPA and then dried with nitrogen after the final sonication. A (35 ± 2) nm poly(3,4-ethylenedioxythio phene) poly(styrenesulfonate) (PEDOT:PSS, Ossila Ltd.) holetransport layer was deposited by spin-coating at 5000rpm, and annealed at 125°C for 15 min. The perovskite precursor solution was spin cast in air (relative humidity of (30 ± 2)%) at 4000 rpm from a solution at 70°C onto substrates initially held at 90°C. We note that the ink formulation used here was optimized to work in air, and does not produce working devices if the perovskite is instead deposited in a nitrogen-filled glove box. We have purposely explored this material system, as it is in principle compatible with a high-volume air-based manufacture process. The substrate was then annealed in air at 90°C for 90 min to give a (470 ± 20) nm thick MAPbI 3-x Cl x perovskite layer. A (150 ± 5) nm thick PC 70 BM electron-transport layer was then spin cast at 1000 rpm from chlorobenzene (Sigma-Aldrich, 99.95%) at a concentration of 50 mg/ml in a nitrogen filled glove box. A 2 nm LiF electron-transport layer (0.1 Å/s) and a reflective 100 nm Al cathode (1.0 Å/s) were then deposited by thermal evaporation onto the PC 70 BM at a base pressure of <10 -6 mbar. Finally, the devices were encapsulated under nitrogen. This was performed by depositing one drop of UV curable epoxy (supplied by Ossila Ltd.) onto the device. A glass slide (C181, Ossila Ltd.) was then placed on the epoxy droplet which the spread across the device surface. The epoxy was then cured under a UV lamp (MEGA electronics LV202-E 365 nm peak, P output = 2.5mW/cm 3 ) for 30 min. We have measured the thickness of the cured epoxy layer and find it to be approximately 90 μm. Microscopy measurements performed on such cured epoxy films between glass slides suggest that this film is uniform, homogeneous and devoid of pinholes or gas-bubbles (see Fig. S1). We believe that the thickness of the epoxy film used here is sufficient to absorb the majority of the incident UV radiation used in film curing. For this reason, we do not detect significant perovskite degradation as a direct result of the UV curing stage, although we suspect that some interaction between the uncured epoxy and the device active layer may reduce initial device performance. Once cured we believe that the epoxy protects the device from environmental degradation without causing further degradation in performance.
Devices were characterized under ambient conditions using a Newport 92251A-1000 AM1.5 solar simulator and a Keithley 237 source meter. The output intensity was calibrated to 100 mW/cm 2 using a NREL certified silicon reference cell. An aperture mask was used to define device area to 0.0256 cm 2 . Devices were light-soaked for 20 min and then measured from −1 to 1 V, then 1 to −1 V at a rate of 0.4 V/s. Lifetime data was taken using an Atlas Suntest CPS+ with a 1500 W xenon bulb with IR reducing filters calibrated to 100 mW/cm 2 . Measurements were performed without an aperture mask from −1 to 1 V with a scan rate of 0.1 V/s and devices were held at open circuit between measurements. Further details of the lifetime testing system, including the spectrum of the illumination can be found in reference [15]. External quantum efficiency (EQE) measurements were performed using a tungsten halogen lamp (LOT Oriel LSB117/5), a monochromator, and a Newport 818-UV calibrated silicon photodiode as the reference. Nominally, identical devices were also prepared for dark-storage tests. Here, such samples were wrapped in aluminum foil and placed inside a light-tight container and only removed for JV measurements. The humidity and temperature during dark-storage was 32 ± 2 RH% and 18 ± 2 °C respectively.
Time resolved photoluminescence (TRPL) measurements were performed using a 225 μW, 507 nm pulsed laser (2.5 MHz, 4 μJ/cm 2 ) to excite the sample and a PicoQuant single photon avalanche photodiode to collect the signal. A 550 nm long pass filter was used to prevent laser light from entering the detector. Measurements were performed under dynamic vacuum of at least 10 −3 mbar.
Laser beam induced current (LBIC) mapping was performed on freshly fabricated and devices that had been aged by exposure to light from the solar simulator. The system comprised a mechanically chopped laser that was passed through a spatial filter before being focused to a spot size of ~1 μm onto the sample via a 50x Mitutoyo infinity-corrected long working distance objective. The sample was mounted on a computer controlled XY-stage, and moved in a sawtooth pattern in steps of 1 μm. Two different diode lasers were separately used to generate photocurrent; a blue 3mW, 405 nm diode laser (power density of 27 W/cm 2 ) and a 5 mW, 670 nm (40 W/ cm 2 ). Photocurrent was measured using a Stanford Research Systems SR830 lock-in amplifier referenced to the chopped laser. As the CH 3 NH 3 PbI 3-x Cl x has an absorption that is a strong function of wavelength, photocurrent imaging at different wavelengths will probe the generation of charge carriers at different distances into the bulk of the film. We can in fact quantify this using the values for the real and imaginary refractive index for CH 3 NH 3 PbI 3-x Cl x (see Fig. S4); we calculate that at 405 nm (670 nm) the laser intensity will drop to 1/e of its initial value after penetrating a distance of approximately 30 nm (230 nm) into the film. This indicates that the blue laser will mainly generate carriers toward the perovskite-PEDOT:PSS interface, while the red-laser will generate carriers throughout the bulk of the film.
To explore the evolution in perovskite structure as it underwent degradation, X-ray diffraction was performed on unencapsulated control thin-films consisting of ITO/ PEDOT/perovskite glass using a Bruker D8 diffractometer (Cu-Kα). Scanning electron microscope (SEM) images were also recorded from the same films using a FEI (Inspect F) operating at a beam energy of 2 keV. In all cases, films were explored immediately after deposition, and then after one and two weeks following storage in the dark in dry air (RH 32%). EDS-SEM analysis was performed using an FEI Inspect F50 at 15 keV accelerating voltage with energy dispersive X-ray spectrometer (Oxford Instruments). All point spectral analysis was performed using AZtecEnergy EDS software (Oxford Instruments, Abingdon, UK).

Results and Discussion
In Figure 1, we plot the power conversion efficiency (PCE), fill factor (FF), short circuit current density (J sc ), and open circuit voltage (V oc ) of four CH 3 NH 3 PbI 3-x Cl x devices as a function of irradiance time. The data represented by lines was recorded using the Atlas system, whilst the data represented by symbols was taken using the calibrated Newport solar simulator (AM1.5, 100 mW/cm 2 ). All of the data is normalized to its initial value. It is important to note that a spectral mismatch exists between the xenon lamp of the Atlas system and the solar spectrum, and no aperture mask was used when performing measurements, therefore the data is used only to highlight trends, with all JV curves presented being taken using the Newport solar simulator.
Over the course of the 670 h test, the average PCE of devices decreased by approximately 80%, with the loss primarily originating from a ~ 70% reduction in the J sc . The FF and V oc were affected to a lesser extent, decreasing by 10-20% and 25-30% respectively. The trends seen in the data recorded using the Newport solar simulator are similar to those recorded using the Atlas system, although we observe some difference in the FF recorded using the different systems. We believe that this may originate from the fact that the temperature of the devices recorded using the Atlas system is slightly higher (37 vs. 25°C) [17].
We present the Ts80 lifetime of the devices held under the solar simulator in Table 1, defined as the time taken to reach 80% of the PCE immediately after the burn-in period (160 h). Data is presented measured using the Atlas Suntest CPS+ system and the calibrated Newport solar simulator. It can be seen that the calculated Ts80 lifetimes determined by the two systems are in statistical agreement. Our results indicate therefore that the devices have a Ts80 lifetime of (280 ± 20) hours. This is a shorter lifetime than those seen by Yin et al., who observed 68% loss of PCE after 300 h of aging, followed by very slow degradation over the subsequent 900 h [10]. Further improvements in stability can be gained using cesium-doped FAPbI 3 perovskites [12].
The JV curves used to plot the data-symbols in Figure 1 are plotted in Figure 2A. We also plot the average device metrics before and after aging in Table 2. It can be seen that we observe a large decrease in the shunt resistance (R sh ) [from 1100 ± 150 Ω cm 2 to 460 ± 20 Ω cm 2 ], indicative of an increase in leakage pathways, and an increase in the series resistance (R s ), [5.6 ± 0.3 Ω cm 2 to 25 ± 6 Ω cm 2 ], indicative of an increase in the energetic barriers to charge extraction and the creation of trap states within the active layer. Indeed, the decrease in V oc [0.92 ± 0.01 V to 0.69 ± 0.02 V] indicates an increase in charge carrier recombination rate within the device. It can also be observed that there is an increase in the level of hysteresis during the first week of testing (168 h), due to changes in the J sc between forward and reverse scans, further indicating an increase in the density of trap states and the migration of ionic species within the active layer [15][16][17][18][19][20][21][22][23].
Concomitant with the decrease in J sc , we observe a decrease in the external quantum efficiency (EQE) of the devices as shown in Figure 2B, with the peak EQE value dropping from 80% to 33%. The shape of the EQE curve also changes with time (Fig. S2), with the peak photocurrent wavelength shifting from 468 nm to 432 nm. This is also accompanied by a shift in the band edge (see Fig.  S3). The relative loss of EQE at wavelengths greater than 500 nm is characteristic of an increase in the relative levels of PbI 2 within the device [24]. The peak EQE and  the corresponding wavelengths are detailed in Table S1, along with the integrated and measured J sc .
To further explore the origin of the CH 3 NH 3 PbI 3-x Cl x device degradation route, we measured the PCE, FF, J sc and V oc for devices stored under dark conditions over a period of 840 h. Figure 3A-D shows average device metrics (normalized to their initial values) determined over 40 individual device pixels. Because our measurements were collected on a weekly basis (to avoid significant exposure to light), we are unable to determine a burn-in time as is done for the data presented in Figure 1. However it is clear that over a time interval of 670 h, the average PCE of the devices has fallen to a value that is around 45% of their original value. This reduction is similar to that observed under exposure to the AM1.5 radiation, which underwent a reduction to around 20% of their original efficiency over the same time period (see Fig. 1A). We note that the reduction in efficiency of dark-stored devices occurs principally as a result of a reduction in V oc and J sc ; a result also in accord with measurements performed under the solar simulator. This reasonably close correspondence between degradation processes observed in dark-and light-storage tests strongly suggests that the dominant degradation mechanism observed here is not catalysed by the exposure to light.
To further explore the mechanisms of the degradation, we have used time resolved photoluminescence (TRPL) measurements to explore carrier recombination dynamics. Here, measurements were performed on encapsulated films based on the structure ITO/PEDOT:PSS/ CH 3 NH 3 PbI 3-x Cl x both before illumination, and again after one and two weeks of continuous illumination as shown in Figure 4A. Here, it can be seen that there is an observed drop in the charge carrier lifetime after one week (168 h) of illumination. This effect could result from several different processes, including an increase in the density of trap states within the material, an increase in recombination rate and a decrease charge-carrier mobility [25][26][27].
We have also performed a preliminary study regarding the effectiveness of the encapsulation system. Images of an unencapsulated and an encapsulated ITO/PEDOT:PSS/ CH 3 NH 3 PbI 3-x Cl x film are shown in Figure 4B,C respectively. After 16 h of illumination, it can be seen that the unencapsulated films became yellow; a process characteristic of complete degradation of the CH 3 NH 3 PbI 3-x Cl x to PbI 2 in the presence of light [24,28,29]. In contrast the encapsulated films retained their original dark-brown color characteristic of CH 3 NH 3 PbI 3-x Cl x after two weeks of illumination.  To check whether damage to the LiF/Al cathode occurred during the lifetime test, we recorded images of the cathode using an optical microscope both before and after imaging, as shown in Figure 4D,E respectively, however no obvious delamination or formation of pin-holes was observed.
Laser beam induced current mapping was used before and after the irradiation measurements to investigate changes in spatially resolved photocurrent generation, with typical data plotted in Figure 5. Here, Figure 5A,D present optical microscope images recorded from the position corresponding to the LBIC mapping experiments both before and after 670 h of aging under simulated solar irradiation respectively. It can be seen that no obvious degradation of the film is visible. Figure 5B,E were recorded using a 405 nm laser before and after 670 h aging. Figure 5C,F similarly plot data recorded using a 670 nm laser both before and after irradiation respectively. Unfortunately, the location on the device surface of the two sets of measurements is different. We can, however, analyse the photocurrent maps by plotting a histogram of the photocurrent recorded across the device, with all histograms normalized to their peak photocurrent. This is shown in Figure 5G,H for devices imaged at 405 and 670 nm respectively, with each figure plotting histograms for devices both before and after irradiation.
We find that after aging, the average photocurrent signal measured by LBIC (at both imaging wavelengths) reduced by around 60%; a result consistent with the reduction in device J sc measured in aged devices. Note however that this reduction in photocurrent is correlated with a small increase in the standard deviation of the photocurrent signal, which increased from 4.2% to 7.4%, and 4.0% to 7.2% when imaged at 405 and 670 nm respectively. The relative similarity of the LBIC images recorded from aged devices at 405 and 670 nm suggests that degradation of the perovskite occurs equally both toward the PEDOT:PSS interface and within the bulk of the film. It is apparent, however, that the small increase in the relative width of the photocurrent distribution on aging indicates that perovskite degradation does not occur uniformly across the film, but that some areas are more susceptible to degradation than others. This could be due to thickness or compositional variations of the perovskite film. However, we suspect that this degradation process may be initiated at the edges of the perovskite grains. Larger scale LBIC images covering whole devices were recorded after aging (see Fig. S5). We find that the photocurrent was relatively homogeneous across most pixels, however, an area at the edge of one device exhibited very low current generation, possibly due to complete degradation of the perovskite.
To further characterize the film degradation process, we recorded X-ray diffraction (XRD) spectra on darkstored samples over a period of 2 weeks to explore the effects of dark-stored degradation. Here, films were not encapsulated, but were stored in a dry environment (at a relative humidity of ~30%) to characterize the dominant degradation mechanisms. Typical data are presented in Figure 6, where we show X-ray diffraction around the (110) perovskite and (001) PbI 2 reflections [11,[30][31][32].
Here, it can be seen that after approximately 2 weeks, the presence of PbI 2 is detected through the growth of a (001) scattering feature at an angle of 12.5°.  To explore changes in film morphology at higher spatial-resolution as a result of dark-storage, SEM images were recorded on an unencapsulated ITO/PEDOT:PSS/ CH 3 NH 3 PbI 3-x Cl x sample stored in the dark in dry-air for a period of 2 weeks. Figure 7 plots images of the same sample (but recorded at different positions) when freshly cast, and after one and two weeks. Here, images were recorded over a period of 2 weeks. It can be seen from Figure 7C that after 2 weeks, the perovskite grains appear to separate, leaving pin-holes. We propose that such an evolution in film structure is consistent with degradation of perovskite films that commences at grain boundaries and progresses inwards to the centre of grains. Additionally, Figure S7 is a higher magnification SEM image showing that smaller grains, with a higher proportional grain surface area, are the first to show reduction in size. It is likely that the apparent reduction in perovskite grain size is correlated with the increase in PbI 2 fraction, as evidenced in Figure 6. EDS-SEM analysis was also performed on a degraded perovskite film (Fig.  S8). Here, we found that the Pb:I ratio decreased in degraded regions of the film. We found that the Pb:I ratio (atomic wt%) varied from 1:2.98 to 1:1.24 between regions that appeared undegraded to most degraded respectively. This suggests that in regions where the Pb:I ratio is less than 2, there are also other additional non-PbI 2 degradation products present such as PbCO 3 , Pb(OH) 2 and PbO [33]. The difference could also be due to iodine escaping the film as HI or I 2 degradation products [34]. Our measurements therefore confirm the degradation of the unencapsulated perovskite films under dark-storage, with degraded films appearing less continuous in nature and characterized by an increased fraction of PbI 2 . When the perovskite film is used as the active layer in working devices, we observe a reduction in device performance that also does not appear connected to exposure to light, and thus a light-induced reaction of a superoxide with methylammonium is unlikely to be important here [28,29]. Rather, the significant decrease in J sc , the reduction in the EQE at wavelengths >500 nm and decrease in charge carrier lifetime suggests a reaction with water resulting in the  decomposition of the perovskite into methylamine (CH 3 NH 2 ), hydroiodic acid (HI), iodine, and PbI 2 [11,28,29,35]. Exact differences in the rate of degradation of light-and dark-stored devices are likely to be explained on the basis of differing temperature. Note however at this stage we cannot fully rule out additional reactions between the acidic PEDOT:PSS and ITO or perovskite resulting in additional degradation pathways [14]. We note however that organic photovoltaics incorporating a PEDOT:PSS/ITO anode retain high efficiency after a period of at least one year [37]. We also speculate that the locally reduced photocurrent observed in the LBIC images of aged devices (see Fig. 5E,F) may correlate with regions of increased PbI 2 concentration. Measurements using LBIC and Raman mapping are planned to test this hypothesis.
We have previously found that polymer:fullerene solar cells (using Ca/Al cathodes) encapsulated in the same manner have operational lifetimes greater than 1 year [36], and thus it is unlikely that the water that catalysed the perovskite degradation entered through the encapsulation. This conclusion is based on the fact that ingress of moisture through the encapsulation would most likely be evidenced through initial degradation toward the edge of the encapsulated film resulting from a diffusion-limited process; a result that was not observed here. We suspect therefore that water that was initially bound in the PEDOT:PSS film (which is known to be highly hygroscopic [37,38]), underwent diffusion into the perovskite film and initiated its decomposition. However, it is also possible that the air-based process used to deposit the perovskite resulted in a small fraction of water also being trapped within the perovskite layer itself. We note that as methylamine and HI are soluble in water and are volatile, they would normally escape an unencapsulated CH 3 NH 3 PbI 3-x Cl x film leaving a PbI 2 film. However, the encapsulation used here is likely to significantly reduce the rate at which these species escape, allowing them to remain in the film. As the highest occupied state of methylamine is located at 1.17 eV above the valence band maximum of the perovskite (and well into the band gap of the material) and the lowest unoccupied state of HI exists ~ 50 meV below the conduction band of the perovskite, both of these species can potentially act as trap-state of sites for nonradiative recombination [39]; a result consistent with the observed increase in charge trapping.

Conclusions
We have explored the operational stability of perovskite solar cells encapsulated using both glass and UV-cured epoxy, based on the inverted architecture structure ITO/ PEDOT:PSS/CH 3 NH 3 PbI 3-x Cl x /PC 70 BM/LiF/Al. We find that when exposed to AM1.5 radiation, the operational lifetime of devices (Ts80 lifetime) is (280 ± 20) hours.
Devices stored under dark conditions had similar decay lifetimes to those exposed to light from the solar simulator. Optical microscopy indicated that this degradation was not apparently connected to observable damage to the LiF/ Al cathode. Scanning photocurrent-imaging measurements performed on devices at different excitation wavelengths revealed nonuniformities across the active area of the aged devices, with measurements also confirming that degradation occurred throughout the bulk of the perovskite layer rather than being confined to an interface. Control measurements using XRD on unencapsulated perovskite/ PEDOT:PSS films subject to dark-storage in dry air confirmed the generation of PbI 2 through an observed increase in a (001) PbI 2 scattering signal. SEM imaging performed on the same films indicated that degraded films were characterized by less continuous structure. Our measurements suggest therefore that the principle degradation route in the encapsulated devices does not involve an optically induced reaction with a superoxide species. Instead, we speculate that the observed degradation occurred as a result of a reaction between the perovskite and water that was introduced into the device during fabrication (most probably via the hydroscopic PEDOT:PSS hole-extraction layer), facilitating the decomposition of the perovskite into methylamine, hydroiodic acid and PbI 2 . As the escape of methylamine and hydroiodic acid from the device is likely hindered by the device encapsulation, such species may also act as nonradiative recombination centers, reducing charge transport properties and thus reducing device J sc . Our results highlight the importance of removing hydroscopic materials from the device structure.

Supporting Information
Additional supporting information may be found in the online version of this article: Figure S1. 10x optical microscope image of cured epoxy encapsulation between two clean glass slides. Figure S2. EQE data normalized to the peak value each week, highlighting the relative change in shape and loss of EQE. Figure S3. Tauc plot of EQE band edge. Inset are the estimated values for the optical bandgap for each week at wavelengths longer than 500 nm Figure S4. Real and imaginary refractive index for CH3NH3PbI3-xClx as measured by ellipsometry. Figure S5. Laser beam inducted current maps of all four devices after the 670 h stability test, taken using a 405 nm laser and normalized to the peak photocurrent. Figure S6. XRD measurements taken on the same sample across 2 weeks of dark-storage. Figure S7. Secondary electron SEM image showing grains that appear to be decreasing in size when compared to those in Fig. 7 (main text). Figure S8. EDS-SEM analysis of a degraded sample, (a) SEM image showing three locations for EDS spectral analysis, (b) spectrum at degraded point of film, (c) spectrum at pristine portion of film, (d) spectrum at partially degraded section of film. Quantitative analysis shows the degraded area is lead-rich, with Pb:I ratio (atomic wt%) of 1.24, 2.98, and 2.74 for each spectra (b)-(d). Table S1. Peak EQE and integrated J sc taken each week during the lifetime study.