Spontaneous ordering as an intrinsic effect at the mesoscopic scale: A   vibrational insight in (Zn,Be)Se by Raman scattering and first-principles   calculations
  The recent finding of a 1-bond->2-phonon `percolation'-type behaviour in several random zincblende alloys, supporting an unsuspected 1-bond->2-mode behaviour in the bond length distribution, renews interest for a discussion of CuPt-type spontaneous ordering (CPSO) as a purely intrinsic effect. We investigate this key issue from both experimental (Raman scattering) and theoretical (first-principles bond length and phonon calculations) sides, focusing on Zn[1-x]Be[x]Se (0<x=0.92). Its large contrast in cation-anion bond lengths should stimulate CPSO to some extent, and is at the origin of a uniquely well-resolved 1-bond->2-phonon behaviour for the Be-Se species. Based on percolation, CPSO finds a previously missing natural explanation, at the mesosocopic scale. Also, the transfer of oscillator strength from the high- to the low-frequency Be-Se mode in the Raman spectra potentially emerges as a sensitive probe of CPSO in ZnBeSe. First-principles calculations indicate that the transfer is completed for the value of the long range order parameter of eta~0.5 in ZnBeSe2 (x~0.5), corresponding to a pure 1-bond->1-mode behaviour. With further ordering the alloy is forced to re-adopt a non-rewarding 1-bond->2-mode behaviour, due to the formation of ZnSe/BeSe micro-domains in the crystal. Therefore eta~0.5 appears as an intrinsic limit to CPSO in ZnBeSe2, and possibly in stoichiometric alloys in general. 
O. Pages, A. V. Postnikov, A. Chafi, D. Bormann, P. Simon, F. Firszt,   W. Paszkowicz and E. Tournie