Synthesis of Colloidal Mn2+:ZnO Quantum Dots and High-TC Ferromagnetic   Nanocrystalline Thin Films
  We report the synthesis of colloidal Mn2+-doped ZnO (Mn2+:ZnO) quantum dots and the preparation of room-temperature ferromagnetic nanocrystalline thin films. Mn2+:ZnO nanocrystals were prepared by a hydrolysis and condensation reaction in DMSO under atmospheric conditions. Synthesis was monitored by electronic absorption and electron paramagnetic resonance (EPR) spectroscopies. Zn(OAc)2 was found to strongly inhibit oxidation of Mn2+ by O2, allowing the synthesis of Mn2+:ZnO to be performed aerobically. Mn2+ ions were removed from the surfaces of as-prepared nanocrystals using dodecylamine to yield high-quality internally doped Mn2+:ZnO colloids of nearly spherical shape and uniform diameter (6.1 +/- 0.7 nm). Simulations of the highly resolved X- and Q-band nanocrystal EPR spectra, combined with quantitative analysis of magnetic susceptibilities, confirmed that the manganese is substitutionally incorporated into the ZnO nanocrystals as Mn2+ with very homogeneous speciation, differing from bulk Mn2+:ZnO only in the magnitude of D-strain. Robust ferromagnetism was observed in spin-coated thin films of the nanocrystals, with 300 K saturation moments as large as 1.35 Bohr magneton/Mn2+ and TC > 350 K. A distinct ferromagnetic resonance signal was observed in the EPR spectra of the ferromagnetic films. The occurrence of ferromagnetism in Mn2+:ZnO and its dependence on synthetic variables are discussed in the context of these and previous theoretical and experimental results. 
Nick S. Norberg, Kevin R. Kittilstved, James E. Amonette, Ravi K.   Kukkadapu, Dana A. Schwartz, and Daniel R. Gamelin