{'fraction_non_alphanumeric': 0.026217228464419477, 'fraction_numerical': 0.0, 'mean_word_length': 5.14367816091954, 'pattern_counts': {'":': 0, '<': 0, '<?xml version=': 0, '>': 0, 'https://': 0, 'lorem ipsum': 0, 'www.': 0, 'xml': 0}, 'pii_count': 0, 'substrings_counts': 0, 'word_list_counts': {'cursed_substrings.json': 0, 'profanity_word_list.json': 0, 'sexual_word_list.json': 0, 'zh_pornsignals.json': 0}}
Non-stick Sol-Gel Coating for Aluminium

PTFE-based coatings have been widely used, for example, on aluminium moulds for moulding of polyolefin packaging materials for its non-stick property. However, these coatings do not meet the users’ scratch resistance and durability requirements. This paper describes a preliminary study on the synthesis and characterization of a PTFE/sol-gel composite coating material which combines the required non-stick and low friction properties of PTFE filler with the high scratch resistance and durability of a silica-based sol-gel matrix. The nonstick and low friction properties were achieved by using both the PTFE filler and the lubricious compound resulting from the reaction of a solvent with siloxane. The high scratch resistance was attributed to the enhanced adhesion to the electro-chemically pre-treated surface and the optimized silica and alumina filler contents in the sol-gel material. FE-SEM/EDX, FTIR, contact angle goniometry, scratch testing and a pin-ondisc tribometry were used to evaluate the coating properties.