Direct evidence of rigidity loss and self-organisation in silicate   glasses
  The Brillouin elastic free energy change $DF$ between thermally annealed and quenched $(Na_2O)_x(SiO_2)_{1-x}$ glasses is found to decrease linearly at $x > 0.23$ (floppy phase), and to nearly vanish at $x < 0.18$   (stressed- rigid phase). The observed $D F(x)$ variation closely parallels the mean-field floppy mode fraction $f(x)$ in random networks, and fixes the two (floppy, stressed-rigid) elastic phases. In calorimetric measurements, the non-reversing enthalpy near $T_g$ is found to be large at $x < 0.18$ and at $x > 0.23$, but to nearly vanish in the $0.18 < x < 0.23$ range, suggesting existence of an intermediate phase between the floppy and stressed-rigid phases. 
Y. Vaills, T. Qu, M. Micoulaut, F. Chaimbault and P. Boolchand