Transport properties and superconductivity in $Ba_{1-x}M_xFe_2As_2$   (M=La and K) with double FeAs layers
  We synthesized the samples $Ba_{1-x}M_xFe_2As_2$ (M=La and K) with $ThCr_2Si_2$-type structure. These samples were systematically characterized by resistivity, thermoelectic power (TEP) and Hall coefficient ($R_H$). $BaFe_2As_2$ shows an anomaly in resistivity at about 140 K. Substitution of La for Ba leads to a shift of the anomaly to low temperature, but no superconducting transition is observed. Potassium doping leads to suppression of the anomaly in resistivity and induces superconductivity at 38 K as reported by Rotter et al.\cite{rotter}. The Hall coefficient and TEP measurements indicate that the TEP is negative for $BaFe_2As_2$ and La-doped $BaFe_2As_2$, indicating n-type carrier; while potassium doping leads to change of the sign in $R_H$ and TEP. It definitely indicates p-type carrier in superconducting $Ba_{1-x}K_xFe_2As_2$ with double FeAs layers, being in contrast to the case of $LnO_{1-x}F_xFeAs$ with single FeAs layer. A similar superconductivity is also observed in the sample with nominal composition $Ba_{1-x}K_xOFe_2As_2$. 
G. Wu, R. H. Liu, H. Chen, Y. J. Yan, T. Wu, Y. L. Xie, J. J. Ying, X.   F. Wang, D. F. Fang and X. H. Chen