{'fraction_non_alphanumeric': 0.018361581920903956, 'fraction_numerical': 0.005649717514124294, 'mean_word_length': 5.950980392156863, 'pattern_counts': {'":': 0, '<': 0, '<?xml version=': 0, '>': 0, 'https://': 0, 'lorem ipsum': 0, 'www.': 0, 'xml': 0}, 'pii_count': 0, 'substrings_counts': 0, 'word_list_counts': {'cursed_substrings.json': 0, 'profanity_word_list.json': 0, 'sexual_word_list.json': 0, 'zh_pornsignals.json': 0}}
Metastable Phase Formation in Undercooled Nd-Fe-B Alloys Investigated by In Situ Diffraction Using Synchrotron Radiation

Diffraction experiments on electromagnetically levitated Nd-Fe-B alloys during solidification of the undercooled melt have been performed at the European Synchrotron Radiation Facility (ESRF). By using high intensity synchrotron radiation complete diffraction spectra could be detected within a short period of some seconds thus enabling the observation of metastable solidification products that exhibits a limited lifetime. A metastable phase that crystallizes in wide composition range and that initiates the solidification of the stable Nd2Fe14B1-phase (φ-phase) have been observed.