{'fraction_non_alphanumeric': 0.036775025060862096, 'fraction_numerical': 0.0158671058284405, 'mean_word_length': 4.8959810874704495, 'pattern_counts': {'":': 0, '<': 28, '<?xml version=': 0, '>': 0, 'https://': 0, 'lorem ipsum': 0, 'www.': 0, 'xml': 0}, 'pii_count': 0, 'substrings_counts': 0, 'word_list_counts': {'cursed_substrings.json': 0, 'profanity_word_list.json': 0, 'sexual_word_list.json': 0, 'zh_pornsignals.json': 0}}
Modified Nano-Montmorillonite and Monensin Modulate In Vitro Ruminal Fermentation, Nutrient Degradability, and Methanogenesis Differently

Simple Summary Natural montmorillonite (NM) is the most common clay used as a feed additive in ruminant diets. Under normal pH conditions, it can adsorb hydrogen and may affect methane (CH4) formation; however, it possesses less efficiency than other clays. Due to NM’s negative charge flat surface and positive charge edges, its physicochemical properties can be modified by cationic or anionic surfactants. Therefore, two types of modified nano-montmorillonite (MNM) were developed by ion-exchange reactions using cationic and anionic surfactants. Comparisons were made with monensin as a rumen modulator to reduce CH4 emission from ruminants. The results indicated that the physicochemical properties of both MNM types were enhanced (e.g., cation-exchange capacity and zeta potential). All MNM clays and monensin successfully reduced rumen CH4 production and ammonia concentration; however, clay modified by cationic surfactant was more efficient than what was modified by anionic surfactant in modulating in vitro rumen fermentation properties Abstract Two types of modified nano-montmorillonite (MNM) were developed by ion-exchange reactions using two different surfactants; sodium dodecyl sulfate (SDS) and cetyltrimethylammonium bromide (CETAB), to prepare MNMSDS and MNMCETAB, respectively. Both MNM types were on the nano-scale and had higher cation-exchange capacity values than NM clay. The MNMCETAB had the highest zeta potential (−27 mV) compared with the other clays. Effects of MNM types on in vitro ruminal batch culture fermentation, nutrient degradability, and methane (CH4) emission compared with monensin were evaluated in vitro using a semi-automatic gas production system. The experimental treatments were the control (0 supplementations), monensin (40 mg/kg DM), and NM (5 g NM/kg DM), and two levels of MNMSDS and MNMCETAB were supplemented at 0.05 (low) and 0.5 (high) g/kg DM to the control basal feed substrate. Among the experimental treatments, the high dose of both MNM types reduced (p < 0.01) CH4 production and ammonia concentrations compared with the control, while only MNMCETAB treatment tended to increase (p = 0.08) the truly degraded organic matter compared with monensin. All MNM treatments increased (p < 0.01) acetate molar proportions compared with monensin. The high MNMCETAB increased (p < 0.01) the in vitro ruminal batch culture pH compared with the control and monensin. The MNMCETAB supplemented at 0.5 g/kg DM is the most efficient additive to reduce CH4 emission with the advantage of enhancing the in vitro nutrient degradability of the experimental feed substrate. These results indicated that MNM could modulate the in vitro ruminal fermentation pattern in a dose- and type-dependent manner.


Introduction
Enteric fermentation is considered an actual cause of climate change and environmental pollution due to the emissions of greenhouse gases (e.g., methane (CH 4 ) and carbon dioxide (CO 2 )) [1]. Methane is 28 times more powerful as a potent greenhouse gas than CO 2 ; it is directly produced by ruminal methanogens, while other hydrogen-producing microorganisms (e.g., protozoa) can indirectly contribute the CH 4 formation through a synergistic association relationship with methanogens [1][2][3]. Moreover, the CH 4 emission from ruminants represents a significant loss of dietary energy, which could be redirected towards valuable animal products [2]. Therefore, various rumen fermentation modifiers have been applied for ruminants to inhibit CH 4 emission; however, the dietary antibiotic ionophores (e.g., sodium monensin) seem to be the most successful ones [3]. Ionophores are polyether antibiotics acting as inhibitors to deamination and H+ producing bacteria. They mainly disturb the bacterial cell wall membrane through ion exchange capacity, specifically H+/Na+ and H+/K+ antiport activity [1]. Nevertheless, the current global scenario has shifted the interest towards natural and safe feed supplements instead of antibiotics for protecting the environment and producing safe animal products [2,3].
Geophagy (eating clays) is a common natural habit of ruminants. Therefore, several clay classes are recognized as safe for animal and human consumption [4,5]. Natural montmorillonite (NM), also named microcrystalline kaolinite, has an advantage over other clays because of its high availability, low cost, large surface area, small particle size, and high ion exchange activity characteristics [5,6]. Moreover, it acts as a buffering agent to regulate acidosis. Additionally, it works against bloat and diarrhea and can adsorb heavy metals and aflatoxins [7]; therefore, NM was widely used as a feed additive for ruminants. Natural montmorillonite has lower antibacterial effects than other nano or organically modified clays [5,6]. Tate et al. [5] reported the first investigation on using NM as a rumen modifier to reduce rumen CH 4 production in vitro through a direct inhibition effect on methanogens. They found that NM was less effective in inhibiting methanogenesis than other kaolinite clays.
Montmorillonite platelets have a unique ionic composition: a negative charge flat surface and positive charge edges [5,6]. Thus, inorganic ions in NM can be effectively exchanged with both cationic and anionic surfactants through ion exchange reactions [8]. This phenomenon was exploited to modify and enhance the cation exchange capacity (CEC) and antibacterial properties of NM. Compared with NM, modification of montmorillonite using cationic surfactants (e.g., quaternary ammonium salts) leads to damage to the cellular membrane of Gram-positive bacteria cells (e.g., Staphylococcus aureus) [6]. In addition, montmorillonite modified by anionic organosulfur surfactants that have antimicrobial properties (e.g., sodium dodecyl sulfate (SDS)) possesses high CEC, which in turn increased the uptake of heavy metal ions [8]. Additionally, modifying NM by mechanical grinding improved the clay's stability and physicochemical properties while exhibited intense antibacterial activity against Escherichia coli [4].
Recently, grinding the natural clays (e.g., zeolite) in the nano-scale (1-100 nm) enhanced the clay's chemical stability and physicochemical properties [9]. At the same time, it reduced CH 4 and ammonia production while improved the fiber or organic matter rumen degradability in a dose and particle-size-dependent manner [9]. It can be speculated that, if nano-scale dispersion for modified montmorillonite would be achieved, new exceptional physicochemical properties might appear for the modified clays and/or the lowest effective supplementation dose could be obtained. Our working hypotheses are as follows: (1) The actively modified nano montmorillonite (MNM) can be prepared by chemical and nano grinding modifications. (2) The prepared MNM can modulate ruminal in vitro batch culture fermentation patterns, including methanogenesis. Therefore, we developed two different types of MNM using anionic (sodium dodecyl sulfate (SDS)) and cationic (cetyltrimethylammonium bromide (CETAB)) surfactants. This study is the first investigation to evaluate the effects of modified clays compared with antibiotic monensin on in vitro fermentation, protozoal count, and nutrient degradability.

Materials and Methods
This study was carried out at the Advanced Laboratory of Animal Nutrition, Faculty of Agriculture, Alexandria University, Alexandria, Egypt. All procedures and experimental protocols were carried out according to the guidelines for the care and use of animals in research of Alexandria University (AU 08-200415164).

Preparation of MNM Products
Natural montmorillonite clay (NM) was commercially supplied (Egypt Bentonite and Derivatives Co., Alexandria, Egypt) in powder form. The NM clay contained 544 g/kg dry matter (DM) of silicon dioxide, 190 g/kg dry matter of aluminum oxide, 135 g/kg dry matter of Iron(II) + iron(II, III), 52 g/kg dry matter of sodium oxide, 18.1 g/kg dry matter of titanium dioxide, 31 g/kg dry matter of magnesium oxide, 16 g/kg dry matter of calcium oxide, 12 g/kg dry matter of potassium oxide, and 1.9 g/kg dry matter of phosphorus pentoxide. The method of Bujdáková et al. [10] was followed to obtain the experimental MNM types, using two different surfactants, SDS and CETAB (Sigma Aldrich Co., Irvine, Scotland), to prepare the modified nano montmorillonite by SDS (MNM SDS ) and the modified nano montmorillonite by CETAB (MNM CETAB ), respectively. To obtain the nano-scale of MNM CETAB and MNMsds, the resulting materials were ground using High-Energy Laboratory Planetary Ball Miller (Retsch PM, VERDER SCIENTIFIC, North Rhine-Westphalia, Haan, Germany) for six hours with a reverse rotation speed of 300 rpm and vial rotation speed of 600 rpm with the ball to powder ratio of 9:1 mass/mass.

Physicochemical Properties of NM, MNMsds, and MNM CETAB
The particle size and the surface charge of the experimental clays were measured by zeta potential analysis using a Malvern ZETASIZER Nano series (Malvern, Worcestershire, United Kingdom) with a range of particle size detection from 0.3 nm to 10 microns at 25.0 ± 1 • C temperature, count rate (kcps) 347.4, measurement position (mm) 2.0, and attenuator 7.0.
The pH and electrical conductivity (EC) of the experimental feed additives were determined in a suspension of clay and distilled water (pH = 6.80) in a ratio of 1:2.5 by a multi-parameter pH meter (GLP 21 model; CRISON, Barcelona, Spain). The cationexchange capacity was measured according to [11] using 1 M sodium acetate−0.1 M sodium chloride.
The transmission electron microscope (TEM) was used to provide dimensional images for the experimental NM, MNMsds, MNM CETAB feed additives to detect the size and shape of their nanoparticles. Clay samples were coated with gold to improve the imaging of the clay sample and scanned using a TEM (JSM1400 plus-JEOL, Los Angeles, CA, USA) operated at a vacuum of the order of 10, and the accelerating voltage of the microscope was kept in the range of 10-20 kV.
The functional groups of the experimental feed additives were identified by Fourier Transform Infra-Red Spectroscopy (FTIR) using an infrared spectrometer (Shimadzu FTIR-8400S, Osaka, Japan) equipped with a deuterated triglycine sulfate (DTGS) KBr detector and purge gas generator. A basal feed substrate consisted of 500 g/kg dry matter of concentrate and 500 g g/kg dry matter of berseem hay (Trifolium alexandrinum) of the 3rd cut; this feed substrate was formulated to fulfill the national research council [12] nutrient requirements of growing cattle. The basal feed substrate was chemically analyzed according to the Association of Official Analytical Chemists [13] for DM, organic matter (OM), crude protein (CP; as 6.25 × nitrogen), and ether extract (EE). Neutral detergent fiber (NDF) and acid detergent fiber (ADF), and lignin were analyzed according to Van Soest et al. [14]. All plant cell well fractions were sequentially determined using the semi-automatic fiber analyzer (ANKOM, model A2001, Macedon, New York, NY, USA) using the same sample in a filter bag (F57-ANKOM Technology Corporation, Macedon, New York, NY, USA). Primary ingredients and chemical analyses of the basal feed substrate are shown in Table 1. The experimental treatments were the control (basal feed substrate without supplementations), monensin (basal feed substrate supplemented with 40 mg/kg DM sodium monensin (Rumensin ® , Elanco, Itapira, São Paulo, Brazil)), and NM (basal feed substrate supplemented with 5 g NM/kg DM), and four MNM treatments were tested using two doses (low and high) supplemented to the basal feed substrate. The low dose was 0.05 g MNM SDS or MNM CETAB /kg DM, and the high dose was 0.5 g MNM SDS or MNM CETAB /kg DM. The experimental dose of NM was tested according to Maki et al. [7]. Monensin was evaluated because it is one of the most common ionophore feed additives used to reduce ammonia and CH 4 emissions [1,3]. The experimental dose of monensin was the manufacturer's recommendation; this dosage (with the same source) was previously found to decrease CH 4 production and ammonia concentration in vitro while exerting minimal effects on the in vitro degradation of OM and total short-chain fatty acids (SCFAs) concentrations [3]. Therefore, a dose of 40 mg/ kg DM of monensin was used in the current study.

Procedure of GP
The experimental treatments were evaluated using the semi-automatic GP system according to Bueno et al. [15] and adapted to Soltan et al. [3]. The ruminal contents were collected separately from three fasted, slaughtered crossbred cow calves (440 ± 5 SE kg body weight) from the slaughterhouse that belongs to the Department of Animal and Fish Production, Faculty of Agriculture, Alexandria University, to avoid any unusual individual rumen environmental conditions [16]. These slaughtered calves were fed a local diet for beef production consisting of 500 g berseem hay (Trifolium alexandrinum) and 500 g commercial concentrate mixture (145 g crude protein/kg DM) ad libitum. The ruminal contents were transferred into pre-warmed thermo-containers (40 • C) under CO 2 flushing. To prepare the ruminal inocula (n = 3) to the in vitro incubation, the ruminal contents of each calf were blended for 10 s, squeezed by four layers of cheesecloth, and kept in water bath (39 • C) under continuous flushing of CO 2 .
For each ruminal inoculum, six in vitro incubation flasks (Arab Pharmaceutical Glass Company S.A.E., Suez, Egypt) as analytical replicates were prepared for each experimental treatment in addition to blank flasks (containing Menke's buffered medium and ruminal inoculum) [15] that were used to obtain the net gas production values and internal standard flasks (containing Menke's buffered medium, ruminal inoculum, and berseem clover hay) to correct for sensitivity variations induced by the inocula; variations above 10% were rejected [16].
A sample of 500 mg of each experimental feed substrate was accurately weighed into an incubation flask and incubated with 30 mL of the buffer solution and 15 mL of the inoculum while leaving a headspace of 75 mL [3,16]. The flasks were closed with 20 mm butyl rubber stoppers, sealed with aluminum seals, and incubated at 39 • C in a forced air incubator (FLAC STF-N 52 Lt, Treviglio, Lombardy, Italy) for 24 h. The headspace gas pressure of the flask was determined at 3, 6, 9, 12, and 24 h from the incubation start using a pressure transducer and a data logger (Pressure Press Data GN200, Piracicaba, Sao Paulo, Brazil). The volume of GP (mL) was calculated as 4.97 × measured pressure (psi) + 0.171 (n = 500; r 2 = 0.99) [3].
For CH 4 determination, one mL of the headspace gas was sampled at each pressure measuring time by a 3 mL syringe (Dawliaico, Assiut, Egypt) and was accumulated in

In Vitro Ruminal Batch Culture Fermentation, Protozoal Count, and Nutrient Degradability
After 24 h of incubation, all flasks were placed on ice to stop the microbial fermentation. Values of pH were determined by a portable pH meter (the same model that was used to measure the pH of the clays). The ammonia concentrations were determined calorimetrically using a commercial kit (Biodiagnostic kits, Giza, Egypt). The concentrations of SCFAs were measured according to Palmquist and Conrad [18] and adapted by Soltan et al. [3] using gas chromatography (GC; Thermo TRACE 1300, Rodano, Milan, Italy) equipped with a capillary column (TRFFAP 30 m × 0.53 mm ID × 0.5 µm film (thermo-part No: 260N225 P). The GC separation details have been reported by Salama et al. [16]. Protozoa were counted microscopy following the method described by Dehority et al. [19] using Neubauer improved bright-line hemacytometer counting chamber (Paul Marienfeld GmbH & Co. KG., Baden-Württemberg, Germany).
To determine the truly degraded organic matter (TDOM), the contents of the flasks were treated with the neutral detergent solution for three hour at 90 • C. The residuals non-degraded of the contents of the flasks were filtered in pre-weighed crucibles, washed with hot distilled water and acetone, dried, and allowed to be turned into ash. The TDOM was estimated by the difference between the incubated and non-degraded organic matter amounts, while the truly degraded neutral detergent fiber (TDNDF) was calculated by the difference between the amount of incubated NDF and the non-degraded NDF amounts [3]. The partitioning factor (PF) was calculated as the ratio of TDOM and net gas volume for 24 h [20].

Statistical Analysis
The in vitro assay was completed in one run (one day) for all experimental treatments. The actual statistical replications (n = 3) were the average of the analytical replicates (n = 6/inoculum). The experimental unit was the mean of the six analytical replicates formed one statistical replicate. All data were analyzed by one-way ANOVA using the MIXED procedure of SAS (SAS Institute Inc., Cary, NC, USA, version 9.0). Orthogonal contrast statements (contrast 1 and contrast 2) were designed to test each experimental parameter's linear and quadratic responses to increasing concentrations (0, 0.05, and 0.5 g/kg feed substrate) of MNM SDS and MNM CETAB , respectively. Comparisons among treatments were performed using Tukey's test, the effects were declared significant at p ≤ 0.05, and the trends were accepted if p < 0.10.

Physicochemical of NM, MNMsds, and MNM CETAB
Physicochemical characteristics of the experimental clays are shown in Table 2. Negligible variations in pH were detected among all clay products. The modification of NM either by CETAB or SDS resulted in a numerical reduction in the values of EC but enhanced CEC compared with the NM, MNM CETAB had the lowest EC values, and MNM SDS had the highest CEC values compared with other clays. The Zeta potential of NM clay was negative and became more negative after modifications by CETAB or SDS; MNM CETAB had the highest zeta potential compared with the other clays ( Figure 1).        Table 3 shows that NM treatment had the highest (p < 0.01) GP compared with antibiotic monensin and all MNM treatment except the low level of MNMSDS, while no differ-   Table 3 shows that NM treatment had the highest (p < 0.01) GP compared with antibiotic monensin and all MNM treatment except the low level of MNM SDS , while no differences were observed between the NM and the control. The contrast tests were significant for both MNM products. A linear decrease (p < 0.01) in GP values was observed by increasing the supplemental level of the modified clays. Similar CH 4 reductions (p < 0.01) were observed by all MNM products and monensin treatments compared with the control. The high dose of both MNM treatments resulted in the highest reduction (p < 0.01) in CH 4 production among all the experimental treatments. The contrast analysis showed that the decrease in CH 4 was in a dose-dependent manner by MNM products; MNM SDS reduced CH 4 in linear (p < 0.01) and quadratic (p = 0.02) trends, while MNM CETAB declined CH 4 in a linear (p < 0.01) trend.

Effect of MNM on In Vitro Ruminal Batch Culture GP, CH 4 , Nutrient Degradability, and Partitioning Factor
Monensin tended to reduce (p = 0.08) TDOM compared with MNM CETAB treatments and decreased (p < 0.01) TDNDF compared with all MNM treatments. The contrast analysis showed that TDOM and TDNDF were not affected by MNM SDS supplementation, while quadratic increases (p = 0.01) were recorded with the increasing doses of MNM CETAB supplementation. All MNM treatments (except MNM SDS low) enhanced (p < 0.01) the PF compared with the control. Increasing dosages of MNMsds showed linear increases (p < 0.01) in PF values, while MNM CETAB showed both linear (p < 0.01) and quadratic (p = 0.01) increases in PF values.

Effect of MNM Supplementation on In Vitro Ruminal Batch Culture pH, NH 3 -N and SCFAs
The results of the effects of the experimental montmorillonite types on in vitro pH, NH 3 -N, and SCFAs are shown in Table 4. The high MNM CETAB treatments increased (p < 0.01) ruminal pH compared with the control and monensin treatments. The contrast test showed that MNM CETAB quadratically reduced (p = 0.01) in vitro ruminal pH while MNM sds did not affect the pH values. The high doses of both MNM types, NM and monensin, decreased in (p < 0.01) NH 3 -N compared with the control. Both MNM types resulted in linear reductions (p < 0.01) in the NH 3 -N concentrations. The high MNM SDS and all MNM CETAB treatments increased (p < 0.01) the protozoal count compared with the monensin, and both MNM types linearly (p < 0.05) increased the protozoal count. The experimental treatments did not affect the total SCFAs concentrations, while modifications of molar proportions of individual SCFAs were observed. Increases in the acetate molar proportions and the acetate-to-propionate ratio were observed (p < 0.01) in the MNM treatments compared with monensin. Linear and quadratic increases (p < 0.01) in acetate molar proportions were marked by increasing levels of both MNM types. Monensin followed by MNM CETAB treatment had the highest (p < 0.01) propionate molar proportions compared with other treatments. Treatments with MNM SDS and MNM CETAB had increased (p < 0.05) the propionate molar proportions linearly and quadratically. All MNM treatments and monensin presented similar reductions (p < 0.01) in butyrate compared with NM and control treatments. Linear and quadratic declines (p < 0.05) in butyrate were observed in MNM treatments. All of the experimental feed additives reduced isovalerate compared with the control (p < 0.01), while the high MNM CETAB treatment had higher (p = 0.05) isobutyrate than monensin. Linear and quadratic decreases (p < 0.01) were observed by both MNM types, while MNM CETAB presented quadratic increase (p = 0.03) in isobutyrate molar proportions.  MNM SDS and OMNM CETAB = MNM modified by sodium dodecyl sulfate and cetyltrimethylammonium bromide, respectively. Low and high = MNM supplemented at 0.05 and 0.5 g/kg DM feed substrate, respectively. SEM = standard error of the mean, C 2 /C 3 = acetate to propionate ratio. Contrast: 1 = effects of control (0 supplementation g/kg DM) compared with MNM SDS supplementations, and Contrast: 2 = effects of control (0 supplementation g/kg DM) compared with MNM CETAB supplementations. a,b,c,d Means within a row without a common superscript letter differ significantly at p ≤ 0.05.

Discussion
Natural montmorillonite is a 2:1 phyllosilicate clay and has a unit crystal lattice formed by one alumina octahedral sheet sandwiched between two silica tetrahedral sheets; its interlayer contains water molecules and inorganic cations [4]. Due to this unique form, NM has a high CEC and surface area compared with other 1:1 clays. The mechanical grinding and modification of the natural montmorillonite can lead to the interlayer's collapse and can affect the swelling capacity and surface charge of the modified clays [4]. In this work, the physicochemical properties of the resultant MNM products were affected by the used surfactants compared with NM. The decrease in EC after CETAB and SDS modifications indicated that few electrons could move from the valence band to the conduction band [4]. Electrical conductivity is an indicator of salinity to measure a substrate's ability to allow for the transport of electric charges; thus, the EC of clays may affect ruminal passage rate of the digesta, dilution of feed particles, and microbial degradability [21].
A high CEC was observed for the experimental NM (77.5 mmol/100 g), which became higher by CETAB and SDS modifications. This high CEC of both MNM types can indicate the high number of metal hydrolysates and ions that can be intercalated into the clay interlayer space [22], which in turn improves the clay activity compared with NM. This can be indicated by the frequency shifts and intensity of the hydroxyl H-O-H bond detected by FTIR analysis in the MNM clays compared to NM. Additionally, at the medium frequency range, a new band related to Si-O-Si bond [4] appeared only for both MNM clays, while it was absent in NM. These frequency shifts indicate the higher hydrophobicity of the resultant MNM clays than NM [22]. The most likely explanation for the differences between MNM CETAB and MNM SDS in CEC is the way in which the experimental surfactants bonded the clay interlayer space, which affected the structure and surface affinity of the resultant MNM products. Anionic surfactants as SDS have weaker interactions with the montmorillonite interlayer than cationic surfactants as CETAB [8]. Anions (SO 3 − ) of SDS can be adsorbed on the edges of montmorillonite and compensated for its positive charges [8], while cations (NH 4 +) of CETAB can be adsorbed on the flat surface of the clay. This partly explains the higher negative charge of MNM CETAB than MNM SDS .
Three bands at the low-frequency range corresponding to the bending mode of Si-O and Si-O-M bonds [4] appeared by FTIR analysis in MNM SDS , while just two bands were observed in MNM CETAB . This result could be due to the functional sharing group of SDS with the structure R-O-SO 3 −. The increase of negative charges of MNM CETAB might be favorable to enhance its affinity with cationic matters, which might improve the adsorption capacity. These results confirm our first hypothesis that the physicochemical properties of MNM can be enhanced by the mechanical nano grinding and modification of NM. Thus, we evaluated their effects on rumen fermentation properties.
Rumen microbial fermentation is associated with the formation of greenhouse gasses (mainly CO 2 and CH 4 ). Montmorillonite is a potential adsorbent to capture CO 2 through a reaction between CO 2 molecules and its interlayer -OH groups by forming -HCO 3 − species, which in turn can react with other interlayer cations [23]. The reduction in GP caused by MNM types (especially MNM CETAB ) may suggest that MNM had a higher absorbance capacity to capture CO 2 than the NM. The literature reported that the modified montmorillonite has a higher CO 2 reversible retention capacity than the NM due to increases in hydrophobic surface, interlayer spacing, and intercalation of organic cations between the base -OH sites of the clay and the CO 2 molecules [23]. High CEC, shifts of the frequency and intensity of the hydroxyl H-O-H bonds detected by FTIR analysis, and increased negative charge of the MNM clays compared with NM may enhance the absorptive efficiency of MNM to capture CO 2 . It may be speculated that the CO 2 adsorption is also varied by the solvated cations situated in the MNM interlayer spacing; hence, MNM CETAB was the most effective clay to reduce GP.
Reductions in GP and CH 4 were consistent with enhancements in protozoal count and degradability of OM and NDF by MNM types , while this phenomenon did not appear after monensin treatment in the present study, in which CH 4 inhibition by monensin was consistent with adverse effects on nutrient degradability and protozoal count. These results suggested that monensin had a different CH 4 reduction mechanism from that of MNM. The antibacterial activity of sodium monensin against H 2 producing bacteria (including methanogens and cellulolytic bacteria) arises from disrupting the cell membranes through the ion transport of H+/K+ and Na+/H+ cations [1,24]. Monensin is also known for the inhibition effects of ruminal fungi and protozoa, which contribute to fiber degradation [1,3]; thus, it partly explained the decreased TDOM combined with CH 4 reduction by monensin therein. On the other hand, enhancing the protozoal count, TDOM, and TDNDF by MNM would promote H+ production. Hydrogen is the major intermediary metabolite in the ruminal degradation of NDF and OM that Archaea mainly use to reduce CO 2 into CH 4 . Thus theoretically, enhancing the OM and NDF degradability promotes CH 4 formation [1,25]. Therefore, CH 4 reduction caused by MNM would indicate that it may bind not only CO 2 but also H+. The increase in the intensity on the absorption bands of the OH group detected by FTIR analysis rather than the high negative charge zeta potential of the experimental MNM CETAB would indicate the increased ability to bind the acidic H+. Increases in ruminal in vitro batch culture pH observed by MNM CETAB may confirm such speculation, which in turn was favorable for microbial NDF degradation and may prevent ruminal acidosis.
Although the effect of MNM on the bacterial community was not evaluated (this has to be kept in consideration with MNM future studies), it can speculate that MNM has antibacterial effects against specific communities. However, both clay surfaces and bacterial cells have negatively charged sites; but the literature confirmed the ability of modified montmorillonite clays to bind them [5]. This is because of the presence of positively charged interlayer ions of the clay. In the current study, the changeable cations in MNM SDS and MNM CETAB in the clay edge or surface sites may affect the binding of rumen microbes to MNM surfaces through extracellular polysaccharides of the bacterial cell wall and, as a consequence, may affect the in vitro fermentation, including CH 4 formation [5]. It seems that both MNM types can affect methanogenesis by possessing direct antibacterial activity since the protozoal counts and TDNDF were enhanced [25]. The literature confirmed the synergistic relationship between protozoa and methanogens. Protozoa can provide them with their end metabolites, including H 2 [1]; thus, the protozoal count can indicate whether the treatments affected directly or indirectly the CH 4 emission [1,3]. The anionic organosulfate surfactants (e.g., SDS) possess antibacterial and anti-inflammatory properties by sharing R-O-SO 3 − functional groups [26]; thus, it may affect the antibacterial activity of the prepared MNM SDS . The more substantial reduction in CH 4 caused by MNM CETAB may be due to the quaternary positively charged ammonium group that can interact with Gram-positive bacterial cells, disrupt their cell membranes, and finally causes cell lysis [27]. Moreover, nano-clays have higher anti-methanogenic activity without adverse effects on the TDOM compared with their natural form [9]; this can partly explain the low effectiveness of NM to affect GP and CH 4 compared with MNM in the current study.
Enhancements in PF values may also contribute to the CH 4 reduction observed by MNM CETAB [28]. Removing H+ from the rumen ecosystem is known to increase ruminal pH and to stimulate ruminal microbial activity; thus, when CH 4 decreases, H+ may be used for producing SCFAs to ensure optimal ATP yield for the microbial mass production [2]. Increasing ruminal pH may increase protein solubility and generate branched-chain volatile fatty acids (BCVFA) production as isovalerate and isobutyrate [29]. Thus, it partly explains the increase in isobutyrate molar proportions consistent with high protozoal numbers and PF by MNM CETAB treatment. A puzzling finding of the current study was the decrease in the isovalerate molar proportion found by all clay treatments compared with the control. No clear explanation for this finding can be presented. Branched-chain volatile fatty acids (BCVFA) such as isovalerate and isobutyrate can be produced from leucine and valine degradation, respectively [30]. Consequently, rumen microbes utilize the produced BCVFA to promote protozoa and microbial protein synthesis [31,32]. Thus, it can be assumed that clay treatments may likely be incorporated differently into the rate of microbial degradation of these amino acids and/or BCVFA utilization. Apajalahti et al. [30] found that not all BCVFA produced are incorporated similarly to the microbial protein synthesis.
The typical mode of action to reduce CH 4 emission by monensin has occurred in this study by enhancing the redirections of the SCFAs pattern towards more propionate molar proportions and by reducing the acetate-to-propionate ratio [24]. The declines in ruminal in vitro batch culture pH, protozoal abundance, and TDNDF caused by monensin were favorable conditions for propionate producers [33]. On the other side, the associative enhancements in ruminal in vitro batch culture pH, protozoal numbers, and TDNDF were favorable conditions to acetate producers [3]; thus, acetate proportions were enhanced by MNM clays. Monensin inhibits Gram-positive bacteria, which are involved in protein degradation [24]. Therefore, further indications that monensin reduced the diet protein degradation can be provided by low TDOM, BCVFA, and ammonia values. Theoretically, enhancing TDOM may increase ammonia production; thus, it seems that ammonia reduction caused by MNM treatments was not a result of inhibition of protein degradation. Even NM treatment poetically reduced ammonia concentration without affecting TDOM. These results could be related to the presence of the acidic functional groups of the montmorillonite rather than the clay pore structure, which can enhance ammonia capture capacity to the clay. This function might be improved after the SDS or CETAB modifications because of the increases in CEC and shifts in the hydroxyl H-O-H bonds in addition to the more negative charge of MNM clays. These results may confirm our second hypothesis that MNM clays can modify the in vitro microbial fermentation, including CH 4 emission, and this effect was type-and dose-dependent.

Conclusions
Two different feed additives of MNM have been developed at the nanoscale using cationic (CETAB) and anionic (SDS) surfactants. The modification and the mechanical nano grinding enhanced the physicochemical properties of the natural montmorillonite clay. Both MNM types had lower EC and higher CEC values than the natural clay. The MNM CETAB showed a more significant negative charge than the other clays. All MNM clays and monensin successfully reduced the in vitro ruminal batch culture CH 4 production and ammonia concentration, while MNM CETAB enhanced TDOM, TDNDF, and pH compared with monensin. The experimental feed additives differently modified the SCFAs pattern. All MNM clays increased the acetate molar proportions, while only monensin increased propionate molar proportions. Under the conditions of this study, clay modified by cationic surfactant was more efficient than the anionic surfactant to modify rumen fermentation properties. The MNM CETAB supplemented at 0.5 g/kg can be used as a novel natural feed additive to reduce CH 4 without adversely affecting rumen fermentation or fiber degradability. These results emphasized that MNM clays can modulate in vitro microbial fermentation patterns in different pathways from that of monensin.