One step synthesis of SmO1-xFxFeAs bulks with Tc = 54.6 K: High upper   critical field and critical current density
  A safe, simple and easily scaleable one-step sintering method is proposed to fabricate newly discovered superconductors of SmO1-xFxFeAs. Superconducting transition with the onset temperature of 54.6 K and high critical fields Hc2(0) >=200 T were confirmed in SmO1-xFxFeAs with x = 0.3. At 5 K and self field, critical current density Jc estimated from the magnetization hysteresis using the whole sample size and the average particle size reached 8.5x10^3 and 1.2x10^6 A/cm^2, respectively. Moreover, the Jc exhibited a very weak dependence on magnetic field. Microstructural characterizations revealed that the whole sample Jc improvement could be achieved by either perfect texture or optimization of fabrication process in this strongly-layered superconductor. Our results clearly demonstrated that one-step synthesis technique is unique and versatile and hence can be tailored easily for other rare earth derivatives of REFeAsO superconductors. 
Yanwei Ma, Zhaoshun Gao, Lei Wang, Yanpeng Qi, Dongliang Wang,   Xianping Zhang