Resistivity studies under hydrostatic pressure on a low-resistance   variant of the quasi-2D organic superconductor kappa-(BEDT-TTF)2Cu[N(CN)2]Br:   quest for intrinsic scattering contributions
  Resistivity measurements have been performed on a low (LR)- and high (HR)-resistance variant of the kappa-(BEDT-TTF)_2Cu[N(CN)_2]Br superconductor. While the HR sample was synthesized following the standard procedure, the LR crystal is a result of a somewhat modified synthesis route. According to their residual resistivities and residual resistivity ratios, the LR crystal is of distinctly superior quality. He-gas pressure was used to study the effect of hydrostatic pressure on the different transport regimes for both variants. The main results of these comparative investigations are (i) a significant part of the inelastic-scattering contribution, which causes the anomalous rho(T) maximum in standard HR crystals around 90 K, is sample dependent, i.e. extrinsic in nature, (ii) the abrupt change in rho(T) at T* approx. 40 K from a strongly temperature-dependent behavior at T > T* to an only weakly T-dependent rho(T) at T < T* is unaffected by this scattering contribution and thus marks an independent property, most likely a second-order phase transition, (iii) both variants reveal a rho(T) proportional to AT^2 dependence at low temperatures, i.e. for T_c < T < T_0, although with strongly sample-dependent coefficients A and upper bounds for the T^2 behavior measured by T_0. The latter result is inconsistent with the T^2 dependence originating from coherent Fermi-liquid excitations. 
C. Strack, C. Akinci, B. Wolf, M. Lang, J. A. Schlueter, J. Wosnitza,   D. Schweitzer, J. Mueller