Spin Ordering in LaOFeAs and Its Suppression in Superconductor   LaO0.89F0.11FeAs Probed by M\"ossbauer Spectroscopy
  The 57Fe M\"ossbauer spectroscopy was applied to an iron-based layered superconductor LaO0.89F0.11FeAs with a transition temperature of 26 K and its parent material LaOFeAs. Throughout the temperature range from 4.2 to 298 K, a singlet spectrum with no magnetic splitting was observed as a main component of each M\"ossbauer spectrum of the F-doped superconductor. No additional internal magnetic field was observed for the spectrum measured at 4.2 K under a magnetic field of 7 T. On the other hand, the parent LaOFeAs shows a magnetic transition at around 140 K, and this temperature is slightly lower than that of a structural phase transition from tetragonal to orthorhombic phase, which accompanies the resistivity anomaly at around 150 K. The magnetic moment is estimated to be ~0.35 $\mu$B/Fe at 4.2 K in the orthorhombic phase, and the spin disorder remains in the magnetic ordered state even at 4.2 K. The fact that no magnetic transition in LaO0.89F0.11FeAs was observed even at 4.2 K under 7 T implies a strong spin fluctuation above Tc or small magnetic moment in this system. Therefore, the present results show that the F-doping effectively suppresses the magnetic and structural transitions in the parent material and the suppression leads to emergence of superconductivity in this system. 
S. Kitao, Y. Kobayashi, S. Higashitaniguchi, M. Saito, Y. Kamihara, M.   Hirano, T. Mitsui, H. Hosono and M. Seto